Dual wire welding system and method

A system and method of welding is provided where at least two welding electrodes are provided to and passed through a single orifice on a single contact tip and a welding waveform is provided to the electrodes through the contact tip to weld simultaneously with both electrodes.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description

Notice: More than one reissue application has been filed for the reissue of U.S. Pat. No. 9,839,970. The reissue applications are U.S. application Ser. No. 16/707,701, filed Dec. 9, 2019 (the present application), U.S. application Ser. No. 16/707,659, filed Dec. 9, 2019, and U.S. application Ser. No. 16/707,685, filed Dec. 9, 2019, all of which are reissues of U.S. Pat. No. 9,839,970.

BACKGROUND OF THE INVENTION

Field of the Invention

Devices, systems, and methods consistent with the invention relate to welding with a dual wire configuration using a single contact tip.

Description of the Related Art

When welding, it is often desirable to increase the width of the weld bead or increase the length of the weld puddle during welding. There can be many different reasons for this desire, which are well known in the welding industry. For example, it may be desirable to elongate the weld puddle to keep the weld and filler metals molten for a longer period of time so as to reduce porosity. That is, if the weld puddle is molten for a longer period of time there is more time for harmful gases to escape the weld bead before the bead solidifies. Further, it may desirable to increase the width of a weld bead so as to cover wider weld gap or to increase a wire deposition rate. In both cases, it is common to use an increased electrode diameter. The increased diameter will result in both an elongated and widen weld puddle, even though it may be only desired to increase the width or the length of the weld puddle, but not both. However, this is not without its disadvantages. Specifically, because a larger electrode is employed more energy is needed in the welding arc to facilitate proper welding. This increase in energy causes an increase in heat input into the weld and will result in the use of more energy in the welding operation, because of the larger diameter of the electrode used.

BRIEF SUMMARY OF THE INVENTION

An exemplary embodiment of the present invention is a welding system and method for welding where a welding power supply provides a welding waveform to a contact tip having an exit orifice. A wire feeding mechanism provides at least two welding electrodes having a circular cross-section to a channel in the contact tip, where each of the electrodes passes through the channel in a longitudinal orientation and exits the contact tip through the same exit orifice. The welding waveform is provided to each of the electrodes by the contact tip for a welding operation.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and/or other aspects of the invention will be more apparent by describing in detail exemplary embodiments of the invention with reference to the accompanying drawings, in which:

FIG. 1 illustrates a diagrammatical representation of an exemplary embodiment of the present invention;

FIG. 2 illustrates a diagrammatical representation of another exemplary embodiment of the present invention;

FIG. 3 illustrates a diagrammatical representation of a further exemplary embodiment of the present invention;

FIGS. 4A to 4C illustrate diagrammatical representations of various exemplary embodiments of the present invention; and

FIG. 5 5A illustrates a diagrammatical representation of an exemplary embodiment of a welding system of the present invention;

FIG. 5B illustrates a diagrammatical representation of known prior art rollers each having a single operable groove and designed for a single wire feeding operation in a single wire feeding operation; and

FIG. 5C illustrates a diagrammatical representation of the rollers of FIG. 5B used in an operation for feeding two wires in a dual wire configuration.

 DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS

Exemplary embodiments of the invention will now be described below by reference to the attached Figures. The described exemplary embodiments are intended to assist the understanding of the invention, and are not intended to limit the scope of the invention in any way. Like reference numerals refer to like elements throughout.

FIG. 1 is a representative diagrammatical representation of an exemplary embodiment of the present invention. Specifically, a contact tip 101 is shown having two welding electrodes E passing through the same orifice 103 in the tip 101. Typically, in welding with a contact tip 101 a single electrode E is passed through the orifice 103. However, in the present invention at least two electrodes E are passed through the same orifice 103 in a single tip 101.

In FIG. 1, the electrodes E are shown in a tandem configuration. That is, the electrodes E are positioned in the orifice 103 in a front-to-back configuration related to the direction of travel of the contact tip 101 during welding. This tandem electrode configuration provides an elongated weld puddle WP, but does not increase the width of the weld puddle. FIG. 2 similarly shows an exemplary embodiment of the present invention in which the electrodes E are shown in a side-by-side configuration coming out of the same orifice 103 of the same contact tip 101. In using a side-by-side configuration a wider weld puddle WP can be produced when desired.

By employing embodiments of the present invention, an increase increased weld puddle width or length is achieved without the undesired increase in heat input associated with employing a larger diameter single electrode, as is traditionally done. For example, it may be desirable to have a weld puddle WP width which is consistent with the use of an electrode having a width of 0.0625 inch. Traditionally, a single electrode having a 0.0625 inch diameter would be employed, requiring the energy input necessary to properly weld with an electrode of this size. However, in an exemplary embodiment of the present invention, two electrodes E having a diameter of 0.030 inch each can be employed in a side-by-side configuration to achieve the same weld puddle width. However, rather than requiring the energy input needed to weld with a 0.0625 inch diameter wire, this embodiment of the present invention will only require the energy input necessary for welding with a 0.045 inch diameter wire. This is because, although the width of the weld puddle achieved is similar to that of a 0.0625 inch diameter electrode, the overall cross-sectional area of the combined 0.030 inch diameter electrodes is similar to that of a single 0.045 inch diameter electrode. Thus, only the energy needed to weld with a 0.045 inch diameter electrode need be utilized while a width consistent with a 0.0625 inch diameter electrode is achieved. Similarly, in the example discussed above a welding waveform designed for only a 0.045 inch diameter electrode can be utilized. It is not necessary to employ a welding waveform for a 0.0625 inch diameter electrode.

Furthermore, in an exemplary embodiment of the present invention, a standard sized contact tip can be utilized. For example, in the above discussed example, a standard 0.052 inch diameter orifice contact tip 101 can be utilized. Typically, the actual orifice diameter of a standard 0.052 inch diameter orifice contact tip is about 0.060 inches. Because of this, two 0.030 inch diameter electrodes E can be passed through the single orifice 103 easily. Of course, the present invention is not limited to the example set forth above, which is merely intended to be exemplary to aid in the understanding of the present invention.

In various embodiments of the contact tip 101 the orifice 103 has a diameter sufficient to transfer the welding waveform into each of the electrodes E.

Further, in exemplary embodiments of the present invention the contact tip 101 utilized can be a straight bore type tip. However, in further exemplary embodiments of the present invention, the contact tip can be of a gooseneck type. This is depicted in FIG. 3, in which the contact tip 201 is bent at an angle. In this embodiment the electrode channel 205 is also bent as shown in FIG. 3. In exemplary embodiments of the present invention, the channel 205 is configured to orient the electrodes E relative to each other, as desired. For example, in the embodiment shown the downward angling of the channel 205 in the tip 201 causes the electrodes E to align in a side-by-side orientation when the electrodes E exit the orifice 203. Thus, it is contemplated that the angling and/or cross-section of the channel 205 in the tip 201 can be configured to orient the electrodes E as desired for a particular welding operation.

In another exemplary embodiment, rather than the tip being bent, a standard “gooseneck” type welding gun can be used. In such welding guns, the gun itself has some bent portions through which the electrode travels prior to engaging with the tip, in which the tip can be a standard straight contact tip. In exemplary embodiments of the present invention, such a welding gun is employed such that the electrodes E align themselves appropriately within the bends of the welding gun. In fact, it has been discovered that standard “gooseneck” type welding guns can be used with embodiments of the present invention, such that as the electrodes E pass through the welding gun the electrodes E become aligned in a side-by-side configuration and exit the tip in a side-by-side configuration. Thus, for example, the image of the tip 201 shown in FIG. 3 could be a welding gun tube to which a tip is coupled, rather than a bent torch tip (this is diagrammatically depicted in FIG. 5 discussed below). In fact, in various exemplary embodiments of the present invention, the bend in the torch tube or the torch tip 201 can be as high as 60 degrees. Because the structure and construction of welding guns having a bend are well known in the welding industry they will not be described in detail herein.

Within the channel 205 the electrodes E are positioned adjacent to each other, such that the electrodes are longitudinal to each other throughout the length of the channel 205. The electrodes E may change positioning in the channel E as the electrodes E pass through the channel 205 (that is they may move from side-to-side to on top of each other), but the electrodes E remain longitudinal to each other throughout the length of the channel 205. That is, the electrodes E do not intertwine or twist with each other.

It is known that some electrodes E are manufacturing manufactured having a cast. It is also known, in single electrode operations, that the shape/curvature of the channel 205 (such as in a gooseneck shaped contact tip 101) can orient the cast in the electrode E with the channel 205. Similarly, embodiments of the present invention employ the shape of the channel 205 to aid in orienting the electrode E in conjunction with the cast of the electrode E.

FIGS. 4A-4C depict various orifice configurations for exemplary embodiments of the present invention. As shown in FIG. 4A a circular orifice 303A is employed in the contact tip 301A. The tip 301A can be of a straight or gooseneck type tip. Further, in this embodiment the tip channel (not shown) internal to the tip 301A can have a constant cross-section with the orifice 303A. However, in further exemplary embodiments, the channel can have a cross-section which is different from the orifice 303A so as to orient the electrodes E within the channel before the electrodes E exit the orifice 303A. In a further exemplary embodiment, as shown in FIG. 4B the orifice 303B has a horizontally oriented orifice with an elliptical shape to orient the electrodes in a side-by-side orientation. Similarly, in FIG. 4C the orifice 303C has an elliptical shape which is oriented vertically so that the electrodes E are oriented in a front-to-back orientation.

As with the embodiment in FIG. 4A, in the embodiments shown in FIGS. 4B and 4C, some exemplary embodiments the channel (not shown) in the tip 301B/C has the same cross-section as the orifice 303B/C, while in other embodiments the cross-section of the channel can vary from the orifice 303B/C. For example, it is contemplated while the orifice 303B/C has an elliptical shape; the channel has a circular cross-section. Thus, the shaping of the orifice and/or the tip channel can be configured to orient the electrodes as desired during a welding operation. Additionally, it is noted that the present invention is not limited to either a circular or elliptical shape orifice 303A/B/C as shown in FIGS. 4A-C, but other shapes, such as oval may be used. The present invention is not limited in this regard so long as the desired electrode orientation is achieved during welding.

Further, in exemplary embodiments of the present invention, the contact tip 301B/C is of a design that can be rotated so as to be oriented in at least two positions within a welding gun or welding torch, such that the same contact tip 301B/C can be used to orient the electrodes E in a side-by-side or tandem configuration. In this embodiment, it is not necessary to use two different contact tips for two different welding operations, but rather the change in the orientation of the tip in the torch or gun. Thus, for example, during a welding operation if a turn is to be made it is not necessary to change to the tip or the orientation of the welding torch, just the tip.

In an exemplary embodiment of the present invention a drive mechanism is employed to orient the tip 301B/C within the welding gun. In such an embodiment, the drive mechanism, such as a motor or other means, can turn the tip 301N/C 301B/C as desired to achieve the desired orientation (e.g., FIG. 4B shows the tip 301B rotatable to horizontally orient the electrodes E and FIG. 4C shows the tip 301C rotatable to vertically orient the electrodes E). This can be controlled by an operator or via a computer system, such as in robotic welding operations. Thus, during welding an operator can control manually or automatically the orientation of the tip 301B/C to achieve the desired weld puddle during welding. This control can be achieved remotely, such as at the control center of a welding station or can be controlled at the welding torch. The present invention is not limited in this regard.

Turning now to FIG. 5 an exemplary embodiment of a welding system 400 in accordance with an exemplary embodiment of the present invention is depicted. The welding system 400 contains a welding power source 409 which is coupled to both a welding torch 411 (having a contact tip—not shown) and a wire feeder 405. The torch 411 can be coupled to any known or used welding gun or torch and can be of a straight or gooseneck type as described above. The wire feeder 405 draws the electrodes E1 and E2 from electrode sources 401 and 403, respectively, which can be of any known type, such as reels, spools, containers or the like. The wire feeder 405 is of a known construction and employs feed rolls 407 to draw the electrodes E1 and E2 and push the electrodes to the torch 411. In the illustrated embodiment, the wire feeder 405 includes one pair of feed rolls 407. In an exemplary embodiment of the present invention, the feed rolls 407 and wire feeder 405 are configured for a single electrode operation. It has been discovered that embodiments of the present invention, using a dual wire configuration, can be utilized with a wire feeder 405 and rollers 407 only designed for a single wire feeding operation, such as rollers having only one operable groove for retaining and feeding the single wire. For example, rollers 407 can be configured for a single 0.045 inch diameter electrode, but will be suitable to drive two electrodes of a 0.030 inch diameter without modification to the wire feeder 405 or the rollers 407.

Once driven by the rollers 407, the electrodes E1 and E2 are passed through a liner 413 to deliver the electrodes E1 and E2 to the torch 411. The liner 413 is appropriately sized to allow for the passage of the electrodes E1 and E2 to the torch 411. For example, for two 0.030 inch diameter electrodes, a standard 0.0625 inch diameter liner 413 (which is typically used for a single 0.0625 inch diameter electrode) can be used with no modification.

Although the examples referenced above discuss the use of two electrodes having a same diameter, the present invention is not limited in this regard as embodiments can use electrodes of a different diameter. That is, embodiments of the present invention can use an electrode of a first, larger, diameter and an electrode of a second, smaller, diameter. In such an embodiment, it is possible to more conveniently weld two work pieces of different thicknesses. For example, the larger electrode can be oriented to the larger work piece while the smaller electrode can be oriented to the smaller work piece. Further, embodiments of the present invention can be used for many different types of welding operations including, but not limited to, metal inert gas, submerged arc, and flux-cored welding. Further, embodiments of the present invention can be used for automatic, robotic and semi-automatic welding operations. Additionally, embodiments of the present invention can be utilized with different electrode types. For example, it is contemplated that a cored electrode can be coupled with a non-cored electrode. Thus, embodiments of the present invention can be utilized a broad spectrum of welding operations.

A method of employing an exemplary embodiment of the present invention will now be discussed. Based on a welding operation to be performed electrodes E1 and E2 are selected and an electrode orientation for the welding operation is determined. If it is desired that a longer welding puddle is needed to eliminate porosity, for example for welding galvanized steel, then the appropriate welding torch 411 and contact tip is selected. Alternatively, if it is desired that side-by-side welding is needed, for example for welding sheet metal, then the torch 411 and/or a tip is selected appropriately.

During operation, the wire feeder 405 provides the electrodes E1 and E2 to the torch 411. The power supply 409 provides the desired welding waveform to the torch 411 for the welding operation. Embodiments of the present invention can be utilized with many different types of welding waveforms. For example, embodiments of the present invention can be utilized with pulse welding, short arc welding, surface tension transfer welding, as well as many other types of welding waveform profiles.

During welding, a standard stick-out distance can be utilized. For example, a stick-out of ¾ to 1 inch can be used. As discussed above, the power supply supplies a welding waveform suitable for welding the collective cross-sectional area of the electrodes E1 and E2. For example, if welding with two 0.030 inch diameter electrodes E1 and E2 a welding waveform having sufficient energy or welding current for welding with a single 0.045 inch diameter electrode can be utilized to provide a suitable weld. It is noted that although the cross-sectional area of two 0.030 inch diameter electrodes is not mathematically identical to that of a single 0.045 inch diameter electrode, for purposes of the present invention the relative cross-sectional areas are substantially the same. Surprisingly, it has been discovered that the use of a welding waveform designed for a single 0.045 inch diameter electrode (for example) can be utilized with two 0.030 inch diameter electrodes, requiring no change to the waveform (such as current, etc.) and results in a stable welding operation with the benefits stated above. This avoids the drawbacks of increased heat input that would result from welding with an electrode having a total cross-section larger than needed. That is, the present invention allows for a weld puddle/bead to be increased in size (for example having a width of 0.060 inches) while the total heat input into the weld is that which would normally come from the use of a smaller electrode (for example and electrode having a diameter of 0.045 inches). Of course, the present invention is not limited to the above electrode size examples, which are merely provided as examples to demonstrate the benefits and versatility of the present invention.

This reduction in overall heat input is highly advantageous in many respects. For example, with exemplary embodiments of the present invention it is possible to deposit more filler material (from the electrodes) for a given welding amperage, or to deposit the same amount of filler material with an overall less heat input.

Further, it has been discovered that other advantages can be attained from embodiments of the present invention. Specifically, it has been discovered that during short arc welding an increased range of operable wire feed speed can be obtained because of the increased arc stability provided with welding in accordance with embodiments of the present invention. For example, it has been unexpectedly discovered that two 0.030 inch diameter electrodes can be utilized at a higher wire feed speed, in a stable manner, than a single 0.045 inch diameter electrode, even though the overall cross-sectional area of the two 0.030 inch diameter electrodes is similar to that of a single 0.045 inch diameter electrode, the use of two 0.030 inch diameter electrodes provides a more stable welding. It is believed that this is due to the increase in overall exposed surface area of the two 0.030 inch diameter electrodes for a given stick-out distance over a single 0.045 inch diameter electrode. Because of this increased electrode surface area the arc pinch force is optimized, resulting in a more stable welding arc at higher wire feed speeds.

Therefore, various embodiments of the present invention can not only reduce the overall heat input into a weld while increasing the weld puddle length or width, but can also provide a more stable welding arc at higher wire feed speeds.

Further, although the exemplary embodiments have been discussed above utilizing two electrodes passing through the same orifice, other embodiments of the present invention can utilize more than two electrodes. For example it is contemplated that a three electrode configuration can be utilized consistent with the descriptions and discussions set forth above.

It is noted that the present invention is not limited by the type of welding wire to be utilized or the type of welding operation, but can be used in many different types of welding operations with many different types of welding electrodes and electrode combinations.

While the invention has been particularly shown and described with reference to exemplary embodiments thereof, the invention is not limited to these embodiments. It will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the following claims.

Claims

1. An arc welding system, comprising:

a welding gun including a contact tip having a channel and an exit orifice;
an arc welding power supply which provides an arc welding waveform to at least two arc welding consumable electrodes having a circular cross-section via said contact tip; and
a wire feeding mechanism which provides said at least two arc welding consumable electrodes from respective electrode sources to said channel in said contact tip, where said arc welding electrodes pass through said channel in a longitudinal orientation without intertwining or twisting with each other and exit said contact tip through said exit orifice.

2. The welding system of claim 1, wherein said channel is angled.

3. The welding system of claim 1, wherein said orifice has either an elliptical or oval shape.

4. The welding system of claim 1, wherein said channel has a cross-sectional shape at at least one point along its length which is different from the cross-sectional shape of said orifice.

5. The welding system of claim 1, wherein said channel has a circular cross-section at at least one point along its length.

6. The welding system of claim 1, wherein said contact tip is rotatable so as to change the orientation of said at least two electrodes relative to a weld bead.

7. The welding system of claim 1, wherein said at least two electrodes have a different diameter from each other.

8. The welding system of claim 1, wherein said at least two electrodes have a different composition.

9. The welding system of claim 1, wherein said welding waveform provides a welding current sufficient to weld with a single electrode having a cross-sectional area substantially the same as the total cross-sectional area of said at least two electrodes.

10. An arc welding system, comprising:

a welding torch;
a contact tip;
a channel for receiving two arc welding consumable electrodes from respective electrode sources, wherein said arc welding electrodes pass through said torch in a longitudinal orientation without intertwining or twisting with each other and exit said torch; and
a single wire feeder which drives said two arc welding consumable electrodes from said respective electrode sources to said channel;
wherein said two arc welding consumable electrodes are in contact with each other within said channel;
wherein said wire feeder comprises a single pair of feed rollers configured to drive said two arc welding consumable electrodes to said channel, said feed rollers being designed for a single wire feeding operation; and
wherein an arc welding power supply provides a single arc welding waveform through said contact tip for consuming said two arc welding consumable electrodes to generate one arc and one weld puddle from said two arc welding electrodes.

11. An arc welding system, comprising:

a contact tip, wherein said contact tip aligns two arc welding electrodes from respective electrode sources to pass through said contact tip in a longitudinal orientation without intertwining or twisting with each other and exit said contact tip, wherein said two arc welding electrodes are in contact with each other as the two arc welding electrodes pass through said contact tip, and wherein an arc welding power supply provides an arc welding waveform through said contact tip to consume said two arc welding consumable electrodes to generate one arc and one weld puddle from said two arc welding electrodes; and
a single wire feeder which drives said two arc welding consumable electrodes from said respective electrode sources to said contact tip;
wherein said wire feeder comprises a single pair of feed rollers configured to drive said two arc welding electrodes to said contact tip, each roller having a single operable groove for driving said electrodes.

12. The welding system of claim 10, further comprising a liner disposed between said welding torch and said wire feeder, wherein said wire feeder drives said two electrodes from respective electrode sources through said liner to said welding torch.

13. The welding system of claim 12, wherein said two electrodes pass through said liner in a longitudinal orientation without intertwining or twisting with each other to deliver said two electrodes to said welding torch.

14. The welding system of claim 11, further comprising:

a welding torch and a liner disposed between said welding torch and said wire feeder, wherein the welding torch includes the contact tip, and wherein said wire feeder drives said two electrodes from respective electrode sources through said liner to said welding torch.

15. The welding system of claim 14, wherein said two electrodes pass through said liner in a longitudinal orientation without intertwining or twisting with each other to deliver said two electrodes to said welding torch.

16. The welding system of claim 10, wherein said contact tip comprises a single orifice.

17. The welding system of claim 16, wherein said two electrodes exit said contact tip through said orifice.

18. The welding system of claim 11, wherein said contact tip comprises a single orifice.

19. The welding system of claim 18, wherein said two electrodes exit said contact tip through said orifice.

20. The welding system of claim 10, wherein a single arc welding power supply provides the arc welding waveform.

21. The welding system of claim 11, wherein a single arc welding power supply provides the arc welding waveform.

22. The welding system of claim 16, wherein said orifice has either an elliptical or oval shape.

23. The welding system of claim 18, wherein said orifice has either an elliptical or an oval shape.

24. The arc welding system of claim 10, wherein each of said arc welding consumable electrodes has a diameter of 0.030 inches.

25. The arc welding system of claim 11, wherein each of said arc welding electrodes has a diameter of 0.030 inches.

Referenced Cited
U.S. Patent Documents
1368287 February 1921 Pennington et al.
1605860 November 1926 Snelling
1873847 August 1932 Miller
2583507 January 1952 Carpenter et al.
2594333 April 1952 Medicus
2756311 July 1956 Persson et al.
2845524 July 1958 Morley, Jr.
2849593 August 1958 Volff et al.
2866079 December 1958 Morley et al.
2911517 November 1959 Armstrong
2957101 October 1960 Barkley
3131325 April 1964 Briggs
3274371 September 1966 Saenger, Jr. et al.
3328556 June 1967 Nelson et al.
3384778 May 1968 Jeannette
3624345 November 1971 Armstrong
3693858 September 1972 Araya et al.
3694620 September 1972 Gleason
3746833 July 1973 Ujiie
3933533 January 20, 1976 Uchida et al.
4012621 March 15, 1977 Uchida et al.
4088866 May 9, 1978 Lund et al.
4182947 January 8, 1980 Brower
4295746 October 20, 1981 Hartmann
4336441 June 22, 1982 Godai et al.
4437906 March 20, 1984 Tateishi et al.
4475996 October 9, 1984 Inoue
4541616 September 17, 1985 Dean
4697791 October 6, 1987 Henderson et al.
4743731 May 10, 1988 Seuring et al.
4902873 February 20, 1990 Ivannikov
4968867 November 6, 1990 Banzai et al.
5148001 September 15, 1992 Stava
5324552 June 28, 1994 Opower et al.
5440100 August 8, 1995 Stuart et al.
5491321 February 13, 1996 Stuart et al.
5635091 June 3, 1997 Hori et al.
5714735 February 3, 1998 Offer
5773792 June 30, 1998 Hagiwara
5782987 July 21, 1998 Furman
5791560 August 11, 1998 Rogers et al.
5816466 October 6, 1998 Seufer et al.
5958261 September 28, 1999 Offer et al.
5977504 November 2, 1999 Offer et al.
5981906 November 9, 1999 Parker
6172333 January 9, 2001 Stava
6225589 May 1, 2001 Bartok
6374655 April 23, 2002 Hresc
6512200 January 28, 2003 Norrish et al.
6512220 January 28, 2003 Park
6627839 September 30, 2003 Luckowski et al.
6683271 January 27, 2004 Rogers
6683279 January 27, 2004 Moerke
6737616 May 18, 2004 Sherrill
7112759 September 26, 2006 Severance, Jr.
7183516 February 27, 2007 Blankenship et al.
7271365 September 18, 2007 Stava
7429716 September 30, 2008 Bong et al.
7495192 February 24, 2009 Takahashi et al.
7525067 April 28, 2009 Diez et al.
7705269 April 27, 2010 Daniel
7761336 July 20, 2010 Blankenship et al.
7777447 August 17, 2010 Vogel
8049139 November 1, 2011 Houston
8575517 November 5, 2013 Ertmer
8723082 May 13, 2014 Spiesberger
9186745 November 17, 2015 Jia et al.
9839970 December 12, 2017 Peters et al.
9862056 January 9, 2018 Berger et al.
9895760 February 20, 2018 Peters
9937577 April 10, 2018 Daniel et al.
10052707 August 21, 2018 Henry et al.
10792752 October 6, 2020 Weeks et al.
20010008235 July 19, 2001 Miszczak et al.
20020130153 September 19, 2002 Plow
20030209530 November 13, 2003 Stuart et al.
20040016735 January 29, 2004 Huismann et al.
20050218132 October 6, 2005 Wells
20050224486 October 13, 2005 Matiash
20050230373 October 20, 2005 Kensrue
20060070985 April 6, 2006 Nakabayashi et al.
20060081675 April 20, 2006 Enyedy
20060138115 June 29, 2006 Norrish et al.
20060175313 August 10, 2006 Kooken
20060226137 October 12, 2006 Huismann et al.
20060243704 November 2, 2006 Matz et al.
20070007265 January 11, 2007 Myers
20070145028 June 28, 2007 Artelsmair
20070151964 July 5, 2007 Artelsmair et al.
20070158324 July 12, 2007 O'Donnell et al.
20070164074 July 19, 2007 Schorghuber et al.
20070221643 September 27, 2007 Narayanan
20070251932 November 1, 2007 Vogel
20080128395 June 5, 2008 Aigner et al.
20080169336 July 17, 2008 Spiegel et al.
20080190900 August 14, 2008 Zhang et al.
20090050609 February 26, 2009 Berger et al.
20090188896 July 30, 2009 Khakhalev
20090234483 September 17, 2009 Leko et al.
20100213179 August 26, 2010 Peters
20100301030 December 2, 2010 Zhang et al.
20100314373 December 16, 2010 Patterson
20110171393 July 14, 2011 Margolies et al.
20110309062 December 22, 2011 O'Donnell et al.
20120067859 March 22, 2012 Albrecht et al.
20120074115 March 29, 2012 Kazmaier et al.
20120152921 June 21, 2012 Peters et al.
20120285938 November 15, 2012 McFadden et al.
20130193115 August 1, 2013 Berg
20130264323 October 10, 2013 Daniel
20140027413 January 30, 2014 Lin et al.
20140166633 June 19, 2014 Albrecht
20140197148 July 17, 2014 Chen et al.
20150209889 July 30, 2015 Peters et al.
20150266126 September 24, 2015 Ertmer et al.
20160228972 August 11, 2016 Jogdand et al.
20160368075 December 22, 2016 Ide
20170080511 March 23, 2017 Jaeger et al.
20170165779 June 15, 2017 Barhorst et al.
20170189982 July 6, 2017 Hsu
20170368629 December 28, 2017 Grigorenko
20180207744 July 26, 2018 Stoecker
20180214966 August 2, 2018 Peters
20180214967 August 2, 2018 Peters
20180214972 August 2, 2018 Jansma et al.
20180214973 August 2, 2018 Jansma et al.
20180281097 October 4, 2018 Jansma
20180369947 December 27, 2018 Raudsepp et al.
20190047069 February 14, 2019 Weeks et al.
20190168334 June 6, 2019 Kooken et al.
20190201997 July 4, 2019 Stergios et al.
Foreign Patent Documents
2683302 March 2005 CN
101745726 June 2010 CN
101870032 October 2010 CN
102615398 August 2012 CN
102430846 May 2013 CN
103071899 May 2013 CN
103170713 June 2013 CN
103648702 March 2014 CN
101712095 September 2014 CN
104334305 February 2015 CN
104439623 March 2015 CN
205464747 August 2016 CN
106270978 January 2017 CN
104972205 April 2017 CN
106670630 May 2017 CN
106735769 May 2017 CN
206241445 June 2017 CN
206578445 October 2017 CN
109382566 February 2019 CN
1115382 October 1961 DE
2108614 October 1971 DE
2108614 October 1971 DE
42 04 661 June 1993 DE
19611583 September 1997 DE
19611583 September 1997 DE
19611597 September 1997 DE
19611597 September 1997 DE
29819828 December 1999 DE
97 38 785 December 2001 DE
10 2008 014915 November 2009 DE
20 2013 102 979 July 2013 DE
10 2016 003468 September 2016 DE
10 2015 122135 June 2017 DE
1707296 October 2006 EP
1 294 522 September 2007 EP
3446821 February 2019 EP
3656497 May 2020 EP
3693116 August 2020 EP
990208 April 1965 GB
990208 April 1965 GB
1502288 March 1978 GB
1502288 March 1978 GB
2058637 April 1981 GB
2058637 April 1981 GB
H02-258168 October 1990 JP
02-280968 November 1990 JP
4053617 August 1992 JP
H10-113771 May 1998 JP
2008055506 March 2008 JP
2008055506 March 2008 JP
2008087045 April 2008 JP
2008087045 April 2008 JP
2010069494 April 2010 JP
2010069494 April 2010 JP
2010082624 April 2010 JP
2010082624 April 2010 JP
5133079 January 2013 JP
2013-039624 February 2013 JP
5157006 March 2013 JP
5580869 August 2014 JP
6137053 May 2017 JP
2001-0002945 January 2001 KR
10-2010-0115997 October 2010 KR
10-1412374 June 2014 KR
1237347 June 1986 SU
1237347 June 1986 SU
1997045227 December 1997 WO
9839138 September 1998 WO
2010/080411 July 2010 WO
2012153177 November 2012 WO
Other references
  • D/F Machine Specialties; “D/F Automatic & Robotic MIG Tandem Torch”; https://www.dfmachinespecialties.com/index.php?option=com_content&view=article&id=35; Accessed on Oct. 15, 2018; pp. 1-4.
  • Extended European Search Report from Corresponding Application No. 18187717.6; Dated Jan. 4, 2019; pp. 1-10.
  • Fronius; “CMT Twin”; https://www.fronius.com/en/welding-technology/products/robotic-welding/migmag-high-performance/cmt-twin/cmt-twin; Accessed on Oct. 15, 2018; pp. 1-5.
  • Leng, et al.; “The characteristic of twin-electrode TIG coupling arc pressure”; Journal of Physics D: Applied Physics; vol. 39(6): 1120; Dated Mar. 3, 2006.
  • Lincoln Electric; “Tandem MIG™ 800 Amp Welding Torch”; https://www.lincolnelectric.com/assets/US/EN/literature/E10601.pdf; Accessed on Oct. 15, 2018; pp. 1-4.
  • Lincoln Electric; “Wire Level Gauge”; https://www.lincolnelectric.com/assets/us/en/literature/mc0995.pdf; Accessed on Oct. 17, 2018; p. 6.
  • SKS Welding Systems; “Dual Wire 2.0 for double-speed welding”; https://www.sks-welding.com/en/torch-systems/dual-wire/dual-wire-20/product.html; Accessed on Oct. 15, 2018; pp. 1-2.
  • Ueyama, et al.; “Effects of torch configuration and welding current on weld bead formation in high speed tandem pulsed gas metal arc welding of steel sheets”; Science and Technology of Welding and Joining; vol. 10, No. 6; Dated 2005; Published Online Dec. 4, 2013; pp. 750-759.
  • Wolf Robotics; “Tandem Wire MIG Welding”; Dated Aug. 29, 2007; pp. 1-8.
  • Ye, et al.; “Research on arc interference and welding operating point change of twin wire MIG welding”; The International Journal of Advanced Manufacturing Technology; vol. 89, Issue 1-4; Dated Mar. 2017; pp. 493-502.
  • Extended European Search Report from Corresponding Application No. 19203369.4; Dated Jul. 31, 2020; pp. 1-8.
  • Extended European Search Report from Corresponding Application No. EP19203389.2; Dated Jun. 22, 2020; pp. 1-9.
  • Shi, et al.; “Physical Characteristics of Twin-Wire Indirect Arc Plasma;” Vacuum; vol. 107; Dated Apr. 3, 2014; pp. 41-50.
  • Extended European Search Report from Corresponding Application No. 19205296.7; Dated Aug. 13, 2020; pp. 1-13.
  • Extended European Search Report from Corresponding Application No. 19205356.9; Dated Aug. 13, 2020; pp. 1-9.
  • Extended European Search Report from Corresponding Application No. 21156359.8; Dated Jul. 9, 2021; pp. 1-8.
  • Extended European Search Report from Corresponding Application No. 21153533.1; Dated Jul. 20, 2021; pp. 1-9.
  • Office Action from U.S. Appl. No. 16/707,659 dated Jul. 6, 2021.
  • Office Action from U.S. Appl. No. 16/707,659 dated Feb. 25, 2022.
  • Office Action from U.S. Appl. No. 16/707,685 dated Feb. 25, 2022.
  • Office Action from U.S. Appl. No. 16/707,659 dated Jun. 14, 2023.
  • Office Action from U.S. Appl. No. 16/707,659 dated Nov. 7, 2023.
  • Office Action from U.S. Appl. No. 16/707,685 dated Sep. 14, 2023.
  • Office Action from U.S. Appl. No. 16/707,659 dated May 30, 2024.
  • Office Action from U.S. Appl. No. 16/707,685 dated Jun. 5, 2024.
  • Office Action from U.S. Appl. No. 16/707,685 dated Aug. 6, 2021.
  • Lincoln Electric, “Tandem MIG, Waveform Control Technology,” copyright 2005, NX-3.70 10/05, 16 pages.
  • Office Action from U.S. Appl. No. 16/707,659 dated Jan. 10, 2025.
Patent History
Patent number: RE50752
Type: Grant
Filed: Dec 9, 2019
Date of Patent: Jan 20, 2026
Assignee: LINCOLN GLOBAL, INC. (Sant Fe Springs, CA)
Inventors: Steven Peters (Huntsburg, OH), Dennis Hartman (Wellington, OH)
Primary Examiner: William E Dondero
Application Number: 16/707,701
Classifications
Current U.S. Class: Silicic Material In Coating (428/387)
International Classification: B23K 9/173 (20060101); B23K 9/12 (20060101);