Gear

Info

Publication number: 20050025975
Type: Application
Filed: Jul 30, 2004
Publication Date: Feb 3, 2005
Applicant:
Inventors: Yusuke Okamoto (Kanagawa), Yoshiteru Yasuda (Yokohama), Takuro Yamaguchi (Yokohama), Makoto Kano (Yokohama)
Application Number: 10/902,303

Abstract

A gear comprised of a tooth surface and a hard carbon film formed on at least a part of the tooth surface. When the gear is used in lubricant including a specific component, a friction of a tooth surface of the gear is largely decreased, and therefore the gear performs an excellent power transmission efficiency. Further, when the gear is employed in a planetary gear mechanism or speed reducing mechanism which has a plurality of meshing portions of gears, the power transmission efficiency of the mechanism is also improved.

Description

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

This application has the following related applications: U.S. patent application Ser. Nos. 09/545,181 based on Japanese Patent Application Hei-11-102205 filed on Apr. 9, 1999; 10/468,713 which is the designated state (United States) application number of PCT Application JP02/10057 based on Japanese Patent Application 2001-117680 filed on Apr. 17, 2001; 10/355,099 based on Japanese Patent Application 2002-45576 filed on Feb. 22, 2002; 10/682,559 based on Japanese Patent Application No. 2002-302205 filed on Oct. 16, 2002; and 10/692,853 based on Japanese Patent Application 2002-322322 filed on Oct. 16, 2002.

BACKGROUND OF THE INVENTION

The present invention relates a gear for a power transmission mechanism, and more particularly to a gear which improves a transmission efficiency.

Generally, gears have been employed in various power transmission mechanisms. Representative gears for vehicle transmission mechanisms are mainly made by steel, such as carburized steel, carbonitrided steel, and chromium molybdenum steel.

SUMMARY OF THE INVENTION

Such gears for vehicle transmission mechanisms are required to reduce friction generated at the mesh between the gears in order to improve an output power and a fuel consumption of a vehicle. More specifically, there are a large number of meshes of gears in a planetary mechanism or speed reduction mechanism, and therefore, it has been strongly desired to decrease the frictions at the meshes of the gears in view of improving a power transmission efficiency of such mechanisms.

It is therefore an object of the present invention to provide an improved gear which performs an excellent power transmission efficiency by decreasing friction on the tooth surface of the gear.

An aspect of the present invention resides in a gear which comprises a tooth surface and a hard carbon film formed on at least a part of the tooth surface.

The other objects and features of this invention will become understood from the following description with reference to the accompanying drawings.

DETAILED DESCRIPTION OF THE INVENTION

Gears are generally slidingly contacted with each other during the revolution under an engaged (meshed) state with other gear. Therefore, reducing friction at tooth surfaces of gears is preferable in view of improving a power transmission efficiency of the gears.

A gear of the present invention is constructed such that a hard carbon 10 film (coating) is formed on at least a part of the gear. This hard carbon film is a film of amorphous carbon or hydrogen containing amorphous carbon which is referenced as a-C:H (amorphous carbon or hydrogen containing amorphous carbon), i-C (i carbon) and DLC (diamond-like carbon).

It is known that such a hard carbon film has a low friction coefficient when slides on the other surface under a dry condition (no lubricating condition). Although the principle of having such a low friction coefficient has not been completely elucidated, it can be assumed that a solid lubrication performance and properties such as a low Young's modulus and a high hardness of the hard carbon film attain the reduction of the friction coefficient.

On the other hand, when the hard carbon film is used in lubricant, the friction coefficient of the film in lubricant becomes different from that in the dry condition. A normal hard carbon film is made of carbon and unavoidable impurity, or of carbon, hydrogen and unavoidable impurity. A reactivity of a surface of the hard carbon film is low, and this property relates to a low-friction and a low-abrasion thereof. However, since the hard carbon film has a weak interaction relative to a base oil and additives in lubricant, a reduction merit of the friction coefficient in lubricant is relatively small as compared with that in the dry condition.

The present invention has been achieved by thorough study as to a hard carbon film having a low-friction coefficient in lubricant, a preferable lubricant, and an additive component.

First, a hard carbon film is formed on a tooth surface of a gear. The hard carbon film may be formed on a whole surface of the tooth surface of the gear or a partial surface of the tooth surface. Generally, there is a tendency that a forming of a film on a bottom portion of each gear tooth is not easy as compared with that on a top portion of each gear tooth. However, it is not necessary to forcibly form the hard carbon film on the uneasy forming portion, since the merit obtained by the hard carbon film is obtained according to a ratio of the film formed area. Further, even if a part of the film is worn out in use, the merit of the hard carbon film is maintained according to a size of the remaining hard carbon film.

Although gears are actually used by combining two or more gears, the hard carbon film may be formed on the whole of the tooth surface or may be formed on a part of the tooth surface. A film forming area of the hard carbon film may be properly determined upon taking account of a production cost, a productivity and a degree of the obtained merit.

Although a base metal of the gear is not basically limited, a carburized steel and a chromium molybdenum steel are preferably used to ensure an impact strength and a bending fatigue strength necessary for a gear. Further, carbonitrided steel is preferably used to suppress the softening of the base metal due to the semi-high-temperature condition during the film production process. An intermediate layer may be formed between the base metal and the hard carbon film to decrease the strain between the base metal and the hard carbon film and to improve the adherence of the film relative to the base metal. A commonly known method may be employed to form the intermediate layer.

The hard carbon film can be produced by a chemical vapor deposition (CVD) process or physical vapor deposition (PVD) process. Generally, a hard carbon film formed by CVD process contains hydrogen due to raw materials of organic compound, and the hydrogen amount of such produced film ranges from 15 to 40 atom % (atomic percent). On the other hand, PVD process is capable of producing the hard carbon film with and/or without hydrogen. Various processes of PVD have been proposed and put in practical use. The hard carbon film of the gear according to the present invention is preferable to be formed by means of an arc ion plating or spattering, in view of the adherence of the film on the base metal.

It is preferable that the hydrogen amount in the hard carbon film for the gear is as small as possible since the decrease of the hydrogen amount in the hard carbon film decreases the friction of the gear. Therefore, the hydrogen amount of the hard carbon film of the gear according to the present invention is set to be smaller than 1 atom %, and preferably smaller than 0.3 atom %. That is, it is preferable that the hard carbon film is formed by means of physical vapor deposition (PVC) process. The hydrogen amount in the hard carbon film is capable of being measured by a secondary ion mass spectroscopy (SIMS) or Rutherford backscattering spectroscopy (RBS).

The gear according to the present invention exhibits an excellent characteristic, particularly when it is used in or with lubricant. When the gear according to the present invention is used in lubricant, the lubricant may be properly selected from a lubricant using mineral oil or synthetic oil as base oil, such as gear oil, vehicle engine oil, turbine oil and spindle oil. Further, when poly-α-olefin is used as base oil of the lubricant, the friction decreasing merit is further improved. The reason thereof may be thought to be that poly-α-olefin oil has a property of easy adherence (deposition) onto the hard carbon film formed on the tooth surface of the gear.

Further, it is preferable that a compound including hydroxy group is added to lubricant as an additive, to further improve the friction reducing merit. The reason thereof is guessed that the said additive adheres on to the hard carbon film on the tooth surface of the gear through the hydroxy group. Further, it is preferable that the number of the hydroxy groups included in a molecular of the additive is as large as possible, in view of increasing the adsorption strength. However, if the number of the hydroxy groups is too large, there causes a possibility that the additive is separated from the base oil due to the excessive hydrophilicity. Therefore, the molecular structure of the additive should be designed upon taking account of the above-discussed points. Further it is preferable that the molecular structure of the additive is designed such that the hydroxy groups are located as near as possible in the molecular structure in case that the number of the hydroxy groups in one molecular is the same. A typical molecular for the additive is secondary alcohol (dihdyric alcohol) and tertiary alcohol (trihydric alcohol). Although the additive amount of the additive may be properly varied according to a usage pattern of the lubricant relative to the gear, it is preferable that the additive amount relative to the lubricant is within a range from 0.5 to 8 weight %. If the additive amount is too small, the friction reducing merit becomes small. If too large, there is a possibility that the additive is separated from the base oil.

As an additive of the lubricant, ester is preferable, and monoester of glycerin is more preferable. It is preferable that the number of carbon atoms of fatty acid constructing glycerin monoester is greater than or equal to 8, and preferably greater than or equal to 12. If the molecule size of the fatty acid consisting the ester in the additive is small, a film directly formed on a surface of the hard carbon film due to the additive becomes too thin, and therefore the friction reducing merit is decreased thereby. Polyhydric alcohol except for glycerin may be employed as an ingredient for the fatty ester additive of the lubricant although it is disadvantageous in cost.

Generally lubricant is obtained by adding proper additives in base oil such as mineral oil or synthetic oil. However, according to the usage condition and the usage circumstance of gears, lubricant including a hydroxy compound as a main component may be used instead of the above-discussed lubricant. If the lubricant including hydroxy compound is employed, the power transmission efficiency is largely improved.

Alcohol is preferable as the above-discussed hydroxy compound, and particularly, glycerin performs a large friction reducing effect. Further, when the gear slides in ethylene glycol, the excellent friction reducing merit is ensured thereby subsequent to a case that glycerin is used as lubricant for gears.

It is not necessary to construct the whole of the lubricant by the hydroxy compound. In response to the request and in correspond to usage such as wear prevention, rust prevention, viscosity control and anti-oxidation, various known additives may be added in lubricant. The total amount of such additives in lubricant is normally set to be smaller than or equal to 15 vol. %.

Further, in case that the gear according to the present invention is employed in a mechanism having a lot of mesh portions of gears, such as a planetary gear mechanism and a speed reducing mechanism, the performance of improving the power transmission efficient thereby is clearly ensured. In case that a planetary gear mechanism is employed in a speed reduction mechanism, it is possible to obtain a large speed reduction ratio while suppressing the size of the speed reduction mechanism. However, setting the speed reduction ratio at a large value radically degrades the power transmission efficiency. Accordingly, by using the gear according to the present invention as at least one of a sun gear, planetary gears and a ring gear of a planetary gear mechanism for a speed reduction mechanism, the degradation of the power transmission efficiency in the speed reduction mechanism is suppressed.

Hereinafter, there is discussed Examples according to the present invention and Comparative Examples thereof.

EXAMPLE 1 and COMPARATIVE EXAMPLE 1

Chromium molybdenum steel defined as SCM420H in JIS (Japan Industrial Standard) was employed as material of the gear of Example 1. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear.

Type of gear: spur gear

Module: 4 mm

Number of gear teeth: 60 (that of meshed gear: 40)

Face width: 10 mm

The above discussed gear of Example 1 was surfaced and degreased. Subsequently, a hard carbon film was formed on a tooth surface of the gear of Example 1 by arc ion plating (AIP) process. A thickness of the hard carbon film at a center portion of each tooth was 1.2 μm. The hydrogen amount in the hard carbon film was 0.1 atom % (atomic percent) as a result of the measurement using a secondary ion mass spectroscopy (SIMS).

The tooth surface of the gear coated by the hard carbon film was polished to remove droplets of the hard carbon film and to smoothen the surface thereof. A surface roughness Ra of the polished tooth portion was 0.04 μm. A gear (drive gear) meshed with the film coated gear was not coated with the hard carbon film. A surface roughness Ra of a tooth surface of the meshed (counter) gear was 0.17 μm. Hereinafter, as far as it is not specifically explained, tooth portions of Examples and Comparative Examples were finished such that a surface roughness Ra of the gear coated with DLC (diamond-like carbon) ranged from 0.02 μm to 0.06 μm, and a surface roughness Ra of the gear without DLC ranged from 0.1 μm to 0.3 μm. Since it is difficult to further smoothen the surface of the gear coated with DLC by the polishing due to the property of DLC film, the gear coated with DLC was previously grinded and polished to be smoothed before DLC is formed on the surface of the gear. The surface roughness Ra is explained as Ra₇₅in JIS (Japanese Industrial Standard) B0601(:2001).

The power transmission efficiency of the gear was measured using a power circulation type gear test equipment. In order to separately obtain a loss of a drive gear and bearings and a loss of the tested gear, it is necessary to execute various adaptations such as a special design of the drive gear (counter gear) and a separate measurement of the bearing loss. However, since it is possible to determine the advantages gained by the hard carbon film from the magnitude of the total loss without executing the separate detection of the losses of the total loss, the evaluations of Examples and Comparative Examples have been made from the transmission efficiency corresponding to the total loss.

More specifically, using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa(α)-olefin (PAO) oil and that the drive gear meshed with the tested gear was rotated at a speed of 6000 rpm (the revolution speed of the drive gear).

On the other hand, the gear of Comparative Example 1 was the same in shape and in material as that of Example 1 except that no hard carbon film was formed on the gear of Comparative Example 1. The total loss of Comparative Example 1 was measured under the condition as same as that of Example 1.

EXAMPLE 2 and COMPARATIVE EXAMPLE 2

Chromium molybdenum steel defined as SCM440H in JIS was employed as material of the gear of Example 2. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear.

Type of gear: spur gear

Module: 2 mm

Number of gear teeth: 60 (that of meshed gear: 20)

Face width: 3 mm

The above discussed gear of Example 2 was degreased and set in a vacuum chamber. A hard carbon film was formed on a tooth surface of the gear of Example 2 by arc ion plating (AIP) process in the vacuum chamber. A thickness of the hard carbon film at a center portion of each tooth was 1.4 μm. The hydrogen amount in the hard carbon film was 0.1 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surface was polished to remove droplets of the hard carbon film and to smoothen the surface. A gear (drive gear) meshed with the film coated gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 6000 rpm (the revolution speed of the drive gear). A kinetic viscosity of the employed poly-alfa-olefin was 4.0 cSt at 100° C. Hereinafter, the evaluation of examples and comparative examples was executed using the poly-alfa-olefin as same as that employed in Example 2.

On the other hand, the gear of Comparative Example 2 was the same in shape and in material as that of Example 2 except that no hard carbon film was formed on the gear of Comparative Example 2. The total loss of Comparative Example 2 was measured under the condition as same as that of Example 2.

EXAMPLE 3 and COMPARATIVE EXAMPLE 3

Chromium molybdenum steel defined as SCM420H in JIS (Japan Industrial Standard) was employed as material of the gear of Example 3. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear. Thereafter, a finishing touch was applied to the processed gear.

Type of gear: spur gear

Module: 6 mm

Number of gear teeth: 120 (that of meshed gear: 40)

Face width: 12 mm

The above discussed gear of Example 3 was degreased and set in a vacuum chamber. A hard carbon film was formed on a tooth surface of the gear of Example 3 by arc ion plating (AIP) process in the vacuum chamber. A thickness of the hard carbon film at a center portion of each tooth was 0.9 μm. The hydrogen amount in the film was 0.2 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surface was polished to remove droplets of the hard carbon film and to smoothen the surface. A gear (drive gear) meshed with the coated gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 9000 rpm (the revolution speed of the drive gear).

On the other hand, the gear of Comparative Example 3 was the same in shape and in material as that of Example 3 except that no hard carbon film is formed on the gear of Comparative Example 3. The total loss of Comparative Example 3 was measured under the condition as same as that of Example 3.

EXAMPLE 4 and COMPARATIVE EXAMPLE 4

Chromium molybdenum steel defined as SCM420H in JIS was employed as material of the gear of Example 4. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear. Thereafter, a finishing touch was applied to the processed gear.

Type of gear: spur gear

Module: 6 mm

Number of gear teeth: 120 (that of meshed gear: 40)

Face width: 12 mm

The above discussed gear of Example 4 was degreased and set in a vacuum chamber. A hard carbon film was formed on a tooth surface of the gear of Example 4 by the magnetron spattering process in the vacuum chamber. A thickness of the hard carbon film at a center portion of each tooth was 1.3 μm. The hydrogen amount in the film was 0.1 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surface was polished to remove droplets of the hard carbon film and to smoothen the surface. A gear (drive gear) meshed with the coated gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 9000 rpm (the revolution speed of the drive gear).

On the other hand, the gear of Comparative Example 4 was the same in shape and in material as that of Example 4 except that no hard carbon film was formed on the gear of Comparative Example 4. The total loss of Comparative Example 4 was measured under the condition as same as that of Example 4.

EXAMPLE 5 and COMPARATIVE EXAMPLE 5

Chromium molybdenum steel defined as SCM440H in JIS was employed as material of the gear of Example 5. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear. Thereafter, a finishing touch was applied to the processed gear.

Type of gear: spur gear

Module: 2 mm

Number of gear teeth: 60 (that of meshed gear: 20)

Face width: 3 mm

The above discussed gear of Example 5 was degreased and set in a vacuum chamber. A hard carbon film was formed on a tooth surface of the gear of Example 5 by a plasma CVD process in the vacuum chamber. Gas employed in the CVD process was cyclohexane. A thickness of the hard carbon film at a center portion of each tooth was 3.0 μm. The hydrogen amount in the hard carbon film was 25 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surface was polished to remove droplets of the hard carbon film and to smoothen the surface. A gear (drive gear) meshed with the coated gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 6000 rpm (the revolution speed of the drive gear).

On the other hand, the gear of Comparative Example 5 was as same in shape and in material as that of Example 5 except that no hard carbon film is formed on the gear of Comparative Example 5. The total loss of Comparative Example 5 was measured under the condition as same as that of Example 5.

EXAMPLE 6 and COMPARATIVE EXAMPLE 6

Chromium molybdenum steel defined as SCM420H in JIS was employed as material of the gear of Example 6. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering were applied to the machined gear.

Type of gear: helical gear

Module corresponding to spur gear: 4 mm

Number of gear teeth: 60 (that of meshed gear: 60)

Face width: 20 mm

Helix angle: 12°

The above discussed gear of Example 6 was surfaced (finished) and degreased. Subsequently, the gear for Example 6 was set in a vacuum chamber, and a hard carbon film was formed on a tooth surface of the gear of Example 6 by arc ion plating (AIP) process in the vacuum chamber. A thickness of the film at a center portion of each tooth was 1.0 μm. The hydrogen amount in the film was 0.1 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS).

The tooth surface was polished to remove droplets of the hard carbon film and to smoothen the surface. A gear (drive gear) meshed with the coated gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 6000 rpm (based on the drive gear).

On the other hand, the gear of Comparative Example 6 was as same in shape and in material as that of Example 6 except that no hard carbon film was formed on the gear of Comparative Example 6. The total loss of Comparative Example 6 was measured under the condition as same as that of Example 6.

EXAMPLE 7 and COMPARATIVE EXAMPLE 7

Chromium molybdenum steel defined as SCM440H in JIS was employed as material of the gear of Example 3. The material was machined into a gear defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gear. Thereafter, a finishing touch was applied to the processed gear.

Type of gear: spur gear

Module: 2 mm

number of gear teeth: 60 (that of meshed gear: 20)

Face width: 3 mm

The above discussed gear of Example 7 was degreased and set in a vacuum chamber. A hard carbon film was formed on a tooth surface of the gear of Example 7 by arc ion plating (AIP) process in the vacuum chamber. A thickness of the hard carbon film at a center portion of each tooth was 1.1 μm. The hydrogen amount in the film was 0.1 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surface was polished to remove droplets of the film and to smoothen the surface. A gear (drive gear) meshed with the coated gear was also coated with the hard carbon film. A thickness of the hard carbon film at a center portion of each tooth of the drive gear was 1.0 μm. The hydrogen amount in the hard carbon film of the drive gear was 0.1 atom %.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gear and the counter gear were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear meshed with the drive gear was rotated at a speed of 6000 rpm (the revolution speed of the drive gear).

On the other hand, the gear of Comparative Example 7 was as same in shape and in material as that of Example 7 except that no hard carbon film is formed on the gear of Comparative Example 7. The total loss of Comparative Example 7 was measured under the condition as same as that of Example 7.

EXAMPLE 8 and COMPARATIVE EXAMPLE 8

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 8 and Comparative Example 8 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is oleic acid) of 3 weight % of the total of the lubricant with poly-alfa-olefin. The other conditions of Example 8 and Comparative Example 8 were the same as those of Example 2. The evaluation of Example 8 and Comparative Example 8 were also the same as that of Example 2.

EXAMPLE 9 and COMPARATIVE EXAMPLE 9

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 9 and Comparative Example 9 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is palmitic acid) of 2 weight % in the total of the lubricant with poly-alfa-olefin. The other conditions of Example 9 and Comparative Example 9 were the same as those of Example 2. The evaluation of Example 9 and Comparative Example 9 were also the same as that of Example 2.

EXAMPLE 10 and COMPARATIVE EXAMPLE 10

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 10 and Comparative Example 10 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is stearic acid) of 7 weight % in the total of the lubricant with poly-alfa-olefin. The other conditions of Example 10 and Comparative Example 10 were the same as those of Example 2. The evaluation of Example 10 and Comparative Example 10 were also the same as that of Example 2.

EXAMPLE 11 and COMPARATIVE EXAMPLE 11

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, Lubricant employed in Example 11 and Comparative Example 11 was lubricant obtained by fully mixing an ester component which was butyl stearate of 2 weight % in the total of the lubricant with poly-alfa-olefin. The other conditions of Example 11 and Comparative Example 11 were the same as those of Example 2. The evaluation of Example 11 and Comparative Example 11 were also the same as that of Example 2.

EXAMPLE 12 and COMPARATIVE EXAMPLE 12

Chromium molybdenum steel defined as SCM440H in JIS (Japan Industrial Standard) was employed as material of the gears of Example 12. The material was machined into gears defined by the following specifications, and the carburizing, quenching and tempering processes were applied to the machined gears. Thereafter, a finishing touch was applied to the processed gear. The gears were assembled into a planetary gear mechanism of 2K-H type. In the evaluation of the gears, a sun gear functioning as an input gear, a ring gear was fixed, and a carrier of planetary gears functioning as an output.

Type of gear: spur gear

Module: 2 mm

Number of gear teeth of sun gear: 60

Number of gear teeth of planetary gear: 24

Number of gear teeth of ring gear: 144

Number of planetary gears: 3

Face width: 6 mm

The sun gear and the planetary gears of Example 12 were degreased and set in a vacuum chamber. Hard carbon films were formed on tooth surfaces of the gears by arc ion plating (AIP) process in the vacuum chamber. A thickness of the film at a center portion of the sun gear was 1.7 μm. The hydrogen amount in the film was 0.1 atom % as a result of the measurement using a secondary ion mass spectroscopy (SIMS). The tooth surfaces were polished to remove droplets of the film and to smoothen the surface. The ring gear was not coated with the hard carbon film.

Using the power circulation type gear test equipment, the total loss of the tested gear was measured under a condition that the tested gears were wholly soaked in poly-alfa-olefin (PAO) oil and that the tested gear was rotated at a speed of 6000 rpm (the revolution speed of the sun gear).

On the other hand, the gears of Comparative Example 12 were the same in shape and in material as those of Example 12 except that no hard carbon film was formed on the gears of Comparative Example 12. The total loss of Comparative Example 12 was measured under the condition as same as that of Example 12.

EXAMPLE 13 and COMPARATIVE EXAMPLE 13

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, Lubricant employed in Example 13 and Comparative Example 13 was JIS industrial gear oil specified by type 2 and viscosity classification ISO VG 220. The other conditions of Example 13 and Comparative Example 13 were the same as those of Example 2. The evaluation of Example 13 and Comparative Example 13 were also the same as that of Example 2.

EXAMPLE 14 and COMPARATIVE EXAMPLE 14

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 14 and Comparative Example 14 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is stearic acid) of 5 weight % in the total of the lubricant with JIS industrial gear oil specified by viscosity classification ISO VG 220 type 2. The other conditions of Example 14 and Comparative Example 14 were the same as those of Example 2. The evaluation of Example 14 and Comparative Example 14 were also the same as that of Example 2.

EXAMPLE 15 and COMPARATIVE EXAMPLE 15

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 15 and Comparative Example 15 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is stearic acid) of 4 weight % in the total of the lubricant with JIS industrial turbine oil specified by JIS-2213K type 2. The other conditions of Example 15 and Comparative Example 15 were the same as those of Example 2. The evaluation of Example 15 and Comparative Example 15 were -also the same as that of Example 2.

EXAMPLE 16 and COMPARATIVE EXAMPLE 16

The gears of Example 7 and Comparative Example 7 were evaluated under the different test conditions. More specifically, Lubricant employed in Example 16 and Comparative Example 16 was lubricant obtained by fully mixing an ester component which was fatty monoglyceride (a main component of fatty acid is stearic acid) of 7 weight % with poly-alfa-olefin, as same as that employed in Examples 10 and 11. The other conditions of Example 16 and Comparative Example 16 were the same as those of Example 7. The evaluation of Example 16 and Comparative Example 16 were also the same as that of Example 7 and Comparative Example 7.

EXAMPLE 17 and COMPARATIVE EXAMPLE 17

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 17 and Comparative Example 17 was lubricant obtained by fully mixing an ester component which was fatty diglyceride (a main component of fatty acid is stearic acid) of 2 weight % with poly-alfa-olefin. The other conditions of Example 17 and Comparative Example 17 were the same as those of Example 2. The evaluation of Example 17 and Comparative Example 17 were also the same as that of Example 2.

EXAMPLE 18 and COMPARATIVE EXAMPLE 18

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 18 and Comparative Example 18 was lubricant obtained by fully mixing pinacol having two hydroxy groups in one molecular at 0.8 weight % with poly-alfa-olefin. The other conditions of Example 18 and Comparative Example 18 were the same as those of Example 2. The evaluation of Example 18 and Comparative Example 18 were also the same as that of Example 2.

EXAMPLE 19 and COMPARATIVE EXAMPLE 19

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 19 and Comparative Example 19 was lubricant obtained by fully mixing 1,10-decandiol of 2.0 weight % and poly-alfa-olefin. The other conditions of Example 19 and Comparative Example 19 were-the same as those of Example 2. The evaluation of Example 19 and Comparative Example 19 were also the same as that of Example 2.

EXAMPLE 20 and COMPARATIVE EXAMPLE 20

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 20 and Comparative Example 20 was lubricant obtained by fully mixing dodecyl alcohol of 2.0 weight % with poly-alfa-olefin. The other conditions of Example 20 and Comparative Example 20 were the same as those of Example 2. The evaluation of Example 20 and Comparative Example 20 were also the same as that of Example 2.

EXAMPLE 21 and COMPARATIVE EXAMPLE 21

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 21 and Comparative Example 21 was glycerin. No additive was added in glycerin. The other conditions of Example 21 and Comparative Example 21 were the same as those of Example 2. The evaluation of Example 21 and Comparative Example 21 were also the same as that of Example 2.

EXAMPLE 22 and COMPARATIVE EXAMPLE 22

The gears of Example 2 and Comparative Example 2 were evaluated under the different test conditions. More specifically, lubricant employed in Example 22 and Comparative Example 22 was ethylene glycol. No additive was added in ethylene glycol. The other conditions of Example 22 and Comparative Example 22 were the same as those of Example 2. The evaluation of Example 22 and Comparative Example 22 were also the same as that of Example 2.

As to Examples 1 through 22 and Comparative Examples I through 22, the measurement results of the power transmission efficiencies thereof were shown in Table 1 together with the specifications of the gears, such as material, module, teeth number, film forming method, hydrogen amount in the hard carbon film, and a kind of lubricant.

As is apparent from Table 1, it was recognized that the gears of Examples 1 through 22 according to the present invention performed excellent power transmission efficiencies as compared with Comparative Examples 1 through 22, respectively. Specifically, Example 21 performed the excellent power transmission efficiency. Further, Example 16 is subsequently preferable in case that the selection of lubricant is limited such that the lubricant is commonly used in the other sliding pair. In case that both of cost and power transmission efficiency are balancedly minded, Example 8 through 10 are subsequently preferable.

With the thus arranged gear according to the present invention, by film the hard carbon film on al least a part of tooth face of the gear, it becomes possible to largely decrease the friction of the gear relative to the counter gear (meshed gear). Further, by employing a specifically blended lubricant, the friction of the gear is further preferably decreased. This provides the gear further improved in power transmission efficiency. Specifically, in case that lubricant may be freely selected, a largely improved power transmission efficiency is obtained by a lubricant wherein alcohol group is used as a main component of the lubricant. Further, the gear according to the present invention is preferably adapted to a mechanism which has a lot of gear meshing portions, such as a planetary gear mechanism and speed reduction mechanism. When the gear is employed in such mechanisms, the power transmission efficiency is further improved.

TABLE 1 Example/Comparative Example 1 2 3 4 5 6 7 8 Material SCM420H SCM440H SCM420H SCM420H SCM440H SCM420H SCM440H SMC440H Module (mm) 4 2 6 2 2 4 2 2 Number of 60 60 120 60 60 60 helical 60 60 Teeth Film Forming AIP AIP AIP Spattering Plasma AIP AIP (Both AIP Method CVD Gears) H amount 0.1 0.1 0.2 0.1 25 0.1 0.1 0.1 (atom %) Lubricant PAO PAO PAO PAO PAO PAO PAO PAO + Oleic acid monoglyceride Example 97.5 97.0 96.9 97.7 95.1 96.8 99.0 98.1 Transmission Efficiency (%) Comp. Example 93.3 93.1 94.2 93.1 93.1 94.0 93.1 94.4 Transmission Efficiency (%) Example/Comp. Example 9 10 11 12 13 14 15 Material SCM440H SCM440H SCM440H SCM440H SCM440H SCM440H SCM440H Module (mm) 2 2 2 2 2 2 2 Number of 60 60 60 60/24/144 2K-H 60 60 60 Teeth planetary gear mechanism Film Forming AIP AIP AIP AIP AIP AIP AIP Method H amount 0.1 0.1 0.1 0.1 0.1 0.1 0.1 (atom %) Lubricant PAO + PAO + PAO + Butyl PAO Gear oil Gear oil + Turbine oil + Palmitic acid Stearic acid stearate Stearic acid Stearic acid monoglyceride monoglyceride (Stearic acid monoglyceride monoglyceride butyl ester) Example 97.9 98.4 97.7 93.3 95.5 96.7 94.7 Transmission Efficiency (%) Comp. Example 93.5 94.6 94.4 86.0 92.5 92.2 91.1 Transmission Efficiency (%) Example/Comp. Example 16 17 18 19 20 21 22 Material SCM440H SCM440H SCM440H SCM440H SCM440H SCM440H SCM440H Module (mm) 2 2 2 2 2 2 2 Number of Teeth 60 60 60 60 60 60 60 Film Forming AIP (Both AIP AIP AIP AIP AIP AIP Method Gears) H amount 0.1 0.1 0.1 0.1 0.1 0.1 0.1 (atom %) Lubricant PAO + Stearic PAO + Stearic PAO + Pinacol PAO + 1,10- PAO + Dodecyl Glycerin Ethylene acid acid decanediol alcohol glycol monoglyceride diglyceride Example 99.2 97.9 97.1 97.8 97.6 99.3 99.2 Transmission Efficiency (%) Comp. Example 94.6 93.2 93.2 93.3 93.7 92.7 91.6 Transmission Efficiency (%)
Notes

AIP: arc ion plating process, PAO: poly-alfa (α)-olefin.

This application is based on Japanese Patent Applications No. 2003-204238 filed on Jul. 31, 2003 and No. 2004-127632 filed on Apr. 23, 2004 in Japan. The entire contents of these Japanese Patent Applications are incorporated herein by reference.

Although the invention has been described above by reference to certain embodiments of the invention, the invention is not limited to the embodiments described above. Modifications and variations of the embodiments described above will occur to those skilled in the art, in light of the above teaching. The scope of the invention is defined with reference to the following claims.

Claims

1. A gear comprising:

a tooth surface; and

a hard carbon film formed on at least a part of the tooth surface.

2. The gear as claimed in claim 1, wherein a hydrogen amount in the hard carbon film is smaller than or equal to 1 atomic percent.

3. The gear as claimed in claim 2, wherein a hydrogen amount in the hard carbon film is smaller than or equal to 0.3 atomic percent.

4. The gear as claimed in claim 1, wherein the gear is used as a gear of a planetary gear mechanism.

5. The gear as claimed in claim 1, wherein the gear is used as a gear of a speed reduction mechanism.

6. The gear as claimed in claim 1, wherein the gear is used in a lubricant.

7. The gear as claimed in claim 6, wherein the lubricant includes a mixture employing poly-alfa-olefin (PAO) as a base oil.

8. The gear as claimed in claim 6, wherein the lubricant includes an additive including a hydroxyl group.

9. The gear as claimed in claim 8, wherein the additive includes two or more hydroxyl groups in a molecule.

10. The gear as claimed in claim 6, wherein an additive in the lubricant includes ester.

11. The gear as claimed in claim 6, wherein an additive in the lubricant includes monoester of glycerin.

12. The gear as claimed in claim 6, wherein a main component of the lubricant is a hydroxy-compound.

13. The gear as claimed in claim 12, wherein the hydroxy-compound includes alcohol.

14. The gear as claimed in claim 13, wherein the alcohol includes glycerin.

15. The gear as claimed in claim 13, wherein the alcohol includes ethylene glycol.