BONDED ARTICLE

In a bonded article comprising a pair of substrates joined with a silicone base adhesive, a thin layer comprising a room temperature curable organopolysiloxane composition in the cured state having a lower strength than the adhesive intervenes between the substrate and the adhesive. The article is ready for recycling even after exposure to elevated temperature.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
CROSS-REFERENCE TO RELATED APPLICATION

This non-provisional application claims priority under 35 U.S.C. §119(a) on Patent Application No. 2009-140034 filed in Japan on Jun. 11, 2009, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

This invention relates to bonded articles which are used as electric/electronic components in automobiles, electric appliances or the like, and make more efficient the step of selecting components during recovery, repair and recycle of such products.

BACKGROUND ART

Silicone base adhesives and sealants are widely used in the automotive, electric/electronic, and building fields because of their advantages of adhesion, heat resistance and weather resistance. Since silicone base adhesives and sealants are substantially undegradable by heat, components using them are difficult to repair or recycle.

Today in every field, articles are desired to be recyclable to meet the requirements of environment friendliness and cost saving. In the automotive, electric appliance and electric/electronic fields as well, it is required that members joined with adhesive be disintegrated for recycling purposes.

Several methods are known for easy disintegration of a bonded article joined with a curable resin composition. For example, JP-A 2003-026784 discloses a bonded article of substrates joined with a polyol base curable composition wherein the cured composition is softened or liquefied by heating at 150 to 200° C., whereby the article is disintegrated into substrates. JP-A 2002-327163 discloses a method for disintegrating a bonded structure of components bonded with a moisture-curable urethane prepolymer base adhesive by contacting a halogenated organic solvent with the bonding site to weaken the bond strength of the bonding site and disintegrating the bonded structure at the bonding site into components. JP-A 2008-120903 discloses a releasable adhesive tape using an adhesive layer of a vinyl monomer mixture based on an alkyl(meth)acrylate, which maintains a high bond strength in the normal state, but is reduced in bond strength upon heating, so that the tape may be easily separated and disintegrated.

Unlike general organic adhesives, silicone base adhesives have a problem inherent to their heat resistance and weather resistance, that is, the once cured adhesive is difficult to soften, liquefy or chemically degrade by application of heat, UV or the like. Since silicone base adhesives are used mainly at the place where heat resistance and weather resistance are required, a choice of heat or UV as a trigger for the disintegration process is undesired from the standpoint of adhesion reliability.

A masking silicone base adhesive is proposed as the silicone base adhesive which provides a satisfactory seal, but allows members to be readily disintegrated. Some masking silicone base adhesives are free of a tackifier, but contain a release agent to impart parting properties from glass and metals. For example, JP-A 2005-282165 discloses a silicone base adhesive which develops parting properties upon heating. JP-A 2005-105263 discloses a joint structure of substrates bonded with a silicone base adhesive wherein the substrates are separated by applying ultrasonic vibration to the joint structure.

However, these silicone base adhesives still have drawbacks. Since the release agent itself loses its effect by pyrolysis during temperature service above 200° C., the silicone base adhesive is eventually bonded to the substrates by heat. Substantial constraints are involved in the step of applying ultrasonic vibration to the joint structure.

For example, the masking silicone base adhesive used in a microwave oven for securing a turntable to a casing must have a bonding/securing ability. It develops an enhanced bond to a member by the heat generated during oven operation, making disintegration difficult and hindering recovery and repair.

CITATION LIST

Patent Document 1: JP-A 2003-026784

Patent Document 2: JP-A 2002-327163

Patent Document 3: JP-A 2008-120903

Patent Document 4: JP-A 2005-282165

Patent Document 5: JP-A 2005-105263

DISCLOSURE OF INVENTION

An object of the invention is to provide a bonded article comprising substrates adhesively joined together which exerts a satisfactory seal and is ready for recycling without breakage of the substrates after the normal service and even after exposure to high temperature.

It is desired to make more efficient the step of selection of components during recovery, repair and recycle of electric/electronic products or the like, the component being a bonded article comprising a pair of useful substrates joined together with a silicone base adhesive. The inventors have found that if a thin layer comprising a room temperature curable organopolysiloxane composition in the cured state having a lower strength than the silicone base adhesive is disposed between the substrate and the silicone base adhesive, the bonded article exerts a satisfactory seal and is ready for recycling without breakage of the substrates after the normal service and even after exposure to high temperature.

Specifically, when the silicone base adhesive for joining two substrates together is formed as a discontinuous layer whose rubber strength changes stepwise, the bonded article maintains a satisfactory seal in service because of the bond formed. When a stress for disintegration purpose is applied to the bonded article after degradation at normal temperature or high temperature, the lower rubber strength layer of the discontinuous layer is broken so that the article is readily disintegrable. The discontinuous layer is constructed by combining a thin layer of a room temperature curable organopolysiloxane composition having a relatively low strength in the cured state with a layer of a silicone base adhesive having a high strength. A bonded article ready for recycling is obtainable without detracting from the bond strength of the bonded article. The invention is predicated on this finding.

The invention provides a bonded article ready for recycling comprising a pair of substrates joined with a silicone base adhesive, wherein a thin layer comprising a room temperature curable organopolysiloxane composition in the cured state having a lower strength than the silicone base adhesive intervenes between the substrate and the silicone base adhesive.

In a preferred embodiment, the thin layer has a thickness of 10 to 500 μm. The room temperature curable organopolysiloxane composition in the cured state preferably has a tensile strength of 0.01 to 0.5 MPa according to JIS K-6249. More preferably, a difference in tensile strength between the silicone base adhesive and the room temperature curable organopolysiloxane composition in the cured state is at least 0.5 MPa, provided that the tensile strength is measured according to JIS K-6249.

The substrates are typically of glass and/or metal.

The bonded article is typically an automotive part or electric/electronic part.

ADVANTAGEOUS EFFECTS OF INVENTION

While the bonded article maintains a satisfactory bond and/or seal, it is easily disintegrable for recycle purposes without breakage of constituent substrates.

DESCRIPTION OF EMBODIMENTS

According to the invention, the bonded article ready for recycling is defined as comprising a pair of substrates joined with a silicone base adhesive. A thin layer (or primer layer) comprising a room temperature curable (RTC) organopolysiloxane composition in the cured state having a lower strength than the silicone base adhesive intervenes between the substrate and the silicone base adhesive.

Substrate

The substrates used herein may be of metals, glass, plastics or ceramics, with the metals or glass being preferred. Those substrates suited for use in automotive parts and electric/electronic parts are preferable. A pair of substrates to be joined together may be of the same or different materials.

Silicone Base Adhesive

The silicone base adhesive used herein is selected from silicone adhesives and modified silicone adhesives and includes sealing materials. Of these, silicone adhesives are preferred. They may be of any cure mechanisms including condensation cure, addition reaction cure, radical reaction cure, and UV cure. Inter alia, the condensation cure and addition reaction cure are preferred, with the condensation cure being most preferred. Any commercially available silicone adhesives may be used.

RTC Organopolysiloxane Composition

The RTC organopolysiloxane composition used herein is not particularly limited as long as the cured product thereof has a lower strength than the silicone base adhesive. Preferred is an RTC organopolysiloxane composition comprising

(A) 100 parts by weight of an organopolysiloxane having the general formula (1):

wherein R1 is a substituted or unsubstituted, monovalent hydrocarbon group of 1 to 10 carbon atoms, and n is an integer of at least 10,

(B) 0.1 to 30 parts by weight of a silane compound having in a molecule at least two silicon-bonded hydrolyzable groups and a remainder silicon-bonded organic group(s) selected from methyl, ethyl, propyl, vinyl and phenyl, and/or a partial hydrolyzate thereof, and

(C) 0.01 to 5 parts by weight of a curing catalyst.

The respective components are described in detail.

Component (A) is an organopolysiloxane having the general formula (1):

wherein R1 is a substituted or unsubstituted, monovalent hydrocarbon group of 1 to 10 carbon atoms, and n is an integer of at least 10.

Examples of the monovalent hydrocarbon group represented by R1 include alkyl groups such as methyl, ethyl and propyl, cycloalkyl groups such as cyclohexyl, alkenyl groups such as vinyl and allyl, aryl groups such as phenyl and tolyl, and substituted forms of the foregoing in which some hydrogen atoms are substituted by halogen or the like, such as 3,3,3-trifluoropropyl. Inter alia, methyl is preferred. A plurality of groups R1 in formula (1) may be the same or different.

The subscript n is an integer of at least 10, and is preferably such an integer that the diorganopolysiloxane may have a viscosity of 0.1 to 500,000 mm2/s, especially 10 to 10,000 mm2/s at 25° C. Note that the viscosity is measured by a Brookfield rotational viscometer.

Component (B) is a silane compound having in a molecule at least two silicon-bonded hydrolyzable groups and a remainder silicon-bonded organic group(s) selected from methyl, ethyl, propyl, vinyl and phenyl, and/or a partial hydrolyzate thereof.

The silane compound used herein may have the general formula (2):


R24-aSiXa  (2)

wherein R2 is a group selected from methyl, ethyl, propyl, vinyl and phenyl, X is a hydrolyzable group, and a is 2 or 3. A mixture of such silane compounds is also useful.

Examples of the hydrolyzable group X that the silane compound or partial hydrolyzate thereof as component (B) possesses include ketoxime, alkoxy, acetoxy, and isopropenoxy, with the alkoxy and isopropenoxy being preferred.

Examples of the silane compound (B) include alkoxysilanes such as methyltrimethoxysilane, dimethyldimethoxysilane, vinyltrimethoxysilane, phenyLtrimethoxysilane, and methyltriethoxysilane, isopropenoxysilanes such as methyltriisopropenoxysilane, ethyltriisopropenoxysilane, vinyltriisopropenoxysilane, and phenyltriisopropenoxysilane, and acetoxysilanes such as methyltriacetoxysilane, ethyltriacetoxysilane, and vinyltriacetoxysilane, as well as partial hydrolytic condensates of these silanes.

Component (B) is compounded in an amount of 0.1 to 30 parts, preferably 0.5 to 20 parts, and more preferably 1 to 15 parts by weight per 100 parts by weight of component (A). Less than 0.1 pbw of component (B) fails to incur crosslinking or to provide a useful composition whereas more than 30 pbw may result in a cured composition having poor mechanical properties.

Component (C) is a curing catalyst for catalyzing condensation reaction between components (A) and (B) in the composition. The catalyst may be used alone or in admixture of two or more.

Examples of the catalyst include tin catalysts such as tin dioctoate, dimethyltin diversatate, dibutyldimethoxytin, dibutyltin diacetate, dibutyltin dioctoate, dibutyltin dilaurate, dibutyltin dibenzylmaleate, dioctyltin dilaurate, and tin chelates; strong base compounds such as guanidine and 1,8-diazabicyclo[5.4.0]-7-undecene (DBU), and alkoxysilanes having residues thereof; and titanic acid esters and titanium chelates such as tetraisopropoxytitanium, tetra-n-butoxytitanium, tetrakis(2-ethylhexoxy)titanium, diisopropoxybis(acetylacetonato)titanium, and titanium isopropoxyoctylene glycol.

Component (C) is compounded in an amount of 0.01 to 5 parts, preferably 0.01 to 3 parts, and more preferably 0.02 to 2 parts by weight per 100 parts by weight of component (A). Less than 0.01 pbw of component (C) may provide insufficient cure whereas more than 5 pbw may detract from shelf stability.

In the preferred RTC organopolysiloxane composition, (D) an organopolysiloxane having the general formula (3) is compounded. Inclusion of component (D) facilitates to adjust the viscosity and cured strength of the composition.

Herein R3 is a substituted or unsubstituted, monovalent hydrocarbon group of 1 to 10 carbon atoms, examples of which are the same as exemplified for R1 in formula (1), with methyl being most preferred. The subscript m is an integer of at least 2, preferably 2 to 1,000, and more preferably 2 to 500.

Component (D) is preferably compounded in an amount of 1 to 200 parts, more preferably 5 to 100 parts by weight per 100 parts by weight of component (A).

The RTC organopolysiloxane composition may be diluted with (E) an organic solvent for facilitating to form a thin film and to control the thickness thereof. The organic solvent (E) is not particularly limited as long as components of the silicone composition are dissolved or uniformly dispersed therein. Low polar organic solvents are preferred. Examples include C5-C8 alkanes such as n-pentane and its isomers, n-hexane and its isomers, n-pentane and its isomers, n-octane and its isomers, C5-C8 cycloalkanes such as cyclopentane and its isomers, cyclohexane and its isomers, cycloheptane and its isomers, cyclooctane and its isomers, C3-C6 ketone compounds such as acetone, 2-butanone, 2-pentanone, 3-pentanone, 3-methyl-2-butanone, 2-hexanone, 3-hexanone, 3-methyl-2-pentanone, 4-methyl-2-pentanone, 2-methyl-3-pentanone, 3,3-dimethyl-2-butanone, and aromatic ring-containing organic compounds of 6 to 8 carbon atoms such as benzene, toluene, ethylbenzene, xylene and isomers thereof. Inter alia, C5-C8 alkanes are preferred, with n-hexane and n-heptane being most preferred.

Component (E) is not necessary when the composition has a relatively low viscosity. When compounded, an amount of component (E) is preferably 0 to 2,000 parts, more preferably 50 to 1,500 parts, and even more preferably 100 to 1,000 parts by weight relative to 100 parts by weight of the composition (i.e., total of components (A) to (D), or total of components (A) to (D) plus optional components). An excess amount of component (E) may rather exacerbate working efficiency.

In the RTC organopolysiloxane composition, any well-known additives commonly used in ordinary RTC organopolysiloxane compositions may be added as long as the objects of the invention are not impaired.

The RTC organopolysiloxane composition may be prepared by any well-known methods, specifically by intimately mixing the foregoing components.

The RTC organopolysiloxane composition in the cured state preferably has a tensile strength of 0.01 to 0.5 MPa, and more preferably 0.05 to 0.3 MPa, according to JIS K-6249. A lower tensile strength may lead to a bonded article having a low bond strength whereas a higher tensile strength may interfere with disintegration and recycling.

The invention is characterized by the cured RTC organopolysiloxane composition having a lower strength than the silicone base adhesive. Preferably a difference in tensile strength between the silicone base adhesive and the cured RTC organopolysiloxane composition is at least 0.5 MPa, more preferably 0.5 to 3.5 MPa, provided that the tensile strength is measured according to JIS K-6249. The difference of tensile strength in the range ensures easy disintegration and recycling.

In the bonded article, the thin layer of the cured RTC organopolysiloxane composition preferably has a thickness of 10 to 500 μm, more preferably 20 to 300 μm. Outside the range, a thinner layer may adversely affect disintegration and recycling whereas a thicker layer may detract from the function of the bonded article. The silicone base adhesive layer has a thickness which is usually found in conventional bonded articles although a thickness in the range of 0.1 to 5 mm, especially 0.3 to 3 mm is preferred.

The method of manufacturing the bonded article is not particularly limited. For example, a thin layer of the RTC organopolysiloxane composition is formed on a surface of one substrate. The substrates are then joined together with a silicone base adhesive so that the adhesive layer is sandwiched between the substrates and the thin layer is disposed between the substrate and the adhesive layer.

The bonded article exhibits the properties of the silicone base adhesive during normal service. The bonded article can be easily disintegrated for recycling purposes because the cured layer (or primer layer) of the RTC organopolysiloxane composition is easily broken.

EXAMPLE

Examples of the invention are given below by way of illustration and not by way of limitation.

Example 1

A composition #1 was prepared by agitating 50 parts by weight of a dimethylpolysiloxane capped at either end with a hydroxyl group having a viscosity of 1,000 mm2/s and 50 parts by weight of a dimethylpolysiloxane capped at either end with a hydroxyl group having a viscosity of 5,000 mm2/s at room temperature for 10 minutes, adding thereto 4 parts by weight of vinyltriisopropenoxysilane and 0.35 part by weight of tetramethylguanidylpropyltrimethoxysilane, agitating at room temperature for 10 minutes until uniform, adding 428 parts by weight of n-hexane, and agitating for a further 10 minutes. Composition #1 had a tensile strength of 0.2 MPa in the cured state.

Composition #1 was thinly brush coated on the surfaces of two glass plates and allowed to stand for 30 minutes to form a coating of 15 μm thick. After 30 minutes, an RTV silicone adhesive having a tensile strength of 2.8 MPa in the cured state (available from Shin-Etsu Chemical Co., Ltd.) was applied on the coated surface of one glass plate. The other coated glass plate was rested thereon so that the adhesive was sandwiched between the glass plates to define a spacing of 3 mm. The assembly was aged at 23° C. and 50% RH for 7 days, completing a bonded article #1.

Example 2

A composition #2 was prepared by agitating 100 parts by weight of a dimethylpolysiloxane capped at either end with a hydroxyl group having a viscosity of 1,000 mm2/s, 20 parts by weight of a dimethylpolysiloxane capped at either end with a trimethylsilyl group having a viscosity of 300 mm2/s, 10 parts by weight of vinyltriisopropenoxysilane and 1 part by weight of tetramethylguanidylpropyltrimethoxysilane at room temperature for 20 minutes until uniform, adding 131 parts by weight of n-hexane, and agitating for a further 10 minutes. Composition #2 had a tensile strength of 0.1 MPa in the cured state.

As in Example 1, composition #2 was thinly brush coated on the surfaces of two glass plates and allowed to stand for 30 minutes to form a coating of 20 μm thick. After 30 minutes, an RTV silicone adhesive having a tensile strength of 2.8 MPa in the cured state (available from Shin-Etsu Chemical Co., Ltd.) was applied on the coated surface of one glass plate. The other coated glass plate was rested thereon so that the adhesive was sandwiched between the glass plates to define a spacing of 3 mm. The assembly was aged at 23° C. and 50% RH for 7 days, completing a bonded article #2.

Example 3

A composition #3 was prepared by agitating 80 parts by weight: of a dimethylpolysiloxane capped at either end with a hydroxyl group having a viscosity of 1,000 mm2/s and 20 parts by weight of a dimethylpolysiloxane capped at either end with a hydroxyl group having a viscosity of 30 mm2/s at room temperature for 10 minutes, adding thereto 15 parts by weight of vinyltriisopropenoxysilane and 1 part by weight of tetramethylguanidylpropyltrimethoxysilane, and agitating under a reduced pressure for 30 minutes. Thereafter, 80 parts by weight of a dimethylpolysiloxane capped at either end with a trimethylsilyl group having a viscosity of 0.7 mm2/s was added to the mixture, which was agitated for a further 20 minutes. The resulting composition #3 had a tensile strength of 0.1 MPa in the cured state.

As in Example 1, composition #3 was thinly brush coated on the surfaces of two glass plates and allowed to stand for 30 minutes to form a coating of 30 μm thick. After 30 minutes, an RTV silicone adhesive having a tensile strength of 2.8 MPa in the cured state (available from Shin-Etsu Chemical Co., Ltd.) was applied on the coated surface of one glass plate. The other coated glass plate was rested thereon so that the adhesive was sandwiched between the glass plates to define a spacing of 3 mm. The assembly was aged at 23° C. and 50% RH for 7 days, completing a bonded article #3.

Comparative Example 1

The RTV silicone adhesive having a tensile strength of 2.8 MPa in the cured state (available from Shin-Etsu Chemical Co., Ltd.) was directly applied on the surface of a glass plate without pre-coating it with the composition as in Examples 1, 2 and 3. Another glass plate was rested thereon so that the adhesive was sandwiched between the glass plates to define a spacing of 3 mm. The assembly was aged at 23° C. and 50% RH for 7 days, completing a bonded article #4.

The bonded articles #1 to #4 were held at a high temperature of 250° C. for 1,000 hours and examined at intervals whether they were separated/disintegrated.

TABLE 1 250° C. 0 hr 480 hr 720 hr 1,000 hr Example 1 separated separated separated separated Example 2 separated separated separated separated Example 3 separated separated separated separated Comparative separated not not not Example 1 separable separable separable

Japanese Patent Application No. 2009-140034 is incorporated herein by reference.

Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims.

Claims

1. A bonded article ready for recycling comprising a pair of substrates joined with a silicone base adhesive, wherein a thin layer comprising a room temperature curable organopolysiloxane composition in the cured state having a lower strength than the silicone base adhesive intervenes between the substrate and the silicone base adhesive.

2. The bonded article of claim 1 wherein the thin layer has a thickness of 10 to 500 μm.

3. The bonded article of claim 1 wherein the room temperature curable organopolysiloxane composition in the cured state has a tensile strength of 0.01 to 0.5 MPa according to JIS K-6249.

4. The bonded article of claim 1 wherein a difference in tensile strength between the silicone base adhesive and the room temperature curable organopolysiloxane composition in the cured state is at least 0.5 MPa, provided that the tensile strength is measured according to JIS K-6249.

5. The bonded article of claim 1 wherein the substrates are of glass and/or metal.

6. The bonded article of claim 1 which is an automotive part or electric/electronic part.

Patent History
Publication number: 20100316871
Type: Application
Filed: Jun 8, 2010
Publication Date: Dec 16, 2010
Applicant: Shin-Etsu Chemical Co., Ltd. (Chiyoda-ku)
Inventors: Akitsugu Fujiwara (Annaka-shi), Tsuneo Kimura (Annaka-shi)
Application Number: 12/796,088
Classifications
Current U.S. Class: Including Synthetic Resin Or Polymer Layer Or Component (428/339); As Siloxane, Silicone Or Silane (428/447); As Silicone, Silane Or Siloxane (428/429)
International Classification: B32B 7/12 (20060101); B32B 27/18 (20060101); B32B 17/10 (20060101); B32B 15/08 (20060101);