MAGNESIUM ALLOY
The present invention relates to a magnesium alloy having controlled corrosion resistance properties, which comprises magnesium (Mg) and an alloying element and includes a magnesium phase and a phase composed of magnesium and the alloying element, wherein the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is greater than 0 V but not greater than 0.2 V.
This application claims the benefit of priority of Korean Patent Application No. 10-2009-0120356, filed with the Korean Intellectual Property Office on Dec. 7, 2009, the disclosure of which is incorporated herein by reference in its entirety.
TECHNICAL FIELDThe present invention relates to a magnesium alloy.
BACKGROUND ARTMagnesium alloys are easily shaped, but have disadvantages of poor corrosion resistance and poor strength. Studies are continually performed with the aim of suitably changing the composition of magnesium alloys in order to improve the corrosion resistance and strength of magnesium alloys. In addition, studies have demonstrated that an increase in the amount of alloying elements in the magnesium alloy leads to an increase in the mechanical strength of the magnesium alloy. However, as the amount of alloying elements increases, several phases are formed, and an increase in the difference in electrical potential between these phases results in conditions such that a galvanic circuit, which increases the rate of corrosion of the alloy, is likely to be formed.
Therefore, there is a need for studies on a magnesium alloy, the corrosion resistance properties of which can be controlled and which has excellent corrosion resistance and strength.
DISCLOSURE Technical ProblemIt is an object of the present invention to provide a magnesium alloy whose corrosion resistance properties are controlled by adding an alloying element having an electrical potential different from that of magnesium, depending on the intended use of the magnesium alloy.
Another object of the present invention is to provide a magnesium alloy, the corrosion resistance and strength properties of which can be controlled through post-treatment processing.
Technical SolutionIn order to accomplish the above objects, the present invention provides a magnesium alloy having controlled corrosion resistance properties, which comprises magnesium (Mg) and an alloying element and includes a magnesium phase and a phase composed of magnesium and the alloying element, wherein the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is greater than 0 V but not greater than 0.2 V.
The present invention also provides a method for preparing a magnesium alloy having controlled corrosion resistance properties, the method comprising adding, to a magnesium alloy comprised of magnesium and an alloying element, a third element, thereby reducing the difference in electrical potential between a magnesium phase and a phase composed of magnesium and the alloying element to greater than 0 V but not greater than 0.2 V.
Advantageous EffectsThe corrosion resistance properties of the magnesium alloy according to the present invention can be controlled using the difference in electrical potential between the magnesium and the alloying element. In addition, the corrosion resistance and strength properties of the magnesium alloy of the present invention can also be controlled through post-treatment processing. Furthermore, due to these effects, the magnesium alloy can be used in the industrial and medical fields.
Hereinafter, the present invention will be described in detail.
I. Magnesium Alloy
The present invention is directed to a magnesium alloy having controlled corrosion resistance properties, which comprises magnesium (Mg) and an alloying element and includes a magnesium phase and a phase composed of magnesium and the alloying element.
Herein, the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is greater than 0 V but not greater than 0.2 V, and is preferably close to 0. If the magnesium alloy satisfies the above-described range, it has a very low rate of degradation, and thus can be effectively used in the industrial and medical fields. In addition, the magnesium alloy has excellent corrosion resistance and strength.
The alloying element is not specifically limited, as long as the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element falls within the above-described range. Examples of the alloying element include calcium (Ca), iron (Fe), manganese (Mn), cobalt (Co), nickel (Ni), chromium (Cr), copper (Cu), cadmium (Cd), zirconium (Zr), silver (Ag), gold (Au), palladium (Pd), platinum (Pt), rhenium (Re), iron (Fe), zinc (Zn), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), silicon (Si), phosphorus (P) and selenium (Se).
Meanwhile, the magnesium alloy that realizes the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is preferably represented by the following formula 1:
MgaCabXc [Formula 1]
wherein a, b and c represent the molar fractions of the respective components, a+b+c=1, 0.5≦a<1, 0≦b≦0.4, and 0≦c≦0.4; if at least one of b and c is greater than 0, and c is 0, the content of Ca is 5-33 wt % based on the total weight of the magnesium alloy; and X is one or more selected from among zirconium (Zr), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), chromium (Cr), manganese (Mn), zinc (Zn), silicon (Si), phosphorus (P), nickel (Ni) and iron (Fe).
Even if X represents two or more elements, the total molar fraction of the elements of X satisfies the range of c. As the contents of Ca and X increase, the strength of the magnesium alloy increases while the rate of degradation thereof also increases. Thus, the amounts of Ca and X in the magnesium alloy of the present invention can be determined within the above-described ranges by taking into consideration the required strength of the alloy and the rates of degradation of the additional metals.
When nickel (Ni) is included in X, nickel reduces the toxicity of the magnesium alloy and makes it possible to control the rate of corrosion of the magnesium alloy. Herein, the content of nickel is preferably 100 ppm or less, and more preferably 50 ppm or less. In addition, when iron (Fe) is included in X, iron significantly influences the increase in the rate of corrosion of the magnesium, and for this reason, the content of iron is preferably 1,000 ppm or less, and more preferably 500 ppm or less. If iron is contained in an amount exceeding the upper limit of the above range, iron will be present as an independent factor, without being fixed to magnesium, thus increasing the rate of corrosion of the magnesium alloy.
The magnesium alloy that realizes the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is preferably represented by the following formula 2.
The magnesium alloy represented by formula 2 comprises, based on the total weight thereof, greater than 0 wt % but not greater than 23 wt % of calcium (Ca), greater than 0 wt % but not greater than 10 wt % of Y, and the balance of magnesium (Mg).
Mg—Ca—Y [Formula 2]
wherein Y is Mn or Zn.
When the composition of the magnesium alloy represented by formula 2 falls within the above-described ranges, it has not only improved mechanical properties, but also improved corrosion resistance, and does not undergo brittle fracture.
The magnesium alloy represented by formula 2 preferably comprises, based on the total weight thereof, greater than 0 wt % but not greater than 23 wt % of calcium (Ca), 0.1-5 wt % of Y, and the balance of magnesium (Mg). More preferably, the magnesium alloy represented by formula 2 comprises greater than 0 wt % but not greater than 23 wt % of calcium (Ca), 0.1-3 wt % of Y, and the balance of Mg. The reason for this is that when the same corrosion rate is realized, taking into consideration the possible side effects of impurities, the contents of the impurities should preferably be low.
The magnesium alloy that realizes the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is preferably represented by the following formula 3. The magnesium alloy represented by formula 3 comprises, based on the total weight thereof, greater than 0 wt % but no greater than 40 wt % of Z and the balance of magnesium (Mg).
Mg—Z [Formula 3]
wherein Z is one or more selected from among manganese (Mn), cobalt (Co), nickel (Ni), chromium (Cr), copper (Cu), cadmium (Cd), zirconium (Zr), silver (Ag), gold (Au), palladium (Pd), platinum (Pt), rhenium (Re), iron (Fe), zinc (Zn), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), silicon (Si), phosphorus (P) and selenium (Se). The magnesium alloy is preferably subjected to surface treatment. The surface treatment is preferably shot peening.
The magnesium alloy which is included in an implant of the present invention may be subjected to surface coating. When the surface coating is performed, a corrosion-resistant product can be produced on the surface of the magnesium alloy, whereby the rate of degradation of the magnesium alloy can be delayed.
The surface coating may be performed with a ceramic and/or polymer material.
Hereinafter, the coating of the magnesium alloy surface with a ceramic material will be described. When the magnesium is immersed in a biomimetic solution or physiological saline, the surface of the magnesium alloy can be coated with a corrosion-resistant product. Herein, the corrosion-resistant product may be a ceramic material, in which the ceramic material may be magnesium oxide or calcium phosphate. In addition, after the surface of the biodegradable magnesium alloy is coated with the corrosion-resistant product, it may further be coated with a polymer. Examples of the polymer which may be used in the present invention are as described below.
The polymer that is used to coat the surface of the magnesium alloy is not specifically limited, as long as it is one that is conventionally used in the art. Preferred examples of the polymer for use in the present invention include poly(L-lactide), poly(glycolide), poly(DL-lactide), poly(dioxanone), poly(DL-lactide-co-L-lactide), poly(DL-lactide-co-glycolide), poly(glycolide-co-trimethylene carbonate), poly(L-lactide-co-glycolide), poly(e-caprolactone), and combinations thereof.
The magnesium alloy according to the present invention can be used in various ways. For example, it may be coated on the surface of ceramic, metal and polymer materials. In addition, the magnesium alloy according to the present invention may be used in combination with a ceramic or polymeric material.
II. Preparation Method
The present invention also provides a method for preparing a magnesium alloy having controlled corrosion resistance properties, the method comprising adding, to a magnesium alloy comprised of magnesium and an alloying element, a third element, thereby reducing the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element to greater than 0 V, but not greater than 0.2 V. Herein, the magnesium alloy is preferably an alloy comprising magnesium and calcium. In addition, the third element is preferably zinc.
III. Method for Preparing Magnesium Alloy
The inventive method for preparing the magnesium alloy having controlled corrosion resistance properties may comprise the steps of: a) providing the magnesium alloy; and b) shaping the magnesium alloy.
Step a) of the method is preferably performed by melting the magnesium.
More specifically, step a) may be performed by melting the magnesium in a vacuum atmosphere or in an atmosphere of inert gas such as argon (Ar), which does not react with magnesium. In addition, step a) may be performed by melting the magnesium using various methods, such as a resistance heating method, in which heat is generated by electrically heating a resistive material, an induction heating method, in which a current is allowed to flow through an induction coil, or a method that uses a laser or focused light. Among these melting methods, the resistance heating method is the most economical method. In addition, the melted alloy (hereinafter referred to as the “melt”) is preferably stirred during the melting of magnesium such that impurities can be mixed well.
Step b) of the inventive method for preparing the magnesium alloy may be performed by shaping the molten magnesium alloy using one or more selected from the group consisting of a quenching method, an extrusion method, and a metal processing method.
The quenching method can be used in order to improve the mechanical strength of the magnesium alloy. More specifically, if magnesium is melted in step a), a method of immersing a crucible containing the molten magnesium in water may be used. In addition, a quenching method of spraying inert gas such as argon onto the molten magnesium may also be used. This spray-quenching method can quench the molten magnesium at a very high quenching rate, thereby realizing a very fine structure. However, in the case in which magnesium is cast in a small size, it should be noted that a plurality of pores (black portions) can also be formed.
The extrusion method is used to make the structure of the magnesium uniform and enhance the mechanical performance of the magnesium. The extrusion method can control the strength and corrosion resistance properties of the magnesium alloy of the present invention.
The extrusion method is preferably performed at 300˜450° C. Furthermore, the extrusion of magnesium may be carried out at a ratio of reduction in the cross-sectional area before and after extrusion (an extrusion ratio) of 10:1 to 30:1. As the extrusion ratio increases, the fine structure of the extruded material becomes more uniform, and defects formed during casting are easily removed. In this case, it is preferred to increase the capacity of the extrusion system.
The metal processing method is not particularly limited so long as it is known in the art. Examples of the metal processing method include a method in which the molten magnesium is poured and cast in a mold that is processed such that it has a shape close to the shape of a final product; a method in which the molten magnesium is prepared into an intermediate material such as a rod or a sheet and is then subjected to turning or milling; and a method in which the magnesium alloy is forged at a higher pressure, thus obtaining a final product.
MODE FOR INVENTIONHereinafter, the preparation of magnesium alloys will be described in further detail with reference to examples. It is to be understood, however, that these examples are provided for illustrative purposes only, and are not intended to limit the scope of the present invention.
Examples 1 to 4 and Comparative Examples 1 and 2 Preparation of Magnesium Alloys Examples 1 and 2 and Comparative ExampleElements were mixed to have the compositions shown in Table 1 below, and were charged into a stainless steel (SUS 410) crucible having an inner diameter of 50 mm. Then, while argon (Ar) gas was allowed to flow around the crucible so that the magnesium in the crucible did not come into contact with air, the temperature of the crucible was increased to about 700˜750° C. using a resistance heating furnace, thereby melting the magnesium. The crucible was shaken so that the molten magnesium could be mixed well with the impurities. The completely molted Mg alloy was quenched, thus preparing solid-state magnesium. Also, upon quenching, the crucible was immersed in water (20° C.) to enhance the mechanical strength of magnesium such that the molten magnesium was rapidly quenched, thereby preparing a magnesium alloy.
The magnesium alloys of Examples 1 and 2 and Comparative Example 1 were extruded. The extrusion was performed at 370-375° C., and the ratio of reduction in the cross-sectional area before and after extrusion (the extrusion ratio) was set at 15:1. Herein, the extruded alloy of Example 2 corresponds to the magnesium alloy of Example 1; the extruded alloy of Example 4 corresponds to the magnesium alloy of Example 2; and the extruded alloy of Comparative Example 2 corresponds to the magnesium alloy of Comparative Example 1.
Test Example 1 Evaluation of Rate of Corrosion of Magnesium AlloyIn general, the rate of corrosion of magnesium alloys is determined by measuring the amount of hydrogen generated when the magnesium alloy is immersed in the solution shown in Table 2 below. This is because the biodegradation of magnesium results in the generation of hydrogen and the solution shown in Table 2 is a biomimetic solution.
As can be seen in
The magnesium alloys of Examples 1 to 4 and Comparative Examples 1 and 2 were electric-discharge-machined into specimens having a diameter of 3 mm and a length of 6 mm. The upper and lower surfaces of the specimens were polished with #1000 emery paper to adjust the level of the surface. The specimens were horizontally placed on a jig made of tungsten carbide, and then a force was vertically applied to the specimens using the head of a compression tester with a maximum load of 20 tons. At this time, the vertical speed of the head was 10−4/s. During the test, the changes in strain and compressive stress were recorded in real time using an extensometer and a load cell provided in the compression tester. At this time, the size of the specimen was too small to place the extensometer in the specimen, so the extensometer was placed in the jig of the tester that was used to press the specimen. Therefore, the strain of the specimen was measured as higher than its actual strain.
In addition, Table 3 below shows the strengths of the magnesium alloys of Examples 1 to 4 and Comparative Examples 1 and 2. In Table 3, Y.S indicates yield strength, and UCS indicates ultimate compression strength.
As can be seen in
From the results in
The alloy of Example 2 was subjected to surface treatment (shot peening), and the results of the treatment are shown in
As can be seen in
In addition, after surface treatment, plastic deformation of the surface occurred, thus reducing the rate of degradation of the alloy and increasing the strength thereof. Furthermore, it will reflect less light in an operating room so as not to interfere with vision, and gives an elegant feel. In addition, when the surface of the magnesium becomes rough, the adhesion of bone to the surface can be improved.
Examples 5 to 9 Preparation of Magnesium AlloysMagnesium alloys of Examples 5 to 9 were prepared using the compositions shown in Table 4 below according to the method of Example 1.
As can be seen in
The corrosion rates of the magnesium alloys were determined by measuring the amount of hydrogen that was generated when the magnesium alloys were immersed in the solution of Table 2 above.
As can be seen in
As can be seen in
As can be seen in
Claims
1. A magnesium alloy having controlled corrosion resistance properties, which comprises magnesium (Mg) and an alloying element and includes a magnesium phase and a phase composed of magnesium and the alloying element, wherein the difference in electrical potential between the magnesium phase and the phase composed of magnesium and the alloying element is greater than 0 V but not greater than 0.2 V.
2. The magnesium alloy of claim 1, wherein the magnesium alloy contains no aluminum.
3. The magnesium alloy of claim 1, wherein the magnesium alloy contains no rare earth element.
4. The magnesium alloy of claim 1, wherein the alloying element is one or more selected from among calcium (Ca), iron (Fe), manganese (Mn), cobalt (Co), nickel (Ni), chromium (Cr), copper (Cu), cadmium (Cd), zirconium (Zr), silver (Ag), gold (Au), palladium (Pd), platinum (Pt), rhenium (Re), iron (Fe), zinc (Zn), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), silicon (Si), phosphorus (P) and selenium (Se).
5. The magnesium alloy of claim 1, wherein the magnesium alloy is represented by the following formula 1: wherein a, b and c represent the molar fractions of the respective components, a+b+c=1, 0.5≦a<1, 0≦b≦0.4, and 0≦c≦0.4; if at least one of b and c is greater than 0 and c is 0, the content of Ca is 5-33 wt % based on the total weight of the magnesium alloy; and X is one or more selected from among zirconium (Zr), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), chromium (Cr), manganese (Mn), zinc (Zn), silicon (Si), phosphorus (P), nickel (Ni) and iron (Fe).
- MgaCabXc [Formula 1]
6. The magnesium alloy of claim 1, wherein the magnesium alloy is represented by the following formula 2 and comprises, based on the total weight thereof, greater than 0 wt % but not greater than 23 wt % of calcium (Ca), greater than 0 wt % but not greater than 10 wt % of Y, and a balance of magnesium (Mg): wherein Y is Mn or Zn.
- Mg—Ca—Y [Formula 2]
7. The magnesium alloy of claim 1, wherein the magnesium alloy is represented by the following formula 3 and comprises, based on the total weight thereof, greater than 0 wt % but not greater than 40 wt % of Z and a balance of magnesium (Mg): wherein Z is one or more selected from among manganese (Mn), cobalt (Co), nickel (Ni), chromium (Cr), copper (Cu), cadmium (Cd), zirconium (Zr), silver (Ag), gold (Au), palladium (Pd), platinum (Pt), rhenium (Re), iron (Fe), zinc (Zn), molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti), strontium (Sr), silicon (Si), phosphorus (P) and selenium (Se).
- Mg—Z [Formula 3]
8. The magnesium alloy of claim 1, wherein the magnesium alloy is surface-treated.
9. A method for preparing a magnesium alloy having controlled corrosion resistance properties, the method comprising adding, to a magnesium alloy comprised of magnesium and an alloying element, a third element, thereby reducing the difference in electrical potential between a magnesium phase and a phase composed of magnesium and the alloying element to greater than 0 V but not greater than 0.2 V.
10. The method of claim 9, wherein the magnesium alloy comprises magnesium and calcium, and the third element is zinc.
Type: Application
Filed: Dec 7, 2010
Publication Date: Oct 25, 2012
Inventors: Ja-Kyo Koo (Seoul), Hyun-Kwang Seok (Seoul), Seok-Jo Yang (Daejeon), Yu-Chan Kim (Seoul), Sung-Youn Cho (Uijeongbu-si), Jong-Tack Kim (Jeonju-si)
Application Number: 13/511,891
International Classification: C22C 23/04 (20060101); C22C 23/00 (20060101);