Forming Charge Trap Separation in a Flash Memory Semiconductor Device

- Spansion LLC

During formation of a charge trap separation in a semiconductor device, a polymer deposition is formed in a reactor using a first chemistry. In a following step, a second chemistry can be used to etch the polymer deposition in the reactor. The same or similar second chemistry can be used in a second etching step to expose a first oxide layer in each of the cells of the semiconductor device and to form a flat upper surface. This additional etch step can also be performed by the reactor, thereby reducing the number of machines required in the formation process.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
BACKGROUND

1. Technical Field

The disclosure generally relates to forming a charge trap separation in a semiconductor device, and specifically to reducing the number of different machines needed to perform the formation process.

2. Related Art

Charge trap semiconductors have become commercially viable for use in flash memory devices. Charge trap semiconductor configurations provide significant advantages over other configurations by allowing multiple bits to be stored in each individual cell. However, the manufacturing of charge trap semiconductors can be somewhat time-consuming and complex.

Conventionally, several different machines are used to construct charge trap semiconductors for flash memories. For example, charge trap layers are grown on top of source/drain regions and field oxide regions of a base substrate using one or more first machines, such as a PECVD furnace. A second machine, such as track equipment, is then used to coat a thin organic material above the charge trap layers in order to fill gaps and planarize the surface of the semiconductor using a coating and/or spinning process. A third machine, such as an etcher, is then used to etch back the organic material and remove the exposed charge trap layers in order to create the separate cells of the final semiconductor device.

The need to move the semiconductor between different machines during the conventional manufacturing process greatly increases manufacturing time. In addition, the movements between different machines increase the likelihood of contaminating the semiconductor wafer, and therefore potentially decreases manufacturing yield.

BRIEF DESCRIPTION OF THE DRAWINGS/FIGURES

Embodiments are described with reference to the accompanying drawings. In the drawings, like reference numbers indicate identical or functionally similar elements. Additionally, the left most digit(s) of a reference number identifies the drawing in which the reference number first appears.

FIGS. 1A-1D illustrate side views of a semiconductor device during manufacturing method steps for forming a charge trap separation according to an embodiment;

FIG. 2 illustrates a flowchart of a method for forming a charge trap separation in a flash memory semiconductor device according to an embodiment; and

FIG. 3 illustrates a block diagram of an apparatus configured to form a charge trap separation in a flash memory semiconductor device according to an embodiment.

DETAILED DESCRIPTION

The following Detailed Description refers to accompanying drawings to illustrate exemplary embodiments consistent with the disclosure. References in the Detailed Description to “one exemplary embodiment,” “an exemplary embodiment,” “an example exemplary embodiment,” etc., indicate that the exemplary embodiment described may include a particular feature, structure, or characteristic, but every exemplary embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same exemplary embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an exemplary embodiment, it is within the knowledge of those skilled in the relevant art(s) to affect such feature, structure, or characteristic in connection with other exemplary embodiments whether or not explicitly described.

The exemplary embodiments described herein are provided for illustrative purposes, and are not limiting. Other exemplary embodiments are possible, and modifications may be made to the exemplary embodiments within the spirit and scope of the disclosure. Therefore, the Detailed Description is not meant to limit the invention. Rather, the scope of the invention is defined only in accordance with the following claims and their equivalents.

Method embodiments may be implemented in hardware (e.g., circuits), firmware, software, or any combination thereof. Method embodiments may also be implemented as instructions stored on a machine-readable medium, which may be read and executed by one or more processors. A machine-readable medium may include any mechanism for storing or transmitting information in a form readable by a machine (e.g., a computing device). For example, a machine-readable medium may include read only memory (ROM); random access memory (RAM); magnetic disk storage media; optical storage media; flash memory devices; electrical, optical, acoustical or other forms of propagated signals (e.g., carrier waves, infrared signals, digital signals, etc.), and others. Further, firmware, software, routines, instructions may be described herein as performing certain actions. However, it should be appreciated that such descriptions are merely for convenience and that such actions in fact results from computing devices, processors, controllers, or other devices executing the firmware, software, routines, instructions, etc. Further, any of the implementation variations may be carried out by a general purpose computer.

The following Detailed Description of the exemplary embodiments will so fully reveal the general nature of the invention that others can, by applying knowledge of those skilled in relevant art(s), readily modify and/or adapt for various applications such exemplary embodiments, without undue experimentation, without departing from the spirit and scope of the disclosure. Therefore, such adaptations and modifications are intended to be within the meaning and plurality of equivalents of the exemplary embodiments based upon the teaching and guidance presented herein. It is to be understood that the phraseology or terminology herein is for the purpose of description and not of limitation, such that the terminology or phraseology of the present specification is to be interpreted by those skilled in relevant art(s) in light of the teachings herein.

Those skilled in the relevant art(s) will recognize that this description may be applicable to many various semiconductor devices, and should not be limited to flash memory devices or any other particular type of semiconductor devices.

An Exemplary Semiconductor Device

FIG. 1A illustrates a side view of an exemplary semiconductor device 100 prior to charge trap separation according to an embodiment.

The semiconductor device 100 includes a bulk semiconductor substrate 110 that includes a plurality of source/drain regions 115 extending vertically from a base of the substrate 110. Adjacent vertically-extending source/drain regions 115 define isolation trenches 120 therebetween.

Charge trap layers 150 are formed over a top surface of the substrate 110. The charge trap layers 150 include a first oxide layer 152 that extends into the isolation trenches 120, and which covers a top surface of the substrate 110. The first oxide layer 152 includes substantially rectangular protrusions 153 that extend above the isolation trenches 120. The charge trap layers 150 further include a silicon rich nitride layer 154 uniformly formed over the first oxide layer 152, as well as a second oxide layer 156 uniformly formed over the silicon rich nitride layer 154.

The combined first oxide layer 152, silicon rich nitride layer 154 and second oxide layer 156 define cells 170 at each of the rectangular protrusions 153. Adjacent cells 170 are separated from one another by, and together define, cell separation gaps 175.

FIG. 1B illustrates a side view of the semiconductor device 100 after a subsequent step in an exemplary charge trap separation formation method, according to an embodiment.

In an embodiment, in this step, the semiconductor device 100 is placed in a reactor. In an embodiment, the reactor is a plasma reactor. The reactor is used to grow a polymer deposition 160 over a top surface of the semiconductor device 100, and specifically over the second oxide layer 156 of the charge trap layers 150.

The polymer deposition 160 is formed so as to at least substantially fill the cell separation gaps 175. Particularly, the polymer deposition 160 may be formed within the cell separation gaps 175 sufficiently high such that a future etching step (see FIG. 1D) leaves cell separation gaps 175 completely filled with the polymer deposition 160. Therefore, in an embodiment, in order to ensure sufficient polymer deposition 160, the polymer deposition 160 is formed so as to at least completely fill the cell separation gaps 175.

In an embodiment, in order to grow the polymer deposition 160 on the semiconductor device 100, the reactor employs a chemistry (e.g., a “grow chemistry”) selected from a plurality of hydrocarbon gases and/or fluorocarbon gases. Such chemistries may include, for example, HBr, CH4, CH3F and CH2F2. Other viable chemistries may include CxHyFz, where x, y, and z are each positive integers.

FIG. 1C illustrates a side view of the semiconductor device 100 after a subsequent step in the exemplary charge trap separation formation method, according to an embodiment.

According to an embodiment, in this step, using the same reactor, the semiconductor device 100 is etched using a different chemistry. For example, in this step the chemistry in the reactor is changed to an etch chemistry, such as a CF4/O2 mixture. With this new etch chemistry, the reactor etches away outer portions of the polymer deposition 160 in order to expose the upper edges of the charge trap layers 150.

In an embodiment, this etching step etches the polymer deposition 160 below the top surface of the charge trap layers 150, provided that the polymer deposition 160 still sufficiently fills the cell separation gaps 175 so as to completely fill those gaps 175 after a second subsequent etch (see FIG. 1D).

FIG. 1D illustrates a side view of the semiconductor device 100 after a subsequent step in the exemplary charge trap separation formation method, according to an embodiment.

In an embodiment, using the same reactor, the semiconductor device 100 is further etched in order to expose upper edges of the first oxide layer 152. In order to expose the first oxide layer 152, the reactor etches the polymer deposition 160 together with a portion of the second oxide layer 156 and silicon nitride layer 154 over each of the cells 170. By performing the first etch (FIG. 1C) to maintain the polymer deposition 160 in the cell separation gaps 175, the polymer deposition 160 protects the active regions of the semiconductor device 100 during this second etch.

As a result of this second etch, the semiconductor device 100 includes a plurality of separate cells 170 separated from each other by the polymer deposition 160 filled into the cell separation gaps 175. In addition, the semiconductor device 100 maintains a substantially flat upper surface as a result of the second etch.

By forming the charge trap separation in the manner described above, only a single machine is required for the growing and etching steps. This substantially reduces manufacturing costs, time and complexity. In addition, by maintaining the semiconductor device 100 in a single machine throughout the charge trap separation formation process, the likelihood of contracting contaminants is reduced. Consequently, manufacturing yield and efficiency can be improved over conventional methods.

Exemplary Method for Forming Charge Trap Separation in a Semiconductor Device

FIG. 2 illustrates a flowchart diagram 200 of a method for forming a charge trap separation in a flash memory semiconductor device according to an embodiment. For illustration purposes, flowchart 200 is described with continued reference to FIGS. 1A-1D, although the method 200 is not limited to the example.

In step 210, referring to FIG. 1A, charge trap layers 150 are formed over a top surface of a substrate 110. The charge trap layers 150 include a first oxide layer 152 that extends into isolation trenches 120 defined by vertically-extending source/drain regions 115 of the substrate 110. The first oxide layer 152 includes substantially rectangular protrusions 153 that extend above the isolation trenches 120. The charge trap layers 150 further include a silicon rich nitride layer 154 uniformly formed over the first oxide layer 152, as well as a second oxide layer 156 uniformly formed over the silicon rich nitride layer 154.

In step 220, referring to FIG. 1B, in a reactor, a polymer deposition 160 is formed on a top surface of the semiconductor device 100. The polymer deposition 160 can be formed using a formation chemistry using hydrocarbon gases and/or fluorocarbon gases, such as those described above, although the method 200 is not limited to such examples. The polymer deposition 160 is formed so as to at least substantially fill cell separation gaps 175 defined by adjacent cells 170 of the semiconductor device 100.

In step 230, referring to FIG. 1C, in the same reactor, the polymer deposition 160 is etched using an etch chemistry. The etch chemistry may include a mixture of CF4 and O2 (although the method 200 is not limited to these examples), and should etch the polymer deposition 160 to expose a top surface of the charge trap layers 150 without significantly removing the polymer deposition 160 from the cell separation gaps 175.

In step 240, referring to FIG. 1D, in the same reactor, the upper surface of the semiconductor 100 is etched using the etch chemistry. This second etch removes portions of the second oxide layer 156 and portions of the silicon rich nitride layer 154 so as to expose the first oxide layer 152 at each of the cells 170 of the semiconductor device 100. In addition, the second etch removes portions of the polymer deposition 160 so as to maintain a substantially flat top surface in the resulting semiconductor device 100. In an embodiment, the reactor is a plasma reactor. Also, in certain embodiments, more than one device (reactors) may be used to perform these steps of flowchart 200.

Those skilled in the relevant art(s) will recognize that the above method can additionally or alternatively include any of the steps or substeps described above with respect to FIGS. 1A-1D, as well as any of their modifications. Further, the above description of the exemplary method should not be construed to limit the description of the method depicted in FIGS. 1A-1D.

Exemplary Apparatus for Forming Charge Trap Separation in a Semiconductor Device

FIG. 3 illustrates a block diagram of an exemplary apparatus 300 for forming charge trap separation in a semiconductor device. The apparatus includes a deposition module 310, a first etching module 320 and a second etching module 330. For illustration purposes, the apparatus 300 is described with continued reference to FIGS. 1A-1D.

The apparatus 300 forms charge trap separation in a semiconductor device 100 having charge trap layers 150 formed over a top surface of a substrate 110, as shown for example in FIG. 1A. The charge trap layers 150 include a first oxide layer 152 that extends into isolation trenches 120 defined by vertically-extending source/drain regions 115 of the substrate 110. The first oxide layer 152 includes substantially rectangular protrusions 153 that extend above the isolation trenches 120. The charge trap layers 150 further include a silicon rich nitride layer 154 uniformly formed over the first oxide layer 152, as well as a second oxide layer 156 uniformly formed over the silicon rich nitride layer 154.

The deposition module 310 is configured to form a polymer deposition 160 on a top surface of the semiconductor device 100, as shown for example in FIG. 1B. The polymer deposition 160 can be formed using a formation chemistry using for example and without limitation hydrocarbon gases and/or fluorocarbon gases, such as those described above. The polymer deposition 160 is formed so as to at least substantially fill cell separation gaps 175 defined by adjacent cells 170 of the semiconductor device 100.

The first etching module 320 is configured to etch the polymer deposition 160 using an etch chemistry, as shown for example in FIG. 1C. The etch chemistry may include, but is not limited to, a mixture of CF4 and O2, and should etch the polymer deposition 160 to expose a top surface of the charge trap layers 150 without significantly removing the polymer deposition 160 from the cell separation gaps 175.

The second etching module 330 is configured to etch the upper surface of the semiconductor 100 using the etch chemistry, as shown for example in FIG. 1D. This second etch removes portions of the second oxide layer 156 and portions of the silicon rich nitride layer 154 so as to expose the first oxide layer 152 at each of the cells 170 of the semiconductor device 100. In addition, the second etch removes portions of the polymer deposition 160 so as to maintain a substantially flat top surface in the resulting semiconductor device 100. In an embodiment, the apparatus 300 is a plasma reactor.

Those skilled in the relevant art(s) will recognize that the above method can additionally or alternatively include any of the steps or substeps described above with respect to FIGS. 1A-1D, as well as any of their modifications. Further, the above description of the exemplary method should not be construed to limit the description of the method depicted in FIGS. 1A-1D.

CONCLUSION

It is to be appreciated that the Detailed Description section, and not the Abstract section, is intended to be used to interpret the claims. The Abstract section may set forth one or more, but not all exemplary embodiments, and thus, is not intended to limit the disclosure and the appended claims in any way.

The invention has been described above with the aid of functional building blocks illustrating the implementation of specified functions and relationships thereof. The boundaries of these functional building blocks have been arbitrarily defined herein for the convenience of the description. Alternate boundaries may be defined so long as the specified functions and relationships thereof are appropriately performed.

It will be apparent to those skilled in the relevant art(s) that various changes in form and detail can be made therein without departing from the spirit and scope of the disclosure. Thus, the invention should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims and their equivalents.

Claims

1-13. (canceled)

14. An apparatus for forming charge trap separation in a semiconductor device, the semiconductor device having a charge trap layer formed on a substrate, the apparatus comprising:

a deposition module configured to grow a polymer deposition on the charge trap layer so as to fill cell separation gaps between adjacent cells of the charge trap layer;
a first etching module configured to etch the polymer deposition to expose the charge trap layer such that an upper surface of the polymer deposition is lower than an upper surface of the charge trap layer; and
a second etching module configured to etch the polymer deposition over the cells and within the cell separation gaps together with the charge trap layer so as to expose a bottom portion of the charge trap layer within the cells and form a uniform upper surface among the cells and the cell separation gaps.

15. The apparatus of claim 14, wherein the deposition module is configured to grow the polymer deposition using a grow chemistry, and

wherein at least one of the first etching module and the second etching module is configured to etch using an etch chemistry that is different from the grow chemistry.

16. The apparatus of claim 15, wherein the first etching module and the second etching module are both configured to etch using the etch chemistry.

17. The apparatus of claim 15, wherein the grow chemistry includes at least one of a hydrocarbon gas and a fluorocarbon gas.

18. The apparatus of claim 15, wherein the etch chemistry includes a mixture of CF4 and O2.

19. (canceled)

20. The apparatus of claim 14, wherein the first etching module is configured to remove a portion of the polymer deposition from within the cell separation gaps.

Patent History
Publication number: 20150162226
Type: Application
Filed: Feb 19, 2015
Publication Date: Jun 11, 2015
Applicant: Spansion LLC (Sunnyvale, CA)
Inventor: Angela Tai HUI (Fremont, CA)
Application Number: 14/626,815
Classifications
International Classification: H01L 21/67 (20060101);