Method For Surface-Treating Mirror-Finish Stainless Steel Workpiece
The present invention discloses a method for surface-treating a mirror-finish stainless steel workpiece, which comprises steps: dividing the surface of a mirror-finish stainless steel workpiece into different grinding areas according to the depths of the scratches; selecting sand papers respectively having appropriate grit sizes for the grinding areas, and grinding the grinding areas to remove all the scratches; sequentially using three combinations of polishing agents and grinding materials to undertake polishing; and using an abrasive paste and a fourth grinding material to perform mirror-finishing.
1. Field of the Invention
The present invention relates to a method for surface-treating a mirror-finish stainless steel workpiece, particularly to a method using a series of grinding steps to polish and mirror-finish the surface of a stainless steel workpiece.
2. Description of the Related Art
Some mirror-finish stainless steel workpieces, such as an electric elevator, are unlikely to be fabricated in form of an integral one-piece body but are usually assembled piece by piece with welding. The irregularities caused by welding degrade appearance esthetics and thus need to be finished with grinding, coarse polishing, fine polishing, etc. In the conventional grind-polish technology, tool marks, such as grinding marks and polishing marks, still remain on the fine-polished surface. Further, over-grinding may cause over-heating and distortion on the surface of the mirror-finish stainless steel workpiece. Besides, the conventional grind-polish technology cannot indeed achieve a mirrorlike surface.
On the other side, the stainless steel workpieces, which have been installed in a building, usually have scribed marks, abrasion, corrosion, pollution, etc., on the surface thereof. However, the conventional grind-polish technology is hard to maintain or repair the surface of an electric elevator in situ.
Accordingly, the present invention proposes an innovative method for surface-treating a mirror-finish stainless steel workpiece, which can overcome the conventional problems, and which can promote the esthetics of the polished surface and facilitate in-situ polishing.
SUMMARY OF THE INVENTIONBased on many years' experience in the related field and with persistent research and experiment, the Inventor has been devoted to improving the surface treatment technology and thus proposes a method for surface-treating a mirror-finish stainless steel workpiece of the present invention.
The primary objective of the present invention is to provide a method for surface-treating a mirror-finish stainless steel workpiece, which uses both mechanical and chemical methods to promote the appearance esthetics of a workpiece and achieve a mirrorlike surface.
Another objective of the present invention is to provide a method for surface-treating a mirror-finish stainless steel workpiece, which uses both mechanical and chemical methods to prevent from distortions or recessions caused by over grinding.
A further objective of the present invention is to provide a method for surface-treating a mirror-finish stainless steel workpiece, which can perform surface polishing in situ without dismounting the workpiece.
To achieve the abovementioned objectives, the present invention proposes a method for surface-treating a mirror-finish stainless steel workpiece, which comprises at least the following steps: (1) dividing the surface of a mirror-finish stainless steel workpiece into different grinding areas according to the depths of the scratches; (2) selecting a sand paper having an appropriate grit size for one grinding area, and using a grinder and the sand paper to grind the grinding area; (3) examining whether all the scratches on the grinding area have been eliminated; undertaking Step (5) if the answer is yes; undertaking Step (4) if the answer is no; (4) selecting a sand paper having a greater grit size, and using a grinder and the sand paper to grind the grinding area again, and then undertaking Step (3); (5) examining whether the scratches of all the grinding areas have been eliminated; undertaking Step (6) if the answer is yes; undertaking Step (2) if the answer is no; (6) applying a first polishing agent to all the grinding areas; (7) using a grinder and a first grinding material to eliminate the sand abrasions from all the grinding areas; (8) applying a second polishing agent to all the grinding areas; (9) using a grinder and a second grinding material to eliminate all the marks scribed by the first grinding material from all the grinding areas; (10) applying a third polishing agent to all the grinding areas; (11) using a grinder and a third grinding material to perform a final grinding on all the grinding areas; (12) applying an abrasive paste to all the grinding areas, and letting the abrasive paste stay still on all the grinding areas for a given period of time; (13) using a fourth grinding material to perform mirror-finishing on all the grinding areas.
To achieve the abovementioned objectives and efficacies, the Inventor has persistently improved the conventional technologies and thus proposes a method for surface-treating a mirror-finish stainless steel workpiece, which uses a plurality of polishing agents, grinding materials, and abrasive pastes to enhance the polishing effect. Below, two embodiments are used to demonstrate the technical principles and process of the present invention.
Refer to
In the first embodiment, the first polishing agent adopted in Step 106 is of a BRIGHT-CUT grade, which can fast cut various metals and generates medium brightness. The first grinding material used in Step 107 is a sisal buff, which cooperates with the BRIGHT CUT agent to smooth all the sand abrasions on all the grinding areas. The second polishing agent adopted in Step 108 is of a FASTCUT grade, which has high grinding efficiency and can fast remove the scratches on the surface of a metal, generating lower brightness. The second grinding material used in Step 109 is a cotton buff, which cooperates with the FASTCUT agent to remove the marks scribed on all the grinding areas by the first grinding material. The third polishing agent adopted in Step 110 is of a WHITE CUTTER P2 grade, which can fast cut various metals, contains less wax, and generates a very clean surface having medium brightness. The third grinding material used in Step 111 is a wool buff, which cooperates with the WHITE CUTTER P2 agent to perform a final grinding on all the grinding areas.
In the first embodiment, the abrasive paste used in Step 112 contains at least diluted nitric acid, alumina powder, xanthan gum, water, bentonite, and essence. After applied to all the grinding areas, the abrasive paste stays still on the surface of the workpiece for 30-60 minutes. Then, the process proceeds to Step 113. The fourth grinding material used in Step 113 is a high-density and tough sponge, which cooperates with the abrasive paste to perform mirror-finishing on all the grinding areas. Thus is achieved a highly reflective mirrorlike surface on a stainless steel workpiece.
Refer to
Refer to
In the second embodiment, the first polishing agent adopted in Step 308 is of a BRIGHT-CUT grade, which can fast cut various metals and generates medium brightness. The first grinding material used in Step 309 is a sisal buff, which cooperates with the BRIGHT CUT agent to smooth all the sand abrasions on all the grinding areas. The second polishing agent adopted in Step 310 is of a FASTCUT grade, which has high grinding efficiency and can fast remove the scratches on the surface of a metal, generating lower brightness. The second grinding material used in Step 311 is a cotton buff, which cooperates with the FASTCUT agent to remove the marks scribed on all the grinding areas by the first grinding material. The third polishing agent adopted in Step 312 is of a WHITE CUTTER P2 grade, which can fast cut various metals, contains less wax, and generates a very clean surface having medium brightness. The third grinding material used in Step 313 is a wool buff, which cooperates with the WHITE CUTTER P2 agent to perform a final grinding on all the grinding areas.
In the second embodiment, the abrasive paste used in Step 314 contains at least diluted nitric acid, alumina powder, xanthan gum, water, bentonite, and essence. After applied to all the grinding areas, the abrasive paste stays still on the surface of the workpiece for 30-60 minutes. Then, the process proceeds to Step 315. The fourth grinding material used in Step 315 is a high-density and tough sponge, which cooperates with the abrasive paste to perform mirror-finishing on all the grinding areas. Thus is achieved a highly reflective mirrorlike surface on a stainless steel workpiece.
From the above description, it is known that the present invention has the following advantages:
- 1. The present invention grinds and polishes the surface of a stainless steel workpiece in mechanical and chemical ways and thus can prevent from recessions and distortions caused by over grinding.
- 2. The present invention can maintain or repair the surface of a stainless steel workpiece in situ without dismounting the workpiece.
- 3. The conventional technology usually attaches additional layers on the surface of an electric elevator. The additional layers increase the weight of the electric elevator, make the electric elevator consume more power, and shorten the service life of the electric elevator. The present invention does not use additional layers and is thus exempt from the abovementioned problems.
- 4. The present invention can repair a seriously scratched or polluted object. Thus, the user can keep on using the object and needn't spend money on replacing the object.
- 5. The present invention can polish a scratched region locally to resume the mirrorlike surface without generating a luster difference between the polished and unpolished regions. As the present invention needn't process the total surface of an object, it can repair the object more economically and efficiently.
- 6. The present invention can achieve a real mirrorlike surface because the present invention can repair the surface of an object without leaving any tool mark, such as sand abrasions, random scratches, polishing marks, etc., on the surface of the object.
The embodiments described above are only to demonstrate the technical contents and characteristics of the present invention to enable the persons skilled in the art to understand, make, and use the present invention. However, these embodiments are not intended to limit the scope of the present invention. Therefore, any equivalent modification or variation according to the spirit of the present invention is to be also included within the scope of the present invention.
Claims
1. A method for surface-treating a mirror-finish stainless steel workpiece, comprising steps:
- (1) dividing a surface of a mirror-finish stainless steel workpiece into different grinding areas according to depths of scratches;
- (2) selecting a first sand paper having an appropriate grit size for one of said grinding areas, and using a grinder and said first sand paper to grind said grinding area;
- (3) examining whether all scratches on said grinding area have been eliminated; undertaking Step (5) if the answer is yes; undertaking Step (4) if the answer is no;
- (4) selecting a second sand paper having a greater grit size, and using a grinder and said second sand paper to grind said grinding area again, and then undertaking Step (3);
- (5) examining whether scratches of all said grinding areas have been eliminated; undertaking Step (6) if the answer is yes; undertaking Step (2) if the answer is no;
- (6) applying a first polishing agent to all said grinding areas;
- (7) using a grinder and a first grinding material to eliminate sand abrasions from all said grinding areas;
- (8) applying a second polishing agent to all said grinding areas;
- (9) using a grinder and a second grinding material to eliminate marks scribed by said first grinding material from all said grinding areas;
- (10) applying a third polishing agent to all said grinding areas;
- (11) using a grinder and a third grinding material to perform a final grinding on all said grinding areas;
- (12) applying an abrasive paste to all said grinding areas, and letting said abrasive paste stay still on all said grinding areas for a given period of time; and
- (13) using a fourth grinding material to perform mirror-finishing on all said grinding areas.
2. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said first polishing agent used in said step (6) is a BRIGHT-CUT grade polishing agent that can fast cut various metals and generates medium brightness.
3. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said first grinding material used in said step (7) is a sisal buff.
4. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said second polishing agent used in said step (8) is a FASTCUT grade polishing agent that has high grinding efficiency, can fast remove scratches on a surface of a metal, and generates lower brightness.
5. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said second grinding material used in said step (9) is a cotton buff.
6. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said third polishing agent used in said step (10) is a WHITE CUTTER P2 grade polishing agent that can fast cut various metals, contains less wax, and generates a very clean surface having medium brightness.
7. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said third grinding material used in said step (11) is a wool buff.
8. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said abrasive paste used in said step (12) contains at least diluted nitric acid, alumina powder, xanthan gum, water, bentonite, and essence.
9. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said given period of time in said step (12) is 30-60 minutes.
10. The method for surface-treating a mirror-finish stainless steel workpiece according to claim 1, wherein said fourth grinding material used in said step (13) is a high-density and tough sponge.
Type: Application
Filed: Jul 1, 2010
Publication Date: Nov 17, 2011
Inventor: Chun-Pei Lee (Taipei County)
Application Number: 12/829,211
International Classification: B24B 1/00 (20060101); B24B 7/00 (20060101);