Acellular Bioactive Scaffold Device and Methods of Fabrication and Treatment Relating Thereto
An implantable acellular polymeric scaffold device functionalized with aggrecan is provided. Also provided are methods of fabricating a polymeric scaffold device, including methods of fabricating the scaffold device via 3D printing. Methods of treating a cartilage defect in a subject in need thereof comprise application of the disclosed scaffold device in combination with microfracture procedures. A specialized lid for a centrifugation well plate is also provided.
Latest University of Maryland, College Park Patents:
- Training systems and methods for predicting knee adduction moment
- Delignified wood materials, and methods for fabricating and use thereof
- Photo-immunoconjugate Formulations and Methods of Treatment Relating Thereto
- All solid-state sodium-sulfur or lithium-sulfur battery prepared using cast-annealing method
- Systems and methods for quantum sensing using solid-state spin ensembles
This application is a divisional of, and claims priority to, U.S. patent application Ser. No. 16/743,315 (filed Jan. 15, 2020; pending), which application claims priority to U.S. Provisional Patent Applications Ser. Nos. 62/828,303 (filed Apr. 2, 2019; expired) and 62/792,722 (filed Jan. 15, 2019; expired), each of which applications is herein incorporated by reference in its entirety.
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENTThis invention was made with government support under CBET1264517 and CBET1604742 awarded by the National Science Foundation and under P41 EB023833 awarded by the National Institutes of Health. The government has certain rights in the invention.
FIELD OF THE INVENTIONThe present disclosure relates to an implantable acellular scaffold device, and in particular an acellular PLCL scaffold device functionalized with aggrecan, methods of fabricating the scaffold device, and methods of treating a cartilage defect utilizing the scaffold device.
BACKGROUND OF THE INVENTIONIn the US alone, the cartilage repair and regeneration market was $1.8 billion in 2015 (Grand View Research, May 2017). It is expected to grow at a compound annual growth rate of 5.4% during the next 10 years. Such growth is chiefly due to the increasing prevalence of musculoskeletal disorders, aging population, and rising number of accidents and related injuries. Cartilage defects are common in all age groups due to trauma and/or pathology, and are particularly prevalent in seniors with approximately 70% of the senior population experiencing cartilage degeneration at varying levels of severity. Over time, articular cartilage can deteriorate or become damaged following injury or normal wear and tear, leading to the pain many people feel as they age. As of 2016, approximately 14 million Americans experienced symptomatic knee osteoarthritis (Deshpande, B. R. et al. (2016) “Number of Persons With Symptomatic Knee Osteoarthritis in the US: Impact of Race and Ethnicity, Age, Sex, and Obesity,” Arthritis Care Res 68(12):1743-1750), demonstrating a huge need for the development of translational clinical therapies. Unfortunately, the treatment and repair of articular cartilage defects remains challenging due to the limited endogenous regeneration of the tissue and poor integration with conventional implantations. As such, little long term success has been achieved with current treatment strategies.
Articular cartilage is the highly specialized connective tissue surrounding surfaces at joints. Its primary function is to protect these surfaces by providing smooth, low friction contact and enabling smooth load transfers at the joints. Articular cartilage is structurally complex and difficult to mimic, despite the fact that it is innervated and lacks blood vessels, nerves, and lymphatics. Articular cartilage is composed exclusively of chondrocytes embedded within a dense extracellular matrix (ECM) composed of water, collagen (primarily type II), hyaluronic acid, and proteoglycans (Cohen, N. et al. (1998) “Composition And Dynamics Of Articular Cartilage: Structure, Function, And Maintaining Healthy State,” J Ortho & Sports Phys Ther 28(4):203-215). It includes a banded structure composed of three zones: superficial, transitional, and deep, corresponding to the cartilage depth. The distinct alignment of cells and collagen fibers in each of these zones provides specific support against mechanical loadings.
As the ECM constitutes more than 90% of the dry weight of articular cartilage, it is important to understand and restore the ECM function in cartilage tissue engineering. The ECM of cartilage can be divided into 3 regions: pericellular, territorial, and interterritorial (based on its composition and properties that it lends to cartilage). The pericellular matrix comprises the thin layer surrounding the chondrocytes. It is composed of mainly proteoglycans as well as other proteins, and is responsible for transducing signals to the cell when the cartilage undergoes load bearing. It is believed that the territorial matrix contributes to protecting chondrocytes from mechanical stresses and strains caused, providing strength to the cartilage to endure loads. The interterritorial region composes the largest percentage of the ECM and thus provides most of its mechanical properties. Large collagen fibers with the highest concentration of proteoglycans are randomly oriented throughout this region in order to provide compressive strength.
Proteoglycans play an important role in the ECM as the overall negative charge retains water molecules. The resulting swelling pressure allows the tissue to resist compressive force (Yanagishita, M. (1993) “Function Of Proteoglycans In The Extracellular-Matrix,” Acta Pathologica Japonica 43(6):283-293). The most abundant proteoglycan within the ECM of articular cartilage is aggrecan, structured as a core protein decorated with several types of sulfated glycosaminoglycans (GAGs), including chondroitin sulfate and keratan sulfate. Multiple aggrecan monomers self-assemble into large molecules through covalent bonds with hyaluronic acid, forming large biologically active aggregated proteoglycans which carry a negative charge, resulting in significant amounts of water being retained by the tissue (Kiani, C. et al. (2002) “Structure and Function of Aggrecan,” Cell Res 12(1):19-32; Guo, T. et al. (2017) “Engineering Niches for Cartilage Tissue Regeneration,” in: A. Vishwakarma, J. Karp (Eds.), Biology and Engineering of Stem Cell Niches, Elsevier).
Microfracture and autologous chondrocyte implantation (ACI) are currently the most common surgical methods for treating cartilage defects. Microfracture surgery entails drilling small holes into the subchondral bone underlying a cartilage defect in order to trigger the release of native mesenchymal stem cells (MSCs) from the bone marrow. The MSCs differentiate into chondrocytes to regenerate articular cartilage tissue (Hurst, J. et al. (2010) “Rehabilitation Following Microfracture for Chondral Injury in the Knee,” Clinics in Sports Medicine 29(2):257). However, the post-surgical microenvironment created by conventional techniques fails to orient and guide the MSCs to the defect site properly, resulting in comparatively weak fibrous tissue be created that does not possess the desired and necessary mechanical properties as compared to native cartilage (Steadman, J. R. et al. (2003) “Outcomes Of Microfracture For Traumatic Chondral Defects Of The Knee: Average 11-Year Follow-Up,” Arthroscopy 19(5):477-84; Steinwachs, M. R. et al. (2008) “Marrow Stimulation Techniques,” Injury 39:26-31).
ACI is a two stage operative procedure sometimes used to treat larger defects. A small piece of articular cartilage is removed from a patient's knee in a first operation. The cartilage biopsy is then enzymatically treated in order to isolate and harvest chondrocytes. The harvested chondrocyte population is expanded over approximately 6 to 8 weeks, and then injected under an implanted patch in the patient in a second operation. ACI is typically recommended only for defects larger than two square centimeters and requires extensive recovery time after the surgeries. Additionally, it remains difficult to harvest and successfully cultivate a large enough chondrocyte population to transplant due to the low proliferation rate and differentiation potential during in vitro culture (Jones, D. & Peterson, L. (2006) “Autologous chondrocyte implantation,” Journal of Bone and Joint Surgery-American, 88A(11):2502-2520; Hinckel, B. B. & Gomoll, A. H. (2017) “Autologous Chondrocytes and Next-Generation Matrix-Based Autologous Chondrocyte Implantation,” Clin Sports Med 36(3):525-548). The relatively recent FDA-approved product Matrix-Induced Autologous Chondrocyte Implantation (MACI) provides for culturing of the chondrocytes in a membrane or matrix and then implanting the chondrocyte-seeded matrix. MACI showed some improved results as compared to traditional ACI (Kon, E. et al. (2012) “ACI and MACI,” J. Knee Surgery 25(1):17-22); however, MACI displayed the same drawbacks as ACI, including the requirement for the dual-surgery procedures and less abundant cell source.
Microfracture alone has been shown to be more cost-effective than ACI when comparing clinical scores (e.g., hospital costs, physical therapy, etc.) (Aae, T. F. et al. (2018) “Microfracture Is More Cost-Effective Than Autologous Chondrocyte Implantation: A Review Of Level 1 And Level 2 Studies With 5 Year Follow-Up,” Knee Surgery, Sport. Traumatol. Arthrosc. doi:10.1007/s00167-017-4802-5). As such, microfracture has been extensively used and has dominated the intrinsic repair stimulus segment despite its limitations. For example, an analysis of U.S. commercial insurance databases indicates that among patients undergoing microfracture surgery for cartilage repair, the average two-year reoperation rate is 15% (Frank, R. M. et al. (2018) “Reoperation Rates After Cartilage Restoration Procedures in the Knee: Analysis of a Large US Commercial Database,” Am. J. Orthop 47(6)). Moreover, patients undergoing microfracture were more likely to experience an ultimate conversion to arthroplasty as compared to ACI and other conventional techniques.
Current treatment techniques result in newly formed tissue that is mechanically weakened by unexpected biological changes over time, leading to a loss of tissue function. Although autografts and allografts have been used to treat critical cartilage defects with limited success, there is no satisfactory treatment remedy for severe critical cartilage injuries. To improve upon the microfracture technique, some researchers have attempted to utilize the procedure with the use of biocompatible materials as defect implants. Investigators have shown that the application of hyaluronic acid (HA) after microfracture promoted thicker, hyaline-like cartilage compared to controls in a rabbit model (Leela, S. K. et al. (2008) “Articular Cartilage Regeneration With Microfracture And Hyaluronic Acid,” Biotechnol. Lett. 30:435-9). A recent clinical trial using injected HA as postoperative treatment also indicated some improved performance compared to microfracture alone (Doral, M. N. et al. (2012) “Treatment Of Osteochondral Lesions Of The Talus With Microfracture Technique And Postoperative Hyaluronan Injection,” Knee Surgery, Sport. Traumatol. Arthrosc. 20:1398-1403). In another study, chitosan-glycerol phosphate/blood clots were implanted after microfracture, which was reported as showing an increased filling of the defect (Hoemann, C. D. et al. (2005) “Chitosan-glycerol phosphate/blood implants improve hyaline cartilage repair in ovine microfracture defects,” J. Bone Jt. Surg.—Ser. A 87:2671-2686).
Other tissue engineering strategies have attempted to pursue the regeneration of biomimetic cartilage tissue utilizing various concentrations of collagen type II in a construct (Guo, T. et al. (2017) “Three-Dimensional Printing Articular Cartilage: Recapitulating the Complexity of Native Tissue,” Tissue Engineering Part B-Reviews 23(3):225-236). Others have attempted to isolate chondrocytes from the different cartilage zones and seed them onto scaffolds in an effort to replicate the banded structure in native articular cartilage (Mainil-Varlet, P. et al. (2001) “Articular Cartilage Repair Using A Tissue-Engineered Cartilage-Like Implant: An Animal Study,” Osteoarthritis and Cartilage 9:S6-S15). In addition to the limited biological complexity involved, extensive preparation and characterization are required for these approaches.
Attempts to provide constructs for guiding cartilage repair have also been proposed, and several commercial products are currently available using specific biomaterials, including: polylactin, polydiaxanon and fibrin (BioTissue Technologies, Freiburg, Germany); collagen type I matrix (Arthro Kinetics Biotechnology, Krems, Austria); fibrin, hyaluronic acid (Histogenics Corp., Waltham, MA); agarose, alginate hydrogel (Tissue Bank of France, Lyon, France); bovine collagen (Histogenics Corp. Waltham, MA); and bovine collagen, chondroitin sulphate (Tetec Tissue Engineering Technologies AG, Reutlingen, Germany). However, constructs formed from such materials exhibit much weaker mechanical properties as compared to native cartilage, as noted above. Moreover, such conventional constructs incorporate the use of autologous cells, which may minimize the risk for immune rejection but involve a relatively lengthy surgical procedure (e.g., cell harvesting, expansion, encapsulation in biomaterial) as well as a relatively short product shelf life. Further, conventional strategies fail to provide for the regeneration of the cartilage zonal composition, as discussed in further detail below. Such conventional constructs and/or products have therefore not been successful in meeting the needs of clinicians and patients.
Accordingly, there is a need for an implantable scaffold device that solves one or more of the limitations associated with conventional cartilage repair strategies, and/or that enhances conventional cartilage repair strategies such as microfracture surgery.
SUMMARY OF THE INVENTIONThe present disclosure relates to an implantable acellular scaffold device that facilitates cellular growth. The scaffold is preferably fabricated using three-dimensional (3D) printing methods, and thus may be readily formed in minutes and in a selected geometric configuration suitable for the intended application. 3D printing and bioprinting enables spatiotemporal layer-by-layer fabrication of highly complex tissues such as cartilage structure. The scaffold is preferably fabricated from a composition comprising poly(L-lactide-co-caprolactone) (PLCL) and poly(lactic-co-glycolic acid) (PLGA).
An advantageous feature of the disclosed scaffold devices is the presence of an internal architecture that guides the ingrowth and differentiation of cells, e.g. such as cells released from the bone marrow via microfracture surgery. The disclosed techniques leverage the intrinsic regenerative ability of the human body and provide a physiological template for tissue repair. This paradigm can be applied to a range of applications where a clear source of endogenous stem cells is present, e.g. such as in the knee. The particular configuration of the disclosed implant may be readily modified to match other orthopedic tissue defects (e.g., shape, mechanical properties, composition, etc.) due in part to the use of 3D printing and established biomaterials for fabrication.
In some embodiments, an acellular scaffold that mimics the structure of native cartilage is used to facilitate the growth of cartilage in combination with microfracture surgery. The scaffold is preferably functionalized with aggrecan in order to provide binding sites for MSCs released from the microfracture procedure, thereby improving therapeutic functionality by increasing the repair mechanisms in microfracture. Aggrecan supports the cellular fraction of bone marrow released from microfracture. The disclosed scaffold guides MSCs and growth factors released from the bone marrow to the defect site(s), thereby initiating and/or strengthening the cartilage regeneration process. The biofunctionalized 3D-printed acellular scaffolds may thus be readily utilized in combination with traditional microfracture in order to improve the quality of cartilage regeneration in a cost and labor effective way.
In accordance with disclosed methods, a substantial improvement of regenerated cartilage tissue quality and joint function was demonstrated in animal models. Optical coherence tomography (OCT) revealed doubled thickness of the regenerated cartilage tissue in the group treated with the disclosed aggrecan-functionalized scaffold as compared to the group treated with standard microfracture alone. Haematoxylin and eosin (H&E) staining showed 366±95 chondrocytes present in the unit area of cartilage layer with the support of the disclosed bioactive scaffold implants, while the group treated with microfracture alone showed only 112±26 chondrocytes. In addition, the expression of type II collagen appeared almost 10 times higher in the group treated with the disclosed scaffold as compared to the group treated with microfracture alone, thus demonstrating a significant improvement in cartilage formation when microfracture is combined with the disclosed scaffolds as compared to microfracture alone. The therapeutic effects of the disclosed techniques were also evaluated at the joint function level. Mobility of animal models was evaluated using a modified Basso, Beattie and Bresnahan (BBB) scale. While the defect control group showed no movement improvement over the course of study, all other experimental groups showed a trend of increasing scores (and thus mobility improvement) over time.
In accordance with disclosed embodiments, the present disclosure relates to an implantable device comprising an acellular polymeric scaffold functionalized with aggrecan. In some embodiments, the scaffold is fabricated from a composition comprising poly(L-lactide-co-caprolactone) (PLCL). In some embodiments, the composition further comprises amine end capped poly(lactic-co-glycolic acid) (amine-PLGA) as a reactive portion to bind the aggrecan. The scaffold is preferably fabricated via three-dimensional (3D) printing, e.g., via material extrusion 3D printing.
In some embodiments, the scaffold comprises a first layer having a first fiber pattern, and a second layer having a second fiber pattern different from the first fiber pattern. In some implementations, the first fiber pattern comprises a plurality of spaced parallel fibers, and the second fiber pattern comprises a plurality of spaced parallel fibers. In some embodiments, the plurality of spaced parallel fibers of the first fiber pattern are offset in plan view from the plurality of spaced parallel fibers of the second fiber pattern. The second fiber pattern may comprise a generally crosshatch pattern in plan view. In some embodiments, the first layer has a first thickness, and the second layer has a second thickness at least about twice the first thickness. In some embodiments, the scaffold comprises a third layer having a third fiber pattern different from the first and second fiber patterns. In some implementations, the third fiber pattern comprises a plurality of spaced parallel fibers, wherein the plurality of spaced parallel fibers of the third fiber pattern are generally perpendicular in plan view from the plurality of spaced parallel fibers of the first fiber pattern.
The present disclosure also relates to a method of treating a cartilage defect in a subject, comprising the steps of: creating an opening(s) in a subchondral bone in the subject underlying the cartilage defect and into bone marrow thereof to permit release of mesenchymal stem cells (MSCs) from the bone marrow; and applying an acellular polymeric scaffold functionalized with aggrecan onto the cartilage defect, thereby guiding the MSCs released from the bone marrow through the openings and into the scaffold. In some embodiments, the opening(s) are created via a microfracture procedure.
The present disclosure also relates to a well plate lid comprising a base and a plurality of wells extending outwardly therefrom. The plurality of wells are receivable in correspondingly configured wells of a cell-culture plate. In some embodiments, the plurality of wells of the lid are releasably securable in the wells of the cell-culture plate via interference fit. In some embodiments, the lid is formed from and/or comprises an acrylate-based resin. In some embodiments, the lid is fabricated via three-dimensional (3D) printing, e.g. material extrusion 3D printing.
In some embodiments, at least one well(s) of the lid comprises a retaining member extending outwardly from an interior sidewall of the well(s). In some embodiments, the retaining member extends between opposing surfaces of the interior sidewall of the well(s). For example, the retaining member may have a generally cross-shaped configuration in plan view. However, it should be understood that the retaining member may have other configurations. In addition, the specific configuration of the well(s) of the lid and corresponding well plate may vary (e.g., cylindrical, square, etc.) as desired for a particular application. In some implementations, the retaining member is disposed intermediate an interior base and an upper edge of the sidewall of the well(s) of the lid. In some implementations, the retaining member is configured to retain a scaffold construct in a selected position within said well.
The present disclosure also relates to a centrifugation system comprising the well plate lid as disclosed herein, and a correspondingly configured cell-culture well plate. The centrifugation system may also include a centrifuge device operably associated with the lid and well plate.
The patent or application file contains at least one drawing/photograph executed in color. Copies of this patent or patent application publication with color drawings/photographs will be provided by the Office upon request and payment of the necessary fee.
Biologically active, acellular scaffolds are an attractive alternative to cell-laden constructs given the advantages in manufacturing and preservation as a clinical product. 3D printing technology has been used to manufacture scaffolds to provide a favored cellular environment, and allows for custom shapes and consistent quality (Mironov, V. et al. (2003) “Organ Printing: Computer Aided Jet-Based 3d Tissue Engineering,” Trends Biotechnol 21(4):157-61). To further enhance the cartilage healing process, the present disclosure provides for a bioactive acellular, 3D-printed poly(L-lactide-co-caprolactone) (PLCL) scaffold implant, which is preferably surface modified with aggrecan.
In accordance with the present disclosure, a scaffold implant is specifically designed to guide the ingrowth and differentiation of host MSCs, thus providing a template for proper cartilage regeneration. Disclosed implants are engineered to fully exploit the regenerative potential of host stem cells and, unlike previous approaches, enable the recapitulation of the cartilage zonal architecture that has been shown to impact cartilage physiology and patient functional outcomes.
In accordance with disclosed embodiments, a bioactive acellular scaffold implant is provided that is suitable for use in combination with microfracture surgery in order to further enhance cartilage regeneration. The disclosed treatment methods substantially improved type II cartilage regeneration (10×), tissue thickness (1.9×), GAG content (4.4×), and number of chondrocytes present (3.2×), as compared to conventional microfracture techniques, and showed significantly improved cartilage repair as compared to conventional techniques. The fabrication of the disclosed surface-modified scaffold was done prior to surgery with no extensive additional surgical preparation required, and thus provides substantial benefit as compared to conventional microfracture procedures. Moreover, as compared to cell-based treatments and conventional scaffold designs, the advantages associated with the covalently modified acellular scaffolds disclosed herein demonstrated superior characteristics in treating large cartilage defects in a much more cost and labor effective manner as compared to conventional strategies.
When taking into consideration the type of polymer that should be utilized to fabricate the scaffold, the ability to withstand compressive mechanical stimuli is important. In comparison to prior scaffolds composed solely of poly(lactic acid) (PLA) and/or poly(lactic-co-glycolic acid) (PLGA), the disclosed scaffolds comprise one or more layers formed from poly(L-lactide-co-caprolactone) (PLCL). The scaffolds exhibited surprisingly superior properties, including toughness comparable to that of native cartilage (see, e.g., Athanasiou, K. A. et al. (1991) “Interspecies Comparisons Of In Situ Intrinsic Mechanical Properties Of Distal Femoral Cartilage,” J Orthop Res 9(3):330-40). Assessment of the extracellular matrix accumulation on the cell—inoculated PLCL scaffolds disclosed herein demonstrated that the PLCL material significantly enhanced chondrogenic differentiation (see, e.g., Jung, Y. et al. (2008) “Cartilage Regeneration With Highly-Elastic Three-Dimensional Scaffolds Prepared From Biodegradable Poly(L-Lactide-Co-Epsilon-Caprolactone,” Biomaterials 29(35):4630-6).
Interestingly, the addition of aggrecan significantly lowered the compressive modulus of the wet PLCL scaffold, possibly due to the water retaining effect on plasticizing during mechanical testing. Proteoglycans are a defining factor in force-transmission, growing healthy ECM, and determining the viability of chondrocytes in cartilage. The approach disclosed herein provides for the novel use of aggrecan to strengthen the biological function of a 3D-printed scaffold for tissue regeneration. A prominent indication of aggrecan aiding the chondrocyte microenvironment was increased cell adhesion as quantified by DNA extraction (10×) and flow cytometry (13.6×) from whole bone marrow.
The presence of aggrecan increases the link protein on the cell surface and thus improves cell attachment (see Yang, B. B. et al. (1998) “Aggrecan And Link Protein Affect Cell Adhesion To Culture Plates And To Type II Collagen,” Matrix Biol 16(9):541-61). As the main proteoglycan component in native articular cartilage, the unique complex structure of aggrecan provides functionality that other molecules cannot replicate (Jin, R. et al. (2010) “Synthesis And Characterization Of Hyaluronic Acid-Poly(Ethylene Glycol) Hydrogels Via Michael Addition: An Injectable Biomaterial For Cartilage Repair,” Acta Biomater 6(6):1968-77; Nettles, D. L. et al. (2004) “Photocrosslinkable Hyaluronan As A Scaffold For Articular Cartilage Repair,” Ann Biomed Eng 32(3):391-7). In particular, aggrecan provides binding sites to better recruit stem cells and growth factors to aggregate on the scaffold surface and increase cell attachment. Its function of trapping water in the cartilage microenvironment also enhances the physiological environment for the stem cells released from microfracture.
Thus, in accordance with embodiments of the present disclosure, the scaffold surface is preferably modified with aggrecan. Scaffolds were seeded with bone marrow and the attached cell population analyzed using a customized centrifugation assay. After in vitro evaluation, scaffold functionality was evaluated in a lapine model with microfracture, in comparison with the non-functionalized scaffold and the standard procedure. Animal movement ability and regenerated tissue quality were also assessed, as discussed in further detail below.
In a centrifugation assay, an established force was applied to separate the adhered and non-adhered cells to achieve a precise quantification of the cell population (Ferlin, K. M. et al. “Separation of Mesenchymal Stem Cells Through a Strategic Centrifugation Protocol,” Tissue Engineering Part C-Methods 22(4):348-359). The present disclosure is also directed to a centrifugation system including a specialized lid for the well plate. Fabrication processes have been developed to create microenvironments to control cell attachment and organization on a 3D scaffold. Different scaffolds were fabricated based on the applications, and then cells were seeded on top of the scaffolds. To evaluate the cell function, after certain time the cells need to be isolated from the scaffolds and processed for further analysis. It is important to ensure the complete isolation of cells for different groups in order to achieve precise and reliable results. In prior techniques, the separation of the adhered and non-adhered cells was simply done by trypsin and buffer washes, which is labor intensive particularly when handling large amounts of sample. Moreover, a force must be applied to demonstrate the different adhesion and adsorption. Conventional techniques and devices fail to allow for batch processing of adhered and suspended cell separation from 3D scaffolds.
The present disclosure therefore provides for a novel ccentrifugation system and method designed for the separation of cells from 3D printed scaffolds, including scaffolds fabricated in accordance with disclosed embodiments. The system includes a covering or well plate “lid” specially designed to be compatible with standard well plate (e.g., including 12, 24, 48, etc. well plate) and allowing for the separation of adherent and non-adherent cell populations during centrifugation. In some embodiments, the lid includes an element to capture 3D printed scaffolds to separate three distinct cell populations.
In some embodiments, a cell population is attached to the bottom of the well plate and inserted scaffold, and grown in suspension in the media. The centrifugation system is superior to conventional techniques given it provides the ability to separate multiple samples simultaneously without risk of cross-contamination. The disclosed centrifugation system allows for easy recovery of multiple components, which are readily sterilizable and thus reusable, and the capability of separating multiple cell types based on adhesion characteristics without the need for additional fluorescent markers or chemical agents. In some implementations, the system includes surfaces functionalized with various materials to separate increasingly complex cell populations or facilitate culture directly within the system.
In some embodiments, the lid for the centrifugation system is 3D printed. The 3D printed lid is sized to fit the tissue culture well plate utilized, and designed to hold the 3D printed scaffolds in place while collecting the non-adhered bone marrow portion during centrifugation. For example, the lid may be configured to fit snugly into a standard 24 well plate. The lid may be 3D printed, e.g., using ENVISIONTEC™ Eshell 300 material. The lid is preferably designed with a slight interference fit to allow for centrifugation and separation of adherent and non-adherent populations.
In some embodiments, the system and device are sterilizable and thus reusable if desired, and capable of separating multiple cell types based on adhesion characteristics without the need for additional fluorescent markers or chemical agents. In some embodiments, the surfaces are functionalized, e.g., with plasma (e.g. oxygen, ammonia, etc.), small molecules and/or self-assembled monolayers (e.g. gold-thiol), and/or protein coating (e.g. fibronectin). The device is amenable to functionalization with other materials, as would be appreciated by one of skill in the art. Implementing additional surface functionality may be used to separate increasingly complex cell populations and/or to facilitate culture directly within the separator device.
In accordance with embodiments of the present disclosure, the lid may be fabricated from various biomaterials, e.g., such as polystyrene. Depending on the material, the lid is fabricated via 3D printing or molding techniques known in the art. The centrifugation system and device allows for efficient separation of adherent and suspension cells from various 3D constructs. With surface modification, the system may be utilized to further isolate different cell populations. One of skill in the art would appreciate that the specific dimensions and configuration of the lid may vary depending on the application. Thus, the lid may be readily manufactured with different dimensions, e.g., to fit different well plates. In addition, the lid may be fabricated (e.g., via 3D printing) to cover all or part of the wells as needed. For example, the lid may be fabricated to provide for partial coverage of the well plate (e.g., conventional 48-well plate or 24-well plate).
With aggrecan functionalization, cell attachment efficiency was significantly increased, as demonstrated by the disclosed data. Notably, the presence of aggrecan promoted cell adhesion regardless of cell type. Further, the percentage of hMSCs among all adhered cells was not affected by the aggrecan.
New Zealand White (NZW) rabbits were used as an animal model to further evaluate scaffold biofunctionality. NZW rabbits are well-established for use in orthopedic surgery models because the condyle of mature rabbits is large enough to incorporate scaffold treatment with feasible surgical procedures. The thickness of the cartilage layer in rabbits is also enough to prevent the potential intrinsic repair compared to mouse or rat model (Chu, C. R. et al. (2010) “Animal Models For Cartilage Regeneration And Repair,” Tissue Eng Part B Rev 16(1):105-15). The cartilage regeneration process varies by gender as sex hormones play a role in regulating chondrocyte function and collagen production. Specifically, female rabbits are associated with higher incidences of osteoarthritis (Garstang, S. V. & Stitik, T. P. (2006) “Osteoarthritis: Epidemiology, Risk Factors, And Pathophysiology,” Am J Phys Med Rehabil 85(11 Suppl): S2-14). Therefore, female rabbits were used as the model for the cartilage repair studies in order to provide for consistent cartilage physiology properties and a model associated with the disease prevalence.
Although successful, the random cell differentiation induced by microfracture often leads to the formation of fibrocartilage, which is weaker than native articular cartilage and therefore results in the loss of desired tissue function (see Steadman, J. et al. (2001) “Microfracture: Surgical Technique And Rehabilitation To Treat Chondral Defects,” Clinical Orthopaedics and Related Research 391:S362-S369; see also Mithoefer, K. et al. (2005) “The Microfracture Technique For The Treatment Of Articular Cartilage Lesions In The Knee—A Prospective Cohort Study,” Journal of Bone and Joint Surgery-American Volume 87A(9):1911-1920; and Bae, D. et al. (2006) “Cartilage Healing After Microfracture In Osteoarthritic Knees,” Arthroscopy-the Journal of Arthroscopic and Related Surgery 22(4):367-374). To overcome the lack of chemical cues in microfracture surgery for the released cellular component, an aggrecan-functionalized acellular scaffold was incorporated into the defect area in accordance with disclosed methodologies.
Cell based treatments require an extra surgery to source autologous cells as well as additional time for in vitro maintenance to expand the autologous or allogenic cells (Xu, X. et al. (2017) “In Vivo Repair Of Full-Thickness Cartilage Defect With Human Ipsc-Derived Mesenchymal Progenitor Cells In A Rabbit Model,” Experimental and Therapeutic Medicine 14(1):239-245). In contrast, the acellular scaffolds disclosed herein may be combined with microfracture in a single surgery with little additional preparation time, substantially improving microfracture' s potential for clinical translation over the use of cell-based approaches.
Some minor surgical challenges were encountered using the small animal (lapine) model. During the implantation procedure into the rabbit model, the scaffolds were fixed in place using fibrin glue. Although most of the scaffolds were degraded after 8 weeks, some minor debris was found outside the defect area. Due to the limited soft tissue in the trochlear groove after creating the critical defect, suturing the scaffold in place was not feasible. However, it is believed that this issue would be readily remedied and/or eliminated with a larger animal model and/or by incorporating a more effective biocompatible glue, which would also improve the integration of the local tissue after implantation (Drobnic, M. et al. (2006) “Comparison Of Four Techniques For The Fixation Of A Collagen Scaffold In The Human Cadaveric Knee,” Osteoarthritis Cartilage 14(4):337-44).
According to previous studies, the tissue regenerated by microfracture matures after 8 weeks (Frisbie, D. et al. (2006) “Effects Of Calcified Cartilage On Healing Of Chondral Defects Treated With Microfracture In Horses,” American Journal of Sports Medicine 34(11):1824-1831). Therefore, the knee joints were harvested and evaluated 8 weeks post operation. Clinically, cartilage thickness is an important factor for determining the progression of osteoarthritis. Cartilage thickness was therefore measured to evaluate the regeneration potential of the different treatments. Optical coherence tomography (OCT) presents advantages over ultrasound including higher resolution, and has been used as a non-invasive method to assess tissue qualitatively and quantitatively, including rabbit cartilage (Rogowska, J. et al. (2003) “Cartilage Thickness Measurements From Optical Coherence Tomography,” J Optical Society of America a-Optics Image Science and Vision 20(2):357-367; Han, C. W. et al. (2003) “Analysis Of Rabbit Articular Cartilage Repair After Chondrocyte Implantation Using Optical Coherence Tomography,” Osteoarthritis and Cartilage 11(2): 111-121). OCT therefore provided an effective mechanism to evaluate the 3D structure of the regenerated tissue in addition to histology.
The BBB score was initially developed to evaluate locomotion after spinal cord injury in rats (Basso, D. et al. (1995) “A Sensitive And Reliable Locomotor Rating-Scale For Open-Field Testing In Rats,” Journal of Neurotrauma 12(1):1-21). The application in a rabbit model has also been reported, although a lower range of scores were applied in the study (Yoshil, S. et al. (2009) “Functional Restoration Of Rabbit Spinal Cord Using Collagen Filament Scaffold,” Journal of Tissue Engineering and Regenerative Medicine 3(1):19-25). The rabbits in the present studies exhibited much higher recovery levels, so the BBB scale was adjusted to accurately assess differences in healthy and unhealthy walking patterns. The tail balance criterion specific to rats was modified to standing abilities in this application to better differentiate recovery rates among the rabbits. In general, the score each group received matched the histological performance, although more distinct differences among treatment groups could be reflected with a more tailored scale system focusing on post-orthopedic operation. Moreover, considering the challenges of the functional level of assessment, it is reasonable that such differences were not shown during the early stages of the tissue regeneration. Even though further evaluation may establish a locomotion assessment post orthopedic surgery for rabbits, it is believed that the studies disclosed herein were the first time that tissue function was investigated through movement.
Covering the microfracture area is believed to result in a more robust cartilage regeneration. The mechanism of microfracture to treat cartilage defects is based on the released MSCs from the bone marrow and cellular differentiation with the support of growth factors and cytokines from the platelets (Shapiro, F. et al. (1993) “Cell Origin And Differentiation In The Repair Of Full-Thickness Defects Of Articular Cartilage,” J Bone Joint Surg Am 75(4):532-53). The presence of the scaffolds covering the defect area following the microfracture structurally stabilized the blood clots and resulted in better integrated tissue repair and more robust cartilage regeneration (see, e.g., Erggelet, C. et al. (2009) “Formation Of Cartilage Repair Tissue In Articular Cartilage Defects Pretreated With Microfracture And Covered With Cell-Free Polymer-Based Implants,” J Orthop Res 27(10):1353-60; see also Hoemann, C. D. et al. (2007) “Chitosan-Glycerol Phosphate/Blood Implants Elicit Hyaline Cartilage Repair Integrated With Porous Subchondral Bone In Microdrilled Rabbit Defects,” Osteoarthritis Cartilage 15(1):78-89).
In the present studies, subjects treated with an unmodified PLCL scaffold showed an overall improvement compared to subjects treated with microfracture alone. From OCT 3D scanning, the addition of the PLCL scaffold led to a smoother and more homogeneous regenerated layer of cartilage. Both Alcian blue and safranin-O staining demonstrated the improved proteoglycan formation with the treatment of the bioactive scaffold as compared to conventional microfracture alone.
The evaluation of cartilage-bone interface is important to assess the overall success of the surgical procedure (Shao, X. et al. (2006) “Repair of Large Articular Osteochondral Defects Using Hybrid Scaffolds And Bone Marrow-Derived Mesenchymal Stem Cells In A Rabbit Model,” Tissue Eng 12(6):1539-51; Shao, X. et al. (2006) “Evaluation Of A Hybrid Scaffold/Cell Construct In Repair Of High-Load-Bearing Osteochondral Defects In Rabbits,” Biomaterials 27(7):1071-80; Ho, S.T. et al. (2010) “The Evaluation Of A Biphasic Osteochondral Implant Coupled With An Electrospun Membrane In A Large Animal Model,” Tissue Eng Part A 16(4):1123-41). In the disclosed cartilage defect model, other than the signs from the microfracture drill, no visible difference in the subchondral bone area was observed among all the groups. An important function of aggrecan, as a major proteoglycan in native cartilage, is to mediate the chondrocyte-chondrocyte and chondrocyte-matrix interactions by stabilizing the cell-substratum interactions and sustaining the bioactive molecules in serum and fluids (Kiani, C. et al. (2002) “Structure And Function Of Aggrecan,” Cell Res 12(1):19-32). The G1 domain of aggrecan also plays a role in chondrocyte apoptosis (Cao, L. et al. (1998) “Expression Of The GI Domain Of Aggrecan Interferes With Chondrocyte Attachment And Adhesion,” Matrix Biol 17(5):379-92; Cao, L. et al. (1999) “Chondrocyte Apoptosis Induced By Aggrecan GI Domain As A Result Of Decreased Cell Adhesion,” Exp Cell Res 246(2): 527-37). As such, it is believed that this phenomenon resulted in the subjects treated with aggrecan-PLCL exhibiting a significantly enhanced healing process, as shown by the increased thickness of regenerated cartilage and increased chondrocytes and GAGs presence shown in the histology. More deposition of type II collagen in the regenerated area further confirmed the quality of the newly formed tissue and the importance of incorporating aggrecan to improve the biological function of the scaffold.
The native zonal structure of cartilage tissue is also taken into consideration in studies to restore the desired tissue function (see, e.g., Guo, T. et al. (2017) “Three-Dimensional Printing Articular Cartilage: Recapitulating The Complexity Of Native Tissue,” Tissue Engineering Part B-Reviews 23(3):225-236). The thickness of cartilage tissue in the rabbits limited the possibility of implanting a multi-zonal scaffold (
In accordance with the present disclosure, the PLCL scaffold functionalized with aggrecan effectively guided MSCs and/or growth factors to the defect site(s) and strengthened cartilage regeneration. As demonstrated by the data, the 3D printed scaffolds with aggrecan improved cartilage regeneration ten times more than microfracture alone or in combination with a non-functionalized scaffold. Congruently, aggrecan increased cell attachment to the scaffold by ten times in comparison to a non-functionalized scaffold and thus substantially improved cartilage repair.
The disclosed acellular scaffold devices: i) are inexpensive to fabricate; ii) may be readily approved by regulatory agencies due in part to the absence of any cell component, and to the use of established biomaterials; and iii) may be readily combined with current procedures such as microfracture, providing for a quick and smooth translation from bench-to-bedside. The disclosed scaffold devices may be readily tailored for articular cartilage repair, including hyaline cartilage which is anticipated to experience the fastest growth during the next 10-year period due to high susceptibility of damage to hyaline cartilage (e.g. osteoarthritis in aging population) and the increase in sport injuries. The disclosed methods are much less invasive as compared to other surgical treatment strategies such as mosaicplasty and joint arthroplasty, and, different from osteochondral allograft transfer arthroscopic chondroplasty, the disclosed methods do not involve the use of non-self, material/cells that may cause an adverse immune response.
In addition, the combination of the disclosed scaffold devices with microfracture is expected to result in lower reoperation rate in light of the more robust cartilage repair demonstrated. Given the improved outcome, the disclosed methods are also expected to shorten the rehabilitation period post-surgery, and accordingly result in lower costs for post-operative care (e.g. physical therapy). The disclosed treatment methods entail shorter recovery periods, lower reoperation rates, and lower need for invasive surgery (e.g. arthroplasty) at reoperation as compared to standard microfracture surgery. As such, the disclosed techniques provide for a much more convenient and time-savings repair procedure for patients as well as lower healthcare costs.
Additional characteristics and features of the present disclosure will be further understood through reference to the following additional examples and discussion, which are provided by way of further illustration and are not intended to be limiting of the present disclosure.
EXAMPLES Example 1 Scaffold FabricationAn exemplary scaffold implant device suitable for cartilage implant was fabricated in a layer-by-layer fashion via extrusion-based 3D printing. A scaffold implant customized for a particular patient may be readily fabricated starting from a CAD model that can be either designed using commonly available software, or directly generated from imaging data routinely collected in the clinics (e.g. MRI, CAT scan, etc.). The scaffold was extruded in three different zonal layer patterns (
During microfracture surgery, a series of holes are drilled in the subchondral bones, resulting in the release of cells and ECM from the bone marrow into the cartilage defect. While microfracture successfully promotes neo-cartilage formation, it is also associated with the undesirable formation of fibrous cartilage at articulating surfaces that does not possess the desired mechanical properties, as discussed above. In accordance with the present disclosure, the scaffold device is specifically designed to guide the ingrowth and differentiation of host stem cells, thus provide a template for proper cartilage regeneration. The scaffold was engineered to exploit the regenerative potential of host stem cells and, unlike previous approaches, enable the regeneration of the cartilage zonal architecture. The scaffold is suitable for use in combination with microfracture surgery, and thus may be seamlessly incorporated into current surgical procedures without substantial modification to such procedures and/or to pre/post-operative care.
The use of natural materials allows for high biocompatibility but low mechanical compliance of the implant with the cartilage defect. Scaffolds were fabricated from a composition comprising poly(L-lactide-co-caprolactone) (PLCL) and amine end capped poly(lactic-co-glycolic acid) (NH2-PLGA). Differently from natural hydrogels, both materials withstand mechanical stimuli and PLCL matches mechanical properties of toughness relative to native cartilage. The scaffolds therefore possess cartilage-like mechanical properties while maintaining a high level of biocompatibility.
The presence of amine end capped PLGA in the formulation allows functionalization with ECM molecules upon fabrication. Aggrecan, an ECM protein abundant in cartilage, was successfully conjugated to a PLCL scaffold using standard EDC chemistry (
An extensive study was performed to assess the effect of fabrication parameters (e.g., polymer molecular weight, pressure and temperature of extrusion, etc.) on the scaffold architecture, degradation, and mechanical properties (Guo, T. et al. (2017) “3D Printing PLGA: A Quantitative Examination Of The Effects Of Polymer Composition And Printing Parameters On Print Resolution,” Biofabrication 9(2):024101). A statistical model was built to reveal the correlation and predominant factors that determine 3D printing precision. The model showed a strong relationship between the actual and predicted precision under different combinations of printing conditions and material compositions.
The scaffold implant was fully characterized for its ability to support cell proliferation and chondrogenic differentiation of stem cells in vitro and their ability to guide cell infiltration and alignment according to the designed pattern in vivo (
Unlike complicated nanofabrication processes used to achieve surface patterns in many other conventional devices, the desired polymer molecule and cell alignment was readily achieved in the disclosed scaffolds via the use of extrusion 3D printing and without any additional processing. The cell orientation was maintained in vivo in a subcutaneous scaffold implant, making the disclosed approach ideal for combining with surgical procedures that release native stem cells (e.g., microfracture) for improved cartilage repair. The results on the effect of printed pattern on cell organization and differentiation demonstrated that the disclosed approach may be readily utilized to create implants with controlled cell and ECM arrangement in order to achieve optimized biological function for chondrogenesis.
Example 2An animal study was conducted in order to evaluate the performance of microfracture surgery when combined with the disclosed scaffold implant. As demonstrated herein, the addition of an acellular PLCL scaffold device following microfracture provided effective guidance to the stem cells released from the bone marrow and resulted in substantially enhanced cartilage regeneration. The results were even more significant when using a PLCL scaffold functionalized with aggrecan, and resulted in an even higher cell/ECM retention from the bone marrow via microfracture, thicker cartilage formation, and deposition of ECM (collagen type I, glycosaminoglycans) similar to that of native cartilage.
3D-Printed Aggrecan-Functionalized ScaffoldA 3D-printed scaffold functionalized with aggrecan demonstrated a substantial improvement in the quality of regenerated cartilage tissue during microfracture as compared to conventional techniques. As the main proteoglycan component of native articular cartilage tissue, aggrecan provides binding sites to recruit stem cells and aggregates growth factors to the scaffold surface, further promoting cell attachment. The physiological environment for the MSCs released from microfracture was enhanced by the water and biological components trapped by the aggrecan, mimicking the native cartilage microenvironment.
An aim of the study was to design and verify the scaffold surface modification with aggrecan. The bone marrow and attached cell population's interaction with the scaffold were analyzed using a customized centrifugation assay described herein. After in vitro evaluation, the scaffold functionality was tested in a lapine model, comparing the standard microfracture, with non-functionalized and functionalized scaffolds. As demonstrated by the data, the combined acellular bioactive scaffold and microfracture treatment significantly improved the cartilage tissue repair outcome as compared to conventional techniques and without excessive labor or complicated procedures.
Scaffold FabricationPoly(L-lactide-co-caprolactone) (PLCL, PolySciTech, West Lafayette, IN) with a lactic acid:caprolactone ratio of 70:30 and molecular weight of 45 kD to 55 kD was combined with 15% (w/w) amine end capped poly(lactic-co-glycolic acid) (amine-PLGA, PolySciTech) to make a PLCL-amine scaffold material by grinding the polymers together to form a homogeneous mixture. Scaffolds were fabricated using the 3D BIOPLOTTER™ prototyping tool (EnvisionTEC, Gladbeck, Germany) using direct melt extrusion technique (Guo, T. et al. (2017) “3D Printing PLGA: A Quantitative Examination Of The Effects Of Polymer Composition And Printing Parameters On Print Resolution,” Biofabrication 9(2):024101). The scaffoold material composition of 15% w/w PLGA-amine and 85% PLCL was based on an estimation of amine groups needed for the reaction. The scaffold inner pattern was programmed using the provided ENVISIONTEC® software (EnvisionTEC, Inc., Dearborn, MI). For printing, material was loaded in the printing cartridge and melted at 155° C. for extrusion at 6.5 bar with an average speed of 4 mm/s using a 0.2 mm inner diameter stainless steel needle. Scaffolds had dimensions of 3 mm (length)×3 mm (width)×0.5 mm (height) (
Aggrecan was covalently bound to the printed scaffolds via covalent bonding of EDC and sulfo-NHS (
Bruker ADVANCE III 600™ nuclear magnetic resonance (Bruker Corp., Billerica, MA) spectrometer with BBFO gradient probe was used for the 1H NMR experiments. Polymer samples were dissolved in dimethyl sulfoxide-d6 (CD3SOCD3). The internal solvent signal δ (CD3SOCD3)=2.5 ppm was used as reference. Aggrecan was dissolved in D2O at 1 mg/ml. Printed scaffold functionalized with aggrecan (PLCL-aggrecan) was dissolved in CD3SOCD3/deuterium oxide (D2O) at 2:1 ratio for better solubility. Solvent suppression pulse sequence was used to suppress solvent 1H signal for aggrecan and PLCL-aggrecan samples to achieve the optimum sample signals. A total of 64 scans were used for 1H experiments, and 128 scans for solvent suppression experiments.
Compressive Mechanical TestingMechanical testing was performed on the printed PLCL-amine and aggrecan functionalized PLCL-amine scaffolds (N=6 for each group) using an Instron mechanical testing system (33R/4465) (Instron Engineering Corp., Norwood, MA). The scaffolds were wet in PBS for 24 hours before the compressive mechanical properties were evaluated. All samples were compressed by a 50N load cell at a displacement rate of 0.5 mm/min with a pre-load of approximately 0.05N until the machine protection distance was reached. For every 10 ms, compressive stress and strain were recorded and calculated based on the original cross-sectional area and height of the wet scaffold. The compressive modulus was then determined by definition, which is the slope of the linear region of the stress-strain curve before failure.
Cell Culture and SeedingHuman MSCs (hMSCs, RoosterBio, Frederick, MD) were expanded in RoosterNourish high performance MSC media according to the manufacturer's recommendations and grew 10 times within 7 days of culturing. After reaching the recommended density, cells were lifted with trypsin-EDTA (Gibco-LifeSciences, Gaithersburg, MD) and centrifuged at 200×g for 10 minutes to form a cell pellet. Cells collected in a cell pellet were re-suspended in RoosterNourish media at a concentration of 10 million cells/mL. Approximately 1 million cells were seeded onto each scaffold by adding 100 μL of concentration cell solution to cover the scaffold. Scaffolds were kept at 37° C. for 4 hours to allow for attachment to the scaffold surface. Cell culture media was changed every other day for cell maintenance.
Staining and Confocal ImagingLive/dead assays were used to assess cell viability and morphology. Scaffolds were washed with Hank's buffered saline solution (HBSS, Life Technologies, Carlsbad, CA) for 5 minutes to remove excess media and other reagents. Cells on the scaffolds were stained with 2 μM ethidium homodimer and 4 μM calcein AM (Life Technologies, Carlsbad, CA) combined with HBSS and incubated for 30 minutes in the dark. Scaffolds were then washed with HBSS, soaked in 200 μL of 4% paraformaldehyde for each scaffold, and left to incubate for 15 minutes. Scaffolds were washed with 200 μL of phosphate-buffered saline (PBS) and stored in PBS until they could be imaged using a confocal microscope.
DNA QuantificationhMSCs were lifted from scaffolds using trypsin-EDTA (Gibco-LifeSciences, Gaithersburg, MD) and centrifuged into a cell pellet. DNA was isolated from the hMSCs using a DNeasy Plus MiniKit (Qiagen, Frederick, MD). DNA was quantified using a PICOGREEN™ dsDNA Assay Kit (Quanti-iT, ThermoFisher Scientific, Waltham, MA). DNA isolates from the DNeasy kit were normalized to standard curve generated from the PICOGREEN™ dsDNA Assay to quantify DNA amounts.
Centrifugation Device FabricationLid Fabrication: A lid was designed using SOLIDWORKS® software (Dassault Systémes, Vélizy-Villacoublay, France) for a slight press fit into the inner wells of a standard 24 well plate (
Whole human unprocessed bone marrow (Lonza, Walkersville, MD) was seeded onto the printed scaffolds placed in ultra-low attachment 24-well plate (Thermo Fisher Scientific, Waltham, MA). Equal amount of Dulbecco's modified Eagle's medium (Life Technologies, Gaithersburg, MD) supplemented with 1.0% v/v penicillin/streptomycin (Life Technologies, Gaithersburg, MD) and 0.1 mM nonessential amino acids (Life Technologies, Gaithersburg, MD) was added to each well. The plate was incubated at 37° C., 5% CO2, and 80% humidity for 24 hours to allow attachment.
Centrifugation AssayThe centrifugation assay system set up is shown in
Flow cytometry was conducted to analyze the cell population isolated from the bone marrow. The cells were re-suspended at a concentration of approximately 5 million/mL. Cells and controls were stained using Human MSC Analysis Kit (BD STEMFLOW™; Becton, Dickinson and Co., Franklin Lakes, NJ) following the manufacturer's instruction. The data was analyzed using FLOWJO™ (FlowJo LLC, Ashland, OR) to gate the populations. Briefly, 100 μL of each sample was mixed with 20 μL of the hMSC Positive Cocktail (CD90 FITC, CD73 APC, and CD105 PerCP-Cy5.5) and 20 μL of the hMSC Negative Cocktail (CD34 PE, CD45 PE, CD11b PE, CD19 PE, and HLA-DR PE) and incubated at 4° C. in the dark for 30 min. The mixed cell suspensions were washed twice with 500 μL of PBS containing 1% bovine serum albumin (BSA). The cells were suspended in 500 μL of PBS containing 1% BSA and analyzed using a BD FACSCANTO II™ cell analyzer (Becton, Dickinson and Co., Franklin Lakes, NJ). The positive control using hMSCs (Lonza, Walkersville, MD) and the negative isotype controls was used to set up the gate for all samples. Cells of each group were counted during 90-second run at medium rate, as controlled volume.
Animal Surgery and Tissue Harvest14 female New Zealand White Rabbits (NZW, 7-9 lb) (Covance Inc., Princeton, NJ) were anesthetized with Ketamine (35-40 mg/kg)/Xylazine (2-5 mg/kg). A total of four groups were evaluated including: i) defect control group; ii) microfracture only group; iii) microfracture with unmodified scaffold group; and iv) microfracture with aggrecan-functionalized scaffold group. Three rabbits were included in each group, with one extra in the groups treated with scaffold as a preparation for potential unknown side effects. Post sedation isoflurane delivered from a precision vaporizer (1.5-3%) in 100% O2 was administered via face mask during the surgery. The right hind leg served as the defect limb while the left hind leg was not treated in this unilateral defect model. A midline knee incision was made and a medial parapatellar approach performed to the knee. The patella was dislocated laterally to expose the articular surface of the trochlea. Bupivacaine 0.25% (up to 2 mg/kg) was injected to the trochlear grove prior to patella dislocation as local analgesia. A full thickness cartilage defect in the center of the trochlear groove was created that measured approximately 3 mm in length and width. In the microfracture groups, five holes were drilled to a ˜8 mm depth with a 0.75 mm K-wire. In the two experimental scaffold groups, modified or unmodified polymer constructs were inserted into the cartilage defect site and secured with fibrin glue (TISSEEL™; Baxter, Deerfield, IL). Scaffold implants were fabricated as described above; however, due to the relatively thin cartilage tissue present in the rabbit model (˜500 micron), the scaffold implant utilized for the animal study included the top zone scaffold structure (
The joints from both knees were harvested after 8 weeks. The left knee tissue was used as healthy control in the evaluation assays. Euthanasia was performed with Beuthasol (Pentobarbital IV, 100 mg/kg) in the auricular vein after a ketamine 20-40 mg/kg and 2-5 mg/kg xylazine subcutaneous injection. After euthanasia, the bilateral knee joints (femur end and chondyle) were harvested for further analysis. The animal study, including the locomotion test (protocol #0717009), was approved by Institutional Animal Care and Use Committee (IACUC) at University of Maryland, School of Medicine, Baltimore, MD. All animal studies including the follow up evaluation were conducted as blind tests.
Animal Locomotion Test and EvaluationAfter two weeks (starting on week 3 following surgery recovery per veterinarian advice), the rabbits were taken to an open field restricted by a 1.4 m×0.5 m fence to allow for locomotion evaluation. Videos were recorded of test subjects from the top and side view on weeks 3, 4, 5, 6, and 8 post-surgery. Videos were analyzed and test subjects were evaluated by a modified Basso, Beattie, and Bresnahan (BBB) Locomotor Rating Scale (Table 1) to quantify the subjects' movement, coordination, and weight bearing abilities (
The frequency-domain OCT imaging system was equipped with a wavelength-swept laser light source centered at 1310 nm with 100 nm bandwidth (Tang, Q. et al. (2016) “Depth-Resolved Imaging Of Colon Tumor Using Optical Coherence Tomography And Fluorescence Laminar Optical Tomography,” Biomedical optics express 7(12):5218-5232). The wavelength-swept frequency was 16 kHz and the output power was 17 mW. 3% of the laser output power went into a Mach-Zehnder interferometer and generated a frequency-clock signal with uniformly spaced optical frequency to trigger sampling the OCT signal. The system applied a fiber-based Michelson interferometer and about 97% of the laser power was split evenly to the sample and reference arms of the interferometer. The signals reflected from the sample and reference arms encountered at the fiber couple and formed interference fringes, which encoded different frequencies, were then received by a balanced detector. Depth-resolved tomography was achieved by performing a fast Fourier transform of the interference fringes (Tang, Q. et al. (2014) “Real-Time Epidural Anesthesia Guidance Using Optical Coherence Tomography Needle Probe,” Quantitative Imaging in Medicine and Surgery 5(1):118-124). The scanning field of view (FOV) was set at 5 mm×5 mm to cover the entire defect area with 800 pixels in each direction (
After harvesting and OCT scanning, tissue samples were fixed in buffered 4% paraformaldehyde solution containing 1% sucrose. Samples were decalcified, dehydrated, and embedded in paraffin. The samples were sectioned to 5 μm thick slices and placed on positively charged glass slides. For H&E staining (
The EDC-NHS reaction to covalently bind the carboxyl groups on the side chains of aggrecan and the amine groups on the printed PLCL-amine scaffold is shown in
After confirming the presence of functional groups on the scaffold, the biological response of surface modifying the scaffolds was evaluated. hMSCs were seeded onto PLCL scaffold, PLCL-amine scaffold, and aggrecan modified scaffold. The three groups presented DNA concentrations of 231.91±5.73 ng/ml, 386.86±3.73 ng/ml, and 597.24±8.02 ng/ml, respectively. From the DNA quantification data, after 7 days the aggrecan modified scaffold showed three times more DNA content than the unmodified scaffold (
After demonstrating that aggrecan functionalization improved cell attachment, whole bone marrow was seeded onto the scaffold to evaluate the attached cell population. A cell centrifugation assay isolated the adhered cells from whole bone marrow to determine cell phenotype through flow cytometry (
The adhered/attached cell count in controlled 90 second flow for PLCL-amine-aggrecan modified scaffold, PLCL-amine scaffold, and PLCL scaffold was 286377, 21113, and 32551, respectively (
The above experiments demonstrated substantially improved cell recruitment as a result of aggrecan functionalization. The actual healing process associated with microfracture is more difficult to mimic in the in vitro environment. Accordingly, the animal model was used to further test the therapeutic effect of the scaffold. The animal surgery was completed successfully following the approved protocol. All 14 rabbits survived with overall good health condition until the termination of the study. The knee joints were harvested after 8 weeks for further analysis including tissue evaluation, OCT scanning and histology. The implanted scaffolds were mostly degraded after 8 weeks. A thin layer of regenerated cartilage tissue visibly appeared to cover the defect area in the experimental groups. With the additional scaffold, and especially when functionalized, the newly regenerated cartilage tissue showed a much healthier appearance (
In the locomotion test, rabbit movement was recorded at each time point from both side view and top view throughout the eight week observation period. The locomotion behavior was evaluated using a modified BBB score scale as described above. While the defect control group demonstrated no movement improvement over the course of the study, all experimental groups showed an increasing trend of scores. Rabbits treated with aggrecan functionalized scaffold or plain scaffold had comparable scores with rabbits treated with traditional microfracture. In this study, with modified BBB score to better represent the rabbit locomotion behavior, all rabbits received a score higher than 13 (out of 21). Considering the relatively good recovery observed with regard to movement ability with treatments, no significant differences among the experimental groups were observed at each time point. All experimental groups with treatments had an average score of around 19 on week eight (
After 8 weeks, the femur end of the joints was harvested for OCT scanning and histological analysis (
Histological staining was performed for the harvested joints after embedding and decalcification. In the H&E staining, the nuclei were stained dark purple by hematoxylin and the eosinophilic structures mainly composed of intracellular and extracellular proteins were counterstained by eosin Y as pink. The regenerated cartilage tissue appeared as lighter pink compared to the subchondral bone tissue (
The Alcian blue staining further confirmed the therapeutic effect of the aggrecan-functionalized scaffold (
The aggrecan functionalization resulted in 20 times more GAG production than the non-treated group and 4.4 times more GAG production compared to the microfracture treatment. The production of proteoglycan is proportional to the safranin-O staining in normal cartilage. The healthy control showed a strong affinity to safranin-O to form a red complex with a top layer of counter stained green color. Compared with regular microfracture treatment, the scaffold treatment showed a higher level of proteoglycans, although safranin-O was reported as a not very sensitive indicator when the GAGs were depleted, for example, in the newly formed tissue layer (
A major concern of microfracture is the variance in success among cases because the released MSCs and biomolecules have limited guidance and support in the defect area. The three rabbits in the microfracture group also showed relatively large standard deviations in multiple assessments. However, such variance is reduced by incorporating the aggrecan-PLCL scaffold, indicating the consistency of the treatment effect. To further evaluate the quality of the regenerated cartilage tissue, immunostaining of type II collagen was performed (
A multilayer scaffold composed of poly(L-lactide-co-caprolactone) (PLCL) and amine end-capped poly(lactic-co-glycolic acid) (amine-PLGA) was successfully printed with high resolution. The disclosed approach creates a regenerative environment with a robust bone-cartilage interface within an osteochondral implant. It is believed that co-printing the architecture at the bone-cartilage interface improves the adhesion between the bone and cartilage layers by increasing the contact points between the print strands of the same mixture at the interface.
Preliminary experiments demonstrated the feasibility of interface printing via a 3D printing strategy (
A 3D cylinder model with a dimension of 8.0 mm (diameter)×1.6 mm (height) were designed using SOLIDWORKS® software (Dassault Systémes, Vélizy-Villacoublay, France). A 0.4 mm inner diameter (ID) needle is used to print the scaffolds. According to the manufacturer's (EnvisionTEC, Gladbeck, Germany) instruction, the scaffold is sliced into layers with a slice thickness equal to 80% of the ID of the needle before printing. A second sliced 3D cylinder model is superimposed over the first cylinder model to establish the interface layer using BIOPLOTTER™ RP prototyping tool (EnvisionTEC, Gladbeck, Germany). The interface layer spans two print layers co-printed with the two polymer formulations (
Four patterns for 3D printing fabrication were evaluated to assess the mechanical robustness at the osteochondral implant interface (
An effective method to regenerate critical articular defects was developed by utilizing a 3D-printed bioactive scaffold in combination with microfracture surgery. The surface of the 3D-printed polymer scaffold was covalently modified with aggrecan to improve cell adherence and maintain cell function at the scaffold surface. With the functionalized scaffold, the microfracture outcome was significantly enhanced by providing extra support to the stem cells and growth factors released from bone marrow during the healing process. The additional aggrecan scaffold treatment resulted in a substantially thicker and healthier regenerated cartilage layer. The biofunctionalized acellular scaffold combined with microfracture is thus suitable for various clinical applications, and substantially improves current treatment strategies (e.g., microfracture procedures) without the need for additional surgeries and with a relatively low cost compared to cell-based therapies.
All identified publications and references mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication was specifically and individually indicated to be incorporated by reference in its entirety. While the invention has been described in connection with exemplary embodiments thereof, it will be understood that it is capable of further modifications and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure as come within known or customary practice within the art to which the invention pertains and as may be applied to the features hereinbefore set forth.
Claims
1. A method of treating a cartilage defect in a subject, comprising the steps of:
- creating an opening(s) in a subchondral bone in the subject underlying the cartilage defect and into bone marrow thereof to permit release of mesenchymal stem cells (MSCs) from the bone marrow; and
- applying an acellular polymeric scaffold functionalized with aggrecan onto the cartilage defect, thereby guiding the MSCs released from the bone marrow through the openings and into the scaffold.
2. The method of claim 1, wherein said step of creating the opening(s) comprises a microfracture procedure.
3. The method of claim 1, comprising the step of fabricating the scaffold from a composition comprising poly(L-lactide-co-caprolactone) (PLCL).
4. The method of claim 1, comprising the step of fabricating the scaffold via three-dimensional (3D) printing.
5. A well plate lid comprising a base and a plurality of wells extending outwardly therefrom, said plurality of wells receivable in correspondingly configured wells of a cell-culture plate.
6. The well plate lid of claim 5, wherein said plurality of wells of said lid are releasably securable in said wells of said cell-culture plate via interference fit.
7. The well plate lid of claim 5, wherein at least one well of said plurality of wells of said lid comprises a retaining member extending outwardly from an interior sidewall of said well, wherein said retaining member extends between opposing surfaces of said interior sidewall.
8. The well plate lid of claim 7, wherein said retaining member has a generally cross-shaped configuration in plan view.
9. A centrifugation system comprising the well plate lid of claim 5, and a correspondingly configured cell-culture well plate.
Type: Application
Filed: May 19, 2023
Publication Date: Sep 28, 2023
Applicant: University of Maryland, College Park (College Park, MD)
Inventors: Ting Guo (Cambridge, MA), John Patrick Fisher (Kensington, MD), Hannah Baker (Baltimore, MD), Max Jonah Lerman (Silver Spring, MD), Robert Choe (Arlington, VA)
Application Number: 18/320,760