Abstract

A method of a hydrocarbon product and ammonia comprises introducing C2H6 to a positive electrode of an electrochemical cell comprising the positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The proton-conducting membrane comprising an electrolyte material having an ionic conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 600° C. N2 is introduced to the negative electrode of the electrochemical cell. A potential difference is applied between the positive electrode and the negative electrode of the electrochemical cell. A system for co-producing higher hydrocarbons and NH3, and an electrochemical cell are also described.

Description

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional of U.S. patent application Ser. No. 16/532,276, filed Aug. 5, 2019, which claims the benefit under 35 U.S.C. § 119(e) of U.S. Provisional Patent Application Ser. No. 62/715,159, filed Aug. 6, 2018, the disclosure of each of which is hereby incorporated herein in its entirety by this reference.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

This invention was made with government support under Contract Number DE-AC07-05ID14517 awarded by the United States Department of Energy. The government has certain rights in the invention.

TECHNICAL FIELD

The disclosure, in various embodiments, relates to methods and systems for co-producing hydrocarbon products and ammonia through electrochemical activation of ethane, and to associated electrochemical cells.

BACKGROUND

Large reserves of natural gas continue to be discovered throughout the world, and have resulted in surpluses of ethane (C₂H₆) (i.e., the second major constituent of natural gas after methane (CH₄)). C₂H₆is predominantly used to form ethylene (C₂H₄), a chemical feedstock for plastics (e.g., polyethylene) manufacturing, through conventional stream cracking processes. However, conventional stream cracking processes to convert C₂H₆to C₂H₄can require high temperatures (e.g., temperatures greater than or equal to about 850° C.) to activate C₂H₆, resulting in undesirable energy expenditures (e.g., thermal energy expenditures) and/or environmental impacts (e.g., greenhouse gas emissions effectuated by the energy needs of the stream cracking processes). Moreover, conventional stream cracking processes can require the use of complicated and costly systems and methods to purify (e.g., refine) the resulting ethylene product.

Ammonia (NH₃) is also a valued compound finding use in a wide variety of commercial and industrial applications. For example, NH₃is commonly used as a precursor to various food, fertilizer, pharmaceutical, and cleaning products. However, conventional methods of producing NH₃(e.g., the Haber-Bosch process) through nitrogen gas (N₂) hydrogenation are energy intensive, and can undesirably result in the production of significant amounts of greenhouse gases from combustion-based processes employed to generate the required energy.

It would be desirable to have new methods, systems, and apparatuses for synthesizing hydrocarbon products from C₂H₆. It would also be desirable if the new methods, systems, and apparatuses facilitated the production of hydrocarbons other than C₂H₄, and also facilitated the production (e.g., co-production) and isolation of NH₃. It would further be desirable if the new methods, systems, and apparatuses facilitated increased production efficiency, increased operational life, and were relatively inexpensive and simple in operation.

BRIEF SUMMARY

Embodiments described herein include methods, systems, and apparatuses for co-producing hydrocarbon products and NH₃through electrochemical activation of C₂H₆. In accordance with one embodiment described herein, a method of forming a hydrocarbon product and NH₃comprises introducing C₂H₆to a positive electrode of an electrochemical cell comprising the positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The proton-conducting membrane comprising an electrolyte material having an ionic conductivity greater than or equal to about 10⁻²S/cm at one or more temperatures within a range of from about 150° C. to about 600° C. N₂is introduced to the negative electrode of the electrochemical cell. A potential difference is applied between the positive electrode and the negative electrode of the electrochemical cell.

In additional embodiments, a system for co-producing hydrocarbon products and NH₃comprises a source of C₂H₆, a source of N₂, and an electrochemical apparatus in fluid communication with the source of C₂H₆and the source of N₂. The electrochemical apparatus comprises a housing structure, and an electrochemical cell within an internal chamber of the housing structure. The housing structure is configured and positioned to receive a C₂H₆stream from the source of C₂H₆and to receive a N₂stream from the source of N₂. The electrochemical cell comprises a positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The positive electrode comprising a catalyst material formulated to accelerate reaction rates to produce C₂H₄, H⁺, and e⁻ from C₂H₆, and to accelerate reaction rates to synthesize at least one hydrocarbon product from the produced C₂H₄. The negative electrode comprises another catalyst material formulated to accelerate reaction rates to produce NH₃from N₂, H⁺, and e⁻. The proton-conducting membrane comprises an electrolyte material having an ionic conductivity greater than or equal to about 10⁻²S/cm at one or more temperatures within a range of from about 150° C. to about 600° C.

In further embodiments, an electrochemical cell comprises a positive electrode, a negative electrode, and a proton-conducting membrane between the positive electrode and the negative electrode. The positive electrode comprises a first catalyst material formulated to accelerate to C₂H₆deprotonation reaction rates to produce C₂H₄, H⁺, and e⁻ from C₂H₆, and to accelerate coupling reaction rates to synthesize at least one hydrocarbon product from the produced C₂H₄. The negative electrode comprises a second catalyst material formulated to accelerate N₂protonation reaction rates to produce NH₃from N₂, H⁺, and e⁻. The proton-conducting membrane comprises an electrolyte material having an ionic conductivity greater than or equal to about 10⁻²S/cm at one or more temperatures within a range of from about 150° C. to about 600° C.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a simplified schematic view of a system for co-producing hydrocarbon products and NH₃, in accordance with an embodiment of the disclosure.

DETAILED DESCRIPTION

Methods and systems for co-producing hydrocarbon products and NH₃through electrochemical activation of C₂H₆are disclosed. In some embodiments, a method of co-producing a hydrocarbon product (e.g., butylene, gasoline, diesel, etc.) and NH₃comprises delivering C₂H₆and N₂to electrochemical apparatus including at least one electrochemical cell therein. The electrochemical cell includes a positive electrode (e.g., anode), a negative electrode (e.g., cathode), and a proton-conducting membrane between the positive electrode and the negative electrode. The positive electrode comprises at least one catalyst material formulated to accelerate to C₂H₆deprotonation reaction rates to produce C₂H₄, H⁺, and e⁻ from C₂H₆, and to accelerate ethyl coupling reaction rates to synthesize at least one hydrocarbon product from the produced C₂H₄. The negative electrode comprises at least one additional catalyst material formulated to accelerate N₂protonation reaction rates to produce NH₃from N₂, H⁺, and e⁻. The proton-conducting membrane comprises an electrolyte material having an ionic conductivity greater than or equal to about 10⁻²S/cm at one or more temperatures within a range of from about 150° C. to about 600° C. The C₂H₆is introduced to the positive electrode of the electrochemical cell, the N₂is introduced to the negative electrode of the electrochemical cell, and a potential difference is applied between the positive electrode and the negative electrode of the electrochemical cell to produce the hydrocarbon product and the NH₃. The methods, systems, and apparatuses of the disclosure may be more efficient (e.g., increasing higher hydrocarbon and NH₃production efficiency; reducing equipment, material, and/or energy requirements; etc.), more durable, and/or less complicated as compared to conventional methods, conventional systems, and conventional apparatuses for producing one or more of higher hydrocarbons and NH₃.

The following description provides specific details, such as material compositions and processing conditions (e.g., temperatures, pressures, flow rates, etc.) in order to provide a thorough description of embodiments of the disclosure. However, a person of ordinary skill in the art will understand that the embodiments of the disclosure may be practiced without necessarily employing these specific details. Indeed, the embodiments of the disclosure may be practiced in conjunction with conventional systems and methods employed in the industry. In addition, only those process components and acts necessary to understand the embodiments of the present disclosure are described in detail below. A person of ordinary skill in the art will understand that some process components (e.g., pipelines, line filters, valves, temperature detectors, flow detectors, pressure detectors, and the like) are inherently disclosed herein and that adding various conventional process components and acts would be in accord with the disclosure. In addition, the drawings accompanying the application are for illustrative purposes only, and are not meant to be actual views of any particular material, device, or system.

As used herein, the term “lower hydrocarbon” means and includes an aliphatic hydrocarbon having from one carbon atom to four carbon atoms (e.g., methane, ethane, ethylene, acetylene, propane, propylene, n-butane, isobutene, butane, isobutene, etc.).

As used herein, the terms “higher hydrocarbon” and “hydrocarbon product” mean and include an aliphatic or cyclic hydrocarbon having at least one more carbon atom than a lower hydrocarbon used to form the higher hydrocarbon.

As used herein, the term “cyclic hydrocarbon” means and includes at least one closed ring hydrocarbon, such as an alicyclic hydrocarbon, an aromatic hydrocarbon, or a combination thereof. The cyclic hydrocarbon may include only carbon and hydrogen, or may include carbon, hydrogen, and at least one heteroatom.

As used herein, the term “heteroatom” means and includes an element other than carbon and hydrogen, such as oxygen (O), nitrogen (N), or sulfur (S).

As used herein, the terms “catalyst material” and “catalyst” each mean and include a material formulated to promote one or more reactions, resulting in the formation of a product.

As used herein, the term “negative electrode” means and includes an electrode having a relatively lower electrode potential in an electrochemical cell (i.e., lower than the electrode potential in a positive electrode therein). Conversely, as used herein, the term “positive electrode” means and includes an electrode having a relatively higher electrode potential in an electrochemical cell (i.e., higher than the electrode potential in a negative electrode therein).

As used herein the term “electrolyte” means and includes an ionic conductor, which can be in a solid state, a liquid state, or a gas state (e.g., plasma).

As used herein, the term “compatible” means that a material does not undesirably react, decompose, or absorb another material, and also that the material does not undesirably impair the chemical and/or mechanical properties of the another material.

As used herein, spatially relative terms, such as “beneath,” “below,” “lower,” “bottom,” “above,” “upper,” “top,” “front,” “rear,” “left,” “right,” and the like, may be used for ease of description to describe one element's or feature's relationship to another element(s) or feature(s) as illustrated in the figures. Unless otherwise specified, the spatially relative terms are intended to encompass different orientations of the materials in addition to the orientation depicted in the figures. For example, if materials in the figures are inverted, elements described as “below” or “beneath” or “under” or “on bottom of” other elements or features would then be oriented “above” or “on top of” the other elements or features. Thus, the term “below” can encompass both an orientation of above and below, depending on the context in which the term is used, which will be evident to one of ordinary skill in the art. The materials may be otherwise oriented (e.g., rotated 90 degrees, inverted, flipped) and the spatially relative descriptors used herein interpreted accordingly.

As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

As used herein, “and/or” includes any and all combinations of one or more of the associated listed items.

As used herein, the term “configured” refers to a size, shape, material composition, material distribution, and arrangement of one or more of at least one structure and at least one apparatus facilitating operation of one or more of the structure and the apparatus in a pre-determined way.

As used herein, the term “substantially” in reference to a given parameter, property, or condition means and includes to a degree that one of ordinary skill in the art would understand that the given parameter, property, or condition is met with a degree of variance, such as within acceptable manufacturing tolerances. By way of example, depending on the particular parameter, property, or condition that is substantially met, the parameter, property, or condition may be at least 90.0% met, at least 95.0% met, at least 99.0% met, at least 99.9% met, or even 100.0% met.

As used herein, “about” or “approximately” in reference to a numerical value for a particular parameter is inclusive of the numerical value and a degree of variance from the numerical value that one of ordinary skill in the art would understand is within acceptable tolerances for the particular parameter. For example, “about” or “approximately” in reference to a numerical value may include additional numerical values within a range of from 90.0 percent to 110.0 percent of the numerical value, such as within a range of from 95.0 percent to 105.0 percent of the numerical value, within a range of from 97.5 percent to 102.5 percent of the numerical value, within a range of from 99.0 percent to 101.0 percent of the numerical value, within a range of from 99.5 percent to 100.5 percent of the numerical value, or within a range of from 99.9 percent to 100.1 percent of the numerical value.

An embodiment of the disclosure will now be described with reference to FIG. 1, which schematically illustrates a system 100 (e.g., C₂H₆activation system) for co-producing hydrocarbon products and NH₃. The system 100 may be used to convert C₂H₆and N₂into at least one higher hydrocarbon (e.g., butylene, gasoline, diesel, etc.) and NH₃. As shown in FIG. 1, the system 100 may include at least one C₂H₆source 102 (e.g., containment vessel), at least one N₂source 104 (e.g., containment vessel), and at least one electrochemical apparatus 106 in fluid communication with each of the C₂H₆source 102 and the N₂source 104. The electrochemical apparatus 106 includes a housing structure 108, and at least one electrochemical cell 110 contained within the housing structure 108. The electrochemical cell 110 is electrically connected (e.g., coupled) to a power source 118, and includes a positive electrode 112 (e.g., anode), a negative electrode 116 (e.g., cathode), and a proton-conducting membrane 114 between the positive electrode 112 and the negative electrode 116. As shown in FIG. 1, optionally, the system 100 may also include at least one heating apparatus 120 operatively associated with the electrochemical apparatus 106.

During use and operation, the system 100 directs a C₂H₆stream 122 into the electrochemical apparatus 106 to interact with the positive electrode 112 of the electrochemical cell 110. A potential difference (e.g., voltage) is applied between the positive electrode 112 and the negative electrode 116 of the electrochemical cell 110 by the power source 118 so that as the C₂H₆interacts with the positive electrode 112, H atoms of the C₂H₆release their electrons (e⁻) to generate ethylene (C₂H₄), hydrogen ions (H⁺) (i.e., protons), and electrons (e⁻) through non-oxidative deprotonation according to the following equation:

C₂H₆→C₂H₄+2H⁺+2e⁻ (1).

The generated H⁺ permeate (e.g., diffuse) across the proton-conducting membrane 114 to the negative electrode 116, the generated e⁻ are directed to the power source 118 through external circuitry. At the negative electrode 116, the generated H⁺ exiting the proton-conducting membrane 114 react with N₂delivered into the electrochemical apparatus 106 from an N₂stream 124 directed from the N₂source 104 and e received from the power source 118 in the presence of a catalyst material of the negative electrode 116 to produce NH₃, according to the following equation:

Unlike conventional methods (e.g., the Haber-Bosch process) of forming NH₃that react N₂with hydrogen gas (H₂), the system 100 directly reacts H⁺ with the N₂to form NH₃. Accordingly, the formation of NH₃at the negative electrode 116 is not constrained (e.g., limited) by the previous formation of H₂through a hydrogen evolution reaction (HER). In addition, the N₂reduction reaction occurs at reduced pressures (e.g., ambient pressure) relative to conventional catalytic hydrogenation methods. The produced NH₃exits the electrochemical apparatus 106 as a NH₃stream 126. At the positive electrode 112, the produced C₂H₄may undergo at least one ethyl coupling reaction (ECR) in the presence of a catalyst material of the positive electrode 112 to synthesize at least one hydrocarbon product (e.g., higher hydrocarbon), according to the following equation:

nC₂H₄→C_2nH_4n (2).

The hydrocarbon product may then exit the electrochemical apparatus 106 as a hydrocarbon product stream 128.

As described in further detail below, the hydrocarbon products synthesized at the positive electrode 112 and the production of NH₃at the negative electrode 116 may at least partially depend on the material compositions and flow rates of the C₂H₆stream 122 and the N₂stream 124; the configuration (e.g., size, shape, material composition, material distribution, arrangement) of the positive electrode 112, including the types, quantities, distribution, and properties (e.g., geometric properties, thermodynamic properties, etc.) of catalyst materials thereof promoting C₂H₆deprotonation reactions and/or ethyl coupling reactions; the configuration of the proton-conducting membrane 114, and the impact thereof on the diffusivity (e.g., diffusion rate) of generated H⁺ therethrough; the configuration of the negative electrode 116, including the types, quantities, and properties (e.g., geometric properties, thermodynamic properties, etc.) of catalyst materials thereof; and the operational parameters (e.g., temperatures, pressures, etc.) of the electrochemical apparatus 106. Such operational factors may be controlled (e.g., adjusted, maintained, etc.) as desired to control the types, quantities, and rate of production of the hydrocarbon product(s) synthesized at the positive electrode 112 and to control the quantity and rate of production of the NH₃produced at the negative electrode 116. In some embodiments, the hydrocarbon product(s) exiting the electrochemical apparatus 106 in the hydrocarbon product stream 128 may be examined (e.g., through in-line gas chromatography-mass spectrometry (GS-MS)) and compared to a mathematically modeled Anderson-Schulz-Flory distribution to analyze whether or not sufficient ethyl coupling reactions are occurring at the positive electrode 112 for the synthesis of one or more desired higher hydrocarbons. One or more operational factors of the system 100 (e.g., one or more of the type, quantity, and distribution of catalyst material(s) in the positive electrode 112, the operating temperature of the electrochemical apparatus 106, etc.) may be adjusted or maintained based on the results of the analysis. Accordingly, the operational factors of the system 100 may be tailored to facilitate the co-production of NH₃and one or more specific higher hydrocarbons from the components of the C₂H₆stream 122 and the N₂stream 124.

The C₂H₆stream 122 may be formed of and include C₂H₆. In addition, the C₂H₆stream 122 may, optionally, include one or more other materials (e.g., molecules), such as one or more other lower hydrocarbons (e.g., one or more other C₁to C₄hydrocarbons, such as one or more of CH₄, propane, and butane) that may undergo a chemical reaction in the presence of the positive electrode 112 of the electrochemical cell 110 to produce at least one higher hydrocarbon, and/or one or more other materials (e.g., H₂, N₂, etc.). In some embodiments, the C₂H₆stream 122 is substantially free of materials other than C₂H₆. In additional embodiments, the C₂H₆stream 122 includes C₂H₆and CH₄. The C₂H₆stream 122 may be substantially gaseous (e.g., may only include a single gaseous phase), may be substantially liquid (e.g., may only include a single liquid phase), or may include a combination of liquid and gaseous phases. The phase(s) of the C₂H₆stream 122 (and, hence, a temperature and a pressure of the C₂H₆stream 122) may at least partially depend on the operating temperature of the electrochemical cell 110 of the electrochemical apparatus 106. In some embodiments, the C₂H₆stream 122 is substantially gaseous.

A single (e.g., only one) C₂H₆stream 122 may be directed into the electrochemical apparatus 106 from the C₂H₆source 102, or multiple (e.g., more than one) C₂H₆streams 122 may be directed into the electrochemical apparatus 106 from the C₂H₆source 102. If multiple C₂H₆streams 122 are directed into the electrochemical apparatus 106, each of the multiple C₂H₆streams 122 may exhibit substantially the same properties (e.g., substantially the same material composition, substantially the same temperature, substantially the same pressure, substantially the same flow rate, etc.), or at least one of the multiple C₂H₆streams 122 may exhibit one or more different properties (e.g., a different material composition, a different temperature, a different pressure, a different flow rate, etc.) than at least one other of the multiple C₂H₆streams 122.

The N₂stream 124 entering the electrochemical apparatus 106 may be formed of and include N₂. The N₂may be present in the N₂stream 124 in one or more of gaseous phase and a liquid phase. The phase(s) of the N₂(and, hence, a temperature and a pressure of the N₂stream 124) may at least partially depend on the operating temperature of the electrochemical cell 110 of the electrochemical apparatus 106. For example, at operating temperatures less than or equal to about 250° C. (e.g., within a range of from about 150° C. to about 250° C.), the N₂may be present in the N₂stream 124 in a liquid phase, a gaseous phase, or combination thereof. As another example, at operating temperatures greater than about 250° C. (e.g., greater than about 250° C. and less than or equal to about 650°), the N₂may be present in the N₂stream 124 in a gaseous phase. The N₂stream 124 may only include N₂, or may include N₂and one or more other materials. In some embodiments, the N₂stream 124 is substantially free of materials other than N₂. One or more apparatuses (e.g., heat exchangers, pumps, compressors, expanders, mass flow control devices, etc.) may be employed within the system 100 to adjust the one or more of the temperature, pressure, and flow rate of the N₂stream 124 delivered into the electrochemical apparatus 106.

A single (e.g., only one) N₂stream 124 may be directed into the electrochemical apparatus 106, or multiple (e.g., more than one) N₂streams 124 may be directed into the electrochemical apparatus 106. If multiple N₂streams 124 are directed into the electrochemical apparatus 106, each of the multiple N₂streams 124 may exhibit substantially the same properties (e.g., substantially the same material composition, substantially the same temperature, substantially the same pressure, substantially the same flow rate, etc.), or at least one of the multiple N₂streams 124 may exhibit one or more different properties (e.g., a different material composition, a different temperature, a different pressure, a different flow rate, etc.) than at least one other of the multiple N₂streams 124.

The heating apparatus 120, if present, may comprise at least one apparatus (e.g., one or more of a combustion heater, an electrical resistance heater, an inductive heater, and an electromagnetic heater) configured and operated to heat one or more of the gaseous C₂H₆stream 122, the N₂stream 124, and at least a portion of the electrochemical apparatus 106 to an operating temperature of the electrochemical apparatus 106. The operating temperature of the electrochemical apparatus 106 may at least partially depend on a material composition of the proton-conducting membrane 114 of the electrochemical cell 110 thereof, as described in further detail below. In some embodiments, the heating apparatus 120 heats one or more of the C₂H₆stream 122, the N₂stream 124, and at least a portion of the electrochemical apparatus 106 to a temperature within a range of from about 150° C. to about 650° C. In additional embodiments, such as in embodiments wherein a temperature of the C₂H₆stream 122 is already within the operating temperature range of the electrochemical cell 110 of the electrochemical apparatus 106, the heating apparatus 120 may be omitted (e.g., absent) from the system 100.

With continued reference to FIG. 1, the electrochemical apparatus 106, including the housing structure 108 and the electrochemical cell 110 thereof, is configured and operated to form the NH₃stream 126 and the hydrocarbon product stream 128 from the C₂H₆stream 122 and the N₂stream 124 according to the reactions of Equations (1) through (3) above. The housing structure 108 may exhibit any shape (e.g., a tubular shape, a quadrilateral shape, a spherical shape, a semi-spherical shape, a cylindrical shape, a semi-cylindrical shape, truncated versions thereof, or an irregular shape) and size able to contain (e.g., hold) the electrochemical cell 110 therein, to receive and direct the C₂H₆stream 122 to the positive electrode 112 of the electrochemical cell 110, to direct the high hydrocarbon product(s) synthesized at the positive electrode 112 away from the electrochemical apparatus 106 as the hydrocarbon product stream 128, and to direct the NH₃formed at the negative electrode 116 of the electrochemical cell 110 away from the electrochemical apparatus 106 as the NH₃stream 126. In addition, the housing structure 108 may be formed of and include any material (e.g., glass, metal, alloy, polymer, ceramic, composite, combination thereof, etc.) compatible with the operating conditions (e.g., temperatures, pressures, etc.) of the electrochemical apparatus 106.

The housing structure 108 may at least partially define at least one internal chamber 130 at least partially surrounding the electrochemical cell 110. The electrochemical cell 110 may serve as a boundary between a first region 132 (e.g., an anodic region) of the internal chamber 130 configured and positioned to receive the C₂H₆stream 122 and to direct the hydrocarbon product stream 128 from the electrochemical apparatus 106, and a second region 134 (e.g., a cathodic region) of the internal chamber 130 configured and positioned to receive the NH₃produced at the negative electrode 116 of the electrochemical cell 110. Molecules (e.g., C₂H₆) of the C₂H₆stream 122 may be substantially limited to the first region 132 of the internal chamber 130 by the configurations and positions of the housing structure 108 and the electrochemical cell 110. Keeping the second region 134 of the internal chamber 130 substantially free of molecules from the C₂H₆stream 122 circumvents additional processing of the produced NH₃(e.g., to separate the produced NH₃from C₂H₆) that may otherwise be necessary if the components of the C₂H₆stream 122 were also delivered to within the second region 134 of the internal chamber 130.

As shown in FIG. 1, the positive electrode 112 and the negative electrode 116 of the electrochemical cell 110 are electrically coupled to the power source 118, and the proton-conducting membrane 114 is disposed on and between the positive electrode 112 and the negative electrode 116. The proton-conducting membrane 114 is configured and formulated to conduct H from the positive electrode 112 to the negative electrode 116, while electrically insulating the negative electrode 116 from the positive electrode 112 and preventing the migration of gaseous materials therethrough. Electrons generated at the positive electrode 112 through the reaction of Equation (1) described above may, for example, flow from the positive electrode 112 into a negative current collector, through the power source 118 and a positive electrode current collector, and into negative electrode 116 to facilitate the protonation of N₂at the negative electrode 116 to form NH₃through the reaction of Equation (2) described above.

The proton-conducting membrane 114 may be formed of and include at least one electrolyte material exhibiting an ionic conductivity (e.g., H conductivity) greater than or equal to about 10⁻²S/cm (e.g., within a range of from about 10⁻²S/cm to about 1 S/cm) at one or more temperatures within a range of from about 150° C. to about 650° C. (e.g., from about 200° C. to about 600° C., from about 300° C. to about 500° C.). In addition, the electrolyte material may be formulated to remain substantially adhered (e.g., laminated) to the positive electrode 112 and the negative electrode 116 at relatively high current densities, such as at current densities greater than or equal to about 0.1 amperes per square centimeter (A/cm²) (e.g., greater than or equal to about 0.5 A/cm², greater than or equal to about 1.0 A/cm², greater than or equal to about 2.0 A/cm², etc.). For example, the proton-conducting membrane 114 may comprise one or more of a perovskite material, a solid acid material, and a polybenzimidazole (PBI) material. The material composition of the proton-conducting membrane 114 may provide the proton-conducting membrane 114 with enhanced ionic conductivity at a temperature within the range of from about 150° C. to about 650° C. as compared to conventional membranes (e.g., membranes employing conventional electrolyte materials, such as yttria-stabilized zirconia (YSZ)) of conventional electrolysis cells. By way of non-limiting example, the electrolyte material (e.g., perovskite material, solid acid material, PBI material) of the proton-conducting membrane 114 may have orders of magnitude higher ionic conductivity than YSZ at operational temperatures thereof within the range of from about 150° C. to about 650° C.

In some embodiments, the proton-conducting membrane 114 is formed of and includes at least one perovskite material having an operational temperature (e.g., a temperature at which the H⁺ conductivity of the perovskite material is greater than or equal to about 102 S/cm, such as within a range of from about 10⁻²S/cm to about 10⁻¹S/cm) within a range of from about 350° C. to about 650° C. By way of non-limiting example, the proton-conducting membrane 114 may comprise one or more of a yttrium- and ytterbium-doped barium-zirconate-cerate (BZCYYb), such as BaZr_0.8−yCe_yY_0.2−xYb_xO_3−δ, wherein x and y are dopant levels and δ is the oxygen deficit (e.g., BaZr_0.3Ce_0.5Y_0.1Yb_0.1O₃₋₆); a yttrium- and ytterbium-doped barium-strontium-niobate (BSNYYb), such as Ba₃(Sr_1−xNb_2−yY_xYb_y)O_9−δ, wherein x and y are dopant levels and δ is the oxygen deficit; doped barium-cerate (BaCeO₃)(e.g., yttrium-doped BaCeO₃(BCY)); doped barium-zirconate (BaZrO₃)(e.g., yttrium-doped BaCeO₃(BZY)); barium-yttrium-stannate (Ba₂(YSn)O_5.5); and barium-calcium-niobate (Ba₃(CaNb₂)O₉). In some embodiments, the proton-conducting membrane 114 comprises BZCYYb.

In further embodiments, the proton-conducting membrane 114 is formed of and includes at least one solid acid material having an operational temperature (e.g., a temperature at which the H⁺ conductivity of the solid acid material is greater than or equal to about 10⁻²S/cm, such as within a range of from about 10⁻²S/cm to about 1 S/cm) within a range of from about 200° C. to about 400° C. By way of non-limiting example, the proton-conducting membrane 114 may comprise a solid acid phosphate material, such as solid acid cesium dihydrogen phosphate (CsH₂PO₄). The solid acid material may be doped (e.g., doped CsH₂PO₄), or may be undoped (e.g., undoped CsH₂PO₄). In some embodiments, the proton-conducting membrane 114 comprises CsH₂PO₄.

In additional embodiments, the proton-conducting membrane 114 is formed of and includes at least one PBI material having an operational temperature (e.g., a temperature at which the H⁺ conductivity of the PBI material is greater than or equal to about 10⁻²S/cm, such as within a range of from about 10⁻²S/cm to about 1 S/cm) within a range of from about 150° C. to about 250° C. By way of non-limiting example, the proton-conducting membrane 114 may comprise a doped PBI, such as phosphoric acid (H₃PO₄) doped PBI. In some embodiments, the proton-conducting membrane 114 comprises H₃PO₄-doped PBI.

The proton-conducting membrane 114 may be substantially homogeneous or may be substantially heterogeneous. As used herein, the term “homogeneous” means amounts of a material do not vary throughout different portions (e.g., different lateral and longitudinal portions) of a structure. Conversely, as used herein, the term “heterogeneous” means amounts of a material vary throughout different portions of a structure. Amounts of the material may vary stepwise (e.g., change abruptly), or may vary continuously (e.g., change progressively, such as linearly, parabolically) throughout different portions of the structure. In some embodiments, the proton-conducting membrane 114 is substantially homogeneous. In additional embodiments, the proton-conducting membrane 114 is heterogeneous. The proton-conducting membrane 114 may, for example, be formed of and include a stack of at least two (e.g., at least three, at least four, etc.) different materials. As a non-limiting example, the proton-conducting membrane 114 may comprise a stack of at least two (e.g., at least three, at least four, etc.) different perovskite materials individually having an operational temperature within a range of from about 350° C. to about 650° C. As another non-limiting example, the proton-conducting membrane 114 may comprise a stack of at least two (e.g., at least three, at least four, etc.) different solid acid materials individually having an operational temperature within a range of from about 200° C. to about 400° C. As a further non-limiting example, the proton-conducting membrane 114 may comprise a stack of at least two (e.g., at least three, at least four, etc.) different PBI materials individually having an operational temperature within a range of from about 150° C. to about 250° C.

The proton-conducting membrane 114 may exhibit any desired dimensions (e.g., length, width, thickness) and any desired shape (e.g., a cubic shape, cuboidal shape, a tubular shape, a tubular spiral shape, a spherical shape, a semi-spherical shape, a cylindrical shape, a semi-cylindrical shape, a conical shape, a triangular prismatic shape, a truncated version of one or more of the foregoing, and irregular shape). The dimensions and the shape of the proton-conducting membrane 114 may be selected such that the proton-conducting membrane 114 substantially intervenes between opposing surfaces of the positive electrode 112 and the negative electrode 116, and exhibits an H⁺ conductivity greater than or equal to about 10⁻²S/cm (e.g., from about 10⁻²S/cm to about 1 S/cm) at a temperature within a range of from about 150° C. to about 650° C. A thickness of the proton-conducting membrane 114 may be within a range of from about 5 micrometers (μm) to about 1000 μm, and may at least partially depend on the material composition of the proton-conducting membrane 114. For example, a proton-conducting membrane 114 formed of and including at least one perovskite material may have a thickness with a range of from about 5 μm to about 1000 μm; a proton-conducting membrane 114 formed of and including at least one solid acid material may have a thickness with a range of from about 5 μm to about 1000 μm; and a proton-conducting membrane 114 formed of and including at least one PBI material may have a thickness with a range of from about 50 μm to about 1000 μm.

The positive electrode 112 and the negative electrode 116 may individually be formed of and include at least one catalyst-doped material compatible with the material composition of the proton-conducting membrane 114 and the operating conditions (e.g., temperature, pressure, current density, etc.) of the electrochemical cell 110, and facilitating the formation of the NH₃stream 126 and hydrocarbon product stream 128 from the C₂H₆stream 122 and the N₂stream 124 at an operational temperature within the range of from about 150° C. to about 600° C. Accordingly, the material compositions of the positive electrode 112 and the negative electrode 116 may be selected relative to one another, the material composition of the proton-conducting membrane 114, the material composition of the C₂H₆stream 122, and the operating conditions of the electrochemical cell 110.

The catalyst-doped material of the positive electrode 112 includes at least one catalyst material thereon, thereover, and/or therein that accelerates reaction rates at the positive electrode 112 to produce C₂H₄, H⁺, and e⁻ from C₂H₆in accordance with Equation (1) above, and that also accelerates reaction rates at the positive electrode 112 to synthesize one or more higher hydrocarbons from the produced C₂H₄in accordance with Equation (3) above. The catalyst material of the positive electrode 112 may, for example, comprise a metallic material (e.g., a metal, an alloy, a composite of two or more metals and/or alloys) formulated to accelerate reaction rates at the positive electrode 112 to produce C₂H₄, H⁺, and e⁻ from C₂H₆, and to accelerate reaction rates for the synthesis of higher hydrocarbons from the produced C₂H₄.

The catalyst material of the positive electrode 112 may comprise a single (e.g., only one) element (e.g., a single metal), or may comprise multiple (e.g., more than one) elements (e.g., multiple metals). The catalyst material of the positive electrode 112 may comprise one or more of elemental particles, alloy particles, and composite particles. In some embodiments, the catalyst material of the positive electrode 112 comprises elemental particles of a first metal formulated to accelerate reaction rates at the positive electrode 112 to produce C₂H₄, H⁺, and e⁻ from C₂H₆; and additional elemental particles of a second metal discrete from the elemental particles of the first metal and formulated to accelerate reaction rates for the synthesis of higher hydrocarbons from the produced C₂H₄. In additional embodiments, the catalyst material of the positive electrode 112 comprises alloy particles individually including an alloy comprising the first metal and the second metal. In further embodiments, the catalyst material of the positive electrode 112 comprises composite particles including one of the first metal and the second metal partially (e.g., less than completely) coating (e.g., covering, encapsulating) the other of the first metal and the second metal, such as composite particles individually including a shell of the second metal partially coating a core of the first metal, and/or composite particles individually including a shell of the first metal partially coating a core of the second metal. In yet further embodiments, the catalyst material of the positive electrode 112 comprises composite particles including an alloy including one of the first metal and the second metal partially coating the another alloy including the other of the first metal and the second metal, such as composite particles individually including a shell of an alloy including the second metal partially coating a core of another alloy including the first metal, and/or composite particles individually including a shell of an alloy including the first metal partially coating a core of another alloy including the second metal. In still further embodiments, the catalyst material of the positive electrode 112 comprises composite particles including one of the first metal and the second metal partially coating an alloy including the other of the first metal and the second metal, such as composite particles individually including a shell of the second metal partially coating a core of an alloy including the first metal, and/or composite particles individually including a shell of the first metal partially coating a core of an alloy including the second metal. In yet still further embodiments, the catalyst material of the positive electrode 112 comprises composite particles including an alloy including one of the first metal and the second metal partially coating the other of the first metal and the second metal, such as composite particles individually including a shell of an alloy including the second metal partially coating a core of the first metal, and/or composite particles individually including a shell of an alloy including the first metal partially coating a core of the second metal.

As a non-limiting example, if the proton-conducting membrane 114 comprises a perovskite material (e.g., a BZCYYb, a BSNYYb, a doped BaCeO₃, a doped BaZrO₃, Ba₂(YSn)O_5.5, Ba₃(CaNb₂)O₉, etc.) having an operational temperature within a range of from about 350° C. to about 650° C., the positive electrode 112 may comprise a catalyst-doped perovskite material compatible with the perovskite material of the proton-conducting membrane 114. The positive electrode 112 may, for example, comprise a cermet material comprising at least one catalyst material including one or more (e.g., each) of nickel (Ni) and gold (Au), and at least one perovskite; such as one or more of a Ni/perovskite cermet (Ni-perovskite) material (e.g., Ni—BZCYYb, Ni—BSNYYb, Ni—BaCeO₃, Ni—BaZrO₃, Ni—Ba₂(YSn)O_5.5, Ni—Ba₃(CaNb₂)O₉) or a NiAu/perovskite cermet (NiAu-perovskite) material (e.g., NiAu—BZCYYb, NiAu—BSNYYb, NiAu—BaCeO₃, NiAu—BaZrO₃, NiAu—Ba₂(YSn)O_5.5, NiAu—Ba₃(CaNb₂)O₉). The catalyst material may include one or more of elemental particles individually including Ni or Au (e.g., Ni particles, Au particles), alloy particles individually including one or more (e.g., each) of Ni and Au (e.g., NiAu particles), and composite particles (e.g., core/shell particles) individually including one or more of Ni and Au (e.g., composite particles of Ni and Au). In some embodiments, the positive electrode 112 comprises Ni—BZCYYb. In additional embodiments, the positive electrode 112 comprises NiAu—BZCYYb.

As another non-limiting example, if the proton-conducting membrane 114 comprises a solid acid material (e.g., a doped CsH₂PO₄, an undoped CsH₂PO₄) having an operational temperature within a range of from about 200° C. to about 400° C., the positive electrode 112 may comprise a material (e.g., a catalytic alloy material) including one or more (e.g., each) Ni and Au (e.g., an NiAu alloy) that is compatible with the solid acid material of the proton-conducting membrane 114. In some embodiments wherein the proton-conducting membrane 114 comprises a solid acid material, the positive electrode 112 comprises an NiAu alloy.

As a further non-limiting example, if the proton-conducting membrane 114 comprises a PBI material (e.g., a doped PBI) having an operational temperature within a range of from about 150° C. to about 250° C., the positive electrode 112 may comprise one or more of at least one metal and at least one alloy (e.g., an NiAu alloy) compatible with the PBI material of the proton-conducting membrane 114. In some embodiments wherein the proton-conducting membrane 114 comprises a PBI material, the positive electrode 112 comprises an NiAu alloy.

Particles (e.g., elemental particles, alloy particles, composite particles) of the catalyst material of the catalyst-doped material of the positive electrode 112 may be nano-sized (e.g., individually having a cross-sectional width or diameter less than about one (1) μm, such as less than or equal to about 100 nanometers (nm), less than or equal to about 20 nm, or less than or equal to about 10 nm). In addition, the catalyst-doped material of the positive electrode 112 may exhibit any amount (e.g., concentration) and distribution of the catalyst material and any ratio of components thereof (e.g., any ratio of a first metal formulated to accelerate reaction rates at the positive electrode 112 to produce C₂H₄, H⁺, and e⁻ from C₂H₆to a second metal formulated to accelerate reaction rates for the synthesis of higher hydrocarbons from the produced C₂H₄) facilitating desired non-oxidative C₂H₆deprotonation reaction rates and desired ethyl coupling reaction rates at the positive electrode 112.

The catalyst-doped material of the negative electrode 116 includes at least one catalyst material thereon, thereover, and/or therein that accelerates reaction rates (e.g., nitrogen reduction reaction rates) at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻ in accordance with Equation (2) above. The catalyst material of the negative electrode 116 may, for example, comprise a metallic material (e.g., a metal, an alloy, a composite of two or more metals and/or alloys) formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e.

The catalyst material of the negative electrode 116 may comprise a single (e.g., only one) element (e.g., a single metal), or may comprise multiple (e.g., more than one) elements (e.g., multiple metals). The catalyst material of the negative electrode 116 may comprise one or more of elemental particles, alloy particles, and composite particles. In some embodiments, the catalyst material of the negative electrode 116 comprises elemental particles of one or more metals formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻. In additional embodiments, the catalyst material of the negative electrode 116 comprises alloy particles individually including an alloy comprising two or more metals, wherein at least one of the metals is formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e. In further embodiments, the catalyst material of the negative electrode 116 comprises composite particles including a first metal and a second metal partially (e.g., less than completely) coating (e.g., covering, encapsulating) the first metal, (e.g., composite particles individually including a shell of the second metal partially coating a core of the first metal), wherein at least one of the metals is formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻. In yet further embodiments, the catalyst material of the positive electrode 112 comprises composite particles including an alloy metal partially coating the another alloy, wherein at least one of the alloys includes a metal formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻. In still further embodiments, the catalyst material of the negative electrode 116 comprises composite particles including an elemental metal partially coating an alloy, wherein at least one of the elemental metal and the alloy is formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻. In yet still further embodiments, the catalyst material of the negative electrode 116 comprises composite particles including an alloy partially coating an elemental, wherein at least one of the alloy and the elemental metal is formulated to accelerate reaction rates at the negative electrode 116 to produce NH₃from N₂, H⁺, and e⁻.

As a non-limiting example, if the proton-conducting membrane 114 comprises a perovskite material (e.g., a BZCYYb, a BSNYYb, a doped BaCeO₃, a doped BaZrO₃, Ba₂(YSn)O_5.5, Ba₃(CaNb₂)O₉, etc.) having an operational temperature within a range of from about 350° C. to about 650° C., the negative electrode 116 may comprise a catalyst-doped perovskite material compatible with the perovskite material of the proton-conducting membrane 114. The negative electrode 116 may, for example, comprise a cermet material comprising at least one catalyst material including one or more (e.g., each) of ruthenium (Ru) and an Ru alloy, and at least one perovskite; such as one or more of an Ru/perovskite cermet (Ru-perovskite) material (e.g., Ru—BZCYYb, Ru—BSNYYb, Ru—PrBa_0.5Sr_0.5Co_1.5Fe_0.5O_5+δ(Ru—PBSCF), Ru—PrNi_0.5Co_0.5O_3−δ(Ru—PNC), Ru—Pr_0.5Ba_0.5Co_xFe_1−xO₃, Ru—Pr_0.5Ba_0.5FeO₃, Ru—BaCeO₃, Ru—BaZrO₃, Ru—Ba₂(YSn)O_5.5, Ru—Ba₃(CaNb₂)O₉), an RuNi/perovskite cermet (RuNi-perovskite) material (e.g., RuNi—BZCYYb, RuNi—BSNYYb, RuNi—PBSCF, RuNi—PNC, RuNi—Pr_0.5Ba_0.5Co_xFe_1−xO₃, RuNi—Pr_0.5Ba_0.5FeO₃, RuNi—BaCeO₃, RuNi—BaZrO₃, RuNi—Ba₂(YSn)O_5.5, RuNi—Ba₃(CaNb₂)O₉), an RuCe/perovskite cermet (RuCe-perovskite) material (e.g., RuCe—BZCYYb, RuCe—BSNYYb, RuCe—PBSCF, RuCe—PNC, RuCe—Pr_0.5Ba_0.5Co_xFe_1−xO₃, RuCe—Pr_0.5Ba_0.5FeO₃, RuCe—BaCeO₃, RuCe—BaZrO₃, RuCe—Ba₂(YSn)O_5.5, RuCe—Ba₃(CaNb₂)O₉), and an RuNiCe/perovskite cermet (RuNiCe-perovskite) material (e.g., RuNiCe—BZCYYb, RuNiCe—BSNYYb, RuNiCe—PBSCF, RuNiCe—PNC, RuNiCe—Pr_0.5Ba_0.5Co_xFe_1−xO₃, RuNiCe—Pr_0.5Ba_0.5FeO₃, RuNiCe—BaCeO₃, RuNiCe—BaZrO₃, RuNiCe—Ba₂(YSn)O_5.5, RuNiCe—Ba₃(CaNb₂)O₉). The catalyst material may include one or more of elemental particles individually including Ru (e.g., Ru particles), alloy particles individually including Ru (e.g., RuCe particles, RuNi particles, RuNiCe particles), and composite particles (e.g., core/shell particles) individually including Ru (e.g., composite particles of Ru and Ni, composite particles of Ru and Ce, composite particles of Ru, Ni, and Ce). In some embodiments, the negative electrode 116 comprises RuNi—BZCYYb.

As another non-limiting example, if the proton-conducting membrane 114 comprises a solid acid material (e.g., a doped CsH₂PO₄, an undoped CsH₂PO₄) having an operational temperature within a range of from about 200° C. to about 400° C., the negative electrode 116 may comprise a material including Ru (e.g., elemental Ru, an Ru alloy) that is compatible with the solid acid material of the proton-conducting membrane 114. In some embodiments wherein the proton-conducting membrane 114 comprises a solid acid material, the negative electrode 116 comprises an RuNi alloy. In additional embodiments wherein the proton-conducting membrane 114 comprises a solid acid material, the negative electrode 116 comprises an RuCe alloy. In further embodiments wherein the proton-conducting membrane 114 comprises a solid acid material, the negative electrode 116 comprises an RuNiCe alloy. In yet further embodiments wherein the proton-conducting membrane 114 comprises a solid acid material, the negative electrode 116 comprises elemental Ru.

As a further non-limiting example, if the proton-conducting membrane 114 comprises a PBI material (e.g., a doped PBI) having an operational temperature within a range of from about 150° C. to about 250° C., the positive electrode 112 may comprise one or more of at least one metal and at least one alloy (e.g., an NiAu alloy) compatible with the PBI material of the proton-conducting membrane 114. In some embodiments wherein the proton-conducting membrane 114 comprises a PBI material, the negative electrode 116 comprises an RuNi alloy. In additional embodiments wherein the proton-conducting membrane 114 comprises a PBI material, the negative electrode 116 comprises an RuCe alloy. In further embodiments wherein the proton-conducting membrane 114 comprises a PBI material, the negative electrode 116 comprises an RuNiCe alloy. In yet further embodiments wherein the proton-conducting membrane 114 comprises a PBI material, the negative electrode 116 comprises elemental Ru.

Particles (e.g., elemental particles, alloy particles, composite particles) of the catalyst material of the catalyst-doped material of the negative electrode 116 may be nano-sized (e.g., individually having a cross-sectional width or diameter less than about one (1) μm, such as less than or equal to about 100 nm, less than or equal to about 20 nm, or less than or equal to about 10 nm). In addition, the catalyst-doped material of the negative electrode 116 may exhibit any amount (e.g., concentration) and distribution of the catalyst material and any ratio of components thereof facilitating desired nitrogen reduction reaction rates at the negative electrode 116.

The positive electrode 112 and the negative electrode 116 may each individually exhibit any desired dimensions (e.g., length, width, thickness) and any desired shape (e.g., a cubic shape, cuboidal shape, a tubular shape, a tubular spiral shape, a spherical shape, a semi-spherical shape, a cylindrical shape, a semi-cylindrical shape, a conical shape, a triangular prismatic shape, a truncated version of one or more of the foregoing, and irregular shape). The dimensions and the shapes of the positive electrode 112 and the negative electrode 116 may be selected relative to the dimensions and the shape of the proton-conducting membrane 114 such that the proton-conducting membrane 114 substantially intervenes between opposing surfaces of the positive electrode 112 and the negative electrode 116. Thicknesses of the positive electrode 112 and the negative electrode 116 may each individually be within a range of from about 10 μm to about 1000 μm.

The electrochemical cell 110, including the positive electrode 112, the proton-conducting membrane 114, and the negative electrode 116 thereof, may be formed through conventional processes (e.g., rolling process, milling processes, shaping processes, pressing processes, consolidation processes, etc.), which are not described in detail herein. The electrochemical cell 110 may be mono-faced or bi-faced and may have a prismatic, folded, wound, cylindrical, or jelly rolled configuration. The electrochemical cell 110 may be placed within the housing structure 108 to form the electrochemical apparatus 106, and may be electrically connected to the power source 118.

Although the electrochemical apparatus 106 is depicted as including a single (i.e., only one) electrochemical cell 110 in FIG. 1, the electrochemical apparatus 106 may include any number of electrochemical cells 110. Put another way, the electrochemical apparatus 106 may include a single (e.g., only one) electrochemical cell 110, or may include multiple (e.g., more than one) electrochemical cells 110. If the electrochemical apparatus 106 includes multiple electrochemical cells 110, each of the electrochemical cells 110 may be substantially the same (e.g., exhibit substantially the same components, component sizes, component shapes, component material compositions, component material distributions, component positions, component orientations, etc.) and may be operated under substantially the same conditions (e.g., substantially the same temperatures, pressures, flow rates, etc.), or at least one of the electrochemical cells 110 may be different (e.g., exhibit one or more of different components, different component sizes, different component shapes, different component material compositions, different component material distributions, different component positions, different component orientations, etc.) than at least one other of the electrochemical cells 110 and/or may be operated under different conditions (e.g., different temperatures, different pressures, different flow rates, etc.) than at least one other of the electrochemical cells 110. By way of non-limiting example, one of the electrochemical cells 110 may be configured for and operated under a different temperature (e.g., different operating temperature resulting from a different material composition of one of more components thereof, such as a different material composition of the proton-conducting membrane 114 thereof) than at least one other of the electrochemical cells 110. In some embodiments, two or more electrochemical cells 110 are provided in parallel with one another within the housing structure 108 of the electrochemical apparatus 106, and may individually produce a portion of the N₂protonation products (e.g., NH₃) directed out of the electrochemical apparatus 106 as the NH₃stream 126.

In addition, although the system 100 is depicted as including a single (i.e., only one) electrochemical apparatus 106 in FIG. 1, the system 100 may include any number of electrochemical apparatuses 106. Put another way, the system 100 may include a single (e.g., only one) electrochemical apparatus 106, or may include multiple (e.g., more than one) electrochemical apparatuses 106. If the system 100 includes multiple electrochemical apparatuses 106, each of the electrochemical apparatuses 106 may be substantially the same (e.g., exhibit substantially the same components, component sizes, component shapes, component material compositions, component material distributions, component positions, component orientations, etc.) and may be operated under substantially the same conditions (e.g., substantially the same temperatures, pressures, flow rates, etc.), or at least one of the electrochemical apparatus 106 may be different (e.g., exhibit one or more of different components, different component sizes, different component shapes, different component material compositions, different component material distributions, different component positions, different component orientations, etc.) than at least one other of the electrochemical apparatuses 106 and/or may be operated under different conditions (e.g., different temperatures, different pressures, different flow rates, etc.) than at least one other of the electrochemical apparatuses 106. By way of non-limiting example, one of the electrochemical apparatuses 106 may be configured for and operated under a different temperature (e.g., a different operating temperature resulting from a different material composition of one of more components of an electrochemical cell 110 thereof, such as a different material composition of the proton-conducting membrane 114 thereof) than at least one other of the electrochemical apparatuses 106. In some embodiments, two of more electrochemical apparatuses 106 are provided in parallel with one another. Each of the two of more electrochemical apparatuses 106 may individually receive a C₂H₆stream 122 and a N₂stream 124 and individually form an NH₃stream 126 and a hydrocarbon product stream 128. In additional embodiments, two of more electrochemical apparatuses 106 are provided in series with one another.

Still referring to FIG. 1, the hydrocarbon product stream 128 and the NH₃stream 126 exiting the electrochemical apparatus 106 may individually be utilized or disposed of as desired. In some embodiments, the hydrocarbon product stream 128 and the NH₃stream 126 are individually delivered into one or more storage vessels for subsequent use, as desired. In additional embodiments, at least a portion of one or more of the hydrocarbon product stream 128 and the NH₃stream 126 may be utilized (e.g., combusted) to heat one or more components (e.g., the heating apparatus 120 (if present); the electrochemical apparatus 106; etc.) and/or streams (e.g., the C₂H₆stream 122, the N₂stream 124) of the system 100. By way of non-limiting example, if the heating apparatus 120 (if present) is a combustion-based apparatus, at least a portion of one or more of the hydrocarbon product stream 128 and the NH₃stream 126 may be directed into the heating apparatus 120 and undergo an combustion reaction to efficiently heat one or more of the C₂H₆stream 122 entering the electrochemical apparatus 106, the N₂stream 124 entering the electrochemical apparatus 106, and at least a portion of the electrochemical apparatus 106. Utilizing the hydrocarbon product stream 128 and/or the NH₃stream 126 as described above may reduce the electrical power requirements of the system 100 by enabling the utilization of direct thermal energy.

Thermal energy input into (e.g., through the heating apparatus 120 (if present)) and/or generated by the electrochemical apparatus 106 may also be used to heat one or more other components and/or streams of the system 100. By way of non-limiting example, the hydrocarbon product stream 128 and/or the NH₃stream 126 exiting the electrochemical apparatus 106 may be directed into a heat exchanger configured and operated to facilitate heat exchange between the hydrocarbon product stream 128 and/or the NH₃stream 126 of the system 100 and one or more other relatively cooler streams (e.g., the C₂H₆stream 122, the N₂stream 124) of the system 100 to transfer heat from the hydrocarbon product stream 128 and/or the NH₃stream 126 to the relatively cooler stream(s) to facilitate the recovery of the thermal energy input into and generated within the electrochemical apparatus 106. The recovered thermal energy may increase process efficiency and/or reduce operational costs without having to react (e.g., combust) higher hydrocarbon products of the hydrocarbon product stream 128 and/or NH₃of the NH₃stream 126.

The methods, systems (e.g., the system 100), and apparatuses (e.g., the electrochemical apparatus 106, including the electrochemical cell 110 thereof) of the disclosure facilitate the simple and efficient co-production of higher hydrocarbons (e.g., butylene, gasoline, diesel, etc.) and NH₃from C₂H₆at intermediate temperatures, such as temperatures within a range of from about 150° C. to about 600° C. The methods, systems, and apparatuses of the disclosure may reduce one or more of the time (e.g., processing steps), costs (e.g., material costs), and energy (e.g., thermal energy, electrical energy, etc.) required to produce higher hydrocarbons and NH₃relative to conventional methods, systems, and apparatuses. The methods, systems, and apparatuses of the disclosure may be more efficient, durable, and reliable that conventional methods, conventional systems, and conventional apparatuses of producing higher hydrocarbons and NH₃.

While the disclosure is susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, the disclosure is not limited to the particular forms disclosed. Rather, the disclosure is to cover all modifications, equivalents, and alternatives falling within the scope of the following appended claims and their legal equivalent. For example, elements and features disclosed in relation to one embodiment may be combined with elements and features disclosed in relation to other embodiments of the disclosure.

Claims

1. A system for co-producing hydrocarbon products and NH3, comprising:

a source of C2H6;

a source of N2; and

an electrochemical apparatus in fluid communication with the source of C2H6 and the source of N2, and comprising: a housing structure configured and positioned to receive a C2H6 stream from the source of C2H6 and to receive a N2 stream from the source of N2; and an electrochemical cell within an internal chamber of the housing structure, and comprising: a positive electrode comprising a catalyst material formulated to accelerate reaction rates to produce C2H4, H+, and e− from C2H6, and to accelerate reaction rates to synthesize at least one hydrocarbon product from the produced C2H4; a negative electrode comprising another catalyst material formulated to accelerate reaction rates to produce NH3 from N2, H+, and e−; and a proton-conducting membrane between the positive electrode and the negative electrode and comprising an electrolyte material having an ionic conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 600° C.

2. The system of claim 1, wherein the electrolyte material of the proton-conducting membrane is selected from the group consisting of:

a perovskite material having a H+ conductivity greater than about 10−2 S/cm at one or more temperatures within a range of from about 400° C. to about 600° C.;

a solid acid material having a H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 200° C. to about 400° C.; and

a polybenzimidazole (PBI) material having a H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 200° C.

3. The system of claim 1, wherein:

the proton-conducting membrane comprises a yttrium- and ytterbium-doped barium-zirconate-cerate (BZBYYb);

the catalyst material of the positive electrode comprises one or more of Ni—BZCYYb and NiAu—BZCYYb; and

the another catalyst material of the negative electrode comprises one or more of Ru—BZCYYb, RuNi—BZCYYb, RuCe—BZCYYb, and RuNiCe—BZCYYb.

4. The system of claim 1, wherein:

the proton-conducting membrane comprises CsH2PO4;

the catalyst material of the positive electrode comprises one or more of Ni and Au; and

the another catalyst material of the negative electrode comprises one or more of elemental Ru and an Ru-containing alloy.

5. The system of claim 1, wherein:

the proton-conducting membrane comprises H3PO4-doped polybenzimidazole (PBI);

the catalyst material of the positive electrode comprises one or more of Ni and Au; and

the another catalyst material of the negative electrode comprises one or more of elemental Ru and an Ru-containing alloy.

6. The system of claim 1, further comprising a heating apparatus configured and positioned to heat one or more of the C2H6 stream, the N2 stream, and at least a portion of the electrochemical apparatus.

7. An electrochemical cell, comprising:

a positive electrode comprising a first catalyst material formulated to accelerate C2H6 deprotonation reaction rates to produce C2H4, H+, and e− from C2H6, and to accelerate coupling reaction rates to synthesize at least one hydrocarbon product from the produced C2H4;

a negative electrode comprising a second catalyst material formulated to accelerate N2 protonation reaction rates to produce NH3 from N2, H+, and e; and

a proton-conducting membrane between the positive electrode and the negative electrode and comprising an electrolyte material having an ionic conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 600° C.

8. The electrochemical cell of claim 7, wherein the proton-conducting membrane comprises at least one perovskite material having an H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 350° C. to about 650° C.

9. The electrochemical cell of claim 8, wherein the at least one perovskite material comprises one or more of a yttrium- and ytterbium-doped barium-zirconate-cerate (BZCYYb), a yttrium- and ytterbium-doped barium-strontium-niobate (BSNYYb), a yttrium-doped BaCeO3, a yttrium-doped BaZrO3, Ba2(YSn)O5.5, and Ba3(CaNb2)O9.

10. The electrochemical cell of claim 8, wherein:

the first catalyst material of the positive electrode comprises one or more of a Ni/perovskite cermet and a NiAu/perovskite cermet; and

the second catalyst material of the negative electrode comprises one or more of a Ru/perovskite cermet, an RuNi/perovskite cermet, an RuCe/perovskite cermet, and a RuNiCe/perovskite cermet.

11. The electrochemical cell of claim 7, wherein the proton-conducting membrane comprises at least one solid acid material having an H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 200° C. to about 400° C.

12. The electrochemical cell of claim 11, wherein the at least one solid acid material comprises CsH2PO4.

13. The electrochemical cell of claim 12, wherein:

the first catalyst material of the positive electrode comprises one or more of Ni and Au; and

the second catalyst material of the negative electrode comprises one or more of elemental Ru and an Ru alloy.

14. The electrochemical cell of claim 7, wherein the proton-conducting membrane comprises at least one polybenzimidazole (PBI) material having an H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 150° C. to about 200° C.

15. The electrochemical cell of claim 14, wherein the PBI material comprises H3PO4-doped PBI.

16. The electrochemical cell of claim 15, wherein:

the first catalyst material of the positive electrode comprises one or more of Ni and Au; and

the second catalyst material of the negative electrode comprises one or more of elemental Ru and an Ru alloy.

17. A system for co-producing hydrocarbon products and NH3, comprising:

a source of C2H6;

a source of N2; and

an electrochemical apparatus in fluid communication with the source of C2H6 and the source of N2, and comprising: a housing structure configured and positioned to receive a C2H6 stream from the source of C2H6 and to receive a N2 stream from the source of N2; and electrochemical cells within the housing structure, one or more of the electrochemical cells individually comprising: a positive electrode comprising a first perovskite material formulated to accelerate reaction rates to produce C2H4, H+, and e− from C2H6, and to accelerate reaction rates to synthesize one or more hydrocarbon products from the produced C2H4; a negative electrode comprising a second perovskite material formulated to accelerate reaction rates to produce NH3 from N2, H+, and e; and a proton-conducting membrane between the positive electrode and the negative electrode and comprising a third perovskite material having an H+ conductivity greater than or equal to about 10−2 S/cm at one or more temperatures within a range of from about 400° C. to about 600° C.

18. The system of claim 17, wherein the positive electrode comprises one or more of a Ni-doped yttrium- and ytterbium-doped barium-zirconate-cerate (Ni—BZBYYb), a Ni-doped yttrium- and ytterbium-doped barium-strontium-niobate (Ni—BSNYYb), a Ni-doped BaCeO3, a Ni-doped BaZrO3, an Ni-doped Ba2(YSn)O5.5, a Ni-doped Ba3(CaNb2)O9), a NiAu-doped BZCYYb, a NiAu-doped BSNYYb, a NiAu-doped BaCeO3, a NiAu-doped BaZrO3, a NiAu-doped Ba2(YSn)O5.5, and a NiAu-doped Ba3(CaNb2)O9).

19. The system of claim 18, wherein the negative electrode comprises one or more of Ru-doped yttrium- and ytterbium-doped barium-zirconate-cerate (Ru—BZBYYb) doped with Ru, Ru-doped yttrium- and ytterbium-doped barium-strontium-niobate (Ru—BSNYYb) an Ru-doped PrBa0.5Sr0.5Co1.5Fe0.5O5+δ (Ru—PBSCF), an Ru-doped PrNi0.5Co0.5O3−δ (Ru—PNC), an Ru-doped Pr0.5Ba0.5CoxFe1−xO3, an Ru-doped Pr0.5Ba0.5FeO3, an Ru-doped BaCeO3, an Ru-doped BaZrO3, an Ru-doped Ba2(YSn)O5.5, an Ru-doped Ba3(CaNb2)O9), an RuNi-doped BZCYYb, an RuNi-doped BSNYYb, an RuNi-doped PBSCF, an RuNi-doped PNC, an RuNi-doped Pr0.5Ba0.5CoxFe1−xO3, an RuNi-doped Pr0.5Ba0.5FeO3, an RuNi-doped BaCeO3, an RuNi-doped BaZrO3, an RuNi-doped Ba2(YSn)O5.5, an RuNi-doped Ba3(CaNb2)O9), an RuCe-doped BZCYYb, an RuCe-doped BSNYYb, an RuCe-doped PBSCF, an RuCe-doped PNC, an RuCe-doped Pr0.5Ba0.5CoxFe1−xO3, an RuCe-doped Pr0.5Ba0.5FeO3, an RuCe-doped BaCeO3, an RuCe-doped BaZrO3, an RuCe-doped Ba2(YSn)O5.5, an RuCe-doped Ba3(CaNb2)O9), an RuNiCe-doped BZCYYb, an RuNiCe-doped BSNYYb, an RuNiCe-doped PBSCF, an RuNiCe-doped PNC, an RuNiCe-doped Pr0.5Ba0.5CoxFe1−xO3, an RuNiCe-doped Pr0.5Ba0.5FeO3, an RuNiCe-doped BaCeO3, RuNiCe-doped BaZrO3, an RuNiCe-doped Ba2(YSn)O5.5, and an RuNiCe-doped Ba3(CaNb2)O9).

20. The system of claim 19, wherein the proton-conducting membrane comprises one or more of a yttrium- and ytterbium-doped barium-zirconate-cerate (BZCYYb), a yttrium- and ytterbium-doped barium-strontium-niobate (BSNYYb), a yttrium-doped BaCeO3, a yttrium-doped BaZrO3, Ba2(YSn)O5.5, and Ba3(CaNb2)O9.