MULTI-COLOR ELECTRO-OPTIC DISPLAYS
An electro-optic display comprising at least two separate layers of electro-optic material, with one of these layers being capable of displaying at least one optical state which cannot be displayed by the other layer. The display is driven by a single set of electrodes between which both layers are sandwiched, the two layers being controllable at least partially independently of one another. Another form of the invention uses three different types of particles within a single electrophoretic layer, with the three types of particles being arranged to shutter independently of one another.
This application is a division of copending application Ser. No. 15/059,424, filed Mar. 3, 2016 (Publication No. 2016/0187758), which itself is a continuation of application Ser. No. 14/071,491, filed Nov. 4, 2013 (Publication No. 2014/0055841, now U.S. Pat. No. 9,341,916, issued May 17, 2016), which itself is a division of application Ser. No. 13/113,567, filed May 23, 2011 (now U.S. Pat. No. 8,576,476, issued Nov. 5, 2013), which claims benefit of application Ser. No. 61/347,063, filed May 21, 2010. The entire disclosure of the aforementioned applications is herein incorporated by reference.
BACKGROUND OF INVENTIONThe present invention relates to multi-color electro-optic media and to displays incorporating such media.
The term “electro-optic”, as applied to a material or a display, is used herein in its conventional meaning in the imaging art to refer to a material having first and second display states differing in at least one optical property, the material being changed from its first to its second display state by application of an electric field to the material. The optical property is typically color perceptible to the human eye.
The term “gray state” is used herein in its conventional meaning in the imaging art to refer to a state intermediate two extreme optical states of a pixel, and does not necessarily imply a black-white transition between these two extreme states. For example, several of the E Ink patents and published applications referred to below describe electrophoretic displays in which the extreme states are white and deep blue, so that an intermediate “gray state” would actually be pale blue. The terms “black” and “white” may be used hereinafter to refer to the two extreme optical states of a display, and should be understood as normally including extreme optical states which are not strictly black and white, for example the aforementioned white and dark blue states. The term “monochrome” may be used hereinafter to denote a drive scheme which only drives pixels to their two extreme optical states with no intervening gray states.
The terms “bistable” and “bistability” are used herein in their conventional meaning in the art to refer to displays comprising display elements having first and second display states differing in at least one optical property, and such that after any given element has been driven, by means of an addressing pulse of finite duration, to assume either its first or second display state, after the addressing pulse has terminated, that state will persist for at least several times, for example at least four times, the minimum duration of the addressing pulse required to change the state of the display element. It is shown in U.S. Pat. No. 7,170,670 that some particle-based electrophoretic displays capable of gray scale are stable not only in their extreme black and white states but also in their intermediate gray states, and the same is true of some other types of electro-optic displays. This type of display is properly called “multi-stable” rather than bistable, although for convenience the term “bistable” may be used herein to cover both bistable and multi-stable displays.
Several types of electro-optic displays are known. One type of electro-optic display is a rotating bichromal member type as described, for example, in U.S. Pat. Nos. 5,808,783; 5,777,782; 5,760,761; 6,054,071 6,055,091; 6,097,531; 6,128,124; 6,137,467; and 6,147,791 (although this type of display is often referred to as a “rotating bichromal ball” display, the term “rotating bichromal member” is preferred as more accurate since in some of the patents mentioned above the rotating members are not spherical). Such a display uses a large number of small bodies (typically spherical or cylindrical) which have two or more sections with differing optical characteristics, and an internal dipole. These bodies are suspended within liquid-filled vacuoles within a matrix, the vacuoles being filled with liquid so that the bodies are free to rotate. The appearance of the display is changed by applying an electric field thereto, thus rotating the bodies to various positions and varying which of the sections of the bodies is seen through a viewing surface. This type of electro-optic medium is typically bistable.
Another type of electro-optic display uses an electrochromic medium, for example an electrochromic medium in the form of a nanochromic film comprising an electrode formed at least in part from a semi-conducting metal oxide and a plurality of dye molecules capable of reversible color change attached to the electrode; see, for example O'Regan, B., et al., Nature 1991, 353, 737; and Wood, D., Information Display, 18(3), 24 (March 2002). See also Bach, U., et al., Adv. Mater., 2002, 14(11), 845. Nanochromic films of this type are also described, for example, in U.S. Pat. Nos. 6,301,038; 6,870,657; and 6,950,220. This type of medium is also typically bistable.
Another type of electro-optic display is an electro-wetting display developed by Philips and described in Hayes, R. A., et al., “Video-Speed Electronic Paper Based on Electrowetting”, Nature, 425, 383-385 (2003). It is shown in U.S. Pat. No. 7,420,549 that such electro-wetting displays can be made bistable.
Particle-based electrophoretic displays, in which a plurality of charged particles move through a fluid under the influence of an electric field, have been the subject of intense research and development for a number of years. Electrophoretic displays can have attributes of good brightness and contrast, wide viewing angles, state bistability, and low power consumption when compared with liquid crystal displays. Nevertheless, problems with the long-term image quality of these displays have prevented their widespread usage. For example, particles that make up electrophoretic displays tend to settle, resulting in inadequate service-life for these displays.
As noted above, electrophoretic media require the presence of a fluid. In most prior art electrophoretic media, this fluid is a liquid, but electrophoretic media can be produced using gaseous fluids; see, for example, Kitamura, T., et al., “Electrical toner movement for electronic paper-like display”, IDW Japan, 2001, Paper HCS1-1, and Yamaguchi, Y, et al., “Toner display using insulative particles charged triboelectrically”, IDW Japan, 2001, Paper AMD4-4). See also U.S. Pat. Nos. 7,321,459 and 7,236,291. Such gas-based electrophoretic media appear to be susceptible to the same types of problems due to particle settling as liquid-based electrophoretic media, when the media are used in an orientation which permits such settling, for example in a sign where the medium is disposed in a vertical plane. Indeed, particle settling appears to be a more serious problem in gas-based electrophoretic media than in liquid-based ones, since the lower viscosity of gaseous suspending fluids as compared with liquid ones allows more rapid settling of the electrophoretic particles.
Numerous patents and applications assigned to or in the names of the Massachusetts Institute of Technology (MIT) and E Ink Corporation describe various technologies used in encapsulated electrophoretic and other electro-optic media. Such encapsulated media comprise numerous small capsules, each of which itself comprises an internal phase containing electrophoretically-mobile particles in a fluid medium, and a capsule wall surrounding the internal phase. Typically, the capsules are themselves held within a polymeric binder to form a coherent layer positioned between two electrodes. The technologies described in the these patents and applications include:
(a) Electrophoretic particles, fluids and fluid additives; see for example U.S. Pat. Nos. 7,002,728; and 7,679,814;
(b) Capsules, binders and encapsulation processes; see for example U.S. Pat. Nos. 6,922,276 and; 7,411,719;
(c) Films and sub-assemblies containing electro-optic materials; see for example U.S. Pat. Nos. 6,982,178; and 7,839,564;
(d) Backplanes, adhesive layers and other auxiliary layers and methods used in displays; see for example U.S. Pat. Nos. 7,116,318; and 7,535,624;
(e) Color formation and color adjustment; see for example U.S. Pat. Nos. 6,017,584; 6,664,944; 6,864,875; 7,075,502; 7,167,155; 7,667,684; and 7,791,789; and U.S. Patent Applications Publication Nos. 2004/0263947; 2007/0109219; 2007/0223079; 2008/0023332; 2008/0043318; 2008/0048970; 2008/0211764; 2009/0004442; 2009/0225398; 2009/0237776; 2010/0103502; 2010/0156780; and 2010/0225995;
(f) Methods for driving displays; see for example U.S. Pat. Nos. 7,012,600; and 7,453,445;
(g) Applications of displays; see for example U.S. Pat. No. 7,312,784; and U.S. Patent Application Publication No. 2006/0279527.
Many of the aforementioned patents and applications recognize that the walls surrounding the discrete microcapsules in an encapsulated electrophoretic medium could be replaced by a continuous phase, thus producing a so-called polymer-dispersed electrophoretic display, in which the electrophoretic medium comprises a plurality of discrete droplets of an electrophoretic fluid and a continuous phase of a polymeric material, and that the discrete droplets of electrophoretic fluid within such a polymer-dispersed electrophoretic display may be regarded as capsules or microcapsules even though no discrete capsule membrane is associated with each individual droplet; see for example, U.S. Pat. No. 6,866,760. Accordingly, for purposes of the present application, such polymer-dispersed electrophoretic media are regarded as sub-species of encapsulated electrophoretic media.
A related type of electrophoretic display is a so-called “microcell electrophoretic display”. In a microcell electrophoretic display, the charged particles and the fluid are not encapsulated within microcapsules but instead are retained within a plurality of cavities formed within a carrier medium, typically a polymeric film. See, for example, U.S. Pat. Nos. 6,672,921 and 6,788,449, both assigned to Sipix Imaging, Inc. Hereinafter, the term “microcavity electrophoretic display” may be used to cover both encapsulated (including polymer-dispersed) and microcell electrophoretic displays.
Although electrophoretic media are often opaque (since, for example, in many electrophoretic media, the particles substantially block transmission of visible light through the display) and operate in a reflective mode, many electrophoretic displays can be made to operate in a so-called “shutter mode” in which one display state is substantially opaque and one is light-transmissive. See, for example, U.S. Pat. Nos. 5,872,552; 6,130,774; 6,144,361; 6,172,798; 6,271,823; 6,225,971; and 6,184,856. Dielectrophoretic displays, which are similar to electrophoretic displays but rely upon variations in electric field strength, can operate in a similar mode; see U.S. Pat. No. 4,418,346. Electrophoretic media operating in shutter mode may be useful in multi-layer structures for full color displays; in such structures, at least one layer adjacent the viewing surface of the display operates in shutter mode to expose or conceal a second layer more distant from the viewing surface.
As already indicated, an encapsulated or microcell electrophoretic display typically does not suffer from the clustering and settling failure mode of traditional electrophoretic devices and provides further advantages, such as the ability to print or coat the display on a wide variety of flexible and rigid substrates. (Use of the word “printing” is intended to include all forms of printing and coating, including, but without limitation: pre-metered coatings such as patch die coating, slot or extrusion coating, slide or cascade coating, curtain coating; roll coating such as knife over roll coating, forward and reverse roll coating; gravure coating; dip coating; spray coating; meniscus coating; spin coating; brush coating; air knife coating; silk screen printing processes; electrostatic printing processes; thermal printing processes; ink jet printing processes; electrophoretic deposition (See U.S. Pat. No. 7,339,715); and other similar techniques.) Thus, the resulting display can be flexible. Further, because the display medium can be printed (using a variety of methods), the display itself can be made inexpensively.
There is today an increasing demand for color in all displays. Users familiar with color televisions, color computer displays and color displays on cellular telephones and other portable electronic devices may regard monochrome display as lacking something in visual appeal even in applications such as electronic book readers, where the display aims to reproduce the look of a printed book, most of which are still printed in monochrome.
In conventional printing, full color images of high quality are formed by providing sub-images in each of three subtractive primary colors, typically cyan, magenta and yellow (“CMY”) (black may be included as a four primary in a “CMYK” system) that are overlaid (i.e., more than one color can be present at any point on the page) in such a way that light is filtered through each sub-image before being reflected back from the underlying white paper to the viewer. (Thus, a so-called “four color”, CMYK system is in reality a five-color system; the white color of the underlying paper is part of the color formation system, as is readily appreciated from the fact that this white color appears where no ink whatever is present.) In this arrangement of three or four overlaid sub-images, no area of the printed paper absorbs light unnecessarily, and thus an image of maximum brightness is obtained.
Prior art electrophoretic and similar electro-optic displays have typically relied upon the use of reflective (light-scattering) pigments. Since no substantial amount of light passes through a layer of such pigment, it is not possible to overlay sub-images of differing colors, and in a color display it is necessary to resort to “color area sharing” to render a palette of colors. For example, multiple different sub-regions of the display may be provided with electrophoretic media capable of displaying different colors, for example red, green and blue. (Note that since there is no overlaying of sub-images of different colors, this type of display typically uses additive primaries rather than subtractive primaries.) Alternatively, a monochrome medium can be used and a color filter array provided so that specific pixels can reflect specific primary colors. Either approach suffers, however, from the problem that only a fraction of the area of the display is available for reflection of each primary color, which adversely affects the brightness of the image available. Hence, to improve the brightness of a color reflective display, it is desirable to provide a display which can display any desired color at any pixel of the display, and thereby to maximize the amount of light reflected to a viewer.
Multilayer, stacked electro-optic displays using are known in the prior art. In such displays, ambient light passes through sub-images in each of the three subtractive primary colors, in a manner analogous to conventional color printing. U.S. Pat. No. 6,727,873 describes a stacked electrophoretic display in which three layers of switchable cells are placed over a reflective background. Similar displays are known in which pigments are moved laterally; see for example International Application Publication No. WO 2008/065605) or, pigments in microcavities are moved using a combination of vertical and lateral motion. For a review of such displays, see J. Heikenfeld, P., et al., Journal of the SID, 19(2), 2011, pp. 129-156. In these prior art displays, each pixel of each layer must be capable of being driven independently so as to concentrate or disperse the pigment particles on a pixel-by-pixel basis. This requires three separate pair of electrodes, each of which typically comprises an active matrix backplane having a matrix of thin-film transistors, and an opposed continuous counter-electrode. Two of the active matrix backplanes must be as transparent as possible, as must be each counter-electrode. This approach suffers from the severe disadvantages of the high cost of manufacturing such a complex arrangement of electrodes, and from the fact that in the present state of the art it is difficult to provide an adequately transparent backplane, especially as the white state of the display requires that light pass through several layers of such transparent electrodes; in practice, the light losses in the electrodes have a severe adverse effect on the brightness of the image produced by the display.
Those skilled in the imaging art know that it is necessary to provide independent addressing of each primary color in order to render a full-color image. This is illustrated graphically in
In one aspect, this invention provides a color display in which a single pair of electrodes are used to address independently more than one layer of electrophoretic or similar electro-optic material. Such a color display can provide independent, or at least partially independent addressing of more than one primary color using a single pair or single set of electrodes (for example, the single set of electrodes can be an active matrix backplane and a single continuous counter-electrode. At least one of the layers of electrophoretic or similar material may operate in shutter mode (as defined above).
Shutter mode electrophoretic displays can be used as light modulators. Light modulators represent a potentially important market for electro-optic media. As the energy performance of buildings and vehicles becomes increasingly important, electro-optic media can be used as coatings on windows (including skylights and sunroofs) to enable the proportion of incident radiation transmitted through the windows to be electronically controlled by varying the optical state of the electro-optic media. Effective implementation of such “variable-transmissivity” (“VT”) technology in buildings is expected to provide (1) reduction of unwanted heating effects during hot weather, thus reducing the amount of energy needed for cooling, the size of air conditioning plants, and peak electricity demand; (2) increased use of natural daylight, thus reducing energy used for lighting and peak electricity demand; and (3) increased occupant comfort by increasing both thermal and visual comfort. Even greater benefits would be expected to accrue in an automobile, where the ratio of glazed surface to enclosed volume is significantly larger than in a typical building. Specifically, effective implementation of VT technology in automobiles is expected to provide not only the aforementioned benefits but also (1) increased motoring safety, (2) reduced glare, (3) enhanced mirror performance (by using an electro-optic coating on the mirror), and (4) increased ability to use heads-up displays. Other potential applications of VT technology include privacy glass and glare-guards in electronic devices.
VT media capable of being used as VT windows have been demonstrated and are described in the patent literature; see, for example, U. S. Pat. No. 7,327,511; and U.S. Patent Applications Publication Nos. 2006/0038772; 2007/0146310; and 2008/0130092. However, there are certain remaining problems in such VT media. Firstly, it is difficult to achieve in the same medium acceptable levels of image stability (i.e., stable transmission) and haze. In practice, VT windows need high image stability of the order of several hours, since users do not wish to have their windows adjusting their transmission levels every few minutes. As discussed above (see the aforementioned U.S. Pat. No. 7,170,670), the image stability of electrophoretic media can be increased by dissolving or dispersing a high molecular weight polymer in the fluid in the fluid in which the electrophoretic particles (typically carbon black particles) are dispersed; the aforementioned 2007/0146310 recommends a polystyrene dispersed in a mixture of limonene and a partially hydrogenated terphenyl as a fluid for used in VT electrophoretic media. The effect of adding the polymer to the fluid is to increase the flocculation of the electrophoretic particles once the particles are aggregated together, and thus to increase the image stability. Unfortunately, the polymer also serves to increase particle flocculation even when the electrophoretic particles are intended to be dispersed throughout the fluid, and the resultant increase in particle aggregation and thus effective particle size, substantially increases the optical haze of the medium; the particle size of the aggregated particles is large enough to cause substantial scattering of visible light, even though the individual particles themselves are sufficiently small that they will cause little scattering. The light scattering responsible for haze depends upon both the particle size and the difference in refractive index between the electrophoretic particles and the surrounding fluid. To date, no black pigment has been identified which has a refractive index close enough to that of the fluids typically used in electrophoretic media (or close enough to that of the polymeric phase which typically surrounds the fluid, as discussed above) to reduce haze to an acceptable level, and no mechanism for increasing image stability to the degree considered desirable for commercial sale has been identified which does not increase haze to an undesirable level.
Another problem with prior art VT electrophoretic media (and similar electro-optic media such as electrochromic media) is their inability to vary hue; in other words, the colors capable of being displayed by such media fall on a line between their endpoint colors (a transparent state being regarded as a “color” for purposes of the present application), and the media do not have a color gamut volume. For example, the colors obtainable from the VT media described in the aforementioned U.S. Pat. No. 7,327,511; and U.S. Patent Applications Publication Nos. 2006/0038772; 2007/0146310; and 2008/0130092 vary from black to clear, while electrochromic media typically vary from blue-purple to clear. (Provision of color in VT media may be useful either in enabling the light within a room equipped with VT windows to be varied, or in enabling the use of VT as one layer in a multi-layer display, as discussed in detail below.) Neither type of media can produce additional colors without the addition of a color filter array, and the use of a multi-pixel drive method, typically using a passive or active matrix backplane. Such a backplane inevitably reduces optical transmission through the VT medium and is far more expensive than the simple electrode used in a single pixel VT display
Accordingly, there is still a need for a VT medium which can provide the high image stability desirable in commercial VT displays in combination with low haze. There is also still a need for VT media which can provide a substantial color gamut. In one aspect, the present invention seeks to provide solutions to both these problems.
SUMMARY OF INVENTIONIn one aspect, this invention provides an electro-optic display comprising at least first and second layers of electro-optic material, the first layer being capable of displaying at least one optical state which cannot be displayed by the second layer, the display further comprising a first electrode disposed on one side of the first and second layers, and a second electrode disposed on the opposed side of the first and second layers from the first electrode, there being no electrode between the first and second layers. (The term “electrode” is used herein in its conventional meaning in the electro-optic display art to mean a conductive material the electrical potential of which can be controlled by being connected to a source of known potential, including ground. Thus, for purposes of this application, a conductive material not arranged to be connected to any source of known potential is not an electrode.)
Such a display may further comprises a third layer of electro-optic material, the third layer being capable of displaying at least one optical state which cannot be displayed by the first and second layers, the second electrode being disposed on the opposed side of the first, second and third layers from the first electrode, there being no electrode between the second and third layers. The three layers of electro-optic material may comprise a set of subtractive primary colors, for example cyan, magenta and yellow pigments; it will readily be apparent that these colors may be distributed among the first, second and third layers in any order. (Alternatively, the displays of the present invention may use more than three primary colors, or use primary colors that are not the conventional subtractive primary colors.) The layer containing the yellow pigment may be arranged to have a smaller number of gray levels than the layers containing the cyan and magenta pigments. In one form of the invention, the electro-optic display has a viewing surface through which an observer views the display, and the two electro-optic layers closest to the viewing surface contain cyan and yellow pigments, in either order.
At least one layer of electro-optic material may comprise an electrophoretic material comprising a plurality of charged particles dispersed in a fluid and capable of moving through the fluid on application of an electrical field to the layer. Such an electrophoretic layer may be unencapsulated or may comprise a microcavity electrophoretic material. The charged particles in at least one of the layers (and preferably both the first and second layers) may be movable between a first optical state, in which the pigment particles occupy substantially the whole area of each pixel, and a second optical state, in which the pigment particles occupy only a minor proportion of the area of each pixel. When the first and second electro-optic layers (and the third electro-optic layer if present) are both electrophoretic layers, independent control of the pigments in these layers may be facilitated by controlling a variety of physical parameters of the two layers. For example, the yield stresses of the fluids in the first and second layers may differ; the sizes of the microcavities in the first and second layers may differ; the particles in the first and second layers may differ in at least one of size, shape and electrical conductivity; or the fluids in the first and second layers may differ in at least one of viscosity and electrical conductivity.
A preferred form of electro-optic display of the present invention has a viewing surface at or adjacent the surface of the first electro-optic layer remote from the second electro-optic layer, and has a third electro-optic layer on the opposed side of the second electro-optic layer from the viewing surface, the third electro-optic layer comprising first and second types of particles of differing colors disposed in a fluid and capable of moving through the fluid on application of an electric field to the third electro-optic layer, the first and second types of particles being of differing electrophoretic mobility. The first type of particles in the third electro-optic layer may be white. The particles in the first and second electro-optic layers may be yellow and cyan, in either order, and the second type of particles in the third electro-optic layer may be magenta.
At least one of the first and second electrodes in the electro-optic display of the present invention may occupy only a minor proportion of the area of a pixel. In a microcavity display of the present invention, the walls of the microcavity may have a higher electrically conductivity than the phase comprising the plurality of charged pigment particles dispersed in the fluid. One of the electro-optic layers may have at least two stable states, while a second electro-optic layer may have only one stable state.
In another aspect, this invention provides an electro-optic display comprising first and second layers of cavities disposed adjacent one another with no electrode between the first and second layers, the sections of each of first and second layers of cavities lying adjacent the other layer being of substantially pyramidal form tapering towards the other layer, at least one of the first and second layers comprising colored particles dispersed in a fluid and capable of moving through the fluid on application of an electric field to the display. In such a display, the first and second layers may be formed of deformable capsules. One of the first and second layers may be free from colored particles.
In another aspect, this invention provides an electro-optic display comprising at least first, second and third layers of electro-optic material, the display further comprising a first electrode disposed on one side of the first, second and third layers, and a second electrode disposed on the opposed side of the first, second and third layers from the first electrode, there being no electrode between the first and second layers, or between the second and third layers, the first, second and third layers having the following properties:
-
- (a) the first layer 1 has a voltage and/or impulse threshold, is state stable, and its color depends upon the polarity of the applied voltage;
- (b) the second layer has either a lower threshold than the first layer, is state stable, and its color depends upon the polarity of the applied voltage; and
- (c) the third layer has no threshold, is not state stable, switches faster than the second layer, and reaches the same state whether driven with a positive or a negative impulse and relaxes to its opposite extreme when no potential is applied.
Such a display may be driven by a method comprising:
-
- (a) applying a high voltage to set the first layer to the desired color;
- (b) applying a lower voltage than in step (a) to set the second layer to the desired color; and
- (c) allowing the third layer to relax to its desired color.
In another aspect, this invention provides a microcavity electrophoretic display comprising walls defining at least one cavity, the cavity containing a fluid and first, second and third types of particles dispersed in the fluid, each of the first, second and third types of particles having an unshuttered state, in which the particles occupy substantially the entire area of the microcavity, and a shuttered state, in which the particles occupy only a minor proportion of the areas of the microcavity, the first, second and third particles being of differing colors and differing in dielectrophoretic and/or electro-osmotic properties such that the first, second and third types of particles can be moved between their unshuttered and shuttered states independently of one another. In such a display, the colors of the first, second and third types of particles are such that when all three types of particles are in their unshuttered states the display appears substantially black. This aspect of the present invention is based upon the discovery of a range of colored organic pigments (i.e., having a color other than black) which provide image state stability without the need of a polymeric additive in the fluid of the electrophoretic medium. While the exact image state stability mechanism is not completely understood, it appears that these pigments themselves form loose aggregates when suspended in a fluid. This loose aggregate exhibits a yield stress: when the pigment dispersion is sufficiently concentrated, a gel is formed. With slight agitation, the gel is broken, resulting in a low viscosity fluid. Some of these pigments have refractive indices close to that of the preferred internal phase fluid and polymer phase surrounding the fluid, resulting in a low haze dispersion, even in the flocculated state. By appropriate blending of various colored pigments, a medium having a black optical state can be created.
Many such blends of organic pigments can also be made to display a substantial color gamut. By careful selection of the organic pigments used, the differently colored organic pigments present can be chosen to have substantial different dielectrophoretic mobilities, so that by manipulating the frequency and voltage applied to the electrophoretic medium, each pigment individually can be made to be in a dispersed state or in a packed state, i.e., the different organic pigments can be made to “shutter” independently of one another. Having a particular organic pigment in its dispersed state allows that pigment to absorb the corresponding color of transmitted light; the more uniform the dispersion, the greater the absorption. On the other hand, having a particular organic pigment in its packed state minimizes the fraction of the area of the electrophoretic medium where that pigment is located, thus minimizing the absorption by that pigment. It will readily be apparent by controlling the “shuttering” of differently colored particles independently of one another, a substantial color gamut can be displayed.
Such a multi-colored VT medium can be used directly as a full color display; if a reflective display is desired, a reflector can of course be placed behind the medium (i.e., on the opposed side of the medium from that viewed by the user). Alternatively, such a multi-colored VT medium can be used as a substitute for a conventional “static” color filter array, and used in combination with a monochrome reflective medium (either an inherently reflective medium or a transmissive medium provided with a reflector); this monochrome medium need not be an electrophoretic medium but could be any known type of electro-optic display. Such a dual layer display would have the advantage of allowing the multi-colored VT medium to control only the color of the various pixels or sub-pixels of the display, while the monochrome medium would control the brightly of each pixel or sub-pixel. Requiring the multi-colored VT medium to control only color lessens the demands upon independent control of the multiple pigments used in the VT medium, since no longer is the VT medium required to provide all colors at all levels of saturation.
The VT media of the present invention may be of any of the types of electrophoretic media discussed above. Thus, the VT media may be unencapsulated, encapsulated, microcell or polymer-dispersed media.
(2004) 509, 217-252, show in cross-section a spherical pigment particle surrounded by a solvent that contains a charge control agent, and illustrates the forces acting on the pigment particle in various types of applied electric fields.
As already mentioned, in one aspect this invention provides an electro-optic display comprising at least first and second layers of electrophoretic material, each of which comprises a plurality of charged particles dispersed in a fluid and capable of moving through the fluid on application of an electrical field to the layer. The first layer of electrophoretic material is capable of displaying at least one optical state which cannot be displayed by the second layer. The display further comprises a first electrode disposed on one side of the first and second layers, and a second electrode disposed on the opposed side of the first and second layers from the first electrode; no electrode is present between the first and second layers. Typically, the electrophoretic display will further comprise a third layer of electrophoretic material comprising a plurality of charged particles dispersed in a fluid and capable of moving through the fluid on application of an electrical field to the layer. The third layer is capable of displaying at least one optical state which cannot be displayed by the first and second layers. The second electrode is disposed on the opposed side of the first, second and third layers from the first electrode, and no electrode between the second and third layers, the single pair (or set) of electrodes being used to control all three layers at least partially independently of one another.
The basic concept behind the present invention is perhaps most easily appreciated by considering a three-layer display such as that shown in
The three electro-optic layers of the display are disposed between a single set of electrodes and an appropriate display controller is used to enable the three electro-optic layers to be driven at least partially independently of one another. In a preferred form of the display of the present invention in which the first and second electro-optic layers are shutter mode electrophoretic layers and the third electro-optic layer is a dual particle electrophoretic layer, the third layer can be driven using a direct current driving method, while the first and second layers are driven by different shuttering drive methods, as described in detail below.
Hereinafter for convenience, a material that selectively absorbs light is referred to as a “pigment”, which term should be interpreted to include dyes, photonic crystals, etc., capable of selectively absorbing light. In embodiments of the invention intended to provide full color imaging using three subtractive primary pigments, light will typically be selectively filtered through at least two pigments before being reflected back to the viewer. The third pigment may be transparent or reflective, as described in more detail below. It is therefore necessary for at least two of the pigments used in the present invention to be light-transmissive and not substantially back-scattering. Thus, for example, a magenta pigment is intended to absorb green light but must pass blue and red light to underlying layers. In regions where green light is not intended to be absorbed, it is necessary that the pigment not be present in the optical path. One way in which such removal of the pigment from the optical path may be achieved is to concentrate the pigment in only a (minor) portion of the pixel area, thus reducing its covering power. When magenta color is desired, the pigment is spread over the whole pixel area to enable the maximum amount of light to be absorbed. The process of spatially concentrating the pigment to reduce its areal covering power is referred to as “shuttering” the pigment.
Numerous methods can be used for shuttering pigments in response to an applied electric field, as described in detail below. As already mentioned, the displays of the present invention may make use of electro-optic layer formed from microcapsules, which may be coated in roll-to-roll processes. Alternatively, the electro-optic layers may use microcells, microcups or wells such as are known in the art. Although the invention will hereinafter primarily be described with regard to electro-optic layers using microcapsules, it is believed that those skilled in the technology of electro-optic displays will have no difficulty adapting the microcapsule based structures described to other methods for spatially segregating the pigment containing phases.
As already indicated, the present invention is directed to electro-optic displays in which multiple pigments are controlled by a single set of electrodes. Since the electric fields present between a single set of electrodes are substantially the same regardless of whether one or a plurality of electro-optic layers are present between those electrodes, it will be appreciated that the reaction of various pigments to the electric fields generated the single set of electrodes will in most cases be substantially the same regardless of whether the pigments are present between the electrodes in the same or different electro-optic layers. Accordingly, various embodiments of the present invention can be produced depending upon whether various pigments are present in the same or different electro-optic layers. Although the present invention will primarily be described with reference to embodiments of the invention in which each electro-optic layer (except one) contains only a single pigment, depending upon the exact driving methods used, all the pigments used may be contained in a single layer, or two pigments may be contained in one layer and a third in a different layer, and the means used to shutter the pigments may differ in different layers. A description is given below of one display of the present invention in which three pigments are present in a single layer of capsules.
Certain “geometric” methods for shuttering pigments rely, in some cases, upon the self-assembly of coated layers of microcapsules. Hence, a preliminary discussion of such coated layers is desirable. As discussed in many of the aforementioned E Ink patents and applications, and especially in U.S. Pat. Nos. 6,067,185; 6,392,785; 7,109,968; and 7,391,555, in practice prepared by forming an emulsion in which the discontinuous phase comprises droplets of an electrophoretic internal phase that comprises at least one pigment and a fluid (which is typically a low polarity, substantially water-immiscible hydrocarbon), normally with the addition of a charge control agent. The continuous phase of the emulsion comprises an aqueous solution of a polymer, typically gelatin. Polymeric material is deposited onto the surface of the droplets by, for example, formation of a coacervate of the gelatin and a second polymer, typically acacia, to form a thin capsule wall that may optionally be cross-linked, for example with an aldehyde. The resultant deformable microcapsules are spheres of approximately 20-100 μm in diameter. When such microcapsules are coated on a flat surface at a controlled coverage, they form essentially a monolayer of capsules. When this monolayer is dried, the capsules tend to contract vertically (i.e., perpendicular to the surface on which they are coated) and expand laterally to form oblate spheroids. Eventually, as the capsules expand laterally, their sidewalls come into contact with each other, and the capsules deform into polyhedral prisms whose shapes are similar to those formed by cells in foams. Ideally, a single layer of capsules will form a “honeycomb” (a two dimensional hexagonal lattice) of hexagonal prisms whose side walls, viewed in projection, meet at 120 degree angles, as shown (in idealized form) in
When a second layer of microcapsules is coated on top of the first layer, surface tension forces leading to minimization of surface energy tend to cause deformation of the domed upper surfaces of the capsules in the first layer into a foam-like geometry as illustrated schematically in
Concentrator electrodes may be patterned electrodes by which the display is addressed, for example grids of conductive material such as silver or gold that may be patterned onto a substrate by printing or lithographic methods, or continuous conductors that are masked with patterns of dielectric material. Concentrator electrodes may also be individually-addressable electrodes that are associated with an array of thin-film transistors. Alternatively, discrete, isolated conductive particles that are not directly electrically-addressed may be incorporated into a layer or layers within the display.
Geometrical/capsule wall shuttering can be achieved naturally by the use of more than one layer of capsules whose wall materials are more electrically conductive than their internal phase. For example, a gelatin capsule wall typically has a conductivity on the order of 10−7 S/m (although this value is strongly dependent upon the degree of hydration of the polymeric material comprising the capsule wall). An electrophoretic internal phase typically has a conductivity much less that this, on the order of 10−8 S/m. Thus, the capsule wall of one layer of capsules can act as a concentrator “electrode” for a second layer of capsules. In addition, a geometrical shutter may be provided by the pyramidal shape that may be adopted by the capsule, as described above. If needed, geometrical shutters may be achieved by templated coating of capsules into, for example, V-shaped grooves as described in U.S. Pat. Nos. 6,130,774 and 6,172,798. Geometrical shutters may also be fabricated using photolithographic or embossing methods, or other methods that are well-known in the art.
Other methods for shuttering, such as use of anisotropic particles, for example, needles or plates that may be oriented with their principal axes either perpendicular or parallel to the plane of the display, or color-changing pigments, or swelling and deswelling of gels, or other similar methods that are known in the art, may also be used in the displays of the present invention.
As will readily been seen from the discussion of
The displays of the present invention obviously require some method for dispersing the pigment from its shuttered state to its unshuttered state, in which the pigment occupies substantially the entire area of a pixel. One method for such pigment dispersion that is especially preferred for use in conjunction with concentrator electrode or geometrical/capsule wall shuttering is illustrated schematically in
The present invention is not confined to use of a mobile charged pigment with a capsule wall bearing a charge of the opposite polarity but extends to the use of such a pigment with any fixed surface bearing a charge of the opposite polarity. The fixed surface acts to constrain the motion of the pigment in an applied field. The medium containing the pigment and the surface need not be encapsulated.
The shuttering mechanisms described above may be combined with conventional switching of pigments using DC addressing to give rise to particle motion within a capsule parallel to the applied field as already mentioned with regard to
Shuttering methods of all types tend to impose limitations on the volume fraction of pigments particles which can be present in an electrophoretic medium. It is desirable that at least about 85 per cent of light be transmitted through a layer of shuttered pigment in a single pass, i.e., the pigment should not absorb more than about 15 per cent of the light; this corresponds to a reflection efficiency of about 70 per cent for a double pass through the shuttered layer such as will normally occur in the displays of the present invention.
Such volume fraction limitations for shuttered pigments also imposes constraints on the preferred particle size of such pigments. Particles that are randomly arranged on a surface cover that surface less efficiently than an ordered, close-packed monolayer, such that approximately two monolayer-equivalents of particles are required for an area coverage of 90 per cent. In addition, for a typical dye having an extinction coefficient of 50,000 L/mole/cm, a specific gravity of 1.5 and a molecular weight of 500, a perfectly-packed layer of 70 nm thickness is required for an optical density of 1 (i.e., 90 per cent absorption of light). It is therefore preferred that for such a dye, the diameter of the pigment particle be on the order of half this thickness or less. In practice, pigment particle sizes of less than about 100 nm diameter are preferred for concentrator electrode and geometrical/capsule wall shuttering. Larger particles may be hidden using side-wall shuttering since this method permits a larger loading of pigment for the same degree of shuttering, as described above.
Additional optical losses may occur if the positions at which the pigments are shuttered in separate layers do not overlie one another (i.e., are not registered, as would be the case when the pigments are located in different layers in a display having multiple layers of capsules). If the absorption spectra of the pigments overlap, some light of a wavelength absorbed by both pigments may be absorbed in one area of a pixel by a first shuttered pigment in a first layer and in another area of the same pixel by a second shuttered pigment in a second layer. This problem can be avoided by removing spectral overlap in the shuttering pigments so that there is no wavelength absorbed by two pigments. Thus, in a display when two pigments are shuttered and a third is switched by conventional electrophoresis, it is preferred that the two shuttered pigments be yellow and cyan (whose absorption spectra are both designed to pass green light, and which therefore do not significantly overlap).
As mentioned above, AC addressing may be used to shutter pigments. A rich variety of phenomena occur when AC addressing is employed, including induced-charge electro-osmosis and electrophoresis and induced-dipole effects such as dielectrophoresis and particle chaining. Which behavior occurs is affected by the field strength and frequency applied and by properties of the components in the capsule internal phase, as will now be described in more detail.
It is thought that a particle with immobilized charge on its surface sets up an electrical double layer of opposite charge in the surrounding fluid. Ionic head groups of the CCA may be ion-paired with charged groups on the particle surface, forming a Stern layer of immobilized charged species. Outside this layer is a diffuse layer comprising charged micellar aggregates of CCA. In conventional DC electrophoresis an applied electric field exerts a force on the fixed surface charges and an opposite force on the mobile counter-charges, such that slippage occurs within the diffuse layer and the particle moves relative to the fluid. The electric potential at the slip plane is known as the zeta potential.
Induced-charge electro-osmosis (hereinafter abbreviated “ICEO”, but known as “AC electro-osmosis”) is a similar phenomenon but occurs in response to induced charge rather than fixed surface charges. It is described in V. A. Murtsovkin, Colloid J., 58, 341-349 (1996) and in a series of papers by H. Morgan and co-workers (see, for example, J. Colloid Interface Sci., 217, 420-422 (1999) and Phys. Rev. E, 61, 4011-4018 (2000)), and has more recently been reviewed in detail by Squires and Bazant (J. Fluid Mech., 509, 217-252 (2004). In ICEO, an externally applied electrical field induces a polarization in the vicinity of a surface and simultaneously drives the resulting electro-osmotic flow. This creates a flow velocity that is nonlinear in the applied field strength. In the presence of an applied electric field an induced dipole may be set up (see
Bazant has estimated the charging time for establishment of the double layer (
τc=λDa/D (1)
for a conductive cylinder in an electric field, where λD is the Debye length, a is the particle radius, and D the diffusion constant of the charge carrier in the mobile phase. Although pigment particles are typically composed of dielectric materials, electrical conduction within the Stern layer may occur through a number of known mechanisms, including proton hopping (particularly in the presence of adsorbed water) and therefore the assumption of conductivity is not unreasonable in the present context. The following discussion is included in order to provide a qualitative, heuristic picture of some of the mechanisms that may occur in the present displays and does not in any way limit the scope of the invention.
Equation (1) above shows that the charging time gets longer as the particle gets larger. The maximum induced-charge electro-osmotic velocity is then estimated as:
Umax=εE2a/η(1+ω2τc2) (2)
where E is the magnitude of the applied field, ω the angular frequency and η the viscosity of the mobile phase. It can be seen that as the frequency increases the maximum induced-charge electro-osmotic velocity decreases. At high frequencies, where ω2τc2»1ω2τc2»1, the induced-charge electro-osmotic velocity becomes very low (because there is no time to charge up the double layer) and screening of the induced dipole by the charge carriers in the fluid is reduced. At such frequencies particle-particle interactions leading to chaining, or interactions with field gradients leading to dielectrophoretic mobility, may occur. Thus, applying an AC field with increasing frequency may at low frequencies cause electro-osmotic flow, as described above, but as the frequency is increased particle-particle interactions and dielectrophoresis may dominate. The result may be, for example, that all the particles concentrate by induced-dipole aggregation. They are most likely to concentrate in regions where, at the electro-osmotic driving frequency, stationary points of the flow may be located (i.e., in a ring around the equator in the case of particles within a spherical capsule). The frequency at which particle concentration occurs (in the idealized case) is proportional to the applied field and also depends inversely upon the particle size, since:
Umax=εE2D/ηaω2λD2 (3)
The present inventors have observed that when a display is addressed at relatively low AC frequencies (typically in the range of 30-100 Hz) encapsulated pigment particles exhibit high-speed motion and become uniformly distributed in a capsule. At higher frequencies the pigment particles' motion slows down and they may collect at the capsule walls, leading to transparency (shuttering). If the frequency is suddenly increased from a relatively low to a relatively high value, however, there may not be time for the particles to reach the stationary points of flow at the wall, and they will become immobilized but not shuttered. Thus, for optimal shuttering it is preferred that either the frequency be ramped from a low to a high value at constant voltage, or that the voltage be ramped from a high to a low value at constant frequency, or some combination of these two ramps.
The frequency at which the transition from ICE) motion to a stationary state occurs is related to (and in some cases proportional to) the applied voltage and depends upon particle properties such as size, shape and conductivity and to fluid properties such as viscosity, conductivity and dielectric constant. Thus, pigments may be selectively and independently addressed by varying the frequency of AC used to drive a display. For example, a first pigment in a first capsule may have a large size and be incorporated into a fluid of high viscosity, whereas a second pigment in a second capsule layer may have a small size and be incorporated into a fluid of low viscosity. At a lowest addressing frequency ω1, both pigments will be distributed and spread out by electro-osmotic motion. At a higher addressing frequency ω2 the first pigment may be shuttered while the second pigment is still in motion. At a yet higher frequency 0)3 both pigments may be shuttered. If the frequency is suddenly switched from ω1 to ω3 (or to a frequency slightly lower than □ ω3 and then increased to ω3) there may not be time for the first pigment to shutter but there may be time for the second pigment to do so. Thus, using a constant voltage and varying only the frequency of addressing, it is possible to access different colors while driving each color with the same waveform. It will be clear that the same effect may be obtained by holding the frequency constant and varying the voltage, and that such a scheme may be extended to more than two colors. Examples 1-3 below describe addressing more than one color in a single capsule layer using alternating voltages of different frequencies. (It will of course be apparent that, when the frequency at which the transition from ICEO motion to a stationary state occurs for different particles is controlled by particle properties alone it is possible to incorporate particles of more than one color into a common capsule rather than providing a separate environment for each pigment, as described above.)
Another method for using shuttering a plurality of pigments while driving all pigments with a common waveform is illustrated in
the necessary independent control of the two capsule layers in
The necessary voltage thresholds may be provided in a variety of ways. As mentioned above, the internal phase of a microcapsule may have a yield stress. Particles of opposite charge to the shuttering pigment may be added to the capsule to create a Coulombic threshold. These particles of opposite charge may be substantially non-scattering and non-absorbing, such that they do not affect the absorption of light by the colored pigment and do not affect the overall appearance of the display, being incorporated simply to modulate the switching behavior of the interior of the capsule.
Another technique to address capsule layers independently is to make one layer of capsules multi-stable (i.e., to endow this layer with image hysteresis, as may be achieved by providing a polymer dispersed in the fluid—see U.S. Pat. No. 7,170,670, and to make a second layer that does not exhibit hysteresis and reverts to a default state when not actively addressed.
A larger color gamut may be achieved if the rates of switching of the two layers are not the same.
A third primary color may be provided in the displays shown in
As already indicated, in one aspect the present invention provides a variable transmission electrophoretic medium comprising a plurality of different organic pigments in a fluid, such that when all the pigments are dispersed substantially uniformly through the fluid, the medium appears substantially black. Also, the medium is substantially free from polymeric additives in the fluid (other than charge control or similar agents, and surfactants) but still has a high degree of image stability. In a preferred form of such a variable transmission medium, the pigments are chosen to have substantial different dielectrophoretic mobilities, so that by manipulating the frequency and voltage applied to the electrophoretic medium, each pigment individually can be made to be in a dispersed state or in a packed state, and the medium can display a substantial color gamut.
As is well known to those skilled in the pigment art, a blend of two or more color pigments can be made to provide additional colors, including black. A broad range of color pigments has been developed for demanding applications such as automotive paints, and some of these pigments have demonstrated suitable properties for VT media. Pigments of the quinacridone and phthalocyanine families have been found useful. Such pigments can be blended to yield in total a very broad color gamut, but the added constraint of requiring black to be part of the gamut has hitherto diminished the color gamut achievable in a single medium.
Somewhat unexpectedly, it has been found that that some of the pigments useful in VT media have been found to display a wide range of electrophoretic mobilities in the sense of differing responses to a wide range of applied frequencies and voltages. Accordingly, by manipulating the frequency and voltage applied to the electrophoretic medium, each pigment individually can be made to be in a dispersed state or in a packed state, i.e., the different organic pigments can be made to “shutter” independently of one another. The dispersed state allows the pigment to absorb the transmitted light, the more uniform the dispersion, the better the absorption. The packed state minimizes the areal fraction of the medium where the pigment is located, thereby minimizing the absorption by that pigment. If all the pigments are packed, then the medium will assume its “open” or substantially transparent optical state. If, on the other hand, all the pigments are dispersed throughout the fluid, the medium will assume a substantially black optical state, provided with amounts and colors of the various pigments are balanced to achieve a neutral color.
If at least one pigment is dispersed and at least one pigment is packed, the color of the medium will approach the color of the dispersed pigment, and by independent control of the state of dispersion of the various pigments, a substantial gamut of colors can be produced; for reasons which will be familiar to those skilled in the color imaging art, it is normally preferred that such a VT medium contain at least three different pigments having differing colors and dielectrophoretic mobilities.
The displays of the present invention can, as already discussed, make use of various driving methods to drive three separate pigments (whether those pigments be present in one, two or three separate electro-optic layers). Perhaps surprisingly, it is possible to drive three separate pigments substantially independently of one another using only a single set of electrodes and DC voltages. Conceptually, the methods for driving three different pigments using only DC and a single set of electrodes, may be summarized as follows:
Assume that there are three color-forming layers (although the principle does not require layers) with the following properties:
-
- (a) Layer 1 has a voltage (or impulse) threshold, is state stable, and its color depends upon the polarity of the applied voltage;
- (b) Layer 2 has either a lower threshold or no threshold, is state stable, and its color depends upon the polarity of the applied voltage; and
- (c) Layer 3 has no threshold, is not state stable, and switches faster than layer 2. Layer 3 reaches the same state whether driven with a positive or a negative impulse and relaxes to its opposite extreme when no potential is applied.
Given these three conditions, the drive scheme is:
-
- (a) Use a high voltage to set layer 1 to the desired color. In practice, this could be binary and in this case should be yellow. This will also affect layers 2 and 3.
- (b) Use a lower voltage to set layer 2 to the desired color. This will not affect layer 1, and will switch layer 3 to its extreme state.
- (c) Allow layer 3 to relax to its desired color and keep it there with a holding voltage (or pulses at any voltage).
The alternative to this, if all three layers are state stable, is the more straightforward scheme of addressing sequentially at three different voltages for the three colors and correcting the collateral switching of the faster layers when addressing the slower ones. In this case the slowest layer is addressed first, and layers 1 and 2 each have a threshold. However, this is much harder to engineer.
The following Examples are now given, though by way of illustration only, to show details of preferred reagents, conditions and techniques used in the media of the present invention.
EXAMPLE 1 First Medium Containing Red, Green and Blue PigmentsThe pigments used in this Example were:
-
- Clariant Hostaperm Pink E 02, a red quinacridone pigment (available commercially from Clariant Corporation, 4000 Monroe Road, Charlotte N.C. 28205), stated by the manufacturer to have a specific gravity of 1.45, a surface area of 77 m2/g, and an average particle size of 90 nm;
- Clariant Hostaperm Green GNX, a green copper phthalocyanine pigment from the same manufacturer, and stated by the manufacturer to have a specific gravity of 2.05, a surface area of 40 m2/g, and an average particle size of 50 nm; and
- Clariant Hostaperm Blue B2G-D, a blue copper phthalocyanine pigment from the same manufacturer, and stated by the manufacturer to have a specific gravity of 1.6, a surface area of 44 m2/g, and an average particle size of 75 nm.
Millbases of each pigment containing approximately 20 per cent by weight of the pigment in d-limonene and 0.0044 g of Solsperse 17000 per square meter of pigment surface area (as stated by the manufacturer) were prepared substantially as described in the aforementioned 2007/0146310. Samples of each millbase were diluted to 0.01 weight per cent pigment with d-limonene and the resultant dispersion measured for color transmission with a Minolta CM-3600d spectrometer using 2 mm path length sample cuvettes. The millbases were also blended to produce a mixed dispersion having a color as close to black as possible (i.e., having the smallest possible a* and b* values in the conventional CIE L*a*b* color space). The results are shown in Table 1 below.
Note that the “black” blend actually tended to green even without adding any green pigment; this was caused by the blue-green hue of the “blue” pigment.
Example 1 was repeated except that Clariant Ink Jet Magenta E02 VP 2621, a quinacridone pigment having an average particle size of 70 nm, was substituted for the pink pigment used in Example 1. Again, the millbases were also blended to produce a mixed dispersion having a color as close to black as possible. The results are shown in Table 2 below.
Again, the blended “black” tended to green, and since a suitable alternative blue pigment could not be located, it was determined that a major change in the pigment set was necessary.
Example 1 was repeated except that the pink and blue pigments were replaced with Clariant Hostaperm Violet RL02 and Clariant Novoperm Yellow 4G VP2532 from the same manufacturer. The former is a dioxazine pigment stated by the manufacturer to have a specific gravity of 1.49, a surface area of 80 m2/g, and an average particle size of 50 nm, while the latter is a disazo pigment stated by the manufacturer to have a specific gravity of 1.44, a surface area of 33 m2/g, and an average particle size of 162 nm. Again, the millbases were also blended to produce a mixed dispersion having a color as close to black as possible. The results are shown in Table 3 below.
As may be seen from Table 3, the blend of this set of pigments produces a good, neutral black.
A polymer-dispersed electrophoretic medium was produced using this black blend in substantially the same manner as described in Example 1 of U.S. Pat. No. 6,866,760; the polymer-dispersed medium was coated on the indium-tin-oxide (ITO) coated surface of a polyethylene terephthalate/ITO film, dried, and adhesive layer applied, and the resultant film laminated to a rear electrode to produce an experimental single-pixel display, which were then driven at various combinations of drive voltages and frequencies.
In such a multi-pigment display, if all the pigments are packed, the display appears open (substantially transparent); if all the pigments are dispersed the display appears closed (substantially black). When the fractions of each pigment in its dispersed form is different from the overall proportion of that pigment in the display (i.e., different from the 57.8% green, 22.9% violet, 19.3% yellow shown in Table 3), then the display color approaches the color of the more dispersed pigment. For example, if the yellow pigment is well dispersed, and the green and purple pigments are packed, the display will appear yellow. Alternatively, if the yellow and green pigments are dispersed and only the purple is packed, the display will appear yellow-green. Table 4 below gives examples of applied waveforms and the corresponding colors produced.
The above colors, and others produced using different waveforms, are plotted in the a*b* plane in
It will be seem from the Figure that the experimental display was capable of displaying a substantial color gamut, though only in the green/yellow/blue portion of the a*b* plane; this particular display was not capable of producing a positive a* (i.e., a red color). However, in view of the substantial color gamut capable of being displayed by this experimental display, and the wide range of pigments commercially available and suitable for incorporation in such a display it can be anticipated that evaluation of additional pigments and further work in formulation will produce displays have a broader color gamut more centered in the a*b* plane.
EXAMPLE 4 Coating Slurry for Cyan Shuttering CapsulesA cyan pigment, Irgalite Blue GLVO (available from BASF, Ludwigshafen, Germany) (8 g) was combined with Isopar E (12 g) and a solution of Solsperse 17000 (available from Lubrizol Corporation, Wickliffe, OH, 20 g of a 20% w/w solution in Isopar E) and the mixture was dispersed by stirring with beads to afford a cyan pigment dispersion.
The cyan pigment dispersion thus prepared (5.75 g) was combined with Isopar E (109.25 g) and the resultant mixture mechanically rolled overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated following the procedure described in U.S. Pat. No. 7,002,728. The resultant encapsulated material was isolated by sedimentation, washed with deionized water, and size separated by sieving, using sieves of 45 and 20 μm mesh. Analysis using a Coulter Multisizer showed that the resulting capsules had a mean size of 40 μm and more than 85 percent of the total capsule volume was in capsules having the desired size of between 20 and 60 μm.
The resulting capsule slurry was adjusted to pH 9 and excess water removed. The capsules were then concentrated and the supernatant liquid discarded. The capsules were mixed with an aqueous polyurethane binder (prepared in a manner similar to that described in U. S. Patent Application No. 2005/0124751) and small amounts of Triton X-100 surfactant and hydroxypropylmethyl cellulose were added and mixed thoroughly to provide a slurry ready for use in a display, as described in detail below.
EXAMPLE 5 Coating Slurry for Cyan Shuttering Capsules Containing 1% w/w of PigmentIrgalite Blue GLVO (26 g) was combined with Isopar E (70 g) and a solution of Solsperse 17000 (70 g of a 20% w/w solution in Isopar E) and the mixture was dispersed in an attritor with glass beads to produce a cyan pigment dispersion. The cyan pigment dispersion thus prepared (5.75 g) was combined with Isopar E (109.25 g). The resultant mixture was mechanically rolled overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated following the procedure of Example 4 above to produce capsules having a mean size of 40 μm and with more than 85 percent of the total capsule volume in capsules having the desired size of between 20 and 60 μm. The capsules were then incorporated into a coating slurry in the same way as in Example 4 above.
EXAMPLE 6 Coating Slurry for Magenta Shuttering CapsulesA magenta pigment, Quindo Red 19 (available from Sun Chemical Corporation, Parsippany, N.Y.) was provided with a poly(lauryl methacrylate) coating substantially as described in U.S. Pat. No. 7,002,728. The coated pigment (13 g) was then combined with Isopar E (30 g) to produce a magenta pigment dispersion, which was filtered through a 200 μm mesh film and the per cent solids determined to be 17%.
The magenta pigment dispersion thus prepared (13 g) was combined with Isopar E (88 g) and Solsperse 17000 (8 g of a 20% w/w solution in Isopar E), and the resultant mixture was rolled mechanically overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated as described in Example 4 above to produce capsules having a mean size of 40 μm and with more than 85 percent of the total capsule volume in capsules having the desired size of between 20 and 60 μm. The capsules were then incorporated into a coating slurry in the same way as in Example 4 above.
EXAMPLE 7 Coating Slurry for Magenta/White Vertically Switching CapsulesFunctionalized magenta pigment (10 g, prepared as described in Example 6 above) was combined with Isopar E (40 g) and the resultant mixture dispersed by stirring with beads to produce a magenta pigment dispersion, which was filtered through a 200 μm mesh film and the percent solid determined. This dispersion (18.82 g) was combined with titanium dioxide (R794 available from E. I. du Pont de Nemours Corporation, Wilmington, Del.) (70.57 g of a 60% w/w dispersion treated as described in U.S. Pat. No. 7,002,728), minor amounts of Solsperse 17000 and poly(isobutylene) of molecular weight 600,000, and additional amounts of Isopar E. The resultant mixture was rolled mechanically overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated as described in Example 4 above to produce capsules having a mean size of 40 μm and with more than 85 percent of the total capsule volume in capsules having the desired size of between 20 and 60 μm. The capsules were then incorporated into a coating slurry in the same way as in Example 4 above.
EXAMPLE 8 Coating Slurry for Yellow/White Vertically Switching CapsulesA yellow pigment, Paliotan Yellow L 1145 (available from BASF), was surface-treated with N-[3-(trimethoxysilyl)propyl]-N′-(4-vinylbenzyl)ethylenediamine hydrochloride, followed by provision of a poly(lauryl methacrylate) coating substantially as described in U.S. Pat. No. 7,002,728. This yellow pigment (30 g) was combined with Isopar E (70 g) and sonicated for 2 hours and mechanically rolled overnight. The resultant dispersion (45.6 g) was then combined with the same R794 titanium dioxide as in Example 7 (102.6 g of a 60% w/w dispersion) minor amounts of Solsperse 17000 and poly(isobutylene) of molecular weight 850,000, and additional amounts of Isopar E. The resultant mixture was rolled mechanically overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated as described in Example 4 above to produce capsules having a mean size of 40 μm and with more than 85 percent of the total capsule volume in capsules having the desired size of between 20 and 60 μm. The capsules were then incorporated into a coating slurry in the same way as in Example 4 above.
EXAMPLE 9 Coating Slurry for Capsules Containing No Pigmentsolution of Solsperse 17000 in Isopar E) was rolled mechanically overnight to produce an internal phase ready for encapsulation. The internal phase so prepared was then encapsulated as described in Example 4 above to produce capsules having a mean size of 40 μm and with more than 85 percent of the total capsule volume in capsules having the desired size of between 20 and 60 μm. The capsules were then incorporated into a coating slurry in the same way as in Example 4 above.
EXAMPLE 10 Assembly and Switching of a Cyan/Yellow Bichrome DisplayThe cyan shuttering capsule slurry prepared in Example 4 above was coated on to a 125 μm poly(ethylene terephthalate) (PET) film bearing a printed hexagonal grid metallic electrode of 50 μm pitch and 1 μm line width using a bar coater with a 50 μm gap. The coating was dried at 60° C., following which a second coating of capsules was applied using the yellow/white vertical switching capsule slurry prepared as described in Example 8 above, with a bar coater gap of 100 μm. The second coating layer was dried at 60° C. A layer of polyurethane adhesive doped with a tetraalkylammonium salt, pre-coated onto a release sheet, was laminated on top of the second layer of capsules as described in U.S. Pat. No. 7,002,728. The release sheet was removed and the resultant multilayer structure was laminated onto a graphite rear electrode. As finally assembled the display structure comprised, in order from its viewing surface, a first layer of PET film base, a second layer of patterned electrode, a third layer of cyan shuttering capsules, a fourth layer of yellow/white vertically switching capsules, a fifth layer of a conductively doped lamination adhesive, and a sixth layer comprising a graphite rear electrode.
The display structure so produced was driven by applying a square wave AC signal at 30 Hz and +/−10 V that was offset by DC voltages that ranged from 40 V to −40 V. As the display was driven it was illuminated by a tungsten ring-light source and light reflected from the display was analyzed spectrophotometrically, giving the L*a*b* values shown in Table 5 below.
These results are shown graphically in
This display operates as shown in
The vertically-switching capsules (i.e., capsules in which the particles move parallel to the applied electric field) in the second capsule layer contain a positively-charged yellow pigment and a negatively-charged white pigment, and thus when the top-plane is negatively charged this layer of capsules displays a yellow image (positive b*) and when the top-plane is positively charged a white image (negative b* because of the blue component in the overlying cyan layer).
The a*/b* plot shown in
The display produced in this Example has the structure shown in
The pigment-less capsule slurry prepared in Example 9 above was coated on to a PET film having a transparent, conductive coating of indium tin oxide (ITO) and dried using the same conditions as the first layer of capsules in Example 10 above. A second coating of capsules was applied using the cyan shuttering capsule slurry prepared in Example 5, above, with a bar coater gap of 80 μm, and the coating was dried at 60° C. A third coating of capsules was applied using the magenta/white vertical switching capsule slurry prepared in Example 7 above using a bar coater gap of 100 μm to form a third capsule layer, which was dried at 60° C. An adhesive layer was laminated on top of the third layer of capsules in the same manner as in Example 10 above. The release sheet was removed and the resultant multilayer structure was laminated onto a graphite rear electrode. As finally assembled the display structure comprised, in order from its viewing surface, a first layer of PET film base, a second layer of an unpatterned, continuous transparent electrode, a third layer of pigment-less capsules, a fourth layer of cyan shuttering capsules, a fifth layer of magenta/white vertically switching capsules, a sixth layer of adhesive, and a seventh layer comprising the graphite rear electrode.
The display structure so produced was driven by applying a square wave AC signal at 30 Hz and +/−10 V that was offset by DC voltages that ranged from 40 V to −40 V. As the display was driven it was illuminated by a tungsten ring-light source and light reflected from the display was analyzed spectrophotometrically, giving the L*a*b* values shown in Table 6 below.
These results are shown graphically in
The display operates as follows. The second layer of capsules, in contact with the pigment-less capsules on one side and with the third layer of capsules on the other, contains a positively-charged cyan pigment and shutters as shown conceptually in
The vertically-switching capsules contain a positively-charged magenta pigment and a negatively-charged white pigment, and thus when the top plane is negatively charged this layer of capsules displays a magenta image (more positive a*) and when positive a white image (more negative a*). This switching corresponds to arrow iii in
The first two coating steps of Example 10 above were repeated using the magenta shuttering capsule slurry prepared in Example 6 above for the first coated layer and the cyan shuttering capsule slurry prepared in Example 5 above for the second coated layer, except that in the second coating the bar coater gap was 80 μm. Next, the yellow/white vertical switching capsule slurry prepared in Example 8 above was applied with a bar coater gap of 100 μm to form a third capsule layer, which was dried at 60° C. An adhesive layer was laminated on top of the third layer of capsules, the release sheet removed and the remaining layers laminated on to a graphite rear electrode, all as in Example 10. As finally assembled the display structure comprised, in order from the viewing surface, a first layer of PET film base, a second layer of patterned electrode, a third layer of magenta shuttering capsules, a fourth layer of cyan shuttering capsules, a fifth layer of yellow/white vertically switching capsules, a sixth layer of a conductively doped lamination adhesive, and a seventh layer comprising a graphite rear electrode.
The display structure was driven, illuminated and the light reflected therefrom analyzed, all in the same manner as in Example 10. The results are shown in Table 7 below.
These results are shown graphically in
A display was prepared essentially as described in Example 11 above, except that the ITO coating on the PET was pretreated with a composition comprising an ionic dopant prior to application of the pigment-less capsule layer. This display was addressed by using the waveform shown in Table 8 below.
The drive continued with pulses at 30V of 200 ms length followed by rests of 2 seconds in length. The colors produced by the display are shown in
From the foregoing discussion, it will be seen that the present invention provides variable transmission electrophoretic media capable of displaying multiple colors. When used as a variable color segmented overlay, the media of the present invention can provide a much broader color gamut than a conventional (static) color filter array. The present invention also provides a low haze monochrome variable transmission medium with high image stability.
It will be apparent to those skilled in the art that numerous changes and modifications can be made in the specific embodiments of the invention described above without departing from the scope of the invention. Accordingly, the whole of the foregoing description is to be interpreted in an illustrative and not in a limitative sense.
Claims
1. An electro-optic display comprising at least first and second layers of electro-optic material, the display further comprising a plurality of pixel electrodes disposed on one side of the first and second layers and defining a plurality of pixels of the display, and a single continuous second electrode disposed on the opposed side of the first and second layers from the first electrode and extending across all the pixels of the display, there being no electrode between the first and second layers.
2. An electro-optic display according to claim 1 further comprising a third layer of electro-optic material, the third layer being capable of displaying at least one optical state which cannot be displayed by the first and second layers, the second electrode being disposed on the opposed side of the first, second and third layers from the first electrode, there being no electrode between the second and third layers.
3. An electro-optic display according to claim 2 wherein the three layers contain cyan, magenta and yellow pigments, in any order.
4. An electro-optic display according to claim 3 wherein the layer containing the yellow pigment is arranged to have a smaller number of gray levels than the layers containing the cyan and magenta pigments.
5. An electro-optic display according to claim 3 having a viewing surface through which an observer views the display, and wherein the two electro-optic layers closest to the viewing surface contain cyan and yellow pigments, in either order.
6. An electro-optic display according to claim 1 wherein at least one of the layers of electro-optic material comprises an electrophoretic material comprising a plurality of charged pigment particles dispersed in a fluid and capable of moving through the fluid on application of an electrical field to the layer.
7. An electro-optic display according to claim 6 wherein at least one of the first and second layers comprises a microcavity electrophoretic material.
8. An electro-optic display according to claim 6 wherein the charged particles in at least one of the layers are movable between a first optical state, in which the pigment particles occupy substantially the whole area of each pixel, and a second optical state, in which the pigment particles occupy only a minor proportion of the area of each pixel.
9. An electro-optic display according to claim 8 wherein the charged particles in each of the first and second layers are movable between a first optical state, in which the pigment particles occupy substantially the whole area of each pixel, and a second optical state, in which the pigment particles occupy only a minor proportion of the area of each pixel.
10. An electro-optic display according to claim 9 wherein the yield stresses of the fluids in the first and second layers differ.
11. An electro-optic display according to claim 9 wherein the sizes of the microcavities in the first and second layers differ.
12. An electro-optic display according to claim 9 wherein the particles in the first and second layers differ in at least one of size, shape and electrical conductivity.
13. An electro-optic display according to claim 9 wherein the fluids in the first and second layers differ in at least one of viscosity and electrical conductivity.
14. An electro-optic display according to claim 9 having a viewing surface at or adjacent the surface of the first electro-optic layer remote from the second electro-optic layer, the electro-optic display further comprising a third electro-optic layer on the opposed side of the second electro-optic layer from the viewing surface, the third electro-optic layer comprising first and second types of particles of differing colors disposed in a fluid and capable of moving through the fluid on application of an electric field to the third electro-optic layer, the first and second types of particles being of differing electrophoretic mobility.
15. An electro-optic display according to claim 14 wherein the first type of particles in the third electro-optic layer are white.
16. An electro-optic display according to claim 15 wherein the particles in the first and second electro-optic layers are yellow and cyan, in either order, and the second type of particles in the third electro-optic layer are magenta.
17. An electro-optic display according to claim 1 wherein at least one of the first and second electrodes occupies only a minor proportion of the area of a pixel.
18. An electro-optic display according to claim 7 wherein the walls of the microcavity have a higher electrically conductivity than the phase comprising the plurality of charged pigment particles dispersed in the fluid.
19. An electro-optic display according to claim 1 wherein one of the electro-optic layers has at least two stable states, and the second electro-optic layer has only one stable state.
20. A microcavity electrophoretic display comprising walls defining at least one cavity, the cavity containing a fluid and first, second and third types of particles dispersed in the fluid, each of the first, second and third types of particles having an unshuttered state, in which the particles occupy substantially the entire area of the microcavity, and a shuttered state, in which the particles occupy only a minor proportion of the areas of the microcavity, the first, second and third particles being of differing colors and differing in dielectrophoretic and/or electro-osmotic properties such that the first, second and third types of particles can be moved between their unshuttered and shuttered states independently of one another.
21. A microcavity electrophoretic display according to claim 20 wherein the colors of the first, second and third types of particles are such that when all three types of particles are in their unshuttered states the display appears substantially black.
Type: Application
Filed: Apr 26, 2018
Publication Date: Aug 23, 2018
Inventors: Stephen J. Telfer (Arlington, MA), Richard J. Paolini, JR. (Framingham, MA), Sunil Krishna Sainis (Melrose, MA), Randal M. Hill (The Woodlands, TX), Isaac W. Moran (Maynard, MA), Lee Yezek (Watertown, MA), Alain Bouchard (Boston, MA), William Vetterling (Lexington, MA), George G. Harris (Woburn, MA), Hywel Morgan (Chandlers Ford), Luke Slominski (Sharon, MA), Jay William Anseth (Canton, MA), Jennifer M. Morrison (Wakefield, MA), Craig A. Herb (Medford, MA)
Application Number: 15/963,192