Water-Based Adhesives
An adhesive includes a polymeric latex, a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, a-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler. The adhesive has a solids content of 35-65% and a pH of 9 to 12. Articles of manufacture, such as tires and air springs incorporate the adhesive to join rubber interfaces. A method of making the adhesive is also is provided.
This disclosure relates to adhesives, particularly water-based adhesives for rubber compositions in the tire and air spring industry.
BACKGROUNDArticles made from connected rubber components may be joined together with adhesive. In some applications, adhesives may be the primary option for joining components, particularly when mechanical methods such as stitching are not available, such as in articles that function as air or moisture barriers. For example, rubber air springs and tires include separate rubber components that are joined with adhesives. Retread tires also may employ adhesive to join the new tread to the carcass, or to adhere an intermediate cushion layer to a carcass and/or a tread.
While two similar rubber components can be joined and then cured at the same time and obtain a strong bond at the joint, this method of joining rubber components is not preferable for some manufacturing processes where it is desirable to join the components and store them and/or allow them to cure slowly. Rubber adhesives may be used to provide tack to a rubber component while a rubber article is cured or stored.
SUMMARYIn an embodiment, an adhesive includes a polymeric latex, a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler. The adhesive has a solids content of about 35 to about 65% and a pH of about 9 to 12.
In an embodiment, an article of manufacture includes an elastomeric rubber component comprising an elastomer selected from the group consisting of: polychloroprene, butyl rubber, hevea and non-hevea derived natural rubber, polyisoprene, polybutadiene, nitrile rubber, poly(styrene-butadiene), and combinations thereof. The elastomeric rubber component is joined at an interface with a second rubber component or another portion of the elastomeric rubber component. The interface includes a layer of adhesive, which comprises: a polymeric latex; a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler.
In an embodiment, a method includes the steps of: mixing together an adhesive composition comprising: a polymeric latex; a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler.
U.S. provisional application 61/567,701, titled “Water-Based Adhesive,” filed on Dec. 7, 2011 and U.S. provisional application 61/606,161, titled “Water-Based Adhesive Including Guayule Extract,” filed on Mar. 2, 2012 are incorporated herein by reference for all purposes.
Disclosed herein is a water-based, low VOC, latex adhesive for joining rubber interfaces. The adhesive may be useful in a variety of applications. Particular examples of applications include those that require strong rubber-to-rubber joints and that are utilized to provide an air barrier, such as air springs and tire components. Application of new tread to retreaded tires is another application where the composition described herein may have particular utility.
In an embodiment the adhesive includes the following components: an aqueous polymeric latex, a penetrant, a reinforcing filler, a tackifier, and a stabilizer. In another embodiment, either the penetrant or the stabilizer or both may be omitted.
In an embodiment, the polymeric latex of the adhesive may be an aqueous emulsion of elastomers such as hevea and non-hevea (including guayule) natural rubber, polyisoprene, poly(styrene-butadiene), poly(isoprene-styrene), poly(isoprene-butadiene), polybutadiene, polychloroprene, nitrile rubber, butyl rubber, and combinations thereof.
In an embodiment, the polymeric portion of the latex may have a weight average molecular weight (Mw) of about 100,000 to about 30,000,000 g/mol, such as about 100,000 to about 10,000,000 g/mol or about 100,000 to about 5,000,000 g/mol and a number average molecular weight (Mn) of about 100,000 to about 30,000,000 g/mol, such as about 100,000 to about 10,000,000 g/mol or about 100,000 to about 5,000,000 g/mol. The polymer portion may have a Tg of about −110° C. to about 10° C., such as about −110° C. to about −10° C. or about −110° C. to about −25° C.
In an embodiment, the polymeric latex may have a solids content of about 10% to about 90%, such as about 20% to about 80%, or about 30% to about 70%. The pH of the polymeric latex may be about 7 to about 14, such as about 8 to about 13 or about 9 to about 12.
Without being bound to theory, when the adhesive is applied to an elastomer substrate, the penetrant component operates to open up the interstices of the polymeric matrix of the elastomer it is applied to. This allows the adhesive composition to have better penetration and intermingling with the substrate elastomer. The surface area of the interface between the adhesive and the elastomer substrate is also increased.
In an embodiment, the penetrant is selected from terpenes, such as polylimonene, limonene, α-pinene, dipentene, citronellene; or from the group consisting of carvone, citral, 1,8-cineole, eucalyptol, citronellol, geraniol, terpinen-4-ol, borneol, camphor, and combinations thereof. In certain embodiments the penentrant is substantially or completely free of VOCs.
In another embodiment, the penetrant is guayule resin. As used herein, “guayule resin” means the naturally occurring non-rubber chemical entities present in guayule shrub matter. These chemical entities include, but are not limited to, resins (such as terpenes), fatty acids, proteins, and inorganic materials, and include both polar and non-polar moieties. Guayule resin can result from the isolation of rubber from guayule shrub using organic solvent based processes. The resin represents the dried fraction (i.e., solvent removed) of material isolated in the polar organic solvent phase from such a process.
In an embodiment, the guayule resin can be added as guayule rubber latex, such latex including both the guayule rubber and the guayule resin for use as the penetrant. In this embodiment, two components of the adhesive may be fulfilled by one source material. In another embodiment, purified guayule latex comprising 5% or less, alternatively 3% or less, or 1% or less guayule resin may be used in the adhesive composition. In this embodiment, the penetrant is added separately, and may include guayule resin.
The reinforcing filler component provides improved strength and durability to the adhesive composition. This is in contrast to many adhesives that use no or very little reinforcing filler. For example, some adhesive manufacturers may use carbon black in very small amounts to tint the adhesive, but not in reinforcing amounts.
In an embodiment, the reinforcing filler is carbon black, such as reinforcing grade carbon black. Examples include carbon black in the N100, N200, and N300 series. In some embodiments, a higher surface area carbon black may provide improved performance. For example, the carbon black may have an N2SA surface area of about 10 to about 150 m2/g, such as about 20 to about 140 m2/g or about 30 to about 130 m2/g. In some embodiments, an aqueous carbon black dispersion may be used. Preferably, the dispersion contains carbon black in an amount from about 20% to about 50% by weight of the dispersion and the dispersion has a pH from about 7 to about 12. The particle size of the carbon black used in such dispersions is preferably from about 10 to about 150 m2/g. Aqueous carbon black dispersions which may be employed include, for example, AQUABLAK 5101, which is available from Solution Dispersions, and includes a N100 series carbon black with 40% solids and pH of 10-1, and is stabilized with anionic and non-ionic surfactants.
The reinforcing fillers may be present in the adhesive in an amount of about 10 to about 80 phr (“per hundred rubber” is a by weight measure, and is based on the weight of the polymer in the polymeric latex set to 100), for example, about 15 to about 60 phr, or about 20 to about 40 phr.
The tackifier provides improved tack to the adhesive. Tackifiers that may be employed include, for example, TACOLYN 5003, TACOLYN 5070, or AQUATAC 6025. TACOLYN 5003 and 5070 are from EASTMAN CHEMICAL COMPANY, and they are aliphatic hydrocarbon resin tackifiers with a softening point of 70-130° C. and a solids content of 45-50%. AQUATAC 6025 is from ARIZONA CHEMICAL, Co., and has a softening point of 26° C. and a solids content of 59-63%.
In an embodiment, the tackifier may be present in an amount of about 5 to about 40 phr, such as about 10 to about 35 phr, or about 15 to about 30 phr. In an embodiment, the tackifier has a pH of about 2 to about 13, such as about 3 to about 12, or about 4 to about 11 and a solids content of about 30 to about 80%, such as about 35 to about 75%, or about 40 to about 70%. In an embodiment, the tackifier has a softening point of about 5 to about 170° C., such as about 15 to about 150° C., or about 25 to about 130° C.
The stabilizer component aids in keeping the composition in a latex emulsion state. An example class of stabilizers is non-ionic surfactants, such as IGEPAL CO-887, which is a non-ionic surfactant from Rhodia Group. IGEPAL CO-887 is a nonylphenoxy poly(ethyleneoxy)ethanol surfactant stabilizer with a 70% solids content. Other examples of stabilizers that may be used in embodiments of the adhesive composition include: PLURONIC F-68 from BASF, probenecid (4-(dipropylsulfamoyl)benzoic acid), tetraethyl orthosilicate, TWEEN 80, and acryloamido-2-methyl-1-propanesulfonic acid. The stabilizer may also be present in the polymeric latex component, rather than as a separately added component.
In an embodiment, the stabilizer may be present in an amount of about 0 to about 10 phr, such as about 1 to about 6 phr, or about 2 to about 4 phr. In an embodiment, the stabilizer has a pH of about 5 to about 13, such as about 6 to about 12, or about 7 to about 11 and a solids content of about 35 to about 85%, such as about 40 to about 80%, or about 45 to about 75%.
In an embodiment, the composition is substantially or completely free of cure agents, such as, for example, sulfur or peroxide. Substantially free in this context means that no cure agents are added for the purpose of curing the composition, and are only present for another purpose in the composition or as accidental contaminants, for example, less than 1 phr or less than 0.1 phr. However, in another embodiment, cure agents may also be used in conventional quantities. Without being bound by theory, it is believed that the cure agents and accelerators that leach out of the elastomer substrate that the adhesive is applied to are sufficient to impart a cure to the adhesive under curing conditions. The penetrant is believed to aid in leaching sufficient quantities of the cure agent and accelerators from the elastomer substrate.
In an embodiment, the entire adhesive composition will have a pH of about 7 to about 14, such as about 8 to about 13, or about 9 to about 12, and a solids content of about 25 to about 75%, such as, about 30% to about 70%, or about 35 to about 65%. Furthermore, in an embodiment, the adhesive will be substantially or completely free of VOCs. A volatile organic compound (VOC) is any carbon-based compound that will vaporize at standard room temperatures. There are many organic compounds that fall into this category, with methane, formaldehyde and acetone among the most prevalent and well-known VOCs. These compounds are produced through natural biological processes as well as through chemical reactions in manufacturing and industry. Whether a composition is free or substantially free of VOCs is based upon its vapor pressure.
In an embodiment of the method of making of the adhesive the components listed above are mixed together at ambient temperature. Namely, the polymeric latex, the penetrant, the reinforcing filler, the tackifier, and the stabilizer are mixed together. In another embodiment, either the penetrant or the stabilizer or both may be omitted.
The components may be added sequentially or simultaneously, in the order they are listed above or in a different order. For example, the components may be sequentially added and allowed to slowly rotate in a closed vessel long enough to ensure mixing and good dispersion, such as at least 24 hours.
While the mixing conditions and order of component addition may be varied, care should be taken to maintain the composition in the latex emulsion phase. In this regard, maintaining a solids content of 35-65% and a pH of 9 to 12 throughout the steps of the method is preferred.
The adhesive composition thus formed may be applied to a substrate such as a cured or an uncured rubber composition by, for example, rolling, spraying, or extruding it onto the substrate. After application to an uncured rubber substrate the adhesive and the uncured composition may be then cured under conditions necessary for the substrate to cure. Without being bound by theory, the cure agent and accelerators in the substrate are believed to leach into the adhesive in a sufficient quantity to cause the adhesive to cure also.
The substrates that the adhesive may be utilized to join include elastomeric rubber substrates such as rubber compositions that have as the polymeric component polychloroprene, butyl rubber, hevea and non-hevea natural rubber, polyisoprene, polybutadiene, nitrile rubber, poly(isoprene-styrene), poly(isoprene-butadiene), poly(styrene-butadiene), and combinations thereof. The adhesive may also have some utility for bonding metals, wood, and other types of substrates.
In one example, the application adhesive is applied between rubber layers for air-springs to securely join them at an interface. Within such rubber layers it may contain fibers and/or woven-fabric for reinforcement.
Air springs are widely used in large vehicles, such as buses and trucks, because they allow fixedly holding a vehicle's posture against a load change from curb weight to payload weight by controlling the supply of air and the discharge of air to the exterior. In addition, the spring constant can be set to a low level to improve the ride comfort and prevent the damage of freight.
Typical air spring rubber compositions include one or more diene polymers, such as polychloroprene; a reinforcing filler, such as carbon black, in an amount such as 20-100 phr; a cure agent, accelerators, wax, plasticizing oil, antioxidants, and other additives. An example air spring composition is disclosed in WO 2010/019862, which is incorporated herein by reference.
In tire retreading, the cured tread and the cured tire carcass are joined together by combining a cushion layer. The retreaded tire is then heated in a standard set of conditions to allow for curing to occur. In forming a retreaded tire 300, the adhesive may be applied to join a cushion layer 302 to a retreaded carcass 306 or a cushion layer to a new tread 304, as shown in
Typical tire rubber compositions include one or more diene polymers, reinforcing filler, such as carbon black, in an amount such as 40-100 phr, sulfur (cure agent), accelerators, plasticizing oil, antioxidants, and other additives.
New tires are constructed by assembling the individual components in an uncured (green) state, and then, once assembled, the green tire is cured as a whole. An example tire manufacturing method is disclosed in U.S. Pat. No. 4,824,501, which is incorporated herein by reference.
As the Examples below show, the adhesive described herein is well-suited for use in the manufacture of rubber articles such as tires and air springs.
EXAMPLES Examples 1 and 2The example adhesives were prepared by sequentially mixing the components listed in Table 1 and allowing them to slowly rotate in a closed vessel for at least 24 hours to ensure mixing and good dispersion. The final example adhesives had solids contents in the range of 35-65% and a pH in the range of 9-12.
Examples 3-10 were performed to test the tackiness and the strength/durability of the Example 1 and 2 adhesives in comparison to other adhesives and against a stock to stock control when applied to a neoprene rubber composition. Neoprene rubber is commonly used in air springs.
Examples 3-6 were prepared to measure the uncured (green) peel strength. This measurement primarily shows the tackiness of the joint. This indicates an initial adhesiveness to hold a joint together temporarily until it can be cured.
Examples 7-10 were prepared to measure the cured peel strength, which shows the strength and durability of the final cured joint.
The application of the adhesive onto the green rubber stock was done with a foam/sponge brush, in order to get a thin uniform layer of application. The adhesive was allowed to dry at room temperature for one hour before the uncured samples were tested, and before the cured samples were cured by heating at 171° C. for 11.5 min.
In Examples 3 and 7 no adhesive was applied. In Example 3, two uncured neoprene stocks were applied together in an uncured state. In Example 7 the neoprene stocks were applied together uncured and then later cured. This provides a very strong bond, because the same material is being contacted and cured together. The joint is only slightly weaker than an unjointed piece of rubber, partly because some contaminants may bloom to the surface of the joint and contaminate the curing at the joint. Accordingly, these Examples are considered control examples, not comparative Examples.
Examples 4 and 8 were neoprene rubber strips joined with a hexane solvent-based adhesive made from natural rubber and styrene-butadiene rubber.
Examples 5, 6, 9, and 10 employed the adhesives made in Examples 1 and 2.
Examples 11-18 are analogs to Examples 3-10, only differing in that a different Neoprene rubber was used. The Neoprene rubbers 1 and 2 were copolymers of chloroprene and 2,3-dichloro-1,3-butadiene. Neoprene rubber 1 had a Mooney viscosity of about 100-120, and neoprene rubber 2 had a Mooney viscosity of about 41-51.
The peel strength test strength Examples are summarized in Tables 2 and 3.
In the construction of the uncured adhesion pads that were used in the tack testing of Examples 3-6, the backing pad was secured to the green rubber neoprene stock using superglue (cyanoacrylate). For the cured adhesion pads that were used in Examples 7-10 to determine the strength and durability of the adhesive bond, the backing pad was cured onto the rubber stock without superglue.
In Examples 3-10, the green rubber stock and the backing pad were weighed before any adhesive was applied. For the adhesive application, a foam/sponge brush was used to apply the adhesive in a thin, uniform layer onto each face of the adhesion pad. It was observed that all of the adhesives coated and wetted the rubber well. The pads were weighed again after the adhesive had been applied and dried at room temperature for at least an hour in order to get the weight of the adhesive. The weights of adhesive in each Example were approximately the same. In Examples 7-10, after the pads were assembled, the samples were cured at 171° C. for 11.5-min.
A standard procedure for 180° peel testing on an Instron 4501 was used for all of the Examples 3-10. These Examples were peel tested at a rate of 2 in/min and the gap distance was 127 mm. The cured Examples 15-18 were aged for 5 days before testing. This same test was performed for both uncured (Examples 3-6, 11-14) and cured adhesion (Examples 7-10, 15-18).
Shown in Table 2 are the uncured and cured results for the 180° peel test for Examples 3-10, respectively. Shown in Table 3 are the uncured and cured results for the 180° peel test for Examples 11-18, respectively. In each Figure the higher the average peel strength indicates the better the adhesive performance.
Table 2 and 3 show the uncured tack comparison and the cured adhesive strength comparison. The Example 1 and 2 adhesive formulations demonstrate versatility on different types of air spring rubber, and in either the uncured or cured state. In addition, the water-based adhesives of Examples 1 and 2 reduce the VOC emissions released upon drying in comparison to a traditional solvent-based adhesive.
Example 19The Example 19 adhesive was prepared by sequentially mixing the components listed in Table 4 and allowing them to slowly rotate in a closed vessel for at least 24 hours to ensure mixing and good dispersion. The final adhesive had a solids content in the range of 35-65% and a pH in the range of 9-12.
Examples 20-25 were performed to test the tackiness and the strength/durability of the Example 19 adhesive in comparison to other adhesives and against a stock to stock control when applied to a typical styrene-butadiene and natural rubber blend tire compound that also included carbon and silica, sulfur, and accelerators.
Examples 20-22 were prepared to measure the uncured (green) peel strength, which primarily shows the tackiness of the joint. This indicates an initial adhesiveness to hold a joint together temporarily until it can cure.
Examples 23-25 were prepared to measure the cured peel strength, which shows the strength and durability of the final cured joint.
The application of the adhesive onto the green SBR/NR stock was done with a foam/sponge brush, in order to get a thin uniform layer of application. The adhesive was allowed to dry at room temperature for one hour before the uncured samples were tested, and before the cured samples were cured by heating at 171° C. for 15 min. The amount of adhesive was approximately equal in all Examples.
In Examples 20 and 23 no adhesive was applied. In Example 20, two uncured SBR/NR stocks were applied together in an uncured state, in Example 23 the stocks were applied together uncured and then cured.
Examples 21 and 24 were SBR/NR strips joined with a hexane solvent-based adhesive made from natural rubber and styrene-butadiene rubber.
Examples 22 and 25 employed the adhesive made in Example 19.
The same test method was performed on Examples 20-25 that was performed on Examples 3-18.
Shown in Table 5 are the uncured and then cured results for the 180° peel test for Examples 20-25, respectively. In Table 5 the higher the average peel strength indicates the better adhesive performance.
Table 5 also shows the uncured tack comparison of Examples 20-22 and the cured adhesive strength comparison of Examples 23-25. The Example 19 adhesive formulation tested in Examples 22 and 25 demonstrates excellent performance on SBR/NR in either the cured or uncured state. In addition, the water-based adhesive of Example 19 reduces the VOC emissions released upon drying in comparison to the traditional solvent-based adhesive.
Prospective Examples 26-28Prospective example adhesives incorporating guayule resin may be prepared by sequentially mixing the components listed in Table 6 and allowing them to slowly rotate in a closed vessel to ensure mixing and good dispersion.
In Prospective Examples 26 and 27 a guayule resin may be incorporated as the penetrant.
In Prospective Example 27, a purified form of guayule rubber latex may be used as the latex component of the adhesive.
In Prospective Example 28 guayule latex may be used that includes both the guayule rubber and guayule resin.
The final products in each of Prospective Examples 26-28 would be expected to have a solids content in the range of 35-65% and a pH in the range of 9-12.
It is expected that the prospective water-based adhesive formulations above will have reduced VOC emissions and improved tack and cured adhesion. In particular, these advantages may be useful in tire building applications.
The adhesives in Examples 29 and 30 were prepared by sequentially mixing the components listed in Table 7 and allowing them to slowly rotate in a closed vessel to ensure mixing and good dispersion. The final adhesives had a solids content in the range of 50-60% and a pH in the range of 9.5-11.5. The guayule latex used in Example 30 was in a purified form that included only guayule rubber with little or no guayule resin present.
Example 31 is a comparative example of a solvent based adhesive. A comparison of cured and uncured peel strengths is provided below in Table 8. The peel tests were conducted by applying the adhesives onto uncured (green) and cured styrene-butadiene rubber stock at approximately equal thicknesses. The adhesive was allowed to dry at room temperature for one hour before the uncured samples were tested. The cured samples were prepared by heating the green stocks with the adhesive applied on them at 171° C. for 15 min
To the extent that the term “includes” or “including” is used in the specification or the claims, it is intended to be inclusive in a manner similar to the term “comprising” as that term is interpreted when employed as a transitional word in a claim. Furthermore, to the extent that the term “or” is employed (e.g., A or B) it is intended to mean “A or B or both.” When the applicants intend to indicate “only A or B but not both” then the term “only A or B but not both” will be employed. Thus, use of the term “or” herein is the inclusive, and not the exclusive use. See Bryan A. Garner, A Dictionary of Modern Legal Usage 624 (2d. Ed. 1995). Also, to the extent that the terms “in” or “into” are used in the specification or the claims, it is intended to additionally mean “on” or “onto.” Furthermore, to the extent the term “connect” is used in the specification or claims, it is intended to mean not only “directly connected to,” but also “indirectly connected to” such as connected through another component or components.
While the present application has been illustrated by the description of embodiments thereof, and while the embodiments have been described in considerable detail, it is not the intention of the applicants to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. Therefore, the application, in its broader aspects, is not limited to the specific details, the representative apparatus, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of the applicant's general inventive concept.
Claims
1-20. (canceled)
21. An adhesive comprising:
- a polymeric latex;
- a penetrant selected from the group consisting of: terpenes, limonene, polylimonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof;
- a reinforcing filler;
- wherein the adhesive has a solids content of 35-65% and a pH of 9 to 12.
22. The adhesive of claim 21 wherein the pH of the polymeric latex is within the range of about 7 to about 14.
23. The adhesive of claim 21 wherein the solids content of the polymeric latex is in the range of about 10% to about 90% by weight.
24. The adhesive of claim 21 wherein the reinforcing filler is carbon black and is present in an amount of 10 to 80 phr.
25. The adhesive of claim 21 further comprising a tackifier with a pH of about 2 to about 13 and a solids content of about 30 to about 80.
26. The adhesive of claim 21 wherein the reinforcing filler is carbon black and is selected from the following series: N100, N200, N300, N400, N500, N600, N700, N800, and N900.
27. The adhesive of claim 21 wherein the polymeric latex comprises water and a polymer selected from the group consisting of polychloroprene, butyl rubber, hevea or non-hevea natural rubber, polyisoprene, polybutadiene, nitrile rubber, poly(styrene-butadiene), and combinations thereof.
28. The adhesive of claim 21 wherein the polymeric latex comprises water and a polymer selected from the group consisting of polychloroprene, butyl rubber, hevea or non-hevea natural rubber, polyisoprene, polybutadiene, nitrile rubber, and combinations thereof.
29. The adhesive of claim 21 further comprising a non-ionic surfactant stabilizer.
30. The adhesive of claim 21 wherein the adhesive is substantially or completely free of VOC-containing or eluting solvent.
31. The adhesive of claim 21 wherein the adhesive is substantially or completely free of cure agents.
32. The adhesive of claim 21, wherein the penetrant is guayule resin.
33. An article of manufacture comprising:
- an elastomeric rubber component comprising an elastomer selected from the group consisting of: polychloroprene, butyl rubber, natural rubber, guayule rubber, polyisoprene, polybutadiene, nitrile rubber, poly(styrene-butadiene), and combinations thereof;
- the elastomeric rubber component being joined at an interface with a second rubber component or another portion of the elastomeric rubber component;
- wherein the interface includes a layer of adhesive, the adhesive comprising: a polymeric latex; a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and
- a reinforcing filler.
34. The article of manufacture of claim 33, wherein the article is a rubber air spring or a tire component.
35. The article of manufacture of claim 33, wherein the adhesive has a solids content of 35-65% and a pH of 9 to 12.
36. A method comprising the steps of:
- mixing together an adhesive composition comprising: a polymeric latex; a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, α-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler.
37. The method of claim 36 wherein the reinforcing filler is added as an aqueous dispersion.
38. The method of claim 36 further comprising:
- maintaining a solids content of 35-65% and a pH of 9 to 12 in the composition throughout the steps.
39. The method of claim 36, further comprising the step of applying the adhesive to an uncured rubber composition.
40. The method of claim 36, further comprising applying the adhesive to a tire component or an air spring joint interface.
Type: Application
Filed: Dec 7, 2012
Publication Date: Nov 6, 2014
Inventors: Amy M. Randall (Akron, OH), William L. Hergenrother (Akron, OH), Sheel Agarwal (Solon, OH), Ashley S. Hilton (Massillon, OH)
Application Number: 14/363,230
International Classification: C09J 111/02 (20060101); B32B 25/04 (20060101); C09J 11/08 (20060101); C08K 3/04 (20060101); C08K 5/01 (20060101); C09J 11/06 (20060101); C09J 11/04 (20060101); B32B 7/12 (20060101); C09J 107/02 (20060101);