Abstract: Provided are various embodiments of a positive electrode for a secondary battery, which in one embodiment includes a first positive electrode material mixture layer formed on a positive electrode collector, and a second positive electrode material mixture layer formed on the first positive electrode material mixture layer, wherein the first positive electrode material mixture layer has an operating voltage of 4.25 V to 6.0 V and includes an active material for overcharge which generates lithium and gas during charge; a method of preparing such a positive electrode for a secondary battery; and a lithium secondary battery including such a positive electrode.

Abstract: A positive electrode material for a secondary battery, including a first positive electrode active material and a second positive electrode active material, wherein the first positive electrode active material and the second positive electrode active material consist of a lithium composite transition metal oxide including at least two or more transition metals selected from the group consisting of nickel (Ni), cobalt (Co) and manganese (Mn) are provided. The average particle size (D50) of the first positive electrode active material is two or more times larger than that of the second positive electrode active material, and the first positive electrode active material has a concentration gradient in which at least one of Ni, Co or Mn contained in the lithium composite transition metal oxide has a concentration difference of 1.5 mol % or more between the center and the surface of a particle of the lithium composite transition metal oxide.

Abstract: The present disclosure relates to a cathode additive, a method for preparing the same, and a cathode and a lithium secondary battery including the same.

Abstract: A positive electrode active material for a secondary battery including a core part and a shell part formed around the core part is provided. Here, the core part and the shell part include a lithium composite transition metal oxide including Ni and Co, and at least one or more selected from the group consisting of Mn and Al, and a ratio of the diameter of the core part to the total diameter of a particle of the positive electrode active material is 0.5 to 0.85, and the shell part has a concentration gradient such that a Ni concentration at the start point of the shell part near the core part is 30 mol % or higher than that at the end point of the shell part near the particle surface.

Abstract: A lithium cobalt-based positive electrode active material is provided. The lithium cobalt-based positive electrode active material includes a core portion including a lithium cobalt-based oxide represented by Formula 1 and a shell portion including a lithium cobalt-based oxide represented by Formula 2, wherein the lithium cobalt-based positive electrode active material includes 2500 ppm or more, preferably 3000 ppm or more of a doping element M based on the total weight of the positive electrode active material. An inflection point does not appear in a voltage profile measured during charging/discharging a secondary battery including the lithium cobalt-based positive electrode active material.

Abstract: The present invention provides a positive electrode active material precursor for a secondary battery which includes primary particles of Co3O4 or Co0OH, wherein the primary particle contains a doping element in an amount of 3,000 ppm or more, and has an average particle diameter (D50) of 15 pm or more, and a positive electrode active material for a secondary battery which includes particles of a lithium cobalt-based oxide, wherein the primary particle contains a doping element in an amount of 2,500 ppm or more, and has an average particle diameter (D50) of 15 ?m or more.

Abstract: The present disclosure relates to a positive electrode material which includes a first positive electrode active material, and a second positive electrode active material in the form of a single particle, wherein an amount of lithium impurities on a surface of the second positive electrode active material is 0.14 wt % or less based on a total weight of the second positive electrode active material, and at least one of nickel, cobalt, and manganese included in the second positive electrode active material has a concentration gradient gradually changing from the center of the particle to a surface thereof, a method of preparing the positive electrode material, and a positive electrode for a lithium secondary battery and a lithium secondary battery which include the positive electrode material.

Abstract: The present disclosure relates to a method for producing a positive electrode for a secondary battery, the method including applying a composition for forming a positive electrode on a positive electrode current collector to form a positive electrode mixture layer, and rolling the positive electrode mixture layer such that the elongation of the positive electrode current collector is less than 1%, to produce a positive electrode.

Abstract: Provided are a cathode active material including lithium transition metal phosphate particles, including a first secondary particle formed by agglomeration of two or more first primary particles, and a second secondary particle formed by agglomeration of two or more second primary particles in the first secondary particle, and a method of preparing the same. Since the cathode active material may include first and second primary particles having different average particle diameters, the exfoliation of the cathode active material from a cathode collector may be minimized and performance characteristics, such as high output characteristics and an increase in available capacity, of a secondary battery may be further improved.

Abstract: A positive electrode active material for a secondary battery is provided. The positive electrode active material being a lithium cobalt-based oxide includes a doping element M. A lithium cobalt-based oxide particle containing the doping element M in an amount of 3,000 ppm or more, wherein in a bulk portion corresponding to 90% of a core side among the radius from a core of the particle to a surface thereof, the doping element M in the lithium cobalt-based oxide particle is contained at a constant concentration, and in a surface portion from the surface of the particle to 100 nm in a core direction, the doping element M is contained at a concentration equal to or higher than that in the bulk portion and has a concentration in which the concentration thereof is gradient gradually decreased in the core direction from the surface of the particle.

Abstract: The present disclosure relates to a positive electrode material which includes a first positive electrode active material and a second positive electrode active material, wherein the second positive electrode active material has an electrical conductivity of 0.1 ?S/cm to 150 ?S/cm, which is measured after the second positive electrode active material is prepared in the form of a pellet by compressing the second positive electrode active material at a rolling load of 400 kgf to 2,000 kgf, a method of preparing the positive electrode material, and a positive electrode for a lithium secondary battery and a lithium secondary battery which include the positive electrode material.

Abstract: Provided are a positive electrode active material for a secondary battery, in which, since the positive electrode active material includes a lithium-metal oxide having high-temperature stability and a metal oxide on a surface of a particle and a surface side in the particle, there is no concern about gas generation, because the occurrence of cracks on the surface of the active material is prevented during charge and discharge, and high-temperature storage stability and life characteristics may be improved when the positive electrode active material is used in the battery, and a secondary battery including the same.

Abstract: A method for producing a positive electrode active material, a positive electrode active material produced thereby, and a positive electrode and a lithium secondary battery including the same are provided. The method includes preparing a nickel-manganese-aluminum precursor having an atomic fraction of nickel of 90 atm % or greater in all transition metals, and mixing the nickel-manganese-aluminum precursor, a cobalt raw material, and a lithium raw material and heat treating the mixture.

Abstract: A positive electrode material and a method of producing thereof is provided. The positive electrode material having a bimodal particle diameter distribution and including large-diameter particles and small-diameter particles, wherein the small-diameter particle is a lithium composite transition metal oxide in the form of a single particle and containing a rock salt phase formed on a surface portion thereof.

Abstract: A method for producing a high-nickel positive electrode active material, a positive electrode active material produced thereby, and a positive electrode and a lithium secondary battery including the same is provided. The method includes preparing a lithium composite transition metal oxide having a nickel content of 80 atm % or greater among transition metals, washing the lithium composite transition metal oxide, and mixing the washed lithium composite transition metal oxide with an aluminum raw material and heat treating the mixture at a temperature of 650° C. to 690° C. to obtain a positive electrode active material having a surface portion doped with aluminum.

Abstract: The present disclosure provides a preparing method of a positive electrode additive for a lithium secondary battery capable of reducing the amount of Li-based byproduct and unreacted lithium oxide generated in a preparing process, thereby significantly reducing the amount of gas generated when the electrode is operated.

Abstract: The present invention provides a negative electrode active material for a secondary battery, the negative electrode active material including a core that includes a lithium titanium oxide and a surface treatment layer located on a surface of the core, wherein the surface treatment layer includes a boron-containing lithium oxide at an amount that allows a boron content to have a molar ratio of 0.002 to 0.02 with respect to 1 mole of the lithium titanium oxide, and when 2 g of the negative electrode active material is titrated at pH 5 or lower using 0.1 M HCl, a titrated amount is 0.9 to 1.5 ml, and a secondary battery including the same. The negative electrode active material exhibits an excellent capacity recovery rate and an output characteristic when applied to a battery and is capable of reducing gas generation by preventing electrolyte decomposition.

Abstract: Provided is a positive electrode active material for a lithium secondary battery, the positive electrode active material being a secondary particle formed by agglomerating a plurality of polycrystalline primary particles including a lithium composite metal oxide of Chemical Formula 1, wherein an average crystallite size of the primary particle is 180 to 400 nm, an average particle size D50 of the primary particle is 1.5 to 3 ?m, and the primary particle is doped or surface-coated with at least one element M selected from the group consisting Al, Ti, Mg, Zr, Y, Sr, and B in an amount of 3,800 to 7,000 ppm: Lia(NixMnyCozAw)O2+b ??[Chemical Formula 1] in Chemical Formula 1, A, b, x, y, z, and w are the same as defined in the present specification.

Abstract: Disclosed herein is a high voltage cathode active material and a method for preparing the same. The cathode active material includes particles of a spinel-type compound having a composition represented by Formula (1) and a carbon-based material present on surfaces of the particles of the spinel-type compound: Li1+aMxMn2?xO4?zAz??(1) where ?0.1?a?0.1, 0.3?x?0.8 and 0?z?0.1.

Abstract: A positive electrode active material for a secondary battery is provided, which includes a lithium composite transition metal oxide including nickel (Ni), cobalt (Co), and manganese (Mn), wherein a particle of the lithium composite transition metal oxide includes a core portion and a resistance portion formed on a surface of the core portion, and is composed of a single particle, wherein the core portion has a layered crystal structure of space group R-3m, and the resistance portion has a cubic rock-salt structure of space group Fm-3m.