Polymers with high internal free volume
Shape-persistent organic materials, including polymers, with large degrees of interior free volume are described, along with behaviors and phenomena enabled by their unique properties. One class of such a material is built up from triptycene base moieties wherein three benzene rings are bridged together about a [2.2.2] tricyclic ring system. These units can be assembled into discreet molecules and polymers. These materials and/or formulations thereof with liquid crystals or polymers are useful for the complexation of chemicals and/or polymers; they have very low dielectric constants for use as coatings in dielectric circuits, they provide additional ordering mechanisms in liquid crystals, and they display unusual mechanical responses when subjected to electrochemical, chemical, or mechanical stimuli.
Latest Massachusetts Institute of Technology Patents:
This application is a continuation of U.S. patent application Ser. No. 10/764,768, filed Jan. 26, 2004, which is a continuation of U.S. patent application Ser. No. 09/935,060, filed Aug. 21, 2001 which claims benefit under 35 U.S.C. § 119(e) of priority to Provisional Application Ser. No. 60/226,506, filed Aug. 21, 2000, both of which are incorporated herein by reference.GOVERNMENT FUNDING
This invention was made with government support under Contract Number DABT63-97-C-0008, awarded by the Army and Grant Number N00014-97-0174 awarded by the Navy. The government has certain rights in the invention.BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to organic/polymer chemistry, and more particularly to molecules such as polymers, that can incorporate triptycenes and iptycenes.
2. Description of Related Art
Many materials and molecules have rigid structures that can be said to be shape-persistent. Aromatic, conjugated and polycyclic structures are typically their principle building blocks, and are the base architectures that provide the anisotropic characteristics of liquid crystals and high strength polymers. In general, these materials have flat two-dimensional structures and low degrees of internal free volume.
In contrast, chemical structures that have relatively high internal free volumes include those of the iptycenes. Typical applications of iptycenes and related structures have been as groups to prevent aggregation of polymers, thermally stable elements in structural polymers, and as a rigid scaffolds to define a molecular receptor.SUMMARY OF THE INVENTION
The invention comprises materials, compositions and methods that have, as one element, a shape-persistent material with a high degree of internal free volume. In another aspect, the invention comprises new materials, or known shape-persistent materials with high degree of internal free volume that are used in new ways.
In one embodiment, the invention provides a composition comprising a ladder polymer or an oligomer that comprises an iptycene.
In another embodiment, the invention provides a composition comprising an iptycene, having a molecular weight in excess of 2,000 daltons. The composition comprises a shape-persistent molecule containing bridgehead atoms, with molecular structures radiating from the bridgehead atoms in three directions and extending outwardly therefrom such that each defines a van der Waals contact of furthest point from the bridgehead atoms of no less than 3.5 Å. The composition can be a linear polymer or a ladder polymer. In one embodiment, the composition is arranged as a dielectric material in an electronic component. When the composition defines a polymer, the polymer can include a backbone having backbone atoms bonded to other backbone atoms, where bonds involving the backbone atoms are not freely rotatable.
The compositions described herein have a high degree of free volume, for example, at least 20%, 30%, 50%, 70% or 90% free volume, as defined below. Shape-persistent molecules with higher free volume can be used to improve alignment or orientation of one molecule to another. A variety of exemplary structures, both of polymeric shape-persistent molecules or monomers that can be used alone or can be polymerized to form polymers are described herein. It is to be understood that all examples of monomers and/or polymers described herein can be used in connection with any aspect or embodiment of the invention in which a shape-persistent molecule or polymer is desirable.
Where polymers of the invention are provided, they can comprise polymer chain units including chemical functionality allowing the formation of grafts. One polymer includes a grafted polymer including iptycene or non-iptycene units grafted onto polymer chains. Or, iptycene and non-iptycene units can be used in combination in such a graft polymer. Polymers can be formed of monomer units, each including two reactive sites, one of which has reacted with another monomer unit to form the polymer backbone, and another of which is available for grafting after formation of the polymer.
As noted, high free-volume, shape-persistent structures can be used as dielectrics. Dielectric structures having a dielectric constant of about 1.9 or less, preferably 1.7, 1.5 or 1.2 or less are provided in accordance with the invention.
The invention provides negative Poisson ratio (NPR) materials. One set of materials includes polymeric shape-persistent structures having small pores, on the order of 3-6 Å in size, through which a second polymeric material can be threaded to form an interpenetrating network. For example, polyiptycenes will form porous materials, as described below, and a generally planar structure perpendicular to the pores. Where a flexible polymer interpenetrates pores of such structures, applying tension to the interpenetrating polymer can cause the polyiptycenes to align in a generally planar/planar fashion, causing a greater degree of order between generally planar polyiptycene structures, thereby increasing the free volume of the overall structure. This can define a NPR material. That is, when tension is not applied to the interpenetrating polymer, the generally planar polyiptycene structures are allowed to rotate or otherwise orient themselves in a low-energy, random configuration. This will tend to minimize free volume. When tension is applied to the interpenetrating polymer, the generally planar polyiptycene structures will be moved into alignment generally parallel to each other, forming a higher-energy, higher free-volume structure. The interpenetrating polymer can be, for example, a conjugated polymer, an elastomer, or the like.
In another aspect, the invention comprises a first component comprising a first, porous shape-persistent polymeric component, and a second polymeric component forming an interpenetrating network. The network permeates the pores of the first polymeric component.
As mentioned above, shape-persistent molecules of the invention can assist in alignment or orientation of one molecule to another. This can be important in optical technology, such as liquid crystal display (LCD) technology. Liquid crystals are molecules which, when non-aligned with each other, are generally transparent. When an electric field is applied, they can be made to orient in alignment with each other, becoming opaque. Color LCD displays include liquid crystal molecules in conjunction with chromophores, including dyes. Contrast in color LCD displays is maximized (a significant advantage) when chromophores can be made to align with LCD molecules. The present invention involves including a shape-persistent molecule in conjunction with a chromophore in a LCD matrix. The shape-persistent molecule can assist the alignment of the chromophore with LCD molecules. For example, a shape-persistent molecule with a high degree of free volume can be covalently attached to a dye and combined with LCD molecules. When energy is applied to the system which generally causes LCD molecules to align with each other, the shape-persistent molecule can interact with the LCD molecules to maximize alignment of the dye with the LCD molecules. This is described in greater detail below and demonstrated in the examples section. This increase in alignment between two molecules with the assistance of a shape-persistent molecule can be used in essentially any arrangement in which improved alignment is desired, not limited to LCD systems.
Accordingly, in one embodiment the invention provides a composition including a chromophore, a shape-persistent molecule having at least 20% free volume, and a host material within which the shape-persistent molecule self-orients. The host material can be, for example, LCD molecules.
In another embodiment, the invention involves a method comprising providing a first molecular species in association with a shape-persistent molecule having a high degree of internal free volume, and a second molecular species. The method involves causing a change in orientation of the second molecular species and allowing the shape-persistent molecule to thereby alter the orientation of the first molecule in response to the change in orientation of the second molecule. An example of this involves a second molecular species comprising LCD host material and a first molecular species comprising a dye covalently bonded to an iptycene. A change in orientation of the LCD host material (e.g., alignment) causes a change in orientation of the dye as directed by the iptycene, namely, the dye can orient in alignment with the LCD host material. Translation, as well as or instead of orientation, can be affected in this manner as well.
Shape-persistent molecules of the invention typically include at least two aromatic rings, each parallel to a common axis in a lowest energy state of the composition.
In another embodiment, the invention comprises a composition including a plurality of liquid crystalline species. Each has a primary axis aligned so as to together define an average axis of the liquid crystalline species primary axes. A plurality of chromophores are provided, each having a primary axis aligned so as to together define an average axis of the chromophore primary axes. The alignment of the individual chromophores relative to the average axis of the chromophore primary axes includes less variation than the alignment of the individual liquid crystalline species relative to the average axis of the liquid crystalline species primary axes.
In another embodiment, the invention provides a size-exclusion article. As used herein, “size-exclusion article” defines a material that will allow the passage of species of a particular size, but not allow passage of species larger than that size. Examples include filters, such as zeolite structures, etc. Size-exclusion articles of the invention can be defined by any species described herein that will form pores, such as a ladder polymer or oligomer comprising an iptycene, having pore sizes noted herein.
Compositions of the invention can enhance the modulus of polymeric compositions. This can be effected by blending compositions of the invention into existing polymer blends, forming copolymers, including compositions of the invention, or grafting compositions of the invention onto existing polymers. Accordingly, one composition of the invention includes a first component that is a polymer including an iptycene, and a second component. The second component typically is a high molecular weight linear polymer, such as one having a molecular weight greater than 5,000, 10,000 or 20,000 daltons. The composition has a greater strength compared to a composition that is identical, with the exception that it does not include the iptycene-containing polymer.
In another aspect, the invention comprises a chromophore and a shape-persistent molecule including at least two aromatic rings, each parallel to a common axis in a lowest energy state of the composition.
In another aspect, the invention comprises a composition comprising a shape persistent moiety with a high degree of internal free volume and a chromophore.
Other advantages, novel features, and objects of the invention will become apparent from the following detailed description of the invention when considered in conjunction with the accompanying drawings, which are schematic and which are not intended to be drawn to scale. In the figures, each identical, or substantially similar component that is illustrated in various figures is represented by a single numeral or notation. For purposes of clarity, not every component is labeled in every figure, nor is every component of each embodiment of the invention shown where illustration is not necessary to allow those of ordinary skill in the art to understand the invention.
Preferred, non-limiting embodiments of the present invention will be described by way of example with reference to the accompanying drawings in which:
The present invention provides new shape-persistent molecules with high internal free volume, and new uses and compositions based on these and previously known high internal volume shape-persistent molecules.
A “shape-persistent molecule,” as used herein, is a molecule with a significant amount of rigid structure, as is understood by those of ordinary skill in the art. Preferably, in a shape-persistent molecule, no portion of the molecule having a combined molecular weight of at least 15 g/mol may move relative to other portions of the molecule via rotation about a single bond. In other embodiments of shape-persistent molecules, no portion of the molecule having a molecular weight of greater than 25, 50, or 100 g/mol can move relative to other portions of the molecule via rotation about a single bond. Rigid structures may be provided, for example, by aromatic rings, cyclic structures, cyclic aromatic structures, and the like. For example, molecular structure 1 in
Many of the shape-persistent structures of the invention, and used in techniques of the invention, may belong to the class of polymers and molecules built up from structure 1, known as the iptycenes. Iptycenes and like molecules have previously been reported in, for example, Hart, “Iptycenes, Cuppendophanes and Cappedophanes,” Pure and Applied Chemistry, 65(1):27-34 (1993); or Shahlia et al., “Synthesis of Supertriptycene and Two Related Iptycenes,” Journal of Organic Chemistry, 56:6905-6912 (1991). Triptycene 1 as shown in
Various embodiments of the invention involve use of molecules comprising an iptycene, such as a triptycene. It is to be understood that structures comprising an iptycene include oligomers, polymers, and monomers. Polymers or oligomers comprising an iptycene can include those having a non-iptycene backbone with iptycene pendent groups or those having iptycenes that form part of the backbone. As an example of the latter class, a polymer can be made up of monomer iptycene building blocks that together form a ladder polymer.
The “internal free volume” or “free volume” of a molecule is defined as the volume in space taken up by a molecule, where boundaries defining the internal free volume span all projections or protrusions of the molecule. By way of illustration, a representation 200 in
Shape-persistent molecules may be considered to have a length, width, and thickness. These dimensions may be considered to span an imaginary box which the molecule, as defined by its van der Waals volume, may rest. The molecule may be positioned within the box, in relation to a set of x, y, and z axes, such that the shortest axis in the arrangement defines the molecule's thickness. The minimum thickness of a planar shape-persistent molecule may be defined as the distance between the portions of the molecule located above and below a plane within which the molecule can be defined (or which can be contained completely within the molecule), for example a plane defined by the carbon nuclei of benzene ring. For example, in a benzene ring, the van der Waals radii for the carbon atoms is about ±11.9 Å. A second example is a molecule such as [2.2.2]bicyclooctane, where the thickness of the molecule would be measured from the van der Waals contacts of the outer hydrogen atoms, or about 5.54 Å.
While these examples may have shape-persistent structures, it should be understood that these structures do not define the internal free volume. Rather, the internal free volume is defined by the volume in space taken up by the molecule, where boundaries defining the internal free volume span all projections or protrusions of the molecule. This can be easily understood with reference to
In one set of embodiments of the invention, shape-persistent materials of the invention have a minimum height or length of approximately 6.214 Å, a value based on the distance between the van der Waals contacts of the 1 and 4 hydrogen atoms of a benzene ring. In one set of embodiments, molecules of the invention include bridgehead atoms and the minimum distance that a molecule may extend in height or length from a bridgehead is 3.5 Å. In other embodiments, the minimum distance that a molecule may extend in height or length from a bridgehead is 4.0 Å, 4.5 Å, 5.0 Å, 5.5 Å, 6.0 Å, or 6.2 Å. Each bridgehead may be any suitable atom, for example, a carbon or a nitrogen atom. By way of illustration, molecules 210 and 215 in
In some embodiments, the length of the molecule may be at least twice the height of the molecule. The longer dimension may lie on a two-dimensional plane normal to that height. Other three-dimensional structures may also be built up from these two-dimensional structures.
Molecules of the invention, in preferred embodiments, have at least 20% free volume; preferably at least 30%, more preferably at least 50% free volume, more preferably greater than 70% free volume, and most preferably greater than 90% free volume.
Techniques for determining free volume may include determining the density of the rigid shape-persistent molecule itself, without solvent, and without other, like molecules or different molecules dispersed within the material to take up some of the free volume. Alternatively, or where this is impossible, free volume may be deduced from density measurements. For density measurements for determination of free volume, the density may be compared with a solvent of similar composition. Determination of free volume from density measurement may be carried out in a straightforward manner by those of ordinary skill in the art. For example, most hydrocarbons have a density between 0.7 g/ml and 0.9 g/ml, and many polymers have densities of about 0.8 g/ml; hence, lower densities may be indicative of free volume. For example, a density of 0.4 g/ml may indicate a free volume of about 50%.
As most flexible materials will adopt a structure that may minimize free volume, to maintain high free volume, the precise nature of the rigid shape-persistent structure may be important. Preferred shape-persistent structures used in the invention may minimize the interpenetration of shape-persistent structures into each other's free volume. Such interpenetration may decrease the net internal free volume.
In one aspect of the invention, known rigid shape-persistent structures with high degrees of free volume may be used to create new methods for the alignment of guest molecules or polymers in host polymers and liquid crystals. In one embodiment, a molecule with anisotropic optical properties also comprises a shape-persistent molecule such as an iptycene. For example, structure 1 in
In one set of embodiments of the present invention, compositions of the invention comprising iptycenes are provided that may have average molecular weights greater than 2000 grams/mole (“daltons”), preferably greater than 2500 daltons, and more preferably greater than 3000, 4000, or 5000 daltons. The materials may be soluble in common solvents, for example, selected from the group consisting of water, chloroform, carbon dioxide, toluene, benzene, hexane, dichloromethane, tetrahydrofuran, ethanol, acetone, and acetonitrile. The materials may be soluble in a least one of the solvents, or at least two, or three of any of these solvents. “Soluble” in this context means soluble at greater than 0.5 mg/ml, preferably greater than 1 mg/ml, more preferably greater than 5 mg/ml, and more preferably still greater than 10 mg/ml. The materials of the invention may also be preferably soluble in common liquid crystals (“LC”) such as cyano-biphenyls, bicyclohexyls, or cyclohexylphenyls, and may be miscible with common polymers such as polyethylene, polyvinyl chloride, poly(methyl methacrylate), polydimethylsiloxane, polyimides, polyisoprene, polypropylene, polystyrene, and co- and block polymers that include these.
One structural feature of one set of embodiments of the invention, the iptycenes, is that the [2.2.2]bicyclic ring system forms the intersections of planes defined by aromatic rings.
Another class of molecules of the invention are those molecules that include a [2.2.2]bicyclic ring system, with each branch of the system connecting to cyclic aromatics. Each of the bridgeheads in these molecules may be connected to three cyclic aromatics, and at least one of the cyclic aromatics may be connected to another [2.2.2] bridgehead-pair of center, or may be fused to another aromatic system (shares at least one bond in common with another aromatic system).
In some embodiments, at least two of the cyclic aromatics emanating from the central [2.2.2]system may be fused to another aromatic system or connected to another [2.2.2]center, and in other embodiments, all three cyclic aromatics may be fused to other aromatic systems or connected to a bridgehead center. For example, dienes, such as those shown in
In one set of embodiments shape-persistent, high-free-volume molecules are based upon structures disclosed in International Patent Publication WO 99/57528, published Nov. 11, 1999 and incorporated herein by reference. Specifically, with reference to
In a preferred embodiment, G and H may be the same or different, and each may be selected from the aromatic group consisting of:
I and J may be the same or different and each can be selected from the group consisting of:
Any hydrogen in G, H, I and J may be substituted by R2, where R2 can be selected from the group consisting of C1-C20 alkoxy, phenoxy, C1-C20 thioalkyl, thioaryl, C(O)OR3, N(R3)(R4), C(O)N(R3)(R4), F, Cl, Br, NO2, CN, acyl, carboxylate and hydroky. R3 and R4 may be the same or different, and each may be selected from the group consisting of hydrogen, C1-C20 alkyl, and aryl. Z1 may be selected from the group consisting of O, S and NR8 where R8 can be selected from the group consisting of hydrogen, C1-C20 alkyl, and aryl. Z2 may be selected from the group consisting of F, Cl, OR3, SR3, NR3R4 and SiR8R3R4.
A may be any shape-persistent molecule such as a cyclic aromatic. A can be similar to or identical to a branch G, H, I, or J, as shown in
Bicyclic ring systems of the invention may be produced via synthesis using the Diels-Alder reaction. Other structures may be used in certain embodiments in the invention, for example, ladder polymers or ribbon structures, which each may contain rigid aromatic rings systems. These and related structures may be used in combination with other features of the invention, such as attachment to dyes, “bundling” of molecules, and the like. As used herein, a “ladder” polymer is a polymer having a backbone that can only be severed by breaking two bonds.
In one embodiment of the invention, molecules for use in the formation of rigid shape-persistent polymers with high degrees of internal free volume may involve substitution about the bicyclic ring system, which may provide the needed geometry to provide internal free volume in the structure. In some embodiments of the invention, rigid shape persistent polymers with high degrees of internal free volume may be provided in which the distance from the bridgehead atom to the van der Waals contact of the most distant atom of the smallest substituent directly attached to the bridgehead carbon is more than 4 Å, preferably 5 Å, 6 Å, or 7 Å, or even greater. The significance of this group is that it serves to define additional free volume and internal surfaces, from which important organizational properties in conjunction with polymers and liquid crystals may be optimized. The larger groups further provide structures with greater shape persistence, since the polymers may not be easily collapsed and prevent the interpenetration of one polymer into another.
Larger molecules based upon the triptycene structure are called iptycenes. Their polymers are called polyiptycenes, for example, structure 225 in
In all of the figures, R, R′, and R″ can be the same or different. Preferably, R is H or a hydrocarbon group (including cyclic hydrocarbon groups), optionally interrupted by hetero groups. As used herein, “hydrocarbon” is meant to include alkyl, alkenyl, alkynyl, cycloalkyl, aryl, alkaryl, aralkyl, and the like. Hetero groups can include —O—, —CONH—, —CONHCO—, —NH—, —CSNH—, —CO—, —CS—, —S—, —SO—, —(OCH2CH2)nR (where n=1−10), —(CF2)n— (where n=1−10), olefins, and the like. As used herein, the terms “hydrocarbon,” “alkyl,” “cycloalkyl” and similar hydrocarbon terminology is meant to include alcohols and hydrogen. Examples of such groups are methyl, propenyl, ethynyl, cyclohexyl, phenyl, tolyl, benzyl, hydroxyethyl and the like. R is preferably selected from groups including hydrogen and the general class of lower alkyl compounds such as methyl, ethyl, or the like.
For example, R can be an alkyl group, preferably having 1 to 24 carbon atoms, more preferably 1 to 18 carbon atoms; an alkenyl group, preferably having 2 to 4 carbon atoms; an aminoalkyl group, preferably having 1 to 8 carbon atoms, and optionally substituted on the nitrogen atom with one or, preferably two alkyl groups, preferably having 1 to 4 carbon atoms; an alkyl group, preferably having 1 to 4 carbon atoms, having a five- or six-membered heterocyclic ring as a substituent; an allyloxyalkyl group, preferably having up to 12 carbon atoms; an alkoxyalkyl group, preferably having a total of 2 to 12 carbon atoms; an aryloxyalkyl group, preferably having 7 to 12 carbon atoms; an aralkyl group, or the like.
One polyiptycene structure is illustrated in
In some embodiments of the invention, shape-persistent molecules of the present invention may have high free volume and high thermal stability. Molecules with these characteristics may be useful in dielectric coatings for semiconductor devices. By using a low dielectric overcoat, the coupling between neighboring interconnects on semiconductor devices may be reduced. As the lowest dielectric constant possible of a vacuum, materials with high degrees of free volume, such as materials of the present invention, may posses low dielectric constants, and may be useful for reducing capacitive interactions between neighboring interconnects. Accordingly, one embodiment of the invention involves a low-dielectric material comprising a shape-persistent molecule such as an iptycene. Any of the structures falling within iptycene-like structures described herein can be used. In a preferred set of embodiments dielectric materials of the invention comprising shape-persistent molecules have a dielectric constant of less than 3.0, preferably less than 2.5, preferably less than 2.0, or preferably 1.5 or less. The invention includes electronic devices comprising dielectric components comprising the shape-persistent molecules as would be well-understood by those of ordinary skill in the art.
Additionally, molecules of the present invention may be fluorinated. Fluorinated molecules may display lower dielectric constants, and may further reduce capacitive interactions between neighboring interconnects on semiconductor devices. Altering the hydrophobicity of the molecules may further reduce capacitive interactions.
Shape-persistent polymers may also have solubilizing side chains. These chains may be chosen, for example, to be hydrocarbons or perfluoro groups. Desirable materials may include those that do not contain polar functionality, and may be reoriented or polarized by electric fields, giving a low dielectric constant. Furthermore, the molecular structures may be are chosen such that the molecules have no affinity for water, such as atmospheric water.
Examples of iptycenes contemplated by the present invention are illustrated in
As an illustrative example, in a shape-persistent polymer comprised only from benzoid rings and hydrocarbon side chains, the reduction in dielectric constant that will accompany the internal free volume can be determined as follows. For a material with 50% free volume, the dielectric constant may be reduced to about 1.55 (vacuum=1.0). For a material with 70% free volume, the dielectric constant may be about 1.33, and for 90% free-volume dielectric constant may be about 1.09. In contrast, conventional SiO2 dielectrics with the proper performance typically have dielectric constants of 3.5 to 4.0. Thus, a material with a composite of a shape-persistent materials and a polymer needed to meet other barrier and adhesive properties may be useful as a dielectric coating in high performance integrated circuits.
In one embodiment, the materials of the present invention incorporate free volume directly into the molecular design, allowing for greater uniformity of pore sizes, as well as smaller pore sizes. The present invention provides sub-nanoporous materials in accordance with one set of embodiments. “Sub-nanoporous” materials are defined herein as materials with pores smaller than 10 nm, preferably smaller than 5 nm, and more preferably smaller than 4 nm in size. The structures of the materials may be rigid and non-collapsible. The small pore size may decrease or eliminate metal diffusion and short-circuiting, or lower the dielectric constant of the material.
Polyiptycenes and other shape-persistent polymers disclosed here may have nanoscopic pockets of air, and may display high compressibility in particular directions. Accordingly, another aspect of the invention involves polymeric compositions of the invention constructed and arranged to absorb a compression-causing force. Such an arrangement would be understood by those of ordinary skill in the art, and includes constructions in essentially any known shock or force-absorbing structure such as an athletic shoe sole, automobile bumper, or any other cushioning structure.
In one embodiment, the shape-persistent polymers of the invention may be used to bind polymer chains together. The polymers function as molecular “clips” for polymers, keeping them bundled together and preventing them from splaying. These methods may be used to produce materials with large material strengths. Bundling materials together may prevent single chains from bearing a full load applied to a material.
In another embodiment, shape-persistent structures of the present invention may be used to bind molecules and polymers within their internal structures. The interaction of the shape-persistent structure with other molecules is anisotropic, providing a preferred orientation between elements. This effect produces a new method for aligning materials in liquid crystals and polymers. Host materials, such as liquid crystals or polymers, may fill the free volume as defined by the rigid shape-persistent guest. These structures may used in, for example, liquid crystals or polymer films.
The “aspect ratio” is defined as the ratio of the dimensions of the material. For alignment of a solute in a uniaxial polymer or liquid crystal matrix, the relevant aspect ratio is the longest axis of the material divided by its next longest axis. Alternative aspect ratios may be defined based on the specific nature of the solute.
An efficient packing may be accomplished by a “threading” mechanism wherein the liquid crystal packs within the iptycene void spaces, such as depicted in structure 255 in
The three-dimensional structures of triptycenes result in special solvation properties that may create unique solute orientations. The void spaces between aromatic triptycene faces allow threading of other small molecules, for example, liquid crystals, and macromolecules, for example, polymers, through these spaces. This interaction causes chromophores that are part of the iptycene backbone to align.
This alignment may be used, for example, in color liquid crystal displays. The organization of dichroic dyes in nematic liquid crystals may be required to make a color liquid crystal display. The contrast in these displays may be determined by the contrast ratio between the different states, resulting from the realignment of the liquid crystal director with an electric field. The liquid crystal director in a nematic liquid crystal may be defined as the average direction over which a large grouping of molecular long axes of the liquid crystal point. Control of the director direction may be accomplished in displays by surface forces and electric fields. The individual host molecules may be disordered and have a distribution of directions about the director. The absolute value of the average angle that the individual molecules deviate from the director (direction of orientation) may be used to calculate an order parameter. The size of this angle may be related to intermolecular interactions, thermal fluctuations, and the aspect ratio of the liquid crystals.
Conjugated polymers may be used to fabricate electronics devices. Applications in devices such as light emitting diodes, field-effect transistors, photovoltaic devices, and sensors may be envisioned. In one aspects of the invention, bulky properties of conjugated polymers may be tailored using controlled organization of the polymer chains.
The uniform or quasi-uniform orientation of conjugated polymers may be the result of in the increase of the conductivity and the emission of polarized light. Alignment of the molecules may be achieved using self-organizing liquid crystalline polymers, Langmuir-Blodgett films, or mechanical stretching. Alignment may also be achieved by dissolving the material (“guest”) in a liquid crystal (“host”). The directed orientation of solute molecules in liquid crystals takes place as a result of the anisotropic interactions between the two components, known as the “guest-host effect.”
The solubility of conjugated polymers may be increased by attaching pendant groups such as alkoxy, alkyl, alkylsilyl, or phenyl groups to the main chain. Incorporating iptycenes in poly(p-phenylene ethylene)s (“PPE”) or poly(p-phenylene vinylene)s (“PPV”) may minimize interpolymer chain contacts so as to increase the fluorescence efficiencies. PPVs may be prepared through the coupling between aryl diiodides and phenylene bis(vinylboronate) derivatives, similar to the coupling of arylborate and aryl halide (the “Suzuki” reaction) used in the synthesis of biaryl compounds. Due to the general requirement of highly pure difunctional monomers in step growth polymerizations, pinacol ester derivatives of bisvinyl borates were designated as monomers for the synthesis of PPVs to ensure efficient purification. Pinacol esters of organic borates are stable to column chromatography conditions, facilitating purification. Iptycene moieties may also be incorporated into other conjugated systems to generate polymers with variety of electronic properties. 1,4-diethynyltriptycenes may be prepared as a precursor for the synthesis of both PPV- and PPE-containing triptycene moieties.
If such a structure is dispersed in a liquid crystal or a stretched polymer, the structure may align in such a way that its longest axis lies perpendicular to the direction of orientation of the liquid crystal or the polymer. A composite material containing the shape-persistent polymer and a polymer such as, for example, polyethylene, can exhibit what is known as a negative Poisson ratio (“NPR”). Materials with such properties are also called “auxetics.” An NPR or an NPR material refers to the situation wherein a material being stretched along one axis will expand along another, contrary to what is typically exhibited by polymers.
Accordingly, another aspect of the invention involves use of materials and/or polymers of the invention in constructions making use of NPRs. NPR materials of the invention may be used as structural and mechanical materials. NPR materials of the invention may also be used as adhesives that, when delamination is attempted, the polymer filling the interstitial pores of an object expands and does not pull out of the structure in which it is embedded. NPR materials may also be used in, for example, fasteners or nails that resist any attempt to remove them by pulling. Since the Poisson ratio of a material has an effect on the transmission and reflection of internal stress waves, NPR materials of the invention define a new class of materials that more efficiently distribute stress around holes and cracks. This may be especially useful in, for example, sandwich paneling for aircraft and automobiles. Additionally, such sandwich paneling made from negative Poisson materials may adopt a much stronger convex shape upon bending rather than a saddle shape which positive Poisson material exhibit, and absorb impact without being damaged. This effect may make it difficult for a projectile or other object to puncture an object made from a negative Poisson material. Thus, NPR materials may also be used in the design of protective gear, such as, for example, bulletproof vests or shatterproof windows. In one set of embodiments, NPR materials of the invention are formed by assembling a network of polymeric shape-persistent material, such as structure 240 of
The function and advantage of these and other embodiments of the present invention will be more fully understood from the examples below. The following examples are intended to illustrate the benefits of the present invention, but do not exemplify the full scope of the invention.EXAMPLE 1
Triptycenes 25 and 26 in
Homeotropic alignment of 1 wt % mixtures of anthracene 24 and triptycenes 25 and 26 in 4-(trans-4-pentylcyclohexyl)benzonitrile was achieved using surface rubbed test cells to give uniaxial alignment. Polarized spectra of anthracene 24 in the nematic liquid crystal were consistent with previous literature reports, showing alignment of the molecules with their long-axes along the nematic liquid crystal director. The transition moment of the lowest energy vibronically-coupled absorption (320-380 nm) of anthracene 24 was short-axis polarized, and therefore gave larger UV-Vis absorption with light polarized perpendicular to the liquid crystal director. Observation of the polarization dependence of the similar absorption bands of the anthracenyl-moieties of triptycenes 25 and 26 allowed for detection of their orientation.
Upon measurement, the dichroic ratio of mixtures of triptycenes 25 and 26 were found to be the inverse of anthracene 24, shown in
The observed dependence implies that the alignment of the anthracene chromophores of the triptycenes was normal to the liquid crystal director, a result in which is opposite to the alignment expected on aspect ratio alone. This alignment was likely a result of the large free volume of the iptycene molecules. Based on the aspect ratio argument, triptycene 26 would be expected to align the most efficiently since it traces out larger void spaces due to its size; triptycene 25 would be expected to align poorly. However, triptycene 25 also showed good alignment. The smaller void spaces created by triptycene 25 were sufficient to align molecules showing the powerful effect of void spaces coupled with a rigid backbone.
As an elucidation of the “threading” model, thin solution-cast polyvinyl chloride films containing 1 wt % anthracene 24 and triptycenes 25 and 26 were prepared. These molecules were uniaxially stretched to impart macromolecular alignment. The enlarged UV-Vis window of polyvinyl chloride versus the liquid crystal allows observation of both the strong anthracene absorption at 250 nm as well as the weak 350 nm absorption. As with the liquid crystal host, anthracene 24 aligns with its long-axis along the stretching direction, while triptycenes 25 and 26 both showed a preference for alignment of their long axes normal to the stretching direction, as illustrated in
The preparation of ribbon-type polyiptycenes, illustrated in
Starting with 1,2,4,5-tetrabromobenzene, compound 607 was prepared by trapping the benzyne formed by addition of n-BuLi with 2,5-dioctylfuran. Then, TiCl4/Zn deoxygenation of 607 yielded naphthalene 608 which was converted to the desired compound 609 via trapping of the benzyne form by addition on PhLi with furan. The reaction of 602 and 609 in decalin at 190° C. for 2 days, yielded the Diels-Alder adduct 610 which was dehydrated to the anthracene 611 with polyphosphoric acid at 150° C. Finally, the quinone was obtained through demethylation with BBr3 in dichloromethane to obtain hydroquinone 612, then subsequent oxidation to the quinone 613 with AgO in acetone.
Another route to these monomers is illustrated in
To prepare epoxy-containing monomer 616, the previous synthetic scheme were slightly altered, as illustrated in
Multi-functional monomers may be required for forming hyperbranched polymers, as illustrated in
For multiple dieneophiles, anti-1,4:5,8-diepoxyanthacene 621 may be used, but synthesized monomer 618 containing two octyloxy-groups for increased solubility may also be used. The synthesis was started by adding alkyl groups to 2,3,5,6-tetrabromohydroquinone via a Williamson ether synthesis, giving compound 617. Then, trapping both benzynes formed from 617 with addition of PhLi in the presence of furan yielded monomer 618. Monomer 618 was produced in two diastereomers where both epoxy-groups are either in a syn- or anti-arrangement (53%:47% syn:anti), and were easily separated by column chromatography.
For multiple dienes, monomer 620 was synthesized, giving three anthracene moieties within one triptycene-like core. This was made by a Friedel-Crafts reaction of triptycene with phthalic anhydride in the presence of AlCl3. Then, ring closure of the tris-ketoacid with concentrated sulfuric acid gave compound 619. Conversion of 619 to 620 was achieved with Al/HgCl2 in cyclohexanol.EXAMPLE 5 Ring Opening Metathesis Polymerization (ROMP) Methods
Monomers for direct incorporation of iptycenes into the backbone of a processable polymer may require a reactive alkene for use in ring-opening metathesis polymerization. Along these lines, both diastereomers of 616 may be used, however, the tetrahydrofuran substructure in the resulting polymer would be less stable than the corresponding cyclopentane structure. To provide a more stable structure, monomer 623 was prepared, as illustrated in
Starting from monomer 613, Diels-Alder reaction of the quinone with freshly prepared cyclopentadiene in acetonitrile at 0° C. gave adduct 622. Subsequent tautomerization of the adduct with sodium hydride in DMF followed by methylation with dimethyl sulfate gave monomer 623.
Monomer 623 may be used as a co-monomer (1%-100%) with norbomene in ROMP polymerizations to produce a co-polymer 624 with iptycenes directly in the backbone. Hydrogenation of the remaining double bonds will produce a processable polymer 625 with a potentially negative Poisson ratio.EXAMPLE 6 Polymerization Results
Heating solid samples of diastereomers of 616 (fast-616; slow-616) for 1-4 hours to 200-250° C. under N2 yielded polymers of various sizes and polydispersities. By gel permeation chromatography (GPC), THF soluble fractions gave the molecular weights and polydispersities listed in TABLE 1. Addition of hyperbranched monomers 620 and 621 allowed for initial attempts at hyperbranched polyiptycenes. Mass spectroscopy may also be used to determine the extent and cleanliness of polymerization.
Hyperbranching allows for higher molecular weights with lower overall reaction yields. If all complementary groups are in equal numbers, 90% yields without hyperbranching gives an average degree of polymerization of 10; while hyperbranched monomers, with an average number of functional groups per monomer of 3, would give the same average degree of polymerization at 60% yield. However, imbalance in reactive groups tends to decrease the average molecular weight due to all chains being capped by the same monomer. This effect can be seen in the decreased molecular weight of Entry 6 of TABLE 1 versus Entry 4. However, hyperbranching does cause decreased solubility of the polymer. The maxima for most of the gaussians that describe each molecular weight distribution for Entries 1-7 lie in the 10,000-20,000-g/mol range. These weights correspond to average degrees of polymerization of 14-28 repeating units (based in 616). Ultimately, the fully aromatic polyiptycenes will be prepared by dehydration of 651 the intermediate polymers described above, via acid-catalyzed dehydration methods to yield 652.EXAMPLE 7 Triptycenes in Liquid Crystalline Displays
In this example, the extended free-volume guided alignment of triptycene was used to increase the alignment of commonly used dichroic dyes for liquid crystalline displays (LCDs). Dyes 0, 27, 28, 29 and 30, as illustrated in
Dyes 0, 27, 28, 29 and 30 were dissolved in a common liquid crystal host (1 wt % in 4-trans-(4-pentylcyclohexyl)benzonitrile) and homogeneously aligned in a rubbed polyimide coated test cell (10 μm thick). Polarized UV-Vis spectra, parallel and perpendicular to the liquid crystal alignment, were recorded and their observed order parameters calculated according to the following equation:
These results are summarized in TABLE 3. The polarized UV-Vis spectra for Dyes 0, 27, 28 and 29 are shown in
Dye 30 was designed under the assumption that pentiptycene would give a greater increase in alignment with respect to triptycene, due to its greater free-volume. However, dye 30 did not have increased alignment, but rather decreased with respect to dye 27. This can be attributed to the restricted environment around the central ring of the pentiptycene moiety. Only one liquid crystal molecule can occupy either face of the pentiptycene, where the U-shaped cavity prevents facile rotation, decreasing the local entropy. Triptycenes, on the other hand, allow for more rotational and positional entropy in the nematic liquid crystal. These can sense the director of the liquid crystal and act as a stabilizer-wing to average out the local motions of the host liquid crystal.
To further demonstrate the generality of the effect of the triptycenes on more complex dyes, Dyes 31 and 32 in
As in the previous case, the triptycenes were attached to the dye backbone such that their free-volume guided alignment was complimentary to the aspect-ratio guided alignment of the dye. This design increased in the order parameter with respect to dye 31 on the order of 9%. The polarized UV-Vis spectra for dyes 31 and 32 are shown in
As previously stated, increasing the aspect ratio of a dye may increase the order parameter of dichroic dyes. This is most often achieved by attachment of longer alkyl groups, or extending the size of the chromophore. By extending the dye design into an additional dimension, the size of the molecule is maintained. The overall length of the triptycene-containing dye molecules remains the same while the alignment is increased. This provides dyes with greater solubility without sacrificing alignment. This may be a very powerful tool for designing dichroic dyes with higher alignments for a variety of applications from guest-host reflective LCDs to holographic data storage. The synthesis of dyes 27-29, and 32-38 (dichroic and fluorescent), showing greater alignment, were synthesized and prepared as illustrated in
It is also possible for the dye itself, wither dichroic or fluorescent to be a liquid crystal. In particular, upon cooling from an isotropic state (I), compound 27 enters a nematic liquid crystalline phase (N) at 148° C. and crystallizes (C) at 123° C.
The nematic phase exhibited by 27 may afford the opportunity to make very concentrated solutions of dyes in other nematic liquid crystals used in display or non-linear optical applications since nematic liquid crystals are known to be continuously miscible in varying concentrations in other nematic liquid crystals. It may also be possible to make 27 and/or analogs to display a biaxial optical properties in the nematic phase (biaxial nematic liquid crystal).EXAMPLE 9
The synthesis of triptycene bis(vinyl-dioxoborolane) 43 is shown
In a similar manner, triptycene monomers 48 and 49 carrying two tert-butyl groups were prepared, as illustrated in
Two aryldiiodides 50 and 51, prepared following the procedure of Swager et al., Journal of Physical Chemistry, 99:4886-4893 (1995). Aryldiiodides 50 and 51 were coupled with the bis(vinyldioxaborolane)s. The coupling of the diiodides with 43 and 49 in the presence of a base or fluoride afforded the triptycene incorporating PPVs 52, 53, 54 and 55, as illustrated in
PPEs 56 and 57 in
Fluorescence spectra of a liquid crystal solution of polymer 57 in a LC cell are shown in
PPVs with triptycene in the main chain were prepared through a Suzuki-type coupling procedure. These polymers were highly soluble and cover a wide range of absorption and emission spectra. PPEs with triptycene in the main chain and alkyl pending groups were prepared by Sonogashira coupling. PPVs have absorption and emission spectra in the longer-wavelength regions than those of the corresponding PPEs. Alkyl substituted conjugated polymers absorb and emit in the bluer region than the corresponding alkoxy substituted polymers. tert-Butyl groups on the triptycenes increase the solubility of the polymers, have but little effects on the spectroscopic properties. Lower-molecular-weight PPEs and PPVs incorporating triptycenes form homogeneous solutions in liquid crystals and align to high order. This indicates that these polymers are useful materials for the fabrication of anisotropic optical films. The alignment direction of the polymers in liquid crystals can be switched by the application of electric field.EXAMPLE 11
Synthesis of 9,10-o-benzeno-9,10-dihydro-4-hydroxy-1-octyloxyanthracene
9,10-o-benzeno-9,10-dihydro-4-hydroxy-1-octyloxyanthracene 900 is illustrated in
Synthesis of 9,10-o-benzeno-9,10-dihydro-4-nofylyl-1-octyloxyanthracene
9,10-o-benzeno-9,10-dihydro-4-nofylyl-1-octyloxyanthracene 901 is illustrated in
Synthesis of 9,10-o-benzeno-4-ethynyl-9,10-dihydro-1-octyloxyanthracene
9,10-o-benzeno-4-ethynyl-9,10-dihydro-1-octyloxyanthracene 902 is illustrated in
The orange oil was dissolved in 8 ml THF. 8 ml MeOH is added and the solution purged with Ar for 30 minutes. Next, 555 mg K2CO3 was added and the solution stirred at room temperature for 3 hours. The solution was quenched by pouring it into water and extracting with Et2O. The combined organic extracts were washed with saturated aqueous NH4Cl, water, and saturated aqueous NaCl. After drying over MgSO4, the solution was filtered and condensed in vacuo to yield an orange oil. Purification of compound 902 was by gradient column chromatography from 6:1 to 3:1 hexanes: CHCl3 to yield 342 mg (81%) of a pale yellow oil which solidifies upon drying under vacuum.EXAMPLE 14
Synthesis of 1,4-bis(4′-octyloxyphenylethynyl)-9,10-o-benzeno-9,10-dihydroanthracene
1,4-bis(4′-octyloxyphenylethynyl)-9,10-o-benzeno-9,10-dihydroanthracene 27 is illustrated in
Synthesis of 1,4-bis(9′,10′-o-benzeno-4′-ethynyl-9′,10′ dihydro-1′-octyloxyanthracenyl)benzene
1,4-bis(9′,10′-o-benzeno-4-ethynyl-9′,10′ dihydro-1′-octyloxyanthracenyl)benzene 28 is illustrated in
Synthesis of 1,4-bis(9′,10′-o-benzeno-4′-ethynyl-9′,10′ dihydro-1′-octyloxyanthracenyl)-9,10-o-benzeno-9,10-dihydroanthracene
1,4-bis(9′,10′-o-benzeno-4′-ethynyl-9′,10′ dihydro-1′-octyloxyanthracenyl)-9,10-o-benzeno-9,10-dihydroanthracene 29 is illustrated in
5,7,12,14-bis(o-benzeno)-5,7,12,14-tetrahydro-6,13-bis(4′-octyloxyphenylethynyl)pentacene 30 is illustrated in
Compound 903 is illustrated in
Compound 904 is illustrated in
Compound 905 is illustrated in
Compound 32 is illustrated in
Compound 33 is illustrated in
Compound 906 is illustrated in
Compound 34 is illustrated in
Compound 35 is illustrated in
Synthesis of 1,4-dinitrosotriptycene
1,4-dinitrosotriptycene 907 is illustrated in
Compound 36 is illustrated in
Compound 37 is illustrated in
Compound 38 is illustrated in
Synthesis of 1,4-nonafluorobutanesulfonoxy-9,10-dihydro-9,10-[1′,2′]benzenoanthracene
1,4-nonafluorobutanesulfonoxy-9,10-dihydro-9,10-[1′,2′]benzenoanthracene 40 is illustrated in
Synthesis of 1,4-bis(trimethysilylethynyl)-9,10-dihydro-9,10-[1′,2′]benzenoanthracene
1,4-bis(trimethysilylethynyl)-9,10-dihydro-9,10-[1′,2′]benzenoanthracene 41 is illustrated in
Synthesis of 1,4-diethynyl-9,10-dihydro-9,10-[1′,2′]benzeno-anthracene
1,4-diethynyl-9,10-dihydro-9,10-[1′,2′]benzeno-anthracene 42 is illustrated in
Synthesis of 1,4-bis(4,4,5,5-tetramethyl-1,3,2-dioxoborolan-2-yl-ethenyl-9,10-dihydro-9,10-[1′,2′]benzeno-anthracene
1,4-bis(4,4,5,5-tetramethyl-1,3,2-dioxoborolan-2-yl-ethenyl)-9,10-dihydro-9,10-[1′,2′]benzeno-anthracene 43 is illustrated in
Synthesis of 6,14-di-tert-butyl-9,10-dihydro-9,10[1′,2′]benzenoanthracene-1,4-diol
6,14-di-tert-butyl-9,10-dihydro-9,10[1′,2′]benzenoanthracene-1,4-diol 45 is illustrated in
Synthesis of 6,14-di-tert-butyl-1,4-nonafluorobutanesulfonoxy-[1′,2′]benzenoanthracene
6,14-di-tert-butyl-1,4-nonafluorobutanesulfonoxy-[1′,2′]benzenoanthracene 46 is illustrated in
Synthesis of 6,14-di-tert-butyl-1,4-bis(3-hydroxy-3-methyl-but-1-ynyl)-[1′,2′]benzenoanthracene
6,14-di-tert-butyl-1,4-bis(3-hydroxy-3-methyl-but-1-ynyl)-[1′,2′]benzenoanthracene 47 is illustrated in
Synthesis of 6,14-di-tert-butyl-1,4-diethynyl-[1′,2′]benzenoanthracene
6,14-di-tert-butyl-1,4-diethynyl-[1′,2′]benzenoanthracene 48 is illustrated in
Synthesis of 6,14-di-tert-butyl-1,4-bis(4,4,5,5-tetramethyl-1,3,2-dioxoborolan-2-yl-ethenyl)-[1′, 2′]benzeno-anthracene
6,14-di-tert-butyl-1,4-bis(4,4,5,5-tetramethyl-1,3,2-dioxoborolan-2-yl-ethenyl)-[1′,2′]benzeno-anthracene 49 is illustrated in
Two nematic liquid crystals, 1-(trans-4-hexylcyclohexyl)-4-isothiocyanatobenzene (“6CHBT,” Tm=12.4° C., TNI=42.4° C.), and 4-(trans-4-pentyl-cyclohexyl)benzonitrile (“5PCH,” Tm=30° C., TNI=55° C.), were tested for solubilizing the polymers of one embodiment of the invention. Polymer PPVs with tert-butyl substitutions 53 and 55 in
Absorption spectra were recorded in both parallel and orthogonal directions relative to the expected alignment of the liquid crystals through a polarizer. The absorption along the director of the polyimide on the surface was found to be much stronger, indicating that the long axes (coinciding with the direction of the most probable electronic transition) of the polymers were orientated with the liquid crystals parallel to the polyimide direction. It was observed that the polymer 55 in 6CHBT in a liquid crystal cell preferred to align along with the liquid crystal, and the ordering parameter of transition moment of 6CHBT was found to be 0.69.
When a voltage (9 V) was applied across the cell through the conductive indium tin oxide coating, it was found that the absorption along the polyimide direction was significantly diminished. This indicated a change of the orientation of the polymer long axis as a result of change of the liquid crystal director under electric field, from parallel to the surface to perpendicular to the surface. As a result, less absorption of light takes place because the electric vector of the light coming across the cell is mostly parallel to the surface, interacting preferably with polymers with transition moments aligned parallel to the surface. The absorption along the polyimide direction decreased when the cell was heated up across the nematic-isotropic transition temperature of the liquid crystal.
The liquid crystal cells loaded with PPV solutions in both liquid crystals were highly fluorescent under ultraviolet (“UV”) light, and the fluorescence was found to be highly polarized. Upon the application of a voltage of 9 V across the cell, the fluorescence was significantly diminished due to less absorption of light resulted from the reorientation of the polymer long axis along the electric field. The switch was reversible, i. e., the fluorescence recovered when the voltage was removed. Fluorescence spectra of the liquid crystal cell loaded with a solution of compound 55 in 6CHBT showed that the emission maximum of the liquid crystal solution shifted slightly to the red, relative to the emission from solution, due to induced alignment of the polymer long axis parallel to the surface of the cell.
While several embodiments of the invention have been described and illustrated herein, those of ordinary skill in the art will readily envision a variety of other means and structures for performing the functions and/or obtaining the results or advantages described herein, and each of such variations or modifications is deemed to be within the scope of the present invention. More generally, those skilled in the art would readily appreciate that all parameters, dimensions, materials, and configurations (list modified as appropriate) described herein are meant to be exemplary and that actual parameters, dimensions, materials, and configurations will depend upon specific applications for which the teachings of the present invention are used. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, many equivalents to the specific embodiments of the invention described herein. It is, therefore, to be understood that the foregoing embodiments are presented by way of example only and that, within the scope of the appended claims and equivalents thereto, the invention may be practiced otherwise than as specifically described. The present invention is directed to each individual feature, system, material and/or method described herein. In addition, any combination of two or more such features, systems, materials and/or methods, if such features, systems, materials and/or methods are not mutually inconsistent, is included within the scope of the present invention. In the claims, all transitional phrases or phrases of inclusion, such as “comprising,” “including,” “carrying,” “having,” “containing,” and the like are to be understood to be open-ended, i.e. to mean “including but not limited to.” Only the transitional phrases or phrases of inclusion “consisting of” and “consisting essentially of” are to be interpreted as closed or semi-closed phrases, respectively, as set forth in MPEP section 2111.03.
1. A composition comprising:
- a ladder polymer or oligomer comprising an iptycene.