Abstract: The invention provides semiconductor materials including a gallium nitride material layer formed on a silicon substrate and methods to form the semiconductor materials. The semiconductor materials include a transition layer formed between the silicon substrate and the gallium nitride material layer. The transition layer is compositionally-graded to lower stresses in the gallium nitride material layer which can result from differences in thermal expansion rates between the gallium nitride material and the substrate. The lowering of stresses in the gallium nitride material layer reduces the tendency of cracks to form. Thus, the invention enables the production of semiconductor materials including gallium nitride material layers having few or no cracks. The semiconductor materials may be used in a number of microelectronic and optical applications.

Abstract: An underlying gallium nitride layer on a silicon carbide substrate is masked with a mask that includes an array of openings therein, and the underlying gallium nitride layer is etched through the array of openings to define posts in the underlying gallium nitride layer and trenches therebetween. The posts each include a sidewall and a top having the mask thereon. The sidewalls of the posts are laterally grown into the trenches to thereby form a gallium nitride semiconductor layer. During this lateral growth, the mask prevents nucleation and vertical growth from the tops of the posts. Accordingly, growth proceeds laterally into the trenches, suspended from the sidewalls of the posts. The sidewalls of the posts may be laterally grown into the trenches until the laterally grown sidewalls coalesce in the trenches to thereby form a gallium nitride semiconductor layer.

Abstract: Embodiments of the present invention pendeoepitaxially grow sidewalls of posts in an underlying gallium nitride layer that itself is on a sapphire substrate, at high temperatures between about 1000° C. and about 1100° C. and preferably at about 1100° to reduce vertical growth of gallium nitride on the trench floor from interfering with the pendeoepitaxial growth of the gallium nitride sidewalls of the posts. Thus, widely available sapphire substrates may be used for pendeoepitaxial of gallium nitride, to thereby allow reduced cost and/or wider applications for gallium nitride devices. More specifically, gallium nitride semiconductor layers may be fabricated by etching an underlying gallium nitride layer on a sapphire substrate, to define at least one post in the underlying gallium nitride layer and at least one trench in the underlying gallium nitride layer. The at least one post includes a gallium nitride top and a gallium nitride sidewall. The at least one trench includes a trench floor.

Abstract: Methods of forming compound semiconductor layers include the steps of forming a plurality of selective growth regions at spaced locations on a first substrate and then forming a plurality of semiconductor layers at spaced locations on the first substrate by growing a respective semiconductor layer on each of the selective growth regions. The first substrate is then divided into a plurality of second smaller substrates that contain only a respective one of the plurality of semiconductor layers. This dividing step is preferably performed by partitioning (e.g., dicing) the first substrate at the spaces between the selective growth regions. The step of forming a plurality of semiconductor layers preferably comprises growing a respective compound semiconductor layer (e.g., gallium nitride layer) on each of the selective growth regions. The growing step may comprise pendeoepitaxially growing a respective gallium nitride layer on each of the selective growth regions.

Abstract: An underlying gallium nitride layer on a silicon carbide substrate is masked with a mask that includes an array of openings therein, and the underlying gallium nitride layer is etched through the array of openings to define posts in the underlying gallium nitride layer and trenches therebetween. The posts each include a sidewall and a top having the mask thereon. The sidewalls of the posts are laterally grown into the trenches to thereby form a gallium nitride semiconductor layer. During this lateral growth, the mask prevents nucleation and vertical growth from the tops of the posts. Accordingly, growth proceeds laterally into the trenches, suspended from the sidewalls of the posts. The sidewalls of the posts may be laterally grown into the trenches until the laterally grown sidewalls coalesce in the trenches to thereby form a gallium nitride semiconductor layer.

Abstract: The invention includes providing gallium nitride materials including thermally conductive regions and methods to form such materials. The gallium nitride materials may be used to form semiconductor devices. The thermally conductive regions may include heat spreading layers and heat sinks. Heat spreading layers distribute heat generated during device operation over relatively large areas to prevent excessive localized heating. Heat sinks typically are formed at either the backside or topside of the device and facilitate heat dissipation to the environment. It may be preferable for devices to include a heat spreading layer which is connected to a heat sink at the backside of the device. A variety of semiconductor devices may utilize features of the invention including devices on silicon substrates and devices which generate large amounts of heat such as power transistors.

Abstract: The invention includes providing gallium nitride material devices having backside vias and methods to form the devices. The devices include a gallium nitride material formed over a substrate, such as silicon. The device also may include one or more non-conducting layers between the substrate and the gallium nitride material which can aid in the deposition of the gallium nitride material. A via is provided which extends from the backside of the device through the non-conducting layer(s) to enable electrical conduction between an electrical contact deposited within the via and, for example, an electrical contact on the topside of the device. Thus, devices of the invention may be vertically conducting. Exemplary devices include laser diodes (LDs), light emitting diodes (LEDs), power rectifier diodes, FETs (e.g., HFETs), Gunn-effect diodes, and varactor diodes, among others.

Abstract: A substrate includes non-gallium nitride posts that define trenches therebetween, wherein the non-gallium nitride posts include non-gallium nitride sidewalls and non-gallium nitride tops and the trenches include non-gallium floors. Gallium nitride is grown on the non-gallium nitride posts, including on the non-gallium nitride tops. Preferably, gallium nitride pyramids are grown on the non-gallium nitride tops and gallium nitride then is grown on the gallium nitride pyramids. The gallium nitride pyramids preferably are grown at a first temperature and the gallium nitride preferably is grown on the pyramids at a second temperature that is higher than the first temperature. The first temperature preferably is about 1000° C. or less and the second temperature preferably is about 1100° C. or more. However, other than temperature, the same processing conditions preferably are used for both growth steps.

Abstract: A gallium nitride layer is pendeoepitaxially grown on weak posts on a substrate that are configured to crack due to a thermal expansion coefficient mismatch between the substrate and the gallium nitride layer on the weak posts. Thus, upon cooling, at least some of the weak posts crack, to thereby relieve stress in the gallium nitride semiconductor layer. Accordingly, low defect density gallium nitride semiconductor layers may be produced. Moreover, the weak posts can allow relatively easy separation of the substrate from the gallium nitride semiconductor layer to provide a freestanding gallium nitride layer. The weak posts may be formed by forming an array of posts in spaced apart staggered relation on the substrate. By staggering the posts, later fracturing may be promoted compared to long unstaggered posts. Alternatively, the posts may have a height to width ratio in excess of 0.5, so that the relatively narrow posts promote cracking upon reduction of the temperature.

Abstract: The invention provides semiconductor materials including a gallium nitride material layer formed on a silicon substrate and methods to form the semiconductor materials. The semiconductor materials include a transition layer formed between the silicon substrate and the gallium nitride material layer. The transition layer is compositionally-graded to lower stresses in the gallium nitride material layer which can result from differences in thermal expansion rates between the gallium nitride material and the substrate. The lowering of stresses in the gallium nitride material layer reduces the tendency of cracks to form. Thus, the invention enables the production of semiconductor materials including gallium nitride material layers having few or no cracks. The semiconductor materials may be used in a number of microelectronic and optical applications.

Abstract: A gallium nitride semiconductor layer is fabricated by exposing (111) crystallographic planes in a face of a (100) silicon substrate, and growing hexagonal gallium nitride on the (111) crystallographic planes that are exposed. Thus, a (100) silicon substrate, which is widely used for fabricating conventional microelectronic devices such as bipolar and field effect transistors, may be used to fabricate gallium nitride semiconductor layers thereon. The (111) crystallographic planes may be exposed in the face of the (100) silicon substrate by wet-etching the face of the (100) silicon substrate. More specifically, the face of the (100) silicon substrate may be dipped in KOH for a short period of time, such as about ten seconds or less, to expose the (111) crystallographic planes therein. The face of the (100) silicon substrate may be unmasked when dipped in KOH, to thereby expose randomly spaced apart (111) crystallographic planes in the face of the (100) silicon substrate.

Abstract: A substrate includes non-gallium nitride posts that define trenches therebetween, wherein the non-gallium nitride posts include non-gallium nitride sidewalls and non-gallium nitride tops and the trenches include non-gallium floors. Gallium nitride is grown on the non-gallium nitride posts, including on the non-gallium nitride tops. Preferably, gallium nitride pyramids are grown on the non-gallium nitride tops and gallium nitride then is grown on the gallium nitride pyramids. The gallium nitride pyramids preferably are grown at a first temperature and the gallium nitride preferably is grown on the pyramids at a second temperature that is higher than the first temperature. The first temperature preferably is about 1000° C. or less and the second temperature preferably is about 1100° C. or more. However, other than temperature, the same processing conditions preferably are used for both growth steps.

Abstract: A gallium nitride layer is pendeoepitaxially grown on weak posts on a substrate that are configured to crack due to a thermal expansion coefficient mismatch between the substrate and the gallium nitride layer on the weak posts. Thus, upon cooling, at least some of the weak posts crack, to thereby relieve stress in the gallium nitride semiconductor layer. Accordingly, low defect density gallium nitride semiconductor layers may be produced. Moreover, the weak posts can allow relatively easy separation of the substrate from the gallium nitride semiconductor layer to provide a freestanding gallium nitride layer. The weak posts may be formed by forming an array of posts in spaced apart staggered relation on the substrate. By staggering the posts, later fracturing may be promoted compared to long unstaggered posts. Alternatively, the posts may have a height to width ratio in excess of 0.5, so that the relatively narrow posts promote cracking upon reduction of the temperature.

Abstract: An underlying gallium nitride layer on a silicon carbide substrate is masked with a mask that includes an array of openings therein, and the underlying gallium nitride layer is etched through the array of openings to define posts in the underlying gallium nitride layer and trenches therebetween. The posts each include a sidewall and a top having the mask thereon. The sidewalls of the posts are laterally grown into the trenches to thereby form a gallium nitride semiconductor layer. During this lateral growth, the mask prevents nucleation and vertical growth from the tops of the posts. Accordingly, growth proceeds laterally into the trenches, suspended from the sidewalls of the posts. The sidewalls of the posts may be laterally grown into the trenches until the laterally grown sidewalls coalesce in the trenches to thereby form a gallium nitride semiconductor layer.

Abstract: A gallium nitride microelectronic layer is fabricated by converting a surface of a (111) silicon layer to 3C-silicon carbide. A layer of 3C-silicon carbide is then epitaxially grown on the converted surface of the (111) silicon layer. A layer of 2H-gallium nitride then is grown on the epitaxially grown layer of 3C-silicon carbide. The layer of 2H-gallium nitride then is laterally grown to produce the gallium nitride microelectronic layer. The silicon layer is a (111) silicon substrate, the surface of which is converted to 3C-silicon carbide, or the (111) silicon layer is part of a Separation by IMplanted OXygen (SIMOX) silicon substrate which includes a layer of implanted oxygen that defines the (111) layer on the (111) silicon substrate, or the (111) silicon layer is a portion of a Silicon-On-Insulator (SOI) substrate in which a (111) silicon layer is bonded to a substrate.

Abstract: A substrate includes non-gallium nitride posts that define trenches therebetween, wherein the non-gallium nitride posts include non-gallium nitride sidewalls and non-gallium nitride tops and the trenches include non-gallium floors. Gallium nitride is grown on the non-gallium nitride posts, including on the non-gallium nitride tops. Preferably, gallium nitride pyramids are grown on the non-gallium nitride tops and gallium nitride then is grown on the gallium nitride pyramids. The gallium nitride pyramids preferably are grown at a first temperature and the gallium nitride preferably is grown on the pyramids at a second temperature that is higher than the first temperature. The first temperature preferably is about 1000° C. or less and the second temperature preferably is about 1100° C. or more. However, other than temperature, the same processing conditions preferably are used for both growth steps.

Abstract: Methods of forming compound semiconductor layers include the steps of forming a plurality of selective growth regions at spaced locations on a first substrate and then forming a plurality of semiconductor layers at spaced locations on the first substrate by growing a respective semiconductor layer on each of the selective growth regions. The first substrate is then divided into a plurality of second smaller substrates that contain only a respective one of the plurality of semiconductor layers. This dividing step is preferably performed by partitioning (e.g., dicing) the first substrate at the spaces between the selective growth regions. The step of forming a plurality of semiconductor layers preferably comprises growing a respective compound semiconductor layer (e.g., gallium nitride layer) on each of the selective growth regions. The growing step may comprise pendeoepitaxially growing a respective gallium nitride layer on each of the selective growth regions.

Abstract: More specifically, gallium nitride semiconductor layers may be fabricated by etching an underlying gallium nitride layer on a sapphire substrate, to define at least one post in the underlying gallium nitride layer and at least one trench in the underlying gallium nitride layer. The at least one post includes a gallium nitride top and a gallium nitride sidewall. The at least one trench includes a trench floor. The gallium nitride sidewalls are laterally grown into the at least one trench, to thereby form a gallium nitride semiconductor layer. However, prior to performing the laterally growing step, the sapphire substrate and/or the underlying gallium nitride layer is treated to prevent growth of gallium nitride from the trench floor from interfering with the lateral growth of the gallium nitride sidewalls of the at least one post into the at least one trench.

Abstract: A sidewall of an underlying gallium nitride layer is laterally grown into a trench in the underlying gallium nitride layer, to thereby form a lateral gallium nitride semiconductor layer. Microelectronic devices may then be formed in the lateral gallium nitride layer. Dislocation defects do not significantly propagate laterally from the sidewall into the trench in the underlying gallium nitride layer, so that the lateral gallium nitride semiconductor layer is relatively defect free. Moreover, the sidewall growth may be accomplished without the need to mask portions of the underlying gallium nitride layer during growth of the lateral gallium nitride layer. The defect density of the lateral gallium nitride semiconductor layer may be further decreased by growing a second gallium nitride semiconductor layer from the lateral gallium nitride layer. In one embodiment, the lateral gallium nitride layer is masked with a mask that includes an array of openings therein.

Abstract: A sidewall of an underlying gallium nitride layer is laterally grown into a trench in the underlying gallium nitride layer, to thereby form a lateral gallium nitride semiconductor layer. Microelectronic devices may then be formed in the lateral gallium nitride layer. Dislocation defects do not significantly propagate laterally from the sidewall into the trench in the underlying gallium nitride layer, so that the lateral gallium nitride semiconductor layer is relatively defect free. Moreover, the sidewall growth may be accomplished without the need to mask portions of the underlying gallium nitride layer during growth of the lateral gallium nitride layer. The defect density of the lateral gallium nitride semiconductor layer may be further decreased by growing a second gallium nitride semiconductor layer from the lateral gallium nitride layer. In one embodiment, the lateral gallium nitride layer is masked with a mask that includes an array of openings therein.