Abstract: Provided is a hot dip zinc alloy plated steel sheet which is widely used in vehicles, domestic appliances, construction materials or the like and a method for manufacturing the same. A Zn—Al—Mg hot dip zinc alloy plating bath is used for manufacturing the hot dip zinc alloy plated steel strip, and a small amount of Ga or In is added to the plating bath for inhibiting an oxidation reaction of Mg in the plating bath so as to obtain excellent corrosion resistance and external surface of the plated steel sheet which is manufactured at this point.

Abstract: Provided are a Zn—Mg alloy plated steel sheet and a method for manufacturing same. The Zn—Mg alloy plated steel sheet comprises a base steel sheet and a Zn—Mg plating layer formed on the base steel sheet, wherein the content of Mg in the Zn—Mg plating layer is 8 weight % or less (provided that 0 weight % is excluded), and the Zn—Mg plating layer is a compound phase of Zn and Mg2Zn11. According to the present invention, provided are a Zn—Mg alloy plated steel sheet and a method for manufacturing the same, wherein the Zn—Mg alloy plated steel sheet has excellent corrosion resistance, high adhesion, and superior surface quality of metallic luster.

Abstract: Provided is an austenitic, lightweight, high-strength steel sheet having a high yield ratio and ductility and a method for producing the same, and more particularly, to a high-strength steel sheet for automotive interior panels, exterior panels, and structural parts, and a method for producing the steel sheet. The steel sheet may be a hot-rolled steel sheet, a cold-rolled steel sheet, or a plated steel sheet. The steel sheet includes, by weight %, C: 0.6% to 1.0%, Si: 0.1% to 2.5%, Mn: 10% to 15%, P: 0.02% or less, S: 0.015% or less, Al: 5% to 8%, Ti: 0.01% to 0.20%, N: 0.02% or less, and the balance of Fe and inevitable impurities, wherein the steel sheet has a specific gravity of 7.4 g/cm3 and a Mn/Al ratio of 2 to 3.

Abstract: The present invention provides an apparatus and a method for detecting the presence of and/or determining the amount of a label-free microRNA using an atomic force microscope. The method is extremely selective and/or ultrasensitive. In particular, the present invention provides a cantilever comprising a probe that selectively binds to a double strand of DNA/RNA hybrid complex. The probe comprises a hybrid binding domain (HBD) or a variant thereof.

Abstract: Provided is a dry coating apparatus for coating a coating material, i.e., deposition vapor (metal vapor) on a substrate (a steel strip). The dry coating apparatus includes a coating part disposed in a vacuum to coat deposition vapor generated through heating and evaporation of a supplied coating material onto a proceeding object to be coated and a heating source disposed in an atmosphere to heat and levitate the coating material in the coating part.

Abstract: Provided is a martensitic stainless steel having excellent productivity and high corrosion resistance, which comprises, as percentages by weight, 0.45 to 0.60% carbon, 0.02 to 0.08% nitrogen, 0.2 to 0.4% silicon, 0.3 to 0.6% manganese, 12 to 15% chromium, one or more kinds of 0.1 to 1.5% molybdenum or 0.1 to 1.5% tungsten and Fe and other unavoidable impurities as remnants.

Abstract: A wire rod and steel wire having superior magnetic characteristics and a method for manufacturing same, wherein the wire rod and the steel wire can be used in transformers, vehicles, electric or electronic products, or the like which require low iron loss and high permeability. Provided are a wire rod and steel wire having superior magnetic characteristics and a method for manufacturing same, wherein the wire rod or the steel wire comprises, by wt %, 0.03 to 0.05% of C, 3.0 to 5.0% of Si, 0.1 to 2.0% of Mn, 0.02 to 0.08% of Al, 0.0015 to 0.0030% of N, and the remainder being Fe and unavoidable impurities. The wire rod and steel wire having directional properties may be provided by a general manufacturing process without using expensive alloying elements and without having to add a manufacturing facility.

Abstract: Disclosed herein is a bonded type laminated-core member manufacturing apparatus comprising an adhesive applying unit which is selectively open for applying an adhesive to a material being continuously transferred, and a blanking unit sequentially forming laminar members having a predetermined shape by blanking the material, wherein the adhesive applying unit includes an adhesive applicator having an outlet channel for discharging the adhesive, and a valve closing the outlet channel and opening the outlet channel for discharging the adhesive when the material and the outlet channel come close to each other. since an outlet of a nozzle is opened only when a material approaches an adhesive applying unit and close when the material separates from the adhesive applying unit, leakage of the adhesive prevent can be prevented and the discharge time and the application amount of the adhesive may be regularly controlled.

Abstract: Provided is a wear resistant steel including 2.6 wt % to 4.5 wt % of manganese (Mn), carbon (C) satisfying (6-Mn)/50?C?(10-Mn)/50, 0.05 wt % to 1.0 wt % of silicon (Si), and iron (Fe) as well as other unavoidable impurities as a remainder, wherein a Brinell hardness of a surface portion is in a range of 360 to 440. The wear resistant steel further includes at least one component selected from the group consisting of 0.1 wt % or less (excluding 0 wt %) of niobium (Nb), 0.1 wt % or less (excluding 0 wt %) of vanadium (V), 0.1 wt % or less (excluding 0 wt %) of titanium (Ti), and 0.02 wt % or less (excluding 0 wt %) of boron (B) to complement the performance thereof. The wear resistant steel is characterized in that a microstructure includes martensite in an amount of 90% or more, and an average packet diameter of the martensite is 20 ?m or less.

Abstract: A high-manganese hot-rolled galvanized steel sheet having no surface defects and improved galvanizing and alloying characteristics is manufactured by using a high-manganese hot-rolled steel sheet. Provided are the high-manganese hot-rolled galvanized steel sheet and a method of manufacturing the high-manganese hot-rolled galvanized steel sheet. The high-manganese hot-rolled galvanized steel sheet includes: a hot-rolled steel sheet including 5 wt % to 35 wt % manganese; and a zinc coating layer formed on the hot-rolled steel sheet, wherein an internal oxide layer is formed in an internal region of the hot-rolled steel sheet facing the zinc coating layer.

Abstract: An apparatus for controlling overcurrent of a grid-connected inverter due to an abnormal grid voltage includes a grid voltage sensor configured to sense a grid voltage according to an output current of the grid-connected inverter, a voltage variation calculator configured to calculate a D-axis voltage and a Q-axis voltage of the grid voltage to obtain variation values of the D-axis voltage and the Q-axis voltage, and an output current controller configured to determine whether at least one of the D-axis voltage variation value and the Q-axis voltage variation value exceeds a set value of the grid voltage variation, and decrease the output current by a predetermined value when one of the D-axis voltage variation value and the Q-axis voltage variation value exceeds the set value of the grid voltage variation.

Abstract: There is provided a hot-dip galvanized steel sheet and a hot-dip galvannealed steel sheet, which have excellent elongation properties, and methods for manufacturing the hot-dip galvanized steel sheet and the hot-dip galvannealed steel sheet. The present disclosure relates to a hot-dip galvanized steel sheet in which a hot-dip galvanized layer is formed on a surface of a base steel sheet, the hot-dip galvanized steel sheet having excellent elongation properties and being characterized by the composition and the microstructure thereof.

Abstract: Disclosed herein is a bonded-type laminated core member manufacturing apparatus including an adhesive application unit to apply an adhesive to a material being continuously transferred, and a laminating unit configured to integrate laminar members laminated within a laminating hole by blanking the material, a laminated core member being manufactured by interlayer adhesion between the laminar members, and the laminating unit includes an adhesive hardener to harden the adhesive located between the laminar members so as to integrate the laminar members passing through the laminating hole, and pinchers provided under the adhesive hardener to apply lateral pressure to the laminated core member so as to prevent falling of the laminated core member. Since the laminated core members may be stably extracted, damage to the laminated core member due to falling may be prevented and the laminated core members in an aligned state may be extracted.

Abstract: An apparatus for separating the main component constituting a raw material from impurities includes: a raw material supply unit for supplying a raw material; a charging unit for charging the raw material supplied from the raw material supply unit; an electrostatic sorting unit for sorting the raw material, which has been charged by the charging unit, according to polarity; and a storage unit for collecting the raw material sorted by and falling from the electrostatic sorting unit, wherein the charging unit includes a charging chamber having a space therein for charging the raw material supplied from the raw material supply unit, and a charging rotor rotatably provided in the charging chamber, for impacting the raw material supplied from the raw material supply unit by the rotating force, thus effectively separating the impurities such as ash and sulfur contained in a raw material, e.g. coal.

Abstract: A graphene-coated steel sheet and a method for manufacturing the same are provided. The graphene-coated steel sheet includes a steel sheet and a graphene layer formed on the steel sheet. Therefore, the graphene-coated steel sheet can be useful in preventing corrosion of iron, such as oxidation of iron, and has remarkably excellent thermal conductivity and electrical conductivity, as well as excellent heat resistance resulting from thermal stability of graphene. Also, the method can be useful in manufacturing a high-quality graphene-coated steel sheet having a monocrystalline form and showing substantially no defects or impurities.

Abstract: The present invention relates to an aluminum-magnesium coated steel plate using vacuum coating, wherein an aluminum-magnesium coating layer is constituted by 1 to 45 wt % of magnesium, a balance of aluminum, and other inevitable impurities, and an Al3Mg2 alloy phase is formed in the aluminum-magnesium coating layer by performing heat treatment of the steel plate.

Abstract: There are provided an electromagnetic wiping device, a plated steel sheet wiping apparatus including the electromagnetic wiping device, and a method for manufacturing a plated steel sheet. A portion of a plating layer of a steel sheet having passed through a plating bath is preliminarily removed at least in an edge region of the steel sheet, and a gas wiping operation is performed. Therefore, overplating is prevented at least in the edge region of the steel sheet. In addition, since the load of gas wiping can be reduced while maintaining the line speed of the steel sheet, the quantity of scattered particles and the formation of dross can be reduced for improving the plating quality of the steel sheet and the productivity of a manufacturing process.

Abstract: Provided are a heat recovery apparatus based on a fuel cell and an operating method thereof. In the fuel cell-based heat recovery apparatus and the operating method thereof, hot water and steam may be generated by using heat generated while a molten carbonate fuel cell (MCFC) operates to supply the generated hot water or steam to buildings, thereby reducing a rate of operation in cooling/heating equipment using electricity so as to reduce air-conditioning costs.

Abstract: A conversion coating composition comprising 0.01 wt % to 0.2 wt % of phosphorous (P); 0.01 wt % to 0.2 wt % of magnesium (Mg); 0.005 wt % to 0.15 wt % of zirconium (Zr); 0.005 wt % to 0.15 wt % of titanium (Ti); 0.005 wt % to 0.15 wt % of vanadium (V); 0.05 wt % to 1 wt % of phenol resin; the balance of water and other unavoidable impurities is provided. A surface treated steel sheet comprising a base steel sheet; a zinc or zinc alloy plated layer formed on the base steel sheet; a blackening layer formed on the zinc or zinc alloy plated layer; and an organic and inorganic complex conversion coating layer formed on the blackening layer, wherein the organic and inorganic complex conversion coating layer may satisfy the weight ratio of P:Mg:Zr:Ti:V=1:0.045 to 2:0.035 to 1.5:0.035 to 1.3:0.035 to 1.5 (based on the weight of P) is also provided. A method for manufacturing a steel sheet treated with the conversion coating composition is also provided.

Abstract: An impeller for stirring a melt pool includes: an impeller body extending in the length direction; a blowing nozzle which is provided in such a way as to pass through one part at the bottom end of the impeller body; and a blade provided on the upper part of the impeller body. As a result, when the impeller is used, a stirring flow produced due to the blade and a stirring flow due to substances blown into the melt-pool via the blowing nozzle correspond to each other, and the two flows are combined such that the overall stirring force is improved. Consequently, it is possible to improve the efficiency of stirring by the impeller as compared with hitherto, and, as a result, refining efficiency in the refining step is improved as the rate of reaction between the melt-pool and additives is increased.