Patent number: 8329305Abstract: To provide a highly hard coating film formed on a substrate, as adhered to the surface of the substrate and having a refractive index of from 1.28 to 1.41 and a contact angle with water of from 90° to 115°. A coating film having a refractive index of from 1.28 to 1.41 and a contact angle with water of from 90° to 115°, which is formed as adhered to a substrate surface by forming a reaction mixture comprising a silicon compound (A) of the formula Si(OR)4, a silicon compound (B) of the formula CF3(CF2)nCH2CH2Si(OR1)3, a silicon compound (C) of the formula H2NCOH(CH)mSi(OR2)3, an alcohol (D) of the formula R3CH2OH and oxalic acid (E), in a specific ratio, heating this reaction mixture at a temperature of from 40 to 180° C. in the absence of water to form a solution of a polysiloxane, then applying a coating fluid comprising the polysiloxane solution on a substrate surface to form a coating, and heat-curing the coating at a temperature of from 40 to 450° C.Type: GrantFiled: March 24, 2011Date of Patent: December 11, 2012Assignee: Nissan Chemical Industries, Ltd.Inventors: Kenichi Motoyama, Yoshihiro Tani
-
Publication number: 20120306107Abstract: A silicone resin composition contains a first organopolysiloxane having, in one molecule, both at least two ethylenically unsaturated hydrocarbon groups and at least two hydrosilyl groups; a second organopolysiloxane having, in one molecule, at least two hydrosilyl groups without containing an ethylenically unsaturated hydrocarbon group; a hydrosilylation catalyst; and a hydrosilylation inhibitor.Type: ApplicationFiled: May 11, 2012Publication date: December 6, 2012Applicant: NITTO DENKO CORPORATIONInventors: Munehisa MITANI, Hiroyuki KATAYAMA, Haruka FUJII
-
Publication number: 20120309882Abstract: An anti-fouling composition which comprises a cured or cross-linked polymer free of perfluoropolyether moieties and a fluid fluorinated alkyl- or alkoxy-containing polymer or oligomer. Preferably, the fluorinated alkyl- or alkoxy-containing polymer or oligomer comprises a repeating unit of the general formula: —{[CFR—(CFR)m—(O)n]p—[CFR—O]q}- wherein n is 0 or 1, m is an integer from 0 to 4, R independently is H, F, Cl, Br, or CF3, and the ratio g/p is 0-10, and the fluorine-free polymer is an organosiloxane-containing polymer comprising a repeating unit of the general structure —[SiR1R2—O]—, wherein R1 and R2 are independently hydrogen, alkyl, aryl, aralkyl, or a vinyl group.Type: ApplicationFiled: August 10, 2012Publication date: December 6, 2012Applicant: AKZO NOBEL N.V.Inventors: David Neil WILLIAMS, Nigel Ivor Edward SHEWRING, Adrian James LEE
-
Patent number: 8323745Abstract: An application liquid capable of forming a dense silica-based coating film even when embedded into a fine groove, and a method for formation of a silica-based coating film using the application liquid are provided. An application liquid is used including (A) a siloxane polymer, and (B) a base generator represented by the following general formula (I): wherein, R1 and R2 are a hydrocarbon group having 1 to 5 carbon atoms and which may be the same or different; or one of R1 and R2 is a hydrogen atom and the other is a hydrocarbon group having 1 to 5 carbon atoms; when R1 and R2 are both a hydrocarbon group, these may bind to one another to form a ring structure; R3 is a linking group; and R4 is a condensed ring.Type: GrantFiled: March 26, 2010Date of Patent: December 4, 2012Assignee: Tokyo Ohka Kogyo Co., Ltd.Inventors: Tokonori Yamadaya, Kiyoshi Ishikawa, Atsushi Sawano
-
Publication number: 20120301180Abstract: Provided a charging member which can prevent any contaminants deposited on a cleaning member from adhering thereto by making low a surface free energy and coefficient of friction thereof.Type: ApplicationFiled: August 7, 2012Publication date: November 29, 2012Applicant: CANON KABUSHIKI KAISHAInventors: Yuya Tomomizu, Noriaki Kuroda, Masataka Kodama, Noriko Suzumura, Hiroki Masu
-
Publication number: 20120298299Abstract: A silane-functional polyester of formula (I): wherein Y is an n-valent residue of a polyester P which is solid at room temperature and terminated by hydroxy groups, after removal of n hydroxy groups; R1 is a linear or branched, monovalent carbon residue having 1 to 12 carbon atoms, optionally having one or more C—C multiple bonds and/or having optionally cycloaliphatic and/or aromatic portions; R2 is an acyl residue or a linear or branched, monovalent hydrocarbon residue having 1 to 12 carbon atoms, optionally having one or more C—C multiple bonds and/or having optionally cycloaliphatic and/or aromatic portions; R3 is a linear or branched, divalent hydrocarbon residue having 1 to 12 carbon atoms, optionally having cyclic and/or aromatic portions, and optionally having one or more heteroatoms; the index a has a value of 0, 1 or 2; and the index n has a value of 1 to 3.Type: ApplicationFiled: November 28, 2011Publication date: November 29, 2012Applicant: SIKA TECHNOLOGY AGInventors: Daniele Rutz, Marcel Oertli, Barbara Jucker
-
Patent number: 8317220Abstract: A curable coating composition that exhibits improved cure and adhesion to various substrates, especially synthetic textiles used in the manufacture of air bags, comprises a composition curable by a hydrosilylation reaction, an acryloxy functional alkoxysilane or a methacryloxy functional alkoxysilane, an alkenyl functional silanol terminated organopolysiloxane, and an epoxy functional alkoxysilane. The curable coating composition is especially useful for application to synthetic textiles such as automotive air bags.Type: GrantFiled: September 23, 2011Date of Patent: November 27, 2012Assignees: Dow Corning Corporation, Dow Corning Toray Co., Ltd.Inventors: Randall Paul Sweet, William R. Blackwood, Tsugio Nozoe
-
Patent number: 8318244Abstract: A method for fabricating electronic devices includes the steps of 1) printing a multi-layer electronic device on a silicone-based hard coating on a substrate, and 2) removing the device from the substrate. The silicone-based hard coating is an abrasion resistant coating with hardness ranging from 1 to 10 gigaPascals.Type: GrantFiled: December 18, 2008Date of Patent: November 27, 2012Assignee: Dow Corning CorporationInventors: Michael Brasseur, Karen Hueston, James Tonge
-
Patent number: 8318258Abstract: Silsesquioxane resins useful in antireflective coatings wherein the silsesquioxane resin has the formula (PhSiO(3?x)/2(OR?)x)m(HSiO(3?x)/2(OR?)x)n(MeSiO(3?x)/2(OR?)x)o(RSiO(3?x)/2(OR?)x)p(R2SiO(3?x)/2(OR?)x)q where Ph is a phenyl group, Me is a methyl group; R is selected from a sulfur-containing organic functional group; R? is hydrogen atom or a hydrocarbon group having from 1 to 4 carbon atoms; R2 is selected from ester groups, polyether groups; and polyethylene oxide groups; x has a value of 0, 1 or 2; m has a value of 0.01 to 0.97; n has a value of 0.01 to 0.97; o has a value of 0.01 to 0.97; p has a value of 0.01 to 0.97; q has a value of 0 to 0.96; and m+n+o+p+q?1.Type: GrantFiled: December 5, 2008Date of Patent: November 27, 2012Assignee: Dow Corning Toray Co., Ltd.Inventor: Akihiko Shirahata
-
Publication number: 20120294557Abstract: Self-lubricated bearings contain a substratum and a self-lubricating surface coating composition disposed thereon, wherein the self-lubricating surface coating composition further contains at least one cured thermosetting acrylate and at least one phenolic resin. The phenolic resin preferably contains a mixture of phenolic resin and polyvinyl formal resin. A self-lubricating surface coating composition is also provided, as well as several methods of making the bearings. The self-lubricated bearings of the present invention have surprisingly long service lives.Type: ApplicationFiled: May 16, 2011Publication date: November 22, 2012Applicant: New Hampshire Ball Bearings, Inc.Inventors: Richard Soelch, Thomas Auletto, Grant Drew
-
Publication number: 20120296022Abstract: The present invention provides a polysilazane-containing composition capable of forming a dense siliceous film more rapidly and at a lower temperature than known polysilazane-containing composition. In a process for forming the siliceous film, the composition comprising a polysilazane compound, a particular amine compound and a solvent is coated on a substrate and converted into a siliceous substance. The particular amine compound preferably contains two amine groups separated from each other at the distance corresponding to five C—C bonds or more, and the amine groups preferably have hydrocarbon substituent groups.Type: ApplicationFiled: August 3, 2012Publication date: November 22, 2012Applicant: AZ ELECTRONIC MATERIALS (LUXEMBOURG) S.A.R.L.Inventor: Yuki OZAKI
-
Patent number: 8304023Abstract: Fiberfill fibers are treated with aqueous dispersions of organopolysiloxanes obtained by reaction of condensation-curable organopolysiloxanes with silanes (R3O)3SiCR22—Y or their hydrolyzates, where R2 is hydrogen or a monovalent lower alkyl radical, R3 is an alkyl radical, Y is —NHR4, —NR42 or —NR5 in the presence of water, emulsifier and optionally further silanes (R3O)xR3-xSi—R6—Z or their hydrolyzates, where R6 is a divalent C2-18 hydrocarbyl radical and Z is an amino or aminoalkylamino, epoxy, or (meth)acryloyloxy radical, and x is 1, 2 or 3, and optionally further materials which do not take part in the reaction, wherein no metal-containing catalysts are used and that the organopolysiloxanes and silanes are used in such amounts that the organopolysiloxanes, after removal of water, form elastomeric films insoluble in toluene.Type: GrantFiled: November 7, 2007Date of Patent: November 6, 2012Assignee: Wacker Chemie AGInventors: Konrad Alfons Wierer, Otto Schneider
-
Patent number: 8304092Abstract: An aqueous surface-treatment liquid is a treatment liquid containing a water-soluble zirconium compound, water-dispersive particulate silica, a silane coupling agent, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin emulsion in particular proportions. A surface-treated galvanized steel sheet produced using the treatment liquid is a galvanized steel sheet having a surface-treatment coating on a surface thereof, and the coating contains a zirconium compound, particulate silica, a silane-coupling-agent-derived component, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin in particular proportions. The amount of coating on a zirconium basis is 10 to 200 mg/m2. This surface-treated galvanized steel sheet is chromate-free and has superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming.Type: GrantFiled: December 10, 2007Date of Patent: November 6, 2012Assignee: JFE Steel CorporationInventors: Kazuhisa Okai, Rie Umebayashi, Etsuo Hamada, Akira Matsuzaki, Satoru Ando
-
Patent number: 8304083Abstract: A hydrophilic member comprising a substrate and a hydrophilic coating film provided on the substrate, wherein the hydrophilic coating film is produced by coating a substrate with an aqueous solution containing (a) a hydrophilic polymer, (b) an alkoxide of a metal selected from the group consisting of Si, Ti, Zr, and Al, and (c) a metal complex catalyst, and heat-drying the solution applied.Type: GrantFiled: November 16, 2006Date of Patent: November 6, 2012Assignee: Fujifilm CorporationInventors: Satoshi Hoshi, Toshiaki Aoai, Kazuto Shimada, Satoshi Tanaka, Kazuto Kunita
-
Publication number: 20120273410Abstract: A semi-finished product is disclosed including fibrous materials, binders, 15 to 90% by volume metal fillers, and 0 to 15% by volume non-metal inorganic fillers. The total content of the fillers is not more than 90% by volume of the semi-finished product. The invention further relates to metal materials and processes for manufacturing the materials and semi-finished products and uses thereof.Type: ApplicationFiled: March 25, 2011Publication date: November 1, 2012Applicant: MANN+HUMMEL GMBHInventors: Andreas HOFENAUER, Christoph SORG, Ralf MARKUSCH
-
Publication number: 20120272618Abstract: Water-dilutable coating compositions comprising poly(vinyl alcohol) and/or ethylene-vinyl alcohol copolymer, dispersed clay and polycarboxylic acid polymer that can be prepared using convention apparatus and that provide exceptional oxygen barrier along with good laminate bond strengths at high relative humidity when incorporated into adhesively formed laminates, particularly PET-PE laminate structures.Type: ApplicationFiled: November 19, 2010Publication date: November 1, 2012Applicant: SUN CHEMICAL B.V.Inventors: Derek Ronald Illsley, Sarfaraz Akhtar Khan, Graham Trevor Street
-
Patent number: 8299169Abstract: A coating solution for obtaining sol-gel films, the coating solution being composed of a solid matter and a solvent, the solid matter including a silicon oxide oligomer obtained by subjecting an alkoxysilane to hydrolysis and polycondensation in an acid aqueous solution; the solvent including an organic solvent having a boiling point of 100° C. or higher and a viscosity of 3.5 mPa·s or lower and the aqueous acid solution, the number average molecular weight of the silicon oxide oligomer in terms of polystyrene being 500-4000, the content of the solid matter in the coating solution being 8-30 weight %, and the content of the silicon oxide oligomer in the solid matter being 10 weight % or greater.Type: GrantFiled: April 28, 2008Date of Patent: October 30, 2012Assignee: Central Glass Company, LimitedInventors: Masanori Saito, Shigeo Hamaguchi, Soichi Kumon, Yoshinori Akamatsu
-
Patent number: 8298456Abstract: The present invention relates to a silicone resin composition including a silicone resin and metal oxide fine particles dispersed therein, the silicone resin being obtained by reacting a siloxane derivative having at least one selected from the group consisting of an alkoxysilyl group and a silanol group at a molecular end thereof and having a weight-average molecular weight (Mw) as determined by a gel permeation method of 300 to 6,000, with silica fine particles having silanol groups on a surface thereof.Type: GrantFiled: January 31, 2011Date of Patent: October 30, 2012Assignee: Nitto Denko CorporationInventor: Keisuke Hirano
-
Publication number: 20120269976Abstract: A one-package moisture curable composition is provided. The composition comprises, by weight percentage based on the dry weight of the composition, from 50 to 95% at least one silane terminated polybutadiene based polymer or silane terminated polyol based polymer and from 5 to 50% at least one fluoro/fluoroalkoxy-functionalized silane; wherein the composition, after moisture cured, forms a surface whose water contact angle is larger than 101°. The composition is suitable for the applications in antifouling coatings which affords low surface energy and improved mechanical performance.Type: ApplicationFiled: April 19, 2012Publication date: October 25, 2012Inventors: Yan HUANG, Hongyu CHEN, John ROPER, III, Christopher TUCKER, Gerald VANDEZANDE, Yu ZHANG
-
Patent number: 8293000Abstract: An antireflective coating composition includes a hydrolytic condensate (C1) of alkoxy silane (C11) and fluoric alkoxy silane (C12); a particle-type metal fluoride (C2) with a refractive index of 1.40 or less; and a liquid dispersion-enhancing chelating agent (C3). A coating film to which the above composition is applied controls refractive index, surface energy, film strength and so on, so it ensures excellent antireflective characteristic, excellent scratch resistance, good erasure of liquid stains such as fingerprints, and particularly excellent dust removal, so it may be usefully applied to an outermost layer of a front surface of a display regardless of kind of a display substrate or presence of an additional coating layer.Type: GrantFiled: July 6, 2007Date of Patent: October 23, 2012Assignee: LG Chem, Ltd.Inventors: Joon-Koo Kang, Mi-Young Han, Young-Eun Lee, Young-Jun Hong, Yeong-Rae Chang
-
Patent number: 8293332Abstract: A rust-proof coating, which does not contain a hazardous metal such as chromium and is able to form a thin coating in which crack generation is inhibited even after a baking treatment at a high temperature, including based on the whole composition, 5 to 40% by weight of an organic silicon compound, 0.05 to 5.0% by weight of an organic titanium compound, 20 to 60% by weight of one or more metal powders selected from the group of zinc powder, zinc alloy powder, and aluminum powder, and 10 to 60% by weight of an organic solvent. A coating having excellent anticorrosive properties can be formed by coating the above-mentioned paint composition followed by heating at a temperature of from 200 to 400 degrees C.Type: GrantFiled: December 14, 2011Date of Patent: October 23, 2012Assignee: Yuken Industry Co., Ltd.Inventor: Toshimichi Suzuki
-
Publication number: 20120263881Abstract: Described herein is the use of a modified PET in combination with a vinyl addition silicone water-based release coating to provide performance equivalent to the silicone by itself at a lower cost than the silicone by itself and resulting in a release backing paper that can be repulped and recycled in conventional recycled paper mills avoiding the additional cost of sending the scrap paper to landfill.Type: ApplicationFiled: October 4, 2011Publication date: October 18, 2012Applicant: Eco-Friendly Solutions, LLCInventor: Robert Scott VONFELDEN
-
Publication number: 20120263932Abstract: It is to provide a resin substrate provided with a hard coating film having a silicone type hard coating layer provided on a resin substrate via a primer layer, having excellent abrasion resistance and also having excellent weather resistance such as weather-resistant adhesion and weather-crack resistance of the hard coating layer, and it production process. A resin substrate provided with a hard coating film, comprising, between a primer layer containing an acrylic polymer as the main component and a hard coating layer containing a cured product of an organopolysiloxane as the main component, a middle layer comprising a mixture of components constituting both the layers, in such a thickness that when the thickness of the hard coating layer is Ht and the thickness of the middle layer is Mt, the ratio in thickness of these layers Mt/Ht is from 0.05 to 1.0.Type: ApplicationFiled: June 25, 2012Publication date: October 18, 2012Applicant: Asahi Glass Company, LimitedInventors: Kyoko YAMAMOTO, Takashi SHIBUYA, Kyon Hun Min
-
Publication number: 20120257914Abstract: Exemplary embodiments provide composite materials used for fixing members that can include silsesquioxane-based particles and/or carbon nanotubes dispersed in a polymer matrix.Type: ApplicationFiled: June 5, 2012Publication date: October 11, 2012Applicant: XEROX CORPORATIONInventors: Carolyn Moorlag, Yu Qi, Qi Zhang, Sandra J. Gardner, Gordon Sisler, Guiqin Song, Nan-Xing Hu
-
Publication number: 20120258319Abstract: The disclosure relates to curable polyureasil compounds, methods related to curing of such compounds via hydrolysis and/or condensation to form coatings on a substrate, and coated articles formed from the curable polyureasil compounds. The polyureasil compounds are generally hydrocarbon-based, including multiple urea groups and multiple hydrolysable silyl groups per molecule. The hydrolysable silyl groups can be hydrolyzed and subsequently condensed to provide a networked polymeric structure with siloxane/urea linkages between polyureasil compound precursors to form a cured polyureasil composition useful as a coating for a substrate, in particular an anti-corrosion coating for a metallic substrate.Type: ApplicationFiled: April 5, 2012Publication date: October 11, 2012Applicant: EASTERN MICHIGAN UNIVERSITYInventor: Vijaykumar M. Mannari
-
Publication number: 20120252923Abstract: This disclosure relates to compositions containing a) a silicone resin, b) a first silicone fluid having a viscosity from about 1 to about 15,000 centistokes at 25° C.; c) a second silicone fluid having a viscosity from about 1 to about 30,000 centistokes at 25° C.; d) an acrylic polymer; e) a hydrocarbon solvent; and f) water. The compositions of this disclosure provide long lasting hydrophobic coatings with high water contact angles for automotive surfaces, in which the hydrophobic automotive surfaces possess self-cleaning functions, e.g., water and dirt repellency. This disclosure also relates to methods for treating automotive surfaces and to automotive surfaces coated with the compositions.Type: ApplicationFiled: March 31, 2011Publication date: October 4, 2012Inventor: Ashot K. Serobian
-
Publication number: 20120251801Abstract: A protective film has a soluble polyimide polymer base layer and an exterior layer directly contacting the base layer exterior surface. The base layer is less than 12 microns thick, and is at least 2 meters long. The exterior layer includes at least one of a fluorinated polymer, a dielectric layer, one or more metallic layers, a metalloid layer, or a plurality of dielectric layers where each dielectric layer has a dielectric layer thickness that varies no more than 3%. The exterior layer or the base layer can also include additives, as desired.Type: ApplicationFiled: March 29, 2011Publication date: October 4, 2012Applicant: Nexolve CorporationInventors: James D. Moore, Brian G. Patrick, Brandon S. Farmer, Garrett D. Poe, David L. Rodman, Lonnie F. Bradburn, JR., Amy S. Davis
-
Publication number: 20120252959Abstract: A crosslinked coating composition formed from polyurethane polyols and blocked or unblocked polyisocyanates. The polyisocyanates, in particular, comprise at least bis(isocyanatomethyl) cyclohexane. The coating is substantially free from ester functionality that forms a contiguous part of the network backbone. A clearcoat formed from the described components and having a majority of urethane bonds is very resistant to environmental etch damage.Type: ApplicationFiled: January 10, 2011Publication date: October 4, 2012Applicant: E I DU PONT DE NEMOURS AND COMPANYInventors: Delson Jayme Trindade, Robert R. Matheson
-
Patent number: 8277929Abstract: A method for modifying the surface of a substrate includes the following steps: (1) a step for forming a polysilazane coating by applying a polysilazane onto the surface of a substrate; (2) a step for applying an organic compound of which main backbone comprises an organic group represented by the following formula [1]: —[(R)mO]n— (wherein R represents an alkylene group, and m and n respectively represent a positive number of not less than 1) onto the surface of the polysilazane coating; and (3) a step for heating the substrate having undergone the steps (1) and (2), thereby converting the polysilazane to silica and bonding the organic compound to the silica of the silica layer.Type: GrantFiled: December 16, 2005Date of Patent: October 2, 2012Assignee: The University of TokushimaInventors: Mikito Yasuzawa, Takashi Koide
-
Publication number: 20120244346Abstract: Novel compositions for use in image forming apparatus and fuser members. In particular, the novel composition is a hybrid networked material comprising fluorocarbon chains connected via silane linkages. The novel composition may be used in fuser members comprising a substrate and a top-coat layer disposed over the substrate.Type: ApplicationFiled: March 22, 2011Publication date: September 27, 2012Applicant: XEROX CORPORATIONInventors: Carolyn Moorlag, Nan-Xing Hu, Yu Qi, Qi Zhang
-
Patent number: 8274075Abstract: Solution-processable dielectric materials are provided, along with precursor compositions and processes for preparing the same. Composites and electronic devices including the dielectric materials also are provided.Type: GrantFiled: April 20, 2010Date of Patent: September 25, 2012Assignee: Northwestern UniversityInventors: Tobin J. Marks, Antonio Facchetti, Zhiming Wang, Hyuk-Jin Choi, Nae-Jeong Suh, legal representative
-
Patent number: 8268403Abstract: A method of forming an organic silica film includes forming a coating including a silicon compound having an —Si—O—Si— structure and an —Si—CH2—Si— structure on a substrate, heating the coating, and curing the coating by applying ultraviolet radiation.Type: GrantFiled: April 28, 2005Date of Patent: September 18, 2012Assignee: JSR CorporationInventors: Masahiro Akiyama, Hisashi Nakagawa, Tatsuya Yamanaka, Atsushi Shiota, Takahiko Kurosawa
-
Patent number: 8268067Abstract: A composition and method of treating substrates, in particular substrates having a hard surface such as ceramics, metal or glass, to render them water, oil, stain, and dirt repellent is described.Type: GrantFiled: October 6, 2009Date of Patent: September 18, 2012Assignee: 3M Innovative Properties CompanyInventors: Suresh Iyer, Wayne W. Fan
-
Publication number: 20120231281Abstract: Disclosed are an aluminum alloy article having an excellent bonding force between a resin and an aluminum alloy using an alkoxysilane-containing triazinethiol, and a method for producing the same. The aluminum alloy article comprises a substrate made of aluminum or an aluminum alloy, and a resin bonded onto at least a portion of a surface of the substrate through a dehydrated silanol-containing triazinethiol derivative layer. The aluminum alloy article comprises a metal compound layer containing at least one selected from the group consisting of a hydroxide, a hydrous oxide, an ammonium salt, a carboxylate, a phosphate, a carbonate, a silicate, and a fluoride between the substrate and the dehydrated silanol-containing a triazinethiol derivative layer.Type: ApplicationFiled: September 3, 2010Publication date: September 13, 2012Inventors: Kinji Hirai, Muneya Furukawa, Isamu Akiyama
-
Patent number: 8263717Abstract: The present invention provides a polysilazane-containing composition capable of forming a dense siliceous film more rapidly and at a lower temperature than known polysilazane-containing composition. In a process for forming the siliceous film, the composition comprising a polysilazane compound, a particular amine compound and a solvent is coated on a substrate and converted into a siliceous substance. The particular amine compound preferably contains two amine groups separated from each other at the distance corresponding to five C—C bonds or more, and the amine groups preferably have hydrocarbon substituent groups.Type: GrantFiled: October 27, 2008Date of Patent: September 11, 2012Assignee: AZ Electronic Materials USA Corp.Inventor: Yuki Ozaki
-
Patent number: 8263185Abstract: The invention relates to compositions comprising or consisting of a reaction product obtained from a reaction mixture of aminosilane of formula (I), a mecaptosilane of formula (II) and an epoxysilane of formula (III). Said compositions are suitable as bonding agents, especially in the form of primers. The compositions are highly adhesive and especially suitable for low-temperature applications and especially for sticking glass together.Type: GrantFiled: November 20, 2006Date of Patent: September 11, 2012Assignee: Sika Technology AGInventor: Wolf-Rudiger Huck
-
Patent number: 8263312Abstract: Antireflective coatings comprising (i) a silsesquioxane resin having the formula (PhSiO(3-x)/2(OH)x)mHSiO(3-x)/2(OH)x)n(MeSiO(3-x)/2(OH)x)p where Ph is a phenyl group, Me is a methyl group, x has a value of 0, 1 or 2; m has a value of 0.01 to 0.99, n has a value of 0.01 to 0.99, p has a value of 0.01 to 0.99, and m+n+p=1; (ii) a polyethylene oxide fluid; and (iii) a solvent; and a method of forming said antireflective coatings on an electronic device.Type: GrantFiled: December 7, 2006Date of Patent: September 11, 2012Assignee: Dow Corning CorporationInventors: Peng-Fei Fu, Eric Scott Moyer
-
Publication number: 20120225228Abstract: An air bag coated with a cured organopolysiloxane composition, characterized in that the air bag is top coated with an antifriction coating comprising at least one solid lubricant dispersed in an organic polymer binder.Type: ApplicationFiled: November 12, 2010Publication date: September 6, 2012Inventors: Marita Barth, William Blackwood, Vittorio Clerici, Andrew William Mountney
-
Patent number: 8257797Abstract: The general field of the invention is that of airbags. The invention relates to a process for improving the tear strength and the combing strength of coated fabrics intended for uses in the field of inflatable bags using a silicone composition comprising an additive containing a polyorganosiloxane resin (V) and a calcium carbonate. After coating the composition onto the fabric supports and curing, the coated supports not only have optimum adhesion and crease resistance properties, but also have good properties in terms of combing strength and tear strength.Type: GrantFiled: November 2, 2004Date of Patent: September 4, 2012Assignee: Bluestar Silicones FranceInventors: Laurent Dumont, Alain Pouchelon
-
Patent number: 8252101Abstract: The invention is a method and composition for polishing a wet surface. The invention is a water based composition for polishing wet surfaces and a method of applying the water based composition to polish wet surfaces. The method does not include a dry to haze or buffing step in order to achieve a lasting high gloss shine on the polished surface.Type: GrantFiled: November 11, 2011Date of Patent: August 28, 2012Inventor: Roman A. Glemba, Jr.
-
Publication number: 20120214925Abstract: This invention relates to the use of silyl terminated organic polymers in phenylorganosiloxane based silicone sealant formulations containing silyl terminated organic polymers are described. Subsequent to cure the compositions, provide sealants exhibiting superior mechanical properties, particularly with respect to elongation, tensile strength and adhesion on glass. The composition comprises a phenylorganosiloxane having terminal groups selected from —OH or hydrolysable groups and unsaturated groups. Typically the phenylorganosiloxane has a viscosity of at least 10000 mPa.s at 25° C. Other ingredients include either: (i) one or more organic polymers having terminal and/or pendent silyl groups containing —OH functional groups or hydrolysable functional groups, or (ii) one or more organic polymers having terminal and/or pendent silyl groups containing one or more unsaturated groups, selected in accordance with the terminal groups of (a) as well as fillers, cross-linkers and catalyst.Type: ApplicationFiled: October 22, 2010Publication date: August 23, 2012Applicant: Dow Corning CorporationInventors: Frederic Gubbels, Stephanie Lobry, Loriane Parisot, Anne-Marie Van Stiphoudt
-
Publication number: 20120214007Abstract: A composition for coating paper includes at least one pigment selected from the group consisting of polymeric pigments, aluminosilicates, calcium carbonate, titanium dioxide, talc, barium sulfate, zinc oxide, aluminum trihydrate, amorphous silica and silicates; wherein the pigment is dispersed in an aqueous dispersion of a polymeric binder that is a copolymer of vinyl acetate, ethylene, at least one ethylenically unsaturated sulfonic acid or salt thereof and optionally one or more other monomers, wherein vinyl acetate units constitute in a range of 70-90 wt % of the polymeric binder and ethylene units constitute in a range of 10-30 wt % of the polymeric binder; and wherein the polymeric binder has a mean particle size in a range from 0.1 ?m to 0.Type: ApplicationFiled: February 18, 2011Publication date: August 23, 2012Applicant: Wacker Chemical CorporationInventors: Christian Leonard Daniels, John Richard Boylan
-
Publication number: 20120213935Abstract: Sol gel process for producing hydrophobic transparent films for polymeric substrates, the process relates to the sol-gel reaction of silicon alkoxide carried out in certain conditions. The sols obtained were, without limiting, spin- or dip-coated onto polymeric substrates then thermally cured into transparent-abrasion resistant coating. Such coating transmit visible light, but absorb wavelengths of ultraviolet light which cause degradation of the substrate surface and resultant adhesion-loss of the protective coating upon weathering.Type: ApplicationFiled: April 27, 2012Publication date: August 23, 2012Applicant: Evonik Degussa GmbHInventors: Daniele FREGONESE, Fulvio COSTA
-
Publication number: 20120214003Abstract: This invention relates to a process for applying a shatterproof coating to the surface of a glass item, comprising the following steps: (a) applying, on at least one portion of the surface of a glass item, a polymerisable composition comprising (i) a resin selected from the group consisting of polyurethane resins, polyester resins, acrylic resins, silicone resins and/or their mixes, in water or in an organic solvent; (ii) an adhesion promoter based on an organosilane compound; (iii) possibly a UV photo-initiator; (b) evaporating the water or the organic solvent; (c) polymerising said composition, forming on the glass item a shatterproof coating film capable of containing the dispersion of the glass fragments that may form in the event of the breakage of the item. The process also preferably comprises a step for the application of an additional anti-wear coating film on top of the shatterproof coating.Type: ApplicationFiled: February 16, 2012Publication date: August 23, 2012Applicant: BORMIOLI LUIGI S.P.A.Inventor: Simone Baratta
-
Patent number: 8247067Abstract: A coating composition, coated articles, and methods of coating, wherein the composition includes: a resin system comprising a polysilazane and optionally a polysiloxane and/or optionally an aromatic hydrocarbon; and glass particles having a softening point below operating temperature, a coefficient of thermal expansion of at least 80, and a dielectric constant of at least 5.Type: GrantFiled: October 12, 2005Date of Patent: August 21, 2012Assignee: Valspar Sourcing, Inc.Inventor: Carl L. Cavallin
-
Publication number: 20120208033Abstract: A barrier film is disclosed that includes a polymeric film substrate and at least first and second polymer layers separated by an inorganic barrier layer. The first polymer layer is disposed on the polymeric film substrate. At least one of the first or second polymer layers is prepared from co-deposited amino silane and acrylate or methacrylate monomer. A method of making the barrier film is also disclosed.Type: ApplicationFiled: April 23, 2012Publication date: August 16, 2012Inventors: Mark D. Weigel, Mark A. Roehrig, Alan K. Nachtigal
-
Publication number: 20120208029Abstract: Organosilane condensates are described as well as their use in coating compositions, processes for making them and process for applying the coating compositions. The organosilane condensates can be formed from the hydrolysis of at least one medium to long chain trialkoxy silane compound, an amino silane and optionally one or more additional reactants. Coating compositions containing the organosilane condensates can provide coatings having improved scratch and mar resistance and can have excellent recoat adhesion.Type: ApplicationFiled: October 5, 2010Publication date: August 16, 2012Applicant: E. E. DU PONT DE NEMOURS AND COMPANYInventor: Jun Lin
-
Publication number: 20120208034Abstract: Films or other articles having a barrier coating derived from a concentrated nanocomposite dispersion which includes a silicate filler and a matrix polymer dispersed in an aqueous medium. The dispersions are condensed by selectively removing liquid therefrom to provide high solids coating formulations.Type: ApplicationFiled: April 23, 2012Publication date: August 16, 2012Inventors: Carrie A. Feeney, Harris A. Goldberg, Michele Farrell, Douglas P. Karim
-
Patent number: 8241707Abstract: This invention pertains to silsesquioxane resins useful in antireflective coatings wherein the silsesquioxane resin is comprised of the units (Ph(CH2)rSiO(3?x)/2(OR?)x)m (HSiO(3?x)/2(OR?)x)n (MeSiO(3?x)/2(OR?)x)o (RSiO(3?x)/2(OR?)x)p (R1SiO(3?x)/2(OR?)x)q where Ph is a phenyl group, Me is a methyl group; R? is hydrogen atom or a hydrocarbon group having from 1 to 4 carbon atoms; R is selected from a hydroxyl producing group; and R1 is selected from substituted phenyl groups, ester groups, polyether groups; mercapto groups, and reactive or curable organic functional groups; and r has a value of 0, 1, 2, 3, or 4; x has a value of 0, 1 or 2; wherein in the resin m has a value of 0 to 0.95; n has a value of 0.05 to 0.95; o has a value of 0.05 to 0.95; p has a value of 0.05 to 0.5; q has a value of 0 to 0.5; and m+n+o+p+q?1.Type: GrantFiled: February 3, 2009Date of Patent: August 14, 2012Assignee: Dow Corning CorporationInventors: Peng-Fei Fu, Eric Scott Moyer
-
Patent number: 8241744Abstract: This surface-treated metal material includes a composite film obtained by applying a metal surface treatment agent on a surface of a metal material and drying the metal surface treatment agent, the metal surface treatment agent containing: an organic silicon compound (W) obtained by combining a silane coupling agent (A) containing one amino group in a molecule and one glycidyl group in a molecule, at a solid content mass ratio [(A)/(B)] of 0.7 to 1.7; at least one kind of fluorine compound (X) selected from titanium hydrofluoric acid and zirconium hydrofluoric acid; a phosphoric acid (Y); a vanadium compound (Z); and at least one kind of lubricant (J).Type: GrantFiled: November 14, 2007Date of Patent: August 14, 2012Assignee: Nippon Steel CorporationInventors: Ikuo Kikuchi, Kimitaka Hayashi, Yoshio Kimata, Atsushi Morishita, Taihei Kaneto, Shinji Nomura, Hidehiro Yamaguchi