Abstract: An aqueous seeding solution of palladium acetate, acetic acid and chloride.

Abstract: An interconnect structure in which the adhesion between an upper level low-k dielectric material, such as a material comprising elements of Si, C, O, and H, and an underlying diffusion capping dielectric, such as a material comprising elements of C, Si, N and H, is improved by incorporating an adhesion transition layer between the two dielectric layers. The presence of the adhesion transition layer between the upper level low-k dielectric and the diffusion barrier capping dielectric can reduce the chance of delamination of the interconnect structure during the packaging process. The adhesion transition layer provided herein includes a lower SiOx- or SiON-containing region and an upper C graded region. Methods of forming such a structure, in particularly the adhesion transition layer, are also provided.

Abstract: An interconnect in provided which comprises a copper conductor having both a top surface and a lower surface, with caps formed on the top surface of the metallic conductor. The cap is formed of dual laminations or multiple laminations of films with the laminated films including an Ultra-Violet (UV) blocking film and a diffusion barrier film. The diffusion barrier film and the UV blocking film may be separated by an intermediate film.

Abstract: Methods of forming interconnect structures include forming a first metal wiring pattern on a first dielectric layer and forming a capping layer (e.g., SiCN layer) on the first copper wiring pattern. An adhesion layer is deposited on the capping layer, using a first source gas containing octamethylcyclotetrasilane (OMCTS) at a volumetric flow rate in a range from about 500 sccm to about 700 sccm and a second gas containing helium at a volumetric flow rate in a range from about 1000 to about 3000 sccm. The goal of the deposition step is to achieve an adhesion layer having an internal compressive stress of greater than about 150 MPa therein, so that the adhesion layer is less susceptible to etching/cleaning damage and moisture absorption during back-end processing steps. Additional dielectric and metal layers are then deposited on the adhesion layer.

Abstract: A low k dielectric stack having an effective dielectric constant k, of about 3.0 or less, in which the mechanical properties of the stack are improved by introducing at least one nanolayer into the dielectric stack. The improvement in mechanical properties is achieved without significantly increasing the dielectric constant of the films within the stack and without the need of subjecting the inventive dielectric stack to any post treatment steps. Specifically, the present invention provides a low k dielectric stack that comprises at least one low k dielectric material and at least one nanolayer present within the at least one low k dielectric material.

Abstract: A method to electrolessly plate a CoWP alloy on copper in a reproducible manner that is effective for a manufacturable process. In the method, a seed layer of palladium (Pd) is deposited on the copper by an aqueous seeding solution of palladium acetate, acetic acid and chloride. Thereafter, a complexing solution is applied to remove any Pd ions which are adsorbed on surfaces other than the copper. Finally, a plating solution of cobalt (Co), tungsten (W) and phosphorous (P) is applied to the copper so as to deposit a layer of CoWP on the Pd seed and copper.

Abstract: A porous low k or ultra low k dielectric film comprising atoms of Si, C, O and H (hereinafter “SiCOH”) in a covalently bonded tri-dimensional network structure having a dielectric constant of less than about 3.0, a higher degree of crystalline bonding interactions, more carbon as methyl termination groups and fewer methylene, —CH2— crosslinking groups than prior art SiCOH dielectrics is provided. The SiCOH dielectric is characterized as having a FTIR spectrum comprising a peak area for CH3+CH2 stretching of less than about 1.40, a peak area for SiH stretching of less than about 0.20, a peak area for SiCH3 bonding of greater than about 2.0, and a peak area for Si—O—Si bonding of greater than about 60%, and a porosity of greater than about 20%.

Abstract: An interconnect structure in which the adhesion between an upper level low-k dielectric material, such as a material comprising elements of Si, C, O, and H, and an underlying diffusion capping dielectric, such as a material comprising elements of C, Si, N and H, is improved by incorporating an adhesion transition layer between the two dielectric layers. The presence of the adhesion transition layer between the upper level low-k dielectric and the diffusion barrier capping dielectric can reduce the chance of delamination of the interconnect structure during the packaging process. The adhesion transition layer provided herein includes a lower SiOx— or SiON-containing region and an upper C graded region. Methods of forming such a structure, in particularly the adhesion transition layer, are also provided.

Abstract: A semiconductor device structure and method for manufacture includes a substrate having a top first layer; a second thin transition layer located on top of the first layer; and, a third layer located on top of the transition layer, wherein the second thin transition layer provides strong adhesion and cohesive strength between the first and third layers of the structure. Additionally, a semiconductor device structure and method for manufacture includes an insulating structure comprising a multitude of dielectric and conductive layers with respective transition bonding layers disposed to enhance interfacial strength among the different layers. Further, an electronic device structure incorporates layers of insulating and conductive materials as intralevel or interlevel dielectrics in a back-end-of-the-line (“BEOL”) wiring structure in which the interfacial strength between different pairs of dielectric films is enhanced by a thin intermediate transition bonding layer.

Abstract: An advanced back-end-of-line (BEOL) metallization structure is disclosed. The structure includes a diffusion barrier or cap layer having a low dielectric constant (low-k), where the cap layer is formed of silicon nitride by a plasma-enhanced chemical vapor deposition (PE CVD) process. The metallization structure also includes an inter-layer dielectric (ILD) formed of a carbon-containing dielectric material having a dielectric constant of less than about 4, and a continuous hardmask layer overlying the ILD which is preferably formed of silicon nitride or silicon carbide. A method for forming the BEOL metallization structure is also disclosed. The method includes a pre-clean or pre-activation step to improve the adhesion of the cap layer to the underlying copper conductors. The pre-clean or pre-activation step comprises exposing the copper surface to a reducing plasma including hydrogen, ammonia, nitrogen and/or noble gases.

Abstract: A method for removing a dielectric layer formed upon a semiconductor substrate is disclosed. In an exemplary embodiment of the invention, the method includes subjecting the dielectric layer to a dry etch process and subjecting an adhesion promoter layer underneath the dielectric layer to a wet etch process.

Abstract: An advanced back-end-of-line (BEOL) metallization structure is disclosed. The structure includes a diffusion barrier or cap layer having a low dielectric constant (low-k), where the cap layer is formed of silicon nitride by a plasma-enhanced chemical vapor deposition (PE CVD) process. The metallization structure also includes an inter-layer dielectric (ILD) formed of a carbon-containing dielectric material having a dielectric constant of less than about 4, and a continuous hardmask layer overlying the ILD which is preferably formed of silicon nitride or silicon carbide. A method for forming the BEOL metallization structure is also disclosed. The method includes a pre-clean or pre-activation step to improve the adhesion of the cap layer to the underlying copper conductors. The pre-clean or pre-activation step comprises exposing the copper surface to a reducing plasma including hydrogen, ammonia, nitrogen and/or noble gases.

Abstract: A semiconductor device containing a diffusion barrier layer is provided. The semiconductor device includes at least a semiconductor substrate containing conductive metal elements; and, a diffusion barrier layer applied to at least a portion of the substrate in contact with the conductive metal elements, the diffusion barrier layer having an upper surface and a lower surface and a central portion, and being formed from silicon, carbon, nitrogen and hydrogen with the nitrogen being non-uniformly distributed throughout the diffusion barrier layer. Thus, the nitrogen is more concentrated near the lower and upper surfaces of the diffusion barrier layer as compared to the central portion of the diffusion barrier layer. Methods for making the semiconductor devices are also provided.

Abstract: A method for controlling the shape of copper features, having the following steps:

Abstract: An advanced back-end-of-line (BEOL) metallization structure is disclosed. The structure includes a diffusion barrier or cap layer having a low dielectric constant (low-k), where the cap layer is formed of silicon nitride by a plasma-enhanced chemical vapor deposition (PE CVD) process. The metallization structure also includes an inter-layer dielectric (ILD) formed of a carbon-containing dielectric material having a dielectric constant of less than about 4, and a continuous hardmask layer overlying the ILD which is preferably formed of silicon nitride or silicon carbide. A method for forming the BEOL metallization structure is also disclosed. The method includes a pre-clean or pre-activation step to improve the adhesion of the cap layer to the underlying copper conductors. The pre-clean or pre-activation step comprises exposing the copper surface to a reducing plasma including hydrogen, ammonia, nitrogen and/or noble gases.

Abstract: A diffusion barrier that has a low dielectric constant, k, yet resistant to oxygen and/or moisture permeability is provided. The diffusion barrier includes a dielectric stack having at least two or more dielectric films, each film having a dielectric constant of about 8 or less, wherein the dielectric stack comprises alternating films composed of a high-permeability material and a low-permeability material. A semiconductor structure including substrate having at least one wiring region and the inventive diffusion barrier formed on a surface of the substrate is also provided.

Abstract: A method for forming a planarized dielectric layer upon a semiconductor wafer is disclosed. In an exemplary embodiment of the invention, the method includes applying an adhesion promoter to the wafer, thereby forming an adhesion promoter layer. A dielectric material is applied in a spin-on fashion upon the adhesion promoter layer at a relative humidity of less than 40% and for a thickness setting duration of less than 30 seconds. Then, the dielectric material is dried by baking without additional spinning of the semiconductor wafer.

Abstract: An advanced back-end-of-line (BEOL) metallization structure is disclosed. The structure includes a diffusion barrier or cap layer having a low dielectric constant (low-k), where the cap layer is formed of silicon nitride by a plasma-enhanced chemical vapor deposition (PE CVD) process. The metallization structure also includes an inter-layer dielectric (ILD) formed of a carbon-containing dielectric material having a dielectric constant of less than about 4, and a continuous hardmask layer overlying the ILD which is preferably formed of silicon nitride or silicon carbide. A method for forming the BEOL metallization structure is also disclosed. The method includes a pre-clean or pre-activation step to improve the adhesion of the cap layer to the underlying copper conductors. The pre-clean or pre-activation step comprises exposing the copper surface to a reducing plasma including hydrogen, ammonia, nitrogen and/or noble gases.

Abstract: A method for removing a dielectric layer formed upon a semiconductor substrate is disclosed. In an exemplary embodiment of the invention, the method includes subjecting the dielectric layer to a dry etch process and subjecting an adhesion promoter layer underneath the dielectric layer to a wet etch process.

Abstract: A method for forming a planarized dielectric layer upon a semiconductor wafer is disclosed. In an exemplary embodiment of the invention, the method includes applying an adhesion promoter to the wafer, thereby forming an adhesion promoter layer. A dielectric material is applied in a spin-on fashion upon the adhesion promoter layer at a relative humidity of less than 40% and for a thickness setting duration of less than 30 seconds. Then, the dielectric material is dried by baking without additional spinning of the semiconductor wafer.