IODIDE SCINTILLATOR FOR RADIATION DETECTION

Abstract

The present disclosure discloses, in one arrangement, a single crystalline iodide scintillator material having a composition of the formula AM1-xEuxI3, A3M1-xEuxI5 and AM2(1-x)Eu2xI5, wherein A consists essentially of any alkali metal element (such as Li, Na K, Rb, Cs) or any combination thereof, M consists essentially of Sr, Ca, Ba or any combination thereof, and 0≦x≦1. In another arrangement, the above single crystalline iodide scintillator material can be made by first synthesizing a compound of the above composition and then forming a single crystal from the synthesized compound by, for example, the Vertical Gradient Freeze method. Applications of the iodide scintillator materials include radiation detectors and their use in medical and security imaging.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims the benefit of U.S. Provisional Application Ser. No. 61/332,945, filed May 10, 2010. The present application also relates to commonly assigned non-provisional U.S. patent application entitled “CHLORIDE SCINTILLATOR FOR RADIATION DETECTION”, filed on the same day as the present application and claiming the benefit of U.S. Provisional Application Ser. No. 61/332,972, filed May 10, 2010 and non-provisional U.S. patent application entitled “HALIDE SCINTILLATOR FOR RADIATION DETECTION”, filed on the same day as the present application and claiming the benefit of U.S. Provisional Application Ser. No. 61/332,934, filed May 10, 2010. All applications are incorporated herein by reference.

TECHNICAL FIELD

This disclosure relates to scintillator materials used for detecting ionizing radiation, such as X-rays, gamma rays and thermal neutron radiation and charged particles, in security, medical imaging, particle physics and other applications. This disclosure relates particularly to iodide scintillator materials. Certain arrangements also relate to specific compositions of such scintillator material, method of making the same and devices with such scintillator materials as components.

BACKGROUND

Scintillator materials, which emit light pulses in response to impinging radiation, such as X-rays, gamma rays and thermal neutron radiation and charged particles, are used in detectors that have a wide range of applications in medical imaging, particle physics, geological exploration, security and other related areas. Considerations in selecting scintillator materials typically include, but are not limited to, luminosity, decay time and emission wavelengths.

While a variety of scintillator materials have been made, there is a continuous need for superior scintillator materials.

SUMMARY OF THE DISCLOSURE

The present disclosure relates generally to iodide scintillator materials and method of making such scintillator materials. In one arrangement, an iodide scintillator material is single-crystalline and; has a composition of one of the formulas AM_1-xEu_xI₃, A₃M_1-xEu_xI₅ and AM_2(1-x)Eu_2xI₅, wherein A consists essentially of any alkali metal element (such as Li, Na K, Rb, Cs) or any combination thereof, M consists essentially of Sr, Be or any combination thereof, and 0≦x≦1. Scintillators of this type include single-crystals of ASr_1-xEu_xI₃, A₃Sr_1-xEu_xI₅ and ASr_2(1-x)Eu_2xI₅. More specific examples include single-crystalline CsSr_1-xEu_xI₃, Cs₃Sr_1-xEu_xI₅ and CsSr_2(1-x)Eu_2xI₅.

A further aspect of the present disclosure relates to a method of making chloride scintillator materials of the above-mentioned compositions. In one example, high-purity starting iodides (such as CsI, SrI₂, EuI₂ and rare-earth iodide(s)) are mixed and melted to synthesize a compound of the desired composition of the scintillator material. A single crystal of the scintillator material is then grown from the synthesized compound by the Bridgman method (or Vertical Gradient Freeze (VGF) method), in which a sealed ampoule containing the synthesized compound is transported from a hot zone to a cold zone through a controlled temperature gradient at a controlled speed to form a single-crystalline scintillator from molten synthesized compound.

Another aspect of the present disclosure relates to a method of using a detector comprising one of the scintillation materials described above for imaging.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an energy spectrum of a CsSr_1-xEu_1-xI₃ crystal, with x=0.01 (normalized to BGO standard sample at channel no. 100); the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

FIG. 2 shows an energy spectrum of a CsSr_1-xEu_xI₃ crystal, with x=0.05, under the same conditions as for FIG. 1.

FIG. 3 shows an energy spectrum of a CsSr_1-xEu_xI₃ crystal, with x=0.075, under the same conditions as for FIG. 1.

FIG. 4 shows an energy spectrum of a CsSr_1-xEu_xI₃ crystal, with x=0.1, under the same conditions as for FIG. 1.

FIG. 5 shows a scintillation decay time spectrum of a CsSr_1-xEu_xI₃ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

FIG. 6 shows a scintillation decay time spectrum of a CsSr_2(1-x)Eu_2xI₅ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

FIG. 7 shows energy spectra of two CsSr_1-xEu_xI₃ crystals, with x=0.07 and 0.08, respectively, under the same conditions as for FIG. 1.

FIG. 8 shows a scintillation decay time spectrum of a CsSr_1-xEu_xI₃ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

FIG. 9 shows a scintillation decay time spectrum of a CsSr_2(1-x)Eu_xI₃ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

DETAILED DESCRIPTION

I. Overview

Inorganic scintillators are commonly used in nuclear and high-energy physics research, medical imaging, homeland security, and geological exploration. These materials typically possess sufficient stopping power for detection, high luminosity, high spectral energy resolution at room temperature and short decay time.

The viability of halide scintillators has been, and continues to be, investigated. For example, LaBr₃ doped with Ce³⁺ is one of the best and most commonly used scintillators in security applications. As another example, SrI₂ doped with Eu²⁺ exhibits a high light output of 85,000 photons/MeV and ˜4% energy resolution.

The present disclosure relates to halide scintillator materials and more particularly discloses new iodide single-crystal scintillators and method of making them. In one arrangement, an iodide scintillator material is single-crystalline and has a composition of the formula:

ASr_1-xEu_xI₃,

A₃Sr_1-xEu_xI₅ or

ASr_2(1-x)Eu_2xI₅,

wherein A consists essentially of any alkali metal element (such as Li, Na K, Rb, Cs) or any combination thereof, and 0≦x≦1. More specific examples include CsSr_1-xEu_xI₃, Cs₃Sr_1-xEu_xI₅ and CsSr_2(1-x)Eu_2xI₅.

A further aspect of the present disclosure relates to a method of making chloride scintillator materials of the above-mentioned compositions. In one example, high-purity starting iodides (such as CsI, SrI₂, Eu₂ and rare-earth iodide(s)) are mixed and melted to synthesize a compound; of the desired composition of the scintillator material. A single crystal of the scintillator material is then grown from the synthesized compound by the Bridgman method (or Vertical Gradient Freeze (VGF) method), in which a sealed ampoule containing the synthesized compound is transported from a hot zone to a cold zone through a controlled temperature gradient at a controlled speed to form a single-crystalline scintillator from molten synthesized compound.

In another aspect of the present disclosure, the above-described scintillator materials are used in radiation detection by scintillation. For example, a radiation detector can include a scintillator described above for generating photons in response to the impinging radiation. The scintillator is optically coupled to a photon detector, such as a photomultiplier tube (PMT), arranged to receive the photons generated by the scintillator and adapted to generate a signal indicative of the photon generation. Such detectors can be used in applications such as imaging for security checking and medical diagnosis.

II. Example Configurations

(a) Scintillator Crystal Growth

In one arrangement, iodide single-crystals described above were grown. First, CsI, SrI₂, EuI₂ and additional rare earth iodides were prepared and loaded into a quartz ampoule in a glove box with pure nitrogen atmosphere. The starting materials were all anhydrous beads with at least 99.99% purity (available, e.g., from Sigma-Aldrich). The loaded ampoule was then connected to a vacuum system. The ampoule was sealed by a hydrogen torch after the vacuum inside the quartz ampoules was evacuated to at least 1×10⁻⁶ mBar. Vertical Gradient Freeze (VGF) technique was used to grow ASr_1-xEu_xI₃, A₃Sr_1-xEu_xI₅ and ASr_2(1-x)Eu_2xI₅ single crystals. The single crystals were grown in vacuum-sealed quartz ampoules of up to 1 inch diameter. A Mellen 24-zone Sunfire Electro-Dynamic Gradient furnace was used to create a vertically translating thermal gradient. The thermal gradient was electrically moved through the whole length of the crystal growth ampoule at a speed of 0.5-2 mm/hour (e.g., 1 mm/hour). Single crystal was grown from a capillary connected to the bottom of the ampoules. The capillary insures only one single crystal grain can propagate in to the ampoule body. After the growth was finished, the crystal was cooled down to room temperature at a rate of about 10° C./hour. The crystal was then cut, and ground and polished (as needed) in the glove box. Single crystals samples of about 10 mm across were obtained.

(b) Characterization of Scintillator Crystals

Certain samples were characterized without polishing while for certain others, plates of about 1-3 mm in thickness were cut from the boules and polished using a set of sand papers and mineral oil. To identify the obtained phase, powder X-ray diffraction (XRD) analysis was carried out in air at room temperature. To minimize the effects of self-absorption, small samples (typically 1-2 mm thick, 3 mm×3 mm) were selected for the optical characterization.

Scintillation time profiles were recorded using the time-correlated single photon technique and a ¹³⁷Cs gamma-ray source. Radioluminescence spectra were measured at room temperature (RT) under continuous irradiation from an X-ray generator (operating, e.g., at 35 kV and 0.1 mA). Light output measurements were carried out on samples covered in mineral oil and directly coupled to a photomultiplier tube (PMT) and covered with Teflon tape. A Hamamatsu 3177-50 PMT was used for absolute light output measurements. Gamma-ray energy spectra were recorded using a ¹³⁷Cs source with a 10 μs shaping time. The integral quantum efficiency of the PMT according to the emission spectrum of the scintillators was used to calculate the number of photons per unit gamma ray energy. The energy resolution, at 662 keV was determined from the full-width at half-maximum (FWHM) of the 662 keV photopeak.

(c) Example Results

According to certain aspects of the present disclosure, single crystals of the iodide materials suitable for scintillator applications were made, and their scintillation properties were measured and have demonstrated high performance under optical, X-ray, gamma ray excitations. These scintillators exhibit Eu²⁺ 5d-4f luminescence.

FIGS. 1 to 4 shows the energy spectra for unpolished CsSr_1-xEu_xI₃, where x=0.01, 0.05, 0.075 and 0.1, respectively. The channel numbers are proportional to the relative light output of the sample. The relative light output (photo peak position) of the reference crystal BGO is 100 on this scale. The light output of these samples was at least about 40,000 photons/MeV.

FIGS. 5 and 6 show the scintillation time profiles for unpolished CsSr_0.99Eu_0.01I₃ and CsSr_1.98Eu_0.02I₅ samples, respectively. Both profiles were measured by a ¹³⁷Cs source. The scintillation decay times for CsSr_0.99Eu_0.01I₃ consist of two components: 429 ns for 20% and 1421 ns for 80%. The scintillation decay times for CsSr_1.98Eu_0.02I₅ are 207 ns for 35% and 1,114 ns for 65%.

FIG. 7 shows energy spectra of two polished CsSr_1-xEu_xI₃ crystals, with x=0.07 and 0.08, respectively, as compared to that of BGO. The absolute light yield is about twelve (12) times that of BGO for CsSr_0.93Eu_0.07I₃ and about eight (8) times that of BGO for CsSr_0.92Eu_0.08I₃.

FIG. 8 shows a scintillation decay time spectrum of a polished CsSr_1-xEu_xI₃ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV). The decay spectrum was fitted to a single exponential curve, with a decay time of about 1.7 μs.

FIG. 9 shows a scintillation decay time spectrum of a polished CsSr_2(1-x)Eu_2xI₃ crystal, with x=0.01; the spectrum was measured using ¹³⁷Cs gamma-ray source (662 keV).

In aspect of the present disclosure, certain properties of certain iodide scintillator crystals disclosed above were measured as a function of composition. For example, light yield, energy resolution and scintillation decay times were measured as a function of composition for single-crystalline CsSr_1-xEu_xI₃ samples. The results are listed in Table I.

TABLE I
Summary of scintillation properties for CsSr1−xEuxI3
	light yield	energy resolution	Scintillation decay
Composition	(ph/MeV)	at 662 keV	time (μs)
CsSr0.99Eu0.01I3	32000	9.0%	1.7
CsSr0.92Eu0.08I3	65000	5.9%	3.3
CsEuI3	24000	11.0%	3.4

III. Summary

Thus, Eu-activated iodide scintillator crystals with excellent scintillation properties have been produced according to the present disclosure. Because many embodiments of the invention can be made without departing from the spirit and scope of the invention, the invention resides in the claims hereinafter appended.

Claims

1. A scintillator material comprising a single crystal having a composition of the formula wherein:

AM1-xEuxI3,

A3M1-xEuxI5 or

AM2(1-x)Eu2xI5,

A consists essentially of any alkali metal element or any combination thereof,

M consists essentially of Sr, Ca, Ba or any combination thereof, and

0≦x≦1.

2. The scintillator material of claim 1, the single crystal having a composition of formula

ASr1-xEuxI3,

A3Sr1-xEuxI5 or

ASr2(1-x)Eu2xI5,

3. The scintillator material of claim 2, the single crystal having a composition of formula

CsSr1-xEuxI3,

Cs3Sr1-xEuxI5, or

CsSr2(1-x)Eu2xI5.

4. The scintillator material of claim 1, wherein x is less than, or equal to, about 0.1.

5. The scintillator material of claim 3, having a light output of at least about four times that of BGO when excited with a gamma-ray of 662 keV.

6. The scintillator material of claim 5, having a light output of at least about eight times that of BGO when excited with a gamma-ray of 662 keV.

7. The scintillator material of claim 6, having a light output of at least about twelve times that of BGO when excited with a gamma-ray of 662 keV.

8. A method of making a scintillator material, the method comprising: wherein: growing a single crystal from the synthesized compound.

synthesizing a compound having a composition of the formula AM1-xEuxI3, A3M1-xEuxI5 or AM2(1-x)Eu2xI5,

A consists essentially of any alkali metal element or any combination thereof,

M consists essentially of Sr, Ca, Ba or any combination thereof, and

0≦x≦1;

9. The method of claim 8, wherein the synthesizing step comprises synthesizing a compound having a formula of:

ASr1-xEuxI3,

A3Sr1-xEuxI5 or

ASr2(1-x)Eu2xI5,

10. The method of claim 8, wherein growing a single crystal comprises growing a single crystal from the synthesized compound using a Vertical Gradient Freeze method.

11. The method of claim 8, wherein the synthesizing step comprises heating a mixture of a plurality of iodides above their respective melting temperatures.

12. The method of claim 11, wherein the synthesizing step comprises heating a mixture of CsI, SrI2 and EuI2 above their respective melting temperatures.

13. A radiation detector, comprising:

a scintillator material of claim 1 adapted to generate photons in response to an impinging radiation; and

a photon detector optically coupled to the scintillator material, arranged to receive the photons generated by the scintillator material and adapted to generate an electrical signal indicative of the photon generation.

14. An imaging method, comprising:

using at least one radiation detector of claim 13 to receive radiation from a plurality of radiation sources distributed in an object to be imaged and generate a plurality of signals indicative of the received radiation; and

based on the plurality of signals, deriving a special distribution of an attribute of the object.