Method of manufacturing a thermal dissipation assembly
The present invention discloses a method of providing an integral thermal interface on an interface surface of a heat dissipation device, such as a heat sink. In accordance with the present invention, the phase change material is applied directly onto the interface surface of the heat sink to form an integral interface layer directly on the heat sink during the manufacturing process. This process includes the steps of providing a heat dissipating device having an interface surface, liquefying the phase change material at a controlled temperature so as to decrease the material viscosity to a flowable form, applying the liquefied phase change material directly onto the mating surface of the heat dissipating device either by directly dispensing the material, screen printing or stencil printing and cooling the material causing it to cure on the surface of the heat dissipating device.
This application is a divisional of U.S. patent application Ser. No. 10/224,161, filed Aug. 20, 2002 and is also related to and claims priority from earlier filed provisional patent application No. 60/316,470 filed Aug. 31, 2001.
BACKGROUND OF THE INVENTIONThe present invention relates generally to a method of applying an electronic material composition to an interface surface for use in connection with heat generating electronic devices. More particularly, this invention relates to a new method of applying a phase change thermal interface material to the contact surface of a heat dissipation device such as a heat sink.
In the electronics and computer industries, it has been well known to employ various types of electronic device packages and integrated circuit chips, such as the PENTIUM central processing unit chip (CPU) manufactured by Intel Corporation and RAM (random access memory) chips. These integrated circuit chips generate a great deal of heat during operation, which must be removed to prevent adverse effects on operation of the system into which the device is installed. In the prior art, heat sinks are commonly placed in thermal communication with the heat-generating device to help dissipate heat therefrom, to avoid the above-described adverse effects due to overheating. Heat sinks are often placed and maintained in direct communication with the heat-generating surface of the device to be cooled.
It is well known that the most critical locations that effect the overall performance of these heat transfer assemblies are the interface points. These locations are where two different materials mate to one another introducing two contact surfaces and often an air gap across which the heat being dissipated must be transferred. Generally, the contact surfaces are not always perfectly flat due to milling or manufacturing tolerances thus creating gaps between the heat generating surface and the heat dissipating devices thereby increasing the overall thermal resistance of the assembly. These imperfections and gaps between the mating surfaces often contain small pockets of air and thus reduce the heat transfer potential across the interface between the heat generating surface and the heat-dissipating device.
Various materials have been employed in the prior art in an attempt to bridge this interface gap. In particular, organic base materials such as polysiloxane oils or polysiloxane elastomeric rubbers and thermoplastic materials such as PVC, polypropylene, etc. loaded with thermally conducting ceramics or other fillers such as aluminum nitride, boron nitride or zinc oxide have been used to impart thermally conducting properties to the organic base material. In the case of polysiloxane oils loaded with thermally conducting materials, these materials are applied by smearing the heat sink or other electronic component with the thermally conducting paste and then securing the heat sink in place by mechanical means using clips or screws. The prior art, thermal greases show superior film forming and gap filling characteristics between uneven surfaces thus providing an intimate contact between the surface of the heat sink and the surface of the heat-generating source. However, it has been found that the use of thermal greases exhibit poor adhesions to the surfaces of the heat sink and heat generating surface, thus effectively seeping out from between the heat sink and the heat generating surface, causing air voids to form between the two surfaces, ultimately leading to hot spots. Moreover, excessive pressure placed upon the heat sink by the mechanical fasteners accelerates this seepage from between the heat sink and the surface of the heat-generating surface. It has been reported that excessive squeeze out of polysiloxane oils can evaporate and recondense on sensitive parts of the surrounding microcircuits. The recondensed oils lead to the formation of silicates thereby interfering with the function of the microprocessor and eventually causing failure.
In the case of polysiloxane rubbers and thermoplastic polymers, these materials are typically cast in sheet form and die cut into shapes corresponding to the shape of the heat sink and heat generating device. The resulting preformed sheet is then applied to the surface of the heat-generating surface securing the heat sink by means of clips or screws. The precut films solve the problems associated with greases but do not provide adequate intimate contact required for optimum heat transference between the heat generating source and the heat sink. However, the precut films, often of a phase change material, do not always wet out completely against the surface of the heat dissipation device and the added step of cutting preforms and manually applying the pad adds cost to the assembly process in addition to increasing waste and potential error, as these precut pads tend to be quite fragile. Furthermore, these types of materials show variable performance due to variation in the thickness of the pad and the amount of pressure applied to the thermally conducting precut film, based upon the mechanical device or action used to secure the heat sink.
Therefore, in view of the foregoing, heat transfer assemblies that include integral thermal transfer interfaces for mating the assembly to a heat-generating surface are highly desired. There is also a demand for a heat dissipating assembly for use in an electronic device that is lightweight, has an integral interface surface with gap bridging properties and a reduction in interface material waste when applied to heat dissipation devices having complex geometries.
SUMMARY OF THE INVENTIONThe present invention is generally directed to a method of providing an integral thermal interface on an interface surface of a heat dissipation device, such as a heat sink, thereby eliminating a required assembly step. In accordance with the present invention, the traditional phase change material that in the prior art is applied to a backer film, precut to the shape of the interface surface and subsequently transferred to the desired surface is instead applied directly onto a surface. This process therefore eliminates the additional steps of application of the interface onto a film, die cutting and transferring while also eliminating the waste associated with the die cutting step.
By way of example, the present invention operates as follows, during the manufacturing process of a heat-dissipating device; the phase change material is applied directly onto the interface surface of the heat sink to form an integral interface layer directly on the heat sink. This process includes the steps of providing a heat dissipating device having an interface surface, liquefying the phase change material at a controlled temperature so as to decrease the material viscosity to a flowable form, applying the liquefied phase change material directly onto the mating surface of the heat dissipating device either by directly dispensing the material, screen printing or stencil printing and cooling the material causing it to cure on the surface of the heat dissipating device.
The present invention provides several distinctive advantages over the die-cut sheets of the prior art. First, the material is directly applied to the heat sink at the time of manufacture, eliminating the need for an additional assembly step of removing a die cut sheet and applying the material onto the device, thereby eliminating unnecessary handling of the fragile material and reducing the potential for contamination of the interface material. The need for an adhesive layer to attach the die cut material to the heat sink is also eliminated, as the material is already adhered to the heat sink device. Second, a great deal of waste is reduced in cases where the mating surface of the heat dissipating device is irregular, because only the material necessary to cover the surface is applied to the surface. In contrast, when die cut sheets are used, the overhanging material is trimmed after application and discarded. Finally, a more complete wet out of the part is achieved. Since the material is applied in its molten state, it flows onto the part and fills the voids and manufacturing imperfections on the interface surface more completely, resulting in virtual elimination of any voids or air gaps thereby providing more intimate thermal communication.
The heat sink device is then assembled onto a heat generating electronic device and retained there using any fastening device well known in the art. The present invention therefore provides a lower cost alternative for employing a thermal interface of phase change material while further simplifying assembly by eliminating several steps required in the prior art.
It is therefore an object of the present invention to provide a method of manufacturing a heat dissipation device having an integral phase change thermal interface.
It is also an object of the present invention to provide a method of manufacturing a heat dissipation device having a pre applied phase change thermal interface thereby eliminating the need for applying an interface pad during final installation of the device.
It is a further object of the present invention to provide a method of manufacturing a heat sink assembly with a preapplied thermal interface pad where complete wet out of the interface surface of the heat sink is accomplished at the time of manufacture thereby eliminating any voids or air gaps between the interface pad and the interface surface.
It is yet another object of the present invention to provide a method of manufacturing a heat sink as described above that eliminates the need for a layer of adhesive between the interface pad and the interface surface of the heat sink.
It is a further object of the present invention to provide a method of manufacturing a heat sink having an interface pad on an interface surface there of that eliminates the need for trimming excess material thereby reducing material waste and accommodating complex geometries and a variety of heat sink interface shapes.
Other objects, features and advantages of the invention shall become apparent as the description thereof proceeds when considered in connection with the accompanying illustrative drawings.
BRIEF DESCRIPTION OF THE DRAWINGSThe novel features which are characteristic of the present invention are set forth in the appended claims. However, the invention's preferred embodiments, together with further objects and attendant advantages, will be best understood by reference to the following detailed description taken in connection with the accompanying drawings in which:
Referring now to the drawings, examples of assemblies manufactured in accordance with the method of the present invention are illustrated and generally shown in
The phase change material 12 may be applied to the interface surface 14 of the heat sink 16 either by directly dispensing the material 12, screen-printing or stencil printing. By applying the liquefied phase change material 12 in this manner, the geometric shape and thickness of the material 12 can be carefully controlled. Through stencil and screen printing methods, the interface material 12 can be applied to the contact surfaces 14 of heat sinks 16 having complex geometries with a great deal of repeatability and precision. Further, in contrast to the methods in the prior art, only the precise amount of material 12 required to cover the contact surface 14 is applied, greatly reducing waste and eliminating the trimming step required for the removal of excess material. As can be best seen in
Turning to
Turning now to
The present invention may also include a step whereby adhesive material is incorporated within the molten phase change material 12 before it is applied to the contact surface 14 of the heat sink 16. This provides a thermal interface surface 12 that includes integral adhesive properties, eliminating the need for mechanical fasteners or the addition of an adhesive layer over the thermal interface material 12.
In view of the foregoing, a superior method for manufacturing and applying a phase change thermal interface to a heat dissipating assembly that eliminates the requirement of additional gap pads or thermal interfaces can be realized. The method of the present invention, greatly improves over prior art attempts by integrally providing a heat sink 12 with a thermal interface that is applied at the time of manufacture. This eliminates additional assembly steps and reduces the amount of waste material generated as compared to the processes in the prior art. In particular, the present invention 10 provides a method of manufacturing a heat sink 16 with an integrated thermal interface 12 that is vastly improved over known assemblies and was until now unavailable in the prior art.
While there is shown and described herein certain specific structure embodying the invention, it will be manifest to those skilled in the art that various modifications and rearrangements of the parts may be made without departing from the spirit and scope of the underlying inventive concept and that the same is not limited to the particular forms herein shown and described except insofar as indicated by the scope of the appended claims.
Claims
1. A method of applying a phase change thermal interface comprising:
- providing a thermal heat sink having a contact surface, said contact surface having voids;
- providing a phase change material;
- heating said phase change material to liquefy said material;
- applying said liquefied phase change material to said contact surface, said liquefied phase change material filling said voids and fully wetting out said contact surface; and
- cooling said liquefied phase change material to form a solid thermal interface layer on said contact surface.
2. The method of applying a phase change thermal interface of claim 1, wherein said step of providing a phase change material is providing polysiloxane rubber.
3. The method of applying a phase change thermal interface of claim 1, wherein said step of providing a phase change material is providing thermoplastic polymer.
4. The method of applying a phase change thermal interface of claim 1, wherein said step of applying said liquefied phase change material further includes screen printing said liquefied phase change material.
5. The method of applying a phase change thermal interface of claim 1, wherein said step of applying said liquefied phase change material further includes stencil printing said liquefied phase change material.
6. The method of applying a phase change thermal interface of claim 1, further comprising:
- mixing an adhesive material with said liquefied phase change material, before said step of applying said liquefied phase change material to said contact surface.
7. The method of applying a phase change thermal interface of claim 1, further comprising:
- installing said heat dissipating device onto a heat generating electronic component having a heat generating surface, said applied phase change material being in thermal communication with said heat generating surface, after said step of cooling said applied phase change material.
8. A method of manufacturing a thermal dissipation assembly comprising:
- providing a thermal heat sink having a contact surface, said contact surface having voids;
- providing a phase change material;
- heating said phase change material to liquefy said material;
- filling said voids and fully wetting out said contact surface by applying said liquefied phase change material to said contact surface;
- cooling said liquefied phase change material to form a solid thermal interface layer on said contact surface; and
- installing said heat dissipating device onto a heat generating electronic component having a heat generating surface, said applied phase change material being in thermal communication with said heat generating surface.
Type: Application
Filed: Sep 2, 2004
Publication Date: Feb 10, 2005
Inventor: Kevin McCullough (North Kingstown, RI)
Application Number: 10/932,606