MOLTEN AIR RECHARGEABLE BATTERIES
The present disclosure relates to rechargeable electrochemical battery cells (molten air batteries). The cells use air and a molten electrolyte, are quasi-reversible (rechargeable) and have the capacity for multiple electrons stored per molecule and have high intrinsic electric energy storage capacities. The present disclosure also relates to the use of such in a range of electronic, transportation and power generation devices, such as greenhouse gas reduction applications, electric car batteries and increased capacity energy storage systems for the electric grid.
The present application claims the benefit of U.S. Provisional Application No. 61/762,883, filed Feb. 9, 2013, which is hereby incorporated by reference in its entirety.
FIELD OF THE INVENTIONThe present invention relates to rechargeable electrochemical battery cells (molten air batteries). The cells use air and a molten electrolyte, are quasi-reversible (rechargeable) and have the capacity for multiple electrons stored per molecule. The cells described herein have high intrinsic electric energy storage capacities and are useful in a range of electronic, transportation and power generation devices, such as greenhouse gas reduction applications, electric car batteries and increased capacity energy storage systems for the electric grid.
BACKGROUND OF THE INVENTIONHigh capacity, cost effective batteries are needed for a range of applications, including greenhouse gas reduction applications, overcoming the battery driven “range anxiety” of electric vehicles, and increased energy capacity storage for the electric grid.
A zirconia stabilized VB2 air battery has been described. See, e.g., S. Licht et al., Chem. Comm., 3257-3259, 2008; S. Licht et al., Electrochem. Solid State Lett. 14, A83-A85, 2011; and S. Licht et al., Electrochem. Solid State Lett. 15, A12-A14, 2012. This 11e− (eleven electron) per molecule, room temperature, aqueous electrolyte battery has the highest volumetric energy capacity for a battery, with an intrinsic capacity greater than that of gasoline and an order of magnitude higher than that of conventional lithium ion batteries. The challenge, however, is recharging the battery (i.e., electrochemically reinserting 11e− into the battery discharge products).
Several classes of molten electrolyte batteries have been investigated. A molten sulfur battery has been studied, particularly for electric car and grid applications, See, e.g., B. Dunn et al., Science, 334, 9280935, 2011; and J. B. Goodenough et al., J. Solid State Electrochem., 16, 2019-2029, 2012. During discharge, the battery uses sulfur and sodium (or potassium) for the respective cathode and anode storage materials, and these high temperature molten components are kept from chemically reacting by a solid electrolyte beta alumina separator. Sulfur cells have moderately high capacity. Both the molten and room temperature class of sulfur cathode batteries are limited by the maximum intrinsic capacity of the 2e− per sulfur (2 Faraday/32 g sulfur).
Another class of molten metal electrolyte batteries utilizes an insoluble, dense, molten cathode during discharge situated below a (less dense) molten metal anode floating on a molten electrolyte. Unlike the molten sulfur battery, this class does not require a solid electrolyte separator; but to date has lower capacity. An example of this class of batteries is the magnesium-antimony battery with a molten halide electrolyte. See, e.g., D. J. Bradwell et al., J. Amer. Chem. Soc., 134, 1895-1897, 2012.
Iron has been widely explored for battery storage due to its availability as a resource and its capability for multiple electron charge transfer. In the early 1900s, Edison developed rechargeable batteries based on the discharge of an iron anode (in an aqueous electrolyte at room temperature) to form iron oxide. See, e.g., U.S. Pat. Nos. 678,722 and 692,507. Retention of an even a small fraction of the intrinsic anodic storage capacity of these batteries has been a challenge, and room temperature iron batteries continue to be explored today. The 3e− cathodic capacity of iron oxides has also been explored. See, e.g., S. Licht et al., Science, 285, 1039-1042, 1999; S. Licht et al., Energies, 3, 960-972, 2010; and M. Farmand et al., Electrochem. Comm., 13, 909-912, 2011.
A molten carbonate electrolytic conversion of iron oxide to iron as a CO2-free synthesis alternative to the conventional greenhouse gas intensive industrial production of iron metal has been described. The high solubility of iron oxide in lithiated molten carbonate electrolytes was demonstrated to lead to the facile splitting of iron oxide to iron metal with the concurrent release of oxygen. Sec e.g., S. Licht et al., Advanced Materials, 47, 5592-5612, 2011 and International Publication No. WO 2011/140209.
There is, however, a need for new rechargeable batteries that have the capacity for multiple electrons stored per molecule, have high intrinsic electric energy storage capacities and can operate at lower temperatures.
SUMMARY OF THE INVENTIONThe present inventors have developed a rechargeable electrochemical battery cell that utilizes air and a molten electrolyte, is quasi-reversible (rechargeable) and has the capacity for multiple electrons stored per molecule. The cells described herein have high intrinsic electric energy storage capacities. Unlike previous rechargeable batteries, the batteries of the present invention are not burdened by the weight of the active cathode material. In contrast, the rechargeable molten cathode instead uses oxygen directly from the air to yield a high battery capacity. The cathode is compatible with multiple electron anodes. Additionally, for the batteries of the present invention, external carbon dioxide (which is disadvantageous to battery charging and discharging) is not required for discharge at the air electrode.
In one aspect, the present invention relates to a rechargeable battery cell comprising
-
- a) an air electrode;
- b) a metal electrode, or a nonmetal electrode that is capable of being oxidized; and
- c) a molten electrolyte disposed between the air electrode and the metal electrode or non-metal electrode;
wherein
a the air electrode, the principle reaction is oxygen (O2) reacted to form oxide during discharge, the principle reaction is not carbon dioxide (CO2) and oxygen (O2) being reduced to form carbonate (CO32−) during discharge.
In one embodiment of any of the rechargeable battery cells described herein, external carbon dioxide is not required for discharge at the air electrode.
Thus, in one aspect, the present invention relates to a rechargeable battery cell comprising
-
- a) an air electrode;
- b) a metal electrode, or a nonmetal electrode that is capable of being oxidized; and
- c) a molten electrolyte disposed between the air electrode and the metal electrode or non-metal electrode;
wherein
at the air electrode, the principle reaction is oxygen (O2) reacted to form oxide during discharge, not carbon dioxide (CO2) and oxygen (O2) being reduced to form carbonate (CO32−) during discharge and external carbon dioxide is not required for discharge at the air electrode.
In another aspect, the present invention relates to a rechargeable battery cell comprising
-
- a) an air electrode;
- b) a metal electrode, or a nonmetal electrode that is capable of being oxidized; and
- c) a molten electrolyte disposed between the air electrode and the metal electrode;
wherein - at the air electrode a reduction/oxidation reaction between oxygen and oxide ion takes place; and
- at the metal electrode or the nonmetal electrode that is capable of being oxidized, oxide interacts with the metal electrode or the nonmetal electrode that is capable of being oxidized for capturing/releasing oxide during discharging/charging, respectively.
In one embodiment of any of the rechargeable battery cells described herein, the metal electrode comprises a metal that generates more than one electron when oxidized. For example, in one embodiment of any of the rechargeable battery cells described herein, the metal electrode is selected from, but not limited to iron, zinc, aluminum, magnesium, bismuth, vanadium, manganese, nickel, silver, barium, calcium, strontium, lead, mercury, cadmium, chromium, tin, titanium, and any combination thereof. In one embodiment of any of the rechargeable battery cells described herein, the metal electrode comprises iron.
In one embodiment of any of the rechargeable battery cells described herein, the non-metal electrode that is capable of being oxidized comprises a non-metal that generates more than one electron when oxidized. In one embodiment of any of the rechargeable battery cells described herein, the non-metal electrode is selected from carbons (such as, but not limited to, graphite, amorphous carbon, nanocarbons (e.g., fullerenes, nanorods, nanotubes), borides (such as, but not limited to, vanadium boride, titanium boride, tantalum boride, barium boride, magnesium boride, calcium boride, iron boride, cobalt boride, nickel boride, lanthanum boride, zirconium boride, molybdenum boride, tungsten boride, niobium boride), hydrides, carbides, and combinations thereof. In one embodiment of any of the rechargeable battery cells described herein, the non-metal electrode comprises carbon (C) or VB2. In one embodiment of any of the rechargeable battery cells described herein, the non-metal electrode comprises carbon. In one embodiment of any of the rechargeable battery cells described herein, the non-metal electrode comprises vanadium boride (VB2).
In one embodiment of any of the rechargeable battery cells described herein, the molten electrolyte is molten carbonate, or a mixture thereof. In a preferred embodiment, the molten metal carbonate comprises one or more alkali metal carbonates. In a further preferred embodiment, the molten metal carbonate comprises lithium carbonate, sodium carbonate, potassium carbonate, or any combination thereof.
In one embodiment, the molten electrolyte comprises Li2CO3. In one embodiment, the molten electrolyte comprises Li2CO3, Na2CO3, K2CO3, and any combination thereof. For example, in one embodiment, the molten electrolyte comprises Li2CO3 and Na2CO3. In another embodiment, the molten electrolyte comprises Li2CO3, Na2CO3 and K2CO3.
In one embodiment, the molten electrolyte is selected from Li0.7Na0.9CO3, and Li0.9Na0.6K0.5C3. In another embodiment, the molten electrolyte is selected from Li0.7Na0.93CO3, Li0.85Na0.61K0.54CO3, and Li0.87Na0.63K0.50CO3. In a further embodiment, the molten electrolyte is Li0.87Na0.63K0.50O3.
In one embodiment, the molten electrolyte comprises CaCO3, Na2CO3, K2CO3, and any combination thereof.
In one embodiment, the molten electrolyte is selected from Ca0.3Na0.7K0.8C3 and Ca0.2Na1.0K0.7CO3. In one embodiment, the molten electrolyte is selected from Ca0.27Na0.7K0.73CO3, Ca0.27Na0.70K0.75CO3 and Ca0.16Na1.03K0.65CO3.
In another embodiment, the molten electrolyte comprises one or more molten nonconductive salts (e.g., a molten oxide, such as, but not limited to, a non-metal oxide such as B2O3 (with a melting point of approximately 450° C. to 510° C.), or a metal oxide such as V2O5 (with a melting point of approximately 690° C.), or any combination thereof; and one or more inorganic salts that is conductive when dissolved, such as, but not limited to, a molten soluble metal oxide (e.g., Li2O, LiFeO2, LiVO3, Li2B4O7, BaO, and combinations thereof), a molten soluble metal carbonate, or a molten soluble halide (e.g., lithium chloride, lithium fluoride, vanadium chloride, vanadium fluoride, titanium chloride, titanium fluoride, and combinations thereof), or any combination of the foregoing, such that the electrolyte mix may form an insoluble, reduced metal or non-metal when electrochemically charged. In one embodiment, the dissolved inorganic salt comprises a conductive salt (e.g., a salt that helps to ensure that the electrolyte is electrochemical conductive, rather than a resistive molten glass). For further example, the inorganic salt may be selected from metal oxides (e.g., alkali metal oxides, alkali earth metal oxides), metal halides (e.g., alkali metal halides, alkali earth metal halides), metal sulfates (e.g., alkali metal sulfates, alkali earth metal sulfates), metal nitrates (e.g., alkali metal nitrates, alkali earth metal nitrates), metal halates (e.g., alkali metal halates, alkali earth metal halates), and any combination thereof.
In another embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O), calcium oxide (CaO), or any combination thereof. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) and calcium oxide (CaO) in a molar ratio of about 1:2:4:3. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) and calcium oxide (CaO) in a molar ratio of about 1:2:2:0. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) and calcium oxide (CaO) in a molar ratio of about 1:7:12:0. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) in a ratio of about molar 1:2:0.67. In another embodiment, the molten electrolyte comprises LiVO3 and LiBO2.
In an additional embodiment, any of the molten electrolytes described herein further comprise one or more additional soluble additives that may, for example, extend the cycling life of the battery and/or modify the voltage of the cell. In one embodiment, the molten electrolyte further comprises additional additives selected from sulphates, halides, nitrates, carbonates, oxides, and any combination thereof (e.g., lithium oxide, barium carbonate, calcium carbonate, magnesium oxide, cesium carbonate, calcium oxide, and any combination thereof.)
In one embodiment, the melting point of the molten electrolyte is (i) between about 395° C. and about 900° C. (ii) between about 600° C. and about 900° C., (iii) between about 600° C. and about 900° C., (iv) between about 720° C. and about 900° C., (v) between about 700° C. and about 800° C., or (vi) between about 150° C. and about 500° C.
For example, in one embodiment, the melting point of the electrolyte is between about 395° C. and about 900° C., such as between about 600° C. and about 900° C., between about 720° C. and about 900° C. or between about 700° C. and about 800° C., for example, about 600° C., about 700° C., about 723° C., about 851° C. or about 891° C.
As a further example, in one embodiment, the melting point of the electrolyte is (i) between about 600° C. and about 900° C., (ii) about 600° C. and about 900° C., (iii) between about 720° C. and about 900° C., (iv) between about 700° C. and about 800° C., (v) about 600° C., (vi) about 700° C., (viii) about 723° C., (ix) about 851° C. or (x) about 891° C.
As another example, in another embodiment, the melting point of the electrolyte is between about 395° C. and about 900° C., for example, between about 395° C. and about 700° C., such as about 395° C., about 500° C. or about 600° C.
In another embodiment, the rechargeable battery cell operates at a temperature of between about 395° C. and about 900° C., for example, between about 395° C. and about 700° C. or between about 395° C. and about 600° C., such as about 395° C., about 500° C. or about 600° C.
In a further embodiment, the rechargeable battery cell operates at temperature of between about 150° C. and about 500° C. For example, the molten electrolyte may comprise one or more metal hydroxides, metal hydroxide eutectics, metal carbonates, and any combination thereof. For further example, the molten electrolyte may comprise one or more alkali metal hydroxides, alkali earth metal hydroxides, alkali earth metal hydroxide eutectics, alkali earth metal hydroxide eutectics, alkali metal carbonates, alkali earth metal carbonates and any combination thereof. For example, pure NaOH, KOH and LiOH become molten electrolytes at approximately 320° C., 400° C. and 471° C., respectively. A mole percent mixture containing 49% KOII and 51% NaOII melts at approximately 173° C.; a mole percent mixture containing 71% NaOH and 29% LiOH melts at approximately 216° C., while a mole percent mixture containing 59% KOH and 31% LiOH melts at approximately 225° C. A mole percent mixture containing 91% NaOH and 9% Na2CO3 melts at approximately 295° C.; a mole percent mixture containing 90 mol % KOH and 10% K2CO3 melts at approximately a360° C.; and a mole percent mixture containing 80% LiOH and 20% Li2CO3 melts at approximately 415° C. A carbonate eutectic such as Li0.9Na0.6K0.5CO3 has a inciting point of approximately 400° C. When this carbonate eutectic is mixed with 10 wt % of NaOII, NaNO3 or KCl, the resulting electrolyte melting point is about 388° C., 396° C. or 326° C., respectively. The rechargeable battery cells of the invention may comprise any of the molten electrolyte mixtures described herein. Thus, in one embodiment, the molten electrolyte comprises NaOH, LiOH, KOH, Na2CO3, K2CO3, Li2CO3, and any combination thereof, in any molar ratio. In one embodiment, the molten electrolyte comprises NaOH, LiOH, KOH, and any combination thereof, in any molar ratio. In another embodiment, the molten electrolyte comprises NaOII and Na2CO3 in any molar ratio. In another embodiment, the molten electrolyte comprises KOH and K2CO3 in any molar ratio. In another embodiment, the molten electrolyte comprises LiOH and Li2CO3 in any molar ratio.
In another embodiment of any of the rechargeable battery cells described herein, the overall electrolysis chemistry of the cell can be expressed by one of equations (1), (2) or (3):
Fe+¾O2½ Fe2O3 (1)
C+O2CO2 (2)
VB2+1¼ O2B2O3+½ V2O5 (3)
In another aspect, the present invention relates to an electrical energy storage device comprising a rechargeable battery cell according to any of the embodiments described herein. In another aspect, the present invention relates to a plurality of rechargeable battery cells according to any of the embodiments described herein connected together to provide a bank of cells. Thus, the present invention also provides a hank of cells comprising a plurality of rechargeable battery cells according to any of the embodiments described herein.
In another aspect, the present invention relates to the use of a rechargeable battery cell according to any of the embodiments described herein as a rechargeable energy storage device, for example, for automotive applications, power electronic applications, electric grid storage applications and/or energy storage applications.
In another aspect, the present invention relates to a method of cyclically storing and releasing energy comprising cyclically charging and discharging a rechargeable battery cell according to any of the embodiments described. In one embodiment, the charging/recharging is performed for 2 or more cycles, such as 5 or more cycles, 10 or more cycles, 15 or more cycles, 20 or more cycles, 25 or more cycles, or 30 or more cycles.
The present invention relates to a rechargeable electrochemical battery cell (molten air battery) that utilizes air and a molten electrolyte. The cells include a metal, or a non-metal that that is capable of being oxidized as the anode.
The molten air batteries described herein use molten electrolytes that enhance current flow (improve the kinetics of charge transfer). The molten air batteries also have amongst the highest intrinsic storage capacity of any rechargeable battery as they use oxygen that is freely available from the air, and discharge using anodes that use multiple electrons per molecule storage. For example, one mole of electrons has a charge of 26801 milliampere hour (mAh). An increasing multiple of electrons (e−) stored per molecule and a low formula weight can greatly increase the charge capacity of a battery. For example, when a silver anode releases 1 electron per silver molecule it has a maximum stored capacity of 248 mAh/g (1 mole of silver has a mass of 107.9 gram/mole). The anodic capacity of various materials based on their increasing electrons released per molecule and formula weight is zinc (2e−/65.4 g/mol)=820 mAh/g, iron (3e−/55.8 g/mol)=1450 mAh/g, carbon (4e−/12.0 g/mol)=8930 mAh/gr. VB2 (72.6 g/mol) can release 11 electrons per molecule with a storage capacity of 4060 mAh/g. Volumetric storage capacity is also enhanced by higher density, and iron, carbon and VB2, have several fold higher density than lithium. Lithium ion batteries do not use oxygen freely available from the air and have a much lower anode capacity. Hence, e.g., the iron, carbon and VB2 molten air batteries described herein have an order of magnitude higher intrinsic capacity than Li-ion batteries.
In one embodiment, the rechargeable molten air batteries described herein have an operational temperature that is decreased from about 700-800° C., to about 600° C. or less by, e.g., the use of carbonate eutectics or carbonate/hydroxide mixtures which provide low melting point molten electrolytes (to below 200° C.) for the battery. Lower operational temperature battery chemistries provide greater functionality for molten air batteries in applications such as for electric vehicles.
The Molten Electrolyte
The rechargeable batteries of the present invention utilize a molten electrolyte. In one embodiment, the molten electrolyte is a molten carbonate, or a mixture of molten carbonates. Suitable molten carbonates include, but are not limited to, lithium carbonate, sodium carbonate, potassium carbonate, strontium carbonate, rubidium carbonate, cesium carbonate, barium carbonate, calcium carbonate, and any combination thereof. In additional embodiments, the molten electrolyte further comprises one or more alkali metal hydroxides, alkali earth metal hydroxides, or any combination thereof.
In one embodiment, the molten electrolyte is Li2O3. In another embodiment, the molten electrolyte is a eutectic molten electrolyte, e.g., a combination of one or more of lithium carbonate, sodium carbonate, potassium carbonate and calcium carbonate. In one embodiment, the molten electrolyte comprises Li2CO3. In one embodiment, the molten electrolyte comprises Li2CO3, Na2CO3, K2CO3, and any combination thereof. For example, in one embodiment, the molten electrolyte comprises a mixture of Li2CO3 and Na2CO3. In another embodiment, the molten electrolyte comprises a mixture of Li2CO3, Na2CO3 and K2CO3. In one embodiment, the molten electrolyte is selected from Li0.7Na0.6CO3 and Li0.6Na0.6K0.5CO3. In one embodiment, the molten electrolyte is Li0.7Na0.93CO3. In another embodiment, the molten electrolyte is Li0.85Na0.61K0.54CO3. In a further embodiment, the molten electrolyte is Li0.87Na0.63K0.50CO3
In one embodiment, the molten electrolyte comprises CaCO3, Na2CO3, K2CO3, and any combination thereof. In one embodiment, the molten electrolyte is selected from Ca0.3Na0.7K0.8CO3 and Ca0.2Na1.0K0.7CO3. In one embodiment, the molten electrolyte is selected from Ca0.27Na0.7K0.73CO3, Ca0.27Na0.70K0.75CO3 and Ca0.16N1.03K0.65CO3. In one embodiment, the molten electrolyte is Ca0.27Na0.7K0.73CO3. In a further embodiment, the molten electrolyte is Ca0.27Na0.70K0.75CO3. In a further embodiment, the molten electrolyte is Ca0.16Na1.03K0.65CO3.
Pure Li2O3 melts at 723° C., Na2CO3 melts at 851° C. and K2CO3 melts at 891° C. Therefore, mixtures of alkali carbonates can be advantageous due to lower melting points. For example Li0.7Na0.93CO3 has a melting point of 499° C. and Li0.85Na0.61K0.54CO3 and Li0.87Na0.63K0.50CO3 have a melting point of 393° C.
In a further embodiment, the rechargeable battery cell operates at temperature of between about 150° C. and about 500° C. For example, the molten electrolyte may comprise low melting point alkali metal hydroxides, alkali earth metal hydroxides, alkali earth metal hydroxide eutectics, alkali earth metal hydroxide eutectics, alkali metal carbonates, alkali earth metal carbonates, and any combination thereof. For example, pure NaOH, KOH and LiOH become molten electrolytes at approximately 320° C., 400° C. and 471° C., respectively. A mole percent mixture containing 49% KOH and 51% NaOII melts at approximately 173° C.; a mole percent mixture containing 71% NaOH and 29% LiOH melts at approximately 216° C., while a mole percent mixture containing 59% KOH and 31% LiOH melts at approximately 225° C. A mole percent mixture containing 91% NaOH and 9% Na2CO3 melts at approximately 295° C.; a mole percent mixture containing 90 mol % KOH and 10% K2CO3 melts at approximately 360° C.; and a mole percent mixture containing 80% LiOH and 20% Li2CO3 melts at approximately 415° C. A carbonate eutectic such as Li0.9Na0.6K0.5CO3 has a melting point of approximately 400° C. When this carbonate eutectic is mixed with 10 wt % of NaOH, NaNO3 or KCl, the resulting electrolyte melting point is about 388° C., 396° C. or 326° C., respectively. The rechargeable battery cells of the invention may comprise any of the molten electrolyte mixtures described herein. Thus, in one embodiment, the molten electrolyte comprises NaOH, LiOH, KOH, Na2CO3, K2CO3, Li2CO3, and any combination thereof, in any molar ratio. In one embodiment, the molten electrolyte comprises NaOH, LiOH, KOH, and any combination thereof, in any molar ratio. In another embodiment, the molten electrolyte comprises NaOH and Na2CO3 in any molar ratio. In another embodiment, the molten electrolyte comprises KOH and K2CO3 in any molar ratio. In another embodiment, the molten electrolyte comprises LiOH and Li2CO3 in any molar ratio.
In one embodiment, the molten electrolyte further comprises lithium oxide. Addition of lithium oxide (Li2O) to the molten carbonate electrolyte (i) increases cell potential and (ii) prevents molten carbonate decomposition favoring reactant rather products in the equilibrium
Li2CO3Li2O+O2
Lithiated iron oxide (e.g., lithiated Fe2O3 or Fe3O4) has dramatically increased solubility in molten carbonates compared to non-lithiated iron oxide, as well as the sodium and potassium equivalents of the lithiated iron oxide. The solubility of lithiated iron oxide in molten carbonates enables the use of molten carbonates as an electrolyte for the electrodeposition of iron. It is also contemplated that the lithium ions needed for the formation of the lithiated iron oxide may be provided by another lithium salt, such as lithium chloride, lithium sulphate and the like.
In another embodiment, the molten electrolyte comprises one or more of vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) and calcium oxide (CaO). In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) and calcium oxide (CaO) in a molar ratio of about 1:2:4:3. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) in a molar ratio of about 1:2:2. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) in a ratio of about molar 1:7:12. In one embodiment, the molten electrolyte comprises vanadium oxide (V2O5), boron oxide (B2O3), lithium oxide (Li2O) in a molar ratio of about 1:2:0.67. In another embodiment, the molten electrolyte comprises LiVO3 and LiBO2.
Any of the molten electrolytes described herein (e.g., molten carbonate electrolyte) may further comprise additional additives, e.g., sulphates, carbonates or oxides, such as, but not limited to, barium carbonate (BaCO3), cesium carbonate (Cs2CO3), calcium carbonate (CaCO3), magnesium oxide (Mg2O), calcium oxide (CaO), and any combination thereof. Additionally, any of the molten electrolytes described herein may also comprise an alkali metal nitrate (e.g., NaNO2) an alkali metal halide (e.g., KCl), or any combination thereof.
The electrolytic reactions described herein are typically conducted at a temperature greater than the melting point of the molten carbonate (or combination of carbonates) used as the electrolyte. In some embodiments, the temperature of the electrolytic reaction is 0 to 300 degrees greater than the melting point of the carbonate. Exemplary temperatures are 723 to 1000° C. when the molten carbonate is lithium carbonate.
In one embodiment, the melting point of the electrolyte, such as the carbonate electrolyte (i.e, the operating temperature of the rechargeable cell) is between about 395° C. and about 900° C., such as between about 600° C. and about 900° C., between about 720° C. and about 900° C. or between about 700° C. and about 800° C., for example, about 600° C., about 700° C., about 723° C., about 851° C. or about 891° C.
In another embodiment, the melting point of the electrolyte, such as the carbonate electrolyte (i.e, the operating temperature of the rechargeable cell) is between about 375° C. and about 900° C., such as between about 395° C. and about 600° C., for example, about 395° C., about 500° C. or about 600° C.
The Anode
As described herein, the term “anode” describes the air electrode (the electrode at which oxygen is released by electrochemical oxidation during the battery charging cycle). The anode can be made of any inert material which is stable under the operating conditions of the cell. Effective materials include metals, such as nickel, platinum or iridium, metal oxides such as nickel oxide, tin oxide and titanium oxide, metal alloys such as monel and inconel, and carbon based materials such as glassy carbon and graphite. Enhanced anode surface area, such as with screen or spongy materials, by physical roughening, by chemical or electrochemical etching, or as deposited on a conductive support, decreases electrolysis potential. Additionally, the anode may form part of a crucible, e.g., a nickel crucible. In one embodiment, the anode (air electrode) has a higher surface area than the cathode (thereby decreasing polarization).
In exemplary embodiments, the cells described herein comprise iron, carbon or VB2 as a high capacity discharge anode. In one embodiment, electrochemical storage in these iron, carbon or VB2 molten air batteries is in accord with the following equations:
Iron molten air battery (3e− discharge/charge):
Fe+¾O2½ Fe2O3 (1)
Carbon molten air battery (4e− discharge/charge):
C+O2CO2 (2)
VB2 molten air battery, (11e− discharge/charge):
VB2+1¼O2B2O3+½ V2O5 (3)
Table 1 shows the intrinsic energy storage capacity of the iron, carbon and VB2 molten air batteries described herein:
Volumetric energy capacity (Evol) is calculated from the number of electrons stored (n), the density (d), the Faraday constant (F=26.80 Ah mol−1) the formula weight (FW) and E° in accord with Eqs. 1, 2 or 3 as Evol=ndE°F/FW. The cell potential at unit activity, E°, is temperature dependent. For example, while constant over a wide temperature range at 1.0 V for the carbon anode, E° decreases for the iron anode from 1.2 to 0.9 V with temperature increase from 25° C. to 850° C. (see S. Licht et al., J. Phys. Chem. C, 113, 16283-16292, 2009).
As can be seen from Table 1, the intrinsic capacity of each battery is one to two orders of magnitude greater than that of the volumetric energy capacity of conventional Li ion batteries (6,200 Wh liter−1). Lithium (metal) air batteries also have a lower volumetric energy capacity. While lithium's gravimetric charge capacity (3860 Ah/kg) is similar to that of VB2 (4,060 Ah/kg), it has a lower 6,200 Wh liter−1 volumetric capacity due to a low density (0.534 kg liter−1), and single, rather than multiple, electron charge transfer.
The Cathode
As described herein, the term “cathode” describes the electrode at which the metal or non-metal is formed by electrochemical reduction during the battery charge cycle. The cathode can be made of any conductive material stable under the operating temperature of the cell. Effective materials include metals, such as steel, nickel, platinum or iridium. Enhancing the surface are of the cathode (for example, by using a screen or a spongy material, roughening the cathode surface, chemically or electrochemically etching the cathode surface, or depositing ion a conductive support) decreases the electrolysis potential. Additionally, the cathode may form part of a crucible, such as a steel crucible or a nickel crucible.
EXAMPLESThe present invention is now further illustrated by means of the following non-limiting examples.
Example 1 Iron Molten Air Rechargeable BatteryIron metal synthesis in molten carbonates is conducted via constant current electrolyses. As shown in the constant current electrolyses (left side) of
As evident in the left side of
The top row of
As seen in
The top row of
In
Carbon formation during molten carbonate electrolysis provides charging of the carbon molten air batteries described herein. Molten carbonate cells have been widely probed as robust fuel cells, and this, in combination with the reverse of this process (electrolysis for carbon capture) provide new opportunities for high capacity carbon molten air reversible battery storage.
As seen in the photos of
As calculated from the temperature dependence of the thermochemical enthalpy and entropy of the constituent (see e.g., Chase, J. Phys. Chem. Red. Data, 9, 1, 1998), molten carbonates can be highly stable at elevated temperatures. Increasing the temperature above 800° C. in molten Li2CO3 favors CO via the Boudouard reaction (equation 4). If not collected, this CO gas, instead of solid carbon product, leads to a parasitic charge loss for the carbon battery via the evolution of carbon monoxide gas.
2COC+CO2 (4)
An X-ray powder diffraction (XRPD) pattern of the post-electrolysis, black cathode product is shown in
A carbon molten air battery that exhibits improved energy efficiency is shown in
As seen in
The electrochemical discharge products of VB2, (B2O3 (mpt. 450° C., white, melts clear) and V2O5 (mpt. 690° C., yellow/brown)) have a low melting point compared to VB2 (mpt. 2450° C., black). Molten B2O3 and V2O5 salts are miscible, whereas the charged product, VB2, does not appear to be soluble in the molten B2O3/V2O5 mix. Due to its higher density, VB2 descends in the molten mixture. The B2O3/V2O5 molten phase is without significant ionic dissociation, and hence is an electrochemical insulator. Alone, the melt cannot be electrochemically charged. However, dissolution of an oxide such as Li2O into the B2O3/V2O5 melt provides adequate ionic conductivity for charging. The high temperature (molten) phase of the Li2O/B2O3/V2O5 system has not been previously explored, but the ionic conductivity range of this system in the solid phase at temperatures up to 250° C. has been established (see, e.g., Lee et al., Solid State Ionics, 175, 687, 2005). At higher temperature, the simpler, binary system of B2O3 (mpt. 450° C.) and Li2O (mpt. 1438° C., white, dissolves clear) presents a complex phase diagram with an extensive homogenous liquid phase above 767° C. (see, e.g., Passierb et al., Physica, 304, 463-476, 2001; Ferreira et al., J. Am. Ceram. Soc., 94, 3833, 2011).
The right side of
The experiments performed in this example detail various modifications to the physical chemistry components of the iron battery system that were performed in an attempt to increase the coulombic efficiency and minimize the requisite electrolysis potential of the iron molten air rechargeable battery.
Systematic Optimization of Electrolytic Iron Production in Molten Carbonate.
A systematic, variation of molten iron electrolysis can yield efficient iron production efficiency at low energy. General conditions of the first series of electrolyses are summarized in Table 2. The cathode in this first series of experiments was a thin planar 6.25 cm2 steel sheet. This cathode lies under the anode, and the iron product is deposited on top of the cathode. This cathode surface is the active area exposed to short ion diffusion path between the electrodes.
Table 3 summarizes the effect of electrode spacing and electrolyte mass on electrolysis (1 hour electrolyses at 1 A in an 800° C. molten lithium carbonate electrolyte containing 1.5 m Fe2O3 and 3 m Li2O (to generate 3 m LiFeO2 in solution). In this series of experiments the anode, a coiled pure nickel (McMaster 200 Ni) wire was situated 3 mm below the surface of the electrolyte to facilitate oxygen evolution in an attempt to minimize oxygen interaction with the cathode product.
In Table 3, the electrodes are delineated in Table 2. The electrolyte mass was changed as indicated below, to maintain electrolyte coverage in experiments with smaller or larger inter-electrode separations. Coulombic efficiency, particularly during the 0.25 cm separation electrolysis, may have been impacted by shorting as the iron deposit grew from the cathode towards the anode.
In the first series of experiments, summarized in Table 3, the anode to inter-electrode spacing was varied, and the mass of electrolyte was changed to cover smaller or larger inter-electrode separations. The electrodes before and after electrolysis are shown in
The lithium based electrolyte is highly conductive, and even at these relatively high current densities, electrolytic resistance losses are not significantly impacted by the variation of inter-electrode spacing. The electrolysis potentials at 1 A constant current are the same to within 0.1 V, independent of the 0.25 to 2.0 cm electrode separation. Coulombic efficiency, particularly during the 0.25 cm separation electrolysis may have been impacted by shorting as the iron deposit growing from the cathode approached the anode, and that a maximum of over 50% coulombic efficiency is achieved for an intermediate spacing of 1.0 cm.
Table 4 summarizes iron electrolyses experiments in which the starting concentration of Li2O was varied. The anode/cathode separation was 1.0 cm and the other electrolysis conditions were as given in Table 2. An intermediate Li2O concentration (2 molal) conducted for double the electrolysis time and generated greater iron metal product. In each case, the initial ferric concentration (as added Fe2O3) was maintained constant at 3 molal Fe3+ in Li2CO3. Fe2O3 is not soluble in carbonate unless Li2O is added, and reacts to form LiFeO2 in the molten solution. The Li2O is not consumed in the electrolysis process, as when LiFeO2 is reduced to form iron metal, Li2O is liberated to dissolve the next iteration of added iron ore (Fe2O3). As seen in the photo in
The next series of experiments utilizes the general conditions described in Table 3, at constant (1.0 A) current, but varies the electrolysis time. The anode/cathode separation was 1.0 cm As summarized in Table 5, whereas 1 hour of electrolysis should theoretically yield 0.7 g of iron (assuming 100% coulombic efficiency of the three electron reduction of dissolved Fe3+), 8 hours of electrolysis would be expected to generate 5.6 g of iron metal. As summarized in Table 5, the experimental coulombic efficiency during electrolysis is approximately 50 percent and is not substantially affected by the electrolysis time. What is affected, as shown in the photos in
Sodium carbonate (mpt. 851° C.) or potassium carbonate (mpt. 891° C.) both have higher melting points than lithium carbonate (mpt. 723° C.). However, a eutectic mix of the three carbonates, such as Li0.85Na0.61K0.54CO3, has melting point below 400° C., and provides an opportunity to explore iron electrolysis at lower temperatures. At these lower temperature conditions, the electrolysis potential would be expected to be considerably higher. The reaction of iron oxide to iron and oxygen is endothermic, with (i) an increase in rest potential with decrease in temperature. This will be exacerbated by (ii) a lower solubility of iron oxide in the eutectic at lower temperature and with lower lithium ion content, and (iii) higher overpotential due to the higher electrolyte resistance of a mixed alkali, compared to pure lithium, electrolyte. The general conditions of electrolysis are similar to those in Table 2. At the lower 500° C. temperature, only a lower concentration of iron oxide could be dissolved in the eutectic and the sustainable current at a reasonable electrolysis potential was only 0.4 A, rather than 1 A. Hence, the electrolysis time was increased from 1 to 2.5 hours to provide a constant total current during the experiment. As summarized in Table 6, even at the lower current, the lower temperature still requires a high (3.5 V) average electrolysis potential, and results in a poor coulombic efficiency. As seen in Table 6, by 750° C., the Li0.85Na0.61K0.54CO3 eutectic could readily accommodate the full 3 molal Fe3+ used in the pure lithium carbonate electrolyte at 800 C. It is evident that in the eutectic at 750° C., a higher electrolysis potential was needed to accommodate the same 1 A current used in the pure lithium electrolyte. Interestingly, coulombic efficiencies are high in both cases, and as seen in
Table 7 summarizes attempts to improve the coulombic efficiency of the planar iron foil cathode by increasing or decreasing its surface area. The electrolysis time, current, theoretical maximum mass of iron, and anode are as detailed in Table 2. The anode was a Ni coil, 16 cm length, 2.0 mm diameter, area 10 cm2, and the anode/cathode inter-electrode separation was 1 cm. The cathodes were as described in Table 7. As seen in
Table 8 summarizes attempts to modify the cathode configuration, which was accomplished by transitioning from a planar, to a coiled, steel cathode. The anode, with an anode/cathode separation of 1.0 cm, is detailed in Table 2. Cathodes are described in Table 8. Each electrolysis was at 1 A for 2 hours.
In the absence of silicate, the improvement in coulombic efficiency with the larger surface area coiled, rather than smaller surface area planar, cathode is more evident.
Table 9 summarizes the effect of Fe2O3 concentration on the electrolytic formation of iron. The anode is as detailed in Table 2, with an anode/cathode separation of 1.0 cm. Cathodes are described in the table. Results shown are for electrolyses each using a 10 cm2 coiled cathode, and with either 2, 3, 4 or 6 molal Fe3+, and Li2O in 800° C. molten lithium carbonate. The coulombic efficiency is high and comparable in the 3 and 4 molal electrolytes, with the 3 molal electrolyte) exhibiting a modestly higher efficiency of 70%. In the presence of 10% wt. silicate (SiO2), as seen in Table 10, and continuing with use of the preferred coiled cathode, the coulombic efficiency is somewhat higher in the 3, rather than 2 molal Fe3+, and higher when a 1:1 equivalent ratio, rather than a 2:1 equivalent ratio of Li2O is used. In all cases the presence of the silicate decreases the measured coulombic efficiency.
Table 11 summarizes the effect of temperature on iron electrolysis (1 A, 2 hour) in a pure lithium carbonate electrolyte (but containing silicate, and 3 molal Fe3+ and Li2O). The anode, detailed in Table 2, was separated from the cathode by 1.0 cm. While the electrolysis potential decreases with increasing temperature, the electrolysis efficiency is lowest (23%) at the highest electrolysis temperature (900° C.) and highest (58%) at the lowest electrolysis temperature (750° C.). The lower efficiencies, at higher temperature, may be associated with the greater reactivity and diffusivity of the oxygen produced at the anode, which can back react with iron to form a parasitic iron oxide loss.
Table 12 further probes the silicate effect on iron electrolysis (1 A, 2 hour, anode/cathode separation is 1.0 cm). Higher SiO2 contents (ranging from 10 to 30%—added as a percentage of the iron oxide mass to simulate an impurity in the iron ore), tends to decrease the average electrolysis potential, but also decreases the coulombic efficiency of iron production.
In the next series of experiments the anode stability was improved by raising the anode, from 3 mm below the electrolyte surface (a configuration used in all prior experiments), up to the surface of electrolyte. Prior to this surface anode configuration, anodes occasionally spontaneously broke during the course of the electrolysis. However the surface anodes appear to be fully stable, that is, there is no case of anode discontinuity occurring with the surface anodes in the next 30 experiments, independent of electrolysis conditions, and the anode always appeared to be unaffected by the electrolysis (no corrosion was evident).
In Table 13, two anode parameters were varied, the surface area, and whether the anode wire was loosely or tightly coiled, as illustrated in the photographs of
CO2 is disadvantageous to battery charging and discharging. Table 14 shows the effect of the gas above the electrolysis (1A, 2 hour) on the iron production, when the gas is changed from air, to carbon dioxide, or nitrogen. As can be seen from Table 14, pure CO2 significantly increases the iron charging potential to 1.95 V. A higher battery charging voltage is disadvantageous. Under the same conditions air (containing 21% oxygen and 78% nitrogen) or pure nitrogen lower the charging voltage to 1.71 V and 1.61 V, respectively. As can also be seen from Table 14, nitrogen significantly lowers the electrolysis potential and both nitrogen and carbon dioxide can improve the coulombic efficiency. Pure CO2 will be absorbed in the electrolyte according to the back reaction of the lithium carbonate decomposition/reformation equilibrium. Air contains (0.03%) CO2, and molten situated Li2CO3 below a blanket of air will be relatively stable, while pure N2, without CO2, will slowly decompose in accord with the equilibrium equation: Li2→CO3 CO2+Li2O. Nitrogen above the electrolysis is seen to decrease the electrolysis potential, and has only a marginal impact on coulombic efficiency. As also summarized in Table 14, additional Li2O added to the molten lithium carbonate electrolyte (above 3 molal) decreases coulombic efficiency, but sustains the electrolysis at a lower potential.
Iron molten air batteries, each containing a pure molten lithium carbonate electrolyte with a steel shim cathode and a nickel wire anode were discharged at 750° C., when the gas above the electrolyte contains only (i) a 2 to 1 volume flow ratio of pure CO2 to pure O2, (ii) a 1 to 10 ratio of CO2 to O2, or (iii) pure O2. In each case, the gas mixture is flowed above the battery to ensure that a constant gas composition is maintained throughout the example. In case (i), the flow rates of CO2 and O2 are 75 ml/min and 35.5 ml/min, respectively. In case (ii) the flow rates of CO2 and O2 are 10 ml/min and 100 ml/min, respectively. In case (iii), no CO2 is injected and the pure flow rate of O2 is 100 ml/min. In case (i), the battery discharge voltages at constant ohmic load are: V(1000Ω)=0.93 V, V(100Ω)=0.41 V, V(50Ω)=0.34 V, V(20Ω)=0.26 V, and V(10Ω)=0.18 V. In case (ii), the battery discharge voltages at constant ohmic load are: V(1000Ω)=1.14 V, V(100Ω)=0.54 V, V(50Ω)=0.40 V, V(20.0)=0.27 V and V(10Ω)=0.17V. In case (iii) the battery discharge voltages at constant ohmic load are: V(1000Ω)=1.16 V, V(100Ω)=1.02 V, V(50Ω)=0.76 V, V(20Ω)=0.43 V and V(10Ω)=0.22 V. The battery containing the highest CO2 content (case (i) has the lowest battery discharging voltage. A lower battery discharging voltage is disadvantageous.
Lowering the electrolysis temperature and decreasing the cathode current density can improve coulombic efficiency. As seen in Table 15, (for a 1A, 2 hour electrolytic formation of iron with coiled iron cathodes and an electrolyte of 3.0 m in Fe3+ and Li2O) the columbic efficiency is increased by over 20%, that is to ˜85%, by simultaneously decreasing the electrolysis temperature from 800° C. to 750° C., and/or by increasing the cathode surface area. This is not observed when the temperature is held constant and the cathode surface area is decreased to 7.5 cm2.
Tables 15-21 are presented in an abbreviated format. In each case, the electrolyte total mass is ˜33 g. In each case the electrolyte is 3.0 m in Fe3+ and Li2O without silicates. The coulombic efficiency also depends on when the electrode is removed from the electrolysis chamber (electrolysis time, Table 16) and the electrolysis current (Table 17). As seen in Table 16, removing the electrode after 1 hour negatively impacts the efficiency, although this effect presumably may be mitigated if iron oxide is fed into the electrolysis chamber as iron is produced.
As can be seen from Table 17, current density substantially effects the electrolysis with a maximum coulombic efficiency of 93% observed at 0.5 A, and as seen in
Table 19 shows the effect of the cathode location on the electrolytic formation of iron in molten 730° C. lithium carbonate, and includes even higher coulombic efficiency iron electrolysis configurations. The first column contains the same anode on the surface separated by 1 cm from a cathode near the bottom of the cell. As seen in the second column, the use of a smaller (half) diameter nickel or iron wire for the anode and cathode decreases, rather than increases, the coulombic efficiency. As can be seen from Table 19, at the lower temperature of 730° C. in molten lithium carbonate, an opposite, inverted electrode configuration (i.e., cathode above the anode) is not only functional, but can exhibit both improved coulombic efficiency and lower electrolysis potential. The coulombic efficiency of these inverted cells is at least 94 to 95% (and this may be considered a lower limit if any iron metal drops into the electrolyte during the cathode removal).
Photos of a vertical cathode inside the anode configuration are presented in
The iron electrode electrolysis data presented in Table 20 (vertical anode situated outside the cathode configuration in molten 730° C. Li2CO3 containing 3.0 m Fe3+ and Li2O) and Table 21 (vertical anode inside cathode configuration in molten 730° C. Li2CO3 with 3.0 m Fe3+ and Li2O) are each at 730° C. for 2 hours, but are conducted at 0.5 A, rather than 1.0 A, to probe a path to lower electrolysis potentials, while preserving, or further increasing the high coulombic efficiencies of iron production. Photographs of these electrodes with various surface areas of the inner, vertical cathode and outer anode coiled electrodes are shown in
In an attempt to further prevent any parasitic reaction of the anode and cathode products, the next configuration places an alumina tube between the outer (anode) and inner vertical, coiled electrodes. This configuration is shown in
Further increases in coulombic efficiency and decrease in the energy needed to drive the iron electrolysis may be achieved with relatively small changes to the cathode. As seen in Table 22, replacement of the vertical inner coiled wire cathode with a similar shaped, steel shim (foil) cathode increases the coulombic efficiency. Furthermore, an increase in anode surface area (40 cm2, compared to the 10 cm2 in the first column of Table 21), decreases the electrolysis potential to 1.4 V. Further increases in the cathode diameter of these shim electrodes, with or without a “bottom” on the cathode (as pictured in
The electrolysis configuration is simplified when the electrolysis is conducted in a nickel crucible which comprises both the anode and the cell body in one piece, and can further decrease the electrolysis potential. This configuration of the iron electrolyte cell is presented in
Alternative Carbonate Electrolytes
A more cost effective solution to the corrosivity of the sodium/potassium carbonate melt (other than the use of iridium which is stable as an air electrode during 5 hours of electrolysis in 750° C. Na0.23K0.77CO3, as compared to nickel air electrodes which corrode) may be found by the addition of calcium carbonate or barium salts to the sodium/potassium, lithium-free, carbonate melt. The addition of calcium carbonate can decrease the melting point of a carbonate mix. The sodium/lithium carbonate mix Li1.07Na0.93CO3, has a melting point of 499° C., but decreases to below 450° C. if 2 to 10 mol % equimolar CaCO3 and BaCO3 is added.
In addition to the sodium-potassium carbonate electrolytes, electrolyses were also conducted in calcium/sodium/potassium electrolytes ranging up to a calcium fraction of Ca0.27Na0.70K0.75. Electrodes used are shown in
Materials and Methods
Lithium carbonate (Li2CO3, Alfa Aesar, 99%), ferric oxide (Fe2O3, 99.4%, JT Baker), Li2O (Alfa, 99.5%), 1 mm and 2 mm Ni wire (Alfa, 99.5%), Ni foil (McMaster, pure Ni 200 shim), iron wire (Anchor, dark annealed), steel foil (McMaster, 75 μm 316 steel), crucibles: nickel (VWR AA35906-KY), high purity alumina (AdValue Technology AL-2100), silicon dioxide (SiO2, Spectrum, 325 mesh), lithium orthosilicate (Li4SiO4, Alfa Acasar, 99.9%, Pflatz & Bauer, 99%), boron oxide (B2O3, 99.98%, Alfa Aesar 89964), vanadium (V) oxide (V2O5, 99.6%, Alfa Aesar 89964), lithium vanadium oxide (LiVO3, 99.9%, Alfa Aesar 39358) and anhydrous lithium metaborate (LiBO2, 99.9%, Alfa Aesar 12591).
Electrolyses
Electrolysis conditions and the systematic variation of the electrolysis cell components are described in Example 4. The theoretical maximum mass of iron that can be produced from the ferric salt during the electrolysis is calculated as electrolysis current (A)×electrolysis time (s)×atomic weight Fe/(3 e−×96,485 As).
Analysis
Iron metal is produced by electrolysis in molten carbonate at the cathode. The cathode product was analyzed for iron metal content based on, and improved from the method of Xu et al. (J. Min. Mat. Characterization & Eng., 2, 65, 2003) in which iron metal replaces copper sulfate, and the ferrous sulfate product is analyzed. The procedure was further modified by (i) washing the electrolysis product with deionized water, and (ii) replacement of the previous UV/Vis evaluation, which was used at the end of the procedure, with a more quantitative (less prone to colorimetric interference) titration by dichromate. The initial rinse removes Li2CO3 and Li2O to prevent reaction of Fe0 to form Fe(OH)2 or Fe(OH)3.
In addition to the relative valence state composition of iron, the mass percent of total iron in the sample (including the solidified electrolyte) is shown in the Fetotal of column in Table 2, and the last two columns are measured water soluble and water insoluble mass percent of each sample. The washed, dried insoluble component consists primarily of iron (iron metal and iron oxides). The iron analysis of weighed samples from each layer yields the concentrations: [Fetotal], [Fe°], [Fe2+] and [Fe3+] (the latter concentration is determined from the difference of [Fetotal]−[Fe°]−[Fe2+]). A separate, weighed sample from each layer is washed, followed by subtraction of the mass of the dried insoluble (filtered, dried) component. This yields the mass of the remaining soluble components. The water soluble salts components consist of Li2CO3 and Li2O. The Li2O dissolves as LiOII, including Li2O stripped from lithiated iron oxides when brought in contact with the wash water (e.g. LiFeO2+H2O liberates soluble LiOH), and the 105° C. dried components are weighed as the insoluble salts).
Analysis Procedure for Iron Metal
1) The cathode product is ground in a mortar and pestle until it can be sifted and dispersed through a 70 mesh (212 μm) sieve.
2) The ground product is washed with deionized water, then extracted by suction filtration and the precipitate is rinsed with deionized water until the pH is near 7. The precipitates, residue and filter paper are collected to react with CuSO4.
3) 50 ml of 0.5 M CuSO4 is added to 0.5 g of the ground product to form:
Fe+CuSO4→FeSO4+Cu (5)
4) After boiling this stirred solution for 1 hour, it is immediately filtered (to prevent the reaction of O2 with Fe2+) with a GF/A (Whatman glass microfiber) filter paper into a 250 ml volumetric flask, and the filter paper is washed with double deionized (18 MΩ) water also into the flask, and diluted to 250 ml.
5) 25 ml of the 250 ml filtrate is sampled by pipette into a 250 ml Erlenmeyer flask, and the following solutions are added to the flask: 20 ml of “A”, 20 ml of “B”, 50 ml of water, and 3 drops of indicator solution “C”, where
A: a mix of 50 ml of water with 10 ml concentrated H2SO4
B: 700 ml of water with 150 ml concentrated H2SO4, 150 ml H3PO4 (binds colored Fe3+, which is colored, as colorless Fe(HPO4)2−, to improve clarity of the endpoint)
C: an indicator solution consisting of 0.2% aqueous diphenylamine 4-sulfonic acid sodium salt
D: a titrant consisting of 0.004167 M (6×dilution of 0.025 M) K2Cr2O7 which tritrates as 1 equivalent K2Cr2O7per FeSO4; each ml of solution D=1.3962 mg of Fe° metal.
6FeSO4+K2Cr2O7+H2SO4→3 Fe2(SO4)3+K2SO4+Cr2(SO4)3+7H2O (6)
The endpoint is observed as a color change from light blue (initial) to the endpoint's purple.
This titration analysis is also confirmed by weighing the mass of magnetically removed iron product that was washed & dried to remove oxide. The reliability of the analysis during the titration is improved when solutions are stirred slowly in step 2, rather than rapidly, to prevent significant errors (underestimating the Fe° content of the product with increasing speed of stirring) due to the introduction of oxygen, which can convert ferrous to ferric prior to the titration. The need to switch to a lower stirring speed for the Fe° analysis was discovered and applied to the latter half of the experiments in this study. Under this latter condition replicate analyses of Fe° metal mass from are reproducible to within ±2%.
Analysis Procedure for Total Fe
In accord with the method of Shi et al. (Rock and Mineral Analysis, 28, 197, 2009), a 0.1 g sample was placed in a 250 ml flask and 20 ml of 1:1 diluted HCl was added. The sample was placed on a mixer hot plate at about 90° C. (to prevent volatile loss of FeCl3 at higher temperature) until completely dissolved. 20 ml water was added under N2 (99.999%). Aluminum powder was added in three 0.1 g portions (in large excess of the theoretical amount to reduce Fe3+ to Fe2+). With a minimum of stirring, the Al quickly reacts with Fe3+ and H+ to form Al3+, and Fe3+ is reduced to Fe2+. A color change from yellow to light yellow was observed until the solution was transparent. The analysis occurs in accord with the following equations:
Al+Fe3+→Al3++Fe (7)
Fe+2H+→Fe2++H2 (8)
100 ml of H2O was added and the solution was cooled to room temperature. 20 ml of sulfuric-phosphoric acid solution and 5 drops of the diphenylamine indicator were added after which the solution was titrated with a standard K2Cr2O7 solution (0.0250 mol ⅙ K2Cr2O7/L).
Total Fe (%)=(V×N×FW Fe)/(1000/S)
V standard K2Cr2O7 solution volume (ml)
N standard K2Cr2O7 solution concentration (mol/L)
FW Fe 55.85 g/mol
S specimen weight (g)
Analysis Procedure for Fe2+
This procedure is based on the methods disclosed in Shi et al., Rock and Mineral Analysis, 28, 197, 2009), as modified by (i) ASTM Designation: D8372-86, Standard Test Method for Ferrous lion in lion Oxides, Annual Book of ASTM Standards, 1, 1999; and (ii) Xu et al., J. Min. Mat. Characterization & Eng., 2, 65, 2003.
In this analysis, 0.5 g of the sample to be analyzed was added to a 250 ml flask and 20 ml of 1:1 diluted HCl was added. This solution was mixed on a hot plate under 99.999% N2 at 90° C. until completely dissolved. 100 ml H2O was added and the solution was allowed to cool to room temperature. 20 ml sulfuric-phosphoric acid solution (prepared by adding 600 ml concentrated H2SO4 to 800 ml stirred DI water, then adding 600 ml of 86% phosphoric acid) and 5 drops of the diphenylamine indicator were added and titrated with a standard K2Cr2O7 solution (0.0250 mol ⅙ K2Cr2O7/L) to a sharp endpoint color change from green to purple.
Fe2+(%)=(V×N×FW Fe)/(1000/S)
V standard K2Cr2O7 solution volume (ml)
N standard K2Cr2O7 solution concentration (mol/L)
FW Fe 55.85 g/mol
S specimen weight (g)
The analysis procedure for Fe3+ is the straightforward difference from the known total iron, the sum of the iron metal and ferrous species as: Fe3+(%)=Total Fe(%)−Fe0(%)−Fe2+(%)
Analysis Procedure for the Aqueous Soluble Components
Filters were dried in an oven at 105° C. for 1 hour, then cooled in a desiccator and weighed. After weighing, samples (˜0.3 g) to be analyzed were stirred one hour in 100 ml of DI water (18 MΩ) in a 250 ml flask at room temperature, then filtered using suction. The filtrate was washed on the filter with three 20 mL volumes of DI water. The filter was then transferred onto a glass weighing dish, and dried at 105° C. for a minimum of 1 hour until a minimum mass was measured (after cooling to room temperature in the desiccator).
Water soluble substances (wt %)=(A−B)×100/A
A Specimen weight (g)
B Residue on the filter paper weight (g).
Although the invention herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the present invention. It is therefore to be understood that numerous modifications may be made to the illustrative embodiments and that other arrangements may be devised without departing from the spirit and scope of the present invention as described above. It is intended that the appended claims define the scope of the invention and that methods and structures within the scope of these claims and their equivalents be covered thereby.
All publications, patents and patent applications cited in this application are herein incorporated by reference to the same extent as if each individual publication, patent or patent application was specifically and individually indicated to be incorporated herein by reference.
Claims
1-41. (canceled)
42. A rechargeable battery cell comprising: wherein at the air electrode, the principal reaction is oxygen (O2) being reduced during discharge, the principal reaction is not carbon dioxide (CO2) and oxygen (O2) being reduced to form carbonate (CO32−) during discharge, and wherein the molten electrolyte comprises one or more metal carbonates, wherein external carbon dioxide (CO2) is not required for discharge at the air electrode.
- a. a rechargeable air electrode;
- b. a rechargeable metal electrode that is capable of being oxidized; and
- c. a molten electrolyte disposed between the air electrode and the metal electrode;
43. A rechargeable battery cell comprising: wherein at the air electrode, the principal reaction is oxygen (O2) being reduced during discharge, the principal reaction is not carbon dioxide (CO2) and oxygen (O2) being reduced to form carbonate (CO32−) during discharge, and wherein the molten electrolyte comprises vanadium oxide (V205), boron oxide (B2O3), lithium oxide (LiO2) and calcium oxide (CaO).
- a. a rechargeable air electrode;
- b. a rechargeable metal electrode that is capable of being oxidized; and
- c. a molten electrolyte disposed between the air electrode and the metal electrode;
44. The rechargeable battery cell according to claim 42, wherein the melting point of the molten electrolyte is (i) between about 395° C. and about 900° C. (ii) between about 600° C. and about 900° C., (iii) between about 600° C. and about 900° C., (iv) between about 720° C. and about 900° C., (v) between about 700° C. and about 800° C., or (vi) between about 150° C. and about 500° C.
45. The rechargeable battery cell according to claim 43, wherein the melting point of the molten electrolyte is (i) between about 395° C. and about 900° C. (ii) between about 600° C. and about 900° C., (iii) between about 600° C. and about 900° C., (iv) between about 720° C. and about 900° C., (v) between about 700° C. and about 800° C., or (vi) between about 150° C. and about 500° C.
46. The rechargeable battery cell according to claim 42, wherein the melting point of the molten electrolyte is about 395° C., about 500° C., about 600° C., about 700° C., or about 723° C.
47. The rechargeable battery cell according to claim 43, wherein the melting point of the molten electrolyte is about 395° C., about 500° C., about 600° C., about 700° C., or about 723° C.
48. The rechargeable battery cell according to claim 42, wherein the melting point of the molten electrolyte is between about 395° C. and about 600° C.
49. The rechargeable battery cell according to claim 43, wherein the melting point of the molten electrolyte is between about 395° C. and about 600° C.
50. The rechargeable battery cell according to claim 42, wherein the cell operates at a temperature between about 395° C. and about 600° C.
51. The rechargeable battery cell according to claim 43, wherein the cell operates at a temperature between about 395° C. and about 600° C.
52. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates are selected from lithium carbonate, sodium carbonate, potassium carbonate, strontium carbonate, rubidium carbonate, cesium carbonate, barium carbonate, calcium carbonate, or any combination thereof.
53. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates are selected from lithium carbonate, sodium carbonate, potassium carbonate, or any combination thereof.
54. The rechargeable battery cell according claim 42, wherein the one or more metal carbonates comprises lithium carbonate.
55. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates comprise a binary mixture of lithium carbonate, potassium carbonate or sodium carbonate.
56. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates is Li0.7Na0.9CO3.
57. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates comprises lithium carbonate, sodium carbonate and potassium carbonate.
58. The rechargeable battery cell according to claim 57, wherein the one or more metal carbonates is Li0.9Na0.6K0.5CO3.
59. The rechargeable battery cell according to claim 42, wherein the one or more metal carbonates comprises CaCO3, Na2CO3, K2CO3, or any combination thereof.
60. The rechargeable battery cell according to claim 59, wherein the one or more metal carbonates are selected from Ca0.3Na0.7K0.7CO3, Ca0.3Na0.7K0.8CO3 or Ca0.2Na1.0K0.7CO3.
61. The rechargeable battery cell according to claim 42, wherein the molten electrolyte further comprises one or more alkali metal hydroxides, alkali earth metal hydroxides, alkali metal hydroxide eutectics, alkali earth metal hydroxide eutectics, or any combination thereof.
62. The rechargeable battery cell according to claim 43, wherein the molten electrolyte further comprises one or more alkali metal hydroxides, alkali earth metal hydroxides, alkali metal hydroxide eutectics, alkali earth metal hydroxide eutectics, or any combination thereof.
63. The rechargeable battery cell according to claim 61, wherein the molten electrolyte further comprises NaOH, LiOH, KOH, Na2CO3, Li2CO3, K2CO3, or any combination thereof.
64. The rechargeable battery cell according to claim 62, wherein the molten electrolyte further comprises NaOH, LiOH, KOH, Na2CO3, Li2CO3, K2CO3, or any combination thereof.
65. The rechargeable battery cell according to claim 61, wherein the cell operates at a temperature between about 150° C. and about 500° C.
66. The rechargeable battery cell according to claim 62, wherein the cell operates at a temperature between about 150° C. and about 500° C.
67. The rechargeable battery cell according to claim 42, wherein the molten electrolyte further comprises a molten nonconductive salt and an inorganic salt that is conductive when dissolved.
68. The rechargeable battery cell according to claim 43, wherein the molten electrolyte further comprises a molten nonconductive salt and an inorganic salt that is conductive when dissolved.
69. The rechargeable battery cell according to claim 67, wherein the conductive when dissolved inorganic salt is selected from metal oxides, metal halides, metal sulfates, metal nitrates, metal halates, or any combination thereof.
70. The rechargeable battery cell according to claim 68, wherein the conductive when dissolved inorganic salt is selected from metal oxides, metal halides, metal sulfates, metal nitrates, metal halates, or any combination thereof.
71. The rechargeable battery cell according to claim 67, wherein the conductive when dissolved inorganic salt is selected from alkali metal oxides, alkali earth metal oxides, alkali metal halides, alkali earth metal halides, alkali metal sulfates, alkali earth metal sulfates, alkali metal nitrates, alkali earth metal nitrates, alkali metal halates, alkali earth metal halates, or any combination thereof.
72. The rechargeable battery cell according to claim 68, wherein the conductive when dissolved inorganic salt is selected from alkali metal oxides, alkali earth metal oxides, alkali metal halides, alkali earth metal halides, alkali metal sulfates, alkali earth metal sulfates, alkali metal nitrates, alkali earth metal nitrates, alkali metal halates, alkali earth metal halates, or any combination thereof.
73. The rechargeable battery cell according to claim 42, wherein the molten electrolyte further comprises lithium oxide, magnesium oxide, calcium oxide, or any combination thereof.
74. The rechargeable battery cell according to claim 42, wherein the chemistry of the cell can be expressed by equation (1):
- C+O2CO2 (1).
75. The rechargeable battery cell according to claim 43, wherein the chemistry of the cell can be expressed by equation (1):
- C+O2CO2 (1).
76. The rechargeable battery cell according to claim 42, wherein the metal electrode is selected from iron, zinc, aluminum, magnesium, bismuth, vanadium, manganese, nickel, silver, barium, calcium, strontium, lead, mercury, cadmium, chromium, tin, titanium or any combination thereof.
77. The rechargeable battery cell according to claim 43, wherein the metal electrode is selected from iron, zinc, aluminum, magnesium, bismuth, vanadium, manganese, nickel, silver, barium, calcium, strontium, lead, mercury, cadmium, chromium, tin, titanium or any combination thereof.
78. The rechargeable battery cell according to claim 43, wherein the vanadium oxide (V205), boron oxide (B2O3), lithium oxide (LiO2) and calcium oxide (CaO) are in a molar ratio of about 1:2:4:3, about 1:2:2:0, about 1:7:12:0 or about 1:2:0.67:0.
79. An electrical energy storage product comprising a rechargeable battery cell according to claim 42.
80. An electrical energy storage product comprising a rechargeable battery cell according to claim 43.
81. A bank of cells comprising a plurality of rechargeable battery cells according to claim 42.
82. A bank of cells comprising a plurality of rechargeable battery cells according to claim 43.
83. A rechargeable energy storage device incorporating the rechargeable battery cell according to claim 42.
84. A rechargeable energy storage device incorporating the rechargeable battery cell according to claim 43.
85. A method of cyclically storing and releasing energy comprising cyclically charging and discharging a rechargeable battery cell according to claim 42.
86. A method of cyclically storing and releasing energy comprising cyclically charging and discharging a rechargeable battery cell according to claim 43.
Type: Application
Filed: Jan 9, 2020
Publication Date: May 20, 2021
Patent Grant number: 11094980
Inventor: Stuart Licht (Leesburg, VA)
Application Number: 16/738,745