Abstract: A chemical vapor deposited, p phase polycrystalline silicon carbide having a high thermal conductivity and reduced stacking faults. The silicon carbide is synthesized under specific conditions using hydrogen gas and methyltrichlorosilane gas as reactants. The thermal conductivity of the silicon carbide is sufficiently high such that it can be employed as parts of apparatus and components of electrical devices where a high heat load is generated. Such components may include active thermoelectric coolers, heat sinks and fans.

Abstract: Free standing articles of chemical vapor deposited silicon carbide with electrical resistivities of less than 0.9 ohm-cm are provided without substantially degrading its thermal conductivity or other properties.

Abstract: Near net shape free standing articles can be produced by chemical vapor deposition techniques when a suitable substrate is suspended in a chemical vapor deposition zone according to the disclosed technique. By suspending such substrates from linear suspension supports such as ropes, cables and wires, multiple near net shape articles can be produced with substantial manufacturing cost savings over previously employed techniques.

Abstract: A process of producing relatively large, dense, free-standing silicon carbide articles by chemical vapor deposition is enabled by the provision of specially designed isolation devices. These devices segregate silicon carbide deposits on the intended portions of substrates, thereby alleviating the need to fracture heavy silicon carbide deposits in order to remove, or otherwise move, the substrate, with the heavy deposit thereon, from the deposition furnace. The isolation devices enable the use of more efficient vertically extended vacuum furnaces. The isolation devices also enable the commercial production of relatively dense, large, thin-walled, silicon carbide shells.

Abstract: A process of producing relatively large, dense, free-standing silicon carbide articles by chemical vapor deposition is enabled by the provision of specially designed isolation devices. These devices segregate silicon carbide deposits on the intended portions of substrates, thereby alleviating the need to fracture heavy silicon carbide deposits in order to remove, or otherwise move, the substrate, with the heavy deposit thereon, from the deposition furnace. The isolation devices enable the use of more efficient vertically extended vacuum furnaces. The isolation devices also enable the commercial production of relatively dense, large, thin-walled, silicon carbide shells.

Abstract: A method of forming a light weight, closed-back mirror. The mirror is formed as a monolithic construction by the use of chemical vapor deposition techniques. A first deposition forms sheets of the material, which are machined to the proper size to form reinforcing ribs. A sacrificial mandrel is formed with grooves to receive the ribs in their assembled positions. The upper surface of the mandrel is in proximity to the rear edges of the ribs to form a substantially continuous surface. The mandrel and ribs are then subjected to a chemical vapor deposition process which forms a first coating upon the outer face of the mandrel, forming a back plate and side wall. The mandrel is then turned over, and the base is removed by machining to expose the front edges of the ribs. This process leaves islands of mandrel material between the ribs to form a substantially continuous surface. The mandrel and ribs are then subjected to a chemical vapor deposition process.

Abstract: A susceptor for rapid thermal processing for epitaxial deposition upon semiconductor wafers. The susceptor includes an outer supporting ring upon which the wafer rests. This outer ring is preferably formed of a monolithic mass of silicon carbide, and most preferably high purity .beta.-phase (face-centered cubic) silicon carbide. The wafer is supported upon a small wafer shoulder on the ring. To prevent deposition upon the rear or bottom face of the wafer, a blocker shoulder is also provided in the ring, below the wafer shoulder, and a blocker is placed upon this shoulder. The blocker is preferably formed of quartz, and simply rests upon the shoulder. In this manner the ring and blocker may expand at different rates upon the rapid temperature changes, and the blocker or ring may be replaced.

Abstract: Silicon carbide is produced by chemical vapor deposition at temperatures from 1340.degree.-1380.degree. C., deposition chamber pressures of 180-200 torr, H.sub.2 /methyltrichlorosilane ratio of 4-10 and deposition rate of 1-2 .mu.m/min. Furthermore, H.sub.2 supplied as a part of the gas stream contains less than about 1 part per million (ppm) O.sub.2 gas, and various means are provided to exclude particulate material from the deposition chamber. The silicon carbide is polishable to <5 .ANG. RMS as measured on a Talystep mechanical profiler and has a thermal conductivity of at least about 300 W/mk. The silicon carbide is particularly suitable for applications where high polishability and thermal conductivity is desired, such as hard disc drives and read/write heads of head-disc assemblies, and also optical apparatus which require a very high polish.

Abstract: Silicon carbide is produced by chemical vapor deposition at temperatures from 1340.degree.-1380.degree. C., deposition chamber pressures of 180-200 torr, H.sub.2 /methyltrichlorosilane ratio of 4-10 and deposition rate of 1-2 .mu.m/min. Furthermore, H.sub.2 supplied as a part of the gas stream contains less than about 1 part per million (ppm) O.sub.2 gas, and various means are provided to exclude particulate material from the deposition chamber. The silicon carbide is polishable to <5 .ANG. RMS as measured on a Talystep mechanical profiler and has a thermal conductivity of at least about 300 W/mk. The silicon carbide is particularly suitable for applications where high polishability and thermal conductivity is desired, such as hard disc drives and read/write heads of head-disc assemblies, and also optical apparatus which require a very high polish.

Abstract: A process and apparatus for the manufacture of chemical vapor deposition deposited structures which comprises supplying a solid zinc metal continuously to a heated retort at a controlled rate. The retort is a body of refractory material having a top and a bottom and a traverse cross section which decreases from the top to the bottom of the retort. The zinc is melted, vaporized, and conveyed to a chemical vapor deposition zone defined by a number of heated mandrel plates where it is reacted with either hydrogen sulfide or hydrogen selenide to form a chemical vapor deposited structure. The process and apparatus provide for improved control over the evaporation rate of zinc and a reduction in the furnace volume needed to melt and vaporize the zinc.

Abstract: Silicon carbide is produced by chemical vapor deposition at temperatures from 1340.degree.-1380.degree. C., deposition chamber pressures of 180-200 torr, H.sub.2 /methyltrichlorosilane ratio of 4-10 and deposition rate of 1-2 .mu.m/min. Furthermore, H.sub.2 supplied as a part of the gas stream contains less than about 1 part per million (ppm) O.sub.2 gas, and various means are provided to exclude particulate material from the deposition chamber. The silicon carbide is polishable to <5 .ANG. RMS as measured on a Talystep mechanical profiler and has a thermal conductivity of at least about 300 W/mk. The silicon carbide is particularly suitable for applications where high polishability and thermal conductivity is desired, such as hard disc drives and read/write heads of head-disc assemblies, and also optical apparatus which require a very high polish.

Abstract: A process is disclosed for fabricating lightweight honeycomb type structures out of material such as silicon carbide (SiC) and silicon (S). The lightweight structure consists of a core to define the shape and size of the structure. The core is coated with an appropriate deposit such as SiC or Si to give the lightweight structure strength and stiffness and for bonding the lightweight structure to another surface. The core is fabricated from extremely thin ribs of appropriately stiff and strong material such as graphite. First, a graphite core consisting of an outer hexagonal cell with six inner triangular cells is constructed from the graphite ribs. The graphite core may be placed on the back-up side of a SiC faceplate and then coated with SiC to produce a monolithic structure without the use of any bonding agent. Cores and methods for the fabrication thereof in which the six inner triangular cells are further divided into a plurality of cells are also disclosed.

Abstract: A process is disclosed by which the finish and figure of polished preshaped structures (such as mirrors) can be replicated directly by chemical vapor deposition, with only minor polishing of the replica being required to obtain a final product, and with the original substrate being reusable for further replication. Relevant conditions under which the process can be carried out are given. Featured in the process is a pretreatment step prior to the deposition of a layer of silicon carbide to form the replica, which pretreatment step involves the formation on the polished substrate of an oxide layer and a carbon layer of high finish and uniform thickness. The carbon layer allows easy separation of the substrate and replica which otherwise would be bound together.

Abstract: A fluid dynamic method and apparatus effects the isolation of a predetermined deposition area in a hot-walled chemical vapor deposition chamber and limits the deposition to that area. The disclosed technique reduces stress and cracking in materials produced by chemical vapor deposition, prevents backside growth, and has particular utility in the fabrication by the chemical vapor deposition process of large, lightweight mirrors.