Composition comprising a liquid absorbed on a support based on precipitated silica

Abstract

The invention concerns a conditioned composition comprising at least a liquid absorbed on a support containing a precipitated silica, said silica being in the form of substantially spherical beads and having: a mean pellet size greater than 150 &mgr;m; a filling density in compact state (DRT) greater than 0.29; an oversize rate for a grid with mesh aperture size of 75 &mgr;m of at least 92% by weight. The invention also concerns the use of such a silica as a support for liquid.

Description

[0001] The present invention concerns a composition comprising a liquid, in particular a liquid supplement for animal feed, absorbed on a support based on a particular precipitated silica.

[0002] It also relates to the use of this silica as a support for liquid.

[0003] It is known to condition liquids, in particular animal feed additives, on solid supports, in particular on a silica support. The aim of this conditioning is generally to convert a liquid which is not, or not readily handleable into a fluid powder that can be stored with ease, for example in bags, and can be handled more straightforwardly, thus being readily dispersible and easy to mix with other divided solid constituents.

[0004] In the explanation which follows, the term conditioned composition will be used to refer to the composition thus obtained, that is to say a liquid absorbed on a silica support.

[0005] This conditioned composition is to be readily handleable, which implies a high degree of fluidity and little dust formation. It is also to contain a fairly large proportion of active material (liquid) and to have a high density. These various requirements are sometimes contradictory, and are often not fulfilled by the silica supports of the prior art.

[0006] The principal object of the invention is thus to provide a novel form of conditioned composition which furthermore advantageously has both a high degree of fluidity, produces very little or no dust and has a high density.

[0007] To this end, the Applicant Company has found it particularly satisfactory to use a precipitated silica which, amongst other things, has a highly specific morphology, in the case in point being in the form of substantially spherical beads, and a relatively high average particle size, as a support for liquids, in particular for vitamin E (or its acetate).

[0008] In the following explanation, the average particle size is measured according to the standard NF X 11607 (December 1970) by dry screening and determining the diameter corresponding to a 50% cumulative residue.

[0009] The packed filling density (PFD) is determined according to the standard NF T 30-042.

[0010] The DOP oil absorption value is measured according to the standard NF T 30-022 (March 1953) using dioctylphthalate.

[0011] The pore volumes which are given are measured by mercury porosymmetry; each sample may be prepared as follows: each sample is predried for 2 hours in an oven at 200° C., then placed in a test container within 5 minutes after removal from the oven and degassed under vacuum, for example using a rotary valve pump; the pore diameters are calculated using WASHBURN's relationship with a contact angle theta equal to 140° and a surface tension gamma equal to 484 dynes/cm (MICROMERITICS 9300 porosimeter).

[0012] The BET specific surface is determined according to the BRUNAUER-EMMET-TELLER method described in “The journal of the American Chemical Society”, Vol. 60, page 309, February 1938 and corresponding to the standard NF T 45007 (November 1987).

[0013] The CTAB specific surface is the external surface area determined according to the standard NF T 45007 (November 1987) (5.12).

[0014] The flow time tf of the conditioned compositions, which illustrates their flowability, is measured by passing 50 grams of product through a glass hopper with a calibrated orifice: cylinder diameter: 50 mm; cylinder height: 64 mm; cone angle: 530; passage diameter at cone base: 8 mm. According to this method, the hopper, which is closed at its base, is filled using 50 grams of product; then its base is opened and the transit time, referred to as the flow time tf of the product, after all of the said 50 grams have flowed through is noted.

[0015] The angle of repose is measured according to the standard NF T 20-221.

[0016] The composition according to the invention comprises at least one liquid absorbed on a support containing a precipitated silica, the said precipitated silica being in the form of substantially spherical beads, and having:

[0017] an average bead size in excess of 150 &mgr;m,

[0018] a packed filling density (PFD) in excess of 0.29,

[0019] a 75 &mgr;m screen oversize of at least 92% by weight.

[0020] The precipitated silica used in the conditioned composition according to the invention is thus in a highly specific form, in the case in point in the form of substantially spherical beads.

[0021] The average size of the said beads is in excess of 150 &mgr;m, and advantageously equal to at least 200 &mgr;m; in general, it is at most 320 &mgr;m, preferably at most 300 &mgr;m; it may be between 200 and 290 &mgr;m, in particular between 210 and 285 &mgr;m, for example between 215 and 280 &mgr;m. This size may, in particular, be between 260 and 280 &mgr;m.

[0022] The said precipitated silica has a fairly high density: its packed filling density (PFD) is in excess of 0.29. It is preferably at least 0.30, in particular at least 0.31. It may be at least 0.32.

[0023] This silica has a 75 &mgr;m screen oversize of at least 92% by weight, preferably at least 93% by weight. This means that at least 92% by weight, preferably at least 93% by weight, of the particles of this silica are retained by a screen whose mesh size is 75 &mgr;m.

[0024] This silica thus has a low proportion by weight of fine particles.

[0025] Even more preferably, its 75 &mgr;m screen oversize is at least 94% by weight, in particular at least 95% by weight; it may for example be at least 96% by weight, or even at least 97% by weight. It is generally at most 98% by weight, in particular at most 97.5% by weight.

[0026] The precipitated silica used in the conditioned composition according to the invention therefore produces little dust.

[0027] In general, it has an oil absorption value (DOP) of at least 250 ml/100 g, preferably between 250 and 280 ml/100 g. It may be between 255 and 275 ml/100 g, for example between 255 and 270 ml/100 g.

[0028] The said silica customarily has a pore volume (Vd1) made up of pores having a diameter smaller than 1 &mgr;m of less than 1.95 cm3/g, in particular of less than 1.90 cm3/g.

[0029] Its BET specific surface is generally between 140 and 240 m2 &mgr;g, in particular between 140 and 200 m2/g. It is for example between 150 and 190 m2/g. It may in particular be between 160 and 170 m2/g.

[0030] Its CTAB specific surface may be between 140 and 230 m2/g, in particular between 140 and 190 m2/g. It is for example between 150 and 180 m2/g, in particular between 150 and 165 m2/g.

[0031] It generally has a low moisture content; its moisture content (loss on drying at 105° C. for 2 hours) is preferably less than 5% by weight.

[0032] Advantageously, the silica employed in the composition according to the invention results from the use of a nozzle atomizer to dry a suspension of silica obtained by precipitation. Preferably, the said silica suspension to be dried has a solids content of between 22 and 24% by weight, preferably between 22.5 and 23.5% by weight.

[0033] This silica may be prepared according to a process of the type comprising the reaction of a silicate with an acidifying agent, by means of which a suspension of precipitated silica is obtained, following which this suspension is separated and dried using a nozzle atomizer, the precipitation being carried out in the following way:

[0034] 1) an initial stock solution is formed, containing at least some of the total amount of silicate employed in the reaction and, in general, at least one electrolyte, the silicate concentration (expressed as SiO2) in the said initial stock solution being less than 100 g/l, in particular 90 g/l, and the electrolyte concentration (for example sodium sulphate) in the said initial stock solution being less than 17 g/l, for example less than 14 g/l,

[0035] 2) the acidifying agent is added to the said stock solution until a pH value of at least about 7, generally between about 7 and 8, is obtained for the reaction medium,

[0036] 3) acidifying agent is added to the reaction medium, where appropriate together with the remaining amount of the silicate at the same time, the suspension to be dried having a solids content of between 22 and 24% by weight, in particular of between 22.5 and 23.5% by weight.

[0037] It should be noted in general that the process in question is a process for synthesizing silica by precipitation, that is to say an acidifying agent is reacted with a silicate under specific conditions.

[0038] The choice of the acidifying agent and of the silicate is made in a manner which is well known per se.

[0039] It may be recalled that the acidifying agent generally used is a strong inorganic acid such as sulphuric acid, nitric acid or hydrochloric acid, or an organic acid such as acetic acid, formic acid or carbonic acid.

[0040] The acidifying agent may be dilute or concentrated; its normality may be between 0.4 and 8 N, for example between 0.6 and 1.5 N.

[0041] In particular, in the case when the acidifying agent is sulphuric acid, its concentration may be between 40 and 180 g/l, for example between 60 and 130 g/l.

[0042] Any common form of silicate, such as metasilicates, disilicates and advantageously an alkali metal silicate, in particular sodium or potassium silicate, may moreover be used as the silicate.

[0043] The silicate may have a concentration, expressed as silica, of between 40 and 330 g/l, in particular between 60 and 300 g/l, for example between 60 and 250 g/l.

[0044] In general, sulphuric acid is used as the acidifying agent and sodium silicate is used as the silicate.

[0045] In the case when sodium silicate is used, it generally has an SiO2/Na2O weight ratio of between 2 and 4, for example between 3.0 and 3.7.

[0046] The initial stock solution generally comprises an electrolyte. The term electrolyte is intended to be understood here in its normal meaning, that is to say it indicates any ionic or molecular substance which, when it is in solution, decomposes or dissociates to form ions or charged particles. Examples of electrolytes which may be mentioned include a salt of the group consisting of the salts of the alkali and alkaline-earth metals, in particular the salt of the metal of the starting silicate and of the acidifying agent, for example sodium chloride in the case of reacting a sodium silicate with hydrochloric acid, or preferably sodium silicate in the case of reacting a sodium silicate with sulphuric acid.

[0047] In the (preferred) case of a starting stock solution comprising only some of the total amount of the silicate employed in the reaction, simultaneous addition of acidifying agent and the remaining amount of silicate is carried out in step (3).

[0048] This simultaneous addition is preferably carried out in such a way that the pH is continuously equal (to within +/−0.2) to the value reached at the end of step (2).

[0049] In general, in a subsequent step, an additional amount of acidifying agent is added to the reaction medium, preferably until the pH obtained for the reaction medium has a value of between 3 and 6.5, in particular between 4 and 6.5.

[0050] It may then be advantageous, after this addition of an extra amount of acidifying agent, to mature the reaction medium, it being possible for this maturation to last, for example, from 2 to 60 minutes, in particular from 3 to 20 minutes.

[0051] In the case of a starting stock solution containing the total amount of the silicate employed in the reaction, acidifying agent is preferably added in step (3) until a pH for the reaction medium is obtained with a value of between 3 and 6.5, in particular between 4 and 6.5.

[0052] It may then be advantageous, after this step (3), to mature the reaction medium, it being possible for this maturation to last, for example, from 2 to 60 minutes, in particular from 3 to 20 minutes.

[0053] The temperature of the reaction medium is generally between 70 and 98° C.

[0054] According to a variant of the process, the reaction is carried out at a constant temperature, preferably of between 80 and 95° C.

[0055] According to another (preferred) variant of the process, the temperature at the end of the reaction is higher than the temperature at the start of the reaction: thus, the temperature at the start of the reaction is preferably maintained at between 70 and 950 C, then the temperature is increased, preferably to a value of between 80 and 98° C., at which value it is maintained until the end of the reaction.

[0056] At the end of the steps which have just been described, a silica broth is obtained which is then separated (liquid/solid separation).

[0057] In general, the said separation comprises filtration and washing using a filter equipped with a compacting means.

[0058] This filter may be a belt filter equipped with a roller which performs the compaction.

[0059] Nevertheless, this filter is preferably a filter press, and the separation then generally comprises filtration, washing then compacting with the aid of the said filter.

[0060] The suspension of precipitated silica recovered in this way (filter cake) is then spray-dried using a nozzle atomizer.

[0061] It is highly advantageous for this suspension to have a solids content between 22 and 24% by weight, in particular between 22.5 and 23.5% by weight, immediately before it has been dried.

[0062] It should be noted that the filter cake is not always in a form suitable for atomization, in particular because it has high viscosity. In a manner which is known per se, the cake is then subjected to a crumbling operation. This operation may be carried out by passing the cake through a mill of the colloidal or ball type. The crumbling is generally carried out in the presence of an aluminium compound, in particular sodium aluminate. The crumbling operation makes it possible, in particular, to lower the viscosity of the suspension which is subsequently to be dried.

[0063] The Applicant Company has found that the precipitated silica as defined above, therefore having a highly specific morphology, in the case in point being in the form of substantially spherical and dense beads, and a relatively large average particle size, had a high degree of fluidity and produced little dust, and was particularly well suited to the conditioning of liquids.

[0064] Examples of liquids which may be mentioned include, in particular, organic liquids such as organic acids, surfactants, for example used in detergents, either of the ionic type such as sulphonates or of the non-ionic type such as alcohols, organic additives for rubber, and pesticides. Preservatives (phosphoric acid, propionic acid in particular), flavourings and colorants may be used as the liquids.

[0065] The Applicant Company has observed that the precipitated silica described above was particularly suited to the conditioning of nutritional supplements in liquid form, in particular for animal feed.

[0066] The liquid contained in the conditioned composition according to the invention is thus preferably a liquid supplement for animal feed. Mention may be made in particular of choline, its chloride salt, vitamins such as vitamins A, B, C, D, K and, preferably, vitamin E (or its acetate).

[0067] The operation of absorbing the liquid on the support based on the said precipitated silica may be carried out in the conventional way, in particular by spraying the liquid onto the silica in a mixer.

[0068] Although the amount of liquid absorbed generally depends on the intended application, the composition according to the invention customarily has, in particular in the case of vitamin E (or its acetate), a liquid content of at least 50% by weight, in particular between 50 and 65% by weight, especially between between 50 and 60% by weight (relative to the total weight of the composition); it may for example be between 52 and 56% by weight.

[0069] Even higher liquid contents may be used, in particular in the case of the chloride salt of choline.

[0070] Owing to the presence of the precipitated, silica having the abovementioned characteristics, the conditioned composition according to the invention advantageously produces very little or no dust and has an excellent degree of fluidity, these properties being combined with a high density.

[0071] Thus, preferably, the said precipitated silica provides this composition, in particular in the case of vitamin E (or of its acetate), with a 75 &mgr;m screen oversize of at least 97% by weight, in particular of at least 98% by weight. This ratio, in particular in the case of vitamin E (or of its acetate), is preferably at least 99% by weight, for example at least 99.5% by weight, or even at least 99.7% by weight; it may even be at least 99.8% by weight. This composition thus has an extremely low proportion by weight of fine particles. It therefore produces little or no dust.

[0072] Furthermore, the conditioned composition according to the invention, in particular in the case of vitamin E (or of its acetate), preferably has a flow time tf (measured for 50 grams of product and for a passage diameter of 8 mm) of less than 10 seconds, in particular of less than 9 seconds and, for example, at most 8 seconds, which evinces it excellent degree of fluidity.

[0073] It may be noted that the angle of repose of this composition, in particular in the case of vitamin E (or of its acetate) is generally at most 31°, and may be less than 30°.

[0074] The conditioned composition according to the invention, in particular in the case of vitamin E (or of its acetate), customarily has a packed filling density (PFD) of at least 0.63, for example of at least 0.65, and the value may be at least 0.70.

[0075] The invention also relates to the use of the precipitated silica described above as a support for liquid, such as for example one of the liquids mentioned above.

[0076] The following example illustrates the invention, but without limiting its scope.

EXAMPLE

[0077] 1) The following ingredients:

[0078] 345 litres of water

[0079] 7.5 kg of Na2SO4

[0080] 586 litres of aqueous sodium silicate having an SiO2/Na2O weight ratio equal to 3.5 and a density at 20° C. equal to 1.133 are introduced into a stainless-steel reactor fitted with an impeller stirring system and a jacket heating system.

[0081] The silicate concentration expressed as SiO2, in the initial stock solution is thus 85 g/l. The mixture is then heated to a temperature of 79° C. while continuing to stir it. 386 litres of dilute sulphuric acid, with a density at 20° C. equal to 1.050, are then introduced therein until a pH equal to 8.0 is obtained in the reaction medium (value measured at the temperature of the medium). The reaction temperature is 79° C. for the first 25 minutes; it is then increased from 79 to 86° C. in 15 minutes, then maintained at 86° C. until the end of the reaction. 83 litres of aqueous sodium silicate, of the type described above, and 134 litres of sulphuric acid, also of the type described above, are then jointly introduced into the reaction medium (that is to say when the pH of the reaction medium has reached a value of 8.0), this simultaneous introduction of acid and of silicate being carried out in such a way that the pH of the reaction medium is continuously equal to 8.0±0.1 throughout the introduction period. After all of the silicate has been introduced, introduction of the dilute acid is continued for 9 minutes so as to bring the pH of the reaction medium to a value equal to 5.2. After this introduction of acid, stirring of the reaction broth which is obtained is continued for 5 minutes.

[0082] The total reaction time is 119 minutes.

[0083] A precipitated silica broth or suspension is thus obtained, which is then filtered and washed using a filter press with vertical plates (the said plates being equipped with a deformable diaphragm allowing the filter cake to be compressed by introducing pressurized air), at a pressure of 7.5 bar and for the time needed to obtain a silica cake whose loss on ignition is equal to 77.1% (therefore a solids content of 22.9% by weight).

[0084] The cake obtained is then fluidized by mechanical and chemical action (addition of an amount of sodium aluminate corresponding to an Al/SiO2 weight ratio of 3000 ppm). After this crumbling operation, the resulting broth, with a pH equal to 6.6, is dried using a nozzle atomizer.

[0085] The precipitated silica P1 which is obtained is in the form of substantially spherical beads and has the following additional characteristics: 1 average particle size 270 &mgr;m PFD 0.31 75 &mgr;m screen oversize 96.7% DOP oil absorption 265 ml/100 g value pore volume (Vd1) made <1.90 cm3/g up of pores with d < 1 &mgr;m BET specific surface 165 m2/g CTAB specific surface 156 m2/g

[0086] 2) The vitamin E is placed on a support formed by the silica P1 prepared in 1).

[0087] The vitamin E is placed on the support in a 7-litre V mixer rotating at 20 rpm, with an inner shaft rotating at 1900 rpm, fitted with plates through which the vitamin E is sprayed, and on which emitter blades are fixed.

[0088] All of the silica P1 is introduced into the mixer, then the vitamin E is sprayed (at a temperature of 70° C. and at a rate of 100 ml/min) onto this silica. Mixing is carried out for 15 minutes, then homogenization is carried out for a further 2 minutes.

[0089] The conditioned composition then obtained contains 45% by weight of precipitated silica P1 and 55% by weight of vitamin E, and has the following additional characteristics: 2 75 &mgr;m screen oversize 99.7% flow time tf 8 seconds angle of repose 29.9° PFD >0.65

[0090] This conditioned composition based on a precipitated silica support, in the form of substantially spherical beads, thus has a very high degree of fluidity (which is illustrated in particular by a short flow time tf) and produces a negligible amount of dust (which is illustrated in particular by a very high 75 &mgr;m screen oversize), while having a high density.

Claims

1. Conditioned composition comprising at least one liquid absorbed on a support containing a precipitated silica, characterized in that the said silica is in the form of substantially spherical beads and has:

an average bead size in excess of 150 &mgr;m,

a packed filling density (PFD) in excess of 0.29,

a 75 &mgr;m screen oversize of at least 92% by weight.

2. Composition according to claim 1, characterized in that the said silica has an average bead size of at least 200 &mgr;m, in particular between 200 and 290 &mgr;m.

3. Composition according to one of claims 1 and 2, characterized in that the said silica has a packed filling density of at least 0.30, in particular of at least 0.31.

4. Composition according to one of claims 1 to 3, characterized in that the said silica has a 75 &mgr;m screen oversize of at least 93% by weight, in particular of at least 94% by weight.

5. Composition according to one of claims 1 to 4, characterized in that the said silica has a DOP oil absorption value of at least 250 ml/100 g, preferably between 250 and 280 ml/100 g, in particular between 255 and 275 ml/100 g.

6. Composition according to one of claims 1 to 5, characterized in that the said silica has a pore volume (Vd1) made up of pores having a diameter smaller than 1 &mgr;m of less than 1.95 cm3/g, in particular of less than 1.90 cm3/g.

7. Composition according to one of claims 1 to 6, characterized in that the said silica results from the use of a nozzle atomizer to dry a suspension of silica obtained by precipitation.

8. Composition according to claim 7, characterized in that, before it is dried, the said silica suspension has a solids content of between 22 and 24% by weight, preferably between 22.5 and 23.5% by weight.

9. Composition according to one of claims 1 to 8, characterized in that the said composition has a liquid content of at least 50% by weight, in particular between 50 and 65% by weight.

10. Composition according to one of claims 1 to 9, characterized in that the said liquid is a preservative, a flavouring, a colorant or a liquid supplement for animal feed.

11. Composition according to one of claims 1 to 10, characterized in that the said liquid is vitamin E or vitamin E acetate.

12. Composition according to one of claims 1 to 11, characterized in that the said composition has a 75 &mgr;m screen oversize of at least 97% by weight, in particular of at least 98% by weight.

13. Composition according to one of claims 1 to 12, characterized in that the said composition has a flow time tf of less than 10 seconds for 50 grams and for a passage diameter of 8 mm, preferably of less than 9 seconds.

14. Use of a precipitated silica as a liquid support, in particular as a liquid supplement for animal feed, characterized in that the said silica is in the form of substantially spherical beads and has:

an average bead size in excess of 150 &mgr;m, preferably in excess of 200 &mgr;m,

a packed filling density (PFD) in excess of 0.29, preferably of at least 0.30,

a 75 &mgr;m screen oversize of at least 92% by weight, preferably of at least 93% by weight.

15. Use according to claim 14, characterized in that the said silica has a DOP oil absorption value of at least 250 ml/100 g, preferably between 250 and 280 ml/100 g.

16. Use according to one of claims 14 and 15, characterized in that the said silica has a pore volume (Vd1) made up of pores having a diameter smaller than 1 &mgr;m of less than 1.95 cm3/g, in particular of less than 1.90 cm3/g.

17. Use according to one of claims 14 to 16, characterized in that the said silica results from the use of a nozzle atomizer to dry a suspension of silica obtained by precipitation, the said silica suspension preferably having a solids content of between 22 and 24% by weight before it is dried.

18. Use according to one of claims 14 to 17, characterized in that the said liquid is vitamin E or vitamin E acetate.