METHOD FOR FORMING CONDUCTIVE PATTERN BY DIRECT RADIATION OF ELECTROMAGNETIC WAVE, AND RESIN STRUCTURE HAVING CONDUCTIVE PATTERN THEREON
Provided are a method for forming conductive pattern by direct radiation of an electromagnetic wave capable of forming fine conductive patterns on various kinds of polymer resin products or resin layers under a relatively low power by a simplified process, even without containing specific inorganic additives in the polymer resin itself, and a resin structure having the conductive pattern formed thereon. The method for forming the conductive pattern by direct radiation of the electromagnetic wave includes: forming a first region having a predetermined surface roughness by selectively radiating the electromagnetic wave on a polymer resin substrate containing carbon-based black pigment; forming a conductive seed on the polymer resin substrate; forming a metal layer by plating the polymer resin substrate having the conductive seed formed thereon; and removing the conductive seed and the metal layer from a second region of the polymer resin substrate, wherein the second region has surface roughness smaller than that of the first region.
The present invention relates to a method for forming conductive pattern by direct radiation of a relatively low power electromagnetic wave capable of forming fine conductive patterns on various kinds of polymer resin products or resin layers by a simplified process, even without containing specific inorganic additives in the polymer resin itself, and a resin structure having the conductive pattern formed thereon.
BACKGROUND ARTIn recent years, as a fine electronic technology is developed, demand for a structure in which fine conductive patterns are formed on a surface of polymer resin substrates (or products) of various kinds of resin products or resin layers, and the like has been increased. The conductive patterns on the surface of the polymer resin substrate and the structure may be applied to form various targets such as antennas integrated into a cellular phone case, various kinds of sensors, MEMS structures, RFID tags, and the like.
In particular, recent portable devices such as a smart phone, and the like, need to have simultaneously mounted local area network functions such as communication, bluetooth, Wi-Fi, electronic payment, and the like, unlike the existing cellular phone, and the like, and due to this reason, it is required to simultaneously mount various antennas in one smart phone. However, since aesthetic design aspect of the portable devices such as the smart phone, and the like, in addition thereto, is emphasized, a method for forming conductive pattern capable of serving as various antennas on the surface of the polymer resin substrate such as the case of the portable devices, and the like, has been continuously suggested and researched so as to simultaneously meet these demands.
As the interest in the technology of forming conductive patterns on the surface of the polymer resin substrate has been increased, several technologies regarding this were suggested. For example, a method of forming conductive patterns on a polymer resin substrate by blending and molding specific inorganic additives containing transition metals such as copper, chromium, or the like, (for example, CuCr2O4, and the like, in a spinel structure) in a polymer resin chip to form a polymer resin substrate, directly radiating an electromagnetic wave such as a laser, and the like, on a predetermined region, and plating the laser radiated region to form a metal layer was suggested. In this method, the inorganic additive-derived components in the laser radiated region are exposed and function as a seed for a kind of plating, such that the metal layer and conductive patterns may be formed.
However, since a substantial amount of high priced and specific inorganic additives should be used in the method of forming the conductive patterns, there is a disadvantage in that the total manufacturing cost is increased. In addition, since the inorganic additive needs to be blended into the polymer resin chip itself, the inorganic additive may deteriorate physical properties such as mechanical properties, dielectric constant, and the like, of the polymer resin substrate or resin products formed therefrom, or may cause dielectric loss. Further, the specific inorganic additives such as CuCr2O4 having the spinel structure, and the like, have own unique colors, and these colors are not complete black color or white color, such that the specific inorganic additives may be deteriorating factors in implementing the polymer resin substrates or the resin products containing the specific inorganic additives, with black color, white color or other various colors desirable to consumers.
Due to the disadvantages, a technology capable of forming fine conductive patterns by a simplified process on various kinds of the polymer resin products or the resin layers without containing the specific inorganic additives in the polymer resin itself has been demanded. However, in the case of simply omitting the adding of the specific inorganic additives, since the electromagnetic wave needs to be radiated by relatively strong power, the manufacturing cost may be rather increased, physical properties of the polymer resin product itself may be deteriorated, and there is a technical difficulty in that it is difficult to satisfactorily form fine conductive patterns.
SUMMARY OF INVENTION Technical ProblemThe present invention has been made in an effort to provide a method for forming conductive pattern by direct radiation of a relatively low power electromagnetic wave capable of forming fine conductive patterns on various kinds of polymer resin products or resin layers by a simplified process, even without containing specific inorganic additives in the polymer resin itself.
In addition, the present invention has been made in an effort to provide a resin structure having the conductive pattern obtained by the method for forming the conductive pattern.
Solution to ProblemAn exemplary embodiment of the present invention provides a method for forming conductive pattern by direct radiation of an electromagnetic wave, the method including: forming a first region having a predetermined surface roughness by selectively radiating the electromagnetic wave on a polymer resin substrate containing carbon-based black pigment; forming a conductive seed on the polymer resin substrate; forming a metal layer by plating the polymer resin substrate having the conductive seed formed thereon; and removing the conductive seed and the metal layer from a second region of the polymer resin substrate, wherein the second region has surface roughness smaller than that of the first region.
The first region of the polymer resin substrate may have surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of about 1 μm or more, and the second region may have a center line arithmetic average roughness of the absolute values (Ra) smaller than that of the first region.
Another exemplary embodiment of the present invention provides a resin structure having conductive pattern including: a polymer resin substrate divided into a first region formed to have surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of about 1 μm or more and a second region having surface roughness smaller than that of the first region, and containing carbon-based black pigment; and a conductive seed and a metal layer selectively formed on the first region of the polymer resin substrate.
Advantageous Effects of InventionAccording to the present invention, even though high priced and specific inorganic additives such as CuCr2O4 having a spinel structure, and the like, are not contained in a polymer resin substrate itself, surface roughness and adhesion to a metal layer, of a region in which conductive patterns are formed by radiating an electromagnetic wave such as laser, or the like, may be adjusted, such that the conductive patterns may be formed on the polymer resin substrate by a simplified process.
In particular, since the process is performed in a state in which carbon-based black pigments showing excellent absorption rate to the electromagnetic wave such as laser, or the like, for example, carbon black which is a low-priced general pigment, and the like, are added, fine conductive patterns may be satisfactorily formed on the polymer resin substrate even under radiation condition of the relatively low power electromagnetic wave.
Therefore, the manufacturing cost of the process of forming the conductive patterns may be decreased, and deterioration of physical properties such as mechanical properties, and the like, of the polymer resin substrate or products caused by the specific inorganic additive, a high power electromagnetic wave radiation, or the like, may be minimized. In addition, since the carbon-based black pigment itself shows a black color which is desirable to consumer, it is significantly easy to obtain black-colored resin products, and the like.
As a result, by using the method for forming the conductive pattern, conductive patterns for antenna, RFID tags, various kinds of sensors, MEMS structures, and the like, may be significantly effectively formed on various kinds of resin products such as a smart phone case, and the like.
Hereinafter, a method for forming conductive pattern by direct radiation of an electromagnetic wave according to a specific exemplary embodiment of the present invention, and a resin structure having the conductive pattern formed therefrom will be described.
According to an exemplary embodiment of the present invention, the method for forming conductive pattern by direct radiation of an electromagnetic wave includes: forming a first region having a predetermined surface roughness by selectively radiating the electromagnetic wave on a polymer resin substrate containing carbon-based black pigment; forming a conductive seed on the polymer resin substrate; forming a metal layer by plating the polymer resin substrate having the conductive seed formed thereon; and removing the conductive seed and the metal layer from a second region of the polymer resin substrate, wherein the second region has surface roughness smaller than that of the first region.
According to the exemplary embodiment of the present invention, first, a surface structure having a shape such as concavo-convex, patterns, amorphous shape, or the like, is formed so that a polymer resin substrate of the first region has a predetermined surface roughness by radiating an electromagnetic wave such as laser, or the like, on a first region in which the conductive patterns are formed. In the first region, adhesion between a surface of the polymer resin substrate and a metal layer to be formed by plating in the first region may be improved due to the predetermined surface roughness.
Meanwhile, in a second region which is not radiated by the electromagnetic wave such as laser, or the like, poor adhesion between the surface of the polymer resin substrate and the metal layer in the second region may be shown due to original surface property of the polymer resin substrate itself.
Here, the process of radiating the electromagnetic wave is performed in a state in which carbon-based black pigments showing excellent absorption rate to the electromagnetic wave such as laser, or the like, for example, carbon black which is a low-priced general pigment, and the like, are added, such that surface roughness at desired level may be formed in the first region and adhesion between the polymer resin substrate surface and the metal layer may be improved to desired level, even under radiation condition of a relatively low power electromagnetic wave.
Accordingly, when a conductive seed for facilitating a plating process is formed on the polymer resin substrate of the first region and the plating process is performed, the metal layer having excellent adhesion with the polymer resin substrate may be favorably formed in the first region; meanwhile, the metal layer which is easily removed due to poor adhesion may be formed in the second region. Therefore, when weak physical power is applied to the polymer resin substrate to selectively remove the metal layer and the conductive seed of the second region, desired conductive patterns may be easily formed on the polymer resin substrate.
As described above, according to an exemplary embodiment of the present invention, for example, even though high priced specific inorganic additives such as CuCr2O4, and the like, having the spinel structure are not contained in the polymer resin substrate itself, surface roughness, adhesion, and the like, of the region in which the conductive patterns are formed by radiating the electromagnetic wave such as laser, or the like, may be adjusted, such that the conductive patterns may be formed on the polymer resin substrate by a simplified process. In addition, by using the carbon-based black pigment as described above, fine conductive patterns may be satisfactorily formed on the polymer resin substrate even under radiation condition of a low power electromagnetic wave.
Therefore, the manufacturing cost of the process of forming the conductive patterns may be decreased, and deterioration of physical properties such as mechanical properties, and the like, of the polymer resin substrate or products caused by the specific inorganic additive, may be minimized. In addition, since the carbon-based black pigment itself shows a black color which is desirable to consumer, it is significantly easy to obtain black colored resin products, and the like.
Meanwhile, hereinafter, the method for forming the conductive pattern by direct radiation of an electromagnetic wave according to an exemplary embodiment of the present invention is more specifically described for each process step with reference to drawings.
As shown in
Here, the polymer resin substrate may include without specific limitation any thermosetting resin or any thermoplastic resin capable of forming various polymer resin products or resin layers. Specific examples of the polymer resin capable of forming the polymer resin substrate may include a polyalkylene terephthalate resin such as an ABS resin, a polybutylene terephthalate resin, a polyethylene terephthalate resin, or the like, a polycarbonate resin, a polypropylene resin, a polyphthalamide resin, and the like, and in addition thereto, the polymer resin substrate may be formed by using various polymer resins.
In addition, the polymer resin substrate contains the carbon-based black pigment to increase absorption rate to the electromagnetic wave such as laser or the like, so as to form the first region having a predetermined surface roughness even under an radiation condition of a low power electromagnetic wave.
As the carbon-based black pigment, any pigment components including carbon-based components as a major component, having high absorption rate to the laser, and the like, and showing color close to black color may be used. Specific examples thereof may be at least one kind selected from the group consisting of carbon black, pine black soot, soot, lamp black, channel black, furnace black, and acetylene black.
In addition, the carbon-based black pigment may be contained in an amount of about 0.01 to 10 wt %, or about 0.1 to 5 wt %, or about 0.2 to 1 wt % based on the weight of the polymer resin substrate. Accordingly, the polymer resin substrate may have excellent absorption rate to the electromagnetic wave, such that the first region having a predetermined surface roughness may be formed even under the radiation condition of a low power electromagnetic wave. In addition, an increase in the manufacturing cost caused by addition of separate additives, or deterioration of physical properties of the polymer resin substrate may be reduced.
Further, it is preferred that the carbon-based black pigment have a particle state having a particle diameter of about 10 nm to 1 μm, or about 20 nm to 200 nm, so as to have appropriate level of absorption rate to an electromagnetic wave in the polymer resin substrate, and to more reduce the deterioration of physical properties of the polymer resin substrate.
Meanwhile, additives which are generally used to form the polymer resin products, for example, an UV stabilizer, a heat stabilizer, an impact reinforcing agent, and the like, may be further added or included in the polymer resin substrate as needed, in addition to the above-described carbon-based black pigment. The additives may be contained in an appropriate amount of about 2 wt % or less, or about 0.05 to 2.0 wt %, based on the weight of the total polymer resin substrate. Meanwhile, the polymer resin substrate does not have to include the specific inorganic additives such as CuCr2O4 having a spinel structure, and the like, used to form the conductive patterns by radiating the electromagnetic wave which are known in the art.
In addition, the first region has a predetermined surface roughness by radiating laser on the above-described polymer resin substrate, wherein in the first region having the surface roughness, relatively standardized patterns such as hole, mesh pattern, and the like, or concavo-convex shapes may be formed, or amorphous surface structure in which a plurality of irregular holes, patterns, or concavo-convex are complexly formed may be formed, and the polymer resin substrate of the first region may have a predetermined surface roughness due to the various surface shapes or structures. Meanwhile, in order to secure excellent adhesion between the metal layer (conductive patterns) to be formed on the first region and the surface of the polymer resin substrate, the polymer resin substrate of the first region may have a predetermined level or more of surface roughness by radiating an electromagnetic wave such as laser, or the like.
As an example, the first region of the polymer resin substrate may have surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of about 1 μm or more, or about 1 to 10 μm, or about 1 to 6 μm, or about 1 to 3 μm, and the second region which is not radiated by the electromagnetic wave may have surface roughness defined by a central line surface roughness (Ra) smaller than that of the first region, for example, about 400 nm or less, or about 300 nm or less, or about 0 to 300 nm, or about 50 to 250 nm.
In addition, in another example, the surface roughness of the first and second regions may also be defined by degree of adhesion to the metal layer measured in a cross-cut test according to ISO 2409 standard method. For example, when a cross-cut test having an interval of 2 mm or less according to ISO 2409 standard method is conducted by using a tape having adhesion of about 4.0 to 6.0N/10 mm width, the first region of the polymer resin substrate may have surface roughness defined by adhesion (for example, ISO class 0 or 1) at which a delamination area of a target metal layer under test corresponds to about 5% or less of an area of the metal layer, and when a cross-cut test having an interval of 2 mm or less according to ISO 2409 standard method is conducted by using a tape having adhesion of about 4.0 to 6.0N/10 mm width, the second region of the polymer resin substrate may have surface roughness defined by adhesion (for example, ISO class 5 or more) at which a delamination area of a target metal layer under test corresponds to about 65% or more of an area of the metal layer.
As the polymer resin substrate of the first region has the above-described surface roughness by radiating the electromagnetic wave such as laser, or the like, when the metal layer is formed on the first region in the following plating process, the metal layer may be formed and maintained on the polymer resin substrate with excellent adhesion, to form excellent conductive patterns. As compared to the first region, as the polymer resin substrate of the second region which is not radiated by an electromagnetic wave such as laser, or the like, has the above-described surface roughness due to surface property of the substrate, when the metal layer is formed on the following plating process, the metal layer may be easily removed due to significantly low adhesion from the second region. As a result, the metal layer of the second region may be easily and selectively removed to form the conductive patterns on the polymer resin substrate of the first region.
Meanwhile, an electromagnetic wave such as laser, or the like, may be radiated under predetermined conditions as described below so that the polymer resin substrate of the first region has the above-described surface roughness.
First, in the radiating of the electromagnetic wave, laser electromagnetic wave may be radiated, for example, laser electromagnetic wave having a wavelength of about 248 nm, about 308 nm, about 355 nm, about 532 nm, about 585 nm, about 755 nm, about 1064 nm, about 1070 nm, about 1550 nm, about 2940 nm or about 10600 nm may be radiated. In another example, laser electromagnetic wave having a wavelength in infrared ray (IR) region may be radiated.
In addition, specific conditions at the time of radiating laser electromagnetic wave may be controlled or changed depending on kinds of the resin, physical properties, thickness, of the polymer resin substrate, kinds or thickness of the metal layer to be formed, or appropriate level of adhesion in consideration of the above-mentioned factors. Meanwhile, the laser electromagnetic wave may be radiated under condition that an average power is about 2 W or more, or about 2 to 20 W, or about 3 to 10 W, so that the polymer resin substrate of the first region has a predetermined surface roughness as described above. As described above, since the carbon-based black pigment having high absorption rate to the electromagnetic wave, and the like, are contained in the polymer resin substrate, the first region having appropriate surface roughness may be formed even under a low power condition, and the metal layer to be formed later may have excellent adhesion to the polymer resin substrate of the first region.
In addition, the laser electromagnetic wave may be radiated once by a relatively high power, but the laser electromagnetic wave may also be radiated two or more times by a relatively low power. As the number of radiating the laser electromagnetic wave is increased, the surface roughness is increased, structures such as concavo-convex, and the like, formed on the surface may be changed from hole shaped patterns to mesh pattern, amorphous surface structures or the like. Therefore, by controlling the condition and the number of radiating laser electromagnetic wave, appropriate surface structure may be formed on the polymer resin substrate of the first region, and the surface roughness having an appropriate degree and excellent adhesion to the metal layer may be provided.
Further, at the time of radiating laser electromagnetic wave, radiation trace of the electromagnetic wave may be formed in a hole shape or the like on the polymer resin substrate depending on an radiation interval. However, in order that the polymer resin substrate of the first region has the above-mentioned appropriate surface roughness, it is preferred that the laser electromagnetic wave be radiated so that an interval between central parts of radiation trace of the electromagnetic wave, or an radiation interval of the electromagnetic wave is about 20 μm or more, or about 20 to 70 μm, but is not particularly limited thereto. As a result, the polymer resin substrate of the first region may have appropriate surface roughness and appropriate adhesion with the metal layer, and deterioration of physical properties or the like of the polymer resin substrate may be decreased.
Meanwhile, as described above, after radiating the electromagnetic wave such as laser, or the like, on the first region, a conductive seed may be formed on the polymer resin substrate as shown in
The conductive seed may contain metal nanoparticles, metal ions, or metal complex ions. In addition, the metal ion or the metal complex ion may be used as ion itself or as metal-containing compounds to which the metal ions are coupled or as metal complexes containing metal complex ions, or even as particles of the metal-containing compounds or the metal complexes.
The kind of the metal atoms which may be included in the conductive seed is not particularly limited as long as the metal atom has conductivity. For example, the conductive seed may contain at least one kind metal selected from the group consisting of copper (Cu), platinum (Pt), palladium (Pd), silver (Ag), gold (Au), nickel (Ni), tungsten (W), titanium (Ti), chromium (Cr), aluminum (Al), zinc (Zn), tin (Sn), lead (Pb), magnesium (Mg), manganese (Mn) and iron (Fe), ions or complex ions thereof.
In addition, in order to form the conductive seed on the polymer resin substrate, a dispersion liquid or solution containing the above-mentioned conductive seed such as the metal nanoparticles, the metal ions, or the metal complex ions may be applied on the polymer resin substrate, followed by a precipitating method, a drying method, and/or a reducing method, to thereby form the conductive seed in a desirable form, for example, a particle form. More specifically, when the dispersion liquid, or the like, contains the metal nanoparticles, the metal nanoparticles are precipitated by difference in solubility and dried to appropriately form the conductive seed in a particle form, and when the dispersion liquid, or the like, contains the metal ions, or the metal complex ions (or the metal compounds or the complexes containing these ions), the metal ions, or the metal complex ions are reduced and dried to appropriately form the conductive seed in a particle form.
Here, the reducing of the metal ion or the metal complex ion may be performed by using general reducing agents, for example, at least one kind reducing agent selected from the group consisting of an alcohol-based reducing agent, an aldehyde-based reducing agent, hypophosphite-based reducing agent such as hypophosphorous acid sodium or hydrates thereof, or the like, hydrazine-based reducing agent such as hydrazine or hydrates thereof, or the like, sodium borohydride and lithium aluminum hydride.
In addition, the dispersion liquid or the solution may appropriately include an aqueous-based polymer solution capable of improving close adhesion between the polymer resin substrate and the conductive seed, or an aqueous-based complexing agent capable of stabilizing the metal ions or the metal complex ions, as a liquid-phase medium.
Further, the dispersion liquid or the solution of the conductive seed may be applied by general processes for applying a liquid-phase composition to the polymer resin substrate, for example, methods such as dipping, spin coating, spraying, or the like.
The conductive seed formed as described above may be formed on the entire surface of the polymer resin substrate including space between the surface concavo-convex, patterns, or surface structures formed on the first region, and may serve to promote favorable formation of the metal layer in the plating process and to control plating rate, physical properties of the metal layer.
Meanwhile, right after the radiating of the electromagnetic wave as described above, the process of forming the conductive seed may be immediately performed; however, after the polymer resin substrate is selectively surface-treated with a surfactant having surface tension lower than that of the dispersion liquid or solution, the process of forming the conductive seed may be performed. In addition, the polymer resin substrate may be surface-treated in a state in which the surfactant is added to the dispersion liquid or the solution itself for forming the conductive seed.
The surfactant may allow the conductive seed to be more uniformly formed and maintained on the surface of the polymer resin substrate, in particular, between the surface concavo-convex, patterns, or surface structures. The reason is because the surfactant removes air between the surface structures to assist the conductive seed in being easily permeated between the surface structures. Therefore, when the treatment with the surfactant is added, the conductive seed is favorably adsorbed entirely onto the first region, and the metal layer may be more uniformly and favorably formed by the plating process. In addition, due to the treatment with the surfactant and the formation of the conductive seed, adhesion between the metal layer and the polymer resin substrate on the first region may be more improved to favorably form the conductive patterns having excellent conductivity.
Kinds of the surfactant may differ depending on kinds of the dispersion liquid or the solution of the conductive seed as described above, and may include any liquid phase medium having surface tension lower than that of the dispersion liquid or the solution. For example, organic solvents such as ethanol, and the like, having relatively low surface tension may be used as the surfactant.
In addition, the surfactant may be treated by a method of immersing the polymer resin substrate for several seconds to several minutes, and the like.
Meanwhile, referring to
For example, the plating process is performed by using a plating solution containing conductive metals forming the metal layer, for example, metal sources such as copper, and the like, complexing agents, pH adjustors, reducing agent, and the like, to form the metal layer on the polymer resin substrate including the first region and the second region. Here, the metal layer may be formed on the grown conductive seed as described above.
The metal layer may be favorably formed on the first region by excellent adhesion; meanwhile, the metal layer may be easily removed from the second region due to poor adhesion to the polymer resin substrate.
After the metal layer is formed, the conductive seed and the metal layer may be selectively removed from the second region of the polymer resin substrate to form the conductive patterns on the remaining first region.
As described above, since the metal layer is formed on the second region in a state in which it is significantly easy to remove the metal layer, the metal layer and the conductive seed may be selectively removed from the second region by simple methods such as applying weak physical power to the polymer resin substrate, and the like. Here, due to excellent adhesion between the metal layer and the polymer resin substrate on the first region, the metal layer may remain to form the conductive patterns.
As described above, the process of removing the conductive seed and the metal layer from the second region, may be performed by any method of applying weak physical power onto the polymer resin substrate such as ultrasonic radiation (sonication), liquid phase washing, liquid phase rinsing, air blowing, taping, brushing, or methods of using a manpower such as directly dusting or wiping with hands, or by a combination of two or more methods selected therefrom.
For example, washing or rinsing is performed in deionized water under the ultrasonic radiation for a predetermined time, and air blowing, and the like, are performed, such that the conductive seed and the metal layer of the second region may be selectively removed.
The resin structure having the conductive pattern formed by the above-described method may include the polymer resin substrate divided into the first region formed to have surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of about 1 μm or more and the second region having surface roughness smaller than that of the first region, containing carbon-based black pigment; and the conductive seed and the metal layer selectively formed on the first region of the polymer resin substrate.
Here, since the surface roughness of the first and second regions is sufficiently described in the method according to an exemplary embodiment, additional description thereof will be omitted. In addition, as described above, the first region may correspond to a region in which the electromagnetic wave such as laser, or the like, is radiated.
In this resin structure, even after radiating the electromagnetic wave such as laser, or the like, the carbon-based black pigment only serves to improve absorption rate of the electromagnetic wave radiation, but is not destroyed by the electromagnetic wave radiation or does not form metal nucleus, and the like, derived from the radiation, which is different from the specific inorganic additives such as CuCr2O4 having a spinel structure, and the like, used in the related art. Further, the resin structure does not include the specific inorganic additive such as CuCr2O4, and the like.
As a result, in the structure, the polymer resin substrate of the second region (or the first region before radiating laser) may show XRD pattern not including peaks derived from the specific inorganic additives, for example, conductive transition metal such as copper or silver, or metal compounds containing the conductive transition metal. One example of the XRD pattern is shown in
Meanwhile, the resin structure as described above may be various kinds of resin products or resin layers such as a smart phone case, and the like, having conductive patterns for antenna, or may be various kinds of resin products or resin layers having conductive patterns such as other RFID tags, various kinds of sensors, or MEMS structures, and the like.
As described above, according to exemplary embodiments of the present invention, even though high priced and specific inorganic additives such as CuCr2O4 having a spinel structure, and the like, are not contained in the polymer resin substrate itself, surface roughness and adhesion to a metal layer, of a region in which conductive patterns are formed by radiating an electromagnetic wave such as laser, or the like, may be adjusted, such that excellent conductive patterns may be formed on the polymer resin substrate by a simplified process under radiation condition of the electromagnetic wave having relatively low power.
Therefore, the manufacturing cost of the process of forming the conductive patterns may be decreased, and possibility of deteriorating physical properties such as mechanical properties, dielectric constant, and the like, of the polymer resin substrate or products, may be reduced by the specific inorganic additive. Further, it is easy to implement polymer resin products having black colors by unique color of the carbon-based black pigment.
Hereinafter, action and effects of the present invention are described by specific examples of the present invention in detail. Meanwhile, these examples are provided by way of example, and therefore, should not be construed as limiting the scope of the present invention.
Example 1 Formation of Conductive Patterns by Laser Direct RadiationA polycarbonate resin substrate containing an UV stabilizer, a thermal stabilizer, and an impact reinforcing agent having a total amount of less than 2 wt %, and containing 0.25 wt % of carbon black was prepared. Laser having a wavelength of 1064 nm was radiated once onto a predetermined region of the polycarbonate resin substrate under radiation condition (average power: 6.7 W) having an power ratio of 25%. Here, the interval between central parts of the laser radiation trace of the polycarbonate resin substrate was controlled to be about 50 μm by controlling the radiation interval of the laser.
Accordingly, the polycarbonate resin substrate radiated by laser had a predetermined surface roughness on the predetermined region. The center line arithmetic average roughness of the absolute values (Ra) of the region radiated by laser and the region which is not radiated by laser were measured. These Ra were measured in an area of 0.2 mm×0.3 mm by using an optical profiler (Nano view E1000, Nanosystem, Korea). As a result of the measurement, the region radiated by laser had Ra of about 5630 nm and the region which is not radiated by laser had Ra of about 226 nm. A photograph of the polycarbonate resin substrate as manufactured above was shown in
Then, the polycarbonate resin substrate was immersed into an aqueous-based polymer solution including Pd-containing compound particles to have Pd ions for about 5 minutes, to form conductive seed particles including Pd on the substrate. Next, the substrate was washed with deionized water, and an electroless-plating was performed by using copper as a conductive metal. At the time of the electroless-plating, a plating solution containing copper source (copper sulfate), a complexing agent (Rochelle salt), a pH adjustor (sodium hydroxide aqueous solution), and a reducing agent (formaldehyde), was used. The electroless-plating was performed at room temperature for about 1 hour, followed by ultrasonic cleaning, to form the metal layer. It could be confirmed that the metal layer was favorably formed on the region radiated by laser; however, the metal layer in the remaining region was formed in a delamination state due to poor adhesion to be significantly easily removed.
Then, the substrate was immersed into the deionized water, followed by ultrasonic radiation (sonication) for 20 minutes, and air blowing, to selectively remove the metal layer of the region which is not radiated by laser. Accordingly, the conductive patterns having the metal layer were selectively formed on the region radiated by laser, and a photograph thereof was shown in
Meanwhile, a cross-cut test according to ISO 2409 standard method was conducted by using a tape having about 4.9N/10 mm width (3M scotch tape #371) in the region radiated by laser, that is, the region having the metal layer and the conductive patterns formed thereon. Here, adhesion between the substrate and the metal layer was tested by cutting the metal layer to be 10×10 graph (an interval of about 2 mm or less), and measuring area of the metal layer delaminated by attaching and detaching the tape. A photograph showing results obtained by conducting the adhesion test was shown in
As a result of the adhesion test, it could be confirmed that the delamination area of the target metal layer under the test corresponds to about 0% (ISO class 0) of the area of the metal layer, and the metal layer and the conductive patterns were favorably formed on the region radiated by laser by excellent adhesion.
Example 2 Formation of Conductive Patterns by Laser Direct RadiationConductive patterns of Example 2 were formed by the same method as Example 1 except for using a multilayer substrate of polycarbonate/ABS resin instead of using the polycarbonate resin substrate.
In Example 2, after radiating laser, the center line arithmetic average roughness of the absolute values (Ra) of the region radiated by laser and the region which is not radiated by laser were measured by the same method as Example 1, and the region radiated by laser had Ra of about 5370 nm and the region which is not radiated by laser had Ra of about 183 nm, respectively.
In addition, after the metal layer and the conductive patterns were formed in Example 2, a cross-cut test was conducted by the same method as Example 1 in the region having the metal layer and the conductive patterns formed thereon. As a result of the adhesion test, it could be confirmed that the delamination area of the target metal layer under test corresponds to about 5% or less (ISO class 1) of the area of the metal layer, and the metal layer and the conductive patterns were favorably formed on the region radiated by laser by excellent adhesion.
Comparative Example 1 Formation of Conductive Patterns by Laser Direct RadiationConductive patterns of Comparative Example 1 were formed by the same method as Example 1 except that the process of forming the conductive seed particles including Pd in Example 1 was not performed. An optical microscope photograph of the metal layer formed on the region radiated by laser through the electroless-plating according to Comparative Example 1 was shown in
It could be appreciated from
Conductive patterns of Comparative Example 2 were formed by the same method as Example 1 except that the carbon black was not used and the radiation condition of the laser was changed into the radiation condition (average power: 18.6 W) having an power ratio of 70%.
In Comparative Example 2, after radiating laser, the center line arithmetic average roughness of the absolute values (Ra) of the region radiated by laser and the region which is not radiated by laser were measured by the same method as Example 1, and the region radiated by laser had Ra of about 830 nm and the region which is not radiated by laser had Ra of about 223 nm, respectively.
In addition, after the metal layer and the conductive patterns were formed in Comparative Example 2, a cross-cut test was conducted by the same method as Example 1 in the region having the metal layer and the conductive patterns formed thereon. As a result of the adhesion test, it could be confirmed that the delamination area of the target metal layer under test corresponds to more than about 5% to 15% or less (ISO class 2) of the area of the metal layer, and therefore, the metal layer and the conductive patterns were formed on the region radiated by laser; however, the conductive patterns were not favorably maintained by relatively poor adhesion to the substrate.
Reference Example 1 Formation of Conductive Patterns by Laser Direct Radiation (Using Specific Inorganic Additive)Reference Example 1 was performed by using 5 wt % of CuCr2O4 instead of using carbon black of Example 1. Then, laser radiation was performed under radiation condition (average power: 6.7 W) having an power ratio of 25%. Conductive patterns of Reference Example 1 were formed by the same method as Example 1 expect that the process of forming the conductive seed particles was not performed after radiating laser, and ultrasonic cleaning was not performed after the electroless-plating process.
In Reference Example 1, after radiating laser, the center line arithmetic average roughness of the absolute values (Ra) of the region radiated by laser and the region which is not radiated by laser were measured by the same method as Example 1, and the region radiated by laser had Ra of about 6200 nm and the region which is not radiated by laser had Ra of about 213 nm, respectively.
In addition, after the metal layer and the conductive patterns were formed in Reference Example 1, a cross-cut test was conducted by the same method as Example 1 in the region having the metal layer and the conductive patterns formed thereon. As a result of the adhesion test, it could be confirmed that the delamination area of the target metal layer under test corresponds to about 5% or less (ISO class 0) of the area of the metal layer, and the metal layer and the conductive patterns were favorably formed on the region radiated by laser. Meanwhile, it could be confirmed that the specific inorganic additive having relatively high content (5 wt %) was required to be used, and the radiation condition of laser corresponding to that of Example 1 was required, in order to form excellent conductive patterns.
Reference Example 2 Formation of Conductive Patterns by Laser Direct RadiationConductive patterns of Reference Example 2 were formed by the same method as Reference Example 1 except that the radiation condition of laser was changed into the radiation condition (average power: 5.3 W) having an power ratio of 20%.
In Reference Example 2, after radiating laser, the center line arithmetic average roughness of the absolute values (Ra) of the region radiated by laser and the region which is not radiated by laser were measured by the same method as Example 1, and the region radiated by laser had Ra of about 970 nm and the region which is not radiated by laser had Ra of about 197 nm, respectively.
In addition, after the metal layer and the conductive patterns were formed in Reference Example 2, a cross-cut test was conducted by the same method as Example 1 in the region having the metal layer and the conductive patterns formed thereon. Photograph showing the result of the above-mentioned test was shown in
It could be confirmed from test results of Examples, Comparative Examples, and Reference Examples as described above that according to Examples, excellent conductive patterns were formed on the region radiated by laser without using the specific inorganic additive even under the radiation condition of the laser having relatively low power.
It could be confirmed from Comparative Examples that since carbon black is not used or the process of forming the conductive seed particles is not performed, excellent conductive patterns could not be formed even under the radiation condition of the laser having relatively high power.
In addition, it could be confirmed that in Reference Example 1, excellent conductive patterns were formed under the radiation condition of laser corresponding to that of Example 1; however, the specific inorganic additive having relatively high content was required, and when the radiation condition of laser is a slightly decreased like Reference Example 2, it is difficult to form excellent conductive patterns.
Experimental Example Comparison in XRD Pattern Between Region Radiated by Laser and Region not Radiated by LaserXRD patterns of the substrates before and after radiating laser according to Example 1 and Comparative Example 2 were analyzed and shown in
In addition, referring to
Claims
1. A method for forming conductive pattern by direct radiation of an electromagnetic wave, the method comprising:
- forming a first region having a predetermined surface roughness by selectively radiating the electromagnetic wave on a polymer resin substrate containing carbon-based black pigment;
- forming a conductive seed on the polymer resin substrate;
- forming a metal layer by plating the polymer resin substrate having the conductive seed formed thereon; and
- removing the conductive seed and the metal layer from a second region of the polymer resin substrate,
- wherein the second region has surface roughness smaller than that of the first region.
2. The method of claim 1, wherein the carbon-based black pigment includes at least one kind selected from the group consisting of carbon black, pine black soot, soot, lamp black, channel black, furnace black, and acetylene black.
3. The method of claim 1, wherein the carbon-based black pigment is contained in an amount of 0.01 to 10 wt % based on a weight of the polymer resin substrate.
4. The method of claim 1, wherein the carbon-based black pigment is contained in a particle state having a particle diameter of 10 nm to 1 μm.
5. The method of claim 1, wherein when a cross-cut test having an interval of 2 mm or less according to ISO 2409 standard method is conducted by using a tape having adhesion of 4.0 to 6.0N/10 mm width, the first region of the polymer resin substrate has surface roughness defined by adhesion at which a delamination area of a target metal layer under test corresponds to 5% or less of an area of the metal layer.
6. The method of claim 1, wherein when a cross-cut test having an interval of 2 mm or less according to ISO 2409 standard method is conducted by using a tape having adhesion of 4.0 to 6.0N/10 mm width, the second region of the polymer resin substrate has surface roughness defined by adhesion at which a delamination area of a target metal layer under test corresponds to 65% or more of an area of the metal layer.
7. The method of claim 1, wherein the first region of the polymer resin substrate has surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of 1 μm or more, and the second region has a center line arithmetic average roughness of the absolute values (Ra) smaller than that of the first region.
8. The method of claim 1, wherein the polymer resin substrate contains at least one kind selected from the group consisting of an ABS resin, a polyalkylene terephthalate resin, a polycarbonate resin, a polypropylene resin, and a polyphthalamide resin.
9. The method of claim 1, wherein the radiating of the electromagnetic wave is performed by radiating a laser electromagnetic wave under radiation condition having 2 to 20 W of an average power.
10. The method of claim 1, wherein the conductive seed contains metal nanoparticles, metal ions, or metal complex ions.
11. The method of claim 10, wherein the conductive seed contains at least one kind metal selected from the group consisting of copper (Cu), platinum (Pt), palladium (Pd), silver (Ag), gold (Au), nickel (Ni), tungsten (W), titanium (Ti), chromium (Cr), aluminum (Al), zinc (Zn), tin (Sn), lead (Pb), magnesium (Mg), manganese (Mn) and iron (Fe), ions or complex ions thereof.
12. The method of claim 10, wherein the forming of the conductive seed includes:
- applying a dispersion liquid or solution containing the metal nanoparticles, the metal ions, or the metal complex ions on the polymer resin substrate; and
- precipitating and drying the metal nanoparticles or reducing and drying the metal ions or the metal complex ions to form the conductive seed in a particle form.
13. The method of claim 12, wherein the reducing of the metal ions or the metal complex ions is performed in the presence of at least one kind reducing agent selected from the group consisting of an alcohol-based reducing agent, an aldehyde-based reducing agent, a hypophosphite-based reducing agent, a hydrazine-based reducing agent, sodium borohydride and lithium aluminum hydride.
14. The method of claim 12, further comprising surface-treating the polymer resin substrate with a surfactant having surface tension lower than that of the dispersion liquid or solution, between the radiating of the electromagnetic wave and the forming of the conductive seed.
15. The method of claim 1, wherein the forming of the metal layer includes electroless-plating a conductive metal on the polymer resin substrate.
16. The method of claim 1, wherein the removing of the conductive seed and the metal layer from the second region includes applying physical power onto the polymer resin substrate by combination of one or two or more method(s) selected from the group consisting of ultrasonic radiation (sonication), liquid phase washing, liquid phase rinsing, air blowing, taping, brushing, and a method of using a manpower.
17. A resin structure having conductive pattern comprising:
- a polymer resin substrate divided into a first region formed to have surface roughness defined by a center line arithmetic average roughness of the absolute values (Ra) of 1 μm or more and a second region having surface roughness smaller than that of the first region, and containing carbon-based black pigment; and
- a conductive seed and a metal layer selectively formed on the first region of the polymer resin substrate.
18. The resin structure of claim 17, wherein the first region corresponds to a region radiated by the electromagnetic wave.
19. The resin structure of claim 18, wherein the polymer resin substrate of the second region does not have a peak derived from copper (Cu) or a compound containing copper on an XRD pattern.
Type: Application
Filed: Aug 7, 2014
Publication Date: Jul 14, 2016
Inventors: Jae Hyun KIM (Daejeon), Eun Kyu SEONG (Daejeon), Su Jeong LEE (Daejeon), Jae Jin KIM (Daejeon), Cheol-Hee PARK (Daejeon), Chee-Sung PARK (Daejeon), Shin Hee JUN (Daejeon), Sang Yun JUNG (Daejeon), Han Nah JEONG (Daejeon)
Application Number: 14/910,633