Abstract: The present invention relates to polyurethane powder lacquers with optimized flow behavior, a process for their production, a process for coating substrates with these powder lacquers, as well as substrates coated with these powder lacquers.

Abstract: Provided is a chromium-free metal surface treatment agent excellent in rust inhibitive performance which can be used in a surface treatment of metal products, in particular, galvanized metal products. The metal surface treatment agent consists essentially of a siliceous binder solution comprising water and/or alcohol as a solvent, and the concentration of the silica component is 8 to 25% by weight. In particular, a metal surface treatment agent containing an alcoholic solution of alkoxysilane oligomer having a weight averaged molecular weight of 1000 to 10000, which is obtained by hydrolyzed condensation polymerization of alkoxysilane, can suppress the occurrence of white rusting for a long time. It is preferred that 3 to 25 parts by weight of a dispersed nano-sized titanium dioxide powder having an average primary particle size of not more than 70 nm, per 100 parts by weight of the silica component be suspended in the siliceous binder solution.

Abstract: A acrylic fiber having property modifying constituents such as thermoregulatory activity, antimicrobial activity, and perfumed and a method of making thereof is disclosed. Micro-reservoirs are formed in the fibers having thermoregulatory activity, antimicrobial constituents, and perfumed constituents.

Abstract: The invention relates to a composition containing, in relation to the total weight of said composition, A) between 50.0% by weight and 99.5% by weight of at least one (meth)acrylate (co)polymer and B) between 0.5% by weight and 50.0% by weight of at least one copolymer, obtained by the polymerisation of a monomer mixture consisting of i. between 70% by weight and 92% by weight of a vinyl aromatic monomer and ii. between 8% by weight and 30% by weight of acryl nitrile or methacryl nitrile or mixtures thereof iii. between 0% by weight and 22% by weight of at least one other monomer, the composition having at 50° C. a ?E of less than 0.15, ?E being defined according to the relationship (1): (1) in which ?L*: the modification of the colour co-ordinates L* compared with the colour co-ordinates L* at 23° C., ?a*: the modification of the colour co-ordinates a* compared with the colour co-ordinates a* at 23° C., ?b*: the modification of the colour co-ordinates b* compared to the colour co-ordinates b* at 23° C.

Abstract: Lubricant compositions and processes for producing such lubricant compositions. More specifically, low viscosity lubricant compositions for the working surface of an extrusion die during the processing of plastics that require lubricants to render them processable, such as polyvinyl chloride, chlorinated polyvinyl chloride, polyvinylidene chloride and copolymers thereof. The lubricant composition may include up to about 70% by weight of at least one metal salt while maintaining a melt viscosity low enough to process on conventional finishing equipment such as prill towers or pastillating equipment.

Abstract: Use of mixtures, comprising a total of at least 50% by weight of n-alkanols, selected from n-C24-C34 alkanols, as additive in the processing of thermoplastic polymers.

Abstract: An aqueous inkjet ink composition suitable for printing on a hydrophobic surface such as a vinyl surface including an aqueous vehicle, a self-dispersed pigment, a silicone-containing surfactant and an aqueous emulsion polymer having a glass transition temperature (Tg) of from ?40° C. to 150° C. Also provided is a method for printing an image on a hydrophobic substrate.

Abstract: Aqueous dispersions of water-insoluble polyolefin-based adhesion promoters are formed by dissolving the adhesion promoter in at least one olefinically unsaturated monomer, forming a mini-emulsion with high shear in the presence of water, surfactant and other additives, and then polymerizing the monomer with a monomer-soluble, substantially water insoluble radical initiator. The polymerized product, a stable dispersion (latex) of polyolefin adhesion promoter and polymerized monomer in water, is useful as a primer or as an additive for improving the adhesion of coatings to polyolefin substrates.

Abstract: Thermoplastic compositions comprising polyacrylonitriles that contain greater than 90% acrylonitrile as monomer, or copolymers of such polyacrylonitriles with an olefinic unsaturated co-monomer, can be formed by the use of certain compatibilizers and/or thermal stabilizers. Other thermoplastic compositions comprising the high nitrile polyacrylonitriles can be obtained by melt blending the polyacrylonitriles with certain aromatic engineering thermoplastic polymers in the presence of compatibilizers and thermal stabilizers. All of the foregoing high nitrile compositions have been found to possess good optical and gas barrier properties, and good stress crack resistance.

Abstract: This invention relates to the preparation of a cis 1,4-polyisoprene rubber-rich rubber composition containing precipitated silica which has been pre-treated with a fatty alcohol and/or epoxidized soybean oil together with an organosilane containing polysulfide coupling agent and to tires having at least one component comprised of such rubber composition.

Abstract: A jettable non-curable support material composition useful for three-dimensional ink jet printing comprising at least one fatty alcohol and at least one abietic rosin ester alcohol, wherein the support material has a melting point between about 50° C. to about 65° C. and a freezing point between about 45° C. to about 55° C.

Abstract: The invention relates to a polymer mixture, based on the (meth)acrylate (co)polymer components a.), b.), c.) and/or d.) according to claim 1, where a test specimen produced from the polymer mixture simultaneously has the following properties: a tensile modulus (ISO 527) of at least 2 500 MPa, a Vicat softening point VSP (ISO 306-350) of at least 110° C., an impact resistance (ISO 179-2D, flatwise) of at least 30 kJ/m2, and a melt index MVR (ISO 1133, 230° C./3.8 kg) of at least 1.0 cm3/10 at least The invention further relates to injection mouldings and to the use of the polymer mixture for production of injection mouldings.

Abstract: The current invention relates to a coating composition comprising a polyisocyanate compound, a hydroxyl-functional film-forming polymer, and a non-volatile branched monoalcohol. An aliphatic branched monoalcohol is preferred. More preferred are long chain non-volatile branched monoalcohols. This results in coating compositions that have improved flow behavior and that produce coatings having improved appearance without an adverse effect on other properties. The invention also relates to a multi-component coating composition. Preferably, the multi-component coating composition is a two-component coating composition comprising a polyisocyanate component and a hydroxyl-functional component, wherein the hydroxyl-functional component, in addition to the hydroxyl-functional film forming polymer also comprises the non-volatile branched monoalcohol.

Abstract: The invention provides a polymer composition comprising cross-linked polyethylene having a non-polar biocompatible lipid disposed in at least a portion of the free volume of the polyethylene. The invention further provides methods for making the polymer composition.

Abstract: A 2-methoxyphenol derivative may be used as an ultraviolet (UV) light absorbing dispersant and, an ink composition may include the 2-methoxyphenol derivative as a light-resistant dispersant. The 2-methoxyphenol derivative absorbs UV light and thus provides light resistance to outputs. The 2-methooxyphenol derivative also improves dispersibility. When the 2-methoxyphenol derivative is used to prepare an ink composition, the ink composition has improved dispersibility and light resistance, and there is no need to add a light-resistant additive.

Abstract: A positive type resist composition comprising: (A) a resin having a monocyclic or polycyclic alicyclic hydrocarbon structure, which increases the solubility in an alkali developing solution by the action of an acid; (B) a compound capable of generating an acid upon irradiation with an actinic ray or a radiation; and (C) an alkoxy alcohol as a solvent, wherein an alkoxy group and an alcoholic hydroxyl group are connected to each other via at least three carbons.

Abstract: A jettable non-curable support material composition useful for three-dimensional ink jet printing comprising at least one fatty alcohol and at least one abietic rosin ester alcohol, wherein the support material has a melting point between about 50° C. to about 65° C. and a freezing point between about 45° C. to about 55° C.

Abstract: To an aqueous PTFE polymer emulsion having a PTFE content of from 10 to 50 mass % obtained by emulsion polymerization of tetrafluoroethylene in the presence of an anionic perfluorocarboxylate surfactant (APFC), from 2 to 20 mass %, based on the mass of PTFE, of a nonionic surfactant having an average molecular weight of from 450 to 800 and an inorganic/organic property ratio of from 1.07 to 1.50 and from 10 to 800 mass %, based on the mass of PTFE, of water are added to obtain an aqueous PTFE dispersion having a PTFE content of from 1 to 40 mass % of PTFE, and then PTFE is concentrated by sedimenting the PTFE and separating a PTFE-rich aqueous dispersion composition from the supernatant. According to the present invention, a PTFE-rich aqueous dispersion composition having a low APFC concentration can be obtained.

Abstract: A golf ball is manufactured by molding and vulcanizing a rubber composition comprising 100 pbw of a base rubber composed primarily of a polybutadiene having a cis-1,4 content of at least 60 wt % and a Mooney viscosity of at least 30 and synthesized using a rare-earth catalyst, 15–50 pbw of an unsaturated carboxylic acid and/or a metal salt thereof, at least 2 pbw of a processing aid having a highest melting point of up to 115° C., and 1–5 pbw of an organic peroxide. The golf ball can be efficiently manufactured and has excellent rebound characteristics.

Abstract: The invention provides a film that includes chloride-containing vinyl polymer and a stabilizer component, wherein the film has a 96-hour Volatile Organic Compound Emission Factor of no more than 1,000 ?g/m2/hour. The invention also provides a film that includes vinyl chloride polymer and a stabilizer component comprising a stabilizer and a diluent, wherein the diluent comprises a monohydric alcohol having 12 or more carbon atoms. Also described are methods of stabilizing a chloride-containing vinyl polymer film, a system for providing a low VOC releasing chloride containing vinyl polymer film, and methods of printing a chloride-containing vinyl polymer film.

Abstract: Liquid compositions and homopolymers or copolymers of olefinically unsaturated compounds, preparable by (co)polymerizing olefinically unsaturated compounds and reactive diluents for thermally curable multisubstance mixtures as reaction medium, and their use to prepare coating compositions, adhesives and sealing compounds.

Abstract: A process for the production of a colored resin composition, comprising a step (A) of producing an aqueous slurry of a pigment, a step (B) of producing a melting composition of metallocene type polyolefin containing a dispersant and a solvent, a step (C) of kneading the aqueous slurry obtained in the step (A) with the melting composition obtained in the step (B) and a step (D) of removing the solvent and the water from the kneaded mixture obtained in the step (C), a colored composition obtained in the above process has excellent in pigment dispersibility and high color developing properties, a colored resin molded article obtained from the colored resin composition do not give a physical-properties inhibition of 5% or higher and has a color developing properties.

Abstract: The present invention provides pigmented inks comprising self-dispersing pigment and an amino-containing compound. The addition of an amino-containing compound to the self-dispersing pigment can improve the reliability and performance of the ink in an inkjet printhead. The present invention also provides methods for making a surface modified pigment comprising associating a self-dispersing pigment with an amino-containing compound having no more than one primary amino group or one secondary amino group.

Abstract: This invention relates generally to water resistant peelable protective and decorative clear or pigmented coating compositions and, more specifically, to solvent and aqueous based, polymeric coating compositions which form a protective and/or decorative coating on a variety of substrates, including automotive paints, metals, plastics, concrete, natural and synthetic elastomers, and ceramics. The coatings are be formulated for temporary or long term protection depending upon the application.

Abstract: A golf ball is characterized by comprising a molded and vulcanized product of a rubber composition as a constituent component, the rubber composition comprising 100 pbw of a base rubber composed primarily of a polybutadiene containing at least 60 wt % of cis-1,4-bond, having a Mooney viscosity (ML1+4, 100° C.) of at least 30, and synthesized using a rare-earth catalyst, 15-50 pbw of an unsaturated carboxylic acid and/or a metal salt thereof, at least 2 pbw of a processing aid having a highest melting point of up to 115° C., and at least two organic peroxides including an organic peroxide having the shortest half-life at 155° C. designated (a) and another organic peroxide having the longest half-life at 155° C. designated (b), a ratio of half-lives (bt/at) being at least 7 wherein at is the half-life of (a) and bt is the half-life of (b), a total content of the organic peroxides being 0.1-0.9 pbw per 100 pbw of the base rubber.

Abstract: Known intermediate foils for compound glasses with improved sound insulation consist of several layers or special materials which cannot be further processed in conventional plants. The aim of the present invention is to provide an intermediate foil for compound glasses with improved sound insulation, whereby said foil consists of one layer as far as possible and is based upon PVB. Said intermediate foil allows for an improved sound insulation of the compound glasses in room temperature and has essentially unchanged working properties, whereby said compound glasses are produced from the intermediate foil. To resolve the aim of the invention, an intermediate foil is provided which contains: 50 to 80 wt. % PVB (partially acetalised polyvinyl alcohol), 20 to 50 wt. % of a softener mixture containing 30 to 70 wt.

Abstract: Organopolysiloxane gel products having a variety of physical forms and which produce a silky feel when applied to the skin are prepared by reacting an unsaturated organopolysiloxane resin, an Si—H functional organosiloxane crosslinker bearing pendant hydrido functionality, a C4 or higher unsaturated hydrocarbon, and optionally, an unsaturated hydrophile component. Products ranging from viscous liquids, creamy gels, pastes, and soft powders may be obtained. The products are highly useful in formulating cosmetic and pharmaceutical products.

Abstract: A silicone composition for preparing a cured silicone product, the composition prepared by mixing: (A) an organopolysiloxane containing an average of at least two epoxy-functional organic groups per molecule; (B) a curing agent in an amount sufficient to cure the composition, provided the curing agent is free of phenolic hydroxy groups; (C) an electrically conductive filler in an amount sufficient to impart electrical conductivity to the silicone product, wherein the filler comprises particles having at least an outer surface of a metal selected from silver, gold, platinum, palladium, and alloys thereof; and (D) an effective amount of a hydroxy-functional organic compound having a molecular weight up to about 1000 and containing at least one hydroxy group per molecule, provided the compound does not substantially inhibit cure of the composition. A cured silicone product and a multi-part silicone composition.

Abstract: The use of an aromatic-free solvent mixture which consists of or comprises

Abstract: The present invention relates to a pigment dispersion and a method of producing a pigment dispersion by grinding a grind mixture comprising a pigment, a humectant, water, and a polymeric dispersant. The invention also relates to an ink composition comprising an aqueous carrier and a pigment dispersion produced by grinding a grind mixture comprising a pigment, a humectant, water, and a polymeric dispersant. The invention also relates to an ink composition comprising a pigment, a polymeric dispersant, a humectant, a basic dye, an aqueous carrier, wherein the pH of the ink composition is less than or equal to 7.

Abstract: A high tear strength, low compression set, low cost heat curable silicon elastomer.

Abstract: A metallic gloss image composition including a hydromorphic solvent and a polsulfurnitride derivative dissolved in the hydromorphic solvent. The polysulfurnitride derivative has the following formula: R1—(—S═N—)n—R2. Instead of the hydromorphic solvent, a thermoplastic renis formed by polymerization of monomers can be used to obtain the metallic gloss image composition.

Abstract: The present invention provides a process for preparing an overbased barium complex and an overbased barium complex prepared thereby. The process includes the steps of: heating a mixture of barium hydroxide monohydrate and an isomeric mixture of from about C10 to about C15 alcohols in the presence of a solvent, thereby producing a first mixture; contacting the first mixture and an isomeric mixture of from about C8 to about C10 branched carboxylic acids, thereby producing a second mixture which includes unreacted barium hydroxide; and contacting the second mixture and carbon dioxide, thereby producing the overbased barium complex. The overbased barium complex of the present invention is useful in the stabilization of halogen-containing polymers.

Abstract: A water-soluble resin composition is provided which comprises (i) 100 parts by weight of a polyvinyl alcohol polymer having a 1,2-glycol linkage content of at least 1.8 mole percent and a degree of hydrolysis of at least 90 mole percent, (ii) 1 to 50 parts by weight of a plasticizer and (iii) 5 to 50 parts by weight of a monosaccharide and/or a polysaccharide, optionally together with (iv) 1 to 20 parts by weight of an inorganic filler. Also provided is a water-soluble resin composition which comprise (i′) 100 parts by weight of a polyvinyl alcohol polymer having a 1,2-glycol linkage content of at least 1.8 mole percent and a degree of hydrolysis of 92 to 99 mole percent, (ii′) 1 to 50 parts by weight of a plasticizer and (iv′) 1 to 20 parts by weight of an inorganic filler, optionally together with (iii′) 5 to 50 parts by weight of a monosaccharide and/or polysaccharide. Further provided are water-soluble films produced by using those water-soluble resin compositions.

Abstract: The invention relates to novel blocked aliphatic polyisocyanate cross-linking agents and use thereof in one-component stoving lacquers, in particular for the coil coating process.

Abstract: A jettable non-curable support material composition useful for three-dimensional ink jet printing comprising at least one fatty alcohol and at least one abietic rosin ester alcohol, wherein the support material has a melting point between about 50° C. to about 65° C. and a freezing point between about 45° C. to about 55° C.

Abstract: Disclosed is a coloring resin composition comprising a dispersing agent, a pigment and a thermoplastic resin, in which the dispersing agent is expressed by the following Formula 1 and the thermoplastic resin is metallocene polyolefin: CnH2n+1(OCH2CH2)mOH  Formula 1 wherein n is an integer of 26 to 50, and m is an integer of 4 to 100. The composition is useful in coloring molded articles of thermoplastic resin. Colored resin molded articles using the composition are also disclosed.

Abstract: A mixture of hydroxy-terminated hydrocarbons useful as a mold release agent for polymers is disclosed. The polymers suitable in the present context are the ones prepared by polyaddition or polycondensation, in particular, thermoplastic polyurethane and polyurethane urea.

Abstract: A method for making a bloom-free thermoplastic polyurethane is disclosed. The method entails blending a chain terminator such as monofunctional alkylene alcohol having at least 14 carbon atoms, mono-isocyanate and mono-amine, in a thermoplastic polyurethane that would, but for the blending of the chain terminator of the invention, feature a blooming defect. The polyurethane suitable for the use in the inventive process is the product of a reaction wherein reactants comprise (i) at least one hydroxy functional polyol such as polyester polyol, polyether polyol and polycarbonate polyol, having a number average molecular weight of 500 to 5000 and a hydroxyl functionality of at least 2, (ii) a chain extending compound, and (iii) an organic diisocyanate. The ratio NCO/H characterizing the relative amounts of named reactants is 0.95 to 1.05. The addition of the chain terminator renders the product bloom-free.

Abstract: A composition comprising from 30 to 65 wt % of fine particles of PTFE, and, based on PTFE, from 2 to 12 wt % of C10H21CH(CH3)CH2O(C2H4O)9C3H6OH and at least 0.01 wt % and less than 1 wt % of a polyethylene oxide having an average molecular weight of from 100,000 to 2,000,000.

Abstract: Organopolysiloxane gels containing gel-bound hydrophillic groups are prepared by reacting a hydrosilylatable unsaturated organopolysiloxane resin, a crosslinker bearing Si—H bound hydrogen, and a hydrosilylatable unsaturated hydrophile, in the presence of an effective amount of a hydrosilylation catalyst, at least a portion of the reaction taking place in the presence of at least 60 weight percent of an oleaginous composition containing at least 50 weight percent low viscosity organopolysiloxane. When sheared, the crosslinked organosiloxane compositions form a stable, preferably incompatible gel which may be used in turn to form a stable emulsion with large amounts of ordinarily incompatible hydrophillic liquids. The emulsions thus formed are suitable for use in a wide variety of cosmetic products.

Abstract: There is disclosed a method for improving the abrasion resistance of a cured rubber composition that is particularly suited for a tire tread compound comprising (a) dispersing from 1.0 phr to 30 phr of a C12-C36 alcohol and from 0.5 to 2.0 phr of sulfur throughout a dry isolated sulfur-vulcanizable rubber and (b) curing the rubber.

Abstract: A process is disclosed for the production of compounds based on hydrolyzable silanes containing epoxy groups. The process involves adding one of the following substances to a pre-hydrolyzed silicon compound A with at least one hydrolytically non-separable group which includes an epoxy ring: i) a particulate substance B which can be selected from oxides, oxyhydrates, nitrides or carbides of Si, Al and B, and of transition metals, the particle size being 1-100 nm; ii) a surface-active agent, preferably non-ionic; iii) an aromatic polyol with an average molecular weight not exceeding 1000. The compounds obtained through this process can be used to produce coatings and molded bodies with a range of properties, in particular high scratch resistance, lasting hydrophilic characteristics, corrosion resistance, good adhesion and transparency.

Abstract: There are disclosed a gel or polymer composition which comprises 100 parts by weight of a polymer blend component comprising 1 to 90% by weight of a poly(vinyl aromatic hydrocarbon) polymer having a syndiotactic configuration and 99 to 10% by weight of a rubbery elastomer and at least 30 parts by weight of an extender oil or a low molecular weight organic component. These gel compositions have super soft properties, heat resistance, and/or damping properties.

Abstract: Novel silicon-containing organic fluoropolymers which are appliable to materials over a wide range and which have excellent antifouling property. The silicon-containing organic fluoropolymer of the invention is represented by the general formula and has a number average molecular weight of from 5×102 to 1×105: wherein Rf represents perfluoroalkyl; Z represents fluoro or trifluoromethyl; a, b, c, d and e each independently represent 0 or an integer of 1 or above, provided that a+b+c+d+e is not less than 1 and the order of the repeating units parenthesized by subscripts a, b, c, d and e occurring in the formula is not limited to that shown; Y represents hydrogen or alkyl containing 1 to 4 carbon atoms; X represents hydrogen, bromo or iodo; R1 represents hydroxy or a hydrolyzable substituent group; R2 represents hydrogen or a monovalent hydrocarbon group; 1 represents 0, 1 or 2; m represents 1, 2 or 3; and n represents an integer of 2 or above.

Abstract: The invention concerns a polyacrylamide-containing composition which is characterized in that it has a molecular weight of between 2,000 and 8,000 g/mol, determined by means of gel permeation chromatography (GPC), and as a 15% aqueous solution still has a Brookfield viscosity of between 100 and 500 mPas at 25° C. The invention further concerns the use of this polyacrylamide-containing composition for the flat bonding of water absorbent and hard surfaces and for equipping plastic surfaces with non-slip protection.

Abstract: A fine cell-containing polyester film of the present invention comprises 70 to 97% by weight of a polyester and 3 to 30% by weight of a thermoplastic resin immiscible with polyester and produced by stretching at least one direction, the difference in gloss between opposite surfaces of said polyester film being not less than 3%, and a gloss of one surface of said polyester film being not less than 25%. Such a fine cell-containing polyester film is excellent in gloss, printability, transport property and/or flexibility.

Abstract: The present invention provides thermoplastic ophthalmic lens blocking compositions that have many advantages over traditional metal alloy materials. Preferred compositions comprise a blend of a homopolymer or copolymer of epsilon-caprolactone with a modifier selected from the group consisting of carboxylic; straight chain monohydric alcohols; branched chain monohydric alcohols; polyethylene glycols; and polyethylene glycol ethers. The composition may also comprise one or more fillers or heat absorbing materials. In one embodiment, the composition is used to fill the cavity between a preformed lens block and a lens. In another embodiment the composition is used to form a lens block. Methods of holding a lens blank are taught. Tapes that provide a receptive surface against which the composition may be adhered are disclosed.

Abstract: The organopolysiloxane compositions are prepared by mixing(1) organopolysiloxanes which contain on average at least 2 aliphatic carbon-carbon multiple bonds per molecule,(2) prehydrophobized oxidic reinforcing fillers having a carbon content, obtained by the hydrophobizing, of at least 0.5% by weight and(3) compounds which are chosen from(3a) silanol compounds of the formulaR--[SiR.sub.2 --O--].sub.a H (I)in whichR is identical or different monovalent, C.sub.1 - to C.sub.10 -hydrocarbon radicals which are free from aliphatic carbon-carbon multiple bonds anda has values from 1 to 10, and(3b) saturated C.sub.1 - to C.sub.18 -alkanols.

Abstract: Room temperature stable aqueous dispersions of ketone resins are prepared by dissolving poly(ethylene oxide) resin and optionally surfactant in the aqueous medium mixed with the ketone resin. Coating formulations with these dispersions can contain additional co-dispersed components such as waxes, additional resins and/or pigments. The coating formulations can provide thermal transfer layers of thermal transfer ribbons which contain both wax and ketone resins.