Abstract: Process for hydrogenating at least one aromatic or polyaromatic compound contained in a hydrocarbon feedstock having a final boiling point of less than or equal to 650° C., said process being performed in the gas phase or in the liquid phase at a temperature of between 30 and 350° C., at a pressure of between 0.1 and 20 MPa, at a hydrogen/(aromatic compounds to be hydrogenated) mole ratio of between 0.1 and 10 and at an hourly space velocity (HSV) of between 0.05 and 50 h?1, in the presence of a catalyst comprising an active phase comprising nickel, said active phase not comprising any group VIB metal, and a support comprising an amorphous mesoporous alumina having a connectivity (Z) of greater than 2.7, the connectivity being determined from the nitrogen adsorption/desorption isotherms.

Abstract: A process for the preparation of a catalyst comprising palladium, a porous support with a specific surface area in the range 140 to 250 m2/g, said catalyst being prepared by a process comprising the following steps: a) preparing a colloidal solution of palladium oxide or palladium hydroxide in an aqueous phase; b) adding said solution obtained from step a) to said porous support at a flow rate in the range 1 to 20 litre(s)/hour; said porous support being contained in a rotary impregnation device functioning at a rotational speed in the range 10 to 20 rpm; c) optionally, submitting the impregnated porous support obtained from step b) to a maturation; d) drying the catalyst precursor obtained from step b) or c); e) calcining the catalyst precursor obtained from step d).

Abstract: Process for preparing alumina gel in a single precipitation step consisting of dissolving an aluminium precursor, aluminium chloride, in water, at a temperature of 10° C. to 90° C. such that the pH of the solution is from 0.5 to 5, for a period of 2 to 60 minutes, then adjusting the pH to 7.5 to 9.5 by adding a basic precursor, sodium hydroxide, to the solution obtained to obtain a suspension, at a temperature of 5° C. to 35° C., and for 5 minutes to 5 hours, followed by a filtration step, said process not comprising any washing steps. Also, novel alumina gel having a high dispersibility index, in particular a dispersibility index of more than 80%, a crystallite dimension of 0.5 to 10 nm, a chlorine content of 0.001% to 2% by weight and a sodium content of 0.001% to 2% by weight, the percentages by weight being expressed with respect to the total weight of the alumina gel.

Abstract: A novel alumina gel is described having an elevated dispersibility index, and in particular a dispersibility index greater than 70%, a crystallite size between 1 and 35 nm, and a sulphur content between 0.001% and 2% by weight, and a sodium content between 0.001% and 2% by weight, the weight percentages being expressed in relation to the total mass of alumina gel. The present invention also discloses the method for preparing said gel comprising at least one step of precipitating at least one aluminium salt, at least one step of heating the suspension obtained and a final heat treatment step for forming the alumina gel.

Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a new method for the preparation of a crystallized and shaped solid material, preferably in extruded form, of formula LiXx.2Al(OH)3,nH2O, wherein n is between 0.01 and 10, x is 1 when X is an anion selected from among chloride, hydroxide and nitrate anions, and x is 0.5 when X is an anion selected from among sulfate and carbonate anions, comprising a boehmite precipitation step a) under specific temperature and pH conditions, at least one basic mixing shaping step, wherein the method also comprises a final hydrothermal treatment step, all to increase the lithium adsorption capacity and the kinetics of adsorption of the materials obtained, compared with the materials of the prior art when it is used in a method for lithium extraction from saline solutions.

Abstract: Preparation of a catalyst comprising an oxide matrix and an active phase comprising nickel: —a calcined porous aluminium oxide is prepared; —the calcined porous aluminium oxide obtained is kneaded with a solution resulting from mixing one or more solution(s) of at least one nickel precursor and at least one solution of at least one organic compound which has at least one carboxylic acid function, or at least one alcohol function, or at least one ester function, or at least one amine function, or at least one amide function, in order to obtain a paste, wherein the mole ratio of said organic compound to the nickel element is between 0.01 and 5.0 mol/mol; —the paste obtained is shaped; —the shaped paste obtained is dried at a temperature of less than 250° C. in order to obtain a dried catalyst.

Abstract: The present invention relates to the field of solid materials for the adsorption of lithium. In particular, the present invention relates to a novel process for preparing a solid crystalline material formed preferably in extrudate form, of formula (LiCl)x.2Al(OH)3,nH2O with n being between 0.01 and 10, x being between 0.4 and 1, comprising a step a) to precipitate boehmite under specific conditions of temperature and pH, a step to place the precipitate obtained in contact with a specific quantity of LiCl, at least one forming step preferably via extrusion, said process also comprising a final hydrothermal treatment step, all allowing an increase in lithium adsorption capacity and in the adsorption kinetics of the materials obtained compared to prior art materials, when used in a process to extract lithium from saline solutions.

Abstract: The present invention relates to the field of solid materials for adsorption of lithium. In particular, the present invention relates to a novel method for preparing a crystallized and shaped solid material, preferably as extrudates, of formula LiXx.2Al(OH)3, nH2O with n being comprised between 0.01 and 10, x being equal to 1 when X is an anion selected from among chloride, hydroxide and nitrate anions, and x being equal to 0.5 when X is an anion selected from among sulfate and carbonate anions, comprising a step a) for precipitation of boehmite under specific temperature and pH conditions, at least one shaping step, preferably by extrusion, said method also comprising a final hydrothermal treatment step, the whole giving the possibility of increasing the adsorption capacity for lithium as well as the adsorption kinetics of the materials obtained as compared with the materials of the prior art when the latter is used in a method for extracting the lithium from saline solutions.

Abstract: A process for the preparation of a catalyst comprising palladium, a porous support with a specific surface area in the range 140 to 250 m2/g, said catalyst being prepared by a process comprising the following steps: a) preparing a colloidal solution of palladium oxide or palladium hydroxide in an aqueous phase; b) adding said solution obtained from step a) to said porous support at a flow rate in the range 1 to 20 litre(s)/hour; said porous support being contained in a rotary impregnation device functioning at a rotational speed in the range 10 to 20 rpm; c) optionally, submitting the impregnated porous support obtained from step b) to a maturation; d) drying the catalyst precursor obtained from step b) or c); e) calcining the catalyst precursor obtained from step d).

Abstract: A catalyst comprising palladium, a porous support comprising at least one refractory oxide selected from the group constituted by silica, alumina and silica-alumina, the palladium content in the catalyst being in the range 0.01% to 2% by weight with respect to the total catalyst weight, at least 80% by weight of the palladium being distributed in a crust at the periphery of said support, the thickness of said crust being in the range 20 to 100 ?m, characterized in that said support is in the form of an extrudate and in that said support comprises a specific surface area in the range 165 to 250 m2/g.

Abstract: The present invention describes a process for hydrocracking at least one hydrocarbon feed in which at least 50% by weight of the compounds have an initial boiling point of more than 300° C. and a final boiling point of less than 540° C. using at least one catalyst comprising at least one metal from group VIB and/or at least one metal from group VIII of the periodic classification of the elements and a support comprising at least one zeolite containing at least one series of channels the opening of which is defined by a ring containing 12 oxygen atoms (12MR), and at least one binder, said support being prepared from a highly dispersible alumina gel, said hydrocracking process being operated at a temperature in the range 200° C. to 480° C.

Abstract: A catalyst comprises an active phase constituted by palladium, and a porous support comprising at least one refractory oxide selected from the group constituted by silica, alumina and silica-alumina, in which: the palladium content in the catalyst is in the range 0.0025% to 1% by weight with respect to the total weight of catalyst; at least 80% by weight of the palladium is distributed in a crust at the periphery of the porous support, the thickness of said crust being in the range 25 to 500 ?m; the specific surface area of the porous support is in the range 1 to 50 m2/g; the metallic dispersion D of the palladium is less than 20%.

Abstract: A catalyst comprises an active phase constituted by palladium, and a porous support comprising at least one refractory oxide selected from the group constituted by silica, alumina and silica-alumina, in which: the palladium content in the catalyst is in the range 0.0025% to 1% by weight with respect to the total weight of catalyst; at least 80% by weight of the palladium is distributed in a crust at the periphery of the porous support, the thickness of said crust being in the range 25 to 450 ?m; the specific surface area of the porous support is in the range 70 to 160 m2/g; the metallic dispersion D of the palladium is less than 20%.

Abstract: A supported catalyst, its method of preparation and use in hydrogenation methods, which catalyst contains an oxide substrate that is for the most part calcined aluminum and an active phase that contains nickel, with the nickel content between 5 and 65% by weight in relation to the total mass of the catalyst, with the active phase not containing a metal from group VIB, the nickel particles having a diameter that is less than or equal to 20 nm, the catalyst having a median mesopore diameter of between 14 nm and 30 nm, a median macropore diameter of between 50 and 200 nm, a mesopore volume that is measured by mercury porosimetry that is greater than or equal to 0.40 mL/g, and a total pore volume that is measured by mercury porosimetry that is greater than or equal to 0.42 mL/g.

Abstract: There is described a hydroprocessing process of at least one gas oil cut having a weighted mean temperature (TMP) between 240° C. and 350° C. using a catalyst comprising at least one metal of the group VIB and/or at least one metal of the group VIII of the periodic classification and a support comprising an amorphous mesoporous alumina having a connectivity (Z) greater than 2.7, the hydroprocessing process operating at a temperature between 250° C. and 400° C., at a total pressure between 2 MPa and 10 MPa with a ratio of hydrogen volume to volume of hydrocarbon-containing feedstock between 100 and 800 litres per litre and at an Hourly Volume Rate (HVR) which is defined by the ratio of the volume flow rate of liquid hydrocarbon-containing feedstock to volume of catalyst fed into the reactor between 1 and 10 h?1.

Abstract: The invention relates to a supported catalyst that comprises an oxide substrate that is for the most part calcined aluminum and an active phase that comprises nickel, with the nickel content being between 5 and 65% by weight of said element in relation to the total mass of the catalyst, with said active phase not comprising a metal from group VIB, the nickel particles having a diameter that is less than or equal to 20 nm, said catalyst having a median mesopore diameter of between 8 nm and 25 nm, a median macropore diameter of greater than 200 nm, a mesopore volume that is measured by mercury porosimetry that is greater than or equal to 0.30 mL/g, and a total pore volume that is measured by mercury porosimetry that is greater than or equal to 0.34 mL/g. The invention also relates to the method for preparation of said catalyst and its use in a hydrogenation method.

Abstract: A description is given of a process for hydrotreatment of at least one hydrocarbon feedstock having a weighted average temperature (WAT) of more than 380° C. using at least one catalyst containing at least one metal from Group VIB and/or at least one metal from Group VIII of the periodic table and a support containing an amorphous mesoporous alumina having a connectivity (Z) of more than 2.7, said hydrotreatment process operating at a temperature of between 250° C. and 430° C., at a total pressure of between 4 MPa and 20 MPa with a ratio of volume of hydrogen to volume of hydrocarbon feedstock of between 200 and 2 000 liters per liter and at an Hourly Volume Velocity (HVV) defined by the ratio of the volume flow of liquid hydrocarbon feedstock to the volume of catalyst fed into the reactor of between 0.5 and 5 h?1.

Abstract: An amorphous mesoporous alumina having a connectivity (Z) greater than 2.7 is described. The present invention also relates to the process for preparing the said alumina, comprising at least one precipitation step of at least one aluminum salt, at least one heating step of the suspension obtained, a thermal treatment step to form the alumina gel, a gentle drying step or spray drying step, a moulding step of the powder obtained, and a final thermal treatment step in order to obtain the alumina.

Abstract: A catalyst comprising a calcined oxide matrix which is mainly alumina and an active phase comprising nickel, said active phase being at least partially co-mixed within said calcined oxide matrix which is mainly alumina, the nickel content being in the range 5% to 65% by weight of said element with respect to the total mass of catalyst, said active phase not comprising any metal from group VIB, the nickel particles having a diameter of less than 15 nm, said catalyst having a median mesopore diameter in the range 12 nm to 25 nm, a median macropore diameter in the range 50 to 300 nm, a mesopore volume, measured by mercury porosimetry, of 0.40 mL/g or more and a total pore volume, measured by mercury porosimetry, of 0.45 mL/g or more. The process for the preparation of said catalyst, and its use in a hydrogenation process.

Abstract: A supported catalyst having a calcined, predominantly aluminum, oxide support and an active phase of 5 to 65% by weight nickel with respect to the total mass of the catalyst, said active phase having no group VIB metal, the nickel particles having a diameter less than or equal to 20 nm, said catalyst having a mesopore median diameter greater than or equal to 14 nm, a mesopore volume measured by mercury porosimetry greater than or equal to 0.45 mL/g, a total pore volume measured by mercury porosimetry greater than or equal to 0.45 mL/g, a macropore volume less than 5% of the total pore volume, said catalyst being in the form of grains having an average diameter comprised between 0.5 and 10 mm. The invention also relates to the process for the preparation of said catalyst and the use thereof in a hydrogenation process.