Patents Assigned to Baoshan Iron & Steel Co., Ltd.
-
Patent number: 9662723Abstract: A method for combined shearing of a steel plate adopts a combination of unrolling and pendulum shearing with laser cutting, wherein after a steel roll is cut by unrolling and pendulum shearing to obtain sheets having a specified length, a part or all of the sheets are directly conveyed to a stack as finished sheet materials and the other part or all of the sheets are transferred to a laser cutting line by means of lateral material discharge from a unrolling and pendulum cutting line, and are picked up by a loading robot and moved to a laser cutting position to subject to a secondary cutting, so as to finally obtain profiled sheet materials which are picked up by a discharged material handling and stacking robot for an operation of stacking the finished products.Type: GrantFiled: April 28, 2014Date of Patent: May 30, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Saidan Yang, Junliang Qiao, Qi Yan, Shengbo Pan, Ruimin Wu, Chengguo Jin, Qian Xiang
-
Patent number: 9663840Abstract: A 500 MPa grade longitudinally welded steel pipe with a low yield ratio and a manufacturing method therefor, the components thereof by weight percentages being as follows: C 0.11%-0.16%, Si 0.15%-0.35%, Mn 0.8%-1.5%, V 0.06%-0.15%, Al 0.002%-0.04%, Ti 0%-0.05%, Nb 0%-0.05%, the balance being Fe and inevitable impurities, and the carbon equivalent Ceq being not more than 0.4%. According to the above component design, molten steel is subjected to smelting in a converter or electric furnace, and is cast into a slab; the slab is heated at 1,200° C.-1,300° C. and rolled into a plate strip, with the finished rolling temperature of the plate strip being between 840° C.-940° C.; the rolled plate strip is subjected to laminar flow cooling with a water curtain, the laminar flow cooling adopting the manner of rear-section cooling, and is coiled into a plate roll when being cooled to the temperature interval of 500° C.-560° C.Type: GrantFiled: October 9, 2013Date of Patent: May 30, 2017Assignee: BAOSHAN IRON & STEEL CO., LTDInventors: Qingchao Tian, Hongde Shi, Huaizhong Wang, Qijiang Wang
-
Patent number: 9659694Abstract: Disclosed are a non-oriented electrical steel plate with low iron loss and high magnetic conductivity and a manufacturing process therefor. The casting blank of the steel plate comprises the following components: Si: 0.1-2.0 wt %, Al: 0.1-1.0 wt %, Mn: 0.10-1.0 wt %, C: ?0.005 wt %, P: ?0.2 wt %, S: ?0.005 wt %, N: ?0.005 wt %, the balance being Fe and unavoidable impurities. The magnetic conductivity of the steel plate meets the following relationship formula: ?10+?13+?15?13982?586.5P15/50; ?10+?13+?15?10000, wherein P15/50 is the iron loss at a magnetic induction intensity of 1.5 T at 50 Hz; ?10, ?13, and ?15 are relative magnetic conductivities at induction intensities of 1.0 T, 1.3 T, and 1.5 T at 50 Hz, respectively. The steel plate can be used for manufacturing highly effective and ultra-highly effective electric motors.Type: GrantFiled: March 27, 2012Date of Patent: May 23, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Aihua Ma, Bo Wang, Xiandong Liu, Liang Zou, Shishu Xie, Hongxu Hei
-
Publication number: 20170114427Abstract: Method for directly producing a pickling-free hot-plated sheet strip product from molten steel comprising: obtaining a refined molten steel; thin strip continuous casting: a mixed gas of an inert gas and a reducing gas is used for protection in the billet casting process; hot rolling: the cast strip is levelled at a high temperature so as to improve the sheet shape and rolled to a suitable thickness so as to change the product specification, or provide a mechanical disruption action on the iron oxide skin on the surface of the cast strip; reduction annealing: a sectional reduction method is used to perform sectional reductions with the temperature held within two ranges, i.e., 450-600° C. and 700-1000° C., wherein the reduction is performed within a range of 450-600° C. for 1-5 minutes and within a range of 700-1000° C.Type: ApplicationFiled: December 23, 2014Publication date: April 27, 2017Applicant: BAOSHAN IRON & STEEL CO.,LTD.Inventors: Jun Li, Ning Tan, Chuang Guan, Yuan Fang, Xinjian Ma
-
Patent number: 9631958Abstract: A device for measuring the flow rate of steel melt near the surface thereof. The device has a flow rate detecting rod and a deflection device for the flow rate detecting rod. The deflection device for the flow rate detecting rod has a flow rate detecting rod counterweight, a deflection bearing sleeve, a deflection bearing, a deflection angle indicating board, a deflection angle pointer and a flow rate detecting rod fastening bolt.Type: GrantFiled: March 20, 2013Date of Patent: April 25, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Jian Yang, Jianjun Zhi, Kai Zhu, Jianhua Zhu, Zhengjie Fan, Ruizhi Wang, Jianguo Shen, Yiyu Zheng
-
Patent number: 9630242Abstract: A device for continuously measuring the flow rate of steel melt near surface thereof, comprising a flow rate detecting rod (18) and a deflection means (B) for the flow rate detecting rod, wherein the flow rate detecting rod (18) comprises a refractory material tube at one end and a stainless steel rod at the other end, and the stainless steel rod is fittedly connected with the refractory material tube. Also provided is a method for continuously measuring the flow rate of steel melt near surface thereof.Type: GrantFiled: March 20, 2013Date of Patent: April 25, 2017Assignee: Baoshan Iron & Steel Co., Ltd.Inventors: Jian Yang, Jianjun Zhi, Kai Zhu, Jianhua Zhu, Zhengjie Fan, Ruizhi Wang
-
Patent number: 9623459Abstract: The present invention relates to the field of strip cold rolling, and in particular to a thickness control method for strips in a tandem cold mill. Frame S1 and one or more additional frames are selected as virtual indirect measuring instruments for the strip performance. A load cell is provided on the frames that are selected as the indirect measuring instruments for the strip performance, and deformation resistance fluctuation of the supplied materials of the frame S is calculated. Finally, the feed-forward adjustment amount of each frame is calculated. The present invention measures the deformation resistance of each section of the strip of the supplied materials through the selected frame, reducing the fluctuation of the thickness of the finished products of the strip and ensuring stable rolling.Type: GrantFiled: May 8, 2013Date of Patent: April 18, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Jianghua Xu, Shanqing Li, Peijie Huang, Zhenglian Jiang, Kangjian Wang, Xin Wang, Hongmei Li
-
Patent number: 9623457Abstract: The present invention discloses a double cold reduction strip for shadow mask and a process for producing the same, comprising the following procedures: converter steelmaking?continuous billet casting?hot rolling?pickling and cold rolling?continuous annealing?double cold reduction?finishing and oiling. The weight percentages of essential elements of the shadow mask strip are: C: ?0.001%, Mn: 0.10˜0.40%, Al: 0.02˜0.06%, Si: ?0.025%, P: ?0.015%, S: ?0.01%, O: ?0.004%, with remainders composed of Fe and inevitable impurities.Type: GrantFiled: May 17, 2013Date of Patent: April 18, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Shoumin Wu, Xiujun Li
-
Patent number: 9604312Abstract: A fast-speed laser scoring method is provided, in which a set of related laser scoring device is used to simultaneously score lines on the upper surface and the lower surface of an oriented silicon steel strip, which is being fed and traveling forwards on a production line, with high-focalized continuous wave laser beam; the lines scored on the upper surface and the lines scored on the lower surface have the same space between every two adjacent scored lines but are staggered each other in order to reduce iron loss evenly. The space between every two adjacent scored lines on the same surface is 6-12 mm, laser power is 1000-3000 W and scanning speed is 100-400 m/min. The machining rate of the scoring method and device attains 1.5-2 times the one of conventional scoring methods which can not simultaneously score the upper and lower surfaces of a steel strip at a time. The lines scored on a steel strip by the method can reduce iron loss of the strip by 10-16%.Type: GrantFiled: April 28, 2011Date of Patent: March 28, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Wangya Huang, Guobao Li, Xinqiang Zhang, Xing Mao, Wanqing Guo, Jianru Zhu, Banglin Xiang
-
Patent number: 9566677Abstract: The present invention discloses a method of motor vehicle sheet blanking and a system of the same, wherein the blanking method comprises: firstly, nesting for motor vehicle sheet material, and cutting it into group sheets with a shape and size confirmed by the multi length of the sheet; next, designing a backing die depending on scraps to be cut from the group sheet, and hollowing in areas corresponding to blanking openings in the backing die, in which the dimensions of the blanking openings are greater than that of the actual scraps to be cut; then, placing a group sheet onto the backing die; laser cutting the group sheet based on the shape of motor vehicle sheet, the cut scraps dropping through the blanking openings in the backing die onto a scrap conveyor belt underneath; stacking the cut sheets. The present invention can effectively process scraps cut from sheets and improve the blanking efficiency.Type: GrantFiled: March 8, 2012Date of Patent: February 14, 2017Assignee: Baoshan Iron & Steel Co., Ltd.Inventors: Ruimin Wu, Wenhai Jin, Qi Yan, Chengguo Jin, Saidan Yang, Yuming Wang, Junliang Qiao, Shengbo Pan, Changqing Lv
-
Patent number: 9550229Abstract: A fluoride-free continuous casting mold flux for ultralow carbon steel, comprising the following components in weight percentage: 3-10% of Na2O, 0-3% of Li2O, 3-8% of MgO, 5-15% of MnO, 0-8% of BaO, 4-12% of Al2O3, and impurities with a content of no more than 2%, the balance being CaO and SiO2, wherein the ratio of CaO/SiO2 is 0.8-1.3; the raw materials are mixed and then pre-melted; the pre-melted mold flux requires micro-adjusting according to the component deviation, and the ratio of the pre-melted material is not lower than 70%; then a carbonaceous material of 1-3% by the total weight of the mold flux is added and mixed so as to obtain the finished product mold flux. Said mold flux has a melting point of 1100-1200° C. and a viscosity of 0.2-0.6 Pa·s at 1300° C.Type: GrantFiled: July 23, 2015Date of Patent: January 24, 2017Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Chen Zhang, Dexiang Cai, Feng Mei, Jianguo Shen
-
Publication number: 20160346877Abstract: Disclosed is a superhigh strength gas shielded welding wire, the contents of chemical elements of the superhigh strength gas shielded welding wire in percentage by mass being: C 0.06-0.12%, Si 0.55-0.80%, Mn 1.60-1.95%, 0<Cu?0.20%, Cr 0.10-0.35%, Mo 0.10-0.50%, Ni 1.00-1.60%, Ti 0.01-0.20%, B 0.0005-0.0060%, and the balance being Fe and other inevitable impurities. Accordingly, further disclosed is a method for manufacturing the welding wire. The welding wire of the present invention has a low alloy content and a low carbon equivalent, and a weld metal formed by welding with the welding wire has all of a higher strength, a greater low-temperature toughness and a better plasticity, with a good compatibility between the three properties. The weld metal formed by welding using the welding wire further has a good crack resistance and a good welding property.Type: ApplicationFiled: June 30, 2015Publication date: December 1, 2016Applicant: BAOSHAN IRON & STEEL CO., LTD.Inventors: QU Zhaoxia, XU Lei, XIA Liqian
-
Patent number: 9496078Abstract: A hot rolled silicon steel producing method comprises: silicon steel slab heating process, rough rolling process and finish rolling process. The heating process comprises a pre-heating stage, a heating stage and a soaking stage. The pre-heating stage satisfies the following formula (1). In the formula, VTp is a temperature increasing rate, in the pre-heating stage, whose unit is ° C./min; t is a total heating time of the slab in the heating furnace, and t=180-240 min; and Tc is an initial temperature when the slab is put into the furnace, whose unit is ° C. By using the foregoing formula, the heating process and the rough rolling process are changed, an occurrence rate of edge defects during the production of the hot rolled silicon steel can be reduced, and the hot rolled silicon steel with good surface quality can be produced. V Tp > 220 ? ? min t × 100 ? ° ? ? C . T C + 200 ? ° ? ? C . × 25 ? ° ? ? C .Type: GrantFiled: March 29, 2012Date of Patent: November 15, 2016Assignee: Baoshan Iron & Steel Co., Ltd.Inventors: Huawei Zhang, Yaping Wu, Yu Gong, Yezhong Sun, Hongxu Hei
-
Patent number: 9460054Abstract: A method for detecting electromagnetic property of oriented silicon steel, the method comprises: measuring Euler angles of each of crystal grains in a specimen by use of metallographic etch-pit method; calculating orientation deviation angle ?i (degree) of the crystal grain; combining area Si (mm2) of the crystal grain and correction coefficient X of element Si (X=0.1˜10 T/degree); correcting on the basis of the magnetic property B0 (saturation magnetic induction, T) of single-crystal material by using these parameters (?i, Si, X), formula for correcting is B 8 = - 0.015 × X × ? n = 1 i ? S i ? ? ? i ? ? n = 1 i ? S i + ( B 0 - 0.04 ) ( 1 ) obtaining electromagnetic property B8 of the oriented silicon steel by the above calculations.Type: GrantFiled: April 12, 2011Date of Patent: October 4, 2016Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Meihong Wu, Weizhong Jin, Huande Sun, Guohua Yang, Kanyi Shen, Jie Huang, Guobao Li
-
Patent number: 9415431Abstract: A hot rolled slab impact type mechanical scale removal device comprises a front cooling water nozzle group, an impact type scale removal gear roller group, a roller cooling device and a cleaning water nozzle group. A slab moves on a slab roller table. The front cooling water nozzle group, the impact type scale removal gear roller group and the cleaning water nozzle group are arranged in sequence along the movement direction of the slab. The impact type scale removal gear roller group is arranged on a support seat. The cooling water nozzle of the roller cooling device is arranged corresponding to the impact type scale removal gear roller group. According to the scale removal device, the oxide skins can be clearly removed, the temperature of the continuous casting slabs can be reduced and the hot rolling quality is improved.Type: GrantFiled: September 24, 2012Date of Patent: August 16, 2016Assignee: BAOSHAN IRON & STEEL CO., LTD.Inventors: Shunhua Xiang, Hongquan Wen
-
Patent number: 9406416Abstract: A method of producing an extremely thick insulation coating on a surface of an electrical steel, comprises the following steps: 1) preparing a coating liquid—stirring sufficiently the coating liquid for 0.1˜4 hours, with the viscosity of the coating liquid being within 10˜80 S; 2) coating a strip steel—using a double-roller or a tri-roller coating machine, wherein the film thickness and evenness can be controlled by adjusting different parameters; 3) baking the coating—using three sections, that is, a drying section, a baking section and a cooling section, to bake the coating, wherein the temperature in the drying section is 100˜400° C., the temperature in the baking section is 200˜370° C.Type: GrantFiled: December 14, 2011Date of Patent: August 2, 2016Assignee: BAOSHAN IRON & STEEL CO., LTDInventors: Yongqiang Lu, Chunguo Lv, Zhicheng Wang, Bin Chen, Xiao Chen, Shishu Xie
-
Patent number: 9383745Abstract: A method for controlling furnace temperature of a fired heating furnace is disclosed, comprising: measuring furnace temperatures to obtain furnace temperature feedback values; calculating the differences between furnace temperature setting values and the furnace temperature feedback values as discrepancy values DV1, in accordance with the furnace temperature feedback values and the furnace temperature setting value; calculating the differences between the furnace temperature setting values and the furnace temperature feedback values in a unit time, i.e.Type: GrantFiled: April 27, 2011Date of Patent: July 5, 2016Assignee: Baoshan Iron & Steel Co., Ltd.Inventors: Yongfeng Liu, Guoqiang Qian, Huazhong Gu, Rong Chen, Zhicheng Wang, Chunguo Lv, Dejian Wen, Peili Zhang
-
Publication number: 20160160330Abstract: The present invention discloses a superstrength cold rolled weathering steel sheet, wherein the weight percentage of the chemical elements thereof are as follows: C: 0.05˜0.16%; Mn: 1.00˜2.20%; Al: 0.02˜0.06%; Cu: 0.20˜0.40%; Cr: 0.40˜0.60%; Ti: 0.015˜0.035%; P: less than 0.03%; and C+Mn/16 is more than 0.19% and less than 0.23%; the remainders thereof being Fe and other unavoidable impurities. The present invention also discloses a method of manufacturing said superstrength cold rolled weathering steel sheet, comprising the following stages: smelting, heating and preservation, hot rolling, coiling, pickling, cold rolling, continuous annealing and skin passing. The advantages of the superstrength cold rolled weathering steel sheet and the method of manufacturing the same are: high strength, i.e.Type: ApplicationFiled: March 26, 2014Publication date: June 9, 2016Applicant: BAOSHAN IRON & STEEL CO., LTD.Inventors: Yong Zhong, Li Wang, Weijun Feng, Xiaoming He, Jnjie Huang, Yanglin Ke
-
Patent number: 9334405Abstract: The present invention refers to a chromium-free insulation coating material for non-oriented silicon steel, comprising, in parts by weight, the following components: metal dihydrogen phosphate salt of 100 parts, epoxy resin of 10˜60 parts, naphthenate drier or isooctanoate metal salt drier of 0.001˜10 parts, organic solvent of 0.001˜100 parts and pure water of 60˜2000 parts. The metal dihydrogen phosphate salt is Al(H2PO4)3, Mg(H2PO4)2, Ca(H2PO4)2 or Zn(H2PO4)2; the epoxy resin is water-soluble epoxy resin or epoxy resin emulsion. Chromium-free insulation coating material of the present invention, after being coated on non-oriented silicon steel, renders highly transparent appearance, and has excellent insulativity, corrosion resistance, adhesiveness, weldability and manufacturability, so as to eliminate defects of the existing chromium-free coating, such as sticky and un-wear-resistant and to meet environment protection requirements.Type: GrantFiled: April 13, 2011Date of Patent: May 10, 2016Assignee: Baoshan Iron & Steel Co., LTD.Inventors: Yunpeng Xu, Yongjie Yang, Dengfeng Li, Yaming Ji, Zipeng Zhao, Lingyun Chen, Xiao Chen, Jie Huang
-
Publication number: 20160122844Abstract: An HT550 steel plate with ultrahigh toughness and excellent weldability and a manufacturing method thereof are disclosed. Based on a component system with ultralow-C, high-Mn, Nb-microalloying, ultramicro Ti treatment, Mn/C is controlled in the range of 15˜30, (% Si)×(% Ceq) is less than or equal to 0.050, (% C)×(% Si) is less than or equal to 0.010, (% Mo)×[(% C)+0.13(% Si)] is in the range of 0.003˜0.020, the ratio Ti/N is in the range of 2.0˜4.0, the steel plate is alloyed with (Cu+Ni+Mo), Ni/Cu is greater than or equal to 1.0, Ca treatment is performed, and Ca/S is in the range of 0.80˜3.00; by optimizing TMCP process, the steel plate has microstructures of fine ferrite plus self-tempered bainite with an average grain size being less than or equal to 15 ?m, yield strength being 460 MPa or more, tensile strength being 550˜700 MPa, yield ratio being 0.85 or less, and ?60° C.Type: ApplicationFiled: March 26, 2014Publication date: May 5, 2016Applicant: Baoshan Iron & Steel Co., Ltd.Inventors: Zicheng Liu, Xianju Li