NONWOVEN FIRE BARRIER WITH ENHANCED CHAR PERFORMANCE

Basalt fiber and/or glass fiber, when combined with flame retardant (FR) cellulosic fiber, forms a nonwoven fire barrier with enhanced fire barrier performance, such as char elongation and char strength.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Patent Application 61/243,580 filed on Sep. 18, 2009, which is herein incorporated by reference.

FIELD OF THE INVENTION

The present invention is related to a nonwoven fire barrier comprised of a blend of fibers. More particularly, the main components of the nonwoven fire barrier are flame retardant (FR) cellulosic fiber and performance-enhancing fiber, which is basalt fiber, glass fiber, or a mixture of these. The nonwoven fire barrier produced is cost-effective and has a variety of uses including without limitation use in mattresses and upholstered furniture.

BACKGROUND

There has been an increasing demand for fire barrier products for use in mattresses and upholstered furniture. For example, the new U.S. federal open-flame mattress standard (CPSC 16 CFR Part 1633) has created a new demand for flame retardant (FR) fibers in the mattress industry. A number of companies have been developing nonwoven fire barriers to meet the federal standard. Examples of the approaches now being used are described in the following recently issued patents.

U.S. Pat. No. 7,410,920.(Davis) describes a nonwoven fire barrier consisting of charring-modified viscose fibers (Visil®) with less than 5% of polymers made from halogenated monomers.

U.S. Pat. No. 7,259,117 (Mater et al.) discloses a nonwoven high-loft fire barrier for mattresses and upholstered furniture. The high-loft nonwoven is composed of melamine fiber alone or in conjunction with other fibers.

There are a number of manufactured FR fibers, i.e., FR compound is added to polymer dope and extruded such that, for example, the polymer backbone is modified to give flame retardancy. Manufactured FR fibers include aramids (Nomex® and Kevlar®), polyimide fibers (Ultem® polyetherimide and Extem® amorphous thermoplastic polyimide fibers), melamine fiber (Basofil®), halogen-containing fibers (Saran® fiber, modacrylics), polyphenylene sulfide fibers (Diofort®, oxidized polyacrylonitrile fibers (Pyron®), cured phenol-aldehyde fibers (Kynol® novoloid fiber), phosphorous FR-containing rayon fibers (Lenzing FR®, Shangdong Helon's Anti-frayon®, and silica-containing rayon fibers (Visil®, Daiwabo's FR Corona®fibers, Sniace's FR fiber, and Shangdong Helon's Anti-fcell®.

Despite their advantages, manufactured FR fibers are expensive. From an economic perspective, most of them are not suitable for mattresses and upholstered furniture due to their high costs. For the mattress and upholstered furniture industries, the most cost-effective commonly available FR cellulosic fibers are FR-treated cotton fiber and FR-treated rayon fiber that are produced by post FR chemical treatment of cotton and rayon fibers. Examples of FR cellulosic fibers are commercially available from Tintoria Piana US, Inc. (Cartersville, Ga., USA). The char forming property of these FR-treated cotton and rayon-fibers make them suitable for fire barrier; however, it would be advantageous to have nonwoven fire barriers with superior fire resistant properties to that afforded by a FR-treated cotton and rayon fibers, but which remain cost effective making them suitable for use in mattresses, upholstered furniture, and in other applications.

SUMMARY

An exemplary embodiment of the present invention is a nonwoven fire barrier containing one or more FR cellulosic fibers and one or more performance-enhancing fibers, such as basalt fibers or glass fibers. The uses of the nonwoven fire barrier include, but are not limited to, mattresses, furniture, building insulations, automotive, appliances, and wall panels for cubicles.

According to the invention, the addition of basalt fiber, glass fiber, or a mixture of these to FR cellulosic fibers can dramatically improve the fire barrier performance, such as char strength and char elongation, which are critical properties of fire barrier nonwoven materials.

DETAILED DESCRIPTION

The present invention generally relates to nonwoven composition which contains FR cellulosic fiber(s) and performance-enhancing fiber, such as basalt fiber, glass fiber, or a mixture of these.

Basalt is a common extrusive volcanic rock. The manufacture of basalt fiber requires the melting of the quarried basalt rock to about 2,730° F. The molten rock is then extruded through small nozzles to produce continuous filaments of basalt fiber. The filaments are cut to desired length depending on final uses. Due to its superior thermal, physical, and chemical properties, it is often used for insulation, construction, automotive, and aircraft applications.

A “nonwoven” is a manufactured sheet, web, or batt of natural and/or man-made fibers or filaments that are bonded to each other by any of several means. Manufacturing of nonwoven products is well described in “Nonwoven Textile Fabrics” in Kirk-Othmer Encyclopedia of Chemical Technology, 3rd Ed., Vol. 16, Jul. 1984, John Wiley & Sons, p. 72˜124 and in “Nonwoven Textiles”, Nov. 1988, Carolina Academic Press. Web bonding methods include mechanical bonding (e.g., needle punching, stitch, and hydro-entanglement), chemical bonding using binder chemicals (e.g., saturation, spraying, screen printing, and foam), and thermal bonding using binder fibers with low-melting points. Two common thermal bonding methods are air heating and calendaring. In air heating, hot air fuses low-melt binder fibers within and on the surface of the web to make high-loft nonwoven. In the calendaring process, the web is passed and compressed between heated cylinders to produce low-loft nonwoven.

In the practice of this invention, the fire barrier material is a nonwoven made from FR cellulosic fiber and performance enhancing fiber selected from basalt and glass fibers. In addition, other fibers (optional fibers) may be included in the nonwoven to achieve properties or characteristics of interest (e.g., color, texture, etc.), The nonwoven may be made using mechanical bonding, chemical bonding, or thermal bonding techniques. In an exemplary embodiment, thermal bonding using low melting point fibers (low-melt binder fiber) is employed to manufacture the nonwoven (i.e., the low melting point fibers melt at a lower temperature than the decomposition temperature of FR cellulosic fibers and the melting point temperature of the performance enhancing fibers, and, after melting and diffusion into the fibers, serve to hold the FR cellulosic fibers and performance enhancing fibers together in the nonwoven). The low-melt binder fibers can be-any of those commonly used for thermal bonding and may preferably, but are not limited to, those that melt from 80 to 150° C. The nonwoven preferably has a basis weight of a basis weight ranging from 0.1˜5.0 oz/ft2 (more preferably, 0.32˜2.0 oz/ft2; however, the basis weight of the nonwoven can vary widely depending on the intended application and desired characteristics of the nonwoven.

Component 1 (Main Component): FR Cellulosic Fiber

FR cellulosic fiber includes FR-treated natural cellulosic fiber, FR-treated manufactured cellulosic fiber, manufactured FR cellulosic fiber, or a mixture of any combination of these fibers. FR chemicals for FR treatment include, but are not limited to, phosphorus-containing FR chemicals, sulfur-containing FR chemicals, halogen-containing FR chemicals, antimony-containing FR chemicals, and boron-containing FR chemicals. Examples of FR chemicals include, but not limited to, phosphoric acid and its derivatives, phosphonic acid and its derivatives, sulfuric acid and its derivatives, sulfamic acid and its derivatives, boric acid and its derivatives, borax, borates, ammonium phosphates, ammonium poly phosphates, ammonium sulfate, ammonium sulfamate, ammonium chloride, ammonium bromide. Natural cellulosic fiber includes, but not limited to, cotton, kapok, flax, ramie, kenaf, abaca, coir, hemp, jute, sisal, and pineapple fiber. Manufactured cellulosic fiber includes, but not limited to, rayon, lyocell, bamboo fiber, Tencel®, and Modal®. Manufactured FR cellulosic fiber includes, but not limited to, Lenzing FR®, Anti-frayon®, Anti-fcell®, Visil®, Daiwabo's FR Corona® fibers, and Sniace's FR rayon.

Component 2 (Main Component): Performance-Enhancing Fiber

Performance-enhancing fiber includes basalt fiber, glass fiber, or a mixture these fibers. Glass fiber includes any type of glass fibers, such as A-glass, E-glass, S-glass, C-glass, T-glass, AR-glass, etc.

Component 3: Low-Melt Binder Fiber (or Powdered Polymer)

Low-melt binder fibers are synthetic fibers and are most widely used for thermal bonded nonwoven materials, although sometimes powdered polymers are used in thermal bonding. Any type of low-melt binder fibers used for thermal bonding process can be used for this application. These synthetic fibers can be either a bicomponent fiber or a fiber with low melting point. Low-melt binder fiber is optional for needle punched nonwoven and chemical-bonded nonwoven. For chemical bonding, binders include, but are not limited to, acrylic latexes, poly vinyl acetate copolymer, poly vinyl chloride copolymer, ethylene vinyl chloride, vinyl acetate-ethylene, acrylic copolymer, butadiene-acrylonitrile copolymers, acrylic binders, styrene acrylonitrile binder, styrene butadiene rubber binder, etc.

Component 4: Optional Fiber

Optional fiber in the practice of this invention is additional fiber(s) added to the blend to provide desired characteristics or cost benefits. Optional fiber includes man-made fibers and natural fibers. These fibers can be untreated or FR chemical treated'to increase flame retardancy. As optional fiber addition, any of these fibers or any combination of these can be added. Man-made fibers include, but are not limited to, polyester, nylon, acrylics, acetate, polyolefins, melamin fibers, elastomeric fibers, polybenzimidazole, aramid fibers, polyimide fibers, modacrylics, polyphenylene sulfide fibers, carbon fibers, Novoloid fibers, manufactured cellulosic fibers (rayon, lyocell, bamboo fiber, tencel®, and modal®), and manufactured FR cellulosic fibers (e.g., Visil®, Anti-fcell®, Daiwabo's FR Corona® fibers, Anti-frayon®, Sniace's FR rayon, and Lenzing FR®). Natural fibers include, but are not limited to, cotton, ramie, coir, hemp, abaca, sisal, kapok, jute, flax, kenaf, coconut fiber, pineapple fiber, wool, cashmere, and silk.

The principle constituents of the nonwoven fire barrier are components 1 and 2. The preferred amount of component 1 (FR cellulosic fiber) is approximately 5˜99.99 wt. % and more preferably 50˜99.99 wt. %. The preferred amount of component 2 (performance-enhancing fiber) is approximately 0.01˜95 wt. % and more preferably at 0.01˜50 wt. % or 0.01˜20 wt. %

In exemplary embodiments, for thermal bonded nonwovens, component 3 (low-melt binder fiber) is required. However, for needle-punched and chemical-bonded nonwovens, component 3 is optional. The preferred amount of component 3 is approximately 1˜70 wt. % and more preferred at 5˜50 wt. %.

Those of skill in the art will recognize that the preferred amounts of components of 1, 2, and 3 are not limited to the ranges specified above, and that, depending on the application, manufacturing process, or other conditions, the amounts of components 1, 2 and 3 can be varied considerably within the practice of this invention.

Component 4 can be optionally added to the blend for providing desired characteristics (e.g., softness, texture, appearance, resilience, etc.) or cost benefit. Components 1 through 4 are blended at different ratios depending on final use and cost of the nonwoven. For example, to provide better resilience property on the final high-loft, nonwoven product and cost benefit, polyester fiber (as component 4) can be added to the blend. One possible example of blend ratio will be FR cellulosic fiber:basalt fiber:polyester fiber:low-melt binder fiber=40-70:5-20:5-20:10-30, e.g., 60:10:10:20.

EXAMPLE 1

Nonwoven web samples with different fiber compositions were prepared using a lab carding machine. For the samples, FR chemical (ammonium phosphate) treated rayon fiber, FR chemical (ammonium phosphate) treated cotton fiber, basalt fiber (diameter: 13 μm, length: 90 mm), glass fiber (E-glass, diameter: 13 μm, length: 90 mm), and low-melt binder fiber (LM) were used. For a fair comparison, the total weight of each blend was controlled to be the same at 10 grams.

The samples were completely burned to form a char using a burner horizontally located beneath the samples. Char strength and elongation were measured by a char tester. The tester is equipped with a loadcell connected to a vertically movable plate which presses char until its breakage. Elongation was measured in the unit of inches and char strength was measured as peak force in the unit of pounds (lb).

TABLE 1 Effect of Basalt and glass fibers on FR-treated rayon fiber Elongation Peak Fiber blends (wt. %) (inch) force (lb) FR-treated rayon:LM = 80:20 0.359 4.21 FR-treated rayon:basalt fiber:LM = 70:10:20 0.609 12.24 FR-treated rayon:glass fiber:LM = 70:10:20 0.639 12.53

TABLE 2 Effect of basalt and glass fibers on FR-treated cotton fiber Elongation Peak Fiber blends (wt. %) (inch) force (lb) FR-treated cotton:LM = 80:20 0.317 1.47 FR-treated cotton:basalt fiber:LM = 70:10:20 0.735 6.83 FR-treated cotton:glass fiber:LM = 70:10:20 0.640 6.55

As demonstrated in Tables 1 and 2, the char elongation and char strength of FR-treated cotton and FR-treated rayon fibers increased dramatically by adding only 10% of basalt or glass fiber. This improved char performance will help to prevent possible char breakage under severe flame conditions which would otherwise cause further flame propagation.

EXAMPLE 2

Thermal bonded high-loft nonwoven samples were prepared by using a commercial production line. FR Cellulosic fibers and low-melt binder fiber (LM) with/without basalt fiber were blended at specific wt. % ratios. The blended fibers were carded to form a fiber web on a conveyor. The web is cross-lapped and passed through an oven to form a high-loft nonwoven. Various blend samples were prepared at different basis weight expressed as ounce per square foot (oz/ft2). The nonwoven samples were tested for char elongation and strength by the same method described in Example 1.

Table 3 shows char properties of FR cellulosic high-loft nonwovens which can be used, for example, in the mattress industry. All these nonwovens show char elongation below 0.4 inch and char strength below 2 lbs, which are pretty common for those products. Table 4 shows performance of some examples of the invented nonwoven blends containing basalt fiber (diameter: 13 μm, length: 90 mm). The results demonstrate significant increases in both char elongation and strength by the addition of basalt fiber.

TABLE 3 Properties of high-loft nonwoven made with FR cellulosic fibers and low-melt binder fiber (LM). Weight of Elongation Peak force Fiber blends (wt. %) nonwoven (oz/ft2) (inch) (lb) Visil ®:LM = 80:20 0.80 0.365 0.92 FR-treated rayon1:Visil ®:LM = 40:40:20 0.77 0.334 1.10 FR-treated cotton1:Visil ®:LM = 40:40:20 0.80 0.352 0.60 FR-treated rayon1:FR-treated cotton1:LM = 40:40:20 0.81 0.244 1.13 FR-treated rayon1:FR-treated cotton1:LM = 40:40:20 1.01 0.284 1.23 FR-treated rayon2:LM = 80:20 0.80 0.210 1.05 FR-treated cotton2:Anti-fcell ®:LM = 40:40:20 1.13 0.336 0.86 1FR treatment with ammonium phosphate 2FR treatment with ammonium sulfate

TABLE 4 Properties of high-loft nonwoven made with FR cellulosic fibers, basalt fiber, and low-melt binder fiber (LM). Weight of Elongation Peak force Fiber blends (%) nonwoven (oz/ft2) (inch) (lb) FR-treated cotton1:basalt:LM = 60:10:30 0.50 0.425 4.60 FR-treated cotton1:basalt:LM = 60:10:30 0.76 0.600 8.33 FR-treated cotton1:basalt:LM = 60:10:30 0.90 0.641 9.65 FR-treated cotton1:basalt:LM = 55:15:30 0.50 0.513 6.05 FR-treated cotton1:basalt:LM = 55:15:30 0.76 0.548 14.28 FR-treated cotton1:basalt:LM = 55:15:30 0.92 0.594 16.61 FR-treated cotton1:FR-treated cotton shoddy1*:basalt:LM = 0.58 0.476 10.78 30:25:15:30 FR-treated cotton1:FR-treated cotton shoddy1*:basalt:LM = 0.80 0.689 13.39 30:25:15:30 FR-treated cotton1:FR-treated cotton shoddy1*:basalt:LM = 0.91 0.714 18.53 30:25:15:30 FR-treated cotton1:FR-treated cotton shoddy1*:basalt:LM = 0.99 0.834 19.97 30:25:15:30 1FR treatment with ammonium sulfate *Cotton shoddy is recycled cotton fiber from textile waste.

Having thus described the invention in rather full detail, it will be understood that such detail need not be strictly adhered to, but that additional changes and modifications may suggest themselves to one skilled in the art, all falling within the scope of the invention as defined by the subjoined claims.

Claims

1. Nonwoven, comprising:

flame retardant (FR) cellulosic fiber; and
performance-enhancing fiber.

2. The nonwoven of claim 1, wherein the FR cellulosic fiber is FR-treated natural cellulosic fiber, FR-treated manufactured cellulosic fiber, manufactured FR cellulosic fiber, or any combination of these fibers.

3. The nonwoven of claim 1, wherein the performance-enhancing fiber is basalt fiber, glass fiber, or a mixture of basalt fiber and glass fiber.

4. The nonwoven of claim 1, further comprising a low-melt binder fiber for thermal bonding of the nonwoven

5. The nonwoven of claim 1, wherein the FR cellulosic fiber and performance-enhancing fiber are mechanically bonded together.

6. The nonwoven of claim 1, wherein the FR cellulosic fiber and performance-enhancing fiber are chemically bonded together.

7. The nonwoven of claim 1, further comprising one or more optional fibers which are different from said FR cellulosic fiber and said performance enhancing fiber.

8. The nonwoven of claim 7 wherein said optional fibers are present in sufficient quantity to provide a characteristic to said nonwoven selected from the group consisting of softness, texture, appearance, resilience, and cost benefit.

9. The nonwoven of claim 1 wherein said nonwoven has a basis weight ranging from 0.1˜5.0 oz/ft2.

10. The nonwoven of claim 1 wherein

said flame retardant FR cellulosic fiber is FR-treated natural cellulosic fiber, FR-treated manufactured cellulosic fiber, manufactured FR cellulosic fiber, or any combination of these fibers,
said performance-enhancing fiber is basalt fiber, glass fiber, or a mixture of basalt fiber and glass fiber, and
said flame retardant FR cellulosic fiber and said performance-enhancing fiber are present in said nonwoven at approximately 5˜99.99 wt. % and 0.01˜95 wt. %, respectively.

11. The nonwoven of claim 10 wherein said FR cellulosic fiber is present in said nonwoven at approximately 50˜99.99 wt. %.

12. The nonwoven of claim 10 wherein said performance-enhancing fiber is present in said nonwoven at approximately 0.01˜20 wt. %.

13. The nonwoven of claim 10 further comprising a low-melt binder fiber at approximately 1˜70 wt. %.

14. The nonwoven of claim 13 further comprising a polyester fiber.

15. The nonwoven of claim 1 wherein

said flame retardant FR cellulosic fiber is FR-treated natural cellulosic fiber, FR-treated manufactured cellulosic fiber, manufactured FR cellulosic fiber, or any combination of these fibers,
said performance-enhancing fiber is basalt fiber, glass fiber, or a mixture of basalt fiber and glass fiber, and said performance-enhancing fiber is present in said nonwoven at approximately 0.01˜20 wt. %.

16. The nonwoven of claim 15 further comprising low-melt binder fibers.

17. The nonwoven of claim 15 further comprising one or more optional fibers.

Patent History
Publication number: 20110070419
Type: Application
Filed: Jun 17, 2010
Publication Date: Mar 24, 2011
Inventors: Sang-Hoon Lim (Kennesaw, GA), Andrea Piana (Atlanta, GA)
Application Number: 12/817,775