BIOFUNCTIONAL MATERIALS

Abstract

Provided are methods for providing thermal stability to a protein whereby a digestive protein is covalently bound to a substrate by a linker moiety bound to an outer surface of said substrate and an active group of the protein, the linker moiety covalently linking the protein to a surface of the substrate wherein the digestive protein forms a layer on the surface of said substrate such that the digestive protein is surface exposed.

Description

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 15/790,846 filed Oct. 23, 2017, which is a continuation of U.S. patent application Ser. No. 11/562,503 filed Nov. 22, 2006 (now U.S. Pat. No. 9,828,597), the entire contents of each of which are incorporated herein by reference.

FIELD

The present disclosure relates to self-cleaning compositions and a process for preventing and reducing surface stain accumulation due to bird droppings, bug wastes, food debris, and other stain causing materials.

TECHNICAL BACKGROUND

Both interior and exterior surfaces of automobile, such as coatings, paints, and seat fabrics, are subject to contamination and corrosions when they are under prolonged exposure to bird dropping, insect debris, resins of conifer, microbes, gums, etc. Certain stains, such as insect-originated stains, are hard to remove with regular automatic brush-free washing. Interior surfaces and coatings may also be easily get stained with oil, protein, sugar and other ingredients in foods and beverages, and timely removal of such stains may present certain challenges.

Here, the present invention specifically involves the incorporation of digestive proteins including lysozymes, proteases, lipases, cellulases, etc., onto surfaces such as paints and coatings. The catalytic activity of the digestive proteins enables ongoing self-cleaning to reduce and eliminate stain contaminations. The mechanism of action of these digestive proteins is mainly enzymatic in nature and does not involve the use of any corrosive or oxidative components; therefore, they are environmentally friendly.

Stains of interests in the initial stage of this work include those formed from broken bodies of bugs, animal (like bird) wastes, foods, milk and other beverages, and cosmetic and personal care products. Although the detailed components vary with sources of stains, the major components of stains that are adhesive to surfaces are proteins, polysaccharides, fats or oils.

DESCRIPTION OF RELATED ART

It is known to incorporate enzymes into coating or into substrates for the purpose of providing a surface with antimicrobial, antifungal or antifouling properties. Yet it is novel to the best knowledge of Applicants to attach digestive proteins to a surface for the purpose of enzymatically decomposing stain molecules in contact with the surface.

U.S. Pat. No. 6,818,212 discloses an enzymatic antimicrobial ingredient for disinfection and for killing microbial cells.

Wang et al. 2001 discloses lifespan extension of an enzyme upon its covalent binding at wet conditions; yet the reference does not seem to mention the utilization of such covalently bound enzyme in the area of surface self-cleaning.

U.S. Pat. No. 3,705,398 discloses polymeric articles having active antibacterial, antifungal and combinations of antibacterial and antifungal properties. The antibacterial and antifungal activating agents are distributed within the polymeric composition and migrate to the surface.

U.S. Pat. No. 5,914,367 discloses a method of preparing a polymer-protein composite including polymerizing a monomer in the presence of a protein dissolved in an organic phase via the ion-pairing of the protein with a surfactant. This reference, however, does not seem to mention the prevention or reduction of stain accumulation using the digestive power of such a polymer-protein composite.

U.S. Pat. No. 6,150,146 discloses a method of releasing a compound having antimicrobial activity from a matrix at a controlled rate. The method includes an enzyme and a substrate within the matrix beforehand to allow the enzyme and substrate to react with each other in the matrix, thereby to produce a compound having antimicrobial activity. The patent also discloses a coating composition comprising a film-forming resin, an enzyme, a substrate and any enzyme capable of reacting with the substrate.

U.S. 2005/0058689 discloses paints and coatings having antifungal growth and antibacterial materials. Specific chemicals and formations are disclosed for incorporation into painted surfaces which are antifungal compositions to inhibit growth of mold, bacterial, and fungi on building materials.

The object of the present invention is to provide self-cleaning composition and process containing digestive proteins for preventing and reducing stain accumulation.

SUMMARY

The following summary of the invention is provided to facilitate an understanding of some of the innovative features unique to the present invention and is not intended to be a full description. A full appreciation of the various aspects of the invention can be gained by taking the entire specification, claims, drawings, and abstract as a whole.

Provided are processes of stabilizing a protein against thermal deactivation that include binding a protein to a substrate whereby the binding includes a linker moiety between the substrate and the digestive protein. The protein may include proteases which hydrolyze protein molecules, lipases which hydrolyze lipids and fats, cellulases which hydrolyze cellulose, and amylases which hydrolyze carbohydrates, etc. A layer of protein may be formed on the surface.

Optionally, a surface may be pretreated with a layer of polymer comprising one or more active groups. A protein suspension may be spin coated onto the polymer layer with the active groups to form covalent bonds between the proteins and the polymer layer. The active groups may comprise alcohol, thiol, aldehyde, carboxylic acid, anhydride, epoxy, and ester, etc. Alternatively, proteins may be attached to nanoparticles before their suspension with paints or coatings.

BRIEF DESCRIPTION OF DRAWINGS

The present invention is further illustrated by reference to the accompanying drawings, in which

FIG. 1 is a depiction of an attachment of enzymes to the surface of polymeric nanoparticles.

FIG. 2 is a depiction of fluorescence images of protease coating prepared via adsorption and covalent cross-linking.

FIG. 3 shows a protein assay calibration curve.

FIG. 4 shows a calibration curve for tyrosine (product of hydrolysis).

FIG. 5 shows a representative GPC chromatograph indicating egg white stain degradation.

FIG. 6 shows the time course of egg white stain degradation.

FIG. 7 shows thermal stability of protease coating at 80° C.

DETAILED DESCRIPTION

The present disclosure relates to, in a first aspect, a composition comprising a substrate, a digestive protein capable of decomposing a stain molecule, and a linker moiety.

This disclosure specifically involves the incorporation of one or more digestive proteins including lysozymes, proteases, lipases, cellulases, etc., onto surfaces such as paints and coatings. The catalytic activity of the digestive proteins enables ongoing self-cleaning to reduce and eliminate stain contaminations.

Various stains include those formed from broken bodies of bugs, animal (such as bird) wastes, foods, milk and other beverages, and cosmetic and personal care products. Although the detailed components vary with sources of stains, the major components of stains that are adhesive to surfaces are proteins, polysaccharides, fats or oils.

The activity of the digestive proteins toward different stain sources may be evaluated in a solution environment. Tests are conducted at different conditions including different pH and temperature, in an attempt to evaluate the proteins' performance in an automobile environment instead of that in a washer machine as they have been traditionally applied. Tests include: protein-related activity; starch-related activity tests; tests with oily stains. Protein activity unit is defined as: one unit of digestive protein hydrolyzes casein to produce absorbance difference equivalent to 1.0 μmol of tyrosine per minute at 37° C. under the conditions of the assay. Results of activity assay show covalent cross-linked protease present an activity that is nine times more than that of a physically absorbed protease.

There are several ways to incorporate the digestive proteins onto a substrate. One of which involves the application of covalent bonds. Specifically, free amine groups of the digestive proteins may be covalently bound to an active group of the substrate. Such active groups include alcohol, thiol, aldehyde, carboxylic acid, anhydride, epoxy, ester, or any combination thereof. This method of incorporating digestive proteins delivers unique advantages. First, the covalent bonds tether the proteins permanently to the substrate and thus place them as an integral part of the final composition with much less, if not at all, leakage of digestive protein species. Second, the covalent bonds provide for extended enzyme lifetime. Over time, proteins typically lose activity because of the unfolding of their polypeptide chains. Chemical binding such as covalent bonding effectively restricts such unfolding, and thus improves the protein life. The life of a protein is typically determined by comparing the amount of activity reduction of a protein that is free or being physically adsorbed with that of a protein covalently-immobilized over a period of time. Results have shown that a protein that is in free form or being physically adsorbed to a substrate loses its activity much faster that a protein in covalent-bond form.

Alternatively, digestive proteins may be uniformly dispersed throughout the substrate network to create a homogenous protein platform. In so doing, digestive proteins may be first modified with polymerizable groups. The modified proteins may be solubilized into organic solvents in the presence of surfactant, and thus engage the subsequent polymerization with monomers such as methyl methacrylate (MMA) or styrene in the organic solution. The resulted composition includes digestive protein molecules homogeneously dispersed throughout the network.

Also, digestive proteins may be attached to surfaces of a substrate in comparison to the above mentioned cross-linking methods. An attachment of digestive proteins corresponding to ˜100% surface coverage was achieved with polystyrene particles with diameters range from 100 to 1000 nm.

The digestive proteins of the composition may include proteases which hydrolyze protein molecules, lipases which hydrolyze lipids and fats, cellulases which hydrolyze cellulose, and amylases which hydrolyze carbohydrates. It is neither required nor necessary for the digestive proteins to have their functional binding pockets all facing toward stain particles. A layer of digestive proteins delivers enough coverage and digesting activity even though the digestive proteins may be randomly arranged on a surface.

Optionally, a surface is pretreated with a layer of polymer comprising one or more surface active groups of succinimide ester. A digestive protein suspension is spin coated onto the layer of the polymer with the active groups to form covalent bonds with the proteins. Alternatively, digestive proteins may be attached to nanoparticles before their suspension with paints or coatings.

This disclosure is further directed to a composition comprising a digestive protein capable of decomposing a stain molecule, and a coating substrate wherein the digestive protein may be entrapped in the coating substrate. In this composition, the digestive protein may be selected from lysozymes, proteases, lipases, cellulases, glycosidases, and amylases.

In another aspect of this disclosure, a process is disclosed for reducing and or eliminating stain contaminations. The process comprises binding a substrate to a surface and forming a linker moiety between an active group of a digestive protein and the substrate. In this process, the substrate may comprise surface active groups such as alcohol, thiol, aldehyde, carboxylic acid, anhydride, epoxy, ester, and any combinations thereof.

Example 1

Enzymes may be attached to surfaces of plastics. An enzyme attachment corresponding to ˜100% surface coverage may be achieved with polystyrene particles with diameters range from 100 to 1000 nm. By coating with digestive protein, these particles may be used along with paints or coatings to functionalize the surfaces of materials. The same chemical bonding approach may be applied to coat enzymes onto preformed plastic parts, and thus form a protein coating on the parts' surfaces. As shown in FIG. 1, particles with diameters ranging from 100 nm to 1000 nm may be synthesized by emulsion polymerization. Emulsion polymerization is a type of polymerization that takes place in an emulsion typically incorporating water, monomer, and surfactant. The most common type of emulsion polymerization is an oil-in-water emulsion, in which droplets of monomer (the oil) are emulsified (with surfactants) in a continuous phase of water.

Particles as previously described may be synthesized by mixing an aqueous solution (mixture of water and ethanol, ˜20 ml), containing a polymerizable surfactant (2-sulfoethylmethacrylate), a stabilizer (polyvinylpyrrolidone, PVP) and an initiator (2,2′-Azobis [2-methyl-N-(2-hydroxyethyl) propionamide]), will be mixed with an organic solution (˜1 ml) of styrene, N-acryloxysuccinimide (NAS, a functionalized vinyl monomer), and divinyl benzene (˜1% v/v). The particle size may be controlled by adjusting phase ratio (1/30˜1/15, oil/aqueous) and the concentration of ethanol (0.125˜0.50 ml/ml), 2-sulfoethyl methacrylate and PVP (0˜5.5 mg/ml). The reaction may be performed with stirring at 70° C. for 10 h, followed by washing the resulted particles with ethanol and DI water in a stirred ultrafiltration cell with a polyethersulfone membrane (cut off MW: 300 kDa).

Example 2

Stains may be generated from different sources of contacts. Body residues of bugs, animal wastes, food, milk and other beverages, and cosmetic and personal care products may all cause stains. Although the detailed components vary with sources of stains, the major components that are adhesive to surfaces are proteins, simple sugars and polysaccharides, fats and/or oils. Digestive proteins including lipases, proteases, amylase and cellulose, each of them attacks different components, are thus far the most effective, safe and economic agents to fight against such stains. As shown below in Table 1, these proteins were examined and tested in our initial screening tests, and eventually we selected protease to proceed for the majority of the subsequent experiments due to the easiness in activity measurement.

TABLE 1
Enzyme	Targeting Stains	Source	Functions	Standard testing conditions
Proteases	Bugs, dairy products,	Bacillus	Hydrolysis of	Casein with Folin &
	animal wastes	licheniformis	proteinaceous	Ciocalteu’s Phenol dye,
		(Subtilisin Carlsberg)	materials	pH 7.5, 37° C.,
				absorbance at 660 nm
Lipase AK	Fats and oils,	Pseudomonas	Hydrolysis of	p-nitro phenyl valerate,
	cosmetics, inks	fluorescens	oils and fats	pH 7.7, 40° C.,
				absorbance at 405 nm
α-Amylase	Juices, soft drinks,	Bacillus subtilis	Hydrolysis of	Dyed Starch,
	foods, animal wastes		starch	pH 6.9, 25° C.,
				absorbance at 540 nm
Cellulase	Beverages, foods,	Aspergillus niger	Hydrolysis of	Dyed cellulose,
	animal wastes,		cellulose	pH 6, 50° C.,
				absorbance at 590 nm

Example 3

Preparation of Enzyme Coating

N-acryloxy succinimide (392 mg), 1.2 ml of styrene and 29.2 mg of 4,4′-azobis-(4-cyanovaleric acid) were mixed with 16 ml of chloroform in a 20 ml glass reaction vial. The vial was purged with nitrogen, sealed and incubated at 70° C. for 12 hrs with stirring, followed by the removal of solvent by purging nitrogen. The polymer product was re-dissolved in chloroform at a concentration of 50 mg/ml. One milliliter of the resulting solution was spin-coated onto a polystyrene plate (11 cm in diameter) at 6000 rpm. Protease from Subtilisin Carlsberg was dissolved in 0.05 M phosphate buffer at a concentration of 10 mg/ml. The enzyme was applied onto the active polymer coated plate via 3-step layer-by-layer spin coating: 1) 1 ml of the protease solution, 2) 1 ml of protease solution containing 0.5% (V/V) of glutaraldehyde, 3) 1 ml of protease solution. The spin-coated plates were kept at 4° C. for 12 h, followed by extensive washing with 0.05 M Tris buffer (pH 8), 2M NaCl solution and DI water. Finally the plates were air-dried and cut into small pieces (1×2 cm). This method was designated as covalent cross-linking. As a comparison, similar procedure was applied on a polystyrene plate without the active polymer coating, which was called as physical adsorption.

Example 4

Visualization of Enzyme Coating

Fluorescent dye (Oregon green, Invitrogen Corp.) was first dissolved in dimethyl sulfoxide at a concentration of 2 mg/ml. The sample plates with physically adsorbed and covalently immobilized enzyme were incubated in the dye solution at room temperature with gentle shaking for 2 hours, followed by rinsing with DI water. The plates were then dried in nitrogen and observed under a fluorescence microscope. The images are shown in FIG. 2, where green color denotes the area covered with enzyme. Compared with physical adsorption, much more enzyme was immobilized on the surface using covalent cross-linking method.

Example 5

Determination of Enzyme Loading

The amount of enzyme attached to the plastic plate was determined by a reversed Bradford method. Typically, a working solution was first prepared by diluting Bradford reagent with DI water (1:5, by volume). A calibration curve was first obtained using free protease as the standards. In a 1 ml cuvette, 0.5 ml of protease solution was mixed with 0.5 ml of the working solution and then allowed to react for 5 min. The absorbance of the solution was measured at 465 nm on a spectrophotometer. After testing a series of different protease concentrations, a calibration curve was obtained as shown in FIG. 3.

To determine the loading of immobilized enzyme, a piece of enzyme-coated plate (1 cm×2 cm) was placed into a 20-ml glass vial, followed by the addition of 0.5 ml of DI water and 0.5 ml of the working solution. The vial was slightly agitated for 5 min at room temperature to allow binding of the dye to the immobilized enzyme. The absorbance of the supernatants was then recorded at 465 nm. Similarly a blank plastic plate without enzyme coating was also measured as the control. The reading obtained with the blank plate was subtracted from the reading obtained from the enzyme loaded plate. Comparing the obtained reading difference with the calibration curve gave the loading on the plate, which was then normalized into a unit of μg/cm². The enzyme loading by covalent cross-linking and physical adsorption were 8.5 and 1.0 μg/cm², respectively.

Example 6

Verification of the Proteolytic Activity of Enzyme Coating

Enzyme in solution: The proteolytic activity of protease was determined using 0.65% (w/v) casein as the substrate. Protease solution (0.1 ml) was incubated with 0.5 ml of casein solution for 10 min at 37° C. The reaction was stopped by the addition of 0.5 ml of tricholoroacetic acid (110 mM). The mixture was centrifuged to remove the precipitation. The resulting supernatant (0.4 ml) was mixed with 1 ml of sodium carbonate (0.5 M) and 0.2 ml of diluted Folin & Ciocalteu's phenol reagent (1:4 by diluting Folin & Ciocalteu's phenol reagent with DI water), followed by incubation at 37° C. for 30 min. Finally the mixture was centrifuged again and the absorbance of the supernatant was measured at 660 nm on a spectrophotometer. Blank experiment was performed without enzyme solution by adding 100 μl of buffer and carrying out similar test. The absorbance of the blank was subtracted from the sample (enzyme solution).

The activity unit was defined as: one unit of enzyme hydrolyzes casein to produce absorbance difference equivalent to 1.0 μmol of tyrosine per minute at 37° C. under the conditions of the assay. Tyrosine amino acid was used for calibration. Various concentrations of tyrosine were reacted with Folin-Ciocalteau reagent and the resulting calibration curve is shown in FIG. 4.

Enzyme coating: The activity of the immobilized protease was determined in a similar manner by using an enzyme coated polymer piece (1×2 cm) instead of enzyme in solution and a blank polymer coated piece as control. The activity of protein was termed as surface activity per unit area.

Results of activity assay showed that plates with covalent cross-linked protease afford 5.6×10⁻³ unit/cm², while physical adsorbed enzyme only displayed an activity of 0.6×10⁻³ unit/cm².

Example 7

Stain Degradation on Enzyme Coating

Egg white was used as the model stain to determine the stain degradation on enzyme coating. Onto a plate (11 cm in diameter) with protease-coating, 2 ml of egg white solution (10 mg/ml in DI water) was spin-coated at 2000 rpm. The plate was then cut into smaller pieces (1×2 cm) and kept at room temperature (25° C.) for various period of time to allow the degradation of egg white. After certain intervals, one small plate was carefully washed with DI water and the egg white in the washing solution was analyzed using gel permeation chromatography (GPC) to determine the molecular weight changes. Typically two peaks were found in the GPC chromatograph (FIG. 5): one has shorter retention time and the other has longer retention time, corresponding to the egg white and degradation products, respectively. Based on the area of the egg white peaks, a time course of egg white degradation was obtained as shown in FIG. 6. Control experiments were also performed using plates without protease coating, but no clear product peaks were identified.

Example 8

Thermal Stability of the Enzyme Coating

Thermal stability of the enzyme coating was studied at 80° C. in an air-heating oven. At certain time intervals, the sample plate(s) were taken out of the oven and the activity were measured following the procedure as described in Working Example 2. The decrease of activity with time was plotted in FIG. 9. It appeared that covalent cross-linked enzyme afforded better stability against thermal inactivation, as compared to physical adsorbed enzyme.

Various modifications of the present invention, in addition to those shown and described herein, will be apparent to those skilled in the art of the above description. Such modifications are also intended to fall within the scope of the appended claims.

It is appreciated that all reagents are obtainable by sources known in the art unless otherwise specified or synthesized by one of ordinary skill in the art without undue experimentation.

Patents and publications mentioned in the specification are indicative of the levels of those skilled in the art to which the invention pertains. These patents and publications are incorporated herein by reference to the same extent as if each individual application or publication was specifically and individually incorporated herein by reference.

The foregoing description is illustrative of particular embodiments of the invention, but is not meant to be a limitation upon the practice thereof. The following claims, including all equivalents thereof, are intended to define the scope of the invention.

Claims

1. A process for stabilizing a protein against thermal inactivation, comprising:

binding a protein to the surface of a solid substrate;

the protein bound to the surface by a linker moiety between an active group of the protein and said substrate such that said binding of the protein to the solid substrate stabilizes the protein against thermal inactivation.

2. The process of claim 1 wherein the protein forms a layer on the surface such that the protein is surface exposed.

3. The process according to claim 1, wherein said substrate comprises one or more selected from the group consisting of alcohol, thiol, aldehyde, carboxylic acid, anhydride, epoxy, and ester.

4. The process according to claim 1, wherein said surface is selected from the group consisting of metal, glass, paint, plastic, and fabrics.

5. The process according to claim 1, wherein the digestive protein is bound to the substrate via a free amine on the protein.

6. The process according to claim 5 wherein said free amine is a lysine, arginine, asparagine, glutamine, or an N-terminus.

7. The process according to claim 1, wherein the protein is a lysozyme, protease, lipase, cellulase, glycosidase, or amylase.

8. The process according to claim 1 wherein the binding is performed by spin coating the protein onto the surface.

9. The process according to claim 1 wherein the surface comprises polystyrene.

10. The process according to claim 1 wherein the binding comprises spin coating a first solution comprising the protein onto the surface, and

spin coating onto the surface a second solution comprising the protein and glutaraldehyde.

11. The process of claim 10 further comprising spin coating onto the surface a third solution comprising the protein.

12. The process of claim 10 further comprising air drying the coated substrate.

13. The process of claim 1 wherein the protein is stabilized against inactivation at 80° C.