Abstract: A new wrought high silicon heat resistant alloy is provided having the broad composition of about 0.16 to 0.30% carbon, about 3.2 to 4.5% silicon, about 0.8 to 1.5% aluminum, about 17 to 20% chromium, about 12 to 16% nickel, up to about 2% manganese, 0 to 0.07% rare earth alloys and the balance iron with residual impurities in ordinary amounts. The alloy is a fully austenitic hot rolled and annealed chromium and nickel containing alloy having high strength and corrosion resistance.
Abstract: A process for preparing an iron group sintered compact involves forming an admixture of an iron group metal alloy powder additive and iron powder wherein the melting point of the alloy additive is at least about 50.degree. C. lower than that of the iron, compacting the admixture to form a green compact, and sintering the green compact at a temperature of from about 20.degree. C. above the solidus to about 100.degree. C. above the liquidus of the alloy additive whereby a sintered compact is formed. A compact having an iron group alloy additive as a continuous phase and iron as a discontinuous phase wherein the continuous phase has a melting point of at least about 50.degree. C. lower than that of the discontinuous phase can be prepared at lower sintering temperatures than a typical iron powder.
Abstract: An austenitic stainless steel exhibiting improved resistance to corrosion caused by nitric acid is disclosed, which consists essentially of:C: not more than 0.03% by weight, Si: 2-6% by weight,Mn: 0.1-8% by weight, Cr: 20-35% by weight,Ni: 17-50% by weight, Mg: not more than 0.02%,at least one of Nb, Ti and Ta in the total amount of 8.times.C(%) or more, but 1.0% by weight or less,S: not more than 0.003% by weight,Oxygen: not more than 0.003% by weight,N: not more than 0.03% by weight,P: not more than 0.02% by weight,Fe and incidental impurities: balancethe composition further satisfying the following relationships;-10.ltoreq.Ni(Bal).ltoreq.-0.1Cr(%).gtoreq.(7/4)Si(%)+16.5Mg(%)-0.75.times.S(%)-1.5.times.Oxygen(%).gtoreq.0wherein, Ni(Bal)=30.times.C(%)+0.5.times.Mn(%)+Ni(%)+8.2-1.1.times.[1.5.times.Si(%) +Cr(%)].
Abstract: This invention relates to a welding material for welding a high-Si austenite stainless steel, capable of ensuring a high corrosion resistance of the weld metal in hot nitric acid of high concentration, while maintaining a toughness of the weld metal not smaller than 2 Kg-m/cm.sup.2, and the method of application therefor. The welding material has a composition containing not greater than 0.015% of C, 5 to 7% of Si, not greater than 2% of Mn, 15 to 20% of Cr, 10 to 22% of Ni, not greater than 0.02% of N, not greater than 0.45% of one or both of Nb and Ta, and the balance substantially Fe and inevitable impurities the sum of C and N contents is selected to be not greater than 0.03% and the sum of Nb and Ta contents is selected to be not smaller than 15.times.(C+N)%. The Ni-balance value given by the following formula ranges between -4 and -2.Ni balance value=% Ni+30(%C+%N)+0.5(%Mn)-1.1(%Cr+1.5.times.%Si)+8.
Type:
Grant
Filed:
September 12, 1984
Date of Patent:
March 31, 1987
Assignees:
Nippon Stainless Steel Co. Ltd., Sumitomo Chemical Co., Ltd.
Abstract: A dual-phase stainless steel exhibiting improved resistance to corrosion caused by nitric acid is disclosed, which consists essentially of:C: not more than 0.02% by weight, Si: 2-6% by weight,Mn: 0.1-2% by weight, Cr: 20-35% by weight,Ni: 3-27% by weight, P: not more than 0.02% by weight,N: not more than 0.30% by weight,Fe and incidental impurities: balance the amount of ferrite to be 30-70% by volume.
Abstract: There is provided a crucible for containing salt baths for the boriding of steels which has a high service life made of a steel which consists of (or consists essentially of) 0.05-0.8% carbon, 0.8-2.5% silicon, 0.1-2.0% manganese, 0-1.5% aluminum, 6-30% chromium, 4-39% nickel and the balance iron.
Type:
Grant
Filed:
July 12, 1984
Date of Patent:
September 9, 1986
Assignee:
Degussa Aktiengesellschaft
Inventors:
Ulrich Baudis, Peter Biberbach, Rainer Engelmann