Abstract: The invention provides a method for producing grain-oriented silicon steel with single cold rolling, comprising: 1) smelting, refining and continuous casting to obtain a casting blank; 2) hot rolling; 3) normalization, i.e. normalizing annealing and cooling; 4) cold-rolling, i.e. single cold rolling at a cold rolling reduction rate of 75-92%; 5) decarburizing annealing at 780-880° C. for 80-350 s in a protective atmosphere having a due point of 40-80° C., wherein the total oxygen [0] in the surface of the decarburized sheet: 171/t?[O]?313/t (t represents the actual thickness of the steel sheet in mm), the amount of absorbed nitrogen: 2-10 ppm; 6) high temperature annealing, wherein the dew point of the protective atmosphere: 0-50° C., the temperature holding time at the first stage: 6-30 h, the amount of absorbed nitrogen during high-temperature annealing: 10-40 ppm; 7) hot-leveling annealing.
Abstract: A method of manufacturing oriented Si steel containing Cu with high electric-magnetic property comprises: hot rolling slab; after first cold rolling, heating it to 800° C. or higher temperature and performing intermediate decarburization annealing in a protective atmosphere with PH2O/PH2 of 0.50˜0.88 for 3-8 minutes, to decrease carbon content of the steel plate to less than 30 ppm; then peening and acid-pickling to remove oxide of Fe on surface and to control oxygen content to lower than 500 ppm; secondary cold rolling to final thickness and coating separation agent in water-slurry form; drying to decrease water content to lower than 1.5%; high-temperature annealing in a protective atmosphere containing hydrogen with oxidation degree (PH2O/PH2) of 0.0001-0.2; finally applying a tension coating and leveling tension annealing.
Type:
Application
Filed:
April 24, 2009
Publication date:
July 28, 2011
Applicant:
BAOSHAN IRON & STEEL CO., LTD.
Inventors:
Yaming JI, Huande Sun, Guohua Yang, Yongjie Yang, Yunpeng Xu, Changguo Huang, Guobao Li
Abstract: A manufacturing method of oriented Si steel with high electric-magnetic property comprises the following steps: smelting steel in converter or electric furnace; refining molten steel in two stages; continuous casting to obtain slab; hot rolling; first cold rolling; decarburizing annealing; secondary cold rolling; applying an annealing separator based on MgO and annealing at high temperature; applying an insulating coating and leveling tension annealing. The slab comprises (in wt %): C 0.020-0.050%, Si 2.6-3.6%, S 0.015-0.025%, Als 0.008-0.028%, N 0.005-0.020%, Mn 0.15-0.5%, Cu 0.3-1.2%, balance Fe and inevitable impurities, in which 10?Mn/S?20 and Cu/Mn?2. The method could produce oriented Si steel with high magnetic induction intensity and low iron loss at low cost.
Type:
Application
Filed:
March 25, 2009
Publication date:
June 16, 2011
Applicant:
BAOSHAN IRON & STEEL CO., LTD.
Inventors:
Guohua Yang, Huande Sun, Yaming Ji, Guobao Li, Hongxu Hei
Abstract: A double cavity type steel slag treatment equipment by barrel method employing mandrel support comprises left and right barrel bodies, flow branching pan, mandrel, feed funnel. Between the left and right barrel bodies is disposed a flow branching pan, over which is mounted a feed funnel and below which is mounted a retaining ring. The mandrel is fixedly connected to the left and right barrel bodies and flow branching pan, supporting bearings are mounted at two ends of the mandrel, left and right barrel bodies have inner and outer portions, inner barrel body is made of grid section, one end of grid section is fixed on the end cover of outer barrel body through an insertion opening made of supporting rings, the other end of grid section is joined with the supporting ring fixedly connected on outer barrel body.
Type:
Grant
Filed:
August 31, 2005
Date of Patent:
May 17, 2011
Assignee:
Baoshan Iron & Steel Co., Ltd.
Inventors:
Yongli Xiao, Hua Chen, Yin Liu, Yongqian Li
Abstract: A water-cooled mold for continuous casting includes two water-cooled wide copper plates arranged opposite to each other in a front and back direction and two water-cooled narrow copper plates arranged opposite to each other in a left and right direction. The upper portion of the cavity of the mold is a sprue area and the lower portion of the cavity is a mold cavity area. The sprue area is gradually narrowed in the casting direction and smoothly transited into the mold cavity, corresponding to the shape of a slab to be cast. The inside surfaces of the water-cooled narrow copper plates are smooth planar surfaces. A portion of the inside surface of the water-cooled wide copper plates in the sprue area is a curved surface and another portion in the mold cavity area is a planar surface. The curved surface and the planar surface portions form a continuous smooth surface.
Type:
Grant
Filed:
September 20, 2004
Date of Patent:
February 22, 2011
Assignee:
Baoshan Iron and Steel Co., Ltd.
Inventors:
Rongjun Xu, Xiao Liu, Yongquan Li, Jian Cui
Abstract: The present invention provides a steel plate having a low welding crack susceptibility and a yield strength of 800 MPa and a manufacturing method for the same. The steel plate having a low welding crack susceptibility comprises the following chemical components (wt. %: percent by weight): C: 0.03-0.08 wt. %, Si: 0.05-0.70 wt. %, Mn: 1.30-2.20 w.t %, Mo: 0.10-0.30 wt. %, Nb: 0.03-0.10 wt. %, V: 0.03-0.45 wt. %, Ti: 0.002-0.040 wt. %, Al: 0.02-0.04 wt. %, B: 0.0010-0.0020 wt. %, the balance being Fe and unavoidable impurities, and the welding crack susceptibility index meets the following formula: Pcm?0.20%. The thermo-mechanical controlled rolling and cooling processes is used to obtain an ultrafine bainite batten matrix structure, which increases the intensity, plasticity and toughness of the steel plate. The steel plate with a low welding crack susceptibility of the present invention has a yield strength of greater than 800 MPa, a tensile strength of greater than 900 MPa, a Charpy impact energy Akv (?20° C.
Abstract: A self-adhesive coating for electrical steel and its uses is described. The coating includes 81-99.9 weight parts of aqueous epoxy resin emulsion, 0.07-17 weight parts of curing agent, and optionally 0.3 weight parts of accelerant. The coating optionally contains additives selected from diluent, filler, toughener, colorant, fire retardant, antirusting agent, antisettling agent, thixotropic agent or antifoamer, thickener, pigment dispersant, preservative, and the like. The coating can be used as electrical steel coating. The coating is capable of making electrical steel with a self-adhesive coating by naked-flame heat, and also there are no poisonous organic solvents to volatilize during the entire process. The coating can avoid use of an apparatus for burning organic solvents, which reduced cost.
Abstract: This invention relates to metallurgical slag treatment equipments. A double cavity type steel slag treatment equipment by barrel method employing mandrel support comprises left and right barrel bodies, flow branching pan, mandrel, feed funnel. Between the left and right barrel bodies is disposed a flow branching pan, over which is mounted a feed funnel and below which is mounted a retaining ring.
Type:
Application
Filed:
August 31, 2005
Publication date:
November 6, 2008
Applicant:
Baoshan Iron & Steel Co., Ltd
Inventors:
Yongli Xiao, Hua Chen, Yin Liu, Yongqian Li