PERIODIC STRUCTURED ORGANIC FILMS
An ordered structured organic film comprising a plurality of segments and a plurality of linkers arranged as a covalent organic framework, wherein the structured organic film may be a multi-segment thick structured organic film.
This application is a divisional application of U.S. patent application Ser. No. 12/815,688, the disclosure of which is totally incorporated herein by reference in its entirety.
CROSS-REFERENCE TO RELATED APPLICATIONSCommonly assigned U.S. patent application Ser. Nos. 12/716,524; 12/716,449; 12/716,706; 12/716,324; 12/716,686; and Ser. No. 12/716,571, entitled “Structured Organic Films,” “Structured Organic Films Having an Added Functionality,” “Mixed Solvent Process for Preparing Structured Organic Films,” “Composite Structured Organic Films,” “Process For Preparing Structured Organic Films (SOFs) Via a Pre-SOF,” “Electronic Devices Comprising Structured Organic Films,” respectively, the disclosures of which are totally incorporated herein by reference in their entireties, describe structured organic films, methods for preparing structured organic films and applications of structured organic films.
BACKGROUND OF THE INVENTIONMaterials whose chemical structures are comprised of molecules linked by covalent bonds into extended structures may be placed into two classes: (1) polymers and cross-linked polymers, and (2) covalent organic frameworks (also known as covalently linked organic networks).
The first class, polymers and cross-linked polymers, is typically embodied by polymerization of molecular monomers to form long linear chains of covalently-bonded molecules. Polymer chemistry processes can allow for polymerized chains to, in turn, or concomitantly, become ‘cross-linked.’ The nature of polymer chemistry offers poor control over the molecular-level structure of the formed material, i.e. the organization of polymer chains and the patterning of molecular monomers between chains is mostly random. Nearly all polymers are amorphous, save for some linear polymers that efficiently pack as ordered rods. Some polymer materials, notably block co-polymers, can possess regions of order within their bulk. In the two preceding cases the patterning of polymer chains is not by design, any ordering at the molecular-level is a consequence of the natural intermolecular packing tendencies.
The second class, covalent organic frameworks (COFs), differ from the first class (polymers/cross-linked polymers) in that COFs are intended to be highly patterned. In COF chemistry molecular components are called molecular building blocks rather than monomers. During COF synthesis molecular building blocks react to form two- or three-dimensional networks. Consequently, molecular building blocks are patterned throughout COF materials and molecular building blocks are linked to each other through strong covalent bonds.
COFs developed thus far are typically powders with high porosity and are materials with exceptionally low density. COFs can store near-record amounts of argon and nitrogen. While these conventional COFs are useful, there is a need, addressed by embodiments of the present invention, for new materials that offer advantages over conventional COFs in terms of enhanced characteristics.
SUMMARY OF THE DISCLOSUREThere is provided in embodiments an ordered (periodic) structured organic film comprising a plurality of segments and a plurality of linkers arranged as a covalent organic framework, wherein at a macroscopic level the covalent organic framework is a film.
Other aspects of the present disclosure will become apparent as the following description proceeds and upon reference to the following figures which represent illustrative embodiments:
“Structured organic film” (SOF) is a new term introduced by the present disclosure to refer to a COF that is a film at a macroscopic level. The term “SOF” refers to a covalent organic framework (COF) that is a film at a macroscopic level. The phrase “macroscopic level” refers, for example, to the naked eye view of the present SOFs. Although COFs are a network at the “microscopic level” or “molecular level” (requiring use of powerful magnifying equipment or as assessed using scattering methods), the present SOF is fundamentally different at the “macroscopic level” because the film is for instance orders of magnitude larger in coverage than a microscopic level COF network. SOFs described herein have macroscopic morphologies much different than typical COFs previously synthesized. COFs previously synthesized were typically obtained as polycrystalline or particulate powders wherein the powder is a collection of at least thousands of particles (crystals) where each particle (crystal) can have dimensions ranging from nanometers to millimeters. The shape of the particles can range from plates, spheres, cubes, blocks, prisms, etc. The composition of each particle (crystal) is the same throughout the entire particle while at the edges, or surfaces of the particle, is where the segments of the covalently-linked framework terminate. The SOFs described herein are not collections of particles. Instead, the SOFs of the present disclosure are at the macroscopic level substantially defect-free SOFs or defect-free SOFs having continuous covalent organic frameworks that can extend over larger length scales such as for instance much greater than a millimeter to lengths such as a meter and, in theory, as much as hundreds of meters. It will also be appreciated that SOFs tend to have large aspect ratios where typically two dimensions of a SOF will be much larger than the third. SOFs have markedly fewer macroscopic edges and disconnected external surfaces than a collection of COF particles.
In embodiments, a “substantially defect-free SOF” or “defect-free SOF” may be formed from a reaction mixture deposited on the surface of an underlying substrate. The term “substantially defect-free SOF” refers, for example, to an SOF that may or may not be removed from the underlying substrate on which it was formed and contains substantially no pinholes, pores or gaps greater than the distance between the cores of two adjacent segments per square cm; such as, for example, less than 10 pinholes, pores or gaps greater than about 250 nanometers in diameter per cm2, or less than 5 pinholes, pores or gaps greater than about 100 nanometers in diameter per cm2. The term “defect-free SOF” refers, for example, to an SOF that may or may not be removed from the underlying substrate on which it was formed and contains no pinholes, pores or gaps greater than the distance between the cores of two adjacent segments per micron, such as no pinholes, pores or gaps greater than about 100 Angstroms in diameter per micron2, or no pinholes, pores or gaps greater than about 50 Angstroms in diameter per micron2, or no pinholes, pores or gaps greater than about 20 Angstroms in diameter per micron2.
In embodiments, the SOF comprises at least one atom of an element that is not carbon, such at least one atom selected from the group consisting of hydrogen, oxygen, nitrogen, silicon, phosphorous, selenium, fluorine, boron, and sulfur. In further embodiments, the SOF is a boroxine-, borazine-, borosilicate-, and boronate ester-free SOF.
Molecular Building Block
The SOFs of the present disclosure comprise molecular building blocks having a segment (S) and functional groups (Fg). Molecular building blocks require at least two functional groups (x≧2) and may comprise a single type or two or more types of functional groups. Functional groups are the reactive chemical moieties of molecular building blocks that participate in a chemical reaction to link together segments during the SOF forming process. A segment is the portion of the molecular building block that supports functional groups and comprises all atoms that are not associated with functional groups. Further, the composition of a molecular building block segment remains unchanged after SOF formation.
Functional Group
Functional groups are the reactive chemical moieties of molecular building blocks that participate in a chemical reaction to link together segments during the SOF forming process. Functional groups may be composed of a single atom, or functional groups may be composed of more than one atom. The atomic compositions of functional groups are those compositions normally associated with reactive moieties in chemical compounds. Non-limiting examples of functional groups include halogens, alcohols, ethers, ketones, carboxylic acids, esters, carbonates, amines, amides, imines, ureas, aldehydes, isocyanates, tosylates, alkenes, alkynes and the like.
Molecular building blocks contain a plurality of chemical moieties, but only a subset of these chemical moieties are intended to be functional groups during the SOF forming process. Whether or not a chemical moiety is considered a functional group depends on the reaction conditions selected for the SOF forming process. Functional groups (Fg) denote a chemical moiety that is a reactive moiety, that is, a functional group during the SOF forming process.
In the SOF forming process the composition of a functional group will be altered through the loss of atoms, the gain of atoms, or both the loss and the gain of atoms; or, the functional group may be lost altogether. In the SOF, atoms previously associated with functional groups become associated with linker groups, which are the chemical moieties that join together segments. Functional groups have characteristic chemistries and those of ordinary skill in the art can generally recognize in the present molecular building blocks the atom(s) that constitute functional group(s). It should be noted that an atom or grouping of atoms that are identified as part of the molecular building block functional group may be preserved in the linker group of the SOF. Linker groups are described below.
Segment
A segment is the portion of the molecular building block that supports functional groups and comprises all atoms that are not associated with functional groups. Further, the composition of a molecular building block segment remains unchanged after SOF formation. In embodiments, the SOF may contain a first segment having a structure the same as or different from a second segment. In other embodiments, the structures of the first and/or second segments may be the same as or different from a third segment, forth segment, fifth segment, etc. A segment is also the portion of the molecular building block that can provide an inclined property. Inclined properties are described later in the embodiments.
In specific embodiments, the segment of the SOF comprises at least one atom of an element that is not carbon, such at least one atom selected from the group consisting of hydrogen, oxygen, nitrogen, silicon, phosphorous, selenium, fluorine, boron, and sulfur.
A description of various exemplary molecular building blocks, linkers, SOF types, strategies to synthesize a specific SOF type with exemplary chemical structures, building blocks whose symmetrical elements are outlined, and classes of exemplary molecular entities and examples of members of each class that may serve as molecular building blocks for SOFs are detailed in U.S. patent application Ser. Nos. 12/716,524; 12/716,449; 12/716,706; 12/716,324; 12/716,686; and 12/716,571, entitled “Structured Organic Films,” “Structured Organic Films Having an Added Functionality,” “Mixed Solvent Process for Preparing Structured Organic Films,” “Composite Structured Organic Films,” “Process For Preparing Structured Organic Films (SOFs) Via a Pre-SOF,” “Electronic Devices Comprising Structured Organic Films,” the disclosures of which are totally incorporated herein by reference in their entireties.
Metrical Parameters of SOFs
SOFs have any suitable aspect ratio. In embodiments, SOFs have aspect ratios for instance greater than about 30:1 or greater than about 50:1, or greater than about 70:1, or greater than about 100:1, such as about 1000:1. The aspect ratio of a SOF is defined as the ratio of its average width or diameter (that is, the dimension next largest to its thickness) to its average thickness (that is, its shortest dimension). The term ‘aspect ratio,’ as used here, is not bound by theory. The longest dimension of a SOF is its length and it is not considered in the calculation of SOF aspect ratio.
Generally, SOFs have widths and lengths, or diameters greater than about 500 micrometers, such as about 10 mm, or 30 mm. The SOFs have the following illustrative thicknesses: about 10 Angstroms to about 250 Angstroms, such as about 20 Angstroms to about 200 Angstroms, for a mono-segment thick layer and about 20 nm to about 5 mm, about 50 nm to about 10 mm for a multi-segment thick layer.
SOF dimensions may be measured using a variety of tools and methods. For a dimension about 1 micrometer or less, scanning electron microscopy is the preferred method. For a dimension about 1 micrometer or greater, a micrometer (or ruler) is the preferred method.
Multilayer SOFs
A SOF may comprise a single layer or a plurality of layers (that is, two, three or more layers). SOFs that are comprised of a plurality of layers may be physically joined (e.g., dipole and hydrogen bond) or chemically joined. Physically attached layers are characterized by weaker interlayer interactions or adhesion; therefore physically attached layers may be susceptible to delamination from each other. Chemically attached layers are expected to have chemical bonds (e.g., covalent or ionic bonds) or have numerous physical or intermolecular (supramolecular) entanglements that strongly link adjacent layers.
Therefore, delamination of chemically attached layers is much more difficult. Chemical attachments between layers may be detected using spectroscopic methods such as focusing infrared or Raman spectroscopy, or with other methods having spatial resolution that can detect chemical species precisely at interfaces. In cases where chemical attachments between layers are different chemical species than those within the layers themselves it is possible to detect these attachments with sensitive bulk analyses such as solid-state nuclear magnetic resonance spectroscopy or by using other bulk analytical methods.
In the embodiments, the SOF may be a single layer (mono-segment thick or multi-segment thick) or multiple layers (each layer being mono-segment thick or multi-segment thick). “Thickness” refers, for example, to the smallest dimension of the film. As discussed above, in a SOF, segments are molecular units that are covalently bonded through linkers to generate the molecular framework of the film. The thickness of the film may also be defined in terms of the number of segments that is counted along that axis of the film when viewing the cross-section of the film. A “monolayer” SOF is the simplest case and refers, for example, to where a film is one segment thick. A SOF where two or more segments exist along this axis is referred to as a “multi-segment” thick SOF.
An exemplary method for preparing physically attached multilayer SOFs includes: (1) forming a base SOF layer that may be cured by a first curing cycle, and (2) forming upon the base layer a second reactive wet layer followed by a second curing cycle and, if desired, repeating the second step to form a third layer, a forth layer and so on. The physically stacked multilayer SOFs may have thicknesses greater than about 20 Angstroms such as, for example, the following illustrative thicknesses: about 20 Angstroms to about 10 cm, such as about 1 nm to about 10 mm, or about 0.1 mm Angstroms to about 5 mm. In principle there is no limit with this process to the number of layers that may be physically stacked.
In embodiments, a multilayer SOF is formed by a method for preparing chemically attached multilayer SOFs by: (1) forming a base SOF layer having functional groups present on the surface (or dangling functional groups) from a first reactive wet layer, and (2) forming upon the base layer a second SOF layer from a second reactive wet layer that comprises molecular building blocks with functional groups capable of reacting with the dangling functional groups on the surface of the base SOF layer. In further embodiments, a capped SOF may serve as the base layer in which the functional groups present that were not suitable or complementary to participate in the specific chemical reaction to link together segments during the base layer SOF forming process may be available for reacting with the molecular building blocks of the second layer to from an chemically bonded multilayer SOF. If desired, the formulation used to form the second SOF layer should comprise molecular building blocks with functional groups capable of reacting with the functional groups from the base layer as well as additional functional groups that will allow for a third layer to be chemically attached to the second layer. The chemically stacked multilayer SOFs may have thicknesses greater than about 20 Angstroms such as, for example, the following illustrative thicknesses: about 20 Angstroms to about 10 cm, such as about 1 nm to about 10 mm, or about 0.1 mm Angstroms to about 5 mm. In principle there is no limit with this process to the number of layers that may be chemically stacked.
In embodiments, the method for preparing chemically attached multilayer SOFs comprises promoting chemical attachment of a second SOF onto an existing SOF (base layer) by using a small excess of one molecular building block (when more than one molecular building block is present) during the process used to form the SOF (base layer) whereby the functional groups present on this molecular building block will be present on the base layer surface. The surface of base layer may be treated with an agent to enhance the reactivity of the functional groups or to create an increased number of functional groups.
In an embodiment the dangling functional groups or chemical moieties present on the surface of an SOF or capped SOF may be altered to increase the propensity for covalent attachment (or, alternatively, to disfavor covalent attachment) of particular classes of molecules or individual molecules, such as SOFs, to a base layer or any additional substrate or SOF layer. For example, the surface of a base layer, such as an SOF layer, which may contain reactive dangling functional groups, may be rendered pacified through surface treatment with a capping chemical group. For example, a SOF layer having dangling hydroxyl alcohol groups may be pacified by treatment with trimethylsiylchloride thereby capping hydroxyl groups as stable trimethylsilylethers. Alternatively, the surface of base layer may be treated with a non-chemically bonding agent, such as a wax, to block reaction with dangling functional groups from subsequent layers.
Molecular Building Block Symmetry
Molecular building block symmetry relates to the positioning of functional groups (Fgs) around the periphery of the molecular building block segments. Without being bound by chemical or mathematical theory, a symmetric molecular building block is one where positioning of Fgs may be associated with the ends of a rod, vertexes of a regular geometric shape, or the vertexes of a distorted rod or distorted geometric shape. For example, the most symmetric option for molecular building blocks containing four Fgs are those whose Fgs overlay with the corners of a square or the apexes of a tetrahedron.
Use of symmetrical building blocks is practiced in embodiments of the present disclosure for two reasons: (1) the patterning of molecular building blocks may be better anticipated because the linking of regular shapes is a better understood process in reticular chemistry, and (2) the complete reaction between molecular building blocks is facilitated because for less symmetric building blocks errant conformations/orientations may be adopted which can possibly initiate numerous linking defects within SOFs.
In embodiments, a Type 1 SOF contains segments, which are not located at the edges of the SOF, that are connected by linkers to at least three other segments. For example, in embodiments the SOF comprises at least one symmetrical building block selected from the group consisting of ideal triangular building blocks, distorted triangular building blocks, ideal tetrahedral building blocks, distorted tetrahedral building blocks, ideal square building blocks, and distorted square building blocks. In embodiments, Type 2 and 3 SOF contains at least one segment type, which are not located at the edges of the SOF, that are connected by linkers to at least three other segments. For example, in embodiments the SOF comprises at least one symmetrical building block selected from the group consisting of ideal triangular building blocks, distorted triangular building blocks, ideal tetrahedral building blocks, distorted tetrahedral building blocks, ideal square building blocks, and distorted square building blocks.
Practice of Linking Chemistry
In embodiments linking chemistry may occur wherein the reaction between functional groups produces a volatile byproduct that may be largely evaporated or expunged from the SOF during or after the film forming process or wherein no byproduct is formed. Linking chemistry may be selected to achieve a SOF for applications where the presence of linking chemistry byproducts is not desired. Linking chemistry reactions may include, for example, condensation, addition/elimination, and addition reactions, such as, for example, those that produce esters, imines, ethers, carbonates, urethanes, amides, acetals, and silyl ethers.
In embodiments the linking chemistry via a reaction between function groups producing a non-volatile byproduct that largely remains incorporated within the SOF after the film forming process. Linking chemistry in embodiments may be selected to achieve a SOF for applications where the presence of linking chemistry byproducts does not impact the properties or for applications where the presence of linking chemistry byproducts may alter the properties of a SOF (such as, for example, the electroactive, hydrophobic or hydrophilic nature of the SOF). Linking chemistry reactions may include, for example, substitution, metathesis, and metal catalyzed coupling reactions, such as those that produce carbon-carbon bonds.
For all linking chemistry the ability to control the rate and extent of reaction between building blocks via the chemistry between building block functional groups is an important aspect of the present disclosure. Reasons for controlling the rate and extent of reaction may include adapting the film forming process for different coating methods and tuning the microscopic arrangement of building blocks to achieve a periodic SOF, as defined in earlier embodiments.
Innate Properties of COFs
COFs have innate properties such as high thermal stability (typically higher than 400° C. under atmospheric conditions); poor solubility in organic solvents (chemical stability), and porosity (capable of reversible guest uptake). In embodiments, SOFs may also possess these innate properties.
Added Functionality of SOFs
Added functionality denotes a property that is not inherent to conventional COFs and may occur by the selection of molecular building blocks wherein the molecular compositions provide the added functionality in the resultant SOF. Added functionality may arise upon assembly of molecular building blocks having an “inclined property” for that added functionality. Added functionality may also arise upon assembly of molecular building blocks having no “inclined property” for that added functionality but the resulting SOF has the added functionality as a consequence of linking segments (S) and linkers into a SOF. Furthermore, emergence of added functionality may arise from the combined effect of using molecular building blocks bearing an “inclined property” for that added functionality whose inclined property is modified or enhanced upon linking together the segments and linkers into a SOF.
An Inclined Property of a Molecular Building Block
The term “inclined property” of a molecular building block refers, for example, to a property known to exist for certain molecular compositions or a property that is reasonably identifiable by a person skilled in art upon inspection of the molecular composition of a segment. As used herein, the terms “inclined property” and “added functionality” refer to the same general property (e.g., hydrophobic, electroactive, etc.) but “inclined property” is used in the context of the molecular building block and “added functionality” is used in the context of the SOF.
The hydrophobic (superhydrophobic), hydrophilic, lipophobic (superlipophobic), lipophilic, photochromic and/or electroactive (conductor, semiconductor, charge transport material) nature of an SOF are some examples of the properties that may represent an “added functionality” of an SOF. These and other added functionalities may arise from the inclined properties of the molecular building blocks or may arise from building blocks that do not have the respective added functionality that is observed in the SOF.
The term hydrophobic (superhydrophobic) refers, for example, to the property of repelling water, or other polar species such as methanol, it also means an inability to absorb water and/or to swell as a result. Furthermore, hydrophobic implies an inability to form strong hydrogen bonds to water or other hydrogen bonding species. Hydrophobic materials are typically characterized by having water contact angles greater than 90° and superhydrophobic materials have water contact angles greater than 150° as measured using a contact angle goniometer or related device.
The term hydrophilic refers, for example, to the property of attracting, adsorbing, or absorbing water or other polar species, or a surface that is easily wetted by such species. Hydrophilic materials are typically characterized by having less than 20° water contact angle as measured using a contact angle goniometer or related device. Hydrophilicity may also be characterized by swelling of a material by water or other polar species, or a material that can diffuse or transport water, or other polar species, through itself. Hydrophilicity, is further characterized by being able to form strong or numerous hydrogen bonds to water or other hydrogen bonding species.
The term lipophobic (oleophobic) refers, for example, to the property of repelling oil or other non-polar species such as alkanes, fats, and waxes. Lipophobic materials are typically characterized by having oil contact angles greater than 90° as measured using a contact angle goniometer or related device.
The term lipophilic (oleophilic) refers, for example, to the property attracting oil or other non-polar species such as alkanes, fats, and waxes or a surface that is easily wetted by such species. Lipophilic materials are typically characterized by having a low to nil oil contact angle as measured using, for example, a contact angle goniometer. Lipophilicity can also be characterized by swelling of a material by hexane or other non-polar liquids.
The term photochromic refers, for example, to the ability to demonstrate reversible color changes when exposed to electromagnetic radiation. SOF compositions containing photochromic molecules may be prepared and demonstrate reversible color changes when exposed to electromagnetic radiation. These SOFs may have the added functionality of photochromism. The robustness of photochromic SOFs may enable their use in many applications, such as photochromic SOFs for erasable paper, and light responsive films for window tinting/shading and eye wear. SOF compositions may contain any suitable photochromic molecule, such as a difunctional photochromic molecules as SOF molecular building blocks (chemically bound into SOF structure), a monofunctional photochromic molecules as SOF capping units (chemically bound into SOF structure, or unfunctionalized photochromic molecules in an SOF composite (not chemically bound into SOF structure). Photochromic SOFs may change color upon exposure to selected wavelengths of light and the color change may be reversible.
SOF compositions containing photochromic molecules that chemically bond to the SOF structure are exceptionally chemically and mechanically robust photochromic materials. Such photochromic SOF materials demonstrate many superior properties, such as high number of reversible color change processes, to available polymeric alternatives.
The term electroactive refers, for example, to the property to transport electrical charge (electrons and/or holes). Electroactive materials include conductors, semiconductors, and charge transport materials. Conductors are defined as materials that readily transport electrical charge in the presence of a potential difference. Semiconductors are defined as materials do not inherently conduct charge but may become conductive in the presence of a potential difference and an applied stimuli, such as, for example, an electric field, electromagnetic radiation, heat, and the like. Charge transport materials are defined as materials that can transport charge when charge is injected from another material such as, for example, a dye, pigment, or metal in the presence of a potential difference.
Conductors may be further defined as materials that give a signal using a potentiometer from about 0.1 to about 107 S/cm.
Semiconductors may be further defined as materials that give a signal using a potentiometer from about 10−6 to about 104 S/cm in the presence of applied stimuli such as, for example an electric field, electromagnetic radiation, heat, and the like. Alternatively, semiconductors may be defined as materials having electron and/or hole mobility measured using time-of-flight techniques in the range of 10−10 to about 106 cm2V−1s−1 when exposed to applied stimuli such as, for example an electric field, electromagnetic radiation, heat, and the like.
Charge transport materials may be further defined as materials that have electron and/or hole mobility measured using time-of-flight techniques in the range of 10−10 to about 106 cm2V−1s−1. It should be noted that under some circumstances charge transport materials may be also classified as semiconductors.
SOFs with hydrophobic added functionality may be prepared by using molecular building blocks with inclined hydrophobic properties and/or have a rough, textured, or porous surface on the sub-micron to micron scale. A paper describing materials having a rough, textured, or porous surface on the sub-micron to micron scale being hydrophobic was authored by Cassie and Baxter (Cassie, A. B. D.; Baxter, S. Trans. Faraday Soc., 1944, 40, 546).
Molecular building blocks comprising or bearing highly-fluorinated segments have inclined hydrophobic properties and may lead to SOFs with hydrophobic added functionality. Highly-fluorinated segments are defined as the number of fluorine atoms present on the segment(s) divided by the number of hydrogen atoms present on the segment(s) being greater than one. Fluorinated segments, which are not highly-fluorinated segments may also lead to SOFs with hydrophobic added functionality.
The above-mentioned fluorinated segments may include, for example, tetrafluorohydroquinone, perfluoroadipic acid hydrate, 4,4′-(hexafluoroisopropylidene)diphthalic anhydride, 4,4′-(hexafluoroisopropylidene)diphenol, and the like.
SOFs having a rough, textured, or porous surface on the sub-micron to micron scale may also be hydrophobic. The rough, textured, or porous SOF surface can result from dangling functional groups present on the film surface or from the structure of the SOF. The type of pattern and degree of patterning depends on the geometry of the molecular building blocks and the linking chemistry efficiency. The feature size that leads to surface roughness or texture is from about 100 nm to about 10 μm, such as from about 500 nm to about 5 μm.
SOFs with hydrophilic added functionality may be prepared by using molecular building blocks with inclined hydrophilic properties and/or comprising polar linking groups.
Molecular building blocks comprising segments bearing polar substituents have inclined hydrophilic properties and may lead to SOFs with hydrophilic added functionality. The term polar substituents refers, for example, to substituents that can form hydrogen bonds with water and include, for example, hydroxyl, amino, ammonium, and carbonyl (such as ketone, carboxylic acid, ester, amide, carbonate, urea).
SOFs with electroactive added functionality may be prepared by using molecular building blocks with inclined electroactive properties and/or be electroactive resulting from the assembly of conjugated segments and linkers. The following sections describe molecular building blocks with inclined hole transport properties, inclined electron transport properties, and inclined semiconductor properties.
SOFs with hole transport added functionality may be obtained by selecting segment cores such as, for example, triarylamines, hydrazones (U.S. Pat. No. 7,202,002 B2 to Tokarski et al.), and enamines (U.S. Pat. No. 7,416,824 B2 to Kondoh et al.) with the following general structures:
The segment core comprising a triarylamine being represented by the following general formula:
wherein Ar1, Ar2, Ar3, Ar4 and Ar5 each independently represents a substituted or unsubstituted aryl group, or Ar5 independently represents a substituted or unsubstituted arylene group, and k represents 0 or 1, wherein at least two of Ar1, Ar2, Ar3, Ar4 and Ar5 comprises a Fg (previously defined). Ar5 may be further defined as, for example, a substituted phenyl ring, substituted/unsubstituted phenylene, substituted/unsubstituted monovalently linked aromatic rings such as biphenyl, terphenyl, and the like, or substituted/unsubstituted fused aromatic rings such as naphthyl, anthranyl, phenanthryl, and the like.
Segment cores comprising arylamines with hole transport added functionality include, for example, aryl amines such as triphenylamine, N,N,N′,N′-tetraphenyl-(1,1′-biphenyl)-4,4′-diamine, N,N′-diphenyl-N,N′-bis(3-methylphenyl)-(1,1′-biphenyl)-4,4′-diamine, N,N′-bis(4-butylphenyl)-N,N′-diphenyl-[p-terphenyl]-4,4″-diamine; hydrazones such as N-phenyl-N-methyl-3-(9-ethyl)carbazyl hydrazone and 4-diethyl amino benzaldehyde-1,2-diphenyl hydrazone; and oxadiazoles such as 2,5-bis(4-N,N-diethylaminophenyl)-1,2,4-oxadiazole, stilbenes, and the like.
Molecular building blocks comprising triarylamine core segments with inclined hole transport properties may be derived from the list of chemical structures including, for example, those listed below:
The segment core comprising a hydrazone being represented by the following general formula:
wherein Ar1, Ar2, and Ar3 each independently represents an aryl group optionally containing one or more substituents, and R represents a hydrogen atom, an aryl group, or an alkyl group optionally containing a substituent; wherein at least two of Ar1, Ar2, and Ar3 comprises a Fg (previously defined); and a related oxadiazole being represented by the following general formula:
wherein Ar and Ar1 each independently represent an aryl group that comprises a Fg (previously defined).
Molecular building blocks comprising hydrazone and oxadiazole core segments with inclined hole transport properties may be derived from the list of chemical structures including, for example, those listed below:
The segment core comprising an enamine being represented by the following general formula:
wherein Ar1, Ar2, Ar3, and Ar4 each independently represents an aryl group that optionally contains one or more substituents or a heterocyclic group that optionally contains one or more substituents, and R represents a hydrogen atom, an aryl group, or an alkyl group optionally containing a substituent; wherein at least two of Ar1, Ar2, Ar3, and Ar4 comprises a Fg (previously defined).
Molecular building blocks comprising enamine core segments with inclined hole transport properties may be derived from the list of chemical structures including, for example, those listed below:
SOFs with electron transport added functionality may be obtained by selecting segment cores comprising, for example, nitrofluorenones, 9-fluorenylidene malonitriles, diphenoquinones, and naphthalenetetracarboxylic diimides with the following general structures:
It should be noted that the carbonyl groups of diphenylquinones could also act as Fgs in the SOF forming process.
SOFs with semiconductor added functionality may be obtained by selecting segment cores such as, for example, acenes, thiophenes/oligothiophenes/fused thiophenes, perylene bisimides, or tetrathiofulvalenes, and derivatives thereof with the following general structures:
The SOF may be a p-type semiconductor, n-type semiconductor or ambipolar semiconductor. The SOF semiconductor type depends on the nature of the molecular building blocks. Molecular building blocks that possess an electron donating property such as alkyl, alkoxy, aryl, and amino groups, when present in the SOF, may render the SOF a p-type semiconductor. Alternatively, molecular building blocks that are electron withdrawing such as cyano, nitro, fluoro, fluorinated alkyl, and fluorinated aryl groups may render the SOF into the n-type semiconductor.
Molecular building blocks comprising acene core segments with inclined semiconductor properties may be derived from the list of chemical structures including, for example, those listed below:
Molecular building blocks comprising thiophene/oligothiophene/fused thiophene core segments with inclined semiconductor properties may be derived from the list of chemical structures including, for example, those listed below:
Examples of molecular building blocks comprising perylene bisimide core segments with inclined semiconductor properties may be derived from the chemical structure below:
Molecular building blocks comprising tetrathiofulvalene core segments with inclined semiconductor properties may be derived from the list of chemical structures including, for example, those listed below:
wherein Ar each independently represents an aryl group that optionally contains one or more substituents or a heterocyclic group that optionally contains one or more substituents.
Similarly, the electroactivity of SOFs prepared by these molecular building blocks will depend on the nature of the segments, nature of the linkers, and how the segments are orientated within the SOF. Linkers that favor preferred orientations of the segment moieties in the SOF are expected to lead to higher electroactivity.
Process for Preparing an Ordered Structured Organic Film
The process for making ordered SOFs typically comprises a number of activities or steps (set forth below) that may be performed in any suitable sequence or where two or more activities are performed simultaneously or in close proximity in time:
A process for preparing a ordered (periodic) structured organic film comprising:
(a) preparing a liquid-containing reaction mixture comprising a plurality of molecular building blocks each comprising a segment and a number of functional groups;
(b) depositing the reaction mixture as a wet film;
(c) promoting a change of the wet film including the molecular building blocks to a dry film comprising the SOF comprising a plurality of the segments and a plurality of linkers arranged as a covalent organic framework, wherein at a macroscopic level the covalent organic framework is a film;
(d) optionally removing the SOF from the coating substrate to obtain a free-standing SOF;
(e) optionally processing the free-standing SOF into a roll;
(f) optionally cutting and seaming the SOF into a belt; and
(g) optionally performing the above SOF formation process(es) upon an SOF (which was prepared by the above SOF formation process(es)) as a substrate for subsequent SOF formation process(es).
The above activities or steps may be conducted at atmospheric, super atmospheric, or subatmospheric pressure. The term “atmospheric pressure” as used herein refers to a pressure of about 760 torr. The term “super atmospheric” refers to pressures greater than atmospheric pressure, but less than 20 atm. The term “subatmospheric pressure” refers to pressures less than atmospheric pressure. In an embodiment, the activities or steps may be conducted at or near atmospheric pressure. Generally, pressures of from about 0.1 atm to about 2 atm, such as from about 0.5 atm to about 1.5 atm, or 0.8 atm to about 1.2 atm may be conveniently employed.
Process Action A: Preparation of the Liquid-Containing Reaction Mixture
The reaction mixture comprises a plurality of molecular building blocks that are dissolved, suspended, or mixed in a liquid. The plurality of molecular building blocks may be of one type or two or more types. When one or more of the molecular building blocks is a liquid, the use of an additional liquid is optional. Catalysts may optionally be added to the reaction mixture to enable SOF formation or modify the kinetics of SOF formation during Action C described above. Additives or secondary components may optionally be added to the reaction mixture to alter the physical properties of the resulting SOF.
The reaction mixture components (molecular building blocks, optionally a liquid, optionally catalysts, and optionally additives) are combined in a vessel. The order of addition of the reaction mixture components may vary; however, typically the catalyst is added last. In particular embodiments, the molecular building blocks are heated in the liquid in the absence of the catalyst to aid the dissolution of the molecular building blocks. The reaction mixture may also be mixed, stirred, milled, or the like, to ensure even distribution of the formulation components prior to depositing the reaction mixture as a wet film.
In embodiments, the reaction mixture may be heated prior to being deposited as a wet film. This may aid the dissolution of one or more of the molecular building blocks and/or increase the viscosity of the reaction mixture by the partial reaction of the reaction mixture prior to depositing the wet layer. This approach may be used to increase the loading of the molecular building blocks in the reaction mixture.
In particular embodiments, the reaction mixture needs to have a viscosity that will support the deposited wet layer. Reaction mixture viscosities range from about 10 to about 50,000 cps, such as from about 25 to about 25,000 cps or from about 50 to about 1000 cps.
The molecular building block loading or “loading” in the reaction mixture is defined as the total weight of the molecular building blocks and optionally the catalysts divided by the total weight of the reaction mixture. Building block loadings may range from about 3 to 100%, such as from about 5 to about 50%, or from about 15 to about 40%. In the case where a liquid molecular building block is used as the only liquid component of the reaction mixture (i.e. no additional liquid is used), the building block loading would be about 100%.
In embodiments, the reaction mixture comprises a plurality of molecular building blocks that are dissolved, suspended, or mixed in a liquid. The plurality of molecular building blocks may be of one type or two or more types. When one or more of the molecular building blocks is a liquid, the use of an additional liquid is optional.
Catalysts may optionally be added to the reaction mixture to enable pre-SOF formation and/or modify the kinetics of SOF formation during Action C described above. The term “pre-SOF” may refer to, for example, at least two molecular building blocks that have reacted and have a molecular weight higher than the starting molecular building block and contain multiple functional groups capable of undergoing further reactions with functional groups of other building blocks or pre-SOFs to obtain a SOF, which may be a substantially defect-free or defect-free SOF, and/or the ‘activation’ of molecular building block functional groups that imparts enhanced or modified reactivity for the film forming process. Activation may include dissociation of a functional group moiety, pre-association with a catalyst, association with a solvent molecule, liquid, second solvent, second liquid, secondary component, or with any entity that modifies functional group reactivity. In embodiments, pre-SOF formation may include the reaction between molecular building blocks or the ‘activation’ of molecular building block functional groups, or a combination of the two. The formation of the “pre-SOF” may be achieved by in a number of ways, such as heating the reaction mixture, exposure of the reaction mixture to UV radiation, or any other means of partially reacting the molecular building blocks and/or activating functional groups in the reaction mixture prior to deposition of the wet layer on the substrate. Additives or secondary components may optionally be added to the reaction mixture to alter the physical properties of the resulting SOF.
The reaction mixture components (molecular building blocks, optionally a liquid, optionally catalysts, and optionally additives) are combined in a vessel. The order of addition of the reaction mixture components may vary; however, typically when a process for preparing a SOF includes a pre-SOF or formation of a pre-SOF, the catalyst, when present, may be added to the reaction mixture before depositing the reaction mixture as a wet film. In embodiments, the molecular building blocks may be reacted actinically, thermally, chemically or by any other means with or without the presence of a catalyst to obtain a pre-SOF. The pre-SOF and the molecular building blocks formed in the absence of catalyst may be may be heated in the liquid in the absence of the catalyst to aid the dissolution of the molecular building blocks and pre-SOFs. In embodiments, the pre-SOF and the molecular building blocks formed in the presence of catalyst may be may be heated at a temperature that does not cause significant further reaction of the molecular building blocks and/or the pre-SOFs to aid the dissolution of the molecular building blocks and pre-SOFs. The reaction mixture may also be mixed, stirred, milled, or the like, to ensure even distribution of the formulation components prior to depositing the reaction mixture as a wet film.
In embodiments, the reaction mixture may be heated prior to being deposited as a wet film. This may aid the dissolution of one or more of the molecular building blocks and/or increase the viscosity of the reaction mixture by the partial reaction of the reaction mixture prior to depositing the wet layer to form pre-SOFs. For example, the weight percent of molecular building blocks in the reaction mixture that are incorporated into pre-reacted molecular building blocks pre-SOFs may be less than 20%, such as about 15% to about 1%, or 10% to about 5%. In embodiments, the molecular weight of the 95% pre-SOF molecules is less than 5,000 daltons, such as 2,500 daltons, or 1,000 daltons. The preparation of pre-SOFs may be used to increase the loading of the molecular building blocks in the reaction mixture.
In the case of pre-SOF formation via functional group activation, the molar percentage of functional groups that are activated may be less than 50%, such as about 30% to about 10%, or about 10% to about 5%.
In embodiments, the two methods of pre-SOF formation (pre-SOF formation by the reaction between molecular building blocks or pre-SOF formation by the ‘activation’ of molecular building block functional groups) may occur in combination and the molecular building blocks incorporated into pre-SOF structures may contain activated functional groups. In embodiments, pre-SOF formation by the reaction between molecular building blocks and pre-SOF formation by the ‘activation’ of molecular building block functional groups may occur simultaneously.
In embodiments, the duration of pre-SOF formation lasts about 10 seconds to about 48 hours, such as about 30 seconds to about 12 hours, or about 1 minute to 6 hours.
In particular embodiments, the reaction mixture needs to have a viscosity that will support the deposited wet layer. Reaction mixture viscosities range from about 10 to about 50,000 cps, such as from about 25 to about 25,000 cps or from about 50 to about 1000 cps.
The molecular building block loading or “loading” in the reaction mixture is defined as the total weight of the molecular building blocks and optionally the catalysts divided by the total weight of the reaction mixture. Building block loadings may range from about 3 to 100%, such as from about 5 to about 50%, or from about 15 to about 40%. In the case where a liquid molecular building block is used as the only liquid component of the reaction mixture (i.e. no additional liquid is used), the building block loading would be about 100%.
In embodiments, the pre-SOF may be made from building blocks with one or more of the added functionality selected from the group consisting of hydrophobic added functionality, superhydrophobic added functionality, hydrophilic added functionality, lipophobic added functionality, superlipophobic added functionality, lipophilic added functionality, photochromic added functionality, and electroactive added functionality. In embodiments, the inclined property of the molecular building blocks is the same as the added functionality of the pre-SOF. In embodiments, the added functionality of the SOF is not an inclined property of the molecular building blocks.
Liquids used in the reaction mixture may be pure liquids, such as solvents, and/or solvent mixtures. Liquids are used to dissolve or suspend the molecular building blocks and catalyst/modifiers in the reaction mixture. Liquid selection is generally based on balancing the solubility/dispersion of the molecular building blocks and a particular building block loading, the viscosity of the reaction mixture, and the boiling point of the liquid, which impacts the promotion of the wet layer to the dry SOF. Suitable liquids may have boiling points from about 30 to about 300° C., such as from about 65° C. to about 250° C., or from about 100° C. to about 180° C.
Liquids can include molecule classes such as alkanes (hexane, heptane, octane, nonane, decane, cyclohexane, cycloheptane, cyclooctane, decalin); mixed alkanes (hexanes, heptanes); branched alkanes (isooctane); aromatic compounds (toluene, o-, m-, p-xylene, mesitylene, nitrobenzene, benzonitrile, butylbenzene, aniline); ethers (benzyl ethyl ether, butyl ether, isoamyl ether, propyl ether); cyclic ethers (tetrahydrofuran, dioxane), esters (ethyl acetate, butyl acetate, butyl butyrate, ethoxyethyl acetate, ethyl propionate, phenyl acetate, methyl benzoate); ketones (acetone, methyl ethyl ketone, methyl isobutylketone, diethyl ketone, chloroacetone, 2-heptanone), cyclic ketones (cyclopentanone, cyclohexanone), amines (1°, 2°, or 3° amines such as butylamine, diisopropylamine, triethylamine, diisoproylethylamine; pyridine); amides (dimethylformamide, N-methylpyrolidinone, N,N-dimethylformamide); alcohols (methanol, ethanol, n-, i-propanol, n-, t-butanol, 1-methoxy-2-propanol, hexanol, cyclohexanol, 3-pentanol, benzyl alcohol); nitriles (acetonitrile, benzonitrile, butyronitrile), halogenated aromatics (chlorobenzene, dichlorobenzene, hexafluorobenzene), halogenated alkanes (dichloromethane, chloroform, dichloroethylene, tetrachloroethane); and water.
Mixed liquids comprising a first solvent, second solvent, third solvent, and so forth may also be used in the reaction mixture. Two or more liquids may be used to aid the dissolution/dispersion of the molecular building blocks; and/or increase the molecular building block loading; and/or allow a stable wet film to be deposited by aiding the wetting of the substrate and deposition instrument; and/or modulate the promotion of the wet layer to the dry SOF. In embodiments, the second solvent is a solvent whose boiling point or vapor-pressure curve or affinity for the molecular building blocks differs from that of the first solvent. In embodiments, a first solvent has a boiling point higher than that of the second solvent. In embodiments, the second solvent has a boiling point equal to or less than about 130° C., such as a boiling point equal to or less than about 100° C., for example in the range of from about 30° C. to about 100° C., or in the range of from about 40° C. to about 90° C., or about 50° C. to about 80° C.
In embodiments, the first solvent, or higher boiling point solvent, has a boiling point equal to or greater than about 65° C., such as in the range of from about 80° C. to about 300° C., or in the range of from about 100° C. to about 250° C., or about 100° C. to about 180° C. The higher boiling point solvent may include, for example, the following (the value in parentheses is the boiling point of the compound): hydrocarbon solvents such as amylbenzene (202° C.), isopropylbenzene (152° C.), 1,2-diethylbenzene (183° C.), 1,3-diethylbenzene (181° C.), 1,4-diethylbenzene (184° C.), cyclohexylbenzene (239° C.), dipentene (177° C.), 2,6-dimethylnaphthalene (262° C.), p-cymene (177° C.), camphor oil (160-185° C.), solvent naphtha (110-200° C.), cis-decalin (196° C.), trans-decalin (187° C.), decane (174° C.), tetralin (207° C.), turpentine oil (153-175° C.), kerosene (200-245° C.), dodecane (216° C.), dodecylbenzene (branched), and so forth; ketone and aldehyde solvents such as acetophenone (201.7° C.), isophorone (215.3° C.), phorone (198-199° C.), methylcyclohexanone (169.0-170.5° C.), methyl n-heptyl ketone (195.3° C.), and so forth; ester solvents such as diethyl phthalate (296.1° C.), benzyl acetate (215.5° C.), γ-butyrolactone (204° C.), dibutyl oxalate (240° C.), 2-ethylhexyl acetate (198.6° C.), ethyl benzoate (213.2° C.), benzyl formate (203° C.), and so forth; diethyl sulfate (208° C.), sulfolane (285° C.), and halohydrocarbon solvents; etherified hydrocarbon solvents; alcohol solvents; ether/acetal solvents; polyhydric alcohol solvents; carboxylic anhydride solvents; phenolic solvents; water; and silicone solvents.
The ratio of the mixed liquids may be established by one skilled in the art. The ratio of liquids a binary mixed liquid may be from about 1:1 to about 99:1, such as from about 1:10 to about 10:1, or about 1:5 to about 5:1, by volume. When n liquids are used, with n ranging from about 3 to about 6, the amount of each liquid ranges from about 1% to about 95% such that the sum of each liquid contribution equals 100%.
In embodiments, the mixed liquid comprises at least a first and a second solvent with different boiling points. In further embodiments, the difference in boiling point between the first and the second solvent may be from about nil to about 150° C., such as from nil to about 50° C. For example, the boiling point of the first solvent may exceed the boiling point of the second solvent by about 1° C. to about 100° C., such as by about 5° C. to about 100° C., or by about 10° C. to about 50° C. The mixed liquid may comprise at least a first and a second solvent with different vapor pressures, such as combinations of high vapor pressure solvents and/or low vapor pressure solvents. The term “high vapor pressure solvent” refers to, for example, a solvent having a vapor pressure of at least about 1 kPa, such as about 2 kPa, or about 5 kPa. The term “low vapor pressure solvent” refers to, for example, a solvent having a vapor pressure of less than about 1 kPa, such as about 0.9 kPa, or about 0.5 kPa. In embodiments, the first solvent may be a low vapor pressure solvent such as, for example, terpineol, diethylene glycol, ethylene glycol, hexylene glycol, N-methyl-2-pyrrolidone, and tri(ethylene glycol) dimethyl ether. A high vapor pressure solvent allows rapid removal of the solvent by drying and/or evaporation at temperatures below the boiling point. High vapor pressure solvents may include, for example, acetone, tetrahydrofuran, toluene, xylene, ethanol, methanol, 2-butanone and water.
In embodiments where mixed liquids comprising a first solvent, second solvent, third solvent, and so forth are used in the reaction mixture, promoting the change of the wet film and forming the dry SOF may comprise, for example, heating the wet film to a temperature above the boiling point of the reaction mixture to form the dry SOF film; or heating the wet film to a temperature above the boiling point of the second solvent (below the temperature of the boiling point of the first solvent) in order to remove the second solvent while substantially leaving the first solvent and then after substantially removing the second solvent, removing the first solvent by heating the resulting composition at a temperature either above or below the boiling point of the first solvent to form the dry SOF film; or heating the wet film below the boiling point of the second solvent in order to remove the second solvent (which is a high vapor pressure solvent) while substantially leaving the first solvent and, after removing the second solvent, removing the first solvent by heating the resulting composition at a temperature either above or below the boiling point of the first solvent to form the dry SOF film.
The term “substantially removing” refers to, for example, the removal of at least 90% of the respective solvent, such as about 95% of the respective solvent. The term “substantially leaving” refers to, for example, the removal of no more than 2% of the respective solvent, such as removal of no more than 1% of the respective solvent.
These mixed liquids may be used to slow or speed up the rate of conversion of the wet layer to the SOF in order to manipulate the characteristics of the SOFs. For example, in condensation and addition/elimination linking chemistries, liquids such as water, 1°, 2°, or 3° alcohols (such as methanol, ethanol, propanol, isopropanol, butanol, 1-methoxy-2-propanol, tert-butanol) may be used.
Optionally a catalyst may be present in the reaction mixture to assist the promotion of the wet layer to the dry SOF. Selection and use of the optional catalyst depends on the functional groups on the molecular building blocks. Catalysts may be homogeneous (dissolved) or heterogeneous (undissolved or partially dissolved) and include Brönsted acids (HCl(aq), acetic acid, p-toluenesulfonic acid, amine-protected p-toluenesulfonic acid such as pyrridium p-toluenesulfonate, trifluoroacetic acid); Lewis acids (boron trifluoroetherate, aluminum trichloride); Brönsted bases (metal hydroxides such as sodium hydroxide, lithium hydroxide, potassium hydroxide; 1°, 2°, or 3° amines such as butylamine, diisopropylamine, triethylamine, diisoproylethylamine); Lewis bases (N,N-dimethyl-4-aminopyridine); metals (Cu bronze); metal salts (FeCl3, AuCl3); and metal complexes (ligated palladium complexes, ligated ruthenium catalysts). Typical catalyst loading ranges from about 0.01% to about 25%, such as from about 0.1% to about 5% of the molecular building block loading in the reaction mixture. The catalyst may or may not be present in the final SOF composition.
Optionally additives or secondary components may be present in the reaction mixture and wet layer. Such additives or secondary components may also be integrated into a dry SOF. Additives or secondary components can be homogeneous or heterogeneous in the reaction mixture and wet layer or in a dry SOF. The terms “additive” or “secondary component,” refer, for example, to atoms or molecules that are not covalently bound in the SOF, but are randomly distributed in the composition. Additives may be used to alter the physical properties of the SOF such as electrical properties (conductivity, semiconductivity, electron transport, hole transport), surface energy (hydrophobicity, hydrophilicity), tensile strength, thermal conductivity, impact modifiers, reinforcing fibers, antiblocking agents, lubricants, antistatic agents, coupling agents, wetting agents, antifogging agents, flame retardants, ultraviolet stabilizers, antioxidants, biocides, dyes, pigments, odorants, deodorants, nucleating agents and the like.
Process Action B: Depositing the Reaction Mixture as a Wet Film
The reaction mixture may be applied as a wet film to a variety of substrates using a number of liquid deposition techniques. The thickness of the SOF is dependant on the thickness of the wet film and the molecular building block loading in the reaction mixture. The thickness of the wet film is dependent on the viscosity of the reaction mixture and the method used to deposit the reaction mixture as a wet film.
Substrates include, for example, polymers, papers, metals and metal alloys, doped and undoped forms of elements from Groups III-VI of the periodic table, metal oxides, metal chalcogenides, and previously prepared SOF films. Examples of polymer film substrates include polyesters, polyolefins, polycarbonates, polystyrenes, polyvinylchloride, block and random copolymers thereof, and the like. Examples of metallic surfaces include metallized polymers, metal foils, metal plates; mixed material substrates such as metals patterned or deposited on polymer, semiconductor, metal oxide, or glass substrates. Examples of substrates comprised of doped and undoped elements from Groups III-VI of the periodic table include, aluminum, silicon, silicon n-doped with phosphorous, silicon p-doped with boron, tin, gallium arsenide, lead, gallium indium phosphide, and indium. Examples of metal oxides include silicon dioxide, titanium dioxide, indium tin oxide, tin dioxide, selenium dioxide, and alumina. Examples of metal chalcogenides include cadmium sulfide, cadmium telluride, and zinc selenide. Additionally, it is appreciated that chemically treated or mechanically modified forms of the above substrates remain within the scope of surfaces which may be coated with the reaction mixture.
In embodiments, the substrate may be composed of, for example, silicon, glass plate, plastic film or sheet. For structurally flexible devices, a plastic substrate such as polyester, polycarbonate, polyimide sheets and the like may be used. The thickness of the substrate may be from around 10 micrometers to over 10 millimeters with an exemplary thickness being from about 50 to about 100 micrometers, especially for a flexible plastic substrate, and from about 1 to about 10 millimeters for a rigid substrate such as glass or silicon.
The reaction mixture may be applied to the substrate using a number of liquid deposition techniques including, for example, spin coating, blade coating, web coating, dip coating, cup coating, rod coating, screen printing, ink jet printing, spray coating, stamping and the like. The method used to deposit the wet layer depends on the nature, size, and shape of the substrate and the desired wet layer thickness. The thickness of the wet layer can range from about 10 nm to about 5 mm, such as from about 100 nm to about 1 mm, or from about 1 μm to about 500 μm.
Process Action C: Promoting the Change of Wet Film to the Dry SOF
The term “promoting” refers, for example, to any suitable technique to facilitate a reaction of the molecular building blocks. In the case where a liquid needs to be removed to form the dry film, “promoting” also refers to removal of the liquid. Reaction of the molecular building blocks and removal of the liquid can occur sequentially or concurrently.
In embodiments, the term “promoting” may also refer, for example, to any suitable technique to facilitate a reaction of the molecular building blocks and/or pre-SOFs, such as a chemical reaction of the functional groups of the building blocks and/or pre-SOFs. Reaction of the molecular building blocks and/or pre-SOFs and removal of the liquid can occur sequentially or concurrently.
In certain embodiments, the liquid is also one of the molecular building blocks and is incorporated into the SOF. The term “dry SOF” refers, for example, to substantially dry films such as, for example, a substantially dry SOF may have a liquid content less than about 5% by weight of the SOF, or a liquid content less than about 2% by weight of the SOF.
Promoting the wet layer to form a dry SOF may be accomplished by any suitable technique. Promoting the wet layer to form a dry SOF typically involves thermal treatment including, for example, oven drying, infrared radiation (IR), and the like with temperatures ranging from 40 to 350° C. and from 60 to 200° C. and from 85 to 160° C. The total heating time can range from about four seconds to about 24 hours, such as from one minute to 120 minutes, or from three minutes to 60 minutes.
IR promotion of the wet layer to the COF film may be achieved using an IR heater module mounted over a belt transport system. Various types of IR emitters may be used, such as carbon IR emitters or short wave IR emitters (available from Heraerus). Additional exemplary information regarding carbon IR emitters or short wave IR emitters is summarized in the following Table.
Process Action D: Optionally Removing the SOF from the Coating Substrate to Obtain a Free-Standing SOF
In embodiments, a free-standing SOF is desired. Free-standing SOFs may be obtained when an appropriate low adhesion substrate is used to support the deposition of the wet layer. Appropriate substrates that have low adhesion to the SOF may include, for example, metal foils, metalized polymer substrates, release papers and SOFs, such as SOFs prepared with a surface that has been altered to have a low adhesion or a decreased propensity for adhesion or attachment. Removal of the SOF from the supporting substrate may be achieved in a number of ways by someone skilled in the art. For example, removal of the SOF from the substrate may occur by starting from a corner or edge of the film and optionally assisted by passing the substrate and SOF over a curved surface.
Process Action E: Optionally Processing the Free-Standing SOF into a Roll
Optionally, a free-standing SOF or a SOF supported by a flexible substrate may be processed into a roll. The SOF may be processed into a roll for storage, handling, and a variety of other purposes. The starting curvature of the roll is selected such that the SOF is not distorted or cracked during the rolling process.
Process Action F: Optionally Cutting and Seaming the SOF into a Shape, Such as a Belt
The method for cutting and seaming the SOF is similar to that described in U.S. Pat. No. 5,455,136 issued on Oct. 3, 1995 (for polymer films), the disclosure of which is herein totally incorporated by reference. An SOF belt may be fabricated from a single SOF, a multi layer SOF or an SOF sheet cut from a web. Such sheets may be rectangular in shape or any particular shape as desired. All sides of the SOF(s) may be of the same length, or one pair of parallel sides may be longer than the other pair of parallel sides. The SOF(s) may be fabricated into shapes, such as a belt by overlap joining the opposite marginal end regions of the SOF sheet. A seam is typically produced in the overlapping marginal end regions at the point of joining. Joining may be affected by any suitable means. Typical joining techniques include, for example, welding (including ultrasonic), gluing, taping, pressure heat fusing and the like. Methods, such as ultrasonic welding, are desirable general methods of joining flexible sheets because of their speed, cleanliness (no solvents) and production of a thin and narrow seam.
Process Action G: Optionally Using a SOF as a Substrate for Subsequent SOF Formation Processes
A SOF may be used as a substrate in the SOF forming process to afford a multi-layered structured organic film. The layers of a multi-layered SOF may be chemically bound in or in physical contact. Chemically bound, multi-layered SOFs are formed when functional groups present on the substrate SOF surface can react with the molecular building blocks present in the deposited wet layer used to form the second structured organic film layer. Multi-layered SOFs in physical contact may not chemically bound to one another.
A SOF substrate may optionally be chemically treated prior to the deposition of the wet layer to enable or promote chemical attachment of a second SOF layer to form a multi-layered structured organic film.
Alternatively, a SOF substrate may optionally be chemically treated prior to the deposition of the wet layer to disable chemical attachment of a second SOF layer (surface pacification) to form a physical contact multi-layered SOF.
Other methods, such as lamination of two or more SOFs, may also be used to prepare physically contacted multi-layered SOFs.
EXAMPLESA number of examples of the process used to make SOFs are set forth herein and are illustrative of the different compositions, conditions, techniques that may be utilized. Identified within each example are the nominal actions associated with this activity. The sequence and number of actions along with operational parameters, such as temperature, time, coating method, and the like, are not limited by the following examples. All proportions are by weight unless otherwise indicated. The term “rt” refers, for example, to temperatures ranging from about 20° C. to about 25° C. Mechanical measurements were measured on a TA Instruments DMA Q800 dynamic mechanical analyzer using methods standard in the art. Differential scanning calorimetery was measured on a TA Instruments DSC 2910 differential scanning calorimeter using methods standard in the art. Thermal gravimetric analysis was measured on a TA Instruments TGA 2950 thermal gravimetric analyzer using methods standard in the art. FT-IR spectra was measured on a Nicolet Magna 550 spectrometer using methods standard in the art. Thickness measurements <1 micron were measured on a Dektak 6m Surface Profiler. Surface energies were measured on a Fibro DAT 1100 (Sweden) contact angle instrument using methods standard in the art. Unless otherwise noted, the SOFs produced in the following examples were either defect-free SOFs or substantially defect-free SOFs.
The SOFs coated onto Mylar were delaminated by immersion in a room temperature water bath. After soaking for 10 minutes the SOF film generally detached from Mylar substrate. This process is most efficient with a SOF coated onto substrates known to have high surface energy (polar), such as glass, mica, salt, and the like.
Given the examples below it will be apparent, that the compositions prepared by the methods of the present disclosure may be practiced with many types of components and may have many different uses in accordance with the disclosure above and as pointed out hereinafter.
Embodiment of a Patterned SOF Composition
An embodiment of the disclosure is to attain a SOF wherein the microscopic arrangement of segments is patterned. The term “patterning” refers, for example, to the sequence in which segments are linked together. A patterned SOF would therefore embody a composition wherein, for example, segment A is only connected to segment B, and conversely, segment B is only connected to segment A. Further, a system wherein only one segment exists, say segment A, is employed is will be patterned because A is intended to only react with A. In principle a patterned SOF may be achieved using any number of segment types. The patterning of segments may be controlled by using molecular building blocks whose functional group reactivity is intended to compliment a partner molecular building block and wherein the likelihood of a molecular building block to react with itself is minimized. The aforementioned strategy to segment patterning is non-limiting. Instances where a specific strategy to control patterning has not been deliberately implemented are also embodied herein.
A patterned film may be detected using spectroscopic techniques that are capable of assessing the successful formation of linking groups in a SOF. Such spectroscopies include, for example, Fourier-transfer infrared spectroscopy, Raman spectroscopy, and solid-state nuclear magnetic resonance spectroscopy. Upon acquiring a data by a spectroscopic technique from a sample, the absence of signals from functional groups on building blocks and the emergence of signals from linking groups indicate the reaction between building blocks and the concomitant patterning and formation of an SOF.
Different degrees of patterning are also embodied. Full patterning of a SOF will be detected by the complete absence of spectroscopic signals from building block functional groups. Also embodied are SOFs having lowered degrees of patterning wherein domains of patterning exist within the SOF. SOFs with domains of patterning, when measured spectroscopically, will produce signals from building block functional groups which remain unmodified at the periphery of a patterned domain.
It is appreciated that a very low degree of patterning is associated with inefficient reaction between building blocks and the inability to form a film. Therefore, successful implementation of the process of the present disclosure requires appreciable patterning between building blocks within the SOF. The degree of necessary patterning to form a SOF is variable and can depend on the chosen building blocks and desired linking groups. The minimum degree of patterning required is that required to form a film using the process described herein, and may be quantified as formation of about 20% or more of the intended linking groups, such as about 40% or more of the intended linking groups or about 50% or more of the intended linking groups; the nominal degree of patterning embodied by the present disclosure is formation of about 60% of the intended linking group, such as formation of about 100% of the intended linking groups. Formation of linking groups may be detected spectroscopically as described earlier in the embodiments.
Production of a Patterned SOF
The following experiments demonstrate the development of a patterned SOF. The activity described below is non-limiting as it will be apparent that many types of approaches may be used to generate patterning in a SOF.
EXAMPLE 1 describes the synthesis of a Type 2 SOF wherein components are combined such that etherification linking chemistry is promoted between two building blocks. The presence of an acid catalyst and a heating action yield a SOF with the method described in EXAMPLE 1.
Example 1 Type 2 SOF(Action A) Preparation of the Liquid Containing Reaction Mixture.
The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.47 g, 3.4 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.12 g, 1.7 mmol)], and 17.9 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.31 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture.
(Action B) Deposition of Reaction Mixture as a Wet Film.
The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 8 mil gap.
(Action C) Promotion of the Change of the Wet Film to a Dry SOF.
The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 3-6 microns, which may be delaminated from the substrate as a single free-standing SOF. The color of the SOF was green. The Fourier-transform infrared spectrum of a portion of this SOF is provided in
To demonstrate that the SOF prepared in EXAMPLE 1 comprises segments from the employed molecular building blocks that are patterned within the SOF, three control experiments were conducted. Namely, three liquid reaction mixtures were prepared using the same procedure as set forth in Action A in EXAMPLE 1; however, each of these three formulations were modified as follows:
-
- (Control reaction mixture 1; Example 2) the building block benzene-1,4-dimethanol was not included.
- (Control reaction mixture 2; Example 3) the building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine was not included.
- (Control reaction mixture 3; Example 4) the catalyst p-toluenesulfonic acid was not included
The full descriptions of the SOF forming process for the above described control experiments are detailed in EXAMPLES 2-4 below.
Example 2 Control Experiment Wherein the Building Block Benzene-1,4-Dimethanol was not Included(Action A) Preparation of the Liquid Containing Reaction Mixture.
The following were combined: the building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.12 g, 1.7 mmol)], and 17.9 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.31 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture.
(Action B) Deposition of Reaction Mixture as a Wet Film.
The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 8 mil gap.
(Action C) Attempted Promotion of the Change of the Wet Film to a Dry SOF.
The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions did not provide a film. Instead, a precipitated powder of the building block was deposited onto the substrate.
Example 3 (Control Experiment Wherein the Building Block N4,N4,N4′,N4′-Tetrakis(4-(Methoxymethyl)Phenyl)Biphenyl-4,4′-Diamine was not Included)(Action A) Preparation of the Liquid Containing Reaction Mixture.
The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.47 g, 3.4 mmol)] and 17.9 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.31 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture.
(Action B) Deposition of Reaction Mixture as a Wet Film.
The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 8 mil gap.
(Action C) Attempted Promotion of the Change of the Wet Film to a Dry SOF.
The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions did not provide a film. Instead, a precipitated powder of the building block was deposited onto the substrate.
Example 4 Control Experiment Wherein the Acid Catalyst p-Toluenesulfonic Acid was not Included(Action A) Preparation of the liquid containing reaction mixture. The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.47 g, 3.4 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.12 g, 1.7 mmol)], and 17.9 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane to yield the liquid containing reaction mixture.
(Action B) Deposition of Reaction Mixture as a Wet Film.
The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 8 mil gap.
(Action C) Attempted Promotion of the Change of the Wet Film to a Dry SOF.
The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions did not provide a film. Instead, a precipitated powder of the building blocks was deposited onto the substrate.
As described in EXAMPLES 2-4, each of the three control reaction mixtures were subjected to Action B and Action C as outlined in EXAMPLE 1. However, in all cases a SOF did not form; the building blocks simply precipitated on the substrate. It is concluded from these results that building blocks cannot react with themselves under the stated processing conditions nor can the building blocks react in the absence of a promoter (p-toluenesulfonic acid). Therefore, the activity described in EXAMPLE 1 is one wherein building blocks (benzene-1,4-dimethanol and N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine) can only react with each other when promoted to do so. A patterned SOF results when the segments p-xylyl and N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine connect only with each other. The Fourier-transform infrared spectrum, compared to that of the products of the control experiments (
Described below are further Examples of defect-free SOFs and/or substantially defect-free SOFs prepared in accordance with the present disclosure. In the following examples (Action A) is the preparation of the liquid containing reaction mixture; (Action B) is the deposition of reaction mixture as a wet film; and (Action C) is the promotion of the change of the wet film to a dry SOF.
Example 5 Type 2 SOF(Action A) The following were combined: the building block benzene-1,3,5-trimethanol [segment=benzene-1,3,5-trimethyl; Fg=hydroxyl (—OH); (0.2 g, 1.2 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.59 g, 0.8 mmol)], and 8.95 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.16 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 20 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 2-4 microns that could be delaminated from the substrate as a single free-standing SOF. The color of the SOF was green.
Example 6 Type 2 SOF(Action A) The following were combined: the building block 1,6-n-hexanediol [segment=n-hexyl; Fg=hydroxyl (—OH); (0.21 g, 1.8 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.58 g, 0.87 mmol)], and 8.95 g of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.16 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 20 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 4-5 microns that could be delaminated from the substrate as a single free standing SOF. The color of the SOF was green. The Fourier-transform infrared spectrum of a portion of this SOF is provided in
(Action A) The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.64 g, 4.6 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.54 g, 2.3 mmol)], and 7.51 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted, which was then filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.28 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 4 min. These actions provided a SOF having a thickness ranging from about 8-12 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green.
Example 8 Type 2 SOF(Action A) The following were combined: the building block 1,6-n-hexanediol [segment=n-hexyl; Fg=hydroxyl (—OH); (0.57 g, 4.8 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.61 g, 2.42 mmol)], and 7.51 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to rt, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 12-20 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green.
Example 9 Type 2 SOF(Action A) The following were combined: the building block 4,4′-(cyclohexane-1,1-diyl)diphenol [segment=4,4′-(cyclohexane-1,1-diyl)diphenyl; Fg=hydroxyl (—OH); (0.97 g, 6 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.21 g, 1.8 mmol)], and 7.51 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to rt, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 12-20 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green. The Fourier-transform infrared spectrum of SOF is provided in
(Action A) The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.52 g, 3.8 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.26 g, 1.9 mmol)], and 6.3 g of 1,4-dioxane and 1.57 g of n-butyl acetate. The mixture was shaken and heated to 60° C. until a homogenous solution resulted, which was then filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.28 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 4 min. These actions provided a SOF having a thickness of 7-10 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green.
Example 11 Type 2 SOF(Action A) Same as EXAMPLE 7. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 20 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 12 Type 2 SOF(Action A) The following were combined: the building block benzene-1,4-dimethanol [segment=p-xylyl; Fg=hydroxyl (—OH); (0.52 g, 3.8 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.26 g, 1.9 mmol)], and 6.3 g of 1,4-dioxane and 1.57 g of methyl isobutyl ketone. The mixture was shaken and heated to 60° C. until a homogenous solution resulted, which was then filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.28 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 4 min. These actions provided a SOF having a thickness ranging from about 7-10 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green.
Example 13 Type 2 SOF(Action A) The following were combined: the building block 1,6-n-hexanediol [segment=n-hexyl; Fg=hydroxyl (—OH); (0.47 g, 4.0 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.31 g, 2.0 mmol)], 6.3 g of 1,4-dioxane, and 1.57 g of n-butyl acetate. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 8-12 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green.
Example 14 Type 2 SOF(Action A) Same as EXAMPLE 10. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 20 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 15 Type 2 SOF(Action A) The following were combined: the building block 1,6-n-hexanediol [segment=n-hexyl; Fg=hydroxyl (—OH); (0.47 g, 4.0 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (1.31 g, 2.0 mmol)], 6.3 g of 1,4-dioxane, and 1.57 g of methyl isobutyl ketone. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 8-12 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green.
Example 16 Type 2 SOF(Action A) The following were combined: the building block 4,4′-(cyclohexane-1,1-diyl)diphenol [segment=4,4′-(cyclohexane-1,1-diyl)diphenyl; Fg=hydroxyl (—OH); (0.8 g)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.8 g, 1.5 mmol)], 1,4-dioxane, and 1.57 g of n-butyl acetate. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to rt, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided SOF having a thickness of about 12 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green.
Example 17 Type 2 SOF(Action A) Same as EXAMPLE 13. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 20 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 18 Type 2 SOF(Action A) The following were combined: the building block 4,4′-(cyclohexane-1,1-diyl)diphenol [segment=4,4′-(cyclohexane-1,1-diyl)diphenyl; Fg=hydroxyl (—OH); (0.8 g, 3.0 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.8 g, 1.5 mmol)], 1,4-dioxane, and 1.57 g of methyl isobutyl ketone. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.22 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided SOF having a thickness of about 12 microns that could be delaminated from the substrate as a single free-standing film. The color of the SOF was green.
Example 19 Type 2 SOF(Action A) Same as EXAMPLE 7. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 20 Type 2 SOF(Action A) Same as EXAMPLE 10. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 21 Type 2 SOF(Action A) Same as EXAMPLE 13. (Action B) The reaction mixture was applied to a photoconductive layer, containing a pigment and polymeric binder, supported on metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns and could not be delaminated.
Example 22 Type 2 SOF(Action A) Same as EXAMPLE 7. (Action B) The reaction mixture was applied to a layered photosensitive member comprising a generator layer and a transport layer containing a diamine type molecule dispersed in a polymeric binder using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 23 Type 2 SOF(Action A) Same as EXAMPLE 10. (Action B) The reaction mixture was applied to layered photosensitive member comprising a generator layer and a transport layer containing a diamine type molecule dispersed in a polymeric binder using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 24 Type 2 SOF(Action A) Same as EXAMPLE 13. (Action B) The reaction mixture was applied to layered photosensitive member comprising a generator layer and a transport layer containing a diamine type molecule dispersed in a polymeric binder using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The supported wet layer was allowed to dry at ambient temperature in an actively vented fume hood for 5 min and was then transferred to an actively vented oven preheated to 120° C. and left to heat for 15 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness ranging from about 9-10 microns.
Example 25 Type 1 SOF(Action A) The following were combined: the building block (4,4′,4″,4′″-(biphenyl-4,4′-diylbis(azanetriyl))tetrakis(benzene-4,1-diyl))tetramethanol [segment=(4,4′,4″,4′″-(biphenyl-4,4′-diylbis(azanetriyl))tetrakis(benzene-4,1-diyl); Fg=alcohol (—OH); (1.48 g, 2.4 mmol)], and 8.3 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.15 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 25 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided SOF having a thickness ranging from about 8-24 microns. The color of the SOF was green.
Example 26 Type 1 SOF(Action A) The following were combined: the building 4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethanol [segment=(4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethyl); Fg=alcohol (—OH); (1.48 g, 4.4 mmol)], and 8.3 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.15 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 15 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided SOF having a thickness ranging from about 6-15 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green. The Fourier-transform infrared spectrum of this film is provided in
(Action A) The following were combined: the building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.26 g, 0.40 mmol)] and a second building block 3,3′-(4,4′-(biphenyl-4-ylazanediyl)bis(4,1-phenylene))dipropan-1-ol [segment=3,3′-(4,4′-(biphenyl-4-ylazanediyl)bis(4,1-phenylene))dipropyl; Fg=hydroxy (—OH); (0.34 g, 0.78 mmol)], and 1.29 mL of 1-methoxy-2-propanol. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.2 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 8 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 150° C. and left to heat for 40 min. These actions provided SOF having a thickness ranging from about 15-20 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green.
Example 28 Type 2 SOF(Action A) Same as EXAMPLE 24. (Action B) The reaction mixture was applied to layered photosensitive member comprising a generator layer and a transport layer containing a diamine type molecule dispersed in a polymeric binder using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The supported wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness of about 5 microns.
Example 29 Type 2 SOF(Action A) Same as EXAMPLE 24. (Action B) The reaction mixture was applied to layered photosensitive member comprising a generator layer and a transport layer containing a diamine type molecule dispersed in a polymeric binder affixed to a spin coating device rotating at 750 rpm. The liquid reaction mixture was dropped at the centre rotating substrate to deposit the wet layer. (Action C) The supported wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a uniformly coated multilayer device wherein the SOF had a thickness of about 0.2 microns.
Example 30 Type 2 SOF(Action A) The following were combined: the building block terephthalaldehyde [segment=benzene; Fg=aldehyde (—CHO); (0.18 g, 1.3 mmol)] and a second building block tris(4-aminophenyl)amine [segment=triphenylamine; Fg=amine (—NH2); (0.26 g, 0.89 mmol)], and 2.5 g of tetrahydrofuran. The mixture was shaken until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.045 g of a 10 wt % solution of p-toluenesulfonic acid in 1-tetrahydrofuran to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 5 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 40 min. These actions provided a SOF having a thickness of about 6 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was red-orange. The Fourier-transform infrared spectrum of this film is provided in
(Action A) The following were combined: the building block 4,4′,4″-nitrilotribenzaldehyde [segment=triphenylamine; Fg=aldehyde (—CHO); (0.16 g, 0.4 mmol)] and a second building block tris(4-aminophenyl)amine[segment=triphenylamine; Fg=amine (—NH2); (0.14 g, 0.4 mmol)], and 1.9 g of tetrahydrofuran. The mixture was stirred until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 5 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 40 min. These actions provided a SOF having a thickness of about 6 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was red. The Fourier-transform infrared spectrum of this film is provided in
(Action A) The following were combined: the building block glyoxal [segment=single covalent bond; Fg=aldehyde (—CHO); (0.31 g, 5.8 mmol—added as 40 wt % solution in water i.e. 0.77 g aqueous glyoxal)] and a second building block tris(4-aminophenyl)amine [segment=triphenylamine; Fg=amine (—NH2); (1.14 g, (3.9 mmol)], and 8.27 g of tetrahydrofuran. The mixture was shaken until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 10 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging from about 6-12 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was red.
Example 33 Type 2 SOF(Action A) The following were combined: the building block terephthalaldehyde [segment=benzene; Fg=aldehyde (—CHO); (0.18 g, 1.3 mmol)] and a second building block tris(4-aminophenyl)amine [segment=triphenylamine; Fg=amine (—NH2); (0.26 g, 0.89 mmol)], 2.5 g of tetrahydrofuran, and 0.4 g water. The mixture was shaken until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 40 min. These actions provided a SOF having a thickness ranging 6 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was red-orange.
Example 34 Type 1 SOF(Action A) The following were combined: the building block 4,4′,4″-nitrilotribenzaldehyde [segment=triphenylamine; Fg=aldehyde (—CHO); (0.16 g, 0.4 mmol)] and a second building block tris(4-aminophenyl)amine [segment=triphenylamine; Fg=amine (—NH2); (0.14 g, 0.4 mmol)], 1.9 g of tetrahydrofuran, and 0.4 g water. The mixture was stirred until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having an 5 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 120° C. and left to heat for 40 min. These actions provided a SOF having a thickness of about 6 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was red-orange.
Example 35 Type 2 SOF(Action A) Same as EXAMPLE 28. (Action B) The reaction mixture was dropped from a glass pipette onto a glass slide. (Action C) The glass slide was heated to 80° C. on a heating stage yielding a deep red SOF having a thickness of about 200 microns which could be delaminated from the glass slide.
Example 36 Type 1 SOF(Action A) The following were combined: the building block tris-[(4-hydroxymethyl)-phenyl]-amine [segment=tri-(p-tolyl)-amine; Fg=hydroxy (—OH); 5.12 g]; the additives Cymel303 (55 mg) and Silclean 3700 (210 mg), and the catalyst Nacure XP-357 (267 mg) and 1-methoxy-2-propanol (13.27 g). The mixture was mixed on a rolling wave rotator for 10 min and then heated at 55° C. for 65 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 240 mm/min. (Action C) The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a SOF having a thickness of about 6.9 microns.
Example 37 Type 1 SOF with Additives(Action A) The following were combined: the building block tris-[(4-hydroxymethyl)-phenyl]-amine [segment=tri-(p-tolyl)-amine; Fg=hydroxy (—OH); 4.65 g]; the additives Cymel303 (49 mg) and Silclean 3700 (205 mg), and the catalyst Nacure XP-357 (254 mg) and 1-methoxy-2-propanol (12.25 g). The mixture was mixed on a rolling wave rotator for 10 min and then heated at 55° C. for 65 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. A polyethylene wax dispersion (average particle size=5.5 microns, 40% solids in i-propyl alcohol, 613 mg) was added to the reaction mixture which was sonicated for 10 min and mixed on the rotator for 30 min. (Action B) The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 240 mm/min. (Action C) The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a film having a thickness of 6.9 microns with even incorporation of the wax particles in the SOF.
Example 38 Type 2 SOF(Action A) The following were combined: the building block N,N,N′,N′-tetrakis-[(4-hydroxymethyl)phenyl]-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetra-(p-tolyl)biphenyl-4,4′-diamine; Fg=hydroxy (—OH); 3.36 g] and the building block N,N′-diphenyl-N,N′-bis-(3-hydroxyphenyl)-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetraphenyl-biphenyl-4,4′-diamine; Fg—hydroxyl (—OH); 5.56 g]; the additives Cymel303 (480 mg) and Silclean 3700 (383 mg), and the catalyst Nacure XP-357 (480 mg) and 1-methoxy-2-propanol (33.24 g). The mixture was mixed on a rolling wave rotator for 10 min and then heated at 55° C. for 65 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 485 mm/min. (Action C) The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a film having a thickness ranging from 6.0 to 6.2 microns.
Example 39 Type 2 SOF(Action A) The following can be combined: the building block dipropylcarbonate [segment=carbonyl [—C(═O)—]; Fg=propoxy (CH3CH2CH2O—); 4.38 g, 30 mmol] and the building block 1,3,5-trihydroxycyclohexane [segment=cyclohexane; Fg—hydroxyl (—OH); 3.24 g, 20 mmol] and catalyst sodium methoxide (38 mg) and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and heated for 40 min.
Example 40 Type 2 SOF(Action A) The following can be combined: the building block dipropylcarbonate [segment=carbonyl [—C(═O)—]; Fg=propoxy (CH3CH2CH2O—); 4.38 g, 30 mmol] and the building block 1,3,5-trihydroxycyclohexane [segment=cyclohexane; Fg—hydroxyl (—OH); 3.24 g, 20 mmol]; phosphoric acid (2 M aq, 100 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 41 Type 2 SOF(Action A) The following can be combined: the building block 1,1′-carbonyldiimidazole [segment=carbonyl [—C(═O)—]; Fg=imidazole; 4.86 g, 30 mmol] and the building block 1,3,5-trihydroxycyclohexane [segment=cyclohexane; Fg—hydroxyl (—OH); 3.24 g, 20 mmol] and catalyst sodium methoxide (38 mg) and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 42 Type 2 SOF(Action A) The following can be combined: the building block carbonyldiimidazole [segment=carbonyl [—C(═O)—]; Fg=imidazole; 4.86 g, 30 mmol] and the building block 1,3,5-trihydroxycyclohexane [segment=cyclohexane; Fg—hydroxyl (—OH); 3.24 g, 20 mmol]; phosphoric acid (2 M aq, 100 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 43 Type 2 SOF(Action A) The following can be combined: the building block trimesic acid [segment=1,3,5-benzenetricarboxylate; Fg=H; 4.20 g, 20 mmol] and the building block 1,6-hexanediol [segment=hexane; Fg—hydroxyl (—OH); 3.55 g, 30 mmol]; phosphoric acid (2 M aq, 100 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 44 Type 2 SOF(Action A) The following can be combined: the building block trimesic acid [segment=1,3,5-benzenetricarboxylate; Fg=H; 4.20 g, 20 mmol] and the building block 1,6-hexanediol [segment=hexane; Fg—hydroxyl (—OH); 3.55 g, 30 mmol]; N,N-dimethyl-4-aminopyridine (50 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 45 Type 2 SOF(Action A) The following can be combined: the building block trimesic acid [segment=1,3,5-benzenetricarboxylate; Fg=H; 4.20 g, 20 mmol] and the building block hexamethylenediamine [segment=hexane; Fg—amine (—NH2); 3.49 g, 30 mmol]; phosphoric acid (2 M aq, 100 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 46 Type 2 SOF(Action A) The following can be combined: the building block trimesic acid [segment=1,3,5-benzenetricarboxylate; Fg=H; 4.20 g, 20 mmol] and the building block hexamethylenediamine [segment=hexane; Fg—amine (—NH2); 3.49 g, 30 mmol]; N,N-dimethyl-4-aminopyridine (50 mg); and N-methyl-2-pyrrolidinone (25.5 g). The mixture is mixed on a rolling wave rotator for 10 min and filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture is applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 200° C. and left to heat for 40 min.
Example 47 Type 2 SOF(Action A) Preparation of liquid containing reaction mixture. The following can be combined: the building block 1,4-diisocyanatobenzene [segment=phenyl; Fg=isocyanate (—N═C═O); (0.5 g, 3.1 mmol)] and a second building block 4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethanol [segment=(4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethyl); (0.69, 2.1 mmol)] 10.1 g of dimethylformamide, and 1.0 g of triethylamine. The mixture is stirred until a homogenous solution is obtained. Upon cooling to room temperature, the solution is filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture is to be applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 8 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 120 min.
Example 48 Type 2 SOF(Action A) Preparation of liquid containing reaction mixture. The following can be combined: the building block 1,4-diisocyanatohexane [segment=hexyl; Fg=isocyanate (—N═C═O); (0.38 g, 3.6 mmol)] and a second building block triethanolamine [segment=triethylamine; (0.81, 5.6 mmol)] 10.1 g of dimethylformamide, and 1.0 g of triethylamine. The mixture is stirred until a homogenous solution is obtained. Upon cooling to room temperature, the solution is filtered through a 0.45 micron PTFE membrane. (Action B) The reaction mixture is to be applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 8 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 120 min.
Example 49 Type 2 SOF(Action A) The following were combined: the building block N,N,N′,N′-tetrakis-[(4-hydroxymethyl)phenyl]-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetra-(p-tolyl)biphenyl-4,4′-diamine; Fg=hydroxy (—OH); 4.24 g] and the building block N,N′-diphenyl-N,N′-bis-(3-hydroxyphenyl)-terphenyl-4,4′-diamine [segment=N,N,N′,N′-tetraphenyl-terphenyl-4,4′-diamine; Fg—hydroxyl (—OH); 5.62 g]; the additives Cymel303 (530 mg) and Silclean 3700 (420 mg), and the catalyst Nacure XP-357 (530 mg) and 1-methoxy-2-propanol (41.62 g). The mixture was mixed on a rolling wave rotator for 10 min and then heated at 55° C. for 65 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 485 mm/min. (Action C) The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a SOF having a thickness of 6.2 microns.
Example 49 Type 2 SOF Attempt(Action A) Attempted preparation of the liquid containing reaction mixture. The following were combined: the building block tris-[(4-hydroxymethyl)-phenyl]-amine [segment=tri-(p-tolyl)-amine; Fg=hydroxy (—OH); 5.12 g]; the additives Cymel303 (55 mg), Silclean 3700 (210 mg), and 1-methoxy-2-propanol (13.27 g). The mixture was heated to 55° C. for 65 min in an attempt to fully dissolve the molecular building block. However it did not fully dissolve. A catalyst Nacure XP-357 (267 mg) was added and the heterogeneous mixture was further mixed on a rolling wave rotator for 10 min. In this Example, the catalyst was added after the heating step. The solution was not filtered prior to coating due to the amount of undissolved molecular building block. (Action B) Deposition of reaction mixture as a wet film. The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 240 mm/min. (Action C) Promotion of the change of the wet film to a dry film. The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions did not provide a uniform film. There were some regions where a non-uniform film formed that contained particles and other regions where no film was formed at all.
Example 50 Type 2 SOF(Action A) The following were combined: the building block tris-[(4-hydroxymethyl)-phenyl]-amine [segment=tri-(p-tolyl)-amine; Fg=hydroxy (—OH); 5.12 g]; the additives Cymel303 (55 mg) and Silclean 3700 (210 mg), and the catalyst Nacure XP-357 (267 mg) and 1-methoxy-2-propanol (13.27 g). The mixture was mixed on a rolling wave rotator for 10 min and then heated at 55° C. for 65 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. It was noted that the viscosity of the reaction mixture increased after the heating step (although the viscosity of the solution before and after heating was not measured). (Action B) The reaction mixture was applied to a commercially available, 30 mm drum photoreceptor using a cup coater (Tsukiage coating) at a pull-rate of 240 mm/min. (Action C) The photoreceptor drum supporting the wet layer was rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min. These actions provided a SOF having a thickness of 6.9 microns.
Example 51 Type 2 SOF(Action A) The following were combined: the building block N,N,N′,N′-tetrakis-[(4-hydroxymethyl)phenyl]-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetra-(p-tolyl)biphenyl-4,4′-diamine; Fg=hydroxy (—OH); 1.84 g] and the building block 3,3′-(4,4′-(biphenyl-4-ylazanediyl)bis(4,1-phenylene))dipropan-1-ol [segment=3,3′-(4,4′-(biphenyl-4-ylazanediyl)bis(4,1-phenylene))dipropyl; Fg=hydroxy (—OH); (2.41 g] and a catalyst p-toluenesulphonic acid (10 wt % solution in dowanol, 460 mg) and 1-methoxy-2-propanol (16.9 g—containing 50 ppm DC510). The mixture was mixed on a rolling wave rotator for 5 min and then heated at 70° C. for 30 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a production-coated web photoreceptor with a Hirano web coater. Syringe pump speed: 4.5 mL/min. (Action C) The photoreceptor supporting the wet layer was fed at a rate of 1.5 m/min into an actively vented oven preheated to 130° C. for 2 min. These actions provided a SOF overcoat layer having a thickness of 2.1 microns on a photoreceptor.
Example 52 Type 2 SOF(Action A) The following were combined: the building block N,N,N′,N′-tetrakis-[(4-hydroxymethyl)phenyl]-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetra-(p-tolyl)biphenyl-4,4′-diamine; Fg=hydroxy (—OH); 5.0 g] and the building block benzenedimethanol [segment=p-xylyl; Fg—hydroxyl (—OH); 2.32 g] and a catalyst p-toluenesulphonic acid (10 wt % solution in dowanol, 720 mg) and 1-methoxy-2-propanol (22.5 g—containing 50 ppm DC510). The mixture was mixed on a rolling wave rotator for 5 min and then heated at 40° C. for 5 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a production-coated, production web photoreceptor a Hirano web coater. Syringe pump speed: 5 mL/min. (Action C) The photoreceptor supporting the wet layer was fed at a rate of 1.5 m/min into an actively vented oven preheated to 130° C. for 2 min. These actions provided a SOF overcoat layer having a thickness of 2.2 microns on a photoreceptor.
Example 53 Type 2 SOF(Action A) The following were combined: the building block N,N,N′,N′-tetrakis-[(4-hydroxymethyl)phenyl]-biphenyl-4,4′-diamine [segment=N,N,N′,N′-tetra-(p-tolyl)biphenyl-4,4′-diamine; Fg=hydroxy (—OH); 5.0 g] and the building block benzenedimethanol [segment=p-xylyl; Fg—hydroxyl (—OH); 2.32 g] and a catalyst p-toluenesulphonic acid (10 wt % solution in dowanol, 720 mg) and 1-methoxy-2-propanol (22.5 g—containing 50 ppm DC510). The mixture was mixed on a rolling wave rotator for 5 min and then heated at 40° C. for 5 min until a homogenous solution resulted. The mixture was placed on the rotator and cooled to room temperature. The solution was filtered through a 1 micron PTFE membrane. (Action B) The reaction mixture was applied to a production-coated, production web photoreceptor with a Hirano web coater. Syringe pump speed: 10 mL/min. (Action C) The photoreceptor supporting the wet layer was fed at a rate of 1.5 m/min into an actively vented oven preheated to 130° C. for 2 min. These actions provided a SOF overcoat layer having a thickness of 4.3 microns on a photoreceptor.
Example 54(Action A) The following were combined: the building 4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethanol [segment=(4,4′,4″-nitrilotris(benzene-4,1-diyl)trimethyl); Fg=alcohol (—OH); (1.48 g, 4.4 mmol)], 0.5 g water and 7.8 g of 1,4-dioxane. The mixture was shaken and heated to 60° C. until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.15 g of a 10 wt % solution of p-toluenesulfonic acid in 1,4-dioxane to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the reflective side of a metalized (TiZr) MYLAR™ substrate using a constant velocity draw down coater outfitted with a bird bar having a 15 mil gap. (Action C) The metalized MYLAR™ substrate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 130° C. and left to heat for 40 min. These actions provided SOF having a thickness ranging from about 4-10 microns that could be delaminated from substrate as a single free-standing film. The color of the SOF was green. Two-dimensional X-ray scattering data is provided in
(Action A) The following can be combined: the building block 4-hydroxybenzyl alcohol [segment=toluene; Fg=hydroxyl (—OH); (0.0272 g, 0.22 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.0728 g, 0.11 mmol)], and 0.88 g of 1-methoxy-2-propanol and 0.01 g of a 10 wt % solution of silclean in 1-methoxy-2-propanol. The mixture is shaken and heated to 55° C. until a homogenous solution is obtained. Upon cooling to rt, the solution is filtered through a 0.45 micron PTFE membrane. To the filtered solution is added an acid catalyst delivered as 0.01 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the aluminum substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The aluminum substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min.
Example 56 Type 2 SOF(Action A) The following can be combined: the building block 4-(hydroxymethyl)benzoic acid [segment=4-methylbenzaldehyde; Fg=hydroxyl (—OH); (0.0314 g, 0.206 mmol)] and a second building block N4,N4,N4′,N4′-tetrakis(4-(methoxymethyl)phenyl)biphenyl-4,4′-diamine [segment=N4,N4,N4′,N4′-tetra-p-tolylbiphenyl-4,4′-diamine; Fg=methoxy ether (—OCH3); (0.0686 g, 0.103 mmol)], and 0.88 g of 1-methoxy-2-propanol and 0.01 g of a 10 wt % solution of silclean in 1-methoxy-2-propanol. The mixture is shaken and heated to 55° C. until a homogenous solution is obtained. Upon cooling to rt, the solution is filtered through a 0.45 micron PTFE membrane. To the filtered solution is added an acid catalyst delivered as 0.01 g of a 10 wt % solution of p-toluenesulfonic acid in 1-methoxy-2-propanol to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied to the aluminum substrate using a constant velocity draw down coater outfitted with a bird bar having a 5 mil gap. (Action C) The aluminum substrate supporting the wet layer is rapidly transferred to an actively vented oven preheated to 140° C. and left to heat for 40 min.
Example 57 Type 2 SOF(Action A) The following were combined: the building block 1,4 diaminobenzene [segment=benzene; Fg=amine (—NH2); (0.14 g, 1.3 mmol)] and a second building block 1,3,5-triformylbenzene [segment=benzene; Fg=aldehyde (—CHO); (0.144 g, 0.89 mmol)], and 2.8 g of NMP. The mixture was shaken until a homogenous solution resulted. Upon cooling to room temperature, the solution was filtered through a 0.45 micron PTFE membrane. To the filtered solution was added an acid catalyst delivered as 0.02 g of a 2.5 wt % solution of p-toluenesulfonic acid in NMP to yield the liquid containing reaction mixture. (Action B) The reaction mixture was applied quartz plate affixed to the rotating unit of a variable velocity spin coater rotating at 1000 RPM for 30 seconds. (Action C) The quartz plate supporting the wet layer was rapidly transferred to an actively vented oven preheated to 180° C. and left to heat for 120 min. These actions provide a yellow film having a thickness of 400 nm that can be delaminated from substrate upon immersion in water.
It will be appreciated that several of the above-disclosed and other features and functions, or alternatives thereof, may be desirably combined into many other different systems or applications. Various presently unforeseen or unanticipated alternatives, modifications, variations or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompassed by the following claims. Unless specifically recited in a claim, steps or components of claims should not be implied or imported from the specification or any other claims as to any particular order, number, position, size, shape, angle, color, or material.
Claims
1. A process for preparing a structured organic film (SOF) comprising:
- (a) preparing a liquid-containing reaction mixture comprising: a first solvent, a second solvent, and a plurality of molecular building blocks each of the plurality of molecular building blocks being either a segment or linker;
- (b) forming a pre-SOF from the plurality of molecular building blocks;
- (c) depositing the formed pre-SOF as a wet film on a substrate; and
- (d) promoting a change of the wet film to a dry film comprising the SOF as a covalent organic framework (COF), wherein at a macroscopic level the covalent organic framework is a film; wherein the SOF is periodic as determined by two-dimensional X-ray scattering.
2. The process of claim 1, wherein the at least one of the molecular building blocks comprises at least one atom that is not carbon.
3. The process of claim 1, wherein forming the pre-SOF comprises heating.
4. The process of claim 1, wherein forming the pre-SOF comprises irradiating with UV radiation.
5. The process of claim 1, further comprising removing the SOF from the substrate to obtain a free-standing SOF.
6. The process of claim 5, further comprising processing the free-standing SOF into a roll.
7. The process of claim 1, further comprising cutting and seaming the SOF into a belt.
8. The process of claim 1, comprising repeating the steps in SOF formation one or more times, wherein the substrate at each iteration is a prior fabricated SOF.
9. The process of claim 1, wherein promoting a change of the wet film to a dry film comprising the SOF comprises heating to remove the first solvent, the second solvent, or both.
10. The process of claim 1, wherein a catalyst is used in forming the pre-SOF.
11. The process of claim 1, wherein the wet film has a viscosity of about 50 cps to about 1000 cps.
12. A process for preparing a structured organic film (SOF) comprising:
- (a) preparing a liquid-containing reaction mixture comprising: a first solvent, a second solvent, and a plurality of molecular building blocks each of the plurality of molecular building blocks being either a segment or linker;
- (b) forming a pre-SOF from the plurality of molecular building blocks;
- (c) depositing the formed pre-SOF as a wet film on a substrate, wherein the substrate is a prior fabricated SOF; and
- (d) promoting a change of the wet film to a dry film comprising the SOF as a covalent organic framework (COF), wherein at a macroscopic level the covalent organic framework is a film; wherein the SOF is periodic as determined by two-dimensional X-ray
13. The process of claim 12, wherein the at least one of the molecular building blocks comprises at least one atom that is not carbon.
14. The process of claim 12, wherein forming the pre-SOF comprises heating.
15. The process of claim 12, wherein forming the pre-SOF comprises irradiating with UV radiation.
16. The process of claim 12, further comprising removing the SOF from the substrate to obtain a free-standing SOF.
17. The process of claim 16, further comprising processing the free-standing SOF into a roll.
18. The process of claim 12, further comprising cutting and seaming the SOF into a belt.
19. The process of claim 12, wherein promoting a change of the wet film to a dry film comprising the SOF comprises heating to remove the first solvent, the second solvent, or both.
20. The process of claim 12, wherein a catalyst is used in forming the pre-SOF.
Type: Application
Filed: Oct 7, 2016
Publication Date: Jan 26, 2017
Inventors: Adrien P. Côté (Kitchener), Matthew A. Heuft (Oakville)
Application Number: 15/288,301