Room temperature crosslinkable ion conductive polymer system

A room temperature crosslinkable polymer system comprising an anhydride containing polymer and an oxyalkylene amine and a polymer electrolyte derived therefrom are prepared and employed as ion conducting materials for batteries such as lithium ion battery, solar cells and electrochromic devices is disclosed.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description

This application claims benefit under 35 USC 119(e) of U.S. provisional application No. 61/005,649, filed Dec. 6, 2007.

The present invention provides a room temperature crosslinkable polymer system comprising an anhydride containing polymer and an oxyalkylene amine and a polymer electrolyte derived therefrom. The polymer and electrolyte are useful as ion conducting materials for batteries such as lithium ion battery, solar cells and electrochromic devices.

BACKGROUND OF THE INVENTION

Polymer electrolytes have attracted great interest because of their potential in the development of new technologies such as polymer batteries, fuel cells and sensors. For example, the lithium ion battery provides high energy density due to the small atomic weight and the large ionization energy of lithium and has become widely used as a power source for many portable electronics such as cellular phones, laptop computers, mini-cameras, etc. In a battery cell, an electron insulating separator is used to separate the two electrodes and electrolytes are used to facilitate the necessary passage of ions between reduction and oxidation sites. Membranes made from polymeric electrolytes can serve as a combination of separator and electrolyte providing greater efficiency in manufacture of the batteries while addressing growing concerns about their safety by eliminating the flammable organic solvents used in many electrolyte systems.

Armand et al. found in 1978 that poly(ethylene oxide) (PEO) can dissolve lithium perchlorate salts forming a complex that can serve as a solid electrolyte. This complex has a relatively good ionic conductivity in a solid state. However, the ionic conductivity is insufficient as compared with the ionic conductivity of the non aqueous electrolyte solution and the cation transport number of the complex is extremely low.

Subsequently a broad range polymer electrolytes composed of linear polyethylene oxide related polymers such as polypropylene oxide, polyethyleneimine, polyurethane and polyester were developed. In general, these polymer electrolytes have an ionic conductivity at room temperature of about 10−7 to 10−6 S/cm. It is believed that ion conduction is due mainly to the amorphous portion of a polyether polymer which conducts ions by local movement of polymer chain segments, Armand, Solid State Ionics, Vol. 9/10, p. 745-754, 1983. A linear polyether polymer such as PEO tends to crystallize with metallic salt dissolved therein and thus limits ion movement so that actual ion conductivity is much lower than the predicted value.

For a polymer electrolyte to offer high ion conductivity, it ideally should have many amorphous regions of good ion conductor mobility and not crystallize even in the presence of a high concentration of dissolved ion-conductive salt. Many attempts to design and make branched PEOs for electrolytes have been reported, for example, Atsushi Nishimoto et al Electrochim Acta, Vol. 43, No. 10-11, pp. 1177-1184, 1998, however, the synthesis is complicated and manufacturing costs are high.

Furthermore, the cation transport number of the PEO complex tends to be extremely low due to a strong interaction of cations with polar groups of the matrix polymer relative to that of anions. In a secondary battery, the electrodes used are active to cations. When an electrolyte with both moveable cations and anions is used, the movement of anions can be interrupted by the cathode resulting in a concentration polarization which may cause fluctuations in voltage or output of the secondary battery. Thus, an ionic conductor having non-moveable anions is desirable. Such material is often referred to as single-ion conductor and generally has a high cation transport number.

U.S. Published Pat. Appl. 2006/0014066A1, incorporated herein in its entirety by reference, discloses an ion conductive polymer having stereospecific structures which are claimed to improve ion conductivity and cationic transport number. The syndiotactic poly(styrene sulfonate) solid polymer electrolyte disclosed therein has a room temperature (25 C) conductivity of 2×10−6 S/cm, which is higher than conventional solid conductive polymer electrolytes.

U.S. Pat. No. 6,537,468, incorporated herein in its entirety by reference, discloses a polymer electrolyte with high conductivity comprising a polymer containing polyvinyl alcohol units substituted or grafted with oxyakylene and a crosslinker to form a semi-interpenetrating network (IPN) structure wherein a branched oxyalkylene polymer confined in an IPN contributes high ion conductivity and the desired tackiness while the crosslinked structure provides shape retention. The conducting branched polyvinyl alcohol is not covalently linked to the crosslinked network. Solid polymer electrolytes with tackiness were formed by heating (e.g., at 100° C.) to achieve crosslinking.

U.S. Pat. No. 6,881,820, incorporated herein in its entirety by reference, discloses a series of rod-coil block polyimide copolymers formed by condensation polymerization of a tetracarboxylic acid dianhydride with a polyoxyalkylene diamine and an aromatic polyfunctional amine that can be fabricated into mechanically resilient film with acceptable ionic or protonic conductivity at variety temperatures. The copolymers consist of short-rigid polyimide rod segments alternating with polyether coil segments. Preparation of copolymers with graft or comb structures consisting of a rigid polymer backbone with polyether coil graft segments is not disclosed, nor is preparation of crosslinked copolymers using polyfunctional anhydride such as styrene and maleic anhydride copolymer with more than two anhydride functional groups.

U.S. Pat. No. 6,368,746, incorporated herein in its entirety by reference, discloses a molded solid electrolyte consisting of an inorganic solid electrolyte such as lithium sulfide (Li2S) and silicon sulfide (SiS2) with an organic binder polymer such as polybutadiene copolymer rubber.

In spite of these efforts, current polymer electrolytes consisting of branched or grafted oxyalkylene polymers to increase the amorphous portion of the polymer and improve conductivity still fail to provide the ion conductivity desired and typically involve complicated syntheses.

Attempts to develop alternate single ion conductive polymers, for example, with fixed anion groups to raise cation transference number and reduce polarization, have encountered similar drawbacks. High-porous membranes capable of encapsulating a liquid electrolyte in its porous structure were exploited for improved mechanical stability. However, there may be disadvantages of poor contact with electrodes and possibility of liquid leakage. Lithium ion conductive inorganic solid electrolytes were also exploited but require high temperatures to make and are not flexible unless used together with organic polymers.

To achieve high conductivity, gel polymer electrolytes (GPE) using soluble polymers such as poly(ethylene oxide) (PEO), PVC, poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF)PEO, were developed for use in polymer Li ion batteries. GPE's potentially have ionic conductivity near the order of magnitude of liquid electrolytes (>10−4 S/cm possible).

Many of these gel polymer electrolytes typically have either high conductivity with poor mechanical properties or good mechanical properties with low conductivity. PEO-based electrolytes have a high degree of crystallinity unfavorably affecting its ionic conduction. PAN-based electrolytes undergo solvent exudation upon long storage and solvent will ooze to the surface of the polymer membrane decreasing the ionic conductivity dramatically. PMMA-based electrolytes have a high ionic conductivity but it is difficult to form a polymer membrane with stable dimensions and good physical properties.

PVDF with its high dielectric constant (∈=0.84) and strong electro-withdrawing functional groups is non-soluble but swellable in carbonate solvents and therefore can provide a supporting structural phase with good mechanical strength when used as the polymer matrix for GPE.

There are many potential advantages in the use of solid polymer electrolytes, for example, adjustable physical properties such as flexibility, rigidity, processibility, softness, hardness, porosity, tackiness etc, low toxicity, minimal fire hazard, light weight, high energy density, lower manufacturing costs, improved performance, etc. However, there remains a need for new solid electrolytes having unique molecular architecture and/or new ion transport mechanisms that can provide good ion conductivity at room temperature with no solvent. For example, room temperature conductivity of conventional solid conductive polymer electrolytes is 1×10−6 s/cm or lower which is insufficient for many applications.

SUMMARY OF THE INVENTION

It has been found that a polymer containing anhydride functional groups (polyanhydride) can react with a mono- and/or poly-oxyalkleneamine at ambient temperature to form a grafted and/or crosslinked oxyalkyleneamide polymer, e.g., an oxyalkylene amic acid containing polymer. The polyanhydride can be a homopolymer or copolymer. Typically each of the anhydride moieties comprised in the backbone are the same, e.g., maleic anhydride, but more than one type of anhydride moiety may be present.

As used herein, “polymer” is a general term which encompasses homopolymers and copolymers. When the phrase “polymer or copolymer” is used, it is used to reinforce the concept that either homopolymers or copolymers may be encountered in the practice of this invention. Typically, however, the polymers are anhydride copolymers.

The graft and/or crosslink reaction can be run at room temperature at low concentration to form the crosslinked or grafted amic acid containing polymer as a gel which is readily converted to a solid membrane by, e.g., solution casting followed by solvent evaporation and completion of the crosslinking or grafting reaction. The graft and/or crosslink reaction can also be carried out in the presence of electrolyte dissolved in organic solvent (organic electrolyte) to form a gel or solid polymer electrolyte with good ion conductivity. For example, the reaction of polyanhydride and polyoxyalkyleneamine proceeds in the presence of a lithium salt at room temperature to form solid polymer electrolyte membranes. Clear rubbery insoluble membranes containing high content of oxyalkylene ether with good ion conductivity are obtained.

The oxyalkyleneamide polymer can also be further treated with heat to transform some or all of the aminic amide moieties into imides for improved mechanical properties. The oxyalkylene amic acid groups of the polymer can also be neutralized with a Li base to form a single ion conductive polymer with fixed anionic carboxylate groups and oxyalkylene ether segments for enhanced ion conductivity and improved cation transference number.

The reaction of polyanhydride and mono-oxy or polyoxyalkyleneamine also proceeds at room temperature in presence of lithium base. The added lithium base neutralizes the formed amic acid providing fixed anion groups in the polymer for enhanced cation transportation. Thus a method is provided for preparing a polymer electrolyte containing a high content of amorphous oxyalkylene ether and fixed anion group having the advantages of both branched polyoxyalkylene and single ion conductive polymer.

The grafted or crosslinked polymer readily forms a molded solid membrane and is suitable for use as solid polymer electrolyte in various applications such as batteries, solar cell and electrochromic devices.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a grafted or crosslinked ion conducting polymer comprising in the backbone of the polymer one or more amic acid or maleimide moieties selected from

wherein

  • * designates connection to the rest of the polymer backbone,
  • G is H, C1-12 alkyl, metal cation or amino cation,
  • A, A′ and A″ are independently of the others C1-24 alkylene, for example C1-12 alkylene,
  • each of x, y and z is a number from 0 to about 125, for example from 0 to 50, typically at least one of x, y or z is 1 or higher, often each of x, y and z is 1 or higher,
  • E is H, C1-12 alkyl, or C1-12 alkyl carbonyl,
  • R′ is H or C1-12 alkyl,
  • R″ is H, C1-12 alkyl, C1-12 alkyl carbonyl, C6-10 aryl, C6-10 aryl substituted by 1 or more C1-12 alkyl, C7-12 aralkyl, C7-12 aralkyl substituted by 1 or more C1-12 alkyl, or a group

  • wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkyl carbonyl,
  • or one E′ is H, C1-12 alkyl, or C1-12 alkyl carbonyl and the other is a carbonyl linking group which forms a crosslink to same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of formula I or Formula II,
  • or the two E′ groups together form a maleimide group which is fused to the same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of formula I or Formula II and thus forming a crosslink.

Alkyl is straight or branched chain of the specified number of carbon atoms, for example, methyl, ethyl, iso-propyl, n-propyl, n-butyl, sec-butyl, tert-butyl, n-hexyl, n-octyl, tert-octyl, 2-ethylhexyl, n-nonyl, n-decyl, n-undecyl, n-dodecyl.

Alkyl carbonyl or alkanoyl is a straight or branched chain of the specified number of carbon atoms which has a carbonyl at the point of attachment.

Alkylene is a chain, which may be linear or branched, of the specified number of carbon atoms substituted at each terminus, for example, methylene, ethylene, propylene, butylene, pentylene, hexylene, octylene, nonylene, decylene, dodecylene, or one of the preceding substituted by one or more C1-12 alkyl groups, for example, methylmethylene, dimethylmethylene, ethylmethylene, diethylmethylene, propylmethylene, pentylmethylene, heptylmethylene, nonylmethylene, undecylmethylene, methylethylene, propylethylene, butylethylene, pentylethylene, hexylethylene, decylethylene, 1,1-dimethylethylene, 1,2-dimethylethylene, 1,1-diethylethylene, 1,2-diethylethylene, 1-methyl-1-ethylethylene, 1-methyl-2-propylethylene, methylpropylene, 1,1-dimethylpropylene, 1,2-dimethylpropylene, 1,1-diethylpropylene, 1,2-diethylpropylene and the like.

For example, the alkylene groups represented by A, A′ and A″ are independently of each other ethylene or alkyl substituted ethylene such as methylethylene. One embodiment of the invention is therefore a grafted or crosslinked ion conducting polymer comprising in the backbone of the polymer one or more amic acid or maleimide moieties selected from

wherein
each R independently of the others is H or C1-12 alkyl, for example, each R independently of the others is H or methyl, and the other variables are as described above.

For example, G is H, C1-12 alkyl or a metal cation selected from Li, Na, K, Mg and Ca, for example, the metal is Li, E is H; each R independently of the others is H or C1-12 alkyl, for example, each R independently of the others is H or methyl; R′ is H or methyl and R″ is H or a group

wherein each E′ is H or one E′ is H and the other is a carbonyl linking group which forms a crosslink as described above, or the two E′ groups together form a maleimide group to form a crosslink as described above.

For example, the polymer contains in the backbone aminic acid or maleimide moieties selected from

and/or crosslinked aminic acid or maleimide moieties selected from

wherein
G is H, C1-12 alkyl, metal cation or amino cation, for example, G is H or Li;
each R is independently C1-12 alkyl, for example methyl;
R′ is H or C1-12 alkyl, for example methyl;
R″ is H, C1-12 alkyl, C1-12 alkylcarbonyl, phenyl, phenyl substituted by 1 or more C1-12 alkyl, benzyl, phenethyl, benzyl or phenethyl substituted by 1 or more C1-12 alkyl, or a group

wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkylcarbonyl.

The polymers of the invention are conveniently prepared by reacting a polymer containing anhydride repeating units in its backbone, for example, a maleic anhydride copolymer, many of which are commercially available, with at least one amine substituted by an alkyleneoxy or polyalkyleneoxy chain or with a diamine wherein the amino groups are linked by an alkyleneoxy or polyalkyleneoxy chain. Typically, polyalkyleneoxy amines or diamines are used. Any number of the anhydride groups of the anhydride containing polymer may be reacted depending on reaction conditions and stoichiometry, for example, 1-99%, for example 10-99%, or 10-95% of the anhydride groups are reacted with amine.

The invention therefore provides a method for the preparation of grafted or crosslinked ion conducting polymers, and the polymers thus prepared, which method comprises reacting a polyanhydride polymer, for example, a maleic anhydride copolymer, with at least one amine of the formula

wherein

  • A, A′ and A″ are independently of the others C1-24 alkylene, for example C1-12 alkylene,
  • each of x, y and z is a number from 0 to about 125, typically at least one of x, y or z is 1 or higher,
  • E is H, C1-12 alkyl, or C1-12 alkyl carbonyl,
  • R′ is H or C1-12 alkyl,
  • R″ is H, C1-12 alkyl, C1-12 alkyl carbonyl, C6-10 aryl, C6-10 aryl substituted by 1 or more C1-12 alkyl, C7-12 aralkyl, C7-12 aralkyl substituted by 1 or more C1-12 alkyl, or a group

  •  wherein each E′ is independently H, C1-12 alkyl or C1-12 alkylcarbonyl.

For example, the alkylene groups represented by A, A′ and A″ are independently of each other ethylene or alkyl substituted ethylene such as methylethylene as in the formula

wherein each R independently of the others is H or C1-12 alkyl, for example, each R independently of the others is H or methyl, and the other variables are as described above.

For example, an anhydride containing polymer, for example, a maleic anhydride copolymer, is reacted with at least one amine of the formula

wherein
each R is independently C1-12 alkyl, for example methyl,
R′ is H or C1-12 alkyl, for example methyl,
R″ is H, C1-12 alkyl, C1-12 alkylcarbonyl, phenyl, phenyl substituted by 1 or more C1-12 alkyl, benzyl, phenethyl, benzyl or phenethyl substituted by 1 or more C1-12 alkyl, or a group

wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkylcarbonyl.

Poly-oxyalkylene amine compounds useful in the invention include those prepared by reacting a polyol initiator with propylene oxide and/or ethylene oxide followed by amination of the terminal hydroxyl groups, for example, glycerol tris[poly(propylene glycol), amine terminated] ether and trimethylolpropane (TMP) tris[poly(propylene glycol), amine terminated] ether, and 2,2-bis(hydroxymethyl)-1-butanol tris[poly(propylene glycol), amine terminated] ether.

Suitable oxyalkyleneamine compounds include commercial products sold by HUNTSMAN under trade name of JEFFAMINES, for example, JEFFAMINE XTJ 502, XTJ505, XTJ 509, and D2000.

Polyanhydride polymers and copolymers useful in the present invention are polymers and copolymers which contain as a repeating unit a cyclic anhydride, such as copolymers comprising maleic anhydride as a monomer unit, for example, maleic anhydride polymers and maleic anhydride copolymers with an ethylenically unsaturated monomer such styrene, olefins, and (meth)acrylic acid esters and amides.

Examples of suitable polyanhydrides include poly(styrene-alt-maleic anhydride) poly(methyl vinyl ether-alt-maleic anhydride), poly(ethyylene-g-maleic anhydride), poly(isobutylene-alt-maleic anhydride), polyisoprene-g-maleic anhydride, poly(maleic anhydride-alt-1-octadecene), poly(ethylene-co-ethyl acrylate-co-maleic anhydride), polyethylene-graft-maleic anhydride . For example, the polyanhydride is a copolymer of maleic anhydride and styrene (PSMAn). PSMAn may contain alkyl ester groups corresponding to an ester produced from a reaction of an anhydride group with an alcohol. Preferred partially esterified PSMAn is one containing methyl ester groups with less than 50% of total anhydride groups being esterified.

The incorporation of styrene repeating units into the polyanhydride copolymers facilitates formation of amorphous regions of the polyether segments in the grafted or crosslinked polymer, especially in the presence of high concentration of ion conductive salt.

For example, the grafted or crosslinked ion conducting polymer of the invention is a poly(styrene-co-PEO maleicamic acid) obtained by reacting PSMAn with an oxyalkyleneamine, preferably a polyfunctional oxyalkyleneamine, such as polyoxyethylene (PEO) diamine. The lithium salt of the poly(styrene-co-PEO maleicamic acid) is readily obtained by neutralization with a lithium base such as lithium hydroxide or lithium methoxide, and conversion to poly(styrene-co-PEO maleic imide) can be effected by heating in vacuum. Of course the actual “styrene-co-PEO maleicamic acid” polymer ultimately obtained by any of these processes, or any combination of these processes may contain a certain amount of aminic acid moieties, acid salts and/or imides based on partial conversion to salt or imide.

Solid polymer electrolyte membranes can be prepared by performing the grafting or crosslinking reaction in the presence of a lithium salt. Gel polymer electrolyte membranes are also prepared by post soaking the preformed poly(styrene-co-PEO maleic) polymers with a liquid electrolyte.

To further illustrate certain aspects of the invention, the reaction of the maleic anhydride copolymers, PSMAn, with amino polyalkyleneoxides, for example, JEFFAMINES, is demonstrated below where R, R′, R″ and R′″ are independently a C1 to C12 alkyl group. Of course, the isomer of the first product is also possible.

Reaction products of PSMAn with mono-functional oxyalkyleneamine are generally soluble. Solid polymer electrolyte membranes can be prepared by dissolving the oxyalkyleneamide or oxyalkyleneimide product in a suitable solvent and/or a liquid electrolyte solution and casting the polymer solution on substrate.

Crosslinked polymers are similarly prepared by reacting PSMAn with an oxyalkylene diamine, or an oxyalkylene poly-amine with more than one amine group per molecule. In such cases, insoluble membranes can be formed by carrying out the reaction in a suitable solvent and casting the reacting solution on a substrate or in a container.

Solid polymer electrolyte membranes or films can be obtained by allowing complete evaporation of solvent at ambient temperature and/or at elevated temperature. Gel polymer electrolyte membranes can be obtained without drying or by partial drying to allow partial solvent evaporation. Solvent or plasticizer content of a gel polymer electrolyte can be easily controlled by preparing the initial reaction solution with desired amount of solvent or by allowing partial evaporation solvent. Solvent mixtures containing volatile and non-volatile solvent (or plasticizer) can be used to prepare gel polymer electrolytes containing desirable amount of solvent or plasticizer content to balance mechanical properties and ion conductivity.

The present invention therefore provides a simple synthesis and easy process for the preparation of membranes with good conductivity and mechanical properties. Clear rubbery insoluble membranes with high oxyalkylene ether content are obtained which are potentially inexpensive to manufacture. The method is versatile and membranes with different mechanical and electrical properties can be made by changing the composition and proportion of the amine/polyanhydride crosslink system.

The presently provided polymer electrolytes contain a high content of amorphous oxyalkylene ether and fixed anion group and possess the advantages of both branched polyoxyalkylene and single ion conductive polymers. The present solid polymer electrolyte membranes without solvent or plasticizer can give high conductivity at room temperature (>10<6 S/cm). Polymer electrolyte gel membranes of the present invention can provide high room temperature conductivity comparable to that of liquid electrolytes (>10−4 S/cm). The covalently crosslinked solid electrolyte and gel electrolyte membranes also have excellent mechanical properties and solvent resistance.

The solid polymer electrolyte or gel electrolyte may include electrolyte salts, including the well-known lithium salts, alkali metal salts, etc. For example, salts such as lithium bis trifluoromethanesulfonate, lithium perchlorate, lithium tetrafluoroborate, etc can be used individually or in mixtures. The solid polymer electrolyte may include additional known ion conductive polymers along with the ion conductive polymer of the present invention.

A solid polymer electrolyte constructed as above comprising the present ion conductive polymer can be employed as an electrolyte material in, for example, a battery. The battery may be applied to either a primary battery or a secondary battery, either of which are well known in the art.

Therefore, one embodiment of the present invention provides a room temperature crosslinkable polymer system, and a polymer derived therefrom, that can be used as a solid polymer electrolyte for ion conducting. Another embodiment of the present invention provides a solid polymer electrolyte having good conductivity and high cation transport number at room temperature. Other embodiments include a flexible solid electrolyte film or membrane to give good contact with an electrode, a crosslinkable polymer system that can be used as binder for making positive electrode (cathode) and negative electrode (anode) for lithium ion batteries.

Another embodiment provides a crosslinked polymer in the form of solid gel containing liquid electrolyte that can be used as a gel polymer electrolyte with excellent ion conductivity in, for example, Li ion batteries.

Another embodiment provides a crosslinked polymer matrix in the form of membranes which are non-soluble but swellable in an organic liquid electrolyte for use as a gel polymer electrolyte with stable dimensions and good physical properties.

Another embodiment provides a versatile method to make clear rubbery insoluble membranes containing a high content of oxyalkylene ether. The membranes can be formed at room temperature and room temperature ion conductivity higher than conventional solid polymer electrolyte can be achieved.

While the chemistry of the invention is detailed above for reacting maleic anhydride copolymers with amino polyalkyleneoxides such as JEFFAMINES, other polymers and alkyleneoxy amines can of course be employed. To further optimize properties of the ion conducting polymer, one can also react additional compounds, for example, alcohols or amines, i.e., mono-amines or polyamines such as ethylenediamine or diethylenetriamine, with the polyanhydride, either in the same step as the amino alkyleneoxides or an additional step.

Various metal salts and metal containing bases can be used in the reactions and incorporated into the resulting polymers. Li salts however offer advantages in solid polymer electrolyte membranes as related in other portions of the specification. Inorganic or organic metal salts can be used, but organic metal salts offer advantages in solubility of solvents commonly employed in the above processes.

The reaction of an anhydride containing polymer and oxyalkyleneamine can be carried out in solvent without or with an electrolyte or lithium salt. Examples of suitable solvents for dissolving polyanhydrides and oxyalkyleneamine include, but are not limited to, ethers such as tetrahydrofuran (THF); ketones such as acetone and methyl ethyl ketone; nitriles such as acetonitrile, propionitrile and valeronitrile; N-alkylamides such as N-methylpyrrolidinone; N-alkylimide such as N-methyl succinimide; carbonates such as ethylene carbonate, propylene carbonate and dimethyl carbonate; and mixtures of the solvents. Examples of lithium salts include lithium perchlorate, lithium trifluoromethane sulfonate, lithium hexafluorophosphate, lithium hexafluoroarsenate, lithium tetrafluoroborate, lithium bromide, lithium trifloromethanesulfonimide, lithium iodide and mixtures of the lithium salts.

Ion conductive polymer electrolyte membranes or films in many cases can be conveniently prepared by solution casting, spin coating or any suitable coating method directly from the reaction solution. The obtained membranes can be further treated with heat at elevated temperature from 60 to 250° C., preferably, 100 to 180° C. to convert to succinimide containing polymers.

Soluble oxyalkyleneamides and polyoxyalkyleneimides can be prepared in solution or solid product forms using a mono-functional oxyalkyleneamine. Ion conductive polymer electrolyte membranes and films can then be prepared by dissolving the polymer in a liquid electrolyte and solution casting or coating the solution onto the substrate.

The following examples illustrate certain embodiments of the invention but the invention is not limited thereto.

EXAMPLES Raw Materials

The following materials are used to prepared crosslinked polymers and electrolytes of the invention.

Table 1 lists three commercially available maleic anhydride/styrene copolymers (PSMAn) with different molecular weight (MW), methyl ester content, Tg and ratio of styrene to maleic anhydride (St:MAN ratio).

TABLE 1 Poly(styrene-co-maleic anhydride) Methyl ester St:MAn PSMAn MW, g/mole content Tg, ° C. ratio A7 Mn = 1,600 0 160 1:1 A7′ Mw = 350,000 10-15% 243 1:0.88 A7″ Mw = 50,000 0 160 1:1

Table 2 lists three commercially available JEFFAMINE polyoxyalkyleneamines with similar molecular weight (2000) but different functionality. JEFFAMINE XTJ502 (C11) and D2000 (C12) are di-functional amine crosslinkers containing mainly polyoxyethylene (PEO) and polyoxypropylene (PPO) segments respectively; XTJ507 (C13) is a mono-functional amine PEO.

TABLE 2 JEFFAMINE Polyoxyalkyleneamines ID nf* Mw Amine meq/g Mp ° C Structure C11 XTJ502 2 2000 0.93 43 C12 D2000 2 2000 0.97 <20 C13 XTJ507 1 2000 0.47 −36 *nf = amine functionality

Tetrahydrofuran (THF) solutions of the copolymers and polyoxyalkyleneamines are readily available by simply dissolving the desired amount of copolymer or polyoxyalkyleneamines in an appropriate amount of THF.

Table 3 lists commercially available lithium salts used to prepare polymer electrolytes with the PEO/PPO containing polymer.

TABLE 3 Lithium Salts FW, Formula g/mole Purities A Lithium perchloride LiClO4 106.39 >99% B Lithium trifluoromethane- CF3SO3Li 156.01 99.995% sulfonate C Lithium hexafluoro- LiPF6 151.9 99.99% phosphate D Lithium hexafluoroarsenate LiAsF6 195.85 98% E Lithium tetrafluoroborate LiBF4 93.74 98% F Lithium bromide LiBr 86.85 99.000% G LiTFSI, Lithium LiN(CF3SO2)2 287.08 99.95% bis(trifluoromethane- sulfonyl)imide,

Conductivity Measurement

For conductivity measurements solid polymer electrolyte membranes or gel polymer electrolyte membranes are sandwiched between two symmetrical electrodes of the same metal (brass or stainless steel). The electric conductivity is determined by AC impedance measurement using a SOLARTRON 1252A frequency response analyzer (FRA) in combination with a SOLARTRON 1287A electrochemical interface (ECI). Complex impedance spectra is obtained with a frequency range from 0.1 to 300 kHz with an AC voltage amplitude of 20 mV. Bulk resistance is obtained from a semicircular arc of the complex impedance spectra to calculate the ion conductivity of the analyzed polymer electrolyte film with known area and thickness.

Example 1

Solid membranes comprising the crosslinked polymers of the invention are prepared by mixing 2.9 grams of a 12% by weight solution of PSMAn copolymer A7 in tetrahydrofuran (THF) and 7.5 grams of a 40% by weight solution of polyethyleneoxide diamine C11 in THF to form a clear reaction solution of low viscosity and about three minutes after preparation of the reaction solution casting approximately 1.5 grams of the reaction solution into each of two glass Petri dishes and an aluminum weighing dish. The cast solutions are allowed to cure and evaporate out solvent at room temperature. After about 15 minutes the cast films were dry to touch and insoluble in THF. Cure, as determined by no further change in appearance, mechanical properties and solvent swelling, is considered complete after standing overnight at room temperature producing clear, rubbery, dry films which are peeled off the casting dishes to yield solid membranes.

The remaining reaction solution which is not cast increases in viscosity and starts to gel in about 150 minutes (pot life) at room temperature. A clear solid gel containing crosslinked polyoxyethyleneamide and THF solvent is obtained over night.

The crosslinked polyoxyethyleneamide in the solid membranes and the gel obtained in this example contain about 90% by weight of ethylene oxide (EO)/propylene oxide (PO) units available for ion complexing and conducting.

It is noted that neither of the starting materials, A7 or C11, are film forming polymers as no coherent film of either is obtained by solution casting from THF.

Example 2

Following a procedure analogous to Example 1, solid membranes comprising crosslinked polymers of differing compositions are prepared by mixing different amounts of a 20% weight solution of PSMAn copolymer A7 in THF and a 40% by weight solution of polyethyleneoxide diamine C11 in THF solution as shown in the table to form a clear solution and casting, after about 5 minutes into each of three separate Petri dishes. The cured dry films are obtained after standing overnight at room temperature and their properties are summarized in Table Ex2 along with their compositions.

Solubility of the polymers is tested by putting a small piece of cured film in different testing solvent: H2O, THF, acetonitrile (CH3CN), chloroform, methanol (MeOH), and isopropanol IPA. Formation of maleicamic acid by reaction of anhydride with primary amine is confirmed by FTIR spectra of the water extracted membrane and non-extracted membrane.

TABLE EX 2 Example 2A 2B 2C 2D 2E 20% Solution of A7, grams  8.40  6.00  4.60 14.50 25.0 40% Solution of C11, grams 20.8  22.00 22.7  17.75 12.5 C11/A7, w/w 83/17 88/12 91/9 71/29 50/50 Amine/anhydride ratio, mol/mol 1.0 1.5 2.0 0.5  0.2 Cured film properties* 1f 1f 2f 3f 3f *1f free standing membranes, transparent and rubbery, insoluble in test solvents: H2O, THF, MeOH, CH2Cl2, CH3CN, and IPA; 2f same as 1f but softer and stickier; 3f films form but are difficult to obtain free standing membranes, very soft and sticky

Example 3

Following the same procedure as in Example 2, membranes of crosslinked EO/PO containing copolymers are prepared by mixing solutions of different PSMAn copolymers with solutions of different polyoxyalkyleneamines as shown in Table Ex 3 to produce a mixture containing a 1:1 ratio of amine to anhydride ratio in a solution containing approximately 20% solids. Thin free-standing films (membranes) with predetermined thickness are obtained by casting the appropriate amount of this reaction solution in Teflon Petri dishes of 28 cm2 area.

Crosslinked polymer electrolyte membranes with fixed anionic carboxylate groups and movable Li+ ions are obtained in Examples 3F, 3G and 3H by including appropriate amount of lithium methoxide (LiOMe) to achieve desired degree of neutralization (DN) of the amic acid.

Crosslinked polymer electrolyte membranes of polyethyleneoxide imide are obtained from Example 3C by heating the membrane of Example 3B at 140° C. in a vacuum oven and from Example 3H by heating the membrane of Example F at 140° C. in a vacuum oven. The membranes after the heat treatment turn color to brown or yellow and appear to have improved mechanic properties.

All crosslinked membranes obtained in theses examples are insoluble but swellable with most organic liquid electrolytes. Swelling index (SI) with LP30 (1 M LiPF6 in 1:1 ethylene carbonate and dimethyl carbonate) is about 4 (gel electrolyte containing 20% polymer). This example also demonstrates that solid polymer electrolyte membranes with required thickness can be prepared by controlling polymer concentration of the casting solution and area of cast container.

TABLE EX 3 Polymer electrolyte membranes of different composition and thickness Composition Solvent Appearance Thickness, mm Ex 3A A7″/C11 CH3CN Cloudy, non-sticky 0.03-0.07 Ex 3B A7/C11/ MEK Cloudy, non-sticky 0.04-0.10 Ex 3C A7/C11/heat* MEK Cloudy, non-sticky, 0.05-0.06 brown Ex 3D A7′/C12 THF Cloudy, non-sticky 0.05-0.07 Ex 3E A7″/C12 THF Transparent, sticky 0.06-0.12 Ex 3F A7″/C11 THF Transparent, non- 0.04-0.12 DN-100% sticky Ex 3G A7/C11 MEK Transparent, sticky 0.05-0.30 DN-36% Ex 3H A7″/C11/heat* THF Transparent, non- 0.05-0.07 DN-100% sticky, yellow *Heat = vacuum heated at 140° C. for converting to imide;

Example 4

Following a procedure analogous to Example 1, solid membranes of non-crosslinked polymers are prepared by reacting solutions of PSMAn A7 and A7′ with a mono-functional EO/PO amine C13 as shown in Table Ex 4. Example 4A provides membranes with 50 wt % of EO/PO ether content with an amine/anhydride ratio of 0.1 from a low MW (1600) PSMAn (A7). Example 4B provides membranes with a high EO/PO content 83 wt % and a high amine/anhydride ratio (0.5) from a high MW (350,000) partially methyl esterified PSMAn (A7′).

Membranes prepared with monofunctional EO/PO amine C13 are transparent but have much poorer mechanical properties than those crosslinked with diamine EO/PO C11 and C12, and require more time to form coherent films with a gel time of about 45 hours even at relatively high polymer concentration. Films with better mechanical properties and solvent resistance are obtained from the high MW (350,000) partially methyl esterified PSMAn (A7′) than from PSMAn (A7.

TABLE EX 4 Reactions w/mono-functional amino EO/PO (C13) Example 4A Example 4B PSMAn A7 A7′ C13, wt % 50 83 Amine/Anhydride ratio 0.1 0.5

Example 5

Following a procedure analogous to Example 1, solid membranes of crosslinked polymers are prepared from solutions of a high MW (50,000) PSMAn A7″ with PO diamine C12 (PPODA) as shown in Table Ex 5. Membranes with improved mechanical properties (stronger and less tacky) were obtained.

TABLE EX 5 Membranes from C12 (PPODA) and A7″ (PSMAn, Mw 50,000) Am/An Gel time* Wt % PPODA ratio min Film Properties Ex 5A 83 1.0 20 Transparent, rubbery Ex 5B 88 1.5 110 Transparent, rubbery Ex 5C 91 2.0 n/d Transparent, rubbery, sticky Ex 5D 71 0.5 160 slight hazy transparent, rubbery, Ex 5E 50 0.2 210 slight hazy transparent, rubbery but harder *at 8% solid concentration; n/d = not determined

Example 6A

Following a procedure similar to Example 1, crosslinked polymer electrolyte membranes containing Li salt are prepared by mixing 8.4 grams of a 20 wt % solution of PSMAn A7 in tetrahydrofuran (THF), 20.8 grams of a 40 wt % solution of polyethyleneoxide diamine C11 in THF, and 0.5 g of lithium perchlorate (LiClO4) (pre-dissolved in THF to give a 10% solution) to form a clear reaction solution and about two minutes after preparation of the reaction solution casting portions of the reaction solution into glass Petri dishes.

Reaction solution remaining in the reaction vessel gels in less than 8 hour at room temperature indicating that crosslinking reaction of the polymers can proceed in presence of the Li salt. The cast solutions in Petri dishes are allowed to cure and evaporate out solvent at room temperature for seven days to provide transparent and rubbery insoluble membranes of solid polymer electrolyte containing 5 wt % of LiClO4.

Example 6B and 6C

Following the procedure of Example 6A using different Li salts and concentrations, polymer electrolyte membranes containing 10 wt % of lithium trifluoromethanesulfonate (CF3SO3Li) (based on total polymer weight) Example 6B, and polymer electrolyte membranes containing 10 wt % of lithium bromide (LiBr) Example 6C, are prepared.

Room temperature (20° C.) ionic conductivity is measured for the membranes and the results shown in the Table Ex6.

TABLE EX 6 Polymer electrolyte membranes C11/A7 of 17/83 w/w Li Salt content Conductivity (20° C.), S/cm Ex 6A LiClO4, 5% 7.43 × 10−6 Ex 6B CF3SO3Li, 10% 1.09 × 10−5 Ex 6C LiBr, 10% 1.06 × 10−5

Example 7A

Following a procedure similar to Example 6, crosslinked polymer electrolyte membranes containing Li salts are prepared from solutions in methylethylketone (MEK) by dissolving 0.5 g of LiClO4 in MEK and then adding with mixing 10.4 grams of a 40% by weight solution of polyethyleneoxide diamine C11 in MEK followed by addition of 4.2 grams of a 20% by weight solution of PSMAn copolymer A7 in MEK. After 5 minutes of mixing portions of the reaction solution are cast into glass Petri dishes and dried overnight under vacuum to provide solid polymer electrolyte membranes containing no solvent.

Example 7B

Following the procedure of Example 7A, solid polymer electrolyte membranes containing 10% LiBF4 salt are prepared substituting the appropriate amount of LiBF4 as the Li salt.

Example 7C

The procedure of Example 7B is repeated except that 0.45 grams of a 10% lithium methoxide (LiOCH3) solution in methanol is added to the MEK solution of LiBF4 to provide solid polymer electrolyte membranes with multiple lithium salts.

Room temperature (20° C.) ionic conductivity is measured for the membranes and the results are shown in the Table Ex 7.

TABLE EX 7 Polymer electrolyte membranes C11/A7 of 17/83 w/w Li Salts Conductivity (20° C.), S/cm Ex 7A LiClO4, 10% 4.47 × 10−6 Ex 7B LiBF4, 10% 2.71 × 10−6 Ex 7C LiBF, 10%, 8.69 × 10−6 LiOCH3, 0.9%

Example 8A

A polymer electrolyte gel of crosslinked polymer is prepared by dissolving 0.83 g of LiClO4 in MEK in a beaker and then adding with mixing 10.4 grams of a 40% by weight solution of polyethyleneoxide diamine C11 in MEK followed by addition of 4.2 grams of a 20% by weight solution of PSMAn copolymer A7 in MEK. The reaction solution is not cast but allowed to gel in the beaker to provide after about 3 hours a semi-solid elastic gel containing about 30% polymer and about 5% LiClO4 (16.6% based on polymer weight).

Example 8B

The procedure of Example 8A is repeated except that 1.5 g instead of 0.83 g of LiClO4 is used to provide a solution that gels in about 65 hours to give a semi-solid elastic gel containing about 20% polymer and about 6% LiClO4 (30% based on polymer weight).

Room temperature (20° C.) ionic conductivity is measured for the membranes and the results shown in Table Ex 8.

TABLE EX 8 Polymer electrolyte membranes C11/A7 of 17/83 w/w Li Salts Conductivity (20° C.), S/cm Ex 8A LiClO4, 17% 4.37 × 10−3 Ex 8B LiClO4, 30% 1.66 × 10−2

Comparative Examples

For comparison to the inventive membranes, solid polymer electrolyte membranes of poly(ethylene oxide) (PEO) containing various amounts of lithium salts are prepared by adding to 37.4 grams of a 6.7 wt % solution of a PEO polymer (MW ˜900,000 g/mole) in acetonitrile either 0.25 g of LiClO4 pre-dissolved in acetonitrile, 0.5 g of LiClO4 pre-dissolved in acetonitrile or 0.37 g of CF3SO3Li pre-dissolved in acetonitrile. The resulting solutions are cast into Petri dishes as above and allowed to stand overnight at room temperature to provide turbid white membranes containing 10% LiClO4 based on PEO weight, 20% LiClO4 based on PEO weight and 15% CF3SO3Li based on PEO weight respectively.

Room temperature (20° C.) ionic conductivity is measured for the membranes and the results shown in Table C Ex 1.

TABLE C EX 1 Li Salts, % on PEO Conductivity (20° C.), S/cm 1A LiClO4, 10% 3.87 × 10−8 1B LiClO4, 20% 4.65 × 10−7 1C CF3SO3Li, 15% 7.00 × 10−8

The solid polymer electrolyte of the present invention as shown in Examples 6-8 provide room temperature conductivity above 10−6 S/cm, more than 10 times higher than that of conventional solid PEO polymer electrolyte.

Claims

1) A grafted or crosslinked ion conducting polymer comprising in the backbone of the polymer one or more amic acid or maleimide moieties selected from wherein

* designates connection to the rest of the polymer backbone,
G is H, C1-12 alkyl, metal cation or amino cation,
A, A′ and A″ are independently of the others C1-24 alkylene,
each of x, y and z is a number from 0 to about 125,
E is H, C1-12 alkyl, or C1-12 alkyl carbonyl,
R′ is H or C1-12 alkyl,
R″ is H, C1-12 alkyl, C1-12 alkyl carbonyl, C6-10 aryl, C6-10 aryl substituted by 1 or more C1-12 alkyl, C7-12 aralkyl, C7-12 aralkyl substituted by 1 or more C1-12 alkyl, or a group
wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkyl carbonyl,
or one E′ is H, C1-12 alkyl, or C1-12 alkyl carbonyl and the other is a carbonyl linking group which forms a crosslink to same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II,
or the two E′ groups together form a maleimide group which is fused to the same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II and thus forming a crosslink.

2) A grafted or crosslinked ion conducting polymer according to claim 1 comprising in the backbone of the polymer one or more amic acid or maleimide moieties selected from wherein

each R independently of the others is H or C1-12 alkyl and at least one of x, y or z is 1 or higher.

3) A grafted or crosslinked ion conducting polymer according to claim 1 wherein

G is H, C1-12 alkyl or a metal cation selected from Li, Na, K, Mg and Ca,
E is H,
each R independently of the others is H or C1-12 alkyl,
R′ is H or methyl
and R″ is H or a group
wherein each E′ is H or one E′ is H, and the other is a carbonyl linking group which forms a crosslink to same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II, or the two E′ groups together form a maleimide group which is fused to the same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II and thus forming a crosslink.

4) A grafted or crosslinked ion conducting polymer according to claim 2 comprising in the backbone of the polymer one or more amic acid or maleimide moieties selected from Wherein

* designate the position of attachment the polymer,
G is H, C1-12 alkyl or a metal cation,
E is H, C1-12 alkyl, or C1-12 alkylcarbonyl,
R′ and each R independently are H or C1-12 alkyl,
R″ is H, C1-12 alkyl, or C1-12 alkylcarbonyl or a group
wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkyl carbonyl,
or one E′ is H, C1-12 alkyl, or C1-12 alkyl carbonyl and the other is a carbonyl linking group which forms a crosslink to same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II,
or the two E′ groups together form a maleimide group which is fused to the same polymer backbone or to the backbone of another polymer chain which comprises in the backbone of the polymer chain one or more amic acid or maleimide moieties of Formula I or Formula II and thus forming a crosslink.

5) A polymer according to claim 2, wherein the polymer contains in the backbone crosslinked aminic acid or maleimide acid moieties selected from wherein

G is H, C1-12 alkyl, metal cation or amino cation,
R′ and each R independently are H or C1-12 alkyl.

6) A polymer according to claim 1 which is prepared by reacting a maleic anhydride polymer with at least one amine of the formula wherein

A, A′ and A″ are independently of the others C1-24 alkylene,
each of x, y and z is a number from 0 to about 125,
E is H, C1-12 alkyl, or C1-12 alkyl carbonyl,
R′ is H or C1-12 alkyl,
R″ is H, C1-12 alkyl, C1-12 alkyl carbonyl, C6-10 aryl, C6-10 aryl substituted by 1 or more C1-12 alkyl, C7-12 aralkyl, C7-12 aralkyl substituted by 1 or more C1-12 alkyl, or a group
 wherein each E′ is independently H, C1-12 alkyl or C1-12 alkylcarbonyl, wherein 1-99% of the anhydride units are reacted with amine.

7) A polymer according to claim 6 which is prepared by reacting a maleic anhydride polymer with at least one amine of the formula wherein each R independently of the others is H or C1-12 alkyl.

8) A polymer according to claim 6 which is prepared by reacting a maleic anhydride polymer with at least one amine of the formula wherein

R is methyl,
R′ is H or methyl,
R″ is H, C1-12 alkyl, C1-12 alkylcarbonyl, phenyl, phenyl substituted by 1 or more C1-12 alkyl, benzyl, phenethyl, benzyl or phenethyl substituted by 1 or more C1-12 alkyl, or a group
wherein each E′ is independently H, C1-12 alkyl, or C1-12 alkylcarbonyl.

9) A polymer according to claim 6, wherein the maleic anhydride polymer is a maleic anhydride copolymer with an ethylenically unsaturated monomer selected from styrenes, olefins, and (meth)acrylic acid esters and amides.

10) A copolymer according to claim 9, wherein the maleic anhydride copolymer is selected from poly(styrene-alt-maleic anhydride), poly(methyl vinyl ether-alt-maleic anhydride), poly(ethyylene-g-maleic anhydride), poly(isobutylene-alt-maleic anhydride), polyisoprene-g-maleic anhydride, poly(maleic anhydride-alt-1-octadecene), poly(ethylene-co-ethyl acrylate-co-maleic anhydride), polyethylene-graft-maleic anhydride.

11) The polymer according to claim 6 wherein 10-99% of the anhydride units are reacted with amine.

12) A process for preparing a polymer according to claim 1 wherein a maleic anhydride polymer is reacted with at least one amine of the formula wherein

A, A′ and A″ are independently of the others C1-24 alkylene,
each of x, y and z is a number from 0 to about 125,
E is H, C1-12 alkyl, or C1-12 alkyl carbonyl,
R′ is H or C1-12 alkyl,
R″ is H, C1-12 alkyl, C1-12 alkyl carbonyl, C6-10 aryl, C6-10 aryl substituted by 1 or more C1-12 alkyl, C7-12 aralkyl, C7-12 aralkyl substituted by 1 or more C1-12 alkyl, or a group
 wherein each E′ is independently H, C1-12 alkyl or C1-12 alkylcarbonyl.

13) A process according to claim 12, wherein the polymer obtained by reaction of the maleic anhydride polymer with the at least one amine is treated with heat at elevated temperature from about 60 to about 25° C.

14) A solid polymer electrolyte or gel electrolyte comprising an ion conductive polymer according to claim 1.

15) A solid polymer electrolyte or gel electrolyte according to claim 14 comprising a metal carboxylic acid salt connected to the polymer backbone or complexed electrolyte salt.

16) A solid polymer electrolyte or gel electrolyte according to claim 15, comprising a lithium carboxylic acid salt connected to the polymer backbone or complexed electrolyte lithium salt.

17. A battery having a cathode, an anode and a solid polymer electrolyte or gel electrolyte according to claim 14.

18. A molded membrane comprising a polymer according to claim 1.

Patent History
Publication number: 20090148777
Type: Application
Filed: Dec 4, 2008
Publication Date: Jun 11, 2009
Inventors: Zhiquang Song (Newton, CT), Suruliappa G. Jeganathan (Chadds Ford, PA), Jacqueline Lau (Dobbs Ferry, NY), Rakesh Gupta (Dayton, OH)
Application Number: 12/315,558