Multifunction abrasive tool with hybrid bond

Abstract

Abrasive tools and techniques are disclosed that can cut hard, brittle materials to relatively precise dimensions. The tools, which can include a hybrid bond of metal or metal alloy and a resin matrix together with fine abrasive grits, can be employed, for example, in mirror finish cutting applications, thereby enabling ‘1×’ or ‘single-pass’ multi-function abrasive processes. The specific selection of resin and metal or metal alloy types is such that the tool is sufficiently brittle for the purpose of manufacture and durability, but ductile enough to withstand the grinding and handling stresses (an exemplary hybrid bond includes bronze and polyimide). Numerous tool types and applications will be apparent in light of this disclosure, including abrasive products for electronic device manufacturing such as thin 1A8 blades (single blade or multi-blade configuration).

Description

FIELD OF THE DISCLOSURE

The disclosure relates to abrasives technology, and more particularly, to abrasive tools suitable, e.g., for simultaneously performing multiple functions, such as dicing and polishing of hard brittle materials.

BACKGROUND

Resin-metal or so-called “hybrid” bonds are generally known in the superabrasives industry. The first resin bonds for diamond tools were based on phenolic systems. It was soon found that the resin itself was not optimum, on its own, for some applications. Thus, tool makers introduced secondary fillers to modify the properties of the resin and enable the performance of tools in various applications to be improved. In particular, silicon carbide powder was introduced where a more brittle, friable bond was needed, and copper powder was introduced when a stronger, tougher bond was required (e.g., copper metal bond tools were used in antiquity with natural diamond powder for cutting gemstones). These fillers are still used in many conventional phenolic resin bond systems.

During the 1970's it was thought that, in some applications, the properties of hybrid resin-metal bonds might enhance performance. In more detail, if the diamond could be distributed in a continuous metal phase (for wear resistance and long life), and if a continuous resin phase could be incorporated into the microstructure (for lower wear resistance and free-cutting properties), then the benefits of both systems might be available. This technique was first successfully employed in the Resimet® bonding system, in which the primary component is a cold-pressed and sintered metal porous structure that firmly secures diamond or CBN grains. The secondary bond component is a vacuum cast resin which completely impregnates the porosity in the metal bond structure. The result is a microstructure with two interpenetrating continuous metal (bronze) and resin (epoxy) phases. Great Britain Patent No. 1,279,413 describes details of such bonding systems. Typical applications for this type of hybrid bond are in grinding of carbide cutting tools, particularly when good corner-holding ability is required, and typical grit sizes are in the mesh range FEPA D46 and coarser (i.e., 325 Mesh and coarser, or 44 microns and coarser).

Phenolic resin has good thermal resistance, but polyimide is even better, so when these types of resins were introduced in the late 1970's by DuPont, one of the first applications was in diamond tools. U.S. Pat. Nos. 4,001,981 and 4,107,125 describe polyimide bonded superabrasive tools. As in phenolic resin tools, various fillers are used to modify the properties of the bonds, and copper and bronze powders are used as well. Such polyimide based bonds are typically used in situations where a lot of heat is generated (i.e., where the bond must be resistant to high temperatures). The primary example application is in fluting of round, cemented carbide tools, such as drills and end-mills.

More exacting applications calling for greater precision and cut quality have historically used different tool configurations and bond types. For example, and as is known, a hard disk drive (HDD) is a commonly used storage mechanism used in numerous consumer electronic applications, including computers and game consoles, mobile phones and personal digital assistants, digital cameras and video recorders, and digital media players (e.g., MP3 players). HDD designs generally include a circular magnetic ‘platter’ (onto which data are recorded) that spins about a spindle. As the platter spins, a read-write head is used to detect and/or modify the magnetization of the platter storage location directly under it. The read-write head itself is attached to a ‘slider,’ which is an aerodynamically shaped block that allows the read-write head to maintain a consistent ‘flying height’ above the platter. The slider is connected to an actuator assembly (e.g., motor and arm) that operates to move the read-write head to any storage location on the platter. Manufacturing of the slider component presents a number of challenges. For instance, as the form factor of the electronic devices that employ HDDs decreases, so does the size of the components that make up the HDD, including the slider (which can be about 1/50^th to 1/100^th the size of a penny). As such, the slider must be cut to fairly precise dimensions. Exacerbating this manufacturing complexity is the fact that sliders are typically made from hard brittle materials (e.g., Al₂O₃—TiC, see for example U.S. Pat. No. 4,430,440), which are difficult to cut without incurring problems such as chipping and excessive kerf.

There remains a continuing need, therefore, for new abrasive tools that can cut hard, brittle materials to precise dimensions.

SUMMARY

One embodiment of the present disclosure provides a multifunction abrasive tool suitable, e.g., for dicing and polishing hard brittle materials in a single pass. The tool includes a hybrid bond of metal/metal alloy and resin, and a plurality of fine abrasive grits blended with the hybrid bond. The metal alloy can be bronze which may, for example, consist essentially of 50/50 by weight of copper and tin, and the resin can be a polyimide such as, for instance, Vespel® SP1 polyimide, available from E. I. du Pont de Nemours and Company, Meldin 7001® polyimide, available from Saint-Gobain Performance Plastics Corporation, or a comparable polyimide. The tool can be substantially straight and have a substantially uniform thickness of 250 microns or less. In specific example cases, the tool is a 1A8 type wheel or a 1A1 type wheel, and has a thickness of about 65 microns or less (other wheel types will be apparent in light of this disclosure). In one particular configuration, the tool includes about 1 to 50 volume percent (vol %) of resin, such as polyimide, about 40 to 85 vol % of metal/metal alloy, such as bronze, and about 5 to 40 vol % of fine abrasive grits. In another more specific configuration, the tool includes about 10 to 40 vol % of resin, such as polyimide, about 45 to 75 vol % of metal/metal alloy, such as bronze, and about 10 to 25 vol % of fine abrasive grits. In another more specific configuration, the tool includes about 11.25 vol % of polyimide, about 70 vol % of bronze, and about 18.75 vol % of fine abrasive grits, with each component having a tolerance of ±20%. The polyimide may, for example, consist essentially of particles having an average diameter of about 40 microns or less, and the bronze may consist essentially of particles having an average diameter of about 40 microns or less, and the fine abrasive grits may consist essentially of diamonds in a 50 to 75 concentration, and having an average diameter of about 40 microns or less. In a more specific such configuration, the bronze consists essentially of particles having an average diameter of about 10 microns or less. The tool may be included in a multi-blade configuration that includes a plurality of such tools in a gang-like arrangement (either distinct tools formed individually and coupled together, or formed as a monolithic structure).

Another embodiment of the present disclosure provides an abrasive tool suitable, e.g., for dicing and/or polishing hard brittle materials. The tool is configured similar to the tool discussed above, but has a substantially straight and substantially uniform thickness in the range of 30 to 125 microns.

Another embodiment of the present disclosure provides an abrasive tool suitable, e.g., for dicing and/or polishing hard brittle materials. The tool includes a hybrid bond of a metal or metal alloy, and a resin associated with a Heat Deflection temperature (e.g., as measured by ASTM standard D648) or other comparable processing temperature parameter (where the resin softens without melting, generally referred to as a “softening temperature”) less than 500° C. (e.g., in the range of about 100° C. to 450° C., or even more specifically, in the range of about 160° C. to 400° C.). The metal or metal alloy (e.g., bronze) has a liquid phase or transient liquid phase at the Heat Deflection or softening temperature of the resin, and a fracture toughness between 1 and 5 MPa.m^0.5 at room temperature. The resin (e.g., polyimide) can have a ductility in the range of about 3% to 25%. The tool further includes a plurality of fine abrasive grits blended with the hybrid bond. In various alternative embodiments, the tool can have a substantially straight and substantially uniform thickness of 250 microns or less. In one particular case, the tool is a multifunction tool capable of both slicing and polishing hard brittle materials in a single pass. Various other abrasive tool parameters as discussed herein can be equally applied to such alternative embodiments.

Another embodiment of the present disclosure provides a method for making abrasive tools suitable, e.g., for dicing and/or polishing hard brittle materials. The method includes providing pre-selected proportions of particulate ingredients including abrasive grains, a polyimide, and a pre-alloyed bronze (e.g., about 50 by weight % of copper and about 50 weight % of tin). The method continues with mixing the particulate ingredients to form a substantially uniform composition, placing the substantially uniform composition into a mold of desired shape, and compressing the mold to a pressure in the range of about 25-200 MPa for a duration effective to form a molded article (e.g., 5 to 30 minutes). The method continues with heating the molded article to a temperature less than 500° C. (e.g., in the range of about 100° C. to 450° C., or even more specifically, in the range of about 160° C. to 400° C.) for a duration effective to sinter the bronze and soften the polyimide, thereby integrating the abrasive grains and sintered bond into a composite of substantially continuous metal alloy phase, with a substantially continuous or substantially discontinuous polyimide phase, and then cooling the composite to form the abrasive tool. The method may continue with lapping or otherwise finishing sides of the abrasive tool to provide desired degree of straightness and thickness (e.g., double-sided lapping, where opposing sides of the tool are simultaneously lapped to provide substantially uniform thickness of about 250 microns or less). In an alternative embodiment, the method includes forming multiple thinner tools from the initial abrasive tool, where each thinner tool has a substantially uniform thickness of 250 microns or less, thereby providing a multi-blade abrasive tool (ganged-like configuration). In one such case, forming multiple thinner tools from the initial abrasive tool is accomplished using electro-discharge machining (EDM).

The features and advantages described herein are not all-inclusive and, in particular, many additional features and advantages will be apparent to one of ordinary skill in the art in view of the drawings, specification, and claims. Moreover, it should be noted that the language used in the specification has been principally selected for readability and instructional purposes, and not to limit the scope of the inventive subject matter.

DETAILED DESCRIPTION OF PRESENTLY PREFERRED EMBODIMENTS

Abrasive tools and techniques are disclosed that can cut hard, brittle materials to relatively precise dimensions. The tools, which include a hybrid bond of metal or metal alloy (e.g., bronze) and a resin (e.g., polyimide) matrix together with fine abrasive grits, can be employed, for example, in mirror finish cutting applications, thereby enabling ‘1×’ or ‘single-pass’ multi-function abrasive processes. Numerous tool types and applications will be apparent in light of this disclosure, including abrasive products for electronic device manufacturing such as thin 1A8 blades (single blade or multi-blade configuration) and other such cutting blades.

In one exemplary application, the disclosed tools can be used in the mirror finish dicing of read-write head sliders. Typically, read-write head sliders made of hard, brittle materials such as alumina titanium carbide (Al₂O₃—TiC) are manufactured in a two-step process involving a dicing step that uses a metal-bonded tool and a subsequent discrete polishing step that uses a resin-bonded tool. A tool configured in accordance with an embodiment of the present disclosure is capable of performing both slicing and polishing in a single pass (also referred to as a “1× process” herein). As will be appreciated in light of this disclosure, note that such embodiments may also be used in multiple-pass or “2×” processes, if so desired.

In more detail, the blade of this example embodiment includes a metal/metal alloy, such as bronze, and a resin, such as polyimide resin, with fine diamond abrasive grit for dicing/polishing of hard and brittle material such as alumina-titanium carbide. The metal alloy can be substantially continuous or discrete in nature, although substantially continuous can have certain performance benefits associated with kerf quality and tool wear, and can be sintered in solid or liquid phase at process temperatures of the polyimide. In addition, the metal alloy can transfer the stiffness to the tool (i.e., no interfacial sliding between metal alloy and polyimide), and its hardness can be less than that of the work material. A suitable polyimide (or other comparable resin) generally has low elongation % and high thermal stability. As will further be appreciated in light of this disclosure, the present disclosure is not intended to be limited to bronze and polyimide. Rather, the bronze can be replaced, for example, by any metal or metal alloy that has a liquid phase or transient liquid phase at the softening temperature (e.g., Heat Deflection temperature as measured, for instance, by ASTM standard D648) of the resin and a fracture toughness between 1 and 5 MPa.m^0.5 at room temperature. Alternatively, the polyimide can be replaced, for example, by any resin or polymer that has a softening temperature less than 500° C. (e.g., in the range of about 160° C. to 400° C.) and a ductility in the range of about 3% to 25%. In general, the specific selection of resin and metal alloy types is such that the tool is sufficiently brittle for the purpose of manufacture and durability, but ductile enough to withstand the grinding and handling stresses (i.e., overly stiff tools are susceptible to breakage).

The content of resin may range, for example, from about 1 to 50 volume percent (vol %), while the content of metal/metal alloy may range, for example, from about 40 to 85 vol %. The metal alloy can be bronze with, for example, 60/40 to 40/60 copper/tin by weight (e.g., 50/50 by weight %). The diamond content (or other suitable abrasive grain) may range, for example, from 10 to 30 vol %, at a concentration ranging from about 40 to 100 concentration. The diamond grit particles may have an average diameter, for instance, of not more than 40 microns in diameter, preferably in the range of 1 micron to 12 microns, and more preferably in the range of 1 micron to 3 microns. The bronze powder and polyimide particles may have an average diameter, for instance, of not more than 40 microns and more preferably 30 microns or less. The actual composition will vary depending on factors such as desired straightness and rigidity/ductility, as well as self-dressing capability and allowable degree of chipping along the kerf (if any). Such tools perform well in 1× slicing/polishing processes for hard brittle workpieces, such as in manufacturing of microelectronic wafer components (e.g., silicon wafers and Al₂O₃—TiC sliders).

The abrasive is not intended to be limited to diamond, and can be essentially any suitable abrasive such as CBN, fused alumina, sintered alumina, silicon carbide, or mixtures thereof. The selection of abrasive depends on factors such as the material being cut and desired tool cost. As is known, the abrasive grains may be provided with a coating which will vary in its nature, depending on the specific abrasive used. For instance, if the abrasive is diamond or CBN then a metal coating on the abrasive (e.g. nickel) can be used to improve grinding properties. Similarly, fused alumina's grinding quality is enhanced, in certain grinding or cutting applications, if the grain is coated with iron oxide or a silane such as gamma amino propyl triethoxy silane. Likewise, sintered sol gel and seeded sol gel alumina abrasive exhibit enhanced grinding properties when they have been supplied with a silica coating, or in some cases, improvement may result if the sintered abrasive is silane treated. The operable abrasive grit size can also vary depending on the desired performance, and in accordance with some embodiments of the present disclosure, the grit size is 40 microns or finer.

In various alternative embodiments, tools of the present application can have a thickness of 250 microns or less, preferably 100 microns or less, more preferably 70 microns or less, and even more preferably 65 microns or less. Although the tool type and its dimensions can vary as well (depending on the target application), one such example tool is a type 1A8 wheel, having a thickness of about 30 to 130 microns (e.g., 65 microns or less), an outside diameter of about 50 to 150 millimeters (e.g., 110 mm), and inside diameter of about 35 to 135 mm (e.g., 90 mm). The abrasive section of the multi-function blade generally extends from the outside diameter to the inside diameter of the wheel, although partial abrasive sections that extend from the outside diameter to some distance from the inner diameter can be used as well, when suitable.

The tool can be manufactured, for example, from a powder blend at around 300 to 420° C. In one such embodiment, the selection of the metal alloy is such that at least one of the phases present in the alloy melts at such a temperature, resulting in improved sinterability of the tool, better diamond retention, enhanced tool stiffness, and a path for extraction of the heat generated in slicing/polishing process. Polyimide generally does not possess a melting point at the process temperatures, but only softens. High pressures can be used to ensure that the densification is complete during the formation process (e.g., molding).

One commercially available abrasive tool consists of cobalt metal, resin, and fine diamond grits. However, the use of cobalt can pose a number of issues. Specifically, a cobalt-based product is typically very brittle and tends to break in handling and use. In addition, use of cobalt leads to a structure that is under-sintered and possesses poor grit retention (this is because cobalt doesn't flow very well at process temperatures associated with suitable resins). Depending on context, cobalt can be environmentally unfriendly. Furthermore, the high stiffness of cobalt may not be transferred to the tool due to sliding at the cobalt-resin interface. Other factors, such as the choice of resin type and fillers used, and process temperature also play a role in tool performance (e.g., beneficial qualities of resin deteriorate when subjected to excessive temperature).

Another subtle but significant issue associated with using cobalt is related to magnetic properties. In particular, cobalt is known as a hard ferro-magnetic material which will readily magnetize. To this end, it is believed that the cobalt in a cobalt-based blade may upset the magnetic properties of the sliced and polished workpiece (e.g., Al₂O₃—TiC sliders). This could be due either to residual cobalt contamination picked up on the surface of the workpiece during cutting (e.g., as the tool wears, cobalt is released from the tool and some of it sticks to or is embedded in the workpiece), or to the effect of cobalt in the tool influencing the local magnetic field around the grinding zone, which subsequently interacts with the workpiece.

In contrast to such conventional cobalt-based products, a tool configured in accordance with an embodiment of the present disclosure has shown superior ability to withstand handling and high grinding forces by maintaining a suitable degree of ductility, and can be used to grind at higher depths of cut. In addition, the exemplary metal alloy does not include any cobalt, and sufficiently flows at process temperatures associated with polyimide to provide excellent sinterability, grit retention, stiffness, and ductility. Moreover, a metal alloy of bronze is non-magnetic and thus does not influence the local magnetic field around the grinding zone, or contaminate the workpiece surface with magnetic particles. U.S. Pat. Nos. 5,313,742, 6,200,208, and 6,485,532 provide additional details relevant to conventional abrasive tools capable of cutting hard brittle materials. Each of the '742, '208, and '532 patents is herein incorporated by reference in its entirety.

Thus, abrasive tools configured in accordance with such embodiments can be used in simultaneous 1× dicing and polishing operations performed in the manufacture of Al₂O₃—TiC sliders and other such components made from hard brittle materials. In a more general sense, abrasive tools configured in accordance with such embodiments can be used to perform 1× processes involving the combination of cutting and polishing to a fine finish workpieces that are traditionally sliced or otherwise cut with one tool and polished with another. Such tools may be used in non-1× applications (e.g., 2×) as well, if so desired. The disclosed tools provide improved tool life, better edge quality (good perpendicularity and no or low degree of chipping), and better finish relative to conventional tools (no or fewer scratches). In addition, the tools effectively reduce manufacturing costs associated with time, labor, and power, by enabling a two-in-one process.

Example Tool Configuration #1

In one specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having a thickness of about 65 microns, an outside diameter of about 110 millimeters, and an inside diameter of about 90 mm, and the blade composition is as follows: 31.25 volume percent Vespel® SP1 polyimide (with the powder particles having an average diameter of about 30 microns), 50 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of about 30 microns), and 18.75 vol % of diamond (at 75 concentration, and having an average diameter of 1 to 3 microns). The diamonds can be, for instance, 1 to 3 μm (−8 μm) RB Amplex® diamond, or 1 to 2 μm (−8) RVM CSG Diamond Innovations® diamond. Other suitable diamond types and sources will be apparent in light of this disclosure. The tolerances on the tool dimensions and composition may be, for example, ±10 percent, although looser tolerances (e.g., ±20 percent or more) or tighter tolerances (e.g., ±5 percent or less) can be used as well, depending of the particular application and desired precision and performance.

The thinness of the tool reduces wasted work material, yet has a straightness that allows for precision slicing and edge quality (low kerf loss with substantially perpendicular kerf wall, such as within 15 degrees of the perpendicular plane or better). Straightness refers to the axial thickness of the wheel being substantially uniform at all radii from the radius of the arbor hole to the outer radius of the wheel. In one embodiment, this thin, straight tool thickness is achieved by double-sided lapping the tool down to 65 microns. Single-sided lapping may be used as well, but care must be given so as to not distort the tool (e.g., using cooling techniques and allocating additional manufacturing time).

In this particular example embodiment, the tool includes a substantially continuous metal alloy phase (pre-alloyed bronze), with either a substantially continuous or substantially discontinuous polyimide phase. This 1A8 tool design can be used, for example, in 1× applications where simultaneous slicing and polishing is desired. The substantially continuous metal alloy phase of bronze improves the stiffness of the tool (high aspect ratio of exposed tool, so stiffness is helpful in controlling kerf), and the polyimide adds a degree of compliance to the tool structure so that, during cutting, the diamond on the tool sides are pressed back slightly into the bond, thereby limiting the depth of cut which they take, and thus improving edge finish on the workpiece.

When compared to a cobalt-based polyimide tool of similar configuration, this example multifunction tool performed comparably with respect to edge straightness and chip thickness proximate the edge. However, the tool configured in accordance with this embodiment was relatively harder than the cobalt-based tool, and exhibited both lower tool wear and smaller kerf relative to the cobalt-based tool. In addition, AFM (atomic force microscope) analysis showed that this tool provided a better workpiece edge finish Ra of 27 Å, compared to the workpiece edge finish Ra of 43 Å provided by the cobalt-based tool.

Table 1 summarizes performance parameters of this comparative analysis between the Example 1 embodiment and the cobalt-based tool. These data are based on the first row or pass of the tool through the workpiece. For additional passes (rows), the difference in wear rate became further pronounced. For instance, after 15 rows (24 slots), the tool wear was about 36 microns for the cobalt-based tool and about 28 microns for the Example 1 embodiment. The comparative testing was done at a table speed of about 100 mm/min and tool speed of 9000 RPMs.

TABLE 1
Performance Comparative Data
		Cobalt-based
	Parameter	Tool	Embodiment #1
	Tool Wear	4	0
	μm
	Straightness	2	2
	μm
	Kerf	74	67
	μm
	Chips	1	1
	μm
	Surface Finish	43	27
	Ra, Å

In addition, it is noted that increasing tool speed of the Example 1 embodiment from 9000 RPMs to, for instance, 11000 to 18000 RPMs (depending on upper limit of machine) improved edge straightness and reduced need for tool dressing. On the other hand, lower tool speeds can be used, if performing intermediate tool dressing operations (e.g., in between each row or sub-set of rows) is acceptable.

With respect to particle sizes, there is generally no specific requirement. Commercially available sizes of the various tool components have been used as described herein, with acceptable results (as also described herein). However, it is generally believed that finer particle sizes of bronze may operate to improve diamond distribution and tool performance. Thus, in some embodiments described herein, bronze particles in the range of 10 microns or less are used (e.g., to improve distribution of the 1 to 3 micron diamond). However, and as will be appreciated in light of this disclosure, larger bronze particles (e.g., in the 30 micron range) are effective as well.

Example Tool Configuration #2

In another specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having dimensions as previously described, and a blade composition as follows: 21.25 volume percent Vespel® SP1 polyimide (with the powder particles having an average diameter of about 30 microns), 60 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of about 30 microns), and 18.75 vol % of diamond (at 75 concentration, and having an average diameter of 1 to 2 microns). Previous discussion with respect to tolerances is equally applicable here.

This example multifunction tool provided a workpiece surface finish Ra of 42 Å, with other performance parameters remaining comparable to the Example 1 embodiment.

Example Tool Configuration #3

In another specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having dimensions as previously described, and a blade composition as follows: 11.25 volume percent Vespel® SP1 polyimide (with the powder particles having an average diameter of about 30 microns), 70 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of about 5 to 8 microns), and 18.75 vol % of diamond (at 75 concentration, and having an average diameter of 1 to 3 microns). Previous discussion with respect to tolerances is equally applicable here.

This example multifunction tool provided a workpiece surface finish Ra of 48 Å, with other performance parameters remaining comparable to the Example 1 embodiment. However, this tool provided improved straightness, better entry and exit geometry (scratch-free entry and exit of cut) relative to Example 1 embodiment, and reduced dressing operations between rows.

Example Tool Configuration #4

In another specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having dimensions as previously described, and a blade composition as follows: 30.25 volume percent Vespel® SP1 polyimide (with the powder particles having an average diameter of about 30 microns), 57.25 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of 5 to 8 microns), and 12.5 vol % of diamond (at 50 concentration, and having an average diameter of 1 to 2 microns). Previous discussion with respect to tolerances is equally applicable here.

This example multifunction tool exhibited performance parameters comparable to Example 1 embodiment.

Example Tool Configuration #5

In another specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having dimensions as previously described, and a blade composition as follows: 20.25 volume percent Vespel® SP1 polyimide (with the powder particles having an average diameter of about 30 microns), 67.25 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of 5 to 8 microns), and 12.5 vol % of diamond (at 50 concentration, and having an average diameter of 1 to 2 microns). Previous discussion with respect to tolerances is equally applicable here.

This example multifunction tool exhibited performance parameters comparable to Example 3 embodiment.

In addition to the performance testing previously described, wear test data were measured for a number of samples having varying amounts of abrasives content, as well as bronze-polyimide ratio, to determine the effect of such variations on tool wear. While there was no significant change in tool wear attributed to varying diamond concentration (e.g., from 60 to 75 concentration), a significant change in tool wear can be achieved by increasing the bronze content (e.g., from 65 vol % to 70 vol % or 75 vol % corresponded to decrease in tool wear).

Example Tool Configuration #6

In another specific abrasive tool configuration according to an embodiment of the present disclosure, the tool is a type 1A8 wheel, having a thickness of about 65 microns, an outside diameter of about 110 millimeters, and an inside diameter of about 90 mm, and the blade composition is as follows: 26.5 volume percent Meldin 7001® polyimide (with the powder particles having an average diameter of about 10 microns), 54.8 vol % bronze (50/50 by weight of copper and tin, with the powder particles having an average diameter of about 8 microns), and 18.7 vol % of diamond (at 75 concentration, and having an average diameter of 1 to 2 microns). The diamonds can be, for instance, 1 to 2 μm (−8 μm) 1 to 2 μm (−8) RVM CSG Diamond Innovations® diamond. The tolerances on the tool dimensions and composition may be, for example, ±10 percent, although looser tolerances (e.g., ±20 percent or more) or tighter tolerances (e.g., ±5 percent or less) can be used as well, depending of the particular application and desired precision and performance. The tools are manufactured in a manner similar to the tools in Example 1.

The thinness of the tool reduces wasted work material, yet has a straightness that allows for precision slicing and edge quality (low kerf loss with substantially perpendicular kerf wall, such as within 15 degrees of the perpendicular plane or better). Straightness refers to the axial thickness of the wheel being substantially uniform at all radii from the radius of the arbor hole to the outer radius of the wheel. In one embodiment, this thin, straight tool thickness is achieved by double-sided lapping the tool down to 65 microns. Single-sided lapping may be used as well, but care must be given so as to not distort the tool (e.g., using special cooling techniques and allocating additional manufacturing time).

In this particular example embodiment, the tool includes a substantially continuous metal alloy phase (pre-alloyed bronze), with either a substantially continuous or substantially discontinuous polyimide phase. This 1A8 tool design can be used, for example, in 1× applications where simultaneous slicing and polishing is desired. The substantially continuous metal alloy phase of bronze improves the stiffness of the tool (high aspect ratio of exposed tool, so stiffness is helpful in controlling kerf), and the polyimide adds a degree of compliance to the tool structure so that, during cutting, the diamond on the tool sides are pressed back slightly into the bond, thereby limiting the depth of cut which they take, and thus improving edge finish on the workpiece.

When compared to a cobalt-based polyimide tool of similar configuration, this example multifunction tool performed comparably with respect to edge straightness and chip thickness proximate the edge.

Table 2 summarizes performance parameters of this comparative analysis between the Example 6 embodiment and the cobalt-based tool. In this example, tool performance was determined after allowing sufficient cuts for it to reach a steady state. The tool wear for example, is determined over 35 cuts after reaching the steady state. The comparative testing was done at a table speed of about 100 mm/min and tool speed of 9000 RPMs.

TABLE 2
Comparative Performance Data
		Cobalt-based
	Parameter	Tool	Embodiment #6
	Tool Wear over	10-11	12-14
	35 cuts,
	μm
	Straightness	2	2
	μm
	Kerf	74	67
	μm
	Chips	1	1
	μm

Methods of making abrasive tools as described herein can include one or more of the following steps:

(a) providing pre-selected proportions of particulate ingredients including superabrasive grains (e.g., fine diamond having average diameter of 1 to 2 microns), a polyimide, and a pre-alloyed bronze consisting essentially of about 40 to about 60 weight % of copper and about 40 to about 60 weight % of tin;

(b) mixing the particulate ingredients to form a substantially uniform composition, which can be formed using any suitable blending apparatus (e.g., double cone tumblers, twin-shell V-shaped tumblers, ribbon blenders, horizontal drum tumblers, and stationary shell/internal screw mixers);

(c) placing the substantially uniform composition into a mold of desired shape (e.g., 1A8 tool);

(d) compressing the mold to a pressure in the range of about 25-200 MPa for a duration effective to form a molded article;

(e) heating the molded article to a temperature less than 500° C. (e.g., in the range of about 100° C. to 450° C., or even more specifically, in the range of about 160° C. to 400° C.) for a duration effective to sinter the bronze and soften the polyimide, thereby integrating the abrasive grains and sintered bond into a composite of substantially continuous metal alloy phase, with a substantially continuous or substantially discontinuous polyimide phase (e.g., higher content such as 30 vol % or more of polyimide tends to provide a substantially continuous phase, while lower content such as less than 30 vol % tends to provide a substantially discontinuous phase; note, however, that either phase is acceptable and provides acceptable results);

(f) cooling the composite to form the abrasive tool; and

(g) lapping sides of the tool to provide desired degree of straightness and thickness (e.g., an axial thickness of the tool being substantially uniform at all radii from the radius of the arbor hole to the outer radius of the tool, with the final thickness being, e.g., about 65 microns). This lapping can be implemented as double-sided lapping, so as to further improve straightness.

The abrasive grits (e.g., diamonds) are generally present in both the bronze and polyimide phases, but predominantly in the bronze phase. The polyimide phase is more elastic than the bronze phase, and imparts a degree of elasticity to the abrasive tool, which is believed to control the depth of cut taken by the abrasive grits on the cutting edge, and possibly the sidewall of the tool (assuming a wheel configuration), so as to reduce the chip size taken due to the intended abrasion process and thus generate the surface finish required.

The abrasive tools described herein can be produced by a densification using cold-press or hot-press techniques. In a cold-press process, sometimes referred to as pressureless sintering, a blend of the composite components is introduced into a mold of desired shape and a high pressure is applied at room temperature to obtain a compact but friable molded article. The high pressure can be, for example, in the range of 25-200 MPa. Subsequently, pressure is relieved and the molded article is removed from the mold then heated to sintering temperature. The heating for sintering can be done, for instance, while the molded article is pressurized in an inert gas atmosphere to a lower pressure than the pre-sintering molding pressure (e.g., less than about 100 MPa, or even more specifically, less than about 50 MPa). Sintering can also take place under vacuum. During this low pressure sintering, the molded article (e.g., thin abrasive wheel of the 1A8 type) can be placed in a mold and/or sandwiched between flat plates, to help maintain its straightness during sintering. In a hot-press process, the blend of particulate bond composition is put in the mold, typically of graphite, and compressed to a high pressure as in the cold-press process. However, an inert gas is utilized and the high pressure is maintained while the temperature is raised, thereby achieving densification while the tool preform is under pressure.

Note that this method may be used to fabricate a single blade or multi-blade configuration. With respect to a multi-blade configuration made up of individually fabricated tools (gang configuration), there is an additional consideration of suitable tolerancing on each member tool of the gang. In more detail, while tolerances in a single blade embodiment may be acceptably higher, such high tolerances in a gang configuration may stack up to provide undesirable results (e.g., lack of desired precision). Thus, and in accordance with one embodiment of the present disclosure, tolerances of the individual tools included in the gang are such that any resulting stacking falls within an acceptable range. The ganged tools can be separated, for example, by spacers of a material such as alumina or steel. Alternatively, another embodiment is a multi-blade tool that is fabricated by forming a monolithic multi-blade structure from a thicker tool. The thicker tool can be made using the previously described manufacturing steps (a through f, and optionally g), with the initial tool thickness being sufficient to allow the desired number of individual tools to be formed therefrom (e.g., 3600 microns or thicker). Each of individual tools formed within that initial tool thickness can be, for example, under 125 microns (or less) and separated by the inner structure itself whose diameter is smaller than the thin outer tool. Such a monolithic structure effectively provides a built-in spacer between individual tools, thereby reducing tolerancing variables. A ganged assembly of individual tools having a thick inner section and thin outer section for cutting is described in the previously incorporated U.S. Pat. No. 5,313,742. This principle (thick inner section and thin outer section) can be adopted into a monolithic structure as described herein. The forming of individual tools from the initial thicker tool can be accomplished, for instance, by electro-discharge machining (EDM), although other suitable machining techniques can be used (e.g., milling, wire sawing, etc). Finishing techniques such as lapping can be used to further refine parameters (thickness and straightness) of the individual tools.

The foregoing description of the embodiments of the disclosure has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of this disclosure. For instance, Vespel® SP1 polyimide is noted as acceptable for use in embodiments, but other comparable polyimides or polymers having qualities that suitably interact with the metal alloy and abrasive can be used as well. Likewise, the wheel types may vary (e.g., 1A1, 1A8, or any relatively thin abrasive wheel configuration). It is intended that the scope of the invention be limited not by this detailed description, but rather by the claims appended hereto.

The Abstract of the Disclosure is provided solely to comply with U.S. requirements and, as such, is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, various features may be grouped together or described in a single embodiment for the purpose of streamlining the disclosure. This disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may be directed to less than all features of any of the disclosed embodiments. Thus, the following claims are incorporated into the Detailed Description, with each claim standing on its own as enabling and describing discretely claimed subject matter.

Claims

1. A multifunction abrasive tool, comprising:

a hybrid bond of a bronze and a polyimide; and

a plurality of fine abrasive grits blended with the hybrid bond;

wherein the tool has a substantially uniform thickness of 250 microns or less.

2. The multifunction abrasive tool of claim 1, wherein the tool is a 1A8 type wheel or a 1A1 type wheel, having a thickness of about 100 microns or less.

3. The multifunction abrasive tool of claim 1, having a substantially uniform thickness of about 65 microns or less.

4. The multifunction abrasive tool of claim 1, wherein the tool includes about 1 to 50 volume percent (vol %) of polyimide, about 40 to 85 vol % of bronze, and about 5 to 40 vol % of fine abrasive grits.

5. The multifimction abrasive tool of claim 4, wherein the tool includes about 10 to 40 vol % of polyimide, about 45 to 75 vol % of bronze, and about 10 to 25 vol % of fine abrasive grits.

6. The multifunction abrasive tool of claim 5, wherein the tool includes about 11.25 vol % of polyimide, about 70 vol % of bronze, and about 18.75 vol % of fine abrasive grits, with each component having a tolerance of ±/−20%.

7. The multifunction abrasive tool of any one of claim 1, wherein the bronze consists essentially of 60/40 to 40/60 by weight of copper and tin.

8. The multifunction abrasive tool of claim 1, wherein the polyimide consists essentially of particles having an average diameter of about 40 microns or less.

9. The multifunction abrasive tool of claim 1, wherein the bronze consists essentially of particles having an average diameter of about 40 microns or less.

10. The multifunction abrasive tool of claim 1, wherein the fine abrasive grits consist essentially of diamonds having an average diameter of about 40 microns or less.

11. The multifunction abrasive tool of claim 10, wherein the diamonds have an average diameter of about 1 to 12 microns.

12. The multifunction abrasive tool of claim 11, wherein the diamonds have an average diameter of about 1 to 3 microns.

13. The multifunction abrasive tool of any one of claim 1, wherein the polyimide is Vespel® SP1 polyimide.

14. The multifunction abrasive tool of claim 1, wherein the polyimide is Meldin 7001® polyimide.

15. The multifunction abrasive tool of claim 1, wherein the tool is included in a multi-blade configuration that includes a plurality of such tools in a gang-like configuration.

16. An abrasive tool, comprising:

a hybrid bond of a metal or metal alloy and a resin associated with a softening temperature less than 500° C., wherein the metal or metal alloy has a liquid phase or transient liquid phase at the softening temperature of the resin and a fracture toughness between 1 and 5 MPa.m0.5 at room temperature,; and

a plurality of fine abrasive grits blended with the hybrid bond;

wherein the tool has a substantially uniform thickness of 250 microns or less.

17. The abrasive tool of claim 16, wherein the softening temperature is a Heat Deflection Temperature as measured by ASTM standard D648, and is in the range of 160 to 400° C.

18. The abrasive tool of claim 16, wherein the resin has a ductility in the range of about 3% to 25%.

19. The abrasive tool of claim 16, wherein the metal or metal alloy is a bronze

20. The abrasive tool of claim 16, wherein the resin is a polyimide.