Abstract: A method for growth and fabrication of semipolar (Ga,Al,In,B)N thin films, heterostructures, and devices, comprising identifying desired material properties for a particular device application, selecting a semipolar growth orientation based on the desired material properties, selecting a suitable substrate for growth of the selected semipolar growth orientation, growing a planar semipolar (Ga,Al,In,B)N template or nucleation layer on the substrate, and growing the semipolar (Ga,Al,In,B)N thin films, heterostructures or devices on the planar semipolar (Ga,Al,In,B)N template or nucleation layer. The method results in a large area of the semipolar (Ga,Al,In,B)N thin films, heterostructures, and devices being parallel to the substrate surface.

Abstract: Lateral epitaxial overgrowth (LEO) of non-polar gallium nitride (GaN) films results in significantly reduced defect density.

Abstract: An etching technique for the fabrication of thin (Al, In, Ga)N layers. A suitable template or substrate is selected and implanted with foreign ions over a desired area to create ion implanted material. A regrowth of a device structure is then performed on the implanted template or substrate. The top growth surface of the template is bonded to a carrier wafer to created a bonded template/carrier wafer structure. The substrate is removed, as is any residual material, to expose the ion implanted material. The ion implanted material on the bonded template/carrier wafer structure is then exposed to a suitable etchant for a sufficient time to remove the ion implanted material.

Abstract: A method for enhancing growth of device-quality planar semipolar nitride semiconductor thin films via metalorganic chemical vapor deposition (MOCVD) by using an (Al, In, Ga)N nucleation layer containing at least some indium. Specifically, the method comprises loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1-xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1-xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method for improved growth of a semipolar (Al,In,Ga,B)N semiconductor thin film using an intentionally miscut substrate. Specifically, the method comprises intentionally miscutting a substrate, loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1-xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1-xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method for growing planar, semi-polar nitride film on a miscut spinel substrate, in which a large area of the planar, semi-polar nitride film is parallel to the substrate's surface.

Abstract: A method for growing planar, semi-polar nitride film on a miscut spinel substrate, in which a large area of the planar, semi-polar nitride film is parallel to the substrate's surface. The planar films and substrates are: (1) {10 11} gallium nitride (GaN) grown on a {100} spinel substrate miscut in specific directions, (2) {10 13} gallium nitride (GaN) grown on a {110} spinel substrate, (3) {11 22} gallium nitride (GaN) grown on a {1 100} sapphire substrate, and (4) {10 13} gallium nitride (GaN) grown on a {1 100} sapphire substrate.

Abstract: A method for improved growth of a semipolar (Al,In,Ga,B)N semiconductor thin film using an intentionally miscut substrate. Specifically, the method comprises intentionally miscutting a substrate, loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1?xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1?xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method for enhancing growth of device-quality planar semipolar nitride semiconductor thin films via metalorganic chemical vapor deposition (MOCVD) by using an (Al,In,Ga)N nucleation layer containing at least some indium. Specifically, the method comprises loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1-xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1-xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method for growing a semi-polar nitride semiconductor thin film via metalorganic chemical vapor deposition (MOCVD) on a substrate, wherein a nitride nucleation or buffer layer is grown on the substrate prior to the growth of the semi-polar nitride semiconductor thin film.

Abstract: A method for growing a semi-polar nitride semiconductor thin film via metalorganic chemical vapor deposition (MOCVD) on a substrate, wherein a nitride nucleation or buffer layer is grown on the substrate prior to the growth of the semi-polar nitride semiconductor thin film.

Abstract: A method for the fabrication of nonpolar indium gallium nitride (InGaN) films as well as nonpolar InGaN-containing device structures using metalorganic chemical vapor deposition (MOVCD). The method is used to fabricate nonpolar InGaN/GaN violet and near-ultraviolet light emitting diodes and laser diodes.

Abstract: A method for the fabrication of nonpolar indium gallium nitride (InGaN) films as well as nonpolar InGaN-containing device structures using metalorganic chemical vapor deposition (MOVCD). The method is used to fabricate nonpolar InGaN/GaN violet and near-ultraviolet light emitting diodes and laser diodes.

Abstract: Growth methods for planar, non-polar, Group-III nitride films are described. The resulting films are suitable for subsequent device regrowth by a variety of growth techniques.

Abstract: The present invention provides nitride semiconductors having a moderate density of basal plane stacking faults and a reduced density of threading dislocations, various products based on, incorporating or comprising the nitride semiconductors, including without limitation substrates, template films, templates, heterostructures with or without integrated substrates, and devices, and methods for fabrication of templates and substrates comprising the nitride semiconductors.

Abstract: Highly planar non-polar GaN films are grown by hydride vapor phase epitaxy (HVPE). The resulting films are suitable for subsequent device regrowth by a variety of growth techniques.

Abstract: A method for growing III-nitride films containing aluminum using Hydride Vapor Phase Epitaxy (HVPE) is disclosed, and comprises using corrosion-resistant materials in an HVPE system, the region of the HVPE system containing the corrosion-resistant materials being an area that contacts an aluminum halide, heating a source zone with an aluminum-containing source above a predetermined temperature, and growing the III-nitride film containing aluminum within the HVPE system containing the corrosion-resistant material.

Abstract: A method for improved growth of a semipolar (Al,In,Ga,B)N semiconductor thin film using an intentionally miscut substrate. Specifically, the method comprises intentionally miscutting a substrate, loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1-xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1-xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method for enhancing growth of device-quality planar semipolar nitride semiconductor thin films via metalorganic chemical vapor deposition (MOCVD) by using an (Al,In,Ga)N nucleation layer containing at least some indium. Specifically, the method comprises loading a substrate into a reactor, heating the substrate under a flow of nitrogen and/or hydrogen and/or ammonia, depositing an InxGa1?xN nucleation layer on the heated substrate, depositing a semipolar nitride semiconductor thin film on the InxGa1?xN nucleation layer, and cooling the substrate under a nitrogen overpressure.

Abstract: A method of growing highly planar, fully transparent and specular m-plane gallium nitride (GaN) films. The method provides for a significant reduction in structural defect densities via a lateral overgrowth technique. High quality, uniform, thick m-plane GaN films are produced for use as substrates for polarization-free device growth.