Abstract: Crosslinking systems suitable for use in a polymer melt composition wherein the polymer melt composition comprises a hydroxyl polymer; polymeric structures made from such polymer melt compositions; and processes/methods related thereto are provided.

Abstract: A process for making patterned cigarette wrapper includes the steps of: preparing a printing solution including the steps of: mixing at least water and a starch to form a starch mixture, heating the starch mixture to a temperature of at least about 180° F. preferably for at least about 30 minutes to release amylopectin and amylose, adding propylene glycol to the starch mixture, and mixing the starch mixture and propylene glycol to form a printing solution, wherein the solution is maintained and applied at elevated temperature (120° F. to 150° F.). The process also includes providing a base web of wrapper and applying the printing solution to the wrapper in a predetermined pattern.

Abstract: The disclosure relates to a surface treatment composition for inkjet media, including: at least one surface sizing agent selected from the group consisting of starch, starch derivatives, polymeric materials, and combinations thereof; and an ink fixative selected from the group consisting of at least one high valence metallic salt, at least one high valence complex poly-salt, and combinations thereof. The ink fixative is present in the surface treatment composition from about 10 weight % to about 50 weight % of the surface treatment composition. The at least one high valence metallic salt and the at least one high valence complex poly-salt have a valence greater than divalent. In addition, the disclosure relates to a method of making and a system for printing the surface treated media; and an inkjet printable paper.

Abstract: Starch can be gelatinised more efficiently by a thermomechanical treatment, if a dialdehyde polysaccharide with a relatively low degree of oxidation is added to the starch. This thermomechanical treatment can be carried out at a temperature below 115 DEG C., or even below 100 DEG C., and with a high throughput rate. With this treatment a granulate or other semi-finished product is obtained that can be shaped to produce an article that has excellent dimensional stability in water. By adding dialdehyde polysaccharide with a low degree of oxidation to starch it is possible to blow transparent films based on thermoplastic starch which have improved mechanical properties.

Abstract: Non-thermoplastic starch fibers having no melting point and having apparent peak wet tensile stress greater than about 0.2 MegaPascals (MPa). The fibers can be manufactured from a composition comprising a modified starch and a cross-linking agent. The composition can have a shear viscosity from about 1 Pascal·Seconds to about 80 Pascal·Seconds and an apparent extensional viscosity in the range of from about 150 Pascal·Seconds to about 13,000 Pascal·Seconds. The composition can comprise from about 50% to about 75% by weight of a modified starch; from about 0.1% to about 10% by weight of an aldehyde cross-linking agent; and from about 25% to about 50% by weight of water. Prior to cross-linking, the modified starch can have a weight average molecular weight greater than about 100,000 g/mol.

Abstract: Non-thermoplastic starch fibers having no melting point and having apparent peak wet tensile stress greater than about 0.2 MegaPascals (MPa). The fibers can be manufactured from a composition comprising a modified starch and a cross-linking agent. The composition can have a shear viscosity from about 1 Pascal·Seconds to about 80 Pascal·Seconds and an apparent extensional viscosity in the range of from about 150 Pascal·Seconds to about 13,000 Pascal·Seconds. The composition can comprise from about 50% to about 75% by weight of a modified starch; from about 0.1% to about 10% by weight of an aldehyde cross-linking agent; and from about 25% to about 50% by weight of water. Prior to cross-linking, the modified starch can have a weight average molecular weight greater than about 100,000 g/mol.

Abstract: Non-thermoplastic starch fibers having no melting point and having apparent peak wet tensile stress greater than about 0.2 MegaPascals (MPa). The fibers can be manufactured from a composition comprising a modified starch and a cross-linking agent. The composition can have a shear viscosity from about 1 Pascal·Seconds to about 80 Pascal·Seconds and an apparent extensional viscosity in the range of from about 150 Pascal·Seconds to about 13,000 Pascal·Seconds. The composition can comprise from about 50% to about 75% by weight of a modified starch; from about 0.1% to about 10% by weight of an aldehyde cross-linking agent; and from about 25% to about 50% by weight of water. Prior to cross-linking, the modified starch can have a weight average molecular weight greater than about 100,000 g/mol.

Abstract: A “one-shot” composition for use in paper sizing comprises an admixture of a rosin emulsion, a soluble aluminium salt and a cationic starch derivative which has a charged state of 1.0 to 3.5 m equivalents per gramme and which is produced by a process in which the starch structure was split prior to the cationising step.