MULTI-LAYER CONVERSION MATERIAL FOR DOWN CONVERSION IN SOLID STATE LIGHTING
Light emitting diodes are disclosed that utilize multiple conversion materials in the conversion process in order to achieve the desired emission color point. Different embodiments of the present invention can comprise different phosphor types in separate layers on, above or around one or a plurality of LED chips to achieve the desired light conversion. The LEDs can then emit a desired combination of light from the LED chips and conversion material. In some embodiments, conversion materials can be applied as layers of different phosphor types in order of longest emission wavelength phosphor first, followed by shorter emission phosphors in sequence as opposed to applying in a homogeneously mixed phosphor converter. The conversion material layers can be applied as a blanket over the LED chips and the area surrounding the chip, such as the surface of a submount holding the LED chips.
This application is a continuation of and claims the benefit of U.S. patent application Ser. No. 13/028,863, to Tong et al., filed on Feb. 16, 2011, and U.S. patent application Ser. No. 13/649,052, to Lowes et al., filed on Oct. 10, 2012.
BACKGROUND OF THE INVENTION1. Field of the Invention
This invention relates to solid state light sources and in particular to efficient and reliable light emitting diode (LED) packages having enhanced emission characteristics through separation of different phosphor components.
2. Description of the Related Art
Incandescent or filament-based lamps or bulbs are commonly used as light sources for both residential and commercial facilities. However, such lamps are highly inefficient light sources, with as much as 95% of the input energy lost, primarily in the form of heat or infrared energy. Compact Fluorescent Lamps are more effective than incandescent at converting the electricity into light but require the use of toxic materials such as Hg such that when the lamps are disposed of these toxic materials that can pollute the environment, including underground water supplies. One solution for improving the efficiency of lamps or bulbs is to use solid state devices such as light emitting diodes (LED or LEDs), rather than metal filaments, to produce light.
Light emitting diodes generally comprise one or more active layers of semiconductor material sandwiched between oppositely doped layers. When a bias is applied across the doped layers, holes and electrons are injected into the active layer where they recombine to generate light. Light is emitted from the active layer and from all surfaces of the LED.
In order to use an LED chip in a circuit or other like arrangement, it is known to enclose an LED chip in a package to provide environmental and/or mechanical protection, color selection, light focusing and the like. An LED package also includes electrical leads, contacts or traces for electrically connecting the LED package to an external circuit. In a typical LED package 10 illustrated in
A conventional LED package 20 illustrated in
LEDs, such as those found in the LED package 20 of
Lamps have also been developed utilizing solid state light sources, such as LEDs, with a conversion material that is separated from or remote to the LEDs. Such arrangements are disclosed in U.S. Pat. No. 6,350,041 to Tarsa et al., entitled “High Output Radial Dispersing Lamp Using a Solid State Light Source.” The lamps described in this patent can comprise a solid state light source that transmits light through a separator to a disperser having a phosphor. The disperser can disperse the light in a desired pattern and/or changes its color by converting at least some of the light through a phosphor. In some embodiments the separator spaces the light source a sufficient distance from the disperser such that heat from the light source will not transfer to the disperser when the light source is carrying elevated currents necessary for room illumination. Additional remote phosphor techniques are described in U.S. Pat. No. 7,614,759 to Negley et al., entitled “Lighting Device.”
The coated LEDs, LED packages and solid state lamps described above can utilize more than one type of conversion material, such as phosphors, to produce the desired overall emission temperature and CRI. Each of the phosphors can absorb light from the LED and re-emit light at a different wavelength of light. Some of these conventional arrangements can utilize a green/yellow phosphor, in combination with a red or orange phosphor, with these phosphors typically absorbing blue LED light and emitting green/yellow and red light, respectively. The re-emitted light can combine with blue LED light to produce the desired emission characteristics.
These conventional arrangements typically mix the different phosphors together at one location, such as in the LED coating, LED package encapsulant, or lamp remote phosphor. One disadvantage of mixing the phosphors together is that there can be significant “cross-talk” or “overlap” between the emission and excitation spectrum for the different phosphors, which can negatively impact the CRI and emission efficiency for the combined emitted light.
The present invention is directed to different LEDs having conversion materials arranged in a layered fashion to improve the LEDs' characteristics. Some of these characteristics include improved emission intensity and color rendering index (CRI), while others can include a reduction in the amount of costly conversion material needed to reach a desired color point or CRI. In some embodiments the different conversion material layers can be arranged so that respective layers absorb light from the LED light source and re-emit light in different wavelength spectrum. In some embodiments, the layers can be tailored so that there is minimal overlap of the emission and excitation spectrums for the conversion materials in the layers.
One embodiment of an LED according to the present invention comprises one or more LED chips on a surface of a submount. A conversion material layer comprising two or more layers of different conversion materials is included covering the one or more LED chips and at least a portion of the submount around said LED chips. An encapsulant is included over the LED chips and the submount.
One embodiment of a solid state emitter according to the present invention comprises one or more of solid state light sources on a planar surface of a submount. A plurality of conversion material layers are included over the light sources and over at least part of the planar surface. One of the conversion material layers that is below the top one of the conversion material layers emits a wavelength of light that does not substantially overlap with the excitation spectrum of one of the layers above it. An encapsulant is included over the solid state light sources and the submount.
Another embodiment of an LED according to the present invention comprises an LED chip. A conversion material layer is included comprising two or more layers of different conversion materials, with the conversion material layer covering said LED chip and the area around the LED chip. The LED produces improved emission characteristics compared to the same LED having a conversion material layer with mixed conversion materials.
These and other aspects and advantages of the invention will become apparent to those skilled in the art from the following detailed description and the accompanying drawings, which illustrate by way of example the features of the invention.
The present invention is directed to solid state emitters, such as light emitting diodes (LED or LEDs) that utilize multiple conversion materials or phosphor types in the conversion process in order to achieve the desired emission color point. Different embodiments of the present invention can apply the different phosphor types in separate layers on, above or around one or a plurality of LED chips to achieve the desired light down conversion. The LEDs can then emit a desired combination of light from the LED chips and conversion material, such as a white light combination.
In some embodiments, one or more of the phosphor layer can be a relatively thin conformal layer having a substantially uniform phosphor particle density. In other embodiments, a phosphor layer may be provided that comprises phosphor particles that are nonuniformly dispersed therein. In some embodiments the layers can have a phosphor-free regions in different locations, such as at the exterior surfaces or near the edges of the phosphor layer. The phosphor layer, or any wavelength conversion layer, can convert a portion of the light emitted from the LED chip to a different wavelength, a process that is known in the art. One example of this process, is converting a portion of blue-emitted light from an LED chip, to yellow/green and red light. As further described below, there are many different phosphors that can be used for this type of light conversion.
In some embodiments, conversion materials can be applied as layers of different phosphor types in order of longest emission wavelength phosphor first (e.g. red), followed by shorter emission phosphors (e.g. yellow or green) in sequence as opposed to applying in a homogeneously mixed phosphor converter. The conversion material layers can be applied as a blanket over the LED chips and the area surrounding the chip, such as the surface of the submount holding the LED chips. The advantages that can be realized with embodiments according to the present invention can include, but is not limited to, improved efficiency at the same color rendering index (CRI), enhanced CRI at the same efficiency, and a reduction in the quantity of certain phosphors needed to achieve a given color target. For example, red phosphors are relatively expensive and in the case where less red phosphors are used the cost savings can be significant.
Some conversion materials can be arranged in different embodiments described herein to achieve the desired emission efficiency (e.g. lumens per watt (LPW)). This discrete layer arrangement can also be optimized to achieve the desired CRI, R9, Qg, thermal quenching, etc. For some embodiments directed to optimized thermal quenching, the most temperature sensitive conversion material can be placed on the LED surface for improved heat sinking.
The layered arrangements according to the present invention can provide for conversion materials separation to reduce the impact of emission and excitation spectrum overlap. Some embodiments of the present invention are directed to LEDs arranged to produce white light with a warm color temperature by utilizing two separate phosphor components in a way that eliminates or reduces the re-absorption (interaction) between the two component phosphors. That is, the separation reduces the amount of light from the first phosphor that interacts with the second phosphor, to reduce or eliminate the re-absorption by the second phosphor. This in turn reduces the color shift in CRI and losses that may be experienced by this re-absorption. This can result in improved emission efficiency of warm white light with a CRI that is significantly higher than those arrangements where re-absorption is not addressed, such as where the different phosphors are mixed.
In some embodiments, the first phosphor can re-emit a wavelength of light that does not overlap with the excitation spectrum of the second phosphor such that light re-emitted from the first phosphor passes through the second phosphor without risk of being absorbed by the second phosphor. The emission spectrum of the second phosphor, however, may emit light that at least partially overlaps with the excitation spectrum of the first phosphor. In arrangements where light from the second phosphor passes through the first phosphor, there may be a risk of light from the second phosphor being re-absorbed by the first phosphor. The separation of the phosphors minimizes the amount of re-emitted light that encounters the first phosphor, thereby minimizing the amount of light that can be re-absorbed by the first phosphor. To allow light from the first phosphor to pass through the second phosphor, in some embodiments can comprise materials such that the emission spectrum of the first phosphor does not overlap the excitation spectrum of the second phosphor.
In some embodiments, the second phosphor can comprise a yellow/green phosphor that absorbs blue light and re-emits yellow/green light, and the first phosphor can comprise a red phosphor that absorbs blue light and emits red light, with the emission spectrum of the yellow/green phosphor overlapping the excitation spectrum of the red phosphor. As described in more detail below, these embodiments provide separation between the first and second phosphors in a way that minimizes the chances that the yellow/green phosphor emission would encounter the red phosphor, and as a result, there is little chance of re-emitted yellow/green light being reabsorbed by the red phosphor. Compared to the mixed phosphor arrangement, the phosphor separation results in overall lamp or package emission having a higher CRI and higher phosphor efficiency.
The separation can take many different forms that can provide different levels of reduction in crosstalk between the first and second phosphors. In some embodiments the separation can comprise separate layers on an LED chip, formed on top of each other, with each layer being a different one of the phosphors or having different phosphors that generally emit in the same or similar emission spectrums. In other embodiments, one of the phosphors can be separated from the others by an intervening layer, or the phosphor can be provided remote to the other phosphor. This remote arrangement can take many different forms. In some embodiments, one of the phosphors can comprise a conformal coat over one or more LEDs and the second phosphor can be remote to the first phosphor, such as in the shape of dome over the LEDs. This arrangement reduces even further the chances of crosstalk between the first and second phosphors by further reducing the chances that light emitted from the second phosphor would encounter the first phosphor.
Different embodiments can also comprise conversion material layers arranged in many different ways. Some can embodiments can include two phosphors, each of which can be provided in a separate layer as described above (e.g. yellow/green phosphor layer on red phosphor layer). In other embodiments more than two phosphors can be used, with some having two or more phosphors with similar emission characteristics in the first layer and two or more phosphors with similar characteristics in the second layer. In some of these embodiments the first layer can have two or more phosphors that are different but that both emit in the red wavelength spectrum. The second layer can also have two or more different phosphors that emit in the yellow/green emission spectrum. The different phosphor can be chosen to provide the desired LED emission characteristics. In other embodiments utilizing multiple phosphors in different emission spectrum, each of the phosphors can be provided in its own separate layer, while others of the phosphors can be in their own layers or can be mixed in a layer. The converter sequence in different embodiments can take many different permutations of mixed and separated layers. These can include different combinations and sequences such as mixed phosphor on a discrete (single phosphor) layer, a discrete layer on a mixed layer, a discrete layer on a mixed layer on a discrete layer, etc.
The present invention is described herein with reference to certain embodiments, but it is understood that the invention can be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. In particular, the present invention is described below in regards to certain LED packages or lamps having one or multiple LEDs or LED chips or LED packages in different configurations, but it is understood that the present invention can be used for many other lamps having many different configurations. Examples of different lamps arranged in different ways according to the present invention are described below and in U.S. Provisional Patent application Ser. No. 61/435,759, to Le et al., entitled “Solid State Lamp”, filed on Jan. 24, 2011, and incorporated herein by reference.
The embodiments below are described with reference to LED or LEDs, but it is understood that this is meant to encompass LED chips and LED packages. The components can have different shapes and sizes beyond those shown and different numbers of LEDs can be included. The present invention is described herein with reference to conversion materials, phosphors, phosphor layers and related terms. The use of these terms should not be construed as limiting. It is understood that the use of the term phosphor or phosphor layers is meant to encompass and be equally applicable to all wavelength conversion materials.
It is also understood that a light source may be comprised of one or multiple LED chips and in embodiments with more than one, different ones of the LED chips can have different emission wavelengths. Although the present invention is described below with reference to phosphor conversion materials, it is understood that many other conversion materials can be used. The present invention is described herein with reference to conversion materials, phosphor layers being remote to one another. Remote in this context refers being spaced apart from and/or to not being on or in direct thermal contact.
It is also understood that when an element such as a layer, region or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. Furthermore, relative terms such as “inner”, “outer”, “upper”, “above”, “lower”, “beneath”, and “below”, and similar terms, may be used herein to describe a relationship of one layer or another region. It is understood that these terms are intended to encompass different orientations of the device in addition to the orientation depicted in the figures. The phosphors are described herein with referenced to red, yellow or green emitting phosphors, but it is understood that this can include other colors close to these emission colors. For red, by example, this can include those close to red in the light spectrum, such as orange.
The present invention is described herein with reference to certain embodiments, but it is understood that the invention can be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. In particular, the present invention is described below in regards to certain LED packages having LED chips in different configurations, but it is understood that the present invention can be used for many other LED packages with other LED configurations. The LED packages can also have many different shapes beyond those described below, such as rectangular, and solder pads and attach pads can be arranged in many different ways. In other embodiments, the emission intensity of the different types of LED chips can be controlled to vary the overall LED package emission.
The present invention can be described herein with reference to conversion materials, wavelength conversion materials, remote phosphors, phosphors, phosphor layers and related terms. The use of these terms should not be construed as limiting. It is understood that the use of the term remote phosphors, phosphor or phosphor layers is meant to encompass and be equally applicable to all wavelength conversion materials.
The embodiments below are described with reference to an LED or LEDs, but it is understood that this is meant to encompass LED chips, and these terms can be used interchangeably. These components can have different shapes and sizes beyond those shown, and one or different numbers of LEDs can be included. It is also understood that the embodiments described below utilize co-planar light sources, but it is understood that non co-planar light sources can also be used. It is also understood that an LED light source may be comprised of multiple LEDs that may have different emission wavelengths. As mentioned above, in some embodiments at least some of the LEDs can comprise blue emitting LEDs covered with a yellow phosphor along with red emitting LEDs, resulting in a white light emission from the LED package. In multiple LED packages, the LEDs can be serially interconnected or can be interconnected in different serial and parallel combinations.
It is also understood that when a feature or element such as a layer, region, encapsulant or submount may be referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. Furthermore, relative terms such as “inner”, “outer”, “upper”, “above”, “lower”, “beneath”, and “below”, and similar terms, may be used herein to describe a relationship of one layer or another region. It is understood that these terms are intended to encompass different orientations of the device in addition to the orientation depicted in the figures. Further, many of the embodiments of the present invention are shown with a “top” primary emission surface. It is understood that any one or more surfaces, including but not limited to a top surface, can be (or can combine to form) a primary emission surface. For example, a package can be designed to have a primary emission out a side emission surface.
Although the terms first, second, etc. may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms are only used to distinguish one element, component, region, layer or section from another region, layer or section. Thus, a first element, component, region, layer or section discussed below could be termed a second element, component, region, layer or section without departing from the teachings of the present invention.
Embodiments of the invention are described herein with reference to cross-sectional view illustrations that are schematic illustrations of embodiments of the invention. As such, the actual thickness of the layers can be different, and variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances are expected. Embodiments of the invention should not be construed as limited to the particular shapes of the regions illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. A region illustrated or described as square or rectangular will typically have rounded or curved features due to normal manufacturing tolerances. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region of a device and are not intended to limit the scope of the invention.
The LED 50 is shown with two LED chips 52 but it is understood that in other embodiments (such as those described below) the light source can comprise one LED chips or more than two LED chips, with some comprising a multiple LED chip array. Many different LED chips can be used such as those commercially available from Cree Inc., under its DA, EZ, GaN, MB, RT, TR, UT and XT families of LED chips. The LED 50 is particularly arranged for use with the DA family of LED chips such as the DA850 chip that can be flip chip mounted and allows for wire-free bonding. These types of chips are generally described in U.S. patent application Ser. No. 12/463,709 to Donofrio et al., entitled “Semiconductor Light Emitting Diodes Having Reflective Structures and Methods of Fabricating Same,” which is incorporated herein by reference. The LED 50 can be arranged similar to the LED packages commercially available from Cree, Inc. under product names Xlamp XQ family of LEDs (e.g. Xlamp XQ-B LED). However, in this embodiment the phosphor is arranged in a discrete layered manner as opposed to the conventional mixed conversion material.
The LED chips 52 can emit many different colors of light, with a preferred LED chips 52 emitting light in the blue wavelength spectrum. It is understood that in some embodiments the LED chips can be provided following removal of its growth substrate. In other embodiments, the LED chip's growth substrate can remain on the LED chips 52 with some of these embodiments having a shaped or textured growth substrate. In some embodiments, the LED chips 52 can comprise a transparent growth substrate such as silicon carbide, sapphire, GaN, GaP, etc. The LED chips can also comprise a three dimensional structure and in some embodiments, the LEDs can have structures comprising entirely or partially oblique facets on one or more surfaces of the chip.
The LED 50 further comprises a submount 54, with the LED chips 52 mounted to the submount 54. The submount 54 can be formed of many different materials with a preferred material being electrically insulating, such as a dielectric material. The submount 54 can comprise a ceramic material such as alumina, aluminum nitride, silicon carbide, or a polymeric material such as polymide and polyester. In the preferred embodiment, the submount 54 can comprise a dielectric material having a relatively high thermal conductivity, such as aluminum nitride and alumina. In other embodiments the submount 54 can comprise a printed circuit board (PCB), sapphire or silicon or any other suitable material, such as T-Clad thermal clad insulated substrate material, available from The Bergquist Company of Chanhassen, Minn. For PCB embodiments different PCB types can be used such as standard FR-4 PCB, metal core PCB, or any other type of printed circuit board.
The top surface of the submount 54 is shown having a planar with patterned conductive features that can comprise first and second die attach pads 64a, 64b. A space is provided between the attach pads 64a, 64b, with the LED chips 52 mounted to the pads 64a, 64b such that respective portions of the LED chips 52 are mounted to a respective one of the pads 64a and 64b and the LED 52 spans the space between the attach pads 64a, 64b. Many different mounting methods can be used, such as methods utilizing conventional solder materials. Other types of LED chips can be electrically connected to the attach pads 64a, 64b or other conductive traces using known surface mount or wire bonding methods depending on the geometry of the LED 50.
The pads 64a, 64b can comprise many different materials, such as metals or other conductive materials, and in one embodiment they can comprise copper deposited using known techniques such as plating. In other embodiments pads 64a, 64b can be sputtered using a mask to form the desired pattern, and in other embodiments they can be formed using known photolithography processes. The pads 64a, 64b can extend beyond the edge of the LED chips 52 to cover most of the top surface of the submount 54. This helps in thermal management for the LED 50 by spreading heat from the LED chips 52 into the pads 64a, 64b so that heat spreads beyond the edge of the LED chips 52 into more area of the submount 54. This allows the heat to be less localized and allows it to more efficiently dissipate through the submount 54 into the ambient.
The LED 50 also comprises first and second solder pads 60a, 60b formed on the bottom surface of the submount 54, which can be used for mounting the LED package 52 in place using known mounting methods. It is understood that in other embodiments LEDs according to the present invention can have more than two solder pads. The solder pads 60a, 60b can be made of the same materials and can be formed of the same way as die attach pads 64a, 64b. First and second conductive vias 62a, 62b can be included that pass through the submount 54 with the vias being formed of an electrically conductive material such as those used for the die attach pads and solder pads, and are arranged to provide an electrically conductive path between the solder pads 60a, 60b and the die attach pads 64a, 64b. In the embodiment shown, first via 62a forms an electrically conductive path between the first solder pad 60a and the first die attach pad 64a, while second via 62b provides a conductive path between the second solder pad 60b and the second die attach pad 64b. This allows an electrical signal applied to the solder pads 60a, 60b to be conducted through the submount 54 along the vias 62a, 62b, to the die attach pads 64a, 64b. The signal is then conducted to the LED chips 52 through the die attach pads. It is understood that in other embodiments the electrical signal can be transmitted to the LED in other ways such as through conductive traces or wire bond pads arranged in different locations in the LED package, and running between the mounting surface or the submount, and the LED.
The LEDs 50 also comprises a polarity indicator 66 in one of the solder pads that can take many different shapes and can comprise a V-shaped notch along an edge of a solder. This polarity indicator 66 can be detected with up-looking cameras on automated pick-and-place equipment during manufacturing. The indicator 66 can be near the center of the pad's inner edge placing it near the center of the submount 54 in the area of the submount 54 that can be visible through hole in a carrier tape. This allows for the indicator 66 (and the corresponding LED package polarity) to be visible and verified carrier tape hole without removing the LED from the carrier tape.
The indicator 66 can have many different shapes beyond V-shaped, such as U-shaped, I-shaped, W-shaped, square shaped, rectangular shaped, star shaped, plus shaped, minus shaped, etc. The notch can also be included in many different locations on the solder pads 60a, 60b. It is noted that other types of polarity indicators can be used, such as holes of different shapes or other cutouts in the solder pads, and in other embodiments the LED packages can have indicators in other locations such as on the top surfaces of the LED 50. In the embodiment shown, the second attach pad 64b can have an indicator to show polarity when viewing the LED package 50 from the top. These indicators can take many different shapes and sizes such as those described above, and in some embodiments can comprise notches or holes as described above.
The conversion material layer 56 is included over the LEDs 52, exposed portions of the pads 64a and 64b, and exposed portions of the submount's top surface. As described in more detail below, the conversion material layer can comprise two or more conversion material layers, each of which has absorbs light from the LED chips 52 and reemits light in a different wavelength range.
Encapsulant 58 is included on the conversion material layer 56, and over the LED 52 and submount 54, with the encapsulant 58 providing environmental and mechanical protection. The encapsulant can take many different shapes and sizes, with some embodiments comprising a hemispheric encapsulant. In other embodiments, the encapsulant 58 can comprise planar surfaces, and in the embodiment shown the encapsulant 58 has a generally cubic shape. The encapsulant includes both vertical and horizontal planar surfaces in the shape of a cube, but it is understood that the encapsulant can take many different shapes such as any shape having a flat top and vertical sidewalls with planar surfaces. These can include but are not limited to different prismatic or polygon shapes such as triangles, pentagons, hexagons, octagons, etc. These shapes can include a horizontal planar surface, with vertical surfaces numbering in the range of 3 to 12 or more. In still other embodiments, the encapsulant can be cylindrical with different cross sections such as circular or oval. Encapsulants with planar surfaces and their advantages are fully described in U.S. patent application Ser. No. 13/649,052, to Lowes et al., which is incorporated herein by reference.
Many different materials can be used for the encapsulant 58 such as silicones, plastics, epoxies or glass, with a suitable material being compatible with molding processes. Silicone is suitable for molding and provides suitable optical transmission properties. It can also withstand subsequent reflow processes and does not significantly degrade over time. The encapsulant can also be formed using many different methods, and in some embodiments a molding process (described in more detail below) can be used that simultaneously forms encapsulants 58 over a multitude of LEDs 52 on a submount panel.
The conversion material layer 56 can also comprise a binder, and different materials can be used for the binder, with materials preferably being robust after curing and substantially transparent in the visible wavelength spectrum. Suitable materials include silicones, epoxies, glass, inorganic glass, dielectrics, BCB, polymides, polymers and hybrids thereof, with the preferred material being silicone because of its high transparency and reliability in high power LEDs. Suitable phenyl- and methyl-based silicones are commercially available from Dow® Chemical. The binder can be cured using many different curing methods depending on different factors such as the type of binder used. Different curing methods include but are not limited to heat, ultraviolet (UV), infrared (IR) or air curing. It is understood, however, that the phosphor particles can be applied without a binder.
For LED 50, the conversion material layer 56 comprises multiple layers having different conversion materials. The different embodiments can have a conversion material layer that comprise multiple layers with at least one layer below the top layer having an emission (or reemission) spectrum that is substantially outside the excitation spectrum of the top layer. This allows for light from the layer below to pass through the top without being substantially absorbed. This can increase the overall emission efficiency of the LED compared to LEDs with mixed phosphors. This also allows for light from the top layer to emit without most of the light passing back into the lower layer where it might be reabsorbed.
For example, the conversion material layer can comprise a bi-layer arrangement having a first layer 56a that absorbs light from the LED chips 52 and reemits light in the red wavelength spectrum. The conversion material layer 56 can also comprise a second layer 56b that absorbs light from the LED chips 52 and reemits light in the yellow/green wavelength spectrum. It is understood that in some embodiments each of the layers 56a, 56b can comprise more than one conversion material type to generate the desired reemission wavelength. For example, the layer reemitting red can have more than one type of conversion material reemitting in the red spectrum. As described below, many different conversion materials can be used to generate the desired LED package light emission, with the present invention being particularly adapted to LED packages emitting white light.
Graph 80 also shows excitation region A of the green/yellow phosphor and excitation region B of the red phosphor. The emission spectrum 81 of the LED chips may fall within a green/yellow phosphor excitation region A, which generates the emission spectrum 83. That is, the phosphor that emits light having the emission spectrum 82 (i.e. the green/yellow phosphor) can be responsive to light having a wavelength within the excitation region A. The emission spectrum 81 of the LED chips may also fall within a excitation region B of the red phosphor that generates the emission spectrum 83. That is, the phosphor that emits light having the emission spectrum 81 can be responsive to light having a wavelength within the excitation region B. It is understood excitation regions A and B illustrated in
The emission spectrum 82 of the green/yellow phosphor can at least partially fall within the excitation region B of the red phosphor. That is, some light that is emitted by the green/yellow phosphor can be re-absorbed by the red phosphor. Such re-absorption can lead to losses, as some energy is lost in every phosphor absorption/emission cycle. The re-absorption can also alter the color point of the combined light output by the structure. However, as further illustrated in
To reduce losses from re-absorption of emitted photons, to provide improved emission characteristics, and/or provide more consistent light output, some embodiments according to the present invention can separate the green/yellow phosphor from the red phosphor containing regions. For example, a green/yellow phosphor layer can be placed on the red phosphor layer so that light from the LED chip(s) passes through the red phosphor first. Un-absorbed blue light from the LED chip and red light generated in the red phosphor layer then pass through the green phosphor layer. However, primarily only the blue light from the LED chip is absorbed by the green/yellow to cause emission of green/yellow light thereby. The light from the red phosphor layer can pass through the green/yellow layer without being substantially absorbed.
The above example shown in
In LED 50, the conversion material layer arrangement provides for increased emission efficiency by minimizing or eliminating the cross absorption of emitted light from the conversion materials. By separating the phosphors in a layer arrangement, as described above, instead of conventional mixing of the phosphors, the reabsorbs ion by an conversion material layer 56b of the emitted light of the lower phosphor layer 56a can be reduced or eliminated. In the case of a green/yellow conversion layer on a red conversion layer, the reabsorption of light from the green/yellow layer by the red conversion layer can be reduced or eliminated. This reabsorption can be further minimized by providing separation between the green/yellow layer and the red layer.
The conversion material layer can be applied using different processes including but not limited to spraying, dispensing, spin coating, sputtering, printing, powder coating, electrophoretic deposition (EPD), and electrostatic deposition, among others. These processes can also include a solvent in the phosphor-binder mixture that can liquefy and lower the viscosity of the mixture. Many different solvents can be used including but not limited to toluene, benzene, zylene, or OS-20 commercially available from Dow Corning®, and different concentration of the solvent can be used. When the solvent-phosphor-binder mixture is sprayed, poured or dispersed heat from the remote phosphor evaporates the solvent and can also cure the binder in the mixture leaving a fixed phosphor layer. Various deposition methods and systems are described in U.S. Patent Application Publication No. 2010/0155763, to Donofrio et al., entitled “Systems and Methods for Application of Optical Materials to Optical Elements,” and also assigned to Cree, Inc.
In LED 50, the first layer 56a is deposited such that is blanket covers the LED chips 52, the top surface of the submount 54 and the pads 64a, 64b. The second layer 56b can then be deposited so that it covers the first layer 56a, thereby providing a bi-layer blanket coverage over the LEDs 52 submount 54 and pads 64a, 64b. LED chip light and converted light from the conversion material layer can emit toward the surface of the encapsulant 58. Some of this light will be reflected at the surface of the encapsulant by total internal reflection (TIR), and can be directed back toward the submount 54. This TIR light will encounter the blanket coverage conversion material layers 56a, 56b where the conversion material can again absorb and reemit at least some of the light. Without this blanked coverage, at least some of the TIR light would be absorbed at the submounts 54 or the pads 64a, 64b. The absorption and reemission of the TIR light can increase the chances that this light will escape from the encapsulant to contribute to LED emission; thereby increasing overall LED emission efficiency. This is referred to as photon recycling as fully described in U.S. patent application Ser. No. 13/649,052, incorporated above.
Different embodiments can comprise other elements arranged to increase emission efficiency. In some embodiments a reflective layer can be arranged in different locations and in different ways in LED packages according to the present invention. In some embodiments the reflective layer can be on the same surface of the submount having the LED chips. The reflective layer can at least partially surround the LED chips, and can cover the surface of the submount. In some embodiments, this surface of the submount can comprise the exposed surfaces of the die attach pads around the LED chips, the top surface of the submount around the LED chips and/or any electrostatic discharge (ESD) chip. In other embodiments where the conversion material layer covers the attach pads and submount, this reflective layer can be on the conversion material layer with the conversion material between the reflective layer and the submount. In still other embodiments, the conversion material layer can be on the reflective layer, with the reflective layer between the conversion material layer and the submount. In still other embodiments, the reflective layer can cover only selective portions of the submount, on selective ones of the die attach pads, wirebonds and any ESD chip. This type of reflective layer and its advantages are generally described in U.S. patent application Ser. No. 14/183,218 to Reiherzer et al., which is incorporated herein by reference.
It is understood that in some embodiments, the bi-layer conversion material 56a, 56b can cover less than all of the top surface of the submount 54 and pads 64a, 64b. In some embodiments the bi-layer conversion material 56a, 56b can cover only the LED chips 52. In still other embodiments different ones of the bi-layers can cover different areas. For example, in some embodiments the first layer 56a can cover only the LED chips 52, while the second layer 56b can cover the LED chips and all or part of the top surface of the submount 54 and pads 64a, 64b. This arrangement still allows for the advantages of photon recycling as described above. These are only some of the many different conversion material coverages that can be used in different LED embodiments according to the present invention.
It is understood that in different embodiments intervening layers not having conversion materials can be included between the multiple conversion material layers. In some embodiments, these intervening layers can be substantially transparent and can be arranged to provide separation between different ones of the layers, to reduce emission or light from the different layers passing into others of the layers to further reduce reabsorption. The intervening layer(s) can also include materials to assist in scattering of the light from the LED. In some embodiments the intervening layers can comprise scattering particles or can be shaped or textured to assist in light scattering.
In some embodiments, the emission efficiency (or luminous flux measured in lumens per watt (LPW)) increase for LEDs according to the present invention with separated phosphors compared to the same LEDs with mixed phosphors, can be more than 20%. In other embodiments it can be greater than 10%, while in still other embodiments it can be greater than or approximately equal to 5%. In still other embodiments it can be in the range of 2-10%. For the embodiment shown in
The layering approach also provides further advantages such as achieving the same target emission characteristics in LED packages according to the present invention, while allowing for reduced amount of red phosphor in comparison to conventional LED chips with mixed phosphors. This can be particularly important in reducing costs based on the higher relative cost of red phosphors. In some embodiments, the same color (as measured by bin) can be achieved at the same color rendering index (CRI), using significantly less red phosphor. In some embodiments, the reduction in red phosphor compared to the same LED with mixed phosphors can be as high as approximately 75%. In other embodiments it can be as high as 50%, while in still other embodiments it can at high as 25%.
As mentioned above, different LED embodiments can have discrete conversion material layers emitting in a particular spectrum, such as one layer in yellow/green and the other in red. These discrete layers can comprise more than one phosphor type to tune the conversion material layer to provide the desired LED emission characteristics. In some embodiments the yellow/green layer can have two or more different types of yellow/green emitting phosphors and the red layer can have two different or more different red phosphors.
The second layer can comprise yellow and green emitting phosphors, with some embodiments comprising a Y3Al5O12:Ce yellow emitting phosphor and a Lu3-xCexAl5O12,Y (Y=Halide) green emitting phosphor. Green and yellow phosphors generally have peak emission wavelengths in the range of 495-590 nm with green typically having a peak emission in the lower portion of this range and yellow having a peak emission in the higher end of this range. In some embodiments, the green and yellow phosphors emit peak emission wavelengths in the range of 520-580 nm with FWHM in the range of 100-130 nm. In some of these embodiments, the yellow emitting phosphor can have a peak emission wavelength of approximately 560 nm and a FWHM of approximately 115 nm. The green emitting phosphor can have a peak emission of approximately 534 nm and a FWHM of approximately 110 nm. It is understood that in other embodiments other phosphors can be used with other characteristics, and each of these phosphors can be provided in discrete layers such that the LED could have four phosphor layers. In these embodiments the two red phosphor layers can be closest to the LED chips. In still other embodiments, some of the phosphors can be mixed in a layer while others can be provided in discrete layers.
In the embodiment shown, the table 90 compares the amount of phosphors necessary in a two layer verses mixed conversion material to achieve target color point in for example the E8 bin, with a CRI of 90 (the LED chips can emit a blue dominant light with a wavelength of 450 and 456 nm). In this embodiment, the bi-layer approach allows for these same emission characteristics as a mixed approach, while allowing for a reduction in red phosphors. In this embodiment, the bi-layer approach the phosphor Red2 can experience a decrease of approximately 25% ratio of the overall red phosphor mixture, and more importantly can experience a reduction of greater than 70% by weight compared to the mixed phosphor approach. The phosphor Red1 can experience an increase in its overall ratio of the red phosphor mixture, but can also experience greater than 20% reduction by weight compared to the mixed layer approach. This can result in significant cost reductions for the LED chip. It is noted that the bi-layer embodiments according to the present invention can also require more yellow and green phosphor, and can require more silicone for encapsulant. These increases can be acceptable based on the relatively low cost of yellow/green phosphors and silicone, and the significant cost of red phosphors.
The different amounts of red and yellow/green bi-layer phosphor approach also result in differences in phosphor ratios of the four phosphor approach compared to the conventional mixed approach.
It is understood that others characteristics of LEDs can also vary when comparing bi-layer conversion material embodiments to conventional mixed conversion material embodiments. For example, the mixed embodiments can experience a greater drop off in emission at increased operating temperature compared to the bi-layer approach.
The above embodiments are only some of the different LED chips and materials that can be used in embodiments according to the present invention. The LED chips can emit light in spectrums other than blue and UV wavelength spectrums. The conversion material layers can comprise many different materials beyond those described above. In some embodiments, the phosphor particles comprise many different compositions and phosphor materials alone or in combination. In one embodiment the single crystalline phosphor can comprise yttrium aluminum garnet (YAG, with chemical formula Y3Al5O12). The YAG host can be combined with other compounds to achieve the desired emission wavelength. In one embodiment where the single crystalline phosphor absorbs blue light and reemits yellow, the single crystalline phosphor can comprise YAG:Ce. This embodiment is particularly applicable to light emitters that emit a white light combination of blue and yellow light. A full range of broad yellow spectral emission is possible using conversion particles made of phosphors based on the (Gd,Y)3(Al,Ga)5O12:Ce system, which include Y3Al5O12:Ce (YAG). Other yellow phosphors that can be used for white emitting LED chips include:
Tb3-xRexO12:Ce (TAG);
RE=Y, Gd, La, Lu; and/or
Sr2-yBaxCaySiO4:Eu.
In other embodiments, other compounds can be used with a YAG host for absorption and re-emission of different wavelengths of light. For example, a YAG:Nb single crystal phosphor can be provided to absorb blue light and reemit red light. First and second phosphors can also be combined for higher CRI white (i.e., warm white) with the yellow phosphors above combined with red phosphors. Various red phosphors can be used including:
SrxCa1-xS:Eu,Y; Y=halide;
CaSiAlN3:Eu; orSr2-yCaySiO4:Eu.
Other phosphors can be used to create saturated color emission by converting substantially all light to a particular color. For example, the following phosphors can be used to generate great saturated light:
SrGa2S4:Eu;
Sr2-yBaySiO4:Eu; or
SrSi2O2N2:Eu.
The following lists some additional suitable phosphors that can be used as conversion particles, although others can be used. Each exhibits excitation in the blue and/or UV emission spectrum, provides a desirable peak emission, has efficient light conversion:
Yellow/Green(Sr,Ca,Ba) (Al,Ga)2S4: Eu2+
Ba2(Mg,Zn) Si2O7Eu2+
Gd0.46Sr0.31Al1.23OxF1.38:Eu2+0.6
(Ba1-x-ySrxCay) SiO4:Eu
Ba2SiO4=Eu2+
Lu2O3=Eu3+
(Sr2-xLax)(Cei—xEux)O4
Sr2C1-xEuxO4
SrTiO3:Pr3+, GA3+
CaAlSiN3IEu2+
Sr2Si5N8=Eu2+
In some embodiments, the layer comprising luminophoric material, the optical coupling layer and/or the optically transparent structure may also provide a functional layer which comprises a light scattering layer, which comprises a binder material as discussed above and light scattering particles, for example titanium oxide particles. In other embodiments, the layer comprises materials to alter the refractive index of the functional layer. In some embodiments, the functional layer comprises a combination of one or more of the types of functional layers described herein (e.g. a wavelength conversion layer and a scattering or refractive index altering layer).
In some embodiments, the LED die is configured to emit blue light, for example light having a dominant wavelength of about 450-460 nm, and the phosphor layer comprises yellow phosphor, such as YAG:Ce phosphor, having a peak wavelength of about 550 nm. In other embodiments, the LED die is configured to emit blue light, and the phosphor layer may comprise a mixture of yellow phosphor and red phosphor, such CASN-based phosphor. In still other embodiments, the LED die is configured to emit blue, and the phosphor layer may comprise a mixture of yellow phosphor, red phosphor and green phosphor, such as LuAG: Ce phosphor particles. Moreover, various combinations and subcombinations of these and/or other colors and/or types of phosphors may be used in mixtures and/or in separate layers.
Alternate wavelength conversion materials may also be used to down-convert light to generate white emissions. Such materials may be, but are not limited to organic fluorescent materials or dyes or inorganic quantum dot materials such as CdSe/ZnS, InP/InAs, CdS/CdSe, CdTe/CdSe or others.
The conversion material can comprise different sized phosphor particles including but not limited to particles in the range of 10 nanometers (nm) to 30 micrometers (μm), or larger. Smaller particle sizes typically scatter and mix colors better than larger sized particles to provide a more uniform light. Larger particles are typically more efficient at converting light compared to smaller particles, but emit a less uniform light.
The conversion material layer 56 can have many different thicknesses depending at least partially on the concentration of conversion material, the size of the conversion material particles, and the desired amount of light to be converted by the conversion material. Conversion material layer according to the present invention can be in a binder with phosphor concentration levels (phosphor loading) above 30%. Other embodiments can have concentration levels above 50%, while in still others the concentration level can be above 60%.
The LEDs according to the present invention can have many different relative thicknesses, with some embodiments comprising a first layer that is closest to the LED chip having the longest emission wavelength of the LED's phosphors. The second layer moving away from the LED chip(s) can be thicker and can have a smaller emission wavelength than the first layer. Additional layers moving away from the LED chip can be thicker and/or can have smaller emission wavelengths than the layers below. In some embodiments the layers can become progressively thicker moving away from the LED chip, while in other embodiments the layers need only be thicker than the first layer. Likewise, in some embodiment the emission wavelengths of the layers can become progressively smaller moving away from the LED chip, with in other embodiments the emission wavelengths need only be smaller than the first layer's emission wavelength.
For LED 50, the bi-layer conversion material layer can have an overall thickness in the range of 50-500 μm, with some embodiments having an overall in the range of 75-300 μm and others having an overall thickness in the range of 100-200 μm. Thickness may also vary across the layer, with different regions having different thicknesses. The first conversion material layer 56a can be different percentages of the overall thickness of the conversion material layer. In some embodiments, the first layer 56a can comprise 5-30% of the overall thickness of the conversion material layer, while in other embodiments it can comprise 10-20% of the overall layer thickness. When measuring the thickness of the layers over the LED chips (or LED chip in other embodiments) the first layer can have many different thicknesses, such as in the range of approximately 10-70 μm. Other embodiments having a thickness in the range of approximately 15-60 μm and still other embodiments a thickness in the range of approximately 20-50 μm. In some embodiments, the first layer over the LED chip can have a thickness greater than approximately 10 μm, while other embodiments can have thicknesses greater than approximately 20 μm. The thickness of the second layer over the LED chips can have a thickness in the range of approximately 40-400 μm, with other embodiments having a thickness in the range of approximately 75-300 μm. Still other embodiments can have a thickness in the range of approximately 90-250 μm. In some embodiments, the first layer can have a thickness greater than approximately 50 μm, while other embodiments can have a thickness greater than approximately 100 μm.
It is understood that these thicknesses and percentages can vary in different conversion material regions and that the conversion material layer can also have different regions in the respective layers with different concentrations of phosphor particles.
Different embodiments according to the present invention can provide the conversion material layers covering the LED chips in different ways. In some embodiments, the first red phosphor layer can comprise a substantial conformal coating over the LED chips, with the yellow/green conversion material layer covering the LED chips and filling gaps between the LEDs chips. In still other embodiments both layers can comprise a conformal coating or both layers can layer covering and substantially filling the gaps between adjacent LED chips.
It is understood that the different embodiments of the present invention can be arranged in many different ways beyond the embodiment shown above. By way of example, other embodiments can have different numbers of LED chips coupled to solder pads and die attach pads in different ways, different encapsulants, different conversion material layers, and without submounts.
Like the embodiment above, the conversion material layer 156 can comprise a bi-layer conversional material layer blanket covering the exposed top surfaces of the submount 154, die attach pads and the LED chips 152. The bi-layer conversion material layer 156 can be made of many of the same materials and deposited in the same manner as the conversion material layers above. Like the embodiments above, the conversion material layer 156 can comprise a first layer 156a that absorbs LED chip light and emits in the red spectrum, and a second layer 156b that absorbs LED chip light and emits light in the yellow/green wavelength spectrum. The LED chips can emit many different colors of light, and in some embodiments some of the LED chips can emit different colors of light than the others of the LED chips. In one embodiment, the LED chips 152 can emit blue light, with the LED 150 emitting a white light combination of LED chip light and conversion material light.
The bi-layer conversion material arrangement in LED 150 can provide the advantages discussed above in regards to LED 150, including but not limited to reduced red phosphor, tuning capabilities based on higher CRI, and different bi-layer recipes. In this embodiment, the first red layer 156a forms a relatively thin layer that conformally coats over the LED chips 152. The yellow/green layer 156b is relatively thick and also covers the LED chips 152 and can be thick enough to fill the space between adjacent ones of the LED chips 152. The resulting conversion material layer 156 can comprise a relatively smooth top surface, with the LED chips embedded in the conversion material layer 156. The conversion material layer 156 in LED 150 can have many different thicknesses, with the first layer 156a being different percentages of the overall layer thickness. In some embodiments, the conversion material layer can be in the range of 50-500 μm, with the layer generally being thinner over the top of the LED chips 152 and thicker between and around the LED chips 152. In some embodiments, the conversion material layer can have a thickness in the range of 100-250 μm. The thickness of the first layer 156a can be in range of 10-40% of the overall thickness of the conversion material layer 156. In still other embodiments it can be approximately 20-35% of the overall thickness. Some LED embodiments can comprise a first conversion material layer having a thickness less than 200 μm, and a second conversion layer having a thickness greater than the first conversion material layer and less than 300 μm.
The LED 150 can also comprise an encapsulant 158 made of the same materials as the encapsulant 58 in LED 50 described above. In LED 150, however, the encapsulant has a generally hemispheric shape. It is understood that many different encapsulants can be used in this embodiment, including those with planar surfaces.
The transparent substrate 206 may include angled sidewalls and in some embodiments, the sidewalls may be stepped, beveled and/or faceted. Non-oblique sidewalls and approximately equal size faces may also be provided in other embodiments. For example, a square or rectangular chip with straight or non-oblique sidewalls may also be used in some embodiments. The LED 200 also comprises a reflective layer 208, which can below the bottom surface of the LED chip 202. In some embodiments, this may also comprise a submount or any other feature.
A conversion material layer 210 is provided over the LED chip 202 and the reflective layer reflective layer. It is understood that the phosphor layer can be arranged in any of the ways described above, and in the embodiment shown comprises a bi-layer conversion material layer, with a first layer 210a on the LED chip 202 and a second layer 210b on the first layer 210a. The layers can comprise different conversion materials or phosphors as described above, with the embodiment shown having first layer 210a with a red phosphor and a second layer 210b with a yellow/green phosphor. In some embodiments, the conversion material layer 210 can also comprise a light scattering material such as, for example, titanium oxide particles. In other embodiments, the layer comprises materials to alter the refractive index of the layer.
The LED 200 also comprises an outer transparent layer 212 that provides a primary optic and can comprise any of the encapsulant materials described above, and in the embodiment shown the layer 212 can comprise silicone. The transparent layer 212 can be free of phosphors and may be shaped to provide a lens, dome and/or other optical components. The transparent layer 212 that is free of phosphor can also encapsulate the conversion material and/or the LED chip 202. In still other embodiments, the transparent layer may be provided on a phosphor layer that comprises phosphor particles that are non-uniformly dispersed therein. The device may further include an additional encapsulant or lens 214, which may be silicon or glass.
The bi-layer conversion material arrangement in LED 200 can comprise any of the materials described above that can be deposited using any of the methods described above. In LED 200, the bi-layer conversion material arrangement provides blanket coverage over the LED chip 202, with it is understood that one or both of the layers 210a, 210b can provide less than full blanket coverage as described above. The conversion material layer can have different thicknesses, with some embodiments having thicknesses in the range of 50-500 μm. Still other embodiments can have thicknesses in the range of 50-300 μm. The first layer 210a can comprise different percentages of the overall layer thickness, with some embodiments having a percentage in the range of 5-30%. In other embodiment, the first layer can comprise a percentage in the range of 8-15%.
The emission wavelength spectrum of the red phosphor layer can be outside of the excitation spectrum of the yellow/green phosphor so that it can pass through the yellow/green phosphor without being absorbed. By dispersing the yellow/green phosphor in the encapsulant, the likelihood of reemitted light from the yellow/green phosphor passing back into the red phosphor layer is reduced. This reduces the chance that the yellow/green light with be reabsorbed in the red layer.
It is understood that there can be many different layered and dispersed phosphor arrangements in other embodiments according to the present invention. There can be more than one phosphor layer over the LED chips used in conjunction with a dispersed phosphor. There can be one or more layers used in conjunction with an encapsulant having more than one dispersed phosphor. It is also understood that this layered/dispersed combination can be used in any of the different LED embodiments according to the present invention.
Other LED embodiments according to the present invention can also provide separation between the LED chips and the layered conversion material layer or can provide separation between ones of the layers in the layered conversion material layer.
A second conversion material layer 306 is also included on the top surface of the encapsulant that can comprise the materials described above and can be deposited using the methods described above. Like above, the conversion layer can be bi-layered with the first layer (closed to the LED chip) 306a comprising a phosphor that absorbs light from the LED chip 302 and reemits light in the red wavelength spectrum. A second layer 306b can be on the first layer 306a and can comprise a phosphor that absorbs LED chip light and emits light in the yellow/green spectrum. The LED 300 can emit the desired white light combination of LED chip light and light from the first and second layer 306a, 306b. It is understood that different embodiments of the present invention can comprise conversion material with more than two layers.
It is understood that these LED can be arranged in many different ways with the encapsulants, with other embodiments used with more than two layers arranged in different locations in the LED. Some can have more than one layer on the LED chip, on the top surface of the encapsulant, or can have one or more layers embedded within the encapsulant. Still other embodiments can have one or more phosphors dispersed in the encapsulant.
As mentioned above, different embodiments according to the present invention can use less than or more than four different phosphors arranged in different ways. In some embodiments, a bi-layer approach can use less than four, with some having one of the layers with two phosphors emitting in the red or yellow/green spectrum, with the other layer having one red phosphor or yellow/green phosphor. These embodiments utilize a total of three phosphors.
Other embodiments can utilize only two phosphors, with the first layer having one phosphor emitting in the red spectrum and the second layer having one phosphor emitting in the yellow/green spectrum. The two phosphors can be tailored to achieve the desired emission characteristics with fewer different phosphors. As described above, LEDs with single layer mixed phosphor deposition do not exhibit the same benefits according to the present invention compared to LEDs having first layer of single red phosphor and then a layer of a single yellow/green phosphor. A first, relatively thin layer of red phosphor can be applied first with an optical silicone, with the phosphor having a peak wavelength of ˜630 um. A thicker second layer of green phosphor having a peak wavelength of ˜539 can then be applied on the first layer. This combination can result in an LED that emits light in the E7 color region, with a CRI >90, CRI9 >40 and a brightness increase of approximately 15%, compared to the same LED with a single mixed layer of the same two phosphors. Other embodiments, the LED chip can experience a brightness increase of greater that approximately 10%. In other embodiments, the LED chip can experience a brightness increase of approximately 15% or more.
If the same red and green phosphors are used in an LED in a mixed single layer approach, the CRI of light emitted by the LED will not reach 90. Reaching a CRI of 90 in mixed layer LED can require 3 or 4 phosphors, with some utilixing one or more additional phosphors such as an additional red phosphor with a peak wavelength of ˜651 nm. Some embodiments can include other additional phosphors, such as one or more yellow and green phosphors. However, for some LEDs the addition of a yellow phosphor to the two red and one green phosphor combination may not significantly add to the LED's ability to reach emission with a CRI of 90. In these embodiments, two reds have the greatest impact on the ability of the LED chip to reach a CRI of 90 in a single mixed layer system, which can be one of the reasons that the mixed layer system emits a lower luminous flux.
Referring now to
Referring now to
The embodiments presented herein are meant to be exemplary. Embodiments of the present invention can comprise any combination of compatible features shown in the various figures, and these embodiments should not be limited to those expressly illustrated and discussed.
Although the present invention has been described in detail with reference to certain preferred configurations thereof, other versions are possible. Therefore, the spirit and scope of the invention should not be limited to the versions described above.
Claims
1. An LED, comprising:
- one or more of LED chips on a surface of a submount;
- a conversion material layer comprising two or more layers of different conversion materials, said conversion material layer covering said one or more LED chips and at least a portion of said submount around said LED chips; and
- an encapsulant over said LED chips and said submount.
2. The LED of claim 1, wherein said conversion material layer comprises a bi-layer conversion material layer.
3. The LED of claim 1, wherein said conversion material layer comprises a layer of red emitting phosphor and a layer of yellow/green emitting phosphor.
4. The LED of claim 3, wherein said red emitting phosphor is between said LED chips and said yellow/green emitting phosphor.
5. The LED of claim 3, wherein said red emitting phosphor layer is directly on said LED chips and said yellow/green emitting phosphor layer is directly on said red emitting phosphor layer.
6. The LED of claim 1, wherein there is separation between said LED chips and said conversion material layer.
7. The LED of claim 3, wherein there is separation between said red emitting phosphor layer and said yellow/green emitting phosphor layer.
8. The LED of claim 1, wherein said conversion material layer blanket covers substantially all of the surface of said submount with said LED chips.
9. The LED of claim 1, wherein one of said two or more conversion material layers below the top one of said layers emits a wavelength of light that does not substantially overlap with the excitation spectrum of one of the layers above it.
10. The LED of claim 1, wherein the said two or more conversion material layers are arranged on one another with the emission wavelength of one of the conversion material layers below the top one of said layers is longer than the emission wavelength of the top one of said layers.
11. The LED of claim 1, wherein one of the conversion material layers below the top one of said layers conforms to said one or more LED chips.
12. The LED of claim 1, wherein said two or more conversion material layers conform to said one or more LED chips.
13. The LED of claim 1, further comprising a reflective layer between said two or more conversion material layers and said submount.
14. The LED of claim 1, wherein said two or more conversion material layers comprises a red phosphor layer below a yellow/green phosphor layer.
15. The LED of claim 14, wherein the emission spectrum of said red phosphor layer does not substantially overlap with the excitation spectrum of said yellow/green phosphor layer.
16. The LED of claim 14, wherein less emitted light from said yellow/green phosphor layer passes through a red phosphor compared to the same LED comprising a conversion material layer with mixed red and yellow/green phosphors.
17. The LED of claim 14, wherein less emitted light from said yellow/green phosphor layer is absorbed by said red phosphor layer compared to the same LED comprising a conversion material with mixed red and yellow/green phosphors.
18. The LED of claim 14, utilizing less red phosphor than the same LED with mixed red and yellow/green phosphor, to emit at the color point and color rendering index (CRI).
19. The LED of claim 14, emitting light at a higher CRI compared to an LED with the same amount of red and yellow phosphors mixed in a conversion material layer.
20. The LED of claim 14, utilizing a lower wavelength emitting red phosphor compared to the same LED with mixed red and yellow/green phosphors, to emit at the same color point at and CRI.
21. The LED of claim 14, exhibiting a lower reduction in emission efficiency over a temperature range compared to the same LED with mixed red and yellow/green phosphors.
22. The LED of claim 1, wherein said encapsulant comprises planar surfaces.
23. The LED of claim 1, wherein said encapsulant is hemispheric.
24. An LED, comprising:
- an LED chip;
- a conversion material layer comprising two or more layers of different conversion materials, said conversion material layer covering said LED chip and the area around said LED chip, wherein said LED produces improved emission characteristics compared to the same LED having a conversion material layer with mixed conversion materials.
25. The LED of claim 24, further comprising an encapsulant over said LED chips and said submount.
26. The LED of claim 24, wherein one of said two or more conversion material layers below the top one of said layers emits a wavelength of light that does not substantially overlap with the excitation spectrum of one of the layers above it.
27. The LED of claim 24, wherein said two or more conversion material layers comprises a red phosphor layer below a yellow/green phosphor layer.
28. The LED of claim 27, wherein the emission spectrum of said red phosphor layer does not substantially overlap with the excitation spectrum of said yellow/green phosphor layer.
29. The LED of claim 24, wherein less emitted light from the top one of said conversion layers passes through a layer below compared to the same LED comprising one conversion material layer with mixed conversion materials.
30. The LED of claim 24, wherein less emitted light from the top one of said conversion material layers is absorbed by a layer below compared to the same LED comprising a conversion material layer with mixed red and yellow/green phosphors.
31. The LED of claim 24, comprising less red phosphor than the same LED with mixed red and yellow/green phosphor, to emit at the same color point and color rendering index (CRI).
32. The LED of claim 24, emitting light at a higher CRI compared to an LED with the same amount of red and yellow phosphors mixed in a conversion material layer.
33. The LED of claim 24, comprising a lower wavelength emitting red phosphor compared to the same LED with mixed red and yellow/green phosphors, to emit at the same color point and CRI.
34. The LED of claim 24, exhibiting a lower reduction in emission efficiency over a temperature range compared to the same LED with mixed red and yellow/green phosphors.
35. An LED, comprising:
- one or more LED chips;
- a first conversion material layer having a thickness less than 200 μm; and
- a second conversion layer having a thickness greater than the first conversion material layer and less than 300 μm.
36. The LED of claim 35, wherein one of said two or more conversion material layers below the top one of said layers emits a wavelength of light that does not substantially overlap with the excitation spectrum of one of the layers above it.
37. The LED of claim 35, wherein said two or more conversion material layers comprises a red phosphor layer below a yellow/green phosphor layer.
38. The LED of claim 37, wherein said red phosphor layer emits light with a peak wavelength in the range of 620-670 nm.
39. The LED of claim 37, wherein said red phosphor layer emits light with a emission pattern having a full width at half maximum in the range of approximately 70-100 nm.
40. The LED of claim 37, wherein said yellow/green phosphor layer emits light with a peak wavelength in the range of 520-580 nm.
41. The LED of claim 37, wherein said yellow/green phosphor layer emits light with a emission pattern having a full width at half maximum in the range of approximately 100-130 nm.
42. An LED, comprising:
- one or more LED chips;
- a first conversion material layer and a second conversion material layer different from and on said first conversion material layer, wherein the overall thickness of said first and second conversion material layers is less than 500 μm, and where the first conversion material layer thickness is no greater than 40% of said overall thickness.
43. An LED, comprising:
- one or more LED chips;
- a first conversion material layer on said LED chips; and
- a second conversion material layer on said first conversion material layer, said second conversion material layer being thicker than said first conversion material layer and having an emission wavelength shorter than said first conversion material layer.
44. The LED of claim 43, wherein said first conversion material layer has an emission wavelength longer than all other conversion material layers.
45. The LED chip of claim 43, comprising one or more subsequent conversion material layers on said second conversion material layer, each of which is thicker than said first conversion material layer.
46. The LED chip of claim 43, comprising one or more subsequent conversion material layers on said second conversion material layer, each of which having smaller emission wavelengths than the layers below.
Type: Application
Filed: Aug 6, 2014
Publication Date: Nov 25, 2021
Patent Grant number: 11251164
Inventors: FAN ZHANG (Goleta, CA), James IBBETSON (Santa Barbara, CA), Bernd KELLER (Santa Barbara, CA), Theodore LOWES (Lompoc, CA), Antony VAN DE VEN (Sai Kung), Deborah KIRCHER (Santa Barbara, CA), Tao Feng GILBERT (Goleta, CA), Peter Andrews (Durham, NC)
Application Number: 14/453,482