Side sill trim part and method of molding same
Improved side sill or rocker panel trim part and methods of molding same are provided. In the methods, a substantially “C” like cross-sectional shaped mold cavity (53) is provided having a pair of terminal cavity portions (56, 58) therein. A living hinge-forming cavity space (54) is provided between a midpoint of the cavity and one of the terminal end portions. The part comprises a longitudinal axis extending therealong and a pair of leg portions and an intermediate section interconnecting the leg portions. The part includes a substantially “C” shaped cross-section transverse to the longitudinal axis with the intermediate section including a show surface side with the legs extending away from the show surface side. A hinge joint is provided adjacent one of the legs so that the part is bendable at the hinge to form a substantially closed “C” position.
This application claims the benefit of U.S. Provisional Patent Application Ser. No. 60/401,873 filed Aug. 8, 2002.
BACKGROUND OF THE INVENTIONAutomotive trim parts and protective molding are often prepared via injection molding techniques with the manufacture of elongated moldings being greatly aided by gas assisted injection molding techniques. For some applications, it is desirable to form deep drawn molded parts wherein the transverse cross section of the elongated part approximates the letter “C”.
For example, it is desirable to provide deep drawn side sill and rocker panel moldings wherein the exterior, show surface of the part (i.e., the outer part surface between the opposed generally horizontal ends of the “C”) has an increased height dimension measured transverse to the longitudinal axis of the part so that the part will extend closely to the road surface exhibiting minimum ground clearance. This effect is not only popular from an aesthetic perspective, but the low disposition of the part also helps to serve an air damming effect helping to promote aerodynamic stability of the vehicle during driving.
Molding of deep drawn substantially “C” cross sectioned plastic parts is difficult. If the opposing longitudinally disposed edges converge toward each other, it is difficult to remove the part from the mold in the absence of elaborate sliding mechanisms.
SUMMARY OF THE INVENTIONA method of making a side sill or rocker panel part of the type having a substantially “C” like cross-sectional shape is disclosed. This “C” like shape is oriented transverse to a longitudinal axis of the part. A mold cavity is provided and defines a space congruent with the desired cross-sectional shape. The mold cavity space has opposing terminal portions with each terminal portion disposed adjacent to the mold part line. An approximate midpoint of the space located between the terminal portions is determined, and a living hinge forming cavity space is provided between that midpoint and one of the terminal end portions.
Molten resin is injected into the cavity over the hinge-forming cavity space and into the terminal portion. The resin is allowed to harden, and the part is then ejected from the mold cavity to form a substantially “C” cross section part with a hinged attachment leg formed adjacent one terminal portion of the part. The hinged attachment leg may be pivoted so that the part forms a substantially closed “C” position. The pivoted attachment leg can then be used as a situs for securing the part to the automotive frame member.
The part itself has a longitudinal axis extending therealong and comprises a pair of leg portions and an intermediate section interconnecting the leg portions so that the part has a substantial “C” shaped cross-sectional configuration when viewed transverse to the longitudinal axis. The intermediate section of the part includes a show surface side with the legs extending away from the show surface side. A hinge joint is provided adjacent one of the legs, and the part is bendable at the hinge to form a substantially closed “C” position.
Other objects and advantages of the invention will be apparent from the following description, the accompanying drawings and the appended claims.
BRIEF DESCRIPTION OF THE DRAWINGS
Turning first to
Referring now to
Turning now to
Turning now to
As is apparent, the terminal portions 56, 58 of the cavity, upon completion of the molding cycle, correspond to and will form the opposing longitudinally extending edges of the finished part.
In accordance with the invention, a method of molding a side sill or rocker panel is provided in which the side sill will have, in transverse cross section, a substantial “C” configuration oriented transverse to the longitudinal axis passing through the part. In the molding method, the mold cavity 53 defines a space that is congruent with the intended cross-sectional shape of the part.
As can be seen in
Turning to
With regard to the molten resins that may be utilized to form the side sill, a host of thermoplastic polymers may be mentioned. These include injection moldable thermoplastic resins such as acrylonitrile-butadiene-styrene, acetals, acrylics, phenolic, polyamides, polycarbonates, copolyesters, polyethylene, polypropylene, polystyrene, polyurethane, polyvinyl chloride, styrene/acrylonitrile blends, acrylonitrile-butadiene styrene/polycarbonate blends, acrylonitrile-butadiene-styrene/thermoplastic polyurethane blends, polybutylene terephthalate/polycarbonate alloys, olefins, thermoplastic poiyolefins, thermoplastic polyesters, vinyls, polybutylene terephthalates, glass filled polybutylene terephthalates, polyphenylene oxides, blends and alloys of polycarbonate and polybutylene terephthalate, polyphenylene esters, blends of polyamides and polyphenylene esters and oxides, and blends of polyolefin and rubber and/or ethylene-propylene-diene monomer. At present, polypropylene is preferred.
As above indicated, the show side surface of the part can be desirably covered with a thin paint film. This is accomplished via conventional co-molding techniques wherein the film is first supplied to the mold cavity followed by injection of a molten polymer. The polymer fuses along one side of the film member with the outer show side of the film then presented along the finished surface of the part.
The paint film laminate used in these co-molding or insert molding techniques may comprise a backing sheet of about 0.020″ in thickness to which paint layers are adhered to form a colored side of the laminate. Typically, the backing sheet comprises an extruded thermoplastic sheet.
In such paint film laminates, a paint film, comprising a cast dried continuous paint coating, is provided over the backing sheet. The paint film may consist of a monocoat, a clear coat over a base coat or a clear coat and a base coat with interposed print or design. The paint film, including base coat, clear coat and print or design, if desired, may range from about 0.5-4mil. in thickness.
The laminated paint films are commercially available. The films are typically provided in a roll, unwound, then trimmed to a proper “preform” size and shape, ready for insertion into the injection mold. The preform is usually placed along the cavity side of the mold with the painted side thereof facing the mold cavity surface. In some instances, the preform may be placed along the core side of the mold. The mold is then clamped, and the desired molten resin is injected into the mold cavity. Heat and pressure conditions in the mold partially melt the backing sheet, and a melt bonding or fusion of the injected resin and film occur. Injection molds used for these processes are rear or edge gated so that the molten resin is directed along the backside of the film.
Techniques for preforming paint film laminates and insert or co-molding of the laminate and substrate are disclosed, for example, in U.S. Pat. No. 5,599,608 (Yamamoto et al.); U.S. Pat. No. 5,746,962 (Yamamoto); U.S. Pat. No. 5,759,477 (Yamamoto); U.S. Pat. No. 5,783,287 (Yamamoto et al.); U.S. Pat. No. 5,968,444 (Yamamoto); U.S. Pat. No. 6,168,742 (Yamamoto); and U.S. Pat. No. 6,227,319 (Hardgrove et al.). The disclosures of these patents are incorporated by reference herein.
While the methods and trim part herein described constitute preferred embodiments of this invention, it is to be understood that the invention is not limited to these specifically disclosed embodiments and that changes may be made without departing from the scope of the invention, which is defined in the appended claims.
Claims
1. Method of making a side sill or rocker panel part of the type having a substantially “C” like cross-sectional shape oriented transverse to a longitudinal axis of the part, comprising, providing a mold cavity defining a space congruent with said cross-sectional shape and having a opposing terminal portions of said space with each terminal portion being disposed adjacent a mold part line, determining an approximate midpoint of the space located between said terminal portions, and providing a living hinge forming cavity space between said midpoint and one of said terminal portions, injecting a mass of molten resin into said cavity over said hinge forming cavity space and into said terminal portions, allowing said molten resin to harden, ejecting said resin from said mold cavity thereby forming a substantially “C” cross-sectional part with a hinged attachment leg formed adjacent one terminal portion of said part.
2. Method as recited in claim 1 further comprising co-molding a paint film over said part.
3. Method as recited in claim 2 wherein said paint film is inserted into said cavity prior to injection of said mass of molten resin into said cavity.
4. Method as recited in claim 1 further comprising positioning said part adjacent an automotive frame member, pivotally moving said attachment leg toward said frame member and securing said attachment leg member to said frame member.
5. Method of making a side sill or rocker panel automotive part having a longitudinal axis extending therealong, said part including a “C” configuration when viewed in a cross-sectional plane taken transverse to said longitudinal axis and having spaced top and bottom legs and an intermediate portion connecting said top and bottom legs and having an inside surface and a show side surface with both of said legs extending away from said inside surface, said method comprising providing a mold cavity defining a space congruent with said configuration and having opposing terminal portions of said space, said terminal portions of said space being disposed relative to each other at an angle of less than 180°, providing a living hinge-forming space in said space proximate to one of said opposing terminal portions, injecting a mass of molten resin into said cavity substantially filling said space and flowing over said hinge-forming space, allowing said molten resin to harden, ejecting said resin from said cavity thereby forming a side sill or rocker panel with one of said legs defining a hinged attachment leg formed along one end of said part and adapted for pivotal movement so that said legs can be disposed relative to each other in a substantially closed “C” position.
6. Method as recited in claim 5 wherein said legs can be disposed relative to each other at an angle of between about 180°-270°.
7. Method as recited in claim 6 wherein said end portions of said legs can be disposed relative to each other at an angle of between about 225° and 270°.
8. Side sill or rocker panel automotive part having a longitudinal axis extending therealong, said part comprising a pair of leg portions and an intermediate section interconnecting said leg portions, said part having a substantial “C” shaped cross section transverse to said longitudinal axis, said intermediate section including a show surface side with said legs extending away from said show surface side, a hinged joint provided adjacent one of said legs, said part being bendable at said hinge to form a substantially closed “C” position.
9. Automotive part as recited in claim 8 wherein said legs are disposed relative to each other at an angle of between about 180° and 270°.
10. Automotive part as recited in claim 9 wherein said legs are disposed relative to each other at an angle of between about 225° to about 270°.
11. Side sill automotive part as recited in claim 8 further including a paint film laminate covering said show surface.
Type: Application
Filed: Aug 1, 2003
Publication Date: Jul 13, 2006
Inventor: Renji Maki (Brookville, OH)
Application Number: 10/524,167
International Classification: B29C 45/14 (20060101); B32B 3/04 (20060101);