DECARBONIZATION PROCESS FOR CARBOTHERMICALLY PRODUCED ALUMINUM

Abstract

A method of recovering aluminum is provided. An alloy melt having Al4C3 and aluminum is provided. This mixture is cooled and then a sufficient amount of a finely dispersed gas is added to the alloy melt at a temperature of about 700° C. to about 900° C. The aluminum recovered is a decarbonized carbothermically produced aluminum where the step of adding a sufficient amount of the finely dispersed gas effects separation of the aluminum from the Al4C3 precipitates by flotation, resulting in two phases with the Al4C3 precipitates being the upper layer and the decarbonized aluminum being the lower layer. The aluminum is then recovered from the Al4C3 precipitates through decanting.

Description

BACKGROUND OF THE INVENTION

The present invention relates to a method of recovering commercial grade aluminum from carbothermically produced Al—C alloy. More particularly, the invention relates to a method for separating and recovering the aluminum from the alloy that contains aluminum and aluminum carbide (A4C₃) particles, that is, decarbonizing the aluminum.

Generally, the overall reaction of direct carbothermic reduction of alumina to produce aluminum is Al₂O₃+3C=2Al+3CO. The carbothermic reduction of alumina may take place in several steps: (1) 2Al₂O₃+9C=Al₄C₃+6CO and (2) Al₄Cl₃+Al₂O₃=6Al+3CO.

The present invention relates to the decarbonization process after the carbothermic reduction of alumina to produce aluminum.

SUMMARY OF THE INVENTION

In one embodiment, the present invention provides a method of recovering commercial grade aluminum. In another embodiment, a method of recovering aluminum from an alloy melt that comprises Al₄C₃ precipitates and aluminum, by cooling the alloy melt; then adding a sufficient amount of a finely dispersed gas to the alloy melt at a temperature of about 700° C. to about 900° C. to separate the aluminum from the Al₄C₃ precipitates. The aluminum recovered is a decarbonized carbothermically produced aluminum where the step of adding a sufficient amount of the finely dispersed gas effects flotation of the Al₄C₃ precipitates.

In one embodiment, the final step of separating the aluminum from the Al₄C₃ precipitates is by decanting, sub-surface or vacuum tapping the decarbonized aluminum to a receiver.

In a further embodiment, the finely dispersed gas used is an inert gas. In another embodiment, the inert gas used is either argon or carbon dioxide.

In yet another embodiment, the finely dispersed gas used is a mixed gas. In another embodiment, the mixed gas is a mixture of inert gas with a reactive gas. In a further embodiment, the inert gas used is argon and the reactive gas is chlorine.

In a further embodiment, the gas is introduced to the alloy melt by a rotating disperser, a bubbler tube, or a porous diffuser.

In yet another embodiment, the gas is introduced to the alloy melt when the alloy melt is at a temperature of about 700° C. to about 900° C.

Accordingly, it is one embodiment of the invention to provide a method of producing aluminum with a very low carbon content.

It is another embodiment of the invention to provide a method of recovering decarbonized carbothermically produced aluminum as claimed herein.

These and other further embodiments of the invention will become more apparent through the following description and drawing.

BRIEF DESCRIPTION OF THE DRAWINGS

For a fuller understanding of the invention, reference is made to the following description taken in connection with the accompanying drawing(s), in which:

FIG. 1 is a flow chart showing one embodiment of the method of producing aluminum in accordance with the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The followings are the definitions of the terms used in this application. As used herein, the term “alloy melt” means a melt of at least an aluminum alloy and Al₄C₃ particles. Note that the alloy melt may include or contain other materials such as Al₂O₃, C, oxycarbides, etc.

As used herein, the term “sufficient amount” means an amount that facilitates the separation of aluminum and aluminum carbide in order to recover greater than 90 weight % of the available aluminum.

The present invention provides a method of decarbonizing aluminum.

In one embodiment, the present invention discloses a method of recovering aluminum from a carbothermically produced alloy melt that comprises aluminum carbide, such as Al₄C₃ and aluminum. The alloy melt is cooled and a sufficient amount of a finely dispersed gas is added to the alloy melt at a temperature of about 700° C. to about 900° C., separating the aluminum from the Al₄C₃ precipitates.

In one embodiment, FIG. 1 shows a flow chart outlining the principal steps of the present invention. Here, an alloy melt is provided in the first step 10. In the second step 20, the alloy melt is cooled. In the third step 30, a finely dispersed gas is added to the alloy melt to assist in transporting the solid precipitates away from the aluminum, forming two phases with the solids being the upper layer. The aluminum is then removed and recovered in the fourth step 40 by means of decanting or tapping.

In the initial step, an alloy melt is provided. In one embodiment, the alloy melt is tapped into a crucible or ladle at very high temperature with the carbon in solution in the form of Al₄C₃. In one embodiment, the temperature of the alloy melt is at least about 2,000° C.

In the second step, alloy melt is cooled. As the alloy melt cools, the Al₄C₃ solidifies and precipitates. In one embodiment, the alloy melt is cooled to a temperature of about 700° C. to about 900° C. In one embodiment, the alloy mixture is cooled by the addition of solid and/or liquid aluminum. In one embodiment, the cooling aluminum is solid and/or liquid scrap of acceptable composition.

In the third step, a finely dispersed gas is added to the alloy melt. In one embodiment, the gas is distributed through the alloy melt by a bubbler tube or a rotating disperser or a porous diffuser at a temperature of about 700° C. to about 900° C. In another embodiment, the action of the gas provides a flotation effect in transporting the solid particles away from the aluminum, with the solid particles rising to the surface. In one embodiment, the rotating disperser is a straight bladed turbine with multiple blades and with an overall diameter of 40 to 60 % of the treatment crucible or ladle. In another embodiment, the disperser is rotated at 100 to 250 revolutions per minute. In another embodiment, the flotation gas is injected through a rotary seal down the hollow shaft of the disperser, exiting underneath the bottom surface of the turbine.

Suitable types of gases that may be used in the present invention include, but are not limited to, inert gases, such as argon, carbon dioxide or nitrogen or a mixture of inert gases with a reactive gas, such as Cl₂. In one embodiment, argon is mixed with about 2 to about 10 volume % of Cl₂. In one embodiment, argon is mixed with 5 volume % of Cl₂ gas. In one embodiment of the invention, an effective flow rate of gas needed to separate aluminum from the Al₄C₃ precipitates is about 5 cm³ /min per cm² of crucible cross sectional area. In one embodiment, the gas dispersion time is about 20 to 30 minutes. In another embodiment, the amount of gas changes depending on the amount of alloy melt quantity.

In the fourth step, decarbonized aluminum is then recovered from the treatment crucible or ladle. In one embodiment, the aluminum is decanted to a receiver, such as a mold.

Optionally, the solids that remain in the treatment vessel are then removed and stored for future recycle to the carbothermic furnace.

Table 1 below shows the amount of aluminum recovery for five examples in which the aluminum recoveries range from 62% to 96%. The aluminum product contained less that 600 ppm of carbon. The gas composition used in Table 1 is 95% argon and 5% Cl₂ by volume.

	TABLE 1
			Ex-
	Example 1	Example 2	ample 3	Example 4	Example 5
Initial charge,	1.0-1.5	10-16	50.9	50.9	50.9
kgs.
Initial carbon,	1.3-3.2	1.1-4.2
weight %
Melt	750	750-800	774	774	774
temperature,
° C.
Aluminum	96	95	92.6	90.6	62.0
product	by rotor	by rotor	by rotor	by rotor	by rotor
recovered,
weight %
Carbon	less	less	11.6	26.3	22.0
content in the	than 100	than 600
aluminum
product
recovered,
ppm

EXAMPLE 1

In Example 1, the melts were approximately 1 kg in weight. The aluminum carbon alloy compositions contained about 1.3 to about 3.2% of carbon. The compositions were cooled and then gas mixtures of 95% argon and 5% Cl₂ were fmely dispersed into the alloy compositions by a rotor at a temperature of 750° C. Here, the aluminum recovery was 96% or higher and the aluminum product contained less than 100 ppm of carbon and less than 100 ppm of chlorides.

EXAMPLE 2

In Example 2, the melts were approximately 10-16 kg in weight. The aluminum carbon alloy compositions contained about 1.1 to about 4.2% of carbon. The compositions were cooled and then gas mixtures of 95% argon and 5% Cl₂ were finely dispersed into the alloy compositions by a rotor at temperatures of 750-800° C. Here, the aluminum recoveries were 95% or higher and the aluminum product contained less than 600 ppm of carbon.

It should be noted that the aluminum recovery is a function of the initial carbon content of the alloy melt. Recovery decreases as carbon content increases. Based on experimental results, recovery decreases by about 4 to 5% for every one % carbon content increase.

EXAMPLE 3

In Example 3, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum contained in a 15.5 inch dia.×23.25 inch deep clay-graphite crucible at 774° C. The carbothermic alloy was mechanically submerged using steel tools. A graphite rotor having a 6″ diameter rotor with 9 teeth evenly spread around the circumference was immersed into the molten mixture. This rotor was attached to a 3 inch diameter graphite tube. A gas mixture of Ar-5% Cl₂ was supplied through the shaft and dispersed into the molten mixture by rotating the shaft/rotor assembly at 350 rpm. During a 30 minute treatment time with this gas mixture, solid materials on the surface of the molten alloy mixture were continually pushed below the surface by mechanical tamping. After the treatment was completed, the rotor was removed from the metal and the thick dross layer that collected on the surface was removed. It should be noted that this dross contained Al₄C₃ particles, aluminum oxide, aluminum oxycarbides and some entrained aluminum metal. The resulting product metal was then manually removed from the crucible with a steel ladle. A total of 77.3 kg of metal was removed from this operation. The dross that was removed was subsequently processed in a separate step by immersing it into a molten salt bath (50% NaCl-50% KCl) to recover the residual metal in the dross. A total of 2.1 kg of metal was removed from the dross during this step. The overall metal recovery for the fluxing operation was calculated to be [(77.3−50.9)/(77.3−50.9+2.1)]*100=92.6%. The carbon content of the aluminum removed from the process was analyzed to be 11.6 ppm.

EXAMPLE 4

In Example 4, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum at 774° C. The molten mixture was treated using the same method as Example 3, except the treatment gas was pure argon. No chlorine was used in this example. A total of 74.0 kg of aluminum was removed from the process. An additional 2.4 kg of aluminum was recovered from the dross, giving an overall metal recovery of 90.6%. The carbon content of the aluminum recovered from the process was 26.3 ppm.

EXAMPLE 5

In Example 5, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum at 774° C. The molten mixture was treated using the same method as Example 4, except the materials floating on the surface were not mechanically submerged by tamping throughout the process. There was no tamping conducted during this example. A total of 64.0 kg of aluminum was removed from this process. An additional 8.0 kg of aluminum was removed from the dross, giving an overall metal recovery of 62.0%. The carbon content of the aluminum removed from this process was 22.0 ppm.

Examples 3, 4 and 5 show that the impure carbothermic alloy containing approximately 3.5% carbon can be purified using the fluxing method to produce a commercially acceptable alloy with a carbon content of less than 30 ppm. A comparison of Examples 3 and 4 shows that the fluxing process can be used either with or without chlorine in the fluxing gas. A comparison of Example 5 to Examples 3 and 4 show that tamping during the fluxing process considerably improves the recovery. Without tamping the recovery was 62%; when tamping was used the recovery was greater than 90%.

While specific embodiments of the invention have been described in detail, it will be appreciated by those skilled in the art that various modifications and alternatives to those details could be developed in light of the overall teachings of the disclosure. Accordingly, the particular arrangements disclosed are meant to be illustrative only and not limiting as to the scope of the invention which is to be given the full breadth of the appended claims and any and all equivalents thereof.

Claims

1. A method of recovering decarbonized aluminum comprising the steps of:

providing an alloy melt that comprises Al4C3 and aluminum;

cooling the alloy melt;

adding a sufficient amount of a finely dispersed gas to the alloy melt at a temperature of about 700° C. to about 900° C. to separate the aluminum from the Al4C3 precipitates; and

recovering the aluminum from the Al4C3 precipitates,

wherein the aluminum recovered is a decarbonized carbothermically produced aluminum,

wherein the step of adding a sufficient amount of the finely dispersed gas effects flotation of the Al4C3 precipitates.

2. The method of claim 1, wherein the step of recovering the aluminum from the Al4C3 precipitates is by decanting, sub-surface or vacuum tapping the aluminum to a receiver.

3. The method of claim 1, wherein the gas is an inert gas.

4. The method of claim 1, wherein the inert gas used is either argon or carbon dioxide.

5. The method of claim 1, wherein the gas is a mixed gas.

6. The method of claim 5, wherein the mixed gas is a mixture of inert gas with a reactive gas.

7. The method of claim 6, wherein the inert gas is argon and the reactive gas is chlorine.

8. The method of claim 1, wherein the gas is introduced to the alloy melt by a rotating disperser, a bubbler tube, or a porous diffuser.

9. The method of claim 7, wherein the mixed gas contains 95 volume % of argon and 5 volume % of Cl2.

10. The method of claim 1, wherein the step of adding of a sufficient amount of the finely dispersed gas to the alloy melt includes tamping the resultant solid materials on the surface of the alloy melt into the alloy melt.