MERCURY REMOVAL SORBENT
A composition comprising a vanadium oxide compound and an alkali metal promoter loaded onto a porous support material is disclosed. Methods of making and using the composition to remove heavy metals or heavy metal containing compounds from a fluid stream are also provided. Such methods are particularly useful in the removal of mercury and mercury compounds from flue gas streams produced from the combustion of hydrocarbon-containing materials such as coal and petroleum fuels.
The invention relates to a composition and method for removing heavy metal contaminates from fluid streams. In one aspect, the invention relates to a method of preparing such composition. In yet another aspect, the invention relates to a process for removing heavy metal contaminates, such as mercury and mercury compounds, from flue gas streams produced from the combustion of hydrocarbon-containing materials.
BACKGROUND OF THE INVENTIONHeavy metals are released during the combustion process of many fossil fuels and/or waste materials. These heavy metals include, for example, arsenic, beryllium, lead, cadmium, chromium, nickel, zinc, mercury, and barium. Most of these heavy metals are toxic to humans and animals. In particular, elemental mercury and mercury compounds such as mercury chlorides are thought to compromise the health and mental acuity of young children and fetuses.
Furthermore, there is every indication that the amount of mercury, and possibly of other heavy metals, now legally allowed to be released by those combusting various fossil fuels and/or waste materials, including coal burning power plants and petroleum refineries, will be reduced by future legislation. While a variety of adsorbents are available for capture of heavy metals (in particular mercury), these adsorbents tend to have low capacities and are easily deactivated by other components in the gas stream, such as sulfur oxides. Thus, there exists a need for a material that removes elemental mercury from gas streams and has a high capacity for retaining mercury as a nonvolatile compound.
SUMMARY OF THE INVENTIONIt is an object of the present invention to provide an improved vanadium material with a high capacity for sorbing heavy metals and heavy metal compounds.
A further object of this invention is to provide a method for making an improved vanadium material by incorporating a vanadium oxide compound and an alkali metal hydroxide promoter with a porous support material.
Another object of this invention is to provide a process for removing heavy metals or heavy metal compounds from a fluid stream by contacting the fluid stream with an improved vanadium material.
Yet another object of this invention is to provide an improved vanadium material which when used in the removal of heavy metals results in the oxidation of the heavy metal to an oxidation state greater than zero.
It should be understood that the above-listed objects are only exemplary, and not all the objects listed above need be accomplished by the invention described and claimed herein.
In accordance with a first embodiment of the invention, the inventive composition comprises a porous support material including a vanadium oxide compound and an alkali metal vanadate incorporated thereon, therein, or thereon and therein.
In accordance with a second embodiment of the invention, the inventive composition comprises a porous support material impregnated with a vanadium oxide compound and an alkali metal promoter selected from the group consisting of lithium hydroxide, lithium vanadate, and mixtures thereof.
In accordance with a third embodiment of the invention, the inventive composition can be prepared by the method of: (a) mixing a vanadium oxide compound and an alkali metal hydroxide promoter with at least one porous support material.
In accordance with a fourth embodiment of the invention, the inventive composition can be used in the removal of at least one heavy metal or heavy metal containing compound from a fluid stream by (a) contacting the fluid stream with a porous support material having incorporated onto, into, or onto and into a vanadium oxide compound and an alkali metal promoter for sorption of at least a portion of the at least one heavy metal or heavy metal containing compound.
In accordance with a fifth embodiment of the invention, the inventive composition can be used in the removal of at least one heavy metal or heavy metal containing compound from a flue gas stream produced by the combustion of a hydrocarbon-containing fuel by: (a) contacting the flue gas stream with a first sorbent material comprising a porous support having incorporated onto, into, or onto and into a vanadium oxide compound and an alkali metal promoter for sorbing at least a portion of the at least one heavy metal or heavy metal containing compound present in the flue gas stream; and (b) contacting the flue gas with a second sorbent material different from the first sorbent material for sorbing at least a portion of the at least one heavy metal-containing compound not sorbed during step (a).
Other objects and advantages of the invention will become apparent from the detailed description and the appended claims.
A preferred embodiment of the present invention is described in detail below with reference to the attached figures, wherein:
Compositions according to the present invention generally comprise a porous support material with a vanadium oxide compound and an alkali metal promoter incorporated thereon, therein, or thereon and therein. Preferably, the vanadium oxide compound comprises V2O5, a hydrate of V2O5, a peroxo complex of vanadium oxide or combinations thereof. However, it is within the scope of the invention for the vanadium component to have any oxidation state greater than zero.
An alkali metal promoter is employed to increase the effectiveness of the vanadium oxide in sorbing heavy metals. Preferably, the alkali metal promoter is an alkali metal hydroxide such as lithium hydroxide. As discussed below, during formation of the inventive compositions, it is possible for at least a portion of the alkali metal hydroxide promoter to react with at least a portion of the vanadium oxide compound to form an alkali metal vanadate such as lithium vanadate. Hydrates of alkali metal hydroxides can also be used such as lithium hydroxide monohydrate. However, it is within the scope of the present invention for the promoter to be an elemental alkali metal, an alkali metal compound, or an ionic alkali metal species. Unless otherwise specified, the term “promoter” refers to any such alkali metal composition whether it was originally added to the inventive sorbent or whether it was formed in situ.
The vanadium oxide compound and promoter are loaded onto a porous support material. Preferably, the support material is selected from the group consisting of amorphous silica-alumina, a zeolite, a material comprising meta-kaolin, alumina, expanded perlite, and combinations thereof. It is most preferable to employ a silica-alumina support material such as meta-kaolin in conjunction with expanded perlite, however, it is possible that the support may comprise pure alumina or calcined alumina.
The porous support material generally comprises at least about 50% by weight of the total composition, preferably between about 50-99% by weight, more preferably between about 75-95% by weight, and most preferably between about 80-90% by weight. In order to maximize the sorptive capacity of the composition, the support material preferably has a surface area of at least about 75 m2/g, more preferably at least about 100 m2/g, and most preferably at least about 150 m2/g.
The overall composition preferably comprises from about 0.5-40% by weight vanadium. Unless otherwise specified, the phrase “by weight vanadium” is defined as the elemental weight of vanadium present in the composition. More preferably, the composition comprises from about 1-35% by weight vanadium, and most preferably from about 2-25% by weight.
The composition preferably comprises from about 0.5-50% by weight of the alkali metal promoter, more preferably from about 1-30% by weight, and most preferably from about 5-25% by weight. The weight ratio of vanadium oxide to promoter is preferably within the range of about 10:1 to 1:10, more preferably between about 5:1 to 1:5, and most preferably between about 4:1 to 1:1.
The sorbent material is formed by mixing a vanadium oxide compound and an alkali metal promoter with at least one porous support. The vanadium oxide compound and promoter should be intimately contacted with the support so that the vanadium oxide compound and promoter become incorporated onto, into, or onto and into the support.
One avenue for accomplishing this intimate mixing is to dispense the vanadium oxide and promoter in a first solution. Water is a preferred solvent for forming this solution, however, any solvent capable of dissolving both the vanadium oxide and promoter may be used. When dispersed in an aqueous solution, the vanadium oxide comprises from about 0.5-70% by weight of the solution, more preferably between about 5-60% by weight, and most preferably from about 10-50% by weight. Similarly, when dispersed in an aqueous solution, the promoter comprises from about 0.05-50% by weight of the solution, more preferably from about 0.5-40% by weight, and most preferably from about 1-30% by weight. At the same time, the porous support is dispersed in a second solution, with water being a preferred solvent.
If an alkali metal hydroxide is selected as the promoter that is mixed with the vanadium oxide compound, generally, at least a portion of the alkali metal hydroxide reacts with at least a portion of the vanadium oxide compound to form an alkali metal vanadate, also referred to herein as a “promoter.”
The first and second solutions are then mixed together thereby loading the vanadium oxide and promoter onto, into, or onto and into the support. The mixture is then dried, and preferably, the resulting sorbent material is in a granular or powder form. It is possible that the porous support used is not in a finely divided form prior to mixing with the vanadium oxide and promoter solution. If such is the case, it is preferable to crush and sieve the dried sorbent material to an acceptable particle size for a given application. The sorbant material may also be pelletized, formed into monoliths, or incorporated into a foam in order to render it suitable for a specific application.
The inventive sorbent material is particularly useful in the removal of heavy metals and heavy metal containing compounds from fluid streams, especially flue gas streams produced by the combustion of hydrocarbon-containing materials such as coal and petroleum fuels. As noted above, such fluid streams are often contaminated with at least one heavy metal or compound containing a heavy metal selected from the group consisting of arsenic, beryllium, lead, cadmium, chromium, nickel, zinc, mercury, and barium. In one aspect, methods of removing heavy metal and heavy metal containing compounds from fluid streams comprise providing a sorbent composition according to the present invention and contacting the stream with the inventive sorbent.
Flue gas, such as that created by the combustion of hydrocarbon-containing compounds, generally comprises at least about 10% by weight N2, more preferably at least about 50% by weight, and most preferably between about 75-90% by weight. Flue gas also generally comprises less than about 10% by weight of uncombusted hydrocarbons, more preferably less than about 5% by weight, and most preferably less than about 1% by weight. As described below, in a particularly preferred application, the flue gas will have already been treated for removal of NOx and SOx prior to any heavy metal removal process as the presence of high levels of NOx and SOx compounds may lead to fouling of the heavy metal removal sorbents. Generally, the flue gas comprises less than about 800 ppm of SOx compounds such as SO2, more preferably less than about 500 ppm, and most preferably less than about 400 ppm. Also, the flue gas preferably comprises less than about 400 ppm NOx such as NO and NO2, more preferably less than about 250 ppm, and most preferably less than about 150 ppm. Flue gas may also comprise between about 2.5-10% by weight O2, between about 1-5% by weight CO2, and between about 5-20% by weight H2O.
Preferably, the pressure drop associated with the contacting step should not exceed more than about 20 psia. More preferably, the pressure drop in the fluid stream is less than about 10 psia, and most preferably less than about 5 psia. Typically, flue gas streams do not flow under high pressures. Therefore, if the pressure drop is too great, back pressure is created and can affect the combustion process by which the flue gas is created. The arrangement of the sorbent material in the vessel in which contacting occurs can assist in minimizing this pressure drop. Preferably, the sorbent material comprises finely divided particles that are suspended in the fluid stream during the contacting step. Alternatively, the sorbent material may be positioned in a fluidized bed, placed in a packed bed column, formed into monoliths, or incorporated into a foam. With the latter arrangements, pressure drop may become much more of a concern and may require the use of fans or other equipment to increase the pressure of the flue gas stream.
The fluid stream containing the heavy metal contaminant preferably has a temperature of between about 50-400° F. during the contacting step, more preferably between about 100-375° F., and most preferably between about 200-350° F. The temperature of the fluid stream at the contacting stage is in part affected by upstream processes such as particulate removal systems (i.e., cyclones), other contaminant removal systems, heat exchange systems, etc. The contacting step results in the sorption of at least about 80% by weight of the heavy metals contained in the fluid stream, more preferably at least about 90% by weight, even more preferably at least about 95% by weight, and most preferably at least about 98% by weight. As previously stated, the vanadium oxide incorporated support material exhibits a high capacity for sorbing heavy metals and heavy metal containing compounds. Preferably, the vanadium oxide material is capable of sorbing at least about 1 atom of a heavy metal per every 5 atoms of vanadium. More preferably, the ratio of heavy metal atoms sorbed to vanadium atoms is at least about 1:3, and most preferably 1:1.
The sorbent material also exhibits the ability to oxidize the elemental heavy metal into a heavy metal containing compound such as a heavy metal oxide or chloride. Using mercury as an example, the sorbent material oxidizes mercury into various oxidized species such as Hg+1, Hg+2, or mercury compounds such as HgO, HgCl, and HgCl2. At times, due to system inefficiencies or sorbent saturation, some of these heavy metal containing compounds may desorb or break free from the sorbent material. In that case, it can be particularly useful to employ a downstream heavy metal compound removal system in conjunction with the above-described sorbent system. In the heavy metal compound removal system, the gaseous product stream is contacted with a separate adsorbent in an adsorption zone. The adsorbent can be any adsorbent capable of adsorbing a heavy metal; however, preferred materials for removing the heavy metal compounds include those having a hydrophobic surface with pore openings of less than about 10 Å, and high pore volumes. More preferably, the adsorbent comprises, consists of or consists essentially of a material selected from the group consisting of a zeolite, amorphous carbon and combinations thereof. The amorphous carbon can be an activated carbon and/or activated charcoal. Exemplary zeolites include those with 8-12 member ring openings, and particularly ZSM-5 zeolite. Furthermore, the material may be in the form of granules, pellets, monoliths, powders that are collected on filters, or combinations thereof. A treated gaseous product stream is withdrawn from the adsorption zone and contains less than about 20 weight %, preferably less than about 10 weight %, and more preferably less that about 5 weight % of the heavy metal in the gaseous feed stream.
The heavy metal compound removal system may be contained in a separate downstream vessel from the vanadium oxide sorbent, or can be situated along with the vanadium oxide sorbent in a multiple stage contacting vessel so that the flue gas first contacts the vanadium oxide sorbent followed by the heavy metal compound removal sorbent.
While the vanadium oxide sorbent material exhibits a relatively high capacity for sorbing heavy metals and heavy metal containing compounds, its cost is relatively higher than the cost for conventional heavy metal compound sorbent materials such as zeolite. Therefore, from an economic standpoint, it may be desirable to employ a relatively small amount of the vanadium oxide sorbent compared to the conventional sorbent material. Once the sorptive capacity of the vanadium oxide sorbent has sufficiently diminished, it will not be able to sorb sufficient quantities of the heavy metal containing compounds formed by the catalytic action of the vanadium oxide sorbent. These heavy metal containing compounds may then be sorbed by the lesser expensive heavy metal compound sorbent material located downstream from the vanadium oxide sorbent.
The heavy metal compound removal system preferably results in the sorption of at least about 80% by weight of the heavy metal containing compounds that break through the vanadium oxide sorbent material, more preferably at least about 90% by weight, and most preferably at least about 95% by weight.
In addition to the vanadium oxide sorbent material becoming saturated, the overall sorptive efficiency may be affected by the presence of NOx and SOx compounds present in the flue gas. For example, SO2 contained in the flue gas stream may be oxidized to SO3 and then converted to H2SO4 in the presence of water. The H2SO4 then may fill the pores of the vanadium oxide sorbent thereby decreasing the sorptive capacity thereof and blocking active catalyst sites. Therefore, it is preferable to employ an upstream NOx and SOx removal process in order to avoid fouling of the vanadium oxide sorbent material. Any conventional NOx and SOx removal process would be suitable for use with the present invention. The NOx and SOx removal process should preferably remove at least about 50% by weight of all NOx and SOx present in the flue gas stream. It is preferable for the flue gas stream immediately prior to contact with the vanadium oxide sorbent to comprise less than about 400 ppm NOx, more preferably less than about 250 ppm, and most preferably less than about 150 ppm. Likewise, it is preferable for the flue gas stream immediately prior to contact with the vanadium oxide sorbent to comprise less than about 800 ppm SOx, more preferably less than about 500 ppm, and most preferably less than about 400 ppm.
The heavy metal compound removal system is capable of performing effectively even at high flue gas flow rates (i.e., greater than 10,000 gas hourly space velocity). The sorbent material used in the heavy metal compound removal system may be placed in a fluidized or packed bed vessel, however, as with the vanadium oxide sorbent material system above, the pressure drop of the flue gas stream should be minimized to avoid requiring the use of additional equipment to compensate for the pressure drop.
EXAMPLEThe following example illustrates preferred sorbent materials and methods of making the same in accordance with the present invention. This example should not be taken as limiting the scope of the present invention in any way.
In this example, a sorbent material according to the present invention was prepared by forming a solution comprising 17.816 g of LiOH•H2O and 77.229 g of V2O5 dissolved in 60 g of deionized water. A separate dispersion was prepared containing 60 g of deionized water, 30 g of alumina (DISPAL), 60 g of expanded perlite, and 20 g of calcined Kaolin or more generally calcined clay, or more specifically meta Kaolin. The solution and dispersion were mixed together forming a thick, paste-like material. This material was extruded through a ⅛ inch die and dried overnight at 248° F. The next day, the extrudate was crushed so as to form a granular material that could be passed through a 20-40 mesh sieve.
The material was then tested for efficacy in removing elemental mercury entrained in an air stream at a concentration of approximately 1000 μg/m3 (ppb w/v). Approximately 0.97 g of the sorbent was placed in a fixed bed reactor, the temperature of which was held constant at 300° F. The air flow rate through the fixed bed reactor was fixed at a gas hourly space velocity of >10,000 (approximately 200 mL/min). The air stream entering and exiting the fixed bed reactor was periodically analyzed using a Jerome Mercury Analyzer.
Claims
1-19. (canceled)
20. A method for forming a sorbent material comprising:
- (a) mixing a vanadium oxide compound and an alkali metal hydroxide promoter with at least one porous support material.
21. A method in accordance with claim 20 wherein said method further comprises:
- (b) dispersing said vanadium oxide and said promoter in a first aqueous solution prior to step (a).
22. A method in accordance with claim 21 wherein said first aqueous solution comprises from about 0.5-70% by weight of said vanadium oxide compound and from about 0.05-50% by weight of said promoter.
23. A method in accordance with claim 21 wherein said method further comprises:
- (c) dispersing said porous support components in a second aqueous solution prior to step (a).
24. A method in accordance with claim 20 wherein said promoter is lithium hydroxide.
25. A method in accordance with claim 20 wherein said at least one porous support material is selected from the group consisting of amorphous silica-alumina, a zeolite, a material comprising meta-kaolin, alumina, expanded perlite, and combinations thereof.
26. A method in accordance with claim 20 wherein at least a portion of said alkali metal hydroxide promoter reacts with at least a portion of said vanadium oxide compound to form an alkali metal vanadate.
27-55. (canceled)
Type: Application
Filed: Jul 17, 2008
Publication Date: Nov 6, 2008
Inventors: Joseph B. Cross (Bartlesville, OK), Glenn W. Dodwell (Bartlesville, OK), Marvin M. Johnson (Bartlesville, OK), Edward L. Sughrue (Bartlesville, OK), Jianhua Yao (Bartlesville, OK)
Application Number: 12/175,257
International Classification: B01J 20/284 (20060101); B01J 20/00 (20060101); B01J 20/04 (20060101); B01J 20/10 (20060101); B01J 20/12 (20060101); B01J 20/16 (20060101); B01J 20/283 (20060101);