Abstract: The present invention provides an organic anti-reflection coating composition comprising a copolymer represented by the following Formula 1, a light absorbent, a thermal acid generating agent, and a curing agent: wherein R1, R2 and R3 are each independent to each; R1 represents hydrogen or an alkyl group having 1 to 10 carbon atoms; R2 represents hydrogen, an alkyl group having 1 to 10 carbon atoms or an arylalkyl group having 1 to 20 carbon atoms; R3 is hydrogen or a methyl group; m and n are repeating units in the main chain, while m+n=1, and they have values of 0.05<m/(m+n)<0.95 and 0.05<n/(m+n)<0.95. The anti-reflection coating using the polymer of the invention has excellent adhesiveness and storage stability, and a very high dry etching rate, and exhibits excellent resolution in both C/H patterns and L/S patterns.

Abstract: Disclosed are polysilazane, a method of synthesizing the polysilazane, a composition for manufacturing a semiconductor device, and a method of manufacturing a semiconductor device using the composition. The polysilazane is synthesized through a reaction, under a catalyst, between dichlorosilane, trichlorosilane, and ammonia added in a reaction solvent as a reactant. In this instance, a polystyrene conversion weight average molecular weight of the polysilazane is about 2,000 to 30,000.

Abstract: Disclosed is a photosensitive resin composition, comprising 0.1 to 20 parts by weight of a polygonal oligomeric silsesquioxane derivative, and 5 to 30 parts by weight of a compound generating acid by light, based on 100 parts by weight of a polyamide derivative.

Abstract: Disclosed herein is a novel stabilizer for preparing a polymer polyol, which is used to prepare polyurethane foam having improved physical properties. The stabilizer is prepared by allowing maleic anhydride to react with a polyether polyol, having an OH functionality of 3-8 and a molecular weight of 3,000-15,000, and then adding ethylene oxide to the reaction solution. Because the molecular weight and functionality of the stabilizer are increased through aging and dimerization, the stabilizer has a high molecular weight of 5,000-30,000, a high OH functionality of 6-10 and a viscosity of 3,000-15,000 cps/25° C. A polymer polyol derived from the stabilizer has low viscosity compared to those of prior products and contributes to the improvement in the physical properties of the resulting polyurethane foam.

Abstract: Disclosed are 1,4-polybutadiene functionalized with an aromatic organosulfur compound, providing improved processability due to decreased Mooney viscosity and providing improved feel on hitting and flying performance due to decreased compression and increased restitution when used to prepare a golf ball core, and a composition for the preparation of a golf ball core including the same.

Abstract: The present invention relates to a method of preparing N-substituted maleimide in high purity and high yield, wherein, unlike a conventional method of preparing N-substituted maleimide after preparing N-substituted maleamic acid, an organic solvent, an acid catalyst, a dehydration co-catalyst and a stabilizer are added into a reactor without separately preparing N-substituted maleamic acid, and then a primary amine is added into the reactor to form an amine salt, maleic anhydride is added into the reactor, and the resulting mixture is subjected to a dehydration-cyclization reaction, wherein water produced during the reaction is azeotropically distilled with the organic solvent so as to effectively suppress formation of a maleimide polymer.

Abstract: The present invention relates to a light absorbent for organic anti-reflection coating formation, and an organic anti-reflection film composition containing the same. The light absorbent for organic anti-reflection film formation according to the present invention is a compound of the following formula (1a), a compound of the following formula (1b), a mixture of compounds of the formulas (1a) and (1b): wherein X is selected from the group consisting of a substituted or unsubstituted cyclic group having 1 to 20 carbon atoms, aryl, diaryl ether, diaryl sulfide, diaryl sulfoxide and diaryl ketone; and R1 is a hydrogen atom, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, or an aryl group having 1 to 14 carbon atoms.

Abstract: The present invention relates to an adhesive composition comprising a mixture of multi-block copolymers, in particular, an adhesive composition comprising a block copolymer represented by Formula 1, a hydrocarbon adhesive resin and a plasticizer. The adhesive composition according to the present invention can be easily processed due to its low melting point and shows improved adhesive properties such as loop tack, 180° peel strength and holding power.

Abstract: A functional styrene-butadiene copolymer is disclosed. More specifically, the copolymer is prepared by radical polymerization of a styrene monomer, a butadiene monomer and an epoxy acrylate monomer in an emulsion state and ring-opening of the resultant styrene-butadiene-epoxy acrylate copolymer. When blended with silica, the disclosed copolymer provides excellent wet stopping performance and superior wear resistance. Therefore, it can be usefully applied for industrial materials including fuel-efficient tires, snow tires, belts, hoses, etc.

Abstract: Disclosed are a photosensitive compound and a method of manufacturing the same. The photosensitive is composed of a naphthoquinonediazide sulfonic ester compound having at least one naphthoquinonediazide sulfoxy group, and having either at least one carboxy group with 1 to 8 carbon atoms or at least one alkoxy group with 1 to 8 carbon atoms, in one molecule.

Abstract: Disclosed is a positive typed photosensitive composition including a polyamide derivative being represented by where R1 and R2 independently represent a bivalent to hexavalent aryl group with at least two carbon atoms, R3 represents either a hydrogen atom or an alkyl group with 1 to 20 carbon atoms, R4 represents either an alkyl group having a linear structure or an aryl group having a linear structure, R5 represents any one of a bivalent to hexavalent aryl group with at least two carbon atoms, an alkyl group having a linear structure, and an aryl group having a linear structure, k and l independently represent an integer of 10 to 1000, n and m independently represent an integer of 0 to 2 (n+m>0), and X represents either a hydrogen atom or an aryl group with 2 to 30 carbon atoms.

Abstract: Disclosed is a positive typed photosensitive composition including a polyamide derivative represented by the following Chemical Formula, and a heat-acid generator. where R1, R2, R4, and R5 independently represent a bivalent to hexavalent aryl group with at least two carbon atoms, R3 represents either a hydrogen atom or an alkyl group with 1 to 10 carbon atoms, k represents an integer of 10 to 1,000, 1 represents an integer of 1 to 1,000, n and m independently represent an integer of 0 to 2 (n+m>0), and X represents either a hydrogen atom or an aryl group with 2 to 30 carbon atoms.

Abstract: Disclosed are a synthetic resin composition for use as building materials such as window frames, as well as a product manufactured using the same. More particularly, the synthetic resin composition comprises a tetrapolymer of acrylic rubber-styrene monomer-butadiene rubber-vinyl cyanide monomer and a styrene-vinyl cyanide copolymer having a high molecular weight and a high degree of dispersion. Unlike products manufactured using prior polyvinyl chloride (PVC), building material such as window frames manufactured using the synthetic resin composition are recyclable, and thus can contribute to a reduction in the generation of hormone-disrupting chemical dioxin, which is released in the burning thereof. Also, the resin composition can be manufactured into products having excellent properties of weather resistance and colorability without using environmental pollutants such as cadmium stearate or lead stearate, which are used as thermal stabilizers.

Abstract: The present invention relates to a catalyst for preparing a carbon nanotube having desired apparent density by controlling the adding amount of co-precipitating agent in the process of preparing a catalyst in order to obtain a catalyst having a minimized particle size. More specifically, this invention relates to a catalyst for preparing carbon nanotube having desired apparent density based upon the reverse-correlation between the amount of co-precipitating agent added in the process of preparing catalyst and the apparent density of catalyst. The carbon nanotube prepared by the catalyst having low apparent density shows excellent electrical conductivity and highly uniformed dispersion in the polymer/carbon nanotube composite.

Abstract: The present invention relates to an organic silica master batch elastomer prepared by mixing a conjugated diene based copolymer, a vinyl aromatic copolymer or a mixture thereof prepared by solution polymerization with organically modified silica in which the surface of silica is modified with a particular organosilicon compound and a silane coupling agent in solution. The resultant organic silica master batch elastomer exhibits improved mechanical properties, wear resistance and blending processability, and can provide the effect of extending durability of a tire.

Abstract: Disclosed are a synthetic resin composition for use as building materials such as window frames, as well as a product manufactured using the same. More particularly, the synthetic resin composition comprises a tetrapolymer of acrylic rubber-styrene monomer-butadiene rubber-vinyl cyanide monomer and a styrene-vinyl cyanide copolymer having a high molecular weight and a high degree of dispersion. Unlike products manufactured using prior polyvinyl chloride (PVC), building material such as window frames manufactured using the synthetic resin composition are recyclable, and thus can contribute to a reduction in the generation of hormone-disrupting chemical dioxin, which is released in the burning thereof. Also, the resin composition can be manufactured into products having excellent properties of weather resistance and colorability without using environmental pollutants such as cadmium stearate or lead stearate, which are used as thermal stabilizers.

Abstract: Disclosed are a maleimide-?-alkylstyrene-based, heat-resistant bulk terpolymer and a preparation process thereof. More specifically, disclosed are a bulk terpolymer, comprising 5-60 wt % of an N-substituted maleimide monomer, 10-70 wt % of an ?-alkylstyrene monomer and 5-50 wt % of an unsaturated nitrile monomer, as well as a continuous bulk polymerization process for preparing the same. The disclosed bulk terpolymer has a weight-average molecular weight (Mw) of 70,000-300,000 and a glass transition temperature of 140-200° C., shows excellent high-temperature thermal stability and heat resistance and a remarkably low melt viscosity, and thus is excellent not only in processability, but also in productivity, processability, moldability and blendability, when it is blended with other resins. Also, the continuous bulk polymerization process is equipped with a devolatilizer and enables the bulk terpolymer to be produced at low cost and high efficiency.

Abstract: An expandable polystyrene bead production method, which is a two-step process, is disclosed. The method includes obtaining suspendable, homogenous micropellets from a mixed composition prepared by mixing graphite particles with a styrene-based resin and extruding the composition, and carrying out seed polymerization by suspending graphite-containing micropellets in water and adding a styrene-based monomer and an aromatic hydrocarbon having 6 to 10 carbon atoms, and impregnation by adding a blowing agent. The produced expandable polystyrene beads, which contain graphite particles, are considerably low in thermal conductivity. In addition, the expandable polystyrene beads exhibit a little change in the thermal conductivity over time due to the use of the graphite particles, so that the heat insulation property can be sustained for an extended period of time.

Abstract: An acid generator represented by the following formula (1) is provided: wherein X represents an alkylene group having 1 to 10 carbon atoms, —X1—O—X2—, or a heteroatom selected from the group consisting of nitrogen, sulfur and fluorine; X1 and X2 each independently represent an alkylene group having 1 to 10 carbon atoms; Y represents a cyclic hydrocarbon group having 5 to 30 carbon atoms and containing one or more aromatic rings, while one or more hydrogen atoms on the ring of the cyclic hydrocarbon group may be substituted by one or more members selected from the group consisting of —O—Y1, —CO—Y2, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a perfluoroalkyl group having 1 to 4 carbon atoms, a perfluoroalkoxy group having 1 to 4 carbon atoms, a hydroxyalkyl group having 1 to 6 carbon atoms, a halogen atom, a hydroxyl group and a cyano group; Y1 and Y2 each independently represent an alkyl group having 1 to 6 carbon atoms; n represents an integer of 0 or 5; and A+

Abstract: A radial multi-block copolymer contains a tapered block as represented by the following formula 1. The radial multi-block copolymer, which includes a polystyrene block, a poly(isoprene-styrene)tapered block, a polyisoprene block, and a polybutadiene block, can be used as an excellent pressure-sensitive adhesive material. (pA-pT-pB)m-X-n(pC-pB-pT-pA)??Formula 1 where pA is the polyvinyl aromatic block; pT is the poly(isoprene-styrene)tapered block; pB is the polyisoprene block; pC is the polybutadiene block; X is the residue of a multi-functional coupling agent used in preparation of the radial multi-block copolymer; m and n are integers equal to or greater than 1, representing the number of branches associated with X; and pT=pTA+pTB, where pTA is the pA component of pT, and pTB is the pB component of pT.