LIQUID CRYSTAL DISPLAY DEVICE
The liquid crystal display device includes a first substrate, a second substrate, and a liquid crystal layer between the first substrate and the second substrat. The first substrate includes a transistor including an oxide semiconductor film including a channel formation region; a pixel electrode electrically connected to the transistor; an insulating layer in contact with the pixel electrode; and a first common electrode in contact with the insulating layer. The second substrate faces the first substrate and includes a second common electrode. A negative liquid crystal material is used for the liquid crystal layer. The specific resistivity of the liquid crystal material is greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·cm.
The present invention relates to, for example, a semiconductor device, a display device, a light-emitting device, a driving method thereof, or a manufacturing method thereof. In particular, the present invention relates to, for example, an active matrix liquid crystal display device.
2. Description of the Related ArtWith the recent rapid spread of portable information terminals such as smartphones, improvement in their performance has progressed rapidly. Their screens have been increased in size and resolution. In addition to improvement in the resolution of a screen, emphasis has been put on power consumption of a display device. A typical example of the display device is a liquid crystal display device using liquid crystal elements.
Examples of display modes for the liquid crystal display device include a vertical alignment (VA) mode in which liquid crystal molecules with negative dielectric constant anisotropy are aligned vertical to a substrate surface; an in-plane switching (IPS) mode and and a fringe field switching (FFS) mode in which liquid crystal molecules with positive or negative dielectric constant anisotropy are aligned horizontal to a substrate surface and a horizontal electric field is applied to a liquid crystal layer.
For example, as an FFS-mode liquid crystal display device, a display device having high-speed response and wide viewing angle is disclosed (see Patent Document 1). The display device includes a first substrate with a first common electrode layer; liquid crystal between the first substrate and a second substrate; and a means for generating an electric field between the first common electrode layer on the first substrate and both a pixel electrode layer and a second common electrode layer on the second substrate so that the display device provides high-speed responses to high input data rates and allows for wide viewing angles for viewers.
Furthermore, as an FFS-mode liquid crystal display device, a liquid crystal display device capable of high-speed response by driving liquid crystal with two pairs of electrodes is disclosed (see Patent Document 2).
REFERENCE Patent Document [Patent Document 1] Japanese Translation of PCT International Application No. 2006-523850[Patent Document 2] international Publication WO 2013/001979
SUMMARY OF THE INVENTIONFor wide viewing angle and high-speed response, the liquid crystal drive device disclosed in Patent Document 1 uses three electrodes to control liquid crystal molecules. However, even when high-speed response can be achieved, the three electrodes need to be driven separately, which increases the power consumption of the display device.
In the liquid crystal drive device disclosed in Patent Document 2, two pairs of electrodes, that is, four electrodes are used to drive liquid crystal and at least four power supply lines are needed; thus, there is a problem in that die number of power supply lines is increased. The increase in the number of power supply lines complicates a method for driving or controling voltage applied to the liquid crystal and increases power consumption.
In view of the above technical background, an object of one embodiment of the present invention is to provide a liquid crystal display device with low power consumption. Another object of one embodiment of the present invention is to provide a liquid crystal display device in which change in transmittance is reduced. Another object of one embodiment of the present invention is to provide a liquid crystal display device in which change in display luminance is reduced. Another object of one embodiment of the present invention is to provide a liquid crystal display device in which flickers of display are reduced. Another object of one embodiment of the present invention is to provide a liquid crystal display device capable of eye-friendly display. Another object of one embodiment of the present invention is to provide a liquid crystal display device that causes less eye fatigue.
Note that the description of these objects does not disturb the existence of other objects. In one embodiment of the present invention, there is no need to achieve all the objects. Other objects will be apparent from and can be derived from the description of the specification, the drawings, the claims, and the like.
In a liquid crystal display device of one embodiment of the present invention, an insulated-gate field-effect transistor (hereinafter, simply referred to as a transistor) with extremely low off-state current is provided in a pixel in order to keep display of images on a pixel portion after die writing of image signals to the pixel portion is stopped. By using the above transistor as an element for controlling the supply of voltage to a liquid crystal element included in the pixel, the voltage applied to the liquid crystal element can be held for a long time. Thus, for example, in the case where image signals having the same image data are repeatedly written to Use pixel portion during continuous frame periods as in the case of displaying a still image, the displayed image can be maintained even when the driving frequency is lowered by temporarily stopping the writing of image signals to the pixel portion, that is, even when the number of times of writing of image signals in a certain period is reduced.
In the liquid crystal display device of one embodiment of the present invention, a liquid crystal element includes a liquid crystal layer to which an electric field is applied by three electrodes (a pixel electrode, a first common electrode, and a second common electrode). A negative liquid crystal material is used for the liquid crystal layer. The specific resistivity of the liquid crystal material is greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·m. With this structure, the liquid crystal display device causes less change in transmittance and few image flickers perceivable by users even when the number of image signal writing operations in a certain period is reduced.
One embodiment of the present invention can provide a liquid crystal display device with low power consumption. Another embodiment of the present invention can provide a liquid crystal display device with less change in transmittance.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Note that the present invention is not limited to the following description and it is easily understood by those skilled in the an that the mode and details can be variously changed without departing from the scope and spirit of the present invention. Accordingly, the present invention should not be construed as being limited to the description of the embodiments below.
Note that in this specification, a panel in which liquid crystal elements are formed in respective pixels, and a module in which an IC or the like including a driver circuit or a controller is mounted on the panel fall into the category of a liquid crystal display device. Further, an element substrate corresponding to one mode before a liquid crystal element is completed in a manufacturing process of a liquid crystal display device falls into the category of the liquid crystal display device of one embodiment of the present invention.
In addition, the liquid crystal display device of one embodiment of the present invention may include a touch panel which is a position input device capable of detecting a position pointed at with a finger, a stylus, or the like and generating a signal including the positional information.
Embodiment 1In this embodiment, a configuration example of a pixel in a liquid crystal display device of one embodiment of the present invention is described with reference to
The liquid crystal clement 111 includes a pixel electrode, a first common electrode, a second common electrode, and a liquid crystal layer which contains a liquid crystal material and to which a voltage is applied across the pixel electrode, the first common electrode, and the second common electrode.
In the liquid crystal element 111 illustrated in
The transistor 112 controls whether the potential of an image signal input to a wiring SL is applied to the pixel electrode of the liquid crystal element 111. A predetermined reference potential VCOM1 is applied to the first common electrode of the liquid crystal element 111.
Hereinafter, the connection relationship among the liquid crystal element 111, the transistor 112, and the capacitor 113 will be described in detail.
Note that in this specification, the term “connection” means electrical connection and corresponds to a state in which a current, a voltage, or a potential can be supplied or transmitted. Therefore, a state of being “connected” means not only a state of direct connection but also a slate of indirect connection through a circuit element such as a wiring, a resistor, a diode, or a transistor so that a current, a voltage, or a potential can be supplied or transmitted.
In addition, even when different components are connected to each other in a circuit diagram, there is actually a case where one conductive film has functions of a plurality of components, for example, a ease where part of a wiring serves as an electrode. In this specification, the term “connection” also means such a case where one conductive film has functions of a plurality of components.
The terms “source” and “drain” of a transistor interchange with each other depending on the type of the channel of the transistor or levels of potentials applied to the terminals. In general, in an n-channel transistor, a terminal to which a lower potential is applied is called a source, and a terminal to which a higher potential is applied is called a drain. In a p-channel transistor, a terminal to which a lower potential is applied is called a drain, and a terminal to which a higher potential is applied is called a source. In this specification, the connection relation of the transistor is described in some cases assuming that the source and the drain are fixed for convenience; actually, the names of the source and the drain interchange with each other depending on the relation of the potentials.
A source of a transistor means a source region that is part of a semiconductor film functioning as an active layer or a source electrode that is connected to the semiconductor film. Similarly, a drain of a transistor means a drain region that is part of the semiconductor film or a drain electrode that is connected to the semiconductor film. A gate means a gate electrode.
In the pixel 100 illustrated in
In one embodiment of the present invention, the transistor 112 has an extremely low off-state current, so that the voltage applied to the liquid crystal element 111 can be held for a long time. Thus, for example, in the case where image signals having the same image data are written to the pixel 100 during continuous frame periods as in the ease of displaying a still image, the displayed gray scale can be maintained even when the driving frequency is lowered, that is, even when the number of times of writing of image signals to the pixel 100 in a certain period is reduced. For example, by using a highly purified oxide semiconductor for a channel formation region of the transistor 112, the interval between writing operations of image signals can be made longer than or equal to 10 seconds, preferably longer than or equal to 30 seconds, and more preferably longer than or equal to one minute. An increase in the interval between writing operations of image signals results in a reduction in power consumption.
When a semiconductor having a wider bandgap and lower intrinsic carrier density than silicon or germanium, such as an oxide semiconductor, is used for the transistor 112, the withstand voltage of the transistor 112 can be increased and the off-state current can be made extremely low. Thus, as compared to the case where a transistor including a normal semiconductor such as silicon or germanium is used, degradation of the transistor 112 can be prevented and the voltage held in the liquid crystal clement 111 can be maintained.
Note that even when a small amount of charge is leaked through the transistor 112, the electric field applied to the liquid crystal layer might vary depending on some factors after the writing of an image signal is completed.
One of the factors in changing the electric field applied to the liquid crystal layer is adsorption of ionic impurities on an alignment film. A liquid crystal material includes ionic impurities, and when the impurities are adsorbed on the alignment film, an electric field called residual DC is generated in some cases. The residual DC caused by the adsorption of the impurities changes the electric field applied to the liquid crystal layer, thereby changing the transmittance of the liquid crystal element 111. The residual DC increases when a direct-current voltage is applied to the liquid crystal clement for a longer time. Hence, in the case of the driving method with a long interval between writing operations of image signals as in one embodiment of the present invention, the transmittance is mote likely to vary than that in the case of a normal driving method with a frame frequency of about 60 Hz.
Another factor in changing the electric field applied to the liquid crystal layer is a leakage current through the liquid crystal element 111. When a voltage is applied to the liquid crystal element 111, a small amount of leakage current flows between the pixel electrode and the first common electrode or between the pixel electrode and the second common electrode through the liquid crystal layer; accordingly, the absolute value of a voltage applied to the liquid crystal element 111 decreases over time. Hence, in the case of the driving method with a long interval between writing operations of image signals as in one embodiment of the present invention, for example, the transmittance is more likely to vary than that in the case of a normal driving method with a frame frequency of about 60 Hz.
However, in the liquid crystal display device of one embodiment of the present invention, a negative liquid crystal material is used for the liquid crystal layer of the liquid crystal element 111, and the specific resistivity of the liquid crystal material is greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·cm, preferably greater than or equal to 1.0×1014 Ω·cm and less than or equal to 1.0×1016 Ω·cm. Note that the specific resistivity of the liquid crystal material in this specification and the like is measured at 20° C.
A negative liquid crystal material is used for the liquid crystal layer in the liquid crystal element 111, so that change in the transmittance of the liquid crystal clement 111 can be reduced. Furthermore, the specific resistivity of the liquid crystal material is set within the above range, so that leakage current flowing through the liquid crystal element 111 can be reduced.
The transmittance of the liquid crystal element 111 varies depending on the polarity (the positive (+) or negative (−) polarity) applied to the liquid crystal layer. For example, a difference in transmittances due to different polarities in the case of using a positive liquid crystal material for the material of the liquid crystal layer in the liquid crystal element 111 might be different from a difference in transmittances due to different polarities in the case of using a negative liquid crystal material. Here, the difference in transmittances depending on the polarity is described with reference to
For example, a nematic liquid crystal exhibits spontaneous polarization under splay or bend deformation. To liquid crystal molecules themselves, the polarity of an applied voltage docs not essentially make a difference, but spontaneous polarization tends to exhibit opposite behaviors based on the polarities of an electric field. This probably produces a difference in transmittances depending on the polarity. The flexo-electric polarization P that is caused by the flexo-electric effect is expressed by Formula (1) below.
{right arrow over (P)}=esplay({right arrow over (n)}∇·{right arrow over (n)})+ebend({right arrow over (n)}×∇×{right arrow over (n)}) (1)
Here, e represents the flexoelectric coefficient mainly based on molecular shape, and n represents the liquid crystal director. The polarization is expressed as a product of the flexoelectric coefficient and the deformation.
Accordingly, to prevent occurrence of polarization and reduce flickers, it is preferable that the flexo-coefficient or the distortion of orientation be small.
The results of
In the liquid crystal display device of one embodiment of the present invention, driving of the liquid crystal element 111 is controlled by the pixel electrode, the first common electrode, and the second common electrode. A method for driving the liquid crystal element 111 is described below with reference to
The liquid crystal element 111 includes a first common electrode 122 over a substrate 120; an insulating layer 124 over the first common electrode 122; a pixel electrode 126 over the insulating layer 124; a liquid crystal layer 134 over the insulating layer 124 and the pixel electrode 126; a second common electrode 132 over the liquid crystal layer 134; and a substrate 130 over the second common electrode 132. As in
In the cross-sectional view of
In the cross-sectional view of
For example, 5.5 V is applied to the pixel electrode 126; 0 V, the first common electrode 122; and 0.8 V, the second common electrode 132, so that the liquid crystal element 111 illustrated in
Thus, the potential difference between the first common electrode 122 and the second common electrode 132 is smaller than the potential difference between the first common electrode 122 and the pixel electrode 126, whereby change in the transmittance of the liquid crystal layer 134 can be made small.
It is preferable that a negative liquid crystal material with a resistivity of greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·cm be used for the liquid crystal layer 134 of the liquid crystal element 111.
As described above, the liquid crystal layer 134 is controlled by three electrodes (the first common electrode 122, the pixel electrode 126, and the second common electrode 132). and a negative liquid crystal material is used for the liquid crystal layer 134, so that change in the transmittance of the liquid crystal layer 134 can be made small and thus, occurrence of perceivable flickers can be prevented. This is an excellent effect that can be achieved only by one embodiment of the present invention.
Moreover, in the liquid crystal display device of one embodiment of the present invention, the voltage VLC1 of the liquid crystal element 111 can be held by the capacitor 113, which results in a reduction in the area of the capacitor 113. In other words, the perception of flicker can be prevented while the area of the capacitor 113 is reduced. Accordingly, high-definition pixels are achieved and the interval between writing operations of image signals can be increased; it is thus possible to provide an eye-friendly liquid crystal display device that gives less eye fatigue to a user.
Configuration Example of PanelNext, description will be made on a configuration example of a panel which corresponds to one embodiment of the liquid crystal display device.
In a panel 230 illustrated in
Note that the kinds and number of the wirings in the pixel portion 231 can be determined by the structure, number, and arrangement of the pixels 100. Specifically, in the pixel portion 231 illustrated in
In one embodiment of the present invention, since the driver circuit 232 and the driver circuit 233 are operated intermittently, the number of times of writing image signals to the pixel portion 231 can be greatly reduced while the image is continuously displayed. For example, by using a highly purified oxide semiconductor for a channel formation region of the transistor 112, the length of a frame period can be made longer than or equal to 10 seconds, preferably larger than or equal to 30 seconds, and more preferably longer than or equal to one minute. Accordingly, the drive frequency of the driver circuit 232 and the driver circuit 233 can be significantly reduced, leading to a reduction in the power consumption of the liquid crystal display device.
Note that in one embodiment of the present invention, it is possible to employ dot sequential driving in which image signals are sequentially input from the driver circuit 233 to the wirings SL1 to SLx, or line sequential driving in which image signals are concurrently input from the driver circuit 233 to the wirings SL1 to SLx. Alternatively, the liquid crystal display device of one embodiment of the present invention may employ a driving method in which image signals are sequentially input to every plural wirings SL.
The selection of the wirings GL may be performed by either progressive scan or interlaced scan.
Note that the response time of a liquid crystal from application of voltage to saturation of the change in transmittance is generally about ten milliseconds. Thus, the slow response of the liquid crystal tends to be perceived as a blur of a moving image. As a countermeasure, one embodiment of the present invention may employ overdriving in which a voltage applied to the liquid crystal element 111 is temporarily increased so that alignment of the liquid crystal is changed quickly. By overdriving, the response speed of the liquid crystal can be increased, a blur of a moving image can be prevented, and the quality of the moving image can be improved.
Further, if the transmittance of the liquid crystal element 111 keeps changing without reaching a constant value after the transistor 112 is turned off, the relative dielectric constant of the liquid crystal also changes; accordingly, the voltage held in the liquid crystal element 111 easily changes. In particular, in the case where the capacitor 113 connected to the liquid crystal element 111 has small capacitance as in one embodiment of the present invention, the change in the voltage held in the liquid crystal element 111 tends to occur remarkably. However, by the overdriving, the response time can be shortened and therefore the change in the transmittance of the liquid crystal element 111 after the transistor 112 is turned off can be made small. Hence, even in the case where the capacitor 113 connected in parallel to the liquid crystal element 111 has small capacitance, it is possible to prevent the change in the voltage held in the liquid crystal element 111 after the transistor 112 is turned off.
Since a negative liquid crystal material with a resistivity of greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 ·cm is used for the liquid crystal element 111, voltage held in the liquid crystal element 111 can be prevented from varing after the transistor 112 is turned off.
Configuration Example of Structure of Liquid Crystal Display DeviceNext, description will be made on a configuration example of the liquid crystal display device of one embodiment of the present invention.
Note that the controller 241 has a function of supplying the panel 230 with various driving signals for controlling the operation of the driver circuit 232, the driver circuit 233, or the like. Examples of the driving signals include a start pulse signal for controlling the operation of the driver circuit 233, a clock signal for the driver circuit 233, a start pulse signal for controlling the operation of the driver circuit 232, and a clock signal for the driver circuit 232.
The input device 242 has a function of applying data or an instruction to the CPU 243 included in the liquid crystal display device 240. For example, an instruction to transfer the panel 230 from an operation state to a non-operation state, or an instruction to transfer the pixel portion 231 from a non-operation state to an operation stale can be given to the CPU 243 by the input device 242. As the input device 242, a keyboard, a pointing device, a touch panel, or the like can be used.
The CPU 243 has a function of decoding an instruction input from the input device 242 and executing the instruction by totally controlling the operation of various circuits included in the liquid crystal display device 240.
For example, in the case where the instruction to transfer the pixel portion 231 from the operation state to the non-operation state is sent from the input device 242, the CPU 243 gives an instruction to the controller 241 to stop the supply of a power source voltage Vp from the power source circuit 247 to the pixel portion 231, and to stop the supply of a driving signal to the panel 230.
In the case where an instruction to transfer the pixel portion 231 from the non-operation state to the operation state is sent from the input device 242, the CPU 243 gives the instruction to the controller 241 to restart the supply of the power source voltage Vp from the power source circuit 247 to the pixel portion 231, and to restart the supply of the driving signal to the panel 230.
The image memory 245 has a function of storing data 246 which has image data and is input to the liquid crystal display device 240. Note that although just one image memory 245 is provided in the liquid crystal display device 240 in
As the image memory 245, for example, memory circuits such as a dynamic random access memory (DRAM) or a static random access memory (SRAM) can be used. Alternatively, a video RAM (VRAM) may be used as the image memory 245.
The image processing circuit 244 has a function of writing and reading the data 246 to and from the image memory 245 in response to an instruction from the controller 241 and generating an image signal from the data 246.
The power source circuit 247 has a function of supplying the power source voltage Vp to the panel 230 and supplying the potential VCOM1 and the potential VCOM2 to the pixel 100.
Top View of PixelIn the pixel 100 illustrated in
An insulating film 306 is provided over the substrate 302 to cover the conductive film 304. An oxide semiconductor film 308 serving as a channel formation region of the transistor 112 is provided over the insulating film 306 in a region overlapping with the conductive film 304. A conductive film 310 and a conductive film 312 are formed over the oxide semiconductor film 308. A conductive film 313 formed in the same step as the conductive films 310 and 312 is provided over the insulating film 306. The conductive film 310 serves as the wiring SL and one of the source and drain of the transistor 112. The conductive film 312 serves as the other of the source and drain of the transistor 112. The conductive film 313 serves as a capacitor line.
An insulating film 314 is provided over the insulating film 306, the oxide semiconductor film 308, and the conductive films 310, 312, and 313. An insulating film 316 serving as a planarization film is provided over the insulating film 314. An opening 360 reaching the conductive film 312 is formed in the insulating films 314 and 316. In addition, an opening 362 reaching the conductive film 313 is formed in the insulating films 314 and 316.
The first common electrode 318 is provided over the insulating film 316. The first common electrode 318 is connected to the conductive film 313 through the opening 362. An insulating film 320 is provided over the insulating film 316 and the first common electrode 318. A pixel electrode 322 is provided over the insulating film 320 in a position overlapping with the first common electrode 318. The insulating film 320 has an opening 364 in a region overlapping with the opening 360. The conductive film 312 and the pixel electrode 322 are connected to each other through the openings 360 and 364. As in the top view of
A substrate 330 is provided to face the substrate 302. A light-blocking film 332 having a function of blocking visible light, a color film 334 transmitting visible light within a certain wavelength range, an insulating film 336 in contact with the light-blocking film 332 and the color film 334, a second common electrode 338 in contact with the insulating film 336, and an alignment film 340 in contact with the second common electrode 338 are provided under the substrate 330. The insulating film 336 has a function of preventing the shapes of the surfaces of the light-blocking film 332 and the color film 334 from affecting the planarity of the second common electrode 338 or the alignment film 340. Note that a structure in which the insulating film 336 is not provided may be employed.
Between the substrate 302 and the substrate 330, a liquid crystal layer 350 containing a liquid crystal material is interposed between the alignment film 324 and the alignment film 340. The liquid crystal element 111 includes at least the first common electrode 318, the insulating film 320, the pixel electrode 322, the second common electrode 338, and the liquid crystal layer 350. Note that a negative liquid crystal material is used for the liquid crystal layer 350, and the specific resistivity of the liquid crystal material is greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·cm.
Manufacturing MethodAn example of a method for manufacturing the pixel illustrated in
As illustrated in
The substrate 302 is preferably a substrate having heat resistance high enough to withstand a later manufacturing step; for example, a glass substrate, a ceramic substrate, a quartz substrate, or a sapphire substrate.
The conductive film 304 may be formed using a single layer or a stacked layer of a conductive film containing one or more kinds selected from aluminum, titanium, chromium, cobalt, nickel, copper, yttrium, zirconium, molybdenum, ruthenium, silver, tantalum, and tungsten. For example, the conductive film 304 may be a conductive film in which a copper film is stacked over a tungsten nitride film or a single-layer tungsten film.
The insulating film 306 may be formed using a single layer or a stacked layer of an insulating film containing one or more kinds of aluminum oxide, magnesium oxide, silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, gallium oxide, germanium oxide, yttrium oxide, zirconium oxide, lanthanum oxide, neodymium oxide, hafnium oxide, and tantalum oxide.
For example, in the case where the insulating film 306 has a two-layer structure, a silicon nitride film and a silicon oxide film may be used as the first layer and the second layer, respectively. A silicon oxynitride film may be used as the second layer instead of the silicon oxide film. A silicon nitride oxide film may be used as the first layer instead of the silicon nitride film.
As the silicon oxide film, a silicon oxide film with a low defect density is preferably used. Specifically, a silicon oxide film which has a spin density of 3×1017 spins/cm3 or less, preferably 5×1016 spins/cm3 or less corresponding to a signal at a g-factor of 2.001 in electron spin resonance (HSR) spectroscopy is used. As the silicon oxide film, a silicon oxide film having excess oxygen is preferably used. As the silicon nitride film, a silicon nitride film from which hydrogen and ammonia are less released is used. The amount of released hydrogen and ammonia is preferably measured by thermal desorption spectroscopy (TDS) analysis.
A material that can be used for the oxide semiconductor film 308 is described in detail in Embodiment 2. When The oxide semiconductor film used as the oxide semiconductor film 308 contains a large amount of hydrogen, the hydrogen and the oxide semiconductor are bonded to each other, so that part of the hydrogen becomes donors and generates electrons serving as carriers. As a result, the threshold voltage of the transistor shifts in the negative direction. Therefore, it is preferable that, after forming the oxide semiconductor film, dehydration treatment (dehydrogenation treatment) be performed to remove hydrogen or moisture from the oxide semiconductor film so that the oxide semiconductor film contains impurities as little as possible.
Note that oxygen in the oxide semiconductor film is also reduced by the dehydration treatment (dehydrogenation treatment) in some cases. Accordingly, it is preferable that oxygen be added to the oxide semiconductor film to fill oxygen vacancies increased by the dehydration treatment (dehydrogenation treatment).
In this manner, hydrogen or moisture is removed from the oxide semiconductor film by the dehydration treatment (dehydrogenation treatment) and oxygen vacancies therein are filled by the oxygen adding treatment, whereby the oxide semiconductor film can be turned into an i-type (intrinsic) oxide semiconductor film or a substantially i-type (intrinsic) oxide semiconductor film which is extremely close to an i-type oxide semiconductor film.
Next, a conductive film is formed over the insulating film 306 and the oxide semiconductor film 308 and processed by etching or the like, whereby the conductive films 310 and 312 in contact with the oxide semiconductor film 308 are formed, as illustrated in
The conductive films 310, 312, and 313 are formed to have a single-layer structure or a stacked-layer structure including any of metals such as aluminum, titanium, chromium, nickel, copper, yttrium, zirconium, molybdenum, silver, tantalum, and tungsten or an alloy containing any of these metals as its main component. As examples of the stacked-layer structure, a two-layer structure in which a titanium film is stacked over an aluminum film, a two-layer structure in which a titanium film is stacked over a tungsten film, a two-layer structure in which a copper film is formed over a copper-magnesium-aluminum alloy film, a three-layer structure in which a titanium film or a titanium nitride film, an aluminum film or a copper film, and a titanium film or a titanium nitride film are stacked in this order, and a three-layer structure in which a molybdenum film or a molybdenum nitride film, an aluminum film or a copper film, and a molybdenum film or a molybdenum nitride film are stacked in this order are given. Note that a transparent conductive material containing indium oxide, tin oxide, or zinc oxide may be used. The conductive film can be formed by a sputtering method, for example.
Next, as in
For example, the silicon oxide film or the silicon oxynitride film which is used as the insulating film 314 can be formed under the following conditions: the substrate placed in a treatment chamber of a plasma CVD apparatus, which is vacuum-evacuated, is held at a temperature higher than or equal to 180° C. and lower than or equal to 400° C., preferably higher than or equal to 200° C. and lower than or equal to 370° C., the pressure in the treatment chamber is greater than or equal to 30 Pa and less than or equal to 250 Pa, preferably greater than or equal to 40 Pa and less than or equal to 200 Pa with introduction of a source gas into the treatment chamber, and high-frequency power is supplied to an electrode provided in the treatment chamber.
The source gas of the insulating film 314 is preferably a deposition gas containing silicon and an oxidizing gas. Typical examples of the deposition gas containing silicon include silane, disilane, trisilane, and silane fluoride. Examples of the oxidizing gas include oxygen, ozone, dinitrogen monoxide, and nitrogen dioxide.
In this embodiment, the insulating film 314 has a stacked-layer structure of a first insulating film and a second insulating film. For example, as the first insulating film, a 50-nm-thick silicon oxynitride film is formed by a plasma CVD method under the following conditions: silane with a flow rate of 20 sccm and dinitrogen monoxide with a flow rale of 3000 sccm are used as the source gases, the pressure in the treatment chamber is 40 Pa, the substrate temperature is 220° C., and a high-frequency power of 100 W is supplied to parallel plate electrodes with a high-frequency power supply of 27.12 MHz. Note that a plasma CVD apparatus is a parallel plate plasma CVD apparatus in which the electrode area is 6000 cm2, and power per unit area (power density) into which supplied power is converted is 1.6×10−2 W/cm2. Under the above conditions, a silicon oxynitride film that pastes oxygen can be formed.
As the second insulating film, a silicon oxide film or a silicon oxynitride film is formed under the following conditions: the substrate placed in a treatment chamber of the plasma CVD apparatus that is vacuum-evacuated is held at a temperature higher than or equal to 180° C. and lower than or equal to 260° C., preferably higher than or equal to 180° C. and lower than or equal to 230° C., the pressure is greater than or equal to 100 Pa and less than or equal to 250 Pa preferably greater than or equal to 100 Pa and less than or equal to 200 Pa with introduction of a source gas into the treatment chamber, and a high-frequency power of 0.17 W/cm2 to 0.5 W/cm2, preferably 0.25 W/cm2 to 0.35 W/cm2 is supplied to an electrode provided in the treatment chamber.
As the deposition conditions of the second insulating film, the high -frequency power having the power density is supplied to the electrode in the treatment chamber having the pressure, so that the degradation efficiency of the source gas in plasma is increased, oxygen radicals are increased, and oxidation of the source gas is promoted. Thus, the oxygen content in the second insulating film becomes higher than that in the stoichiometric composition. However, in the case where the substrate temperature is within the above temperature range, the bond between silicon and oxygen is weak; thus, part of oxygen is released by heating. Accordingly, it is possible to form an oxide insulating film which contains oxygen at a higher proportion than the stoichiometric composition and from which part of oxygen is released by heating.
In this embodiment, as the second insulating film, a 400-nm-thick silicon oxynitride film is formed by a plasma CVD method under the following conditions: silane with a flow rale of 160 sccm and dinitrogen monoxide with a flow rate of 4000 sccm are used as the source gases, the pressure in the treatment chamber is 200 Pa, the substrate temperature is 220° C., and a high-frequency power of 1500 W is supplied to parallel plate electrodes with a high-frequency power supply of 27.12 MHz. Note that a plasma CVD apparatus is a parallel plate plasma CVD apparatus in which the electrode area is 6000 cm2, and power per unit area (power density) into which supplied power is converted is 2.5×10−1 W/cm2.
It is preferable that heat treatment be performed at least after the formation of the insulating film 314 so that oxygen contained in the insulating film 314 enters the oxide semiconductor film 308 to fill oxygen vacancies in the oxide semiconductor film 308.
Next, as in
The openings 360 and 362 are formed, for example, by a dry etching method or a wet etching method. Alternatively, the openings 360 and 362 may be formed by a combination of a dry etching method and a wet etching method.
Next, as in
Next, as in
For example, a conductive film containing any of the followings can be used as the first common electrode 318: indium oxide containing tungsten oxide; indium zinc oxide containing tungsten oxide; indium oxide containing titanium oxide; indium tin oxide containing titanium oxide; indium tin oxide; indium zinc oxide; and indium tin oxide to which silicon oxide is added. The first common electrode 318 can be formed by a sputtering method.
As the insulating film 320, a silicon oxide film, a silicon oxynitride film, a silicon nitride film, a silicon nitride oxide film, or the like can be used. In particular, a silicon nitride film or a silicon nitride oxide film is preferably used as the insulating film 320 because the insulating film 320 has a function as a dielectric of a capacitor and a function as a protection film for the transistor.
For example, a silicon nitride film, a silicon nitride oxide film, or the like having a thickness of from 50 nm to 400 nm can be used as the insulating film 320. In this embodiment, a silicon nitride film having a thickness of 100 nm is used as the insulating film 320.
The silicon nitride film is preferably formed at a high temperature to have an improved blocking property; for example, the silicon nitride film is preferably formed at a temperature in the range from the substrate temperature of 100° C. to the strain point of the substrate, more preferably at a temperature in the range from 300° C. to 400° C. Note that in the case where the silicon nitride film is formed at a high temperature, a phenomenon in which oxygen is released from the oxide semiconductor film 308 and the carrier concentration is increased is caused in some cases; therefore, the upper limit of the temperature is a temperature at which the phenomenon is not caused.
Next, as in
Next, as in
The pixel electrode 322 is formed in such a manner that a transparent conductive film is formed over the insulating film 320 and processed by etching or the like.
As the pixel electrode 322, a conductive film containing the following can be used: indium oxide containing tungsten oxide, indium zinc oxide containing tungsten oxide, indium oxide containing titanium oxide, indium tin oxide containing titanium oxide, indium tin oxide, indium zinc oxide, indium tin oxide to which silicon oxide is added, or the like.
Next, an alignment film 324 (not illustrated) is formed over the insulating film 320 and the pixel electrode 322. The alignment film 324 can be formed by a rubbing method, an optical alignment method, or the like.
Through the above steps, the components formed over the substrate 302 can be formed.
Next, a method for manufacturing a structure formed below the substrate 330 facing the substrate 302 is described below.
First, the substrate 330 is prepared. For materials of the substrate 330, the materials used for the substrate 302 can be referred to. Next, the light-blocking film 332 and the color film 334 which are in contact with the substrate 330 are formed. The light-blocking film 332 and the color film 334 are each formed in a desired position with any of various materials by a printing method, an inkjet method, an etching method using a photolithography technique, or the like.
Then, the insulating film 336 in contact with the light-blocking film 332 and the color film 334 is formed, For the insulating film 336, an organic insulating film of an acrylic resin or the like can be used. With the insulating film 336, an impurity or the like contained in the color film 334 can be prevented from diffusing into the liquid crystal layer 350 side, for example.
The second common electrode 338 in contact with the insulating film 336 is formed. A conductive layer that can be used for the second common electrode 338 can be formed using a light-transmitting conductive material such as indium oxide containing tungsten oxide; indium zinc oxide containing tungsten oxide; indium oxide containing titanium oxide; indium tin oxide containing titanium oxide; indium tin oxide (hereinafter referred to as ITO); indium zinc oxide; or indium tin oxide to which silicon oxide is added. The conductive layer that can be used for the second common electrode 338 can be formed by a sputtering method, for example.
Next, the alignment film 340 in contact with the second common electrode 338 is formed. The method for forming the alignment film 324 can be referred to for a method for forming the alignment film 340.
Through the above steps, the structure formed below the substrate 330 can be formed.
After that, the liquid crystal layer 350 is formed between the substrate 302 and the substrate 330. The liquid crystal layer 350 can be formed by a dispenser method (a dropping method), or an injecting method by which liquid crystal is injected using a capillary phenomenon after the substrate 302 and the substrate 330 are bonded to each other.
Through the above steps, the pixel illustrated in
The structures, the methods, and the like described in this embodiment can be combined as appropriate with any of the structures, the methods, and the like described in the other embodiments.
Embodiment 2In this embodiment, an oxide semiconductor film that can be used in the liquid crystal display device of one embodiment of the present invention is described.
A highly purified oxide semiconductor (a purified OS) obtained by reduction of impurities such as moisture or hydrogen that serve as electron donors (donors) and reduction of oxygen vacancies is an intrinsic (i-type) semiconductor or a substantially intrinsic semiconductor. Thus, a transistor including a channel formation region in a highly purified oxide semiconductor film has extremely low off-state current and high reliability.
Specifically, various experiments can prove low off-state current of a transistor including a channel formation region in a highly purified oxide semiconductor film. For example, even when an clement has a channel width of 1×106 μm and a channel length of 10 μm, off-state current can be lower than or equal to the measurement limit of a semiconductor parameter analyzer, i.e., lower than or equal to 1×10−13 A, at a voltage (drain voltage) between a source electrode and a drain electrode of 1 V to 10 V. In that case, it can be seen that off-state current normalized on the channel width of the transistor is lower than or equal to 100 zA/μm. In addition, a capacitor and a transistor were connected to each other and off-state current was measured using a circuit in which electric charge flowing to or from the capacitor is controlled by the transistor. In the measurement, a highly purified oxide semiconductor film was used for the channel formation region of the transistor, and the off-state current of the transistor was measured from a change in the amount of electric charge of the capacitor per unit hour. As a result, it was found that, in the case where the voltage between the source electrode and the drain electrode of the transistor is 3 V, a lower off-state current of several tens of yoctoamperes per micrometer is obtained. Accordingly, the transistor using the highly purified oxide semiconductor film for the channel formation region has much lower off-state current than a crystalline silicon transistor.
Unless otherwise specified, in the case of an n-channel transistor, the off-state current in this specification is a current that flows between a source and a drain when the potential of a gate is lower than or equal to 0 with the potential of the source as a reference potential while the potential of the drain is higher than those of the source and the gate. Meanwhile, in the case of a p-channel transistor, the off-state current in this specification is a current that flows between a source and a drain when the potential of a gate is higher than or equal to 0 with the potential of the source as a reference potential while the potential of the drain is tower than those of the source and the gate.
As the semiconductor film, at least indium (In) or zinc (Zn) is preferably included as an oxide semiconductor. The oxide semiconductor preferably contains, in addition to In and Zn, gallium (Ga) serving as a stabilizer that reduces variations in electric characteristics among transistors using the above-described oxide semiconductor. Tin (Sn) is preferably contained as a stabilizer. Hafnium (Hf) is preferably contained as a stabilizer. Aluminum (Al) is preferably contained as a stabilizer. Zirconium (Zr) is preferably contained as a stabilizer.
Among the oxide semiconductors, unlike silicon carbide, gallium nitride, or gallium oxide, an In—Ga—Zn-based oxide, an In—Sn—Zn-based oxide, or the like has an advantage of high mass productivity because a transistor with favorable electric characteristics can be formed by sputtering or a wet process. Further, unlike silicon carbide, gallium nitride, or gallium oxide, the In—Ga—Zn-based oxide allows a transistor with favorable electric characteristics to be formed over a glass substrate. Further, a larger substrate can be used.
As another stabilizer, one or plural kinds of lanthanoid such as lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), or lutetium (Lu) may be contained.
As the oxide semiconductor, any of the following oxides can be used, for example: indium oxide, gallium oxide, tin oxide, zinc oxide, In—Zn-based oxide, Sn—Zn-based oxide, Al—Zn-based oxide, Zn—Mg-based oxide, Sn—Mg-based oxide, In—Mg-based oxide, In—Ga-based oxide, In—Ga—Zn-based oxide (also referred to as IGZO). In—Al—Zn-based oxide, In—Sn—Zn-based oxide, Sn—Ga—Zn-based oxide, Al—Ga—Zn-based oxide, Sn—Al—Zn-based oxide, In—Hf—Zn-based oxide, In—La—Zn-based oxide, In—Pr—Zn-based oxide, In—Nd—Zn-based oxide. In—Sm—Zn-based oxide, In—Eu—Zn-based oxide, In—Gd—Zn-based oxide, In—Tb—Zn-based oxide, In—Dy—Zn-based oxide, In—Ho—Zn-based oxide, In—Er—Zn-based oxide, In—Tm—Zn-based oxide, In—Yb—Zn-based oxide, In—Lu—Zn-based oxide, In—Sn—Ga—Zn-based oxide, In—Hf—Ga—Zn-based oxide, In—Al—Ga—Zu-based oxide, In—Sn—Al—Zn-based oxide, In—Sn—Hf—Zn-based oxide, and In—Hf—Al—Zn-based oxide.
Note that, for example, an In—Ga—Zn-based oxide means an oxide containing In, Ga, and Zn, and there is no limitation on the ratio of In, Ga, and Zn. In addition, the In—Ga—Zn-based oxide may contain a metal clement other than In, Ga, and Zn. Further, the In—Ga—Zn-based oxide may contain a metal element other than In, Ga, and Zn. The In—Ga—Zn-based oxide has sufficiently high resistance when no electric field is applied thereto, so that off-state current can be sufficiently reduced. Further, the In—Ga—Zn-based oxide has high mobility.
For example, an In—Ga—Zn-based oxide with an atomic ratio of In:Ga:Zn=1:1:1, In:Ga:Z=1:1:1.2 (=5:5:6), In:Ga:Zn=2:2:1; or In:Ga:Zn=3:1:2, or an oxide with an atomic ratio close to the above atomic ratios can be used. Alternatively, an In—Sn—Zn-based oxide with an atomic ratio of In:Sn:Zn=1:1:1, In:Sn:Zn=2:1:3, or In:Sn:Zn=2:1:5, or an oxide with an atomic ratio close to the above atomic ratios may be used.
For example, with an In—Sn—Zn-based oxide, high mobility can be realized relatively easily. However, even with at In—Ga—Zn-based oxide, mobility can be increased by reducing the defect density in the bulk.
An oxide semiconductor film is classified roughly into a single-crystal oxide semiconductor film and a non-single-crystal oxide semiconductor film. The non-single-crystal oxide semiconductor film includes any of a c-axis aligned crystalline oxide semiconductor (CAAC-OS) film, a polycrystalline oxide semiconductor film, a microcrystalline oxide semiconductor film, an amorphous oxide semiconductor film, and the like.
Here, the CAAC-OS film is described.
The CAAC-OS film is one of oxide semiconductor films including a plurality of crystal parts, and most of the crystal parts each fit inside a cube whose one side is less than 100 nm. Thus, there is a case where a crystal part included in the CAAC-OS film fits inside a cube whose one side is less than 10 nm, less than 5 nm, or less than 3 nm.
In a transmission electron microscope (TEM) image of the CAAC-OS film, a boundary between crystal ports, that is, a grain boundary is not clearly observed. Thus, in the CAAC-OS film, a reduction in electron mobility due to the grain boundary is less likely to occur.
According to the TEM image of the CAAC-OS film observed in a direction substantially parallel to a sample surface (cross-sectional TEM image), metal atoms are arranged in a layered manner in the crystal parts. Each metal atom layer has a morphology reflected by a surface over which the CAAC-OS film is formed (hereinafter, a surface over which the CAAC-OS film is formed is referred to as a formation surface) or a top surface of the CAAC-OS film, and is arranged in parallel to the formation surface or the top surface of the CAAC-OS film.
On the other hand, according to the TEM image of the CAAC-OS film observed in a direction substantially perpendicular to the sample surface (plan TEM image), metal atoms are arranged in a triangular or hexagonal configuration in the crystal parts. However, there is no regularity of arrangement of metal atoms between different crystal parts.
In this specification, the term “parallel” indicates that the angle formed between two straight lines is greater than or equal to −10° and less than or equal to 10°, and accordingly also includes the case where the angle is greater than or equal to −5° and less than or equal to 5°. In addition, the term “perpendicular” indicates that the angle formed between two straight lines is greater than or equal to 80° and less than or equal to 100°, and accordingly includes the case where the angle is greater than or equal to 85° and less than or equal to 95°.
From the results of the cross-sectional TEM image and the plan TEM image, alignment is found in the crystal parts in the CAAC-OS film.
A CA AC-OS film is subjected to structural analysis with an X-ray diffraction (XRD) apparatus. For example, when the CAAC-OS film including an InCaZnO4 crystal is analyzed by an out-of-plane method, a peak appears frequently when the diffraction angle (2θ) is around 31°. This peak is derived from the (009) plane of the InGaZnO4 crystal, which indicates that crystals in the CAAC-OS film have c-axis alignment, and that the c-axes are aligned m a direction substantially perpendicular to the formation surface or the top surface of the CAAC-OS film.
On the other hand, when the CAAC-OS film is analyzed by an in-plane method in which an X-ray enters a sample in a direction substantially perpendicular to the c-axis. a peak appears frequently when 2θ around 56°. This peak is derived from the (110) plane of the InGaZnO4 crystal. Here, analysis (ϕ scan) is performed under conditions where the sample is rotated around a normal vector of a sample surface as an axis (ϕ axis) with 2θ fixed at around 56°. In the case where the sample is a single-crystal oxide semiconductor film of InGaZnO4, six peaks appear. The six peaks are derived from crystal planes equivalent to the (110) plane. On the other hand, in the case of a CAAC-OS film, a peak is not clearly observed even when φ scan is performed with 2θ fixed at around 56°.
According to the above results, in the CAAC-OS film having c-axis alignment, while the directions of a-axes and b-axes are different between crystal parts, the c-axes are aligned in a direction parallel to a normal vector of a formation surface or a normal vector of a top surface of the CAAC-OS film. Thus, each metal atom layer arranged in a layered manner observed in the cross-sectional TEM image corresponds to a plane parallel to the a-b plane of the crystal.
Note that the crystal part is formed concurrently with deposition of the CAAC-OS film or is formed through crystallization treatment such as heat treatment. As described above, the c-axis of the crystal is aligned in a direction parallel to a normal vector of a formation surface or a normal vector of a top surface. Thus, for example, in the case where a shape of the CAAC-OS film is changed by etching or the like, the c-axis might not be necessarily parallel to a normal vector of a formation surface or a normal vector of a top surface of the CAAC-OS film.
Further, the degree of crystallinity in the CAAC-OS film is not necessarily uniform. For example, in the case where crystal growth leading to the CAAC-OS film occurs from the vicinity of the top surface of the film, the degree of the crystallinity in the vicinity of the top surface is higher than that in the vicinity of the formation surface in some cases. Further, when an impurity is added to the CAAC-OS film, the crystallinity in a region to which the impurity is added is changed, and the degree of crystallinity in the CAAC-OS film varies depending on regions.
Note that when the CAAC-OS film with an InGaZnO4 crystal is analyzed by an out-of-plane method, a peak of 2θ may also be observed at around 36°, in addition to the peak of 2θ at around 31°. The peak of 2θ at around 36° is derived from the (311) plane of a ZnGa2O4 crystal; such a peak indicates that a ZnGa2O4 crystal is included in part of the CAAC-OS film including the InGaZnO4 crystal. It is preferable that in the CAAC-OS film, a peak of 2θ appears at around 31° and a peak of 2θ do not appear at around 36°.
The CAAC-OS film is an oxide semiconductor film having low impurity concentration. The impurity is an clement other than the main components of the oxide semiconductor film, and examples of the impurity include hydrogen, carbon, silicon, and a transition metal element. In particular, an element that has higher bonding strength to oxygen than a metal element included in the oxide semiconductor film, such as silicon, disturbs the atomic arrangement of the oxide semiconductor film by depriving the oxide semiconductor film of oxygen and causes a decrease in crystallinity. Furthermore, a heavy metal such as iron or nickel, argon, carbon dioxide, or the like has a large atomic radius (molecular radius), and thus disturbs die atomic arrangement of the oxide semiconductor film and causes a decrease in crystallinity when it is contained in the oxide semiconductor film. Note that the impurity contained in the oxide semiconductor film might serve as a carrier trap or a carrier generation source.
The CAAC-OS film is an oxide semiconductor film having a low density of defect states. In some cases, oxygen vacancies in the oxide semiconductor film serve as carrier traps or serve as carrier generation sources when hydrogen is captured therein.
The state in which impurity concentration is low and density of defect states is low (the number of oxygen vacancies is small) is referred to as a “highly purified intrinsic” or “substantially highly purified intrinsic” state. A highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor film has few carrier generation sources, and thus can have a low carrier density. Thus, a transistor including the oxide semiconductor film rarely has negative threshold voltage (is rarely normally on). The highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor film has few carrier traps. Accordingly, the transistor including the oxide semiconductor film has little variation in electric characteristics and high reliability. Electric charge trapped by the carrier traps in the oxide semiconductor film takes a long time to be released, and might behave like fixed electric charge. Thus, the transistor which includes the oxide semiconductor film having high impurity concentration and a high density of defect states has unstable electric characteristics in some cases.
In a transistor using the CAAC-OS film, change in electric characteristics due to irradiation with visible light or ultraviolet light is small.
For example, the CAAC-OS film is formed by a sputtering method using a polycrystalline metal oxide target. When ions collide with the target, a crystal region included in the target may be separated from the target along an a-b plane; in other words, a sputtered particle having a plane parallel to an a-b plane (flat-plate-like sputtered particle or pellet-like sputtered particle) may flake off from the target. In that case, the flat-plate-like or pellet-like sputtered particle reaches a substrate in the state of maintaining its crystal state, whereby the CAAC-OS film can be formed.
For the deposition of the CAAC-OS film, the following conditions are preferably used.
By reducing the amount of impurities entering the CAAC-OS film during the deposition, the crystal state can be prevented from being broken by the impurities. For example, the concentration of impurities (e.g., hydrogen, water, carbon dioxide, and nitrogen) which exist in the treatment chamber may be reduced. Furthermore, the concentration of impurities in a deposition gas may be reduced. Specifically, a deposition gas whose dew point is −80° C. or lower, preferably −100° C. or lower is used.
By increasing the substrate heating temperature during the deposition, migration of a sputtered particle is likely to occur after the sputtered particle reaches a substrate surface. Specifically, the substrate heating temperature during the deposition is from 100° C. to 740° C., preferably from 200° C. to 500° C. By increasing the substrate heating temperature during the deposition, when the flat-plate-like or pellet-like sputtered particle reaches the substrate, migration occurs on the substrate surface, so that a flat plane of the sputtered particles is attached to the substrate.
Furthermore, it is preferable that the proportion of oxygen in the deposition gas be increased and the power be optimized in order to reduce plasma damage at the deposition. The proportion of oxygen in the deposition gas is 30 vol % or higher, preferably 100 vol %.
The oxide semiconductor layer may have a stacked-layer structure.
Here, an example in which the oxide semiconductor film 308 used in the transistor 112 illustrated in
Metal oxides used for the oxide semiconductor film 307 and the oxide semiconductor film 309 preferably contain at least one same constituent element. Alternatively, the constituent elements of the oxide semiconductor film 307 may be the same as those of the oxide semiconductor film 309 and the composition of the constituent elements of the oxide semiconductor film 307 may be different from those of the oxide semiconductor film 309.
In the case where the oxide semiconductor film 307 is In-M-Zn oxide (M represents Al, Ga, Ge, Y, Zr, Sn, La, Ce, or Hf), it is preferable that the atomic ratio of metal elements of a sputtering target used for forming a film of the In-M-Zn oxide satisfy In≥M and Zn≥M. As the atomic ratio of metal elements of the sputtering target, In:M:Zn=1:1:1, In:M:Zn=5:5:6 (1:1:1.2), and In:M:Zn=3:1:2 are preferable. Note that the proportion of the atomic ratio of the oxide semiconductor film 307 formed using the above-described sputtering target varies within a range of ±20% as an error.
When an In-M-Zn oxide is used for the oxide semiconductor film 307, the proportions of In and M, not taking Zn and O into consideration, is preferably as follows; the atomic percentage of In is greater than or equal to 25 at. % and the proportion of M is less than 75 at. %; more preferably, the proportion of In is greater than or equal to 34 at. % and the proportion of M is less than 66 at. %.
The energy gap of the oxide semiconductor film 307 is 2 eV or more, preferably 2.5 eV or more, further preferably 3 eV or more. The off-state current of the transistor 112 can be reduced by using an oxide semiconductor having a wide energy gap.
The thickness of the oxide semiconductor film 307 is greater than or equal to 3 nm and less than or equal to 200 nm, preferably greater than or equal to 3 nm and less than or equal to 100 nm, further preferably greater than or equal to 3 nm and less than or equal to 50 nm.
The oxide semiconductor film 309 is typically In—Ga oxide, In—Zn oxide, or In-M-Zn oxide (M represents Al, Ga, Ge, Y, Zr, Sn, La, Ce, or Hf). The energy at the conduction band bottom thereof is closer to a vacuum level man that of the oxide semiconductor film 307 is, and typically, the difference between the energy al the conduction band bottom of the oxide semiconductor film 309 and the energy at the conduction band bottom of the oxide semiconductor film 307 is any one of 0.05 eV or more, 0.07 eV or more, 0.1 eV or more, and 0.15 eV or more, and any one of 2 eV or less, 1 eV or less, 0.5 eV or less, and 0.4 eV or less. That is, the difference between the electron affinity of the oxide semiconductor film 309 and the electron affinity of the oxide semiconductor film 307 is greater than or equal to 0.05 eV, greater than or equal to 0.07 eV, greater than or equal to 0.1 eV, or greater than or equal to 0.15 eV and also less than or equal to 2 eV, less than or equal to 1 eV, less than or equal to 0.5 eV, or less than or equal to 0.4 eV.
When the oxide semiconductor film 309 contains a larger amount of the element M in an atomic ratio than the amount of In in an atomic ratio, any of the following effects may be obtained: (1) the energy gap of the oxide semiconductor film 309 is widened; (2) the electron affinity of the oxide semiconductor film 309 decreases; (3) an impurity from the outside is blocked; (4) an insulating property increases as compared to the oxide semiconductor film 307. Further, oxygen vacancies are less likely to be generated in the oxide semiconductor film 309 containing a larger amount of M in an atomic ratio than the amount of In in an atomic ratio because M is a metal element which is strongly bonded to oxygen.
When an In-M-Zn oxide is used for the oxide semiconductor film 309, the proportions of In and Mt not taking Zn and O into consideration, is preferably as follows: the atomic percentage of In is less than 50 at. % and the atomic percentage of M is greater than or equal to 50 at. %; further preferably, the atomic percentage of In is less than 25 at. % and the atomic percentage of M is greater than or equal to 75 at. %.
Further, in the case where each of the oxide semiconductor film 307 and the oxide semiconductor film 309 is In-M-Zn oxide (M represents Al, Ga, Ge, Y, Zr, Sn, La, Ce, or Hf), the proportion of M atoms in the oxide semiconductor film 309 is higher than the proportion of M atoms in the oxide semiconductor film 307. Typically, the proportion of M atoms in the oxide semiconductor layer 309 is higher than or equal to 1.5 times, preferably higher than or equal to 2 times, further preferably higher than or equal to 3 times as large as that in the oxide semiconductor film 307.
In the case where the oxide semiconductor film 309 has an atomic ratio of In to M and Zn which is x1:y1:z1 and the oxide semiconductor film 307 has an atomic ratio of In to M and Zn which is x2:y2:z2, y1/x1 is larger than y2/x2, preferably y1/x1 is 1.5 times or more as large as y2/x2. It is further preferable that y1/x1 be twice or more as large as y2/x2. It is still further preferable y1/x1 be three or more times as large as y2/x2. In this case, it is preferable that in the oxide semiconductor film, y2 be higher than or equal to x2 because the transistor 102 including the oxide semiconductor film can have stable electric characteristics. However, when y2 is larger than or equal to three or more times x2, the field-effect mobility of the transistor 102 including the oxide semiconductor film is reduced. Thus, it is preferable that y2 be lower than three times x2.
Further, in the case where the oxide semiconductor film 309 is an In-M-Zn oxide film, the atomic ratio of metal elements of a sputtering target used for forming the In-M-Zn oxide preferably satisfies M>In, and more preferably, Zn also satisfies Zn≥M. As the atomic ratio of metal elements of the sputtering target, In:Ga:Zn=1:3:2, In:Ga:Zn=1:3:3, In:Ga:Zn=1:3:4, In:GaZn=1:3:5, In:Ga:Zn=1:3:6, In:Ga:Zn=1:3:7, In:Ga:Zn=1:3:8, In:Ga:Zn=1:3:9, In:Ga:Zn=1:3:10, In:Ga:Zn=1:6:4, In:Ga:Zn=1:6:5, In:Ga:Zn=1:6:6, In:Ga:Zn=1:6:7, In:Ga:Zn=1:6:8, In:Ga:Zn=1:6:9, and In:Ga:Zn=1:6:10 are preferable. Note that the proportion of each metal element in the atomic ratio of each of the oxide semiconductor film 307 and the oxide semiconductor film 309 formed using the above-described sputtering target varies within a range of ±20 % as an error.
Note that, without limitation to the compositions and materials described above, a material with an appropriate composition may be used depending on required semiconductor characteristics and electrical characteristics (e.g., field-effect mobility and threshold voltage) of a transistor. Further, in order to obtain the required semiconductor characteristics of the transistor, it is preferable that the carrier density, the impurity concentration, the defect density, the atomic ratio of a metal clement to oxygen, the interatomic distance, the density, and the like of the oxide semiconductor film 307 be set to appropriate values.
Note that the oxide semiconductor film 309 also functions as a film which relieves damage to the oxide semiconductor film 307 at the time of forming the insulating film 314 later. The thickness of the oxide semiconductor film 309 is greater than or equal to 3 nm and less than or equal to 100 nm, preferably greater than or equal to 3 nm and less than or equal to 50 nm.
When silicon or carbon which is one of elements belonging to Group 14 is contained in the oxide semiconductor film 307 in the transistor 112, the number of oxygen vacancies is increased, and the oxide semiconductor film 307 is changed to an n-type. Thus, the concentration of silicon or carbon (the concentration is measured by SIMS) in the oxide semiconductor film 307 or the concentration of silicon or carbon (the concentration is measured by SIMS) in the vicinity of the interface between the oxide semiconductor film 309 and the oxide semiconductor film 307 is set to be lower than or equal to 2×1018 atoms/cm3, preferably lower than or equal to 2×1017 atoms/cm3.
Further, the concentration of alkali metal or alkaline earth metal of the oxide semiconductor film 307, which is measured by SIMS, is lower than or equal to 1×1018 atoms/cm3, preferably lower than or equal to 2×1016 atoms/cm3. Alkali metal and alkaline earth metal might generate carriers when bonded to an oxide semiconductor, in which case the off-state current of the transistor might be increased. Therefore, it is preferable to reduce the concentration of alkali metal or alkaline earth metal of the oxide semiconductor film 307.
Further, when nitrogen is contained in the oxide semiconductor film 307, electrons serving as carriers are generated to increase the carrier density, so that the oxide semiconductor film 307 easily becomes n-type. Thus, a transistor including an oxide semiconductor which contains nitrogen is likely to be normally on. For this reason, nitrogen in the oxide semiconductor film is preferably reduced as much as possible; the concentration of nitrogen which is measured by SIMS is preferably set to, for example, lower than or equal to 5×1018 atoms/cm3.
Note that in the transistor 112 shown in
Note that the oxide semiconductor firm 307 and the oxide semiconductor film 309 are not formed by simply stacking each layer, but are formed to form a continuous junction (here, in particular, a structure in which the energy of the bottom of the conduction band is changed continuously between each film). In other words, a stacked-layer structure in which there exist no impurity which forms a defect level such as a trap center or a recombination center at each interface is provided. If an impurity exists between the oxide semiconductor film 307 and the oxide semiconductor film 309 which are stacked, a continuity of the energy band is damaged, and the carrier is captured or recombined at the interface and then disappears.
To form the continuous junction, each film needs to be stacked successively without exposure to the atmosphere using a multi-chamber deposition apparatus (sputtering apparatus) including a load lock chamber. Each chamber in the sputtering apparatus is preferably subjected to high vacuum evacuation (to a vacuum of about 5×10−7 Pa to 1×10−4 Pa) with use of a suction vacuum evacuation pump such as a cryopump so that water or the like, which is an impurity for the oxide semiconductor film, is removed as much as possible. Alternatively, a turbo-molecular pump is preferably used in combination with a cold trap to prevent backflow of gas, especially a gas containing carbon or hydrogen into the chamber through an evacuation system.
Here, a band structure of the stacked-layer structure included in the transistor 112 is described with reference to
As shown in
As shown in
Although trap states due to defects or impurities such as silicon or carbon, which is a constituent element of the insulating film 514, might be formed in the vicinity of the interface between the oxide semiconductor film 309 and the insulating film 314 as shown in
By using the above-described oxide semiconductor for a transistor in the liquid crystal display device of one embodiment of the present invention, display of images on a pixel portion can be maintained even after the writing of image signals to the pixel portion is stopped. Furthermore, by using the above transistor as an clement for controlling the supply of voltage to a liquid crystal element included in the pixel, the voltage applied to the liquid crystal element can be held for a long time.
The structures, the methods, and the like described in this embodiment can be combined as appropriate with any of the structures, the methods, and the like described in the other embodiments.
Embodiment 3In this embodiment, a configuration example of a pixel in a liquid crystal display device of one embodiment of the present invention, which is different from the pixel 100 illustrated in the top view of
In the pixel 100 illustrated in
An insulating film 306 is provided over the substrate 302 to cover the conductive film 304. An oxide semiconductor film 308 serving as a channel formation region of the transistor 112 is provided over the insulating film 306 in a region overlapping with the conductive film 304. A conductive film 310 and a conductive film 312 are formed over the oxide semiconductor film 308. A conductive film 313 formed in the same step as the conductive films 310 and 312 is provided over the electrode 354 and the insulating film 306. The conductive film 310 serves as the wiring SL and one of the source and drain of the transistor 112. The conductive film 312 serves as the other of the source and drain of the transistor 112. The conductive film 313 serves as a capacitor line.
The electrode 354 is formed in the same step as the oxide semiconductor film 308. The electrode 354 is a conductive oxide semiconductor having higher electrical conductivity than the oxide semiconductor film 308. The electrode 354 is provided in contact with an insulating film 321 and diffusion of hydrogen contained in the insulating film 321 into the electrode 354 increases the electrical conductivity of the electrode 354. In addition, a region in the electrode 354 in contacat with the conductive film 313 has high electrical conductivity because the region is not in contact with the insulating film 314 and oxygen vacancies in the oxide semiconductor are not filled. Accordingly, although the electrode 354 is an oxide semiconductor film formed in the same step as the oxide semiconductor film 308, it serves as an electrode.
The insulating film 314 is provided to cover the oxide semiconductor film 308 and the conductive films 310 and 312. The insulating film 314 covers one end portion of the electrode 354 and one end portion of the conductive film 313. The insulating film 314 has the opening 364 through which part of the electrode 354 and part of the conductive film 313 are exposed.
The insulating film 321 is provided over the insulating film 314, the electrode 354, and the conductive film 313. An opening 366 reaching the conductive film 312 is formed in the insulating films 314 and 321. The pixel electrode 322 is provided over the insulating film 321, and is connected to the conductive film 312 through the opening 366. The pixel electrode 322 is provided in a position overlapping with the electrode 354 serving as the first common electrode, and has openings (slits) as illustrated in the top view of
A substrate 330 is provided to face the substrate 302. A light-blocking film 332 having a function of blocking visible light, a color film 334 transmitting visible light within a certain wavelength range, an insulating film 336 in contact with the light-blocking film 332 and the color film 334, a second common electrode 338 in contact with the insulating film 336, and an alignment film 340 in contact with the second common electrode 338 are provided under the substrate 330.
Between the substrate 302 and the substrate 330, a liquid crystal layer 350 containing a liquid crystal material is interposed between the alignment film 324 and the alignment film 340. The liquid crystal element 111 includes the electrode 354 serving as the first common electrode, the insulating film 321, the pixel electrode 322, and the second common electrode 338. Note that a negative liquid crystal material is used for the liquid crystal layer 350, and the specific resistivity of the liquid crystal material is greater than or equal to 1.0×1013 Ω·cm and less than or equal to 1.0×1016 Ω·cm.
The configuration of the pixel 100 of this embodiment is different from the configuration of the pixel 100 illustrated in
Since a planarization film is not used, impurities (e.g., water) contained in the planarization film can be prevented from entering the oxide semiconductor film 308. Thus, the reliability of the transistor 112 including the oxide semiconductor film 308 can be improved, leading to a liquid crystal display device with high display quality.
An example of a method for manufacturing the pixel illustrated in
As illustrated in
For the substrate 302, the conductive film 304, the insulating film 306, and the oxide semiconductor film 308, the materials and formation methods for the substrate 302, the conductive film 304, the insulating film 306, and the oxide semiconductor film 308 described in Embodiment 1 can be referred to. The oxide semiconductor film 352 can be formed by using the same material and formation method as the oxide semiconductor film 308.
Next, a conductive film is formed over the insulating film 306 and the oxide semiconductor films 308 and 352 and processed by etching or the like, whereby the conductive films 310 and 312 in contact with the oxide semiconductor film 308 and the conductive film 313 in contact with the oxide semiconductor film 352 are formed, as illustrated in
For the conductive films 310, 312, and 313, the materials and formation method for the conductive films 310, 312, and 313 described in Embodiment 1 can be referred to.
Next, as in
For the insulating film 314, the material and formation method for the insulating film 314 described in Embodiment 1 can be referred to.
Next, as in
The opening 364 is formed, for example, by a dry etching method or a wet etching method. Alternatively, the opening 364 may be formed by a combination of a dry etching method and a wet etching method.
Next, as in
The insulating film 321 is formed using a material which prevents diffusion of impurities from the outside, such as water, alkali metal, and alkaline earth metal, into the oxide semiconductor film, and the material further includes hydrogen. Thus, when hydrogen in the insulating film 321 is diffused into the oxide semiconductor film 352, hydrogen is bonded to oxygen or to oxygen vacancies to generate electrons that are carriers in the oxide semiconductor film 352. As a result, the oxide semiconductor film 352 has higher conductivity than the oxide semiconductor film 308, and becomes the electrode 354 serving as the first common electrode.
For example, a silicon nitride film, a silicon nitride oxide film, or the like having a thickness of from 50 nm to 400 nm can be used as the insulating film 321. In this embodiment, a silicon nitride film having a thickness of 100 nm is used as the insulating film 321.
The silicon nitride film is preferably formed at a high temperature to have an improved blocking property; for example, the silicon nitride film is preferably formed at a temperature in the range from the substrate temperature of 100° C. to the strain point of the substrate, more preferably at a temperature in the range from 300° C. to 400° C. Note that in the case where the silicon nitride film is formed at a high temperature, a phenomenon in which oxygen is released from the oxide semiconductor film 308 and the carrier concentration is increased is caused in some cases; therefore, the upper limit of the temperature is a temperature at which the phenomenon is not caused.
Although not illustrated in
The insulating film formed over the insulating film 321 can smooth an uneven surface caused by a transistor or the like. Furthermore, since the insulating film is formed using an inorganic material, the insulating film contains fewer impurities that adversely affect an oxide semiconductor film than a resin planarization film using an organic material.
It is preferable that heat treatment be performed at least after the formation of the insulating film 314 so that oxygen contained in the insulating film 314 is transferred to the oxide semiconductor film 308 to fill oxygen vacancies in the oxide semiconductor film 308.
Next, as in
The opening 366 is formed by, for example, a dry etching method or a wet etching method. Alternatively, the opening 366 may be formed by a combination of a dry etching method and a wet etching method.
Next, as in
The pixel electrode 322 is formed in such a manner that a transparent conductive film is formed over the insulating film 321 and processed by etching or the like.
For the pixel electrode 322, the material and formation method for the pixel electrode 322 described in Embodiment 1 can be referred to.
Next, an alignment film 324 (not illustrated) is formed over the insulating film 321 and the pixel electrode 322. The alignment film 324 can be formed by a rubbing method, an optical alignment method, or the like.
Through the above steps, the components formed over the substrate 302 can be formed.
For the liquid crystal element 111, the substrate 330 provided to face the substrate 302, and the like, the description in Embodiment 1 can be referred to.
The structures, the methods, and the like described in this embodiment can be combined as appropriate with any of the structures, the methods, and the like described in the other embodiments.
Embodiment 4In this embodiment, examples of electronic devices including the liquid crystal display device of one embodiment of the present invention are described with reference to
The liquid crystal display device of one embodiment of the present invention can be used for display devices, personal computers, or image reproducing devices provided with recording media (typically, devices that reproduce the content of recording media such as digital versatile discs (DVDs) and have displays for displaying the reproduced images). Other examples of the electronic devices to which the liquid crystal display device of one embodiment of the present invention can be applied include cellular phones, game machines (including portable game machines), personal digital assistants, e-book readers, cameras such as video cameras and digital still cameras, goggle-type displays (head mounted displays), navigation systems, audio reproducing devices (e.g., car audio systems and digital audio players), copiers, facsimiles, printers, multifunction printers, automated teller machines (ATMs), and vending machines.
The structures, the methods, and the like described in this embodiment can be combined as appropriate with any of the structures, the methods, and the like described in the other embodiments.
Example 1In this example, the transmittance of the liquid crystal display device of one embodiment of the present invention was measured. The liquid crystal display devices used in this example are described below with reference to
A liquid crystal display device 720 illustrated in
The liquid crystal display device 720 illustrated in
A transistor 712 includes the conductive film 604, the insulating film 606, the oxide semiconductor film 608, and the conductive films 610 and 612. The conductive film 612 included in the transistor 712 is connected to the pixel electrode 622 through an opening formed in the insulating films 616 and 620.
Next, a comparative liquid crystal display device 730 illustrated in
The comparative liquid crystal display device 730 illustrated in
The transistor 712 includes the conductive film 604, the insulating film 606, the oxide semiconductor film 608, and the conductive films 610 and 612. The conductive film 612 included in the transistor 712 is connected to the pixel electrode 622 through an opening formed in the insulating films 616 and 620.
Differences between the liquid crystal display device 720 of one embodiment of the present invention illustrated in
In the structure illustrated in
Methods for manufacturing the liquid crystal display devices 720 and 730 illustrated in
A glass substrate was used as the substrate 602. The conductive film 604 was formed over the substrate 602. A 200-nm-thick tungsten film was formed by a sputtering method as the conductive film 604. Then, the insulating film 606 was formed over the substrate 602 and the conductive film 604. A 400-nm-thick silicon nitride film and a 50-nm-thick silicon oxynitride film were stacked as the insulating film 606.
Note that the silicon nitride film was formed to have a three-layer structure of a first silicon nitride film, a second silicon nitride film, and a third silicon nitride film.
The first silicon nitride film was formed to a thickness of 50 nm under the following conditions: silane with a flow rate of 200 sccm, nitrogen with a flow rate of 2000 sccm, and ammonia with a flow rate of 100 sccm were supplied to a treatment chamber of a plasma CVD apparatus as e source gas; the pressure in the treatment chamber was adjusted to 100 Pa; and a power of 2000 W was supplied with the use of a 27.12 MHz high-frequency power source. The second silicon nitride film was formed to a thickness of 300 nm under the following conditions: silane with a flow rate of 200 sccm, nitrogen with a flow rate of 2000 sccm, and ammonia with a flow rate of 2000 sccm were supplied to a treatment chamber of a plasma CVD apparatus as a source gas; the pressure in the treatment chamber was adjusted to 100 Pa; and a power of 2000 W was supplied with the use of a 27.12 MHz high-frequency power source. The third silicon nitride film was formed to a thickness of 50 nm under the following conditions: silane with a flow rate of 200 sccm and nitrogen with a flow rate of 5000 sccm were supplied to a treatment chamber of a plasma CVD apparatus as a source gas; the pressure in the treatment chamber was adjusted to 100 Pa; and a power of 2000 W was supplied with the use of a 27.12 MHz high-frequency power source. The substrate temperature during the formation of the first silicon nitride film, the second silicon nitride film, and the third silicon nitride film was set to 350® C.
The silicon oxynitride film was formed under the following conditions: silane with a flow rate of 20 sccm and dinitrogen monoxide with a flow rate of 3000 sccm were supplied to a treatment chamber of a plasma CVD apparatus as a source gas; the pressure in the treatment chamber was adjusted to 40 Pa; and a power of 100 W was supplied with the use of a 27.12 MHz high-frequency power source. The substrate temperature during the formation of the silicon oxynitride film was set to 350° C.
Next, the oxide semiconductor film 608 was formed over the insulating film 606 in a region overlapping with the conductive film 604. Here, a 35-nm-thick oxide semiconductor film was formed over the insulating film 614 by a sputtering method.
The oxide semiconductor film was formed under the following conditions: a sputtering target of In:Ga:Zn=1:1:1 (atomic ratio) was used; oxygen with a flow rate of 30 sccm and argon with a flow rate of 270 sccm were supplied as a sputtering gas into a treatment chamber of a sputtering apparatus; the pressure in the treatment chamber was adjusted to 0.6 Pa; and a direct-current power of 5 kW was supplied. The substrate temperature during the formation of the oxide semiconductor film was set to 170° C.
Then, the conductive films 610 and 612 in contact with the oxide semiconductor film 608 were formed.
As the conductive films 610 and 612, a 400-nm-thick aluminum film was formed over a 50-nm-thick tungsten film, and a 100-nm-thick titanium film was formed over the aluminum film.
Next, after the substrate was transferred to a treatment chamber in a reduced pressure and heated at 350° C., the oxide semiconductor film 608 was exposed to oxygen plasma that was generated in a dinitrogen monoxide atmosphere by supply of a high-frequency power of 150 W to an upper electrode provided in the treatment chamber with the use of a 27.12 MHz high-frequency power source.
Next, the insulating film 614 was formed over the oxide semiconductor film 608 and the conductive films 610 and 612. Hera, the insulating film 614 was formed to have a three-layer structure of a first oxide insulating film, a second oxide insulating film, and a nitride insulating film.
First, after the above plasma treatment, the first oxide insulating film and the second oxide insulating film were formed in succession without exposure to the air. A 50-nm-thick silicon oxynitride film was formed as the first oxide insulating film, and a 400-nm-thick silicon oxynitride film was formed as the second oxide insulating film.
The first oxide insulating film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 20 sccm and dinitrogen monoxide with a flow rate of 3000 sccm were used as a source gas; the pressure in the treatment chamber was 200 Pa; the substrate temperature was 350° C.; and a high-frequency power of 100 W was supplied to parallel-plate electrodes.
The second oxide insulating film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 160 sccm and dinitrogen monoxide with a flow rate of 4000 sccm were used as a source gas; the pressure in the treatment chamber was 200 Pa; the substrate temperature was 220° C.; and a high-frequency power of 1500 W was supplied to parallel-plate electrodes. Under the above conditions, it is possible to form a silicon oxynitride film containing oxygen at a higher proportion than oxygen in the stoichiometric composition and from which part of oxygen is released by heating.
Next, by heal treatment, water, nitrogen, hydrogen, and the like were released from the first oxide insulating film and the second oxide insulating film and part of oxygen contained in the second oxide insulating film was supplied to the oxide semiconductor film 608. Here, the heat treatment was performed at 350° C. in a mixed atmosphere of nitrogen and oxygen for one hour.
Then, a 100-nm-thick nitride insulating film was formed over the second oxide insulating film. The nitride insulating film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 50 sccm, nitrogen with a flow rate of 5000 sccm, and ammonia with a flow rate of 100 sccm were used as a source gas; the pressure in the treatment chamber was 100 Pa; the substrate temperature was 350° C.; and a high-frequency power of 1000 W was supplied to parallel plate electrodes.
Next, an opening reaching the conductive film 612 was formed in the insulating film 614. The opening was formed by a dry etching method.
The insulating film 616 having an opening was formed over the insulating film 614. An acrylic resin, which is an organic resin material, was used for the insulating film 616. The thickness of the acrylic resin film was set to 2 μm.
The first common electrode 618 was formed over the insulating film 616. As the first common electrode 618, a 100-nm-thick conductive film of an indium oxide-tin oxide compound (ITO-SiO2) was formed by a sputtering method. Note that the composition of a target used for forming the conductive film was In2O3:SnO2:SiO2=85:10:5 [wt %].
Then, the insulating film 620 was formed over the insulating film 616 and the first common electrode 618. A 300-nm-thick nitride insulating film was formed as the insulating film 620. The nitride insulating film was formed by a plasma CVD method under the following conditions: silane with a flow rate of 50 sccm, nitrogen with a flow fate of 5000 sccm, and ammonia with a flow rate of 100 seem were used as a source gas; the pressure in the treatment chamber was 200 Pa; the substrate temperature was 220° C.; and a high-frequency power of 1000 W was supplied to parallel plate electrodes.
Subsequently, the pixel electrode 622 was formed over the insulating film 620. As the pixel electrode 622, a 80-nm-thick conductive film of an indium oxide-tin oxide compound (ITO-SiO2) was formed by a sputtering method. Note that the composition of a target used for forming the conductive film was the same as the composition of a target used for forming the first common electrode 618. After that, heat treatment was performed in a nitrogen atmosphere at 250° C. for one hour.
Next, the alignment film 624 was formed over the insulating film 620 and the pixel electrode 622. A 60-nm-thick polyimide film was used as the alignment film 624. Note that the resistivity of the polyimide film used as the alignment film 624 was 4.0×1015 Ω·cm.
Through the above steps, the components over the substrate 602 were formed.
Next, a method for forming components on the substrate 630 provided to face the substrate 602 is described. Note that the liquid crystal display device 720 illustrated in
A glass substrate was used as the substrate 630. The light-blocking film 632 was formed in a desired region to be in contact with the substrate 630. As the light-blocking film 632, a 600-nm-thick organic resin film containing black pigment was formed by a spin coating method.
Next, the color film 634 was formed in contact with the substrate 630. As the color film 634, a 1.4-μm-thick organic resin film containing pigment was formed by a spin coating method.
Then, the insulating film 636 was formed in contact with the light-blocking film 632 and the color film 634. A 1.5-μm-thick acrylic resin film was used as the insulating film 636.
Subsequently, the second common electrode 638 was formed in contact with the insulating film 636. As the second common electrode 638, a 100-nm-thick conductive film of an indium oxide-tin oxide compound (ITO-SiO2) was formed by a sputtering method. Note that the composition of a target used for forming the conductive film was the same as the composition of a target used for forming the first common electrode 618.
Then, the alignment film 640 was formed in contact with the second common electrode 638. The alignment film 640 was formed using the same material as the alignment film 624.
Next, the substrate 630 and the substrate 602 were bonded to each other, and a liquid crystal material forming the liquid crystal layer 650 was injected between the substrates by a one drop filling method.
The liquid crystal layer 650 was formed using a negative liquid crystal material (MLC-3006 produced by Merck) such that the cell gap (the distance between the alignment film 624 and the alignment film 640) was set to 3.5 μm.
Through the above steps, Sample 1, which is the liquid crystal display device of one embodiment of the present invention illustrated in
A glass substrate was used as the substrate 630. The light-blocking film 632 was formed in a desired region to be in contact with the substrate 630. As the light-blocking film 632, a 600-nm-thick organic resin film containing black pigment was formed by a spin coating method.
Next, the color film 634 was formed in contact with the substrate 630. As the color film 634, a 1.4-μm-thick organic resin film containing pigment was formed by a spin coating method.
Then, the insulating film 636 was formed in contact with the light-blocking film 632 and the color film 634. A 1.5-μm-thick acrylic resin film was used as the insulating film 636.
Subsequently, the electrode 642 was formed in contact with a surface of the substrate 630 where the insulating film 636 was not provided. As the the electrode 642, a 100-nm-thick conductive film of an indium oxide-tin oxide compound (ITO-SiO2) was formed by a sputtering method. Note that the composition of a target used for forming the conductive film was the same as the composition of a target used for forming the first common electrode 618.
Then, the alignment film 640 was formed in contact with the insulating film 636. The alignment film 640 was formed using the same material as the alignment film 624.
Next, the the substrate 630 and the substrate 602 were bonded to each other, and a liquid crystal material forming the liquid crystal layer 650 was injected between the substrates by a one drop filling method.
The liquid crystal layer 650 was formed using a negative liquid crystal material (MLC-3006 produced by Merck) such that the cell gap (the distance between the alignment film 624 and the alignment film 640) was set to 3.5 μm.
Through the above steps, Comparative Sample 2, which is the comparative liquid crystal display device illustrated in
Next, the transmittances of Sample 1 and Comparative Sample 2 were measured. In measuring the transmittance of Sample 1, voltages of 0 V, 5.5 V, and 0.8 V were applied to the first common electrode 618, the pixel electrode 622, and the second common electrode 638, respectively. The voltage application to the pixel electrode 622, the second common electrode 638, and the second common electrode 638 was performed intermittently, and data writing was performed every time voltage was applied. In measuring the transmittance of Comparative Sample 2, voltages of 0 V, 5.5 V, and 0.8 V were applied to the first common electrode 618, the pixel electrode 622, and the electrode 642, respectively. The voltage application to the pixel electrode 622, the second common electrode 638, and the electrode 642 was performed intermittently and data writing was performed every time voltage was applied. Note that data writing in Sample 1 and Comparative Sample 2 was controlled by the transistor 712 formed in Sample 1 and Comparative Sample 2.
The transmittance-time characteristics shown in
The results shown in
The results shown in
In this example, the transmittance of the liquid crystal display device of one embodiment of the present invention was calculated. The structures of the liquid crystal display devices used for the calculation in this example are described below with reference to
The liquid crystal display device that is used for calculation and illustrated in
For convenience of calculation, the liquid crystal display device for calculation illustrated in
A liquid crystal display device that is used for calculation and illustrated in
The liquid crystal display device for calculation illustrated in
In
In the liquid crystal display device for calculation illustrated in
In the liquid crystal display device for calculation illustrated in
In
From the calculation results shown in
As described above, the liquid crystal display device of one embodiment of the present invention can have high black and white contrast between adjacent pixels.
The structure described in this example can be combined as appropriate with any of the structures described in the embodiments or the other examples.
This application is based on Japanese Patent Application serial no. 2013-106681 filed with Japan Patent Office on May 21, 2013; Japanese Patent Application serial no. 2013-126895 filed with Japan Patent Office on Jun. 17, 2013; and Japanese Patent Application serial no. 2013-153362 filed with Japan Patent Office on Jul. 24, 2013, the entire contents of which are hereby incorporated by reference.
Claims
1. A liquid crystal display device comprising:
- a first substrate comprising: a transistor; a first electrode electrically connected to one of a source electrode and a drain electrode of the transistor; an insulating layer in contact with the first electrode; a second electrode in contact with the insulating layer; and a capacitor line electrically connected to the second electrode,
- a second substrate facing the first substrate, the second substrate comprising a third electrode; and
- a liquid crystal layer comprising a liquid crystal material between the first substrate and the second substrate,
- wherein a potential difference between the second electrode and the third electrode is smaller than a potential difference between the third electrode and the first electrode, and
- wherein the potential difference between the third electrode and the first electrode is smaller than a potential difference between the second electrode and the first electrode.
2. The liquid crystal display device according to claim 1, wherein the second electrode is in contact with the capacitor line.
3. The liquid crystal display device according to claim 1, further comprising a planarization film between the first substrate and the first electrode.
4. The liquid crystal display device according to claim 1, further comprising a color film between the second substrate and the third electrode.
5. A liquid crystal display device comprising:
- a first substrate comprising: a transistor; a first electrode electrically connected to one of a source electrode and a drain electrode of the transistor; an insulating layer in contact with the first electrode; a second electrode in contact with the insulating layer; and a capacitor line electrically connected to the second electrode,
- a second substrate facing the first substrate, the second substrate comprising a third electrode; and
- a liquid crystal layer between the first substrate and the second substrate,
- wherein a potential difference between the second electrode and the third electrode is smaller than a potential difference between the third electrode and the first electrode,
- wherein the potential difference between the third electrode and the first electrode is smaller than a potential difference between the second electrode and the first electrode, and
- wherein the liquid crystal layer comprises a liquid crystal material with negative dielectric anisotropy
6. The liquid crystal display device according to claim 5, wherein the second electrode is in contact with the capacitor line.
7. The liquid crystal display device according to claim 5, wherein a dielectric constant anisotropy of the liquid crystal material with negative dielectric anisotropy is −3.0.
8. The liquid crystal display device according to claim 5, further comprising a planarization film between the first substrate and the first electrode.
9. The liquid crystal display device according to claim 5, further comprising a color film between the second substrate and the third electrode.
10. The liquid crystal display device according to claim 5, wherein the second electrode and the third electrode are connected to different power supply lines.
11. A liquid crystal display device comprising:
- a first substrate comprising: a transistor; a first electrode electrically connected to one of a source electrode and a drain electrode of the transistor; an insulating layer; a second electrode in contact with the insulating layer; and a capacitor line electrically connected to the second electrode,
- a second substrate facing the first substrate, the second substrate comprising a third electrode; and
- a liquid crystal layer comprising a liquid crystal material between the first substrate and the second substrate,
- wherein the second electrode has a region overlapping with the first electrode with the insulating layer provided therebetween,
- wherein a potential difference between the second electrode and the third electrode is smaller than a potential difference between the third electrode and the first electrode, and
- wherein the potential difference between the third electrode and the first electrode is smaller than a potential difference between the second electrode and the first electrode.
12. The liquid crystal display device according to claim 11, wherein the second electrode is in contact with the capacitor line.
13. The liquid crystal display device according to claim 11, further comprising a planarization film between the first substrate and the first electrode.
14. The liquid crystal display device according to claim 11, further comprising a color film between the second substrate and the third electrode.
Type: Application
Filed: Jul 18, 2019
Publication Date: Nov 7, 2019
Inventors: Ryo HATSUMI (Hadano), Shuji FUKAI (Atsugi), Daisuke KUBOTA (Atsugi)
Application Number: 16/515,223