Abstract: A substrate is provided with a patterned layer, such as, a photo resist layer which may exhibit line roughness. The patterned layer may be an EUV photo resist layer utilized in a self-aligned multi-patterning process. A tone inversion process having a tone inversion layer is utilized along with a surface treatment of a sidewall of the tone inversion layer so as to improve line roughness characteristics of the process. More specifically, a tone inversion layer may be patterned and then sidewalls of the tone inversion layer may be treated. A fill material may then be deposited upon the substrate including adjacent the sidewalls of the tone inversion layer. When the tone inversion layer is removed, the roughness of the fill material will be reduced due to the use of the sidewall treatment.

Abstract: A method for forming a fully self-aligned via is provided. A workpiece having a pattern of features in a dielectric layer is received into a common manufacturing platform. Metal caps are deposited on the metal features, and a barrier layer is deposited on the metal caps. A first dielectric layer is added to exposed dielectric material. The barrier layer is removed and an etch stop layer is added on the exposed surfaces of the first dielectric layer and the metal caps. Additional dielectric material is added on top of the etch stop layer, then both the additional dielectric material and a portion of the etch stop layer are etched to form a feature to be filled with metal material. An integrated sequence of processing steps is executed within one or more common manufacturing platforms to provide controlled environments. Transfer modules transfer the workpiece between processing modules within and between controlled environments.

Abstract: A method for filling recessed features with a low-resistivity metal. The method includes providing a patterned substrate containing a recessed feature formed in a first layer and a second layer that is exposed in the recessed feature, forming a nucleation enhancement layer on a sidewall of the first layer in the recessed feature and depositing a metal layer in the recessed feature by vapor phase deposition, where the metal layer is deposited on the second layer and on the nucleation enhancement layer. An initial metal layer may be selectively formed on the second layer in the recessed feature before forming the nucleation enhancement layer.

Abstract: A method of metallization includes receiving a substrate having a recess formed therein. The recess has a bottom and sidewalls, and a conformal liner is deposited on the bottom and sidewalls of the recess. The conformal liner is removed from an upper portion of the recess to expose upper sidewalls of the recess while leaving the conformal liner in a lower portion of the recess covering the bottom and lower sidewalls of the recess. Metal is deposited in a lower portion of the recess to form a metallization feature including the conformal liner in the lower portion of the recess and the metal.

Abstract: A method for filling recessed features with a low-resistivity metal includes providing a patterned substrate containing a recessed feature formed in a first layer and a second layer that is exposed in the recessed feature, pre-treating the substrate with a surface modifier that increases metal deposition selectivity on the second layer relative to on the first layer, and depositing a metal layer on the substrate by vapor phase deposition, where the metal layer is preferentially deposited on the second layer in the recessed feature. The method further includes removing metal nuclei deposited on the first layer, including on a field area and on sidewalls of the first layer in the recessed feature, to selectively form the metal layer on the second layer in the recessed feature, where the removing includes exposing the patterned substrate to an etching gas containing ozone.

Abstract: A method for filling recessed features with a low-resistivity metal. The method includes providing a patterned substrate containing a recessed feature formed in a first layer and a second layer that is exposed in the recessed feature, and pre-treating the substrate with a surface modifier that increases metal deposition selectivity on the second layer relative to on the first layer, depositing a metal layer on the substrate by vapor phase deposition, where the metal layer is preferentially deposited on the second layer in the recessed feature, and removing metal nuclei deposited on the first layer, including on a field area and on sidewalls of the first layer in the recessed feature, to selectively form the metal layer on the second layer in the recessed feature. The steps of pre-treating, depositing and removing may be repeated at least once to increase a thickness of the metal layer in the recessed feature.

Abstract: Methods and systems for selective deposition of conductive a cap for FAV features are described. In an embodiment, a method may include receiving a substrate having an interlayer dielectrics (ILD) layer, the ILD layer having a recess, the recess having a conductive layer formed therein, the conductive layer comprising a first conductive material. Additionally, such a method may include forming a cap within a region defined by the recess and in contact with a surface of the conductive layer, the cap comprising a second conductive material. The method may also include forming a conformal etch stop layer in contact with a surface of the cap and in contact with a region of the ILD layer. Further, the method may include selectively etching the etch stop layer using a plasma etch process, wherein the plasma etch process removes the etch stop layer selective to the second conductive material comprising the cap.

Abstract: A method for filling recessed features with a low-resistivity metal. The method includes providing a patterned substrate containing a recessed feature formed in a first layer and a second layer that is exposed in the recessed feature, and pre-treating the substrate with a surface modifier that increases metal deposition selectivity on the second layer relative to on the first layer, depositing a metal layer on the substrate by vapor phase deposition, where the metal layer is preferentially deposited on the second layer in the recessed feature, and removing metal nuclei deposited on the first layer, including on a field area and on sidewalls of the first layer in the recessed feature, to selectively form the metal layer on the second layer in the recessed feature. The steps of pre-treating, depositing and removing may be repeated at least once to increase a thickness of the metal layer in the recessed feature.

Abstract: A method of preparing a self-aligned via on a semiconductor workpiece includes using an integrated sequence of processing steps executed on a common manufacturing platform hosting a plurality of processing modules including one or more film-forming modules, one or more etching modules, and one or more transfer modules. The integrated sequence of processing steps include receiving the workpiece into the common manufacturing platform, the workpiece having a pattern of metal features in a dielectric layer wherein exposed surfaces of the metal features and exposed surfaces of the dielectric layer together define an upper planar surface; selectively etching the metal features to form a recess pattern by recessing the exposed surfaces of the metal features beneath the exposed surfaces of the dielectric layer using one of the one or more etching modules; and depositing an etch stop layer over the recess pattern using one of the one or more film-forming modules.

Abstract: A method for forming a fully self-aligned via is provided. A workpiece having a pattern of features in a dielectric layer is received into a common manufacturing platform. Metal caps are deposited on the metal features, and a barrier layer is deposited on the metal caps. A first dielectric layer is added to exposed dielectric material. The barrier layer is removed and an etch stop layer is added on the exposed surfaces of the first dielectric layer and the metal caps. Additional dielectric material is added on top of the etch stop layer, then both the additional dielectric material and a portion of the etch stop layer are etched to form a feature to be filled with metal material. An integrated sequence of processing steps is executed within one or more common manufacturing platforms to provide controlled environments. Transfer modules transfer the workpiece between processing modules within and between controlled environments.

Abstract: A method of metallization includes receiving a substrate having a recess formed therein. The recess has a bottom and sidewalls, and a conformal liner is deposited on the bottom and sidewalls of the recess. The conformal liner is removed from an upper portion of the recess to expose upper sidewalls of the recess while leaving the conformal liner in a lower portion of the recess covering the bottom and lower sidewalls of the recess. Metal is deposited in a lower portion of the recess to form a metallization feature including the conformal liner in the lower portion of the recess and the metal.

Abstract: Embodiments are disclosed for a method to process microelectronic workpieces including forming a metal hard mask layer including ruthenium (Ru MHM layer) over one or more underlying layers on a substrate for a microelectronic workpiece, etching the Ru MHM layer to provide a patterned Ru MHM layer, and etching the one or more underlying layers using the patterned Ru MHM layer as a mask to protect portion of the one or more underlying layers. For one embodiment, the Ru MHM layer is a material including 95 percent or more of ruthenium (Ru). For another embodiment, the Ru MHM layer is a material including 70 percent or more of ruthenium (Ru). Further, the Ru MHM layer preferably has a selectivity of 10 or greater with respect to a next underlying layer adjacent to the Ru MHM layer, such as a SiN hard mask layer.

Abstract: A method for forming a fully self-aligned via is provided. A workpiece having a pattern of features in a dielectric layer is received into a common manufacturing platform. Metal caps are deposited on the metal features, and a barrier layer is deposited on the metal caps. A first dielectric layer is added to exposed dielectric material. The barrier layer is removed and an etch stop layer is added on the exposed surfaces of the first dielectric layer and the metal caps. Additional dielectric material is added on top of the etch stop layer, then both the additional dielectric material and a portion of the etch stop layer are etched to form a feature to be filled with metal material. An integrated sequence of processing steps is executed within one or more common manufacturing platforms to provide controlled environments. Transfer modules transfer the workpiece between processing modules within and between controlled environments.

Abstract: A semiconductor device is provided. The semiconductor device can have a substrate including dielectric material. A plurality of narrow interconnect openings can be formed within said dielectric material. In addition, a plurality of wide interconnect openings can be formed within said dielectric material. The semiconductor device can include a first metal filling the narrow interconnect openings to form an interconnect structure and conformally covering a surface of the wide interconnect openings formed in the dielectric material, and a second metal formed over the first metal and encapsulated by the first metal to form another interconnect structure within the wide interconnect openings.

Abstract: A method of processing substrates, in one example microelectronic workpieces, is disclosed that includes forming a multi-layer metal hard mask (MHM) layer in which at least one lower layer of the multi-layer MHM is comprised of ruthenium (Ru). The Ru MHM layer may be an atomic layer deposition (ALD) Ru MHM layer formed over one or more underlying layers on a substrate. The ALD Ru MHM layer may be etched to provide a patterned ALD Ru MHM layer, and then the one or more underlying layers may be etched using, at least in part, the patterned ALD Ru MHM layer as a mask to protect portion of the one or more underlying layers. In one embodiment, at least one of the underlying layers is a hard mask layer.

Abstract: A method for forming a fully self-aligned via is provided. A workpiece having a pattern of features in a dielectric layer is received into a common manufacturing platform. Metal caps are deposited on the metal features, and a barrier layer is deposited on the metal caps. A first dielectric layer is added to exposed dielectric material. The barrier layer is removed and an etch stop layer is added on the exposed surfaces of the first dielectric layer and the metal caps. Additional dielectric material is added on top of the etch stop layer, then both the additional dielectric material and a portion of the etch stop layer are etched to form a feature to be filled with metal material. An integrated sequence of processing steps is executed within one or more common manufacturing platforms to provide controlled environments. Transfer modules transfer the workpiece between processing modules within and between controlled environments.

Abstract: A method of processing materials on a semiconductor workpiece using an integrated sequence of processing steps executed on a common manufacturing platform hosting a plurality of processing modules including one or more film-forming modules, one or more etching modules, and one or more transfer modules is provided. A workpiece having an upper planar surface is received into the common manufacturing platform. The method further includes conformally applying a thin film over the feature pattern using one of the film-forming modules, removing the thin film from upper surfaces of the feature pattern using one of the etching modules to leave behind the thin film in the recessed feature, and removing the fill material from the upper planar surface of the workpiece. The integrated sequence of processing steps is executed in a controlled environment within the common manufacturing platform and without leaving the controlled environment.

Abstract: A semiconductor device includes a plurality of first sources/drains and a plurality of first source/drain (S/D) contacts formed over the first sources/drains. The device also includes a plurality of first dielectric caps. Each of the plurality of first dielectric caps is positioned over a respective first S/D contact to cover a top portion and at least a part of side portions of the respective first S/D contact. The device also includes a plurality of second sources/drains and a plurality of second S/D contacts that are staggered over the plurality of first S/D contacts so as to form a stair-case configuration. A plurality of second dielectric caps are formed over the plurality of second S/D contacts. Each of the plurality of second dielectric caps is positioned over a respective second S/D contact to cover a top portion and at least a part of side portions of the respective second S/D contact.

Abstract: A method is provided for void-free Ru metal filling of features in a substrate. The method includes providing a substrate containing features, depositing a Ru metal layer in the features, removing the Ru metal layer from a field area around an opening of the features, and depositing additional Ru metal in the features, where the additional Ru metal is deposited in the features at a higher rate than on the field area. According to one embodiment, the additional Ru metal is deposited until the features are fully filled with Ru metal.

Abstract: A method for filling recessed features with a low-resistivity metal. The method includes providing a patterned substrate containing a recessed feature formed in a first layer and a second layer that is exposed in the recessed feature, and pre-treating the substrate with a surface modifier that increases metal deposition selectivity on the second layer relative to on the first layer, depositing a metal layer on the substrate by vapor phase deposition, where the metal layer is preferentially deposited on the second layer in the recessed feature, and removing metal nuclei deposited on the first layer, including on a field area and on sidewalls of the first layer in the recessed feature, to selectively form the metal layer on the second layer in the recessed feature. The steps of pre-treating, depositing and removing may be repeated at least once to increase a thickness of the metal layer in the recessed feature.