Methods and apparatus for recycling glass products using submerged combustion

- JOHNS MANVILLE

A method for recycling glass mat waste, wound rovings, and other products includes providing a source of glass mat, or a plurality of rovings, for example on a roll, and routing the glass mat or rovings into a submerged combustion melter. An unwind system and a pair of powered nip rolls, powered conveyors, or other arrangement may work in combination to provide a substantially consistent rate of material into the melter. The melter may operate under less than atmospheric pressure to avoid fumes escaping the melter. A slot in the melter allows ingress of the glass mat or rovings into the melter, and a glass mat former such as a folder may be used to ensure that the mat fits through the slot. Alternatively, the glass mat may be cut by a slitter prior to entering the slot.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
BACKGROUND OF THE DISCLOSURE

1. Field of Disclosure

The present disclosure relates generally to the field of combustion furnaces and methods of use, and more specifically to improved submerged combustion melters and methods of use in producing molten glass from recycled glass mat and other rolled glass materials, such as wound rovings of continuous glass filament.

2. Related Art

Glass mat products such as fiber glass and mat and insulation mat are characterized by a nonwoven mat of glass fibers held together with a binder. Recycling or reclamation of glass mat products has been disclosed in and practiced previously. Many of these disclosed methods involve crushing the glass mat to a maximum fiber or particle size prior to re-melting. Other processes involve a heating step prior to grinding whereby the binder is first burned off without melting the glass fibers. In older processes the binders were typically desired to be removed prior to re-melting because the remnants of the binders may cause production of unsatisfactory glass products.

Submerged combustion has been proposed in several patents for application in commercial glass melting, including U.S. Pat. Nos. 4,539,034; 3,170,781; 3,237,929; 3,260,587; 3,606,825; 3,627,504; 3,738,792; 3,764,287; 6,460,376; 6,739,152; 6,857,999; 6,883,349; 7,273,583; 7,428,827; 7,448,231; 7,565,819, and 7,624,595; published U.S. Pat. Application numbers 2004/0168474; 2004/0224833; 2007/0212546; 2006/0000239; 2002/0162358; 2009/0042709; 2008/0256981; 2007/0122332; 2004/0168474; 2004/0224833; 2007/0212546; and 2010/0064732; and published PCT patent application WO/2009/091558, all of which are incorporated herein by reference in their entireties. In submerged combustion glass melting, the combustion gases are injected beneath the surface of the molten glass and rise upward through the melt. The glass is heated at a higher efficiency via the intimate contact with the combustion gases. However, submerged combustion burners have not heretofore been used to recycle or reclamate glass mat products without first crushing the mat products to reduce the size of the glass fibers. Materials melted with submerged combustion burners may include at least silica-bearing material (such as sand), alkaline earth metal oxide-bearing material (such as limestone or dolomite), boron-oxide-bearing material (such as borax), sodium oxide raw material (such as sodium carbonate), alumina raw material (such as feldspar), and/or cullet.

U.S. Pat. No. 4,397,692 discloses methods and apparatus for the reclamation of inorganic fibers from waste continuous strips of inorganic fibers. The '692 patent mentions another, previous recapture technique is to feed the recaptured fibers directly into the melting furnace with virgin glass batch. The difficulty with this approach, according to the '692 patentees, is that a major amount of the cost of the fiber is not in the material but, in the cost of production and, by melting the fibers, that amount is lost. In addition, the cost of processing the fibers for feeding to a batch furnace is equal to or greater than the cost of the batch it replaces, making this process economically unattractive. According to the Abstract of the '692 patent, a binding agent, such as an organic binder, must be removed before the fibers can be reused or further processed. One or more layers of continuous strips are conveyed to a heating zone where the strips are supported along a predetermined path as a heating fluid is drawn rapidly through the strips to decompose the binder. Unfortunately, the '692 patent suggests that in the case where binder is still present on the fibers in unacceptable levels, these non-reclaimable fibers may be dumped for subsequent disposal. This practice is now unacceptable, due to the lack of landfill space available, and due to the justifiably increased concern for the environment. The '692 patent does not disclose, teach or suggest roll-feeding of fiber glass mat scrap or rovings, or folding shoes, or nip rollers being used to feed fiberglass mat scrap to a melter.

U.S. Pat. No. 4,422,862 describes a process for feeding scrap glass to a glass melting furnace. The scrap glass is fed onto a blanket of batch in the furnace so that organics are burned off before the scrap melts. The scrap glass is either first hammermilled or crushed before it is fed to the glass melting furnace, or enters the furnace in the form of fluffy, fine textured scrap that floats on the batch blanket. There is no teaching or suggestion of roll-feeding, or folding shoes, or of nip rollers being used to feed the scrap to the melter. There is disclosed use of a conveyor belt, but the patentee states “In FIG. 2, scrap glass is manually fed onto belt conveyor 12 at a controlled rate. The cullet glass previously has been processed through a crusher (not shown).” Clearly, crushing is involved, as the patentee states “the crushing advantages are fluffy fine textured scrap that floats on the batch cover allowing good penetration and binder burn-off by furnace gases.”

U.S. Pat. No. 4,432,780 discloses a method of reclaiming chemically coated glass scrap. The scrap is introduced into the oxidizing atmosphere of a hydrocarbon-fuel fired glass melting furnace. Some of the glass is melted with the unmelted portion being melted with the glass batch as it moves through the furnace. The patentees state that “The scrap glass can be introduced into the furnace in any suitable form. Preferably, it will be introduced in particulate form up to about 1¼ inch screen size by means of a blowing wool machine, one or more machines being used depending upon the quantity of scrap glass being introduced.” Despite the broad introductory statement that “the scrap glass can be introduced in any suitable form”, the particulate form is the only form that is disclosed. Thus, this patent fails to disclose, teach, or suggest roll-feeding, or folding shoes, or of nip rollers being used to feed scrap to the melter.

U.S. Pat. No. 4,309,204 discloses a process and apparatus for remelting scrap glass fibers. The removal of binder and remelting of the scrap are carried out in one operation, and the resulting molten scrap fibers are fed directly into a conventional glass melting furnace. Granular raw glass batch also is fed into the glass melting furnace. FIGS. 1 and 2 of the '204 patent show a glass feeder feeding glass strands to a melter through rotating shaft feeders. Thus, this patent fails to disclose, teach, or suggest roll-feeding of fiber glass mat scrap or rovings, or folding shoes, or nip rollers being used to feed fiberglass mat scrap to a melter.

JP 2000351633 is another example method and apparatus for recycling fiber glass waste. The reference discloses use of a burner to feed waste glass fiber to a glass melting tank furnace. The recycling apparatus is provided with a hopper for storing waste glass fiber cut to proper size and a constant-rate discharging apparatus to discharge the waste material at a constant rate. This reference fails to disclose, teach, or suggest roll-feeding of fiber glass mat scrap or rovings, or folding shoes, or nip rollers being used to feed fiberglass mat scrap to a melter.

JP 2002120224 discloses a method for recycling glass fiber-reinforced thermoplastic resin characterized by feeding the glass fiber-reinforced thermoplastic resin for recycling to a vessel wherein a non-recycled thermoplastic resin is under melted condition. Thus, the approach here is not to feed the fiber glass reinforced waste into a glass tank furnace, but into a tank of molten thermoplastic resin. This reference therefore fails to disclose, teach, or suggest roll-feeding of fiber glass mat scrap or rovings, or folding shoes, or nip rollers being used to feed fiberglass mat scrap to a glass tank melter.

It would be an advance in glass mat recycling to develop methods and apparatus for recycling and/or reclaiming glass mat and similar items, such as wound roving of continuous glass filament, that avoid the significant processing needed to shred such materials and/or mill it into a fine powder for re-melting, while taking advantage of the efficiency of submerged combustion burners, to increase melter throughput and produce high quality molten glass.

SUMMARY

In accordance with the present disclosure, methods and apparatus for practicing the methods are described for recycling rolled glass materials, such as glass mat and wound rovings, that reduce or eliminate the need to shred or crush such glass materials before feeding same into a glass tank melter, and that take advantage of the efficiency of submerged combustion burners.

Various terms are used throughout this disclosure. A “web” refers to woven and nonwoven mats of glass fiber, and is typically, but not necessarily, rolled up into a roll. “Mat” as used herein refers to lofted and non-lofted (essentially flat) nonwoven glass fiber articles. An example of a lofted nonwoven is glass fiber insulation batting, while an example of a non-lofted nonwoven is E-Glass mat as is commonly used in roofing shingles and other high-performance applications. “Roving” as used herein refers to a plurality of filaments of glass fiber substantially parallel to a major axis of the roving. “Scrap” is a general term for glass fiber mat pieces, rovings, or other rolls of material that, for one reason or another, is off-specification or trimmed from a larger web of useable material, and would otherwise be landfilled, but for the teaching of the present disclosure. “Submerged” as used herein means that combustion gases emanate from burners under the level of the molten glass; the burners may be floor-mounted, wall-mounted, or in melter embodiments comprising more than one submerged combustion burner, any combination thereof (for example, two floor mounted burners and one wall mounted burner). As used herein the term “combustion gases” means substantially gaseous mixtures of combusted fuel, any excess oxidant, and combustion products, such as oxides of carbon (such as carbon monoxide, carbon dioxide), oxides of nitrogen, oxides of sulfur, and water. Combustion products may include liquids and solids, for example soot and unburned liquid fuels. “Oxidant” as used herein includes air and gases having the same molar concentration of oxygen as air, oxygen-enriched air (air having oxygen concentration of oxygen greater than 21 mole percent), and “pure” oxygen, such as industrial grade oxygen, food grade oxygen, and cryogenic oxygen. Oxygen-enriched air may have 50 mole percent or more oxygen, and in certain embodiments may be 90 mole percent or more oxygen. Oxidants may be supplied from a pipeline, cylinders, storage facility, cryogenic air separation unit, membrane permeation separator, or adsorption unit.

A first aspect of this disclosure is a method comprising:

    • a) providing a source of glass mat or wound roving; and
    • b) routing the glass mat or wound roving at a substantially consistent feed rate into a submerged combustion melter and melting the glass mat or roving.

As used herein the phrase “substantially consistent feed rate” means that the rate of glass mat or roving entering the melter is, in certain embodiments, constant, but may in certain embodiments vary from constant by a small percentage, for example +/−1 percent, or +/−5 percent, or +/−10 percent. In certain embodiments, the mass of a particular web of glass mat or roving per unit of length may not vary significantly as the web or roving is fed into the melter, and in these embodiments the web or roving feed rate (unit of length per unit of time) may not need to vary significantly in order to maintain a substantially consistent feed rate (mass per unit of time) of glass mat or roving into the melter. In certain other embodiments, the mass of a particular web of glass mat or roving may vary with length (for example the web or rovings may decrease in mass as the web or rovings is/are unwound from a roll), and in these instances the linear speed of the web or rovings may be increased so that the feed rate of material into the melter remains substantially consistent over time. In certain methods and apparatus of this disclosure the substantially consistent feed rate may be accomplished by unwinding a web of the glass mat or one or more wound rovings off of one or more rolls using a combination of an unwind system and a pair of powered nip rolls, conveyers, or other arrangement. In certain embodiments, the powered nip rolls could be supplemented with or replaced by a nip compression conveyor, or opposed conveyors compressing the product to accomplish the same aim. To avoid repetition, the term “powered nip rolls” will be used herein, with the understanding that these other arrangements could be used just as well. In certain embodiments, the mat or rovings may be chopped downstream or integral to the nip rollers and/or conveyors and prior to entering the glass tank furnace.

The source of glass mat may be selected from the group consisting of nonwovens and woven materials. Nonwovens may be lofty or non-lofty. High loft is thick and fluffy, low loft is thin and dense. The higher the loft, the better the insulation characteristic.

In certain embodiments, the nonwoven is a non-lofty mat, such as a mat of E-Glass fibers. Such mats are often used in constructing roofing shingles.

In certain embodiments, the method comprises providing a web of substantially continuous glass fibers bound together randomly at points where adjacent fibers touch using a binder.

In certain embodiments, the glass mat and/or rovings enter the submerged combustion melter through a slot in the melter and then directly into molten glass within the melter.

In certain embodiments, more particular to embodiments where glass mat is processed may be rout the glass mat through a forming or converting device prior to entering the powered nip rolls so that the glass mat fits through the slot. One example of such a forming or converting device is a folding device. Another example of a forming device is a cutting or slitting device wherein the glass mat is cut to width prior to entering the powered nip rolls so that the glass mat fits through the slot.

In certain embodiments, the unwinding of the roll comprises changing rolls on the fly, which may comprise splicing a first web unwinding from a first roll to a second web unwinding from a second roll.

In certain methods the melting comprises at least one burner directing combustion products into a melting zone under a level of molten glass in the zone.

In certain methods at least some heat used for the melting of the glass mat and/or roving comprises heat from combustion of at least some of the binder.

In certain methods the melter is operated at a pressure less than atmospheric pressure. These methods may ensure that any combustion products generated during the melting of the glass remain in the system and do not escape through the feed slot.

Another aspect of this disclosure are apparatus comprising:

    • a) a source of rolled glass mat or wound roving material;
    • b) a submerged combustion melter having a slot for feeding the glass mat or wound roving material into the melter and one or more submerged combustion burners; and
    • c) a pair of powered nip rolls for feeding the glass mat or wound roving material into the melter at a substantially consistent rate.

In certain apparatus embodiments, the apparatus comprises an unwind subsystem for unwinding the rolled glass mat or wound roving in combination with the powered nip rolls. Certain embodiments include a glass mat forming device positioned prior to the powered nip rolls so that the glass mat is formed to fit through the slot. Folding, cutting and/or slitting the mat to an acceptable width to fit the mat through the slot are examples of forming devices. Two or more functions of folding, cutting, and the like may be combined in one forming device.

Certain apparatus embodiments of this disclosure may include melters comprising fluid-cooled panels, wherein the slot is covered and integral with a fluid-cooled panel of a wall of the melter. In certain other embodiments, the slot may be integral with an exhaust port or roof of the melter. In certain embodiments, the slot may comprise one or more hinged doors or panels. In certain other embodiments the slot may comprise one or more sliding doors or panels. Certain embodiments may comprise both hinged and sliding doors or panels. The hinged and sliding doors may be water cooled, or cooled by other fluids.

In practice, the submerged combustion melter may include one or more submerged combustion burners comprising one or more oxy-fuel combustion burners.

In all apparatus embodiments the sources of oxidant and fuel may be one or more conduits, pipelines, storage facility, cylinders, or, in the case of oxidant, ambient air. Secondary and tertiary oxidants, if used may be supplied from a pipeline, cylinder, storage facility, cryogenic air separation unit, membrane permeation separator, or adsorption unit such as a vacuum swing adsorption unit.

Certain embodiments may comprise using oxygen-enriched air as the primary oxidant, the fuel is a gaseous fuel, the gaseous fuel being selected from methane, natural gas, liquefied natural gas, propane, carbon monoxide, hydrogen, steam-reformed natural gas, atomized oil or mixtures thereof, and the oxygen-enriched air comprising at least 90 mole percent oxygen. In certain embodiments the oxygen may be injected into an intermediate mixture upstream of a combustion chamber of a burner, while in other embodiments the oxygen may be injected into the combustion chamber.

Apparatus and process embodiments of the disclosure may be controlled by one or more controllers. For example, burner combustion (flame) temperature may be controlled by monitoring one or more parameters selected from velocity of the fuel, velocity of the primary oxidant, mass and/or volume flow rate of the fuel, mass and/or volume flow rate of the primary oxidant, energy content of the fuel, temperature of the fuel as it enters the burner, temperature of the primary oxidant as it enters the burner, temperature of the effluent, pressure of the primary oxidant entering the burner, humidity of the oxidant, burner geometry, combustion ratio, and combinations thereof. Apparatus and processes of this disclosure may also measure and/or monitor feed rate of glass mat or wound roving, mass of glass mat or wound roving per unit length, web or roving linear speed, and combinations thereof, and use these measurements for control purposes. Exemplary apparatus and methods of the disclosure comprise a combustion controller which receives one or more input parameters selected from velocity of the fuel, velocity of the primary oxidant, mass and/or volume flow rate of the fuel, mass and/or volume flow rate of the primary oxidant, energy content of the fuel, temperature of the fuel as it enters the burner, temperature of the primary oxidant as it enters the burner, pressure of the oxidant entering the burner, humidity of the oxidant, burner geometry, oxidation ratio, temperature of the effluent and combinations thereof, and employs a control algorithm to control combustion temperature based on one or more of these input parameters.

Apparatus and methods of the disclosure will become more apparent upon review of the brief description of the drawings, the detailed description of the disclosure, and the claims that follow.

BRIEF DESCRIPTION OF THE DRAWINGS

The manner in which the objectives of the disclosure and other desirable characteristics can be obtained is explained in the following description and attached drawings in which:

FIGS. 1 and 2 are schematic side elevation views, with some parts broken away, of two apparatus and process embodiments in accordance with the present disclosure;

FIG. 3 is one embodiment of a process control schematic diagram for the apparatus and processes of FIGS. 1 and 2; and

FIGS. 4-8 illustrate perspective and side elevation (FIG. 6) views of four embodiments of slots useful in the apparatus and processes in the present disclosure.

It is to be noted, however, that the appended drawings are not to scale and illustrate only typical embodiments of this disclosure, and are therefore not to be considered limiting of its scope, for the disclosure may admit to other equally effective embodiments.

DETAILED DESCRIPTION

In the following description, numerous details are set forth to provide an understanding of various apparatus and process embodiments in accordance with the present disclosure. However, it will be understood by those skilled in the art that the apparatus and processes of using same may be practiced without these details and that numerous variations or modifications from the described embodiments may be possible which are nevertheless considered within the appended claims.

Referring now to the figures, FIGS. 1 and 2 are schematic side elevation views, with some parts broken away, of two apparatus and process embodiments in accordance with the present disclosure. The same numerals are used for the same or similar features in the various figures. In the views illustrated in FIGS. 1 and 2, it will be understood in each case that the figures are schematic in nature, and certain conventional features are not illustrated in order to illustrate more clearly the key features of each embodiment.

Embodiment 100 of FIG. 1 comprises a melter 2, which may be any of the currently known submerged combustion melter designs as exemplified in the patent documents previously incorporated hereby reference in the Background of the present disclosure, or may be one of those described in assignee's currently pending patent application Ser. No. 12/817,754, filed Jun. 17, 2010, incorporated herein by reference. Melter 2 includes a roof 3, side walls 5, a floor 7, one or more submerged combustion burners 8, an exhaust chute 12, one or more molten glass outlets 28 (only one being illustrated), and fluid-cooled panels 30 comprising some or all of side walls 5. Molten glass 4 is sometimes referred to herein simply as the “melt”, and has a level 6 in melter 2. Melter 2 is typically supported on a plant floor 10.

In accordance with the present disclosure, first embodiment 100 comprises one or more roll stands 14 (only one being illustrated), which in turn supports one or more rolls 16 of glass mat. Roll stand 14 connects to roll 16 though an unwind driver and brake combination 15, which are known in the roll-handling art. Roll stand 14 is supported by a plant floor 10′, which may be the same or different floor as floor 10 which supports melter 2 (in other words, roll stand 14 may be supported by a second floor of a plant or facility, although this is not necessary to practice the methods and apparatus of this disclosure).

Other components of embodiment 100 include a glass mat forming device 20, a set of powered nip rolls 24, and a glass mat feed slot 26. In certain embodiments, as mentioned previously, powered nip rolls 24 may be supplemented with or replaced by a nip compression conveyor, or opposed conveyors compressing the product to accomplish the same aim. Forming device 20 is optional, but when present, may be selected from any one or more devices providing one or more functions, for example, but not limited to cutting, slitting (cutting in longitudinal direction), folding, shaping, compacting, pressing, coating, spraying, heating, cooling, and the like, and combinations thereof An example of a single device providing two functions would be a device providing both heating and folding. The powered nip rolls 24 may also provide some degree of heating, cooling, compressing, and other forming function or functions, although their primary function is to draw the glass mat web off of roll 16, in conjunction with unwind driver/brake combination 15. In certain embodiments, as mentioned previously, the powered nip rolls may include cutting knives or other cutting components to cut or chop the mat (or roving, in those embodiments processing rovings) into smaller length pieces prior to entering melter 2.

In operation of embodiment 100 of FIG. 1, glass mat 18 is unwound from a roll of glass mat in conjunction with powered nip rolls 24. Glass mat 18 may be, for example, but not limited to glass mat scrap. Glass mat 18 optionally is routed through one or more forming devices 20 to form a formed glass mat 22. Powered nip rolls 24 then route formed glass mat 22 through feed slot 26, which feeds the glass mat directly into the molten glass 4. Glass mat 22 may be fed into molten glass 4 from above the level 6, as illustrated in embodiment 100 of FIG. 1. Alternatively, in certain embodiments, all or a portion of glass mat 22 may be routed under the level 6 of molten glass 4. Whether the glass mat is fed directly to molten glass 4 through level 6, or all or a portion is fed under level 6 depends on factors such as the configuration and pull rate of melter 2.

Referring now to FIG. 2, embodiment 200 is illustrated. In embodiment 200, melter 2 has a slightly different exhaust chute 12 configuration, and in embodiments such as this, it may be more convenient to position feed slot 26 in exhaust chute 12 and feed glass mat 22 (or wound roving) through feed slot 26 and exhaust chute 12, as illustrated. A dashed, phantom portion of feed slot 26 is illustrated as an extension, which may be present in certain embodiments to ensure that glass mat web 22 enters molten glass 4 in a desired location. Any location is possible, but for the limitation that glass mat is molten before leaving molten glass outlet 28. Also provided in this embodiment is a glass batch feeder 32. Glass batch feeders are well-known in this art and require no further explanation. A glass mat web cutting device 21 is provided in this embodiment.

FIG. 3 is a schematic diagram of one embodiment of a process control scheme for the apparatus and processes of FIGS. 1 and 2. A master process controller 300 may be configured to provide any number of control logics, including feedback control, feed-forward control, cascade control, and the like. The disclosure is not limited to a single master process controller 300, as any combination of controllers could be used. The controller may be selected from PI controllers, PID controllers (including any known or reasonably foreseeable variations of these), and computes a residual equal to a difference between one or more measured values 36, 38, 40, 42, 44, 46, 48, 50, 52, 54, 56, 50, and 60 and one or more set points 34, for example feed rate (mass/time) of glass mat or rovings into melter 2, to produce one or more outputs 62, 64, 66, 68, and 70 to one or more control elements. The controller 300 may compute the residual continuously or non-continuously. Other possible implementations of the disclosure are those wherein the controller comprises more specialized control strategies, such as strategies selected from internal feedback loops, model predictive control, neural networks, and Kalman filtering techniques. In FIG. 3, the lines numbered 36, 38, 40, 42, 44, 46, 48, 50, 52, 54, 56, 50, and 60 may represent sensors, for example sensors for the following parameters, which are merely exemplary examples:

    • 36=weight of mat or roving (mass/length);
    • 38=unwind speed of mat or roving (length/time);
    • 40=temperature of melt 4;
    • 42=temperature of fuel entering a burner;
    • 44=temperature of oxidant entering a burner;
    • 46=temperature of exhaust form melter;
    • 48=level of melt in melter;
    • 50=mass flow rate of fuel entering burner;
    • 52=mass flow rate of primary oxidant entering burner;
    • 54=energy content of fuel;
    • 56=humidity of primary oxidant;
    • 58=width of glass mat web or roving from roll;
    • 60=flow rate of melt out of melter;

The lines numbered 62, 64, 66, 68, and 70 may represent control signals and actuators, respectively, for outputs for the following parameters, which are merely exemplary:

    • 62=corrected mass flow rate of fuel to burners;
    • 64=corrected mass flow of oxidant to burners;
    • 66=corrected speed of unwinding of roll of glass mat or roving;
    • 68=corrected nip roll speed; and
    • 70=corrected flow of melt out of melter.

Other parameters may be included as inputs, such as weight of roll, burner geometry, and combustion ratio.

The term “control”, used as a transitive verb, means to verify or regulate by comparing with a standard or desired value. Control may be closed loop, feedback, feed-forward, cascade, model predictive, adaptive, heuristic and combinations thereof. The term “controller” means a device at least capable of accepting input from sensors and meters in real time or near-real time, and sending commands directly to burner control elements, and/or to local devices associated with burner control elements and glass mat feeding devices able to accept commands. A controller may also be capable of accepting input from human operators; accessing databases, such as relational databases; sending data to and accessing data in databases, data warehouses or data marts; and sending information to and accepting input from a display device readable by a human. A controller may also interface with or have integrated therewith one or more software application modules, and may supervise interaction between databases and one or more software application modules.

The controller may utilize Model Predictive Control (MPC). MPC is an advanced multivariable control method for use in multiple input/multiple output (MIMO) systems. An overview of industrial Model Predictive Control can be found on the Internet, which will direct the reader to many sources, including textbooks. MPC computes a sequence of manipulated variable adjustments in order to optimise the future behavior of the process in question. At each control time k, MPC solves a dynamic optimization problem using a model of the controlled system, so as to optimize future behavior (at time k+1, k+2 . . . k+n) over a prediction horizon n. This is again performed at time k+1, k+2 . . . MPC may use any derived objective function, such as Quadratic Performance Objective, and the like, including weighting functions of manipulated variables and measurements. Dynamics of the process and/or system to be controlled are described in an explicit model of the process and/or system, which may be obtained for example by mathematical modeling, or estimated from test data of the real process and/or system.

FIGS. 4-8 illustrate non-limiting examples of slots useful in apparatus and methods of this disclosure. FIG. 4 illustrates a perspective view of embodiment 80, having a single door or panel 82 which swings open vertically away from melter 2 when it is desired to feed a non-woven 22 into melter 2 for recycling. Door or panel 82 is secured to melter 2 by a hinge 84 which ruins along the bottom edge of door 82, and handles 86, 87 are provided in this embodiment to allow personnel to open and close door 82. Alternatively, or in addition, a mechanical opening and closing mechanism may be provided, such as that discussed in reference to FIG. 7, or equivalent thereof.

FIG. 5 illustrates a perspective view of another embodiment 90 within this disclosure, this embodiment comprising a pair of horizontally opening doors 92, 94, also featuring hinged connections 93, 95, connecting the doors to melter 2, respectively.

FIG. 6 illustrates a side elevation view of an embodiment 110 of a vertical sliding door or panel 112 which may function as a slot in accordance with the present disclosure, where panel 112 is integral with a fluid-cooled wall 30 of melter 2. Sliding door or panel 112 may be held open or closed at a variety of vertical positions, for example using a locking device, clamp or similar mechanism 114. This would allow nonwovens of various thicknesses to be processed. Sliding door or panel 112 may itself be fluid-cooled.

FIG. 7 illustrates a perspective view of yet another embodiment 120 of a slot useful in the apparatus and methods of this disclosure. Embodiment 120 comprises a vertically sliding door or panel 122, and a horizontally sliding door or panel 124. Vertical door or panel 122 slides in vertical guides 126, 128, while horizontal door or panel 124 slides in guides 129. In order to open and close, or adjust the height of vertical door or panel 122, handles 130, 132 may be provided. Alternatively, or in addition thereto, a pneumatic, hydraulic, or electronic actuator 134 may be provided. A similar actuator 136 may be provided to open, close, or adjust width of the slot. Embodiment 120 allows adjustment of either height, width, or both height and width to accommodate various stock sizes (not shown).

FIG. 8 illustrates a perspective view of yet another embodiment 150 of a slot useful in the apparatus and methods of this disclosure for melting one or more rovings 152 of glass fiber. In the case of rovings 152, the adjustable vertically sliding door or panel 122 and horizontally sliding door or panel 124 may be adjusted to accommodate different number and/or sizes of rovings.

Those having ordinary skill in this art will appreciate that there are many possible variations of the slot openings described herein, and will be able to devise alternatives and improvements to those described herein that are nevertheless considered to be within the claims of the present patent. For example, in the embodiments illustrated in FIGS. 7 and 8, a second vertical sliding door or panel could be provided, moving from the bottom of the slot up to meet the one illustrated, or this upwardly moving door or panel could completely replace the one illustrated. Similarly, a second horizontal sliding door or panel could be provided, sliding in from the right-hand side of the slot, or this sliding door or panel could replace the horizontal one illustrated. Sets of ceramic or metallic rollers could be provided to supplement the guides, or completely replace the guides.

Submerged combustion melters useful in the practice of the methods and apparatus of this description may take any number of forms, including those described n assignee's co-pending application Ser. No. 12/817,754, previously incorporated herein by reference, which describes sidewalls forming an expanding melting zone formed by a first trapezoidal region, and a narrowing melting zone formed by a second trapezoidal region, wherein a common base between the trapezoid defines the location of the maximum width of the melter.

Another important feature of apparatus of this disclosure is the provision of submerged combustion burners 8 in melter 2. In embodiments 100 and 200, burners 8 are floor-mounted burners. In certain embodiments, the burners may be positioned in rows substantially perpendicular to the longitudinal axis (in the melt flow direction) of melter 2. In certain embodiments, burners 8 are positioned to emit combustion products into molten glass in the melting zone of melter 2 in a fashion so that the gases penetrate the melt generally perpendicularly to the floor. In other embodiments, one or more burners 8 may emit combustion products into the melt at an angle to the floor, as taught in assignee's pending Ser. No. 12/817,754.

Melters useful in apparatus in accordance with the present disclosure may also comprise one or more wall-mounted submerged combustion burners, and/or one or more roof-mounted burners. Roof-mounted burners may be useful to pre-heat the melter apparatus melting zone, and serve as ignition sources for one or more submerged combustion burners 8. Melter apparatus having only wall-mounted, submerged-combustion burners are also considered within the present disclosure. Roof-mounted burners may be oxy-fuel burners, but as they are only used in certain situations, are more likely to be air/fuel burners. Most often they would be shut-off after pre-heating the melter and/or after starting one or more submerged combustion burners 8. In certain embodiments, if there is a possibility of carryover of particles to the exhaust, one or more roof-mounted burners could be used to form a curtain to prevent particulate carryover. In certain embodiments, all submerged combustion burners 8 are oxy/fuel burners (where “oxy” means oxygen, or oxygen-enriched air, as described earlier), but this is not necessarily so in all embodiments; some or all of the submerged combustion burners may be air/fuel burners. Furthermore, heating may be supplemented by electrical heating in certain embodiments, in certain melter zones. In certain embodiments the oxy-fuel burners may comprise one or more submerged combustion burners each having co-axial fuel and oxidant tubes forming an annular space therebetween, wherein the outer tube extends beyond the end of the inner tube, as taught in U.S. Pat. No. 7,273,583, incorporated herein by reference. Burners 8 may be flush-mounted with floor 7 in certain embodiments. In other embodiments, such as disclosed in the '583 patent, a portion of one or more of the burners 8 may extend slightly into the melt above floor 7.

In certain embodiments, melter side walls 5 may have a free-flowing form, devoid of angles. In certain other embodiments, side walls 5 may be configured so that an intermediate location may comprise an intermediate region of melter 2 having constant width, extending from a first trapezoidal region to the beginning of a narrowing melting region. Other embodiments of suitable melters are described in the above-mentioned '754 application.

As mentioned herein, useful melters may include refractory fluid-cooled panels. Liquid-cooled panels may be used, having one or more conduits or tubing therein, supplied with liquid through one conduit, with another conduit discharging warmed liquid, routing heat transferred from inside the melter to the liquid away from the melter. Liquid-cooled panels may also include a thin refractory liner, which minimizes heat losses from the melter, but allows formation of a thin frozen glass shell to form on the surfaces and prevent any refractory wear and associated glass contamination. Other useful cooled panels include air-cooled panels, comprising a conduit that has a first, small diameter section, and a large diameter section. Warmed air transverses the conduits such that the conduit having the larger diameter accommodates expansion of the air as it is warmed. Air-cooled panels are described more fully in U.S. Pat. No. 6,244,197, which is incorporated herein by reference. In certain embodiments, the refractory fluid cooled-panels are cooled by a heat transfer fluid selected from the group consisting of gaseous, liquid, or combinations of gaseous and liquid compositions that functions or is capable of being modified to function as a heat transfer fluid. Gaseous heat transfer fluids may be selected from air, including ambient air and treated air (for air treated to remove moisture), inert inorganic gases, such as nitrogen, argon, and helium, inert organic gases such as fluoro-, chloro- and chlorofluorocarbons, including perfluorinated versions, such as tetrafluoromethane, and hexafluoroethane, and tetrafluoroethylene, and the like, and mixtures of inert gases with small portions of non-inert gases, such as hydrogen. Heat transfer liquids may be selected from inert liquids which may be organic, inorganic, or some combination thereof, for example, salt solutions, glycol solutions, oils and the like. Other possible heat transfer fluids include steam (if cooler than the oxygen manifold temperature), carbon dioxide, or mixtures thereof with nitrogen. Heat transfer fluids may be compositions comprising both gas and liquid phases, such as the higher chlorofluorocarbons.

The feed slot described in accordance with the present disclosure may be constructed using refractory cooled panels. Both the feed slot and the side walls may include a thin refractory lining, as discussed herein. The thin refractory coating may be 1 centimeter, 2 centimeters, 3 centimeters or more in thickness, however, greater thickness may entail more expense without resultant greater benefit. The refractory lining may be one or multiple layers. Alternatively, melters described herein may be constructed using cast concretes such as disclosed in U.S. Pat. No. 4,323,718. The thin refractory linings discussed herein may comprise materials described in the 718 patent, which is incorporated herein by reference. Two cast concrete layers are described in the 718 patent, the first being a hydraulically setting insulating composition (for example, that known under the trade designation CASTABLE BLOC-MIX-G, a product of Fleischmann Company, Frankfurt/Main, Federal Republic of Germany). This composition may be poured in a form of a wall section of desired thickness, for example a layer 5 cm thick, or 10 cm, or greater. This material is allowed to set, followed by a second layer of a hydraulically setting refractory casting composition (such as that known under the trade designation RAPID BLOCK RG 158, a product of Fleischmann company, Frankfurt/Main, Federal Republic of Germany) may be applied thereonto. Other suitable materials for the refractory cooled panels, melter refractory liners, and refractory block burners (if used) are fused zirconia (ZrO2), fused cast AZS (alumina-zirconia-silica), rebonded AZS, or fused cast alumina (Al2O3). The choice of a particular material is dictated among other parameters by the melter geometry and type of glass to be produced.

Burners useful in the melter apparatus described herein include those described in U.S. Pat. Nos. 4,539,034; 3,170,781; 3,237,929; 3,260,587; 3,606,825; 3,627,504; 3,738,792; 3,764,287; and 7,273,583, all of which are incorporated herein by reference in their entirety. One useful burner, for example, is described in the 583 patent as comprising a method and apparatus providing heat energy to a bath of molten material and simultaneously creating a well-mixed molten material. The burner functions by firing a burning gaseous or liquid fuel-oxidant mixture into a volume of molten material. The burners described in the 583 patent provide a stable flame at the point of injection of the fuel-oxidant mixture into the melt to prevent the formation of frozen melt downstream as well as to prevent any resultant explosive combustion; constant, reliable, and rapid ignition of the fuel-oxidant mixture such that the mixture burns quickly inside the molten material and releases the heat of combustion into the melt; and completion of the combustion process in bubbles rising to the surface of the melt. In one embodiment, the burners described in the 583 patent comprises an inner fluid supply tube having a first fluid inlet end and a first fluid outlet end and an outer fluid supply tube having a second fluid inlet end and a second fluid outlet end coaxially disposed around the inner fluid supply tube and forming an annular space between the inner fluid supply tube and the outer fluid supply tube. A burner nozzle is connected to the first fluid outlet end of the inner fluid supply tube. The outer fluid supply tube is arranged such that the second fluid outlet end extends beyond the first fluid outlet end, creating, in effect, a combustion space or chamber bounded by the outlet to the burner nozzle and the extended portion of the outer fluid supply tube. The burner nozzle is sized with an outside diameter corresponding to the inside diameter of the outer fluid supply tube and forms a centralized opening in fluid communication with the inner fluid supply tube and at least one peripheral longitudinally oriented opening in fluid communication with the annular space between the inner and outer fluid supply tubes. In certain embodiments, a longitudinally adjustable rod is disposed within the inner fluid supply tube having one end proximate the first fluid outlet end. As the adjustable rod is moved within the inner fluid supply tube, the flow characteristics of fluid through the inner fluid supply tube are modified. A cylindrical flame stabilizer element is attached to the second fluid outlet end. The stable flame is achieved by supplying oxidant to the combustion chamber through one or more of the openings located on the periphery of the burner nozzle, supplying fuel through the centralized opening of the burner nozzle, and controlling the development of a self-controlled flow disturbance zone by freezing melt on the top of the cylindrical flame stabilizer element. The location of the injection point for the fuel-oxidant mixture below the surface of the melting material enhances mixing of the components being melted and increases homogeneity of the melt. Thermal NOx emissions are greatly reduced due to the lower flame temperatures resulting from the melt-quenched flame and further due to insulation of the high temperature flame from the atmosphere.

The term “fuel”, according to this disclosure, means a combustible composition comprising a major portion of, for example, methane, natural gas, liquefied natural gas, propane, atomized oil or the like (either in gaseous or liquid form). Fuels useful in the disclosure may comprise minor amounts of non-fuels therein, including oxidants, for purposes such as premixing the fuel with the oxidant, or atomizing liquid fuels.

The total quantities of fuel and oxidant used by the combustion system are such that the flow of oxygen may range from about 0.9 to about 1.2 of the theoretical stoichiometric flow of oxygen necessary to obtain the complete combustion of the fuel flow. Another expression of this statement is that the combustion ratio is between 0.9 and 1.2. In certain embodiments, the equivalent fuel content of the feed material must be taken into account. For example, organic binders in glass fiber mat scrap materials will increase the oxidant requirement above that required strictly for fuel being combusted. In consideration of these embodiments, the combustion ratio may be increased above 1.2, for example to 1.5, or to 2, or 2.5, or even higher, depending on the organic content of the feed materials.

The velocity of the fuel gas in the various burners depends on the burner geometry used, but generally is at least about 15 m/s. The upper limit of fuel velocity depends primarily on the desired mixing of the melt in the melter apparatus, melter geometry, and the geometry of the burner; if the fuel velocity is too low, the flame temperature may be too low, providing inadequate melting, which is not desired, and if the fuel flow is too high, flame might impinge on the melter floor, roof or wall, and/or heat will be wasted, which is also not desired.

In certain embodiments of the disclosure it may be desired to implement heat recovery. In embodiments of the disclosure employing a heat transfer fluid for heat recovery, it is possible for a hot intermediate heat transfer fluid to transfer heat to the oxidant or the fuel either indirectly by transferring heat through the walls of a heat exchanger, or a portion of the hot intermediate fluid could exchange heat directly by mixing with the oxidant or the fuel. In most cases, the heat transfer will be more economical and safer if the heat transfer is indirect, in other words by use of a heat exchanger where the intermediate fluid does not mix with the oxidant or the fuel, but it is important to note that both means of exchanging heat are contemplated. Furthermore, the intermediate fluid could be heated by the hot flue gases by either of the two mechanisms just mentioned.

In certain embodiments employing heat recovery, the primary means for transferring heat may comprise one or more heat exchangers selected from the group consisting of ceramic heat exchangers, known in the industry as ceramic recuperators, and metallic heat exchangers further referred to as metallic recuperators. Apparatus and methods in accordance with the present disclosure include those wherein the primary means for transferring heat are double shell radiation recuperators. Preheater means useful in apparatus and methods described herein may comprise heat exchangers selected from ceramic heat exchangers, metallic heat exchangers, regenerative means alternatively heated by the flow of hot intermediate fluid and cooled by the flow of oxidant or fuel that is heated thereby, and combinations thereof. In the case of regenerative means alternately heated by the flow of hot intermediate fluid and cooled by the flow of oxidant or fuel, there may be present two vessels containing an inert media, such as ceramic balls or pebbles. One vessel is used in a regeneration mode, wherein the ceramic balls, pebbles or other inert media are heated by hot intermediate fluid, while the other is used during an operational mode to contact the fuel or oxidant in order to transfer heat from the hot media to the fuel or oxidant, as the case might be. The flow to the vessels is then switched at an appropriate time.

Glass mat forming devices useful in the invention include slitting devices. These may be hot, cold, shear, or ultrasonic slitting devices, depending on the nature of the glass mat to be recycled. Slitting devices are commercially available, for example from AZCO Corp, Fairfield, N.J. (USA), under the trade designation ACU-SLIT™, and Automazioni Tessili Frigerio S.r.I., Via Giotto, 35-22075 Lurate Caccivio, Italy. AZCO Corp. also supplies a variety of roll handling equipment, such as unwinding equipment. Powered nip rolls are available from a variety of commercial sources, as are roll brakes. Roll handling equipment may comprise a roll chuck, a roll brake, and a safety chuck, useful with the roll stands 14 and unwind devices 15 illustrated in FIGS. 1 and 2. Suitable roll chucks include air-inflated bladder chucks having an air-inflated bladder (not illustrated) which engages an inside surface of a roll core when inflated. Such chucks are available from several commercial sources, including, for example, Double E Company, LLC, West Bridgewater, Mass. (USA). A suitable roll brake includes a series of heat transfer cooling fins illustrated inside a safety cage. Roll brakes are also available from many sources, including the Double E Company. A hand-held air nozzle and compressed air hose may be available locally at roll stands 14. Compressed air nozzles and hoses are useful for the operator for many reasons, including topping off the air in the air-inflated bladder chucks, if deemed necessary by the operator, blowing off accumulated dust from equipment and clothes, and the like. Safety chucks are known in the roll handling art and usually include a mechanism to safely immobilize the roll. Safety chucks are available in a variety of designs, and are available from many sources, including the aforementioned Double E Company.

Roll stand 14 may include a roll alignment sensor, sometimes referred to as an edge guide, which may include a servo cable allowing communication between the sensor and a roll stand controller (not illustrated) to maintain roll of glass mat material 16 unwinding with proper alignment.

Apparatus of this disclosure may further optionally comprise one or more idler rolls and one or more anti-static devices useful with roll stand 14 illustrated in FIGS. 1 and 2. One anti-static device may comprise a rigid delivery tube positioned near the glass mat web as it unwinds, which is connected to a flexible delivery tube which supplies ionized air or other ionized gas to the rigid tube. Ionized air or other ionized gas exits the rigid tube through a plurality of holes or through a ceramic frit material and onto the glass mat material to remove static electricity. Without static electricity reduction, subsequent forming steps and other movements could be difficult. In addition, static shocks to workers can be painful and otherwise disruptive ergonomically.

Powered nip rolls 24 (FIGS. 1 and 2) and alternatives mentioned herein may be controlled by a controller 300 as previously discussed. Nip rolls may be part of a nip roll assembly, comprised of one or more idler rolls. Nip roll pairs may be designed to move up and down when desired by the operator, upon command from a main controller, usually by compressed air-actuated cylinders. Nip rollers in nip roller pairs 24 are typically rubber or rubber-covered rolls, available from many commercial sources.

Although only a few exemplary embodiments of this disclosure have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel apparatus and processes described herein. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims. In the claims, no clauses are intended to be in the means-plus-function format allowed by 35 U.S.C. §112, paragraph 6 unless “means for” is explicitly recited together with an associated function. “Means for” clauses are intended to cover the structures described herein as performing the recited function and not only structural equivalents, but also equivalent structures.

Claims

1. A method of recycling glass mat (18) materials, comprising:

a) providing a source (16) of glass mat (18), wherein the glass mat (18) is selected from the group consisting of nonwoven and woven materials;
b) routing the glass mat (18) at a substantially consistent feed rate into a submerged combustion melter (2) through a slot (26) in the melter (2) and then directly into a well-mixed mass of molten glass (4) within the melter (2) and melting the glass mat (18), wherein the melting comprises at least one burner (8) directing combustion products into a melting zone under a level (6) of the well-mixed molten glass (4) in the zone, and wherein the routing comprises unwinding the glass mat (18) off of a roll (16) of glass mat using an unwind system (14, 15) and a mechanism (24) selected from the group consisting of a pair of powered nip rolls, a nip compression conveyor, and opposed conveyors compressing the product.

2. The method of claim 1 wherein the glass mat (18) is routed through a forming device (20) prior to entering the powered nip rolls (24) so that the glass mat (18) fits through the slot (26).

3. The method of claim 1 wherein the glass mat (18) is cut to width prior to entering the powered nip rolls (24) so that it fits through the slot (80, 90, 110, 120 150).

4. The method of claim 1 wherein the providing the source (16) of glass mat (18) comprises providing a web of substantially continuous glass fibers bound together randomly at points where adjacent fibers touch using a binder.

5. The method of claim 1 wherein the unwinding of the glass mat (18) comprises splicing a first web unwinding from a first roll to a second web unwinding from a second roll.

6. A method of recycling glass fiber roving (152) materials, comprising:

a) providing a source (16) of glass fiber roving (152);
b) routing the glass fiber roving (152) at a substantially consistent feed rate into a submerged combustion melter (2) through a slot (26) in the melter (2) and then directly into a well-mixed mass of molten glass (4) within the melter (2) and melting the glass fiber roving (152),
wherein the melting comprises at least one burner (8) directing combustion products into a melting zone under a level (6) of the well-mixed molten glass (4) in the zone, and wherein the routing comprises unwinding the glass fiber roving (152) off of a roll (16) glass fiber roving using an unwind system (14, 15) and a mechanism (24) selected from the group consisting of a pair of powered nip rolls, a nip compression conveyor, and opposed conveyors compressing the product.

7. The method of claim 6 wherein the glass fiber roving (152) is routed through a forming device (20) prior to entering the powered nip rolls (24) so that the glass fiber roving (152) fits through the slot (26).

8. A method comprising:

a) providing a source of glass mat on a roll;
b) routing the glass mat by unwinding the glass mat from the roll into a submerged combustion melter and melting the glass mat; and
c) recovering heat from hot flue gases.

9. The method of claim 8, wherein b) routing further comprises:

b) routing the glass mat at a substantially consistent feed rate into a submerged combustion melter and melting the glass mat.

10. The method of claim 8, wherein the heat recovered from the hot flue gases is used to heat oxidant or fuel used in the melter.

11. The method of claim 9, wherein the recovery of the heat is by employing a heat transfer fluid, which is then used to heat the oxidant or fuel.

12. A method of recycling glass mat materials, comprising:

a) providing a source of glass mat selected from the group consisting of non-woven materials, woven materials, and combinations or mixtures thereof;
b) routing the glass mat at a substantially consistent feed rate into a submerged combustion melter through a slot in the melter and then directly into molten glass within the submerged combustion melter and melting the glass mat using one or more submerged combustion burners attached to the submerged combustion melter, wherein the substantially consistent feed rate is accomplished by unwinding the glass mat off of a roll of glass mat using an unwind system and a mechanism selected from the group consisting of a pair of powered nip rolls, a nip compression conveyor, and opposed conveyors compressing the product; and
c) wherein heat is recovered from hot flue gases.

13. The method of claim 12, wherein the recovered heat is used to heat oxidant or fuel or both used in the melter.

14. The method of claim 13, wherein the recovery of the heat comprises:

employing a heat transfer fluid, which is then used to heat the oxidant or fuel or both.

15. The method of claim 14, wherein a controller is used in routing the glass mat.

16. The method of claim 12 further comprising:

unwinding a web of glass mat prior to routing the glass mat through the slot of the submerged combustion melter.

17. The method of claim 12, wherein the glass mat comprises at least one of silica-bearing raw material, alkaline earth metal oxide-bearing raw material, boron-oxide-bearing raw material, sodium oxide-bearing raw material, alumina-bearing raw material, or cullet.

18. The method of claim 17, wherein the silica-bearing raw material comprises sand; the alkaline earth metal oxide-bearing raw material comprises limestone, dolomite, or combinations and mixtures thereof; the boron-oxide-bearing raw material comprises borax, the sodium oxide-bearing raw material comprises sodium carbonate, and the alumina-bearing raw material comprises feldspar.

19. The method of claim 12, wherein the glass mat comprises at least one of:

non-lofted woven mats of glass fiber; lofted woven mats of glass fiber; non-lofted non-woven mats of glass fiber; and lofted non-woven mats of glass fiber.

20. A method for producing glass using a submerged combustion melter having an exhaust chute that vents hot flue gases from the submerged combustion melter comprising:

a) feeding glass precursor raw materials from a roll into the submerged combustion melter;
b) melting glass precursor raw materials in the submerged combustion melter using one or more submerged combustion burners attached to the melter; and
c) recovering heat from the hot flue gases via a heat exchanger.

21. The method of claim 20 wherein the recovering heat from the hot flue gases via the heat exchanger comprises routing a heat transfer fluid through the heat exchanger.

22. The method of claim 20, wherein the method is for producing boron-containing glass and the melting comprises:

melting boron-oxide-bearing raw material in the submerged combustion melter.

23. A method for producing glass using one or more submerged combustion burners attached to a submerged combustion melter having an exhaust chute that vents hot flue gases from the submerged combustion melter comprising:

feeding glass precursor raw material through the exhaust chute into the submerged combustion melter, and using heat from the hot flue gases to heat the raw material; and
unwinding the raw material from a roll prior to feeding the raw material through the exhaust chute into the submerged combustion melter.

24. The method of claim 23 wherein the raw material comprises at least one of silica-bearing raw material, alkaline earth metal oxide raw material, boron-oxide-bearing raw material, sodium oxide raw material, alumina raw material, or cullet.

25. The method of claim 23, wherein the raw material comprises at least one of: glass rovings; glass scrap; non-lofted woven mats of glass fiber; lofted woven mats of glass fiber; non-lofted non-woven mats of glass fiber; and lofted non-woven mats of glass fiber.

26. A method for manufacturing a glass product comprising:

unwinding a roll of non-woven mat and introducing the non-woven mat of glass fibers held together with a binder into a submerged combustion melter and then directly into a well-mixed mass comprising molten glass; withdrawing at least a portion of the mass comprising molten glass from the submerged combustion melter; and
forming the mass comprising molten glass into a solidified glass product.

27. The method of claim 26 wherein the binder is an organic binder.

28. The method of claim 26 wherein introducing the non-woven mat comprises: feeding the non-woven mat through an exhaust chute of the submerged combustion melter and into the well-mixed mass comprising molten glass using heat from the hot flue gases to heat the non-woven mat before the non-woven mat contacts the molten glass.

29. The method of claim 26 wherein introducing the non-woven mat further comprises:

introducing the non-woven mat of glass fibers through a slot that provides access to the submerged combustion melter.

30. The method of claim 29 wherein introducing non-woven mat further comprises:

passing the non-woven mat through one or more of powered nip rolls, a folding device, a cutting device, and a slitting device so that the non-woven mat fits through the slot.

31. A method comprising:

a) providing a source of scrap on a roll;
b) routing the scrap by unwinding the roll into a submerged combustion melter and melting the scrap; and
c) recovering heat from hot flue gases.

32. The method of claim 31, wherein b) routing further comprises:

b) routing the scrap at a substantially consistent feed rate into a submerged combustion melter and melting the scrap.

33. The method of claim 31, wherein b) routing further comprises:

b) routing the scrap into a submerged combustion melter using one or more nip rollers.

34. A method comprising:

a) providing a source of glass mat on a roll;
b) routing the glass mat by unwinding the roll at a substantially consistent feed rate into a mass of molten glass in a submerged combustion melter and melting the glass mat using one or more submerged combustion burners attached to the melter; and
c) recovering heat from hot flue gases produced by the burners and melting of the glass mat.

35. The method of claim 34, wherein the heat recovered from the hot flue gases is used to heat oxidant or fuel or both used in the melter.

36. The method of claim 35, wherein the recovery of the heat comprises employing a heat transfer fluid, which is then used to heat the oxidant or fuel or both.

Referenced Cited
U.S. Patent Documents
1716433 June 1929 Ellis
2174533 October 1939 See et al.
2118479 January 1940 McCaskey
2269459 January 1942 Kleist
2432942 December 1947 See et al.
2455907 January 1948 Slayter
2679749 June 1954 Poole
2718096 September 1955 Henry et al.
2773545 December 1956 Petersen
2781756 February 1957 Kobe
2878644 March 1959 Fenn
2890166 June 1959 Heinze
2902029 September 1959 Hill
2981250 April 1961 Stewart
3020165 February 1962 Davis
3056283 October 1962 Tiede
3073683 January 1963 Switzer et al.
3084392 April 1963 Labino
3088812 May 1963 Bitterlich et al.
3104947 September 1963 Switzer et al.
3160578 December 1964 Saxton et al.
3165452 January 1965 Williams
3170781 February 1965 Keefer
3174820 March 1965 See et al.
3215189 November 1965 Bauer
3224855 December 1965 Plumat
3237929 March 1966 Plumat et al.
3241548 March 1966 See et al.
3245769 April 1966 Eck et al.
3248205 April 1966 Dolf et al.
3260587 July 1966 Dolf et al.
3268313 August 1966 Burgman et al.
3285834 November 1966 Guerrieri et al.
3294512 December 1966 Penberthy
3325298 June 1967 Brown
3385686 May 1968 Plumat et al.
3402025 September 1968 Garrett et al.
3407805 October 1968 Bougard
3407862 October 1968 Mustian, Jr.
3432399 March 1969 Schutt
3445214 May 1969 Oremesher
3498779 March 1970 Hathaway
3510393 May 1970 Burgman et al.
3525674 August 1970 Barnebey
3533770 October 1970 Adler et al.
3563683 February 1971 Hess
3592151 July 1971 Webber
3592623 July 1971 Shepherd
3606825 September 1971 Johnson
3617234 November 1971 Hawkins et al.
3627504 December 1971 Johnson
3692017 September 1972 Glachant et al.
3738792 June 1973 Feng
3746527 July 1973 Knavish et al.
3747588 July 1973 Booth
3756800 September 1973 Phaneuf
3763915 October 1973 Perry et al.
3764287 October 1973 Brocious
3771988 November 1973 Starr
3818893 June 1974 Kataoka et al.
3835909 September 1974 Douglas et al.
3840002 October 1974 Douglas et al.
3856496 December 1974 Nesbitt et al.
3885945 May 1975 Rees et al.
3907585 September 1975 Francel et al.
3912534 October 1975 Gurta
3913560 October 1975 Knavish et al.
3929445 December 1975 Zippe
3951635 April 20, 1976 Rough
3976464 August 24, 1976 Wardlaw
4004903 January 25, 1977 Daman et al.
4083711 April 11, 1978 Jensen
4110098 August 29, 1978 Mattmuller
4153438 May 8, 1979 Stream
4185982 January 29, 1980 Schwenninger
4203761 May 20, 1980 Rose
4205966 June 3, 1980 Horikawa
4226564 October 7, 1980 Takahashi et al.
4238226 December 9, 1980 Sanzenbacher et al.
4249927 February 10, 1981 Fakuzaki et al.
4270740 June 2, 1981 Sanzenbacher et al.
4282023 August 4, 1981 Hammel et al.
4303435 December 1, 1981 Sleighter
4309204 January 5, 1982 Brooks
4323718 April 6, 1982 Buhring
4349376 September 14, 1982 Dunn et al.
4353725 October 12, 1982 Hohman
4397692 August 9, 1983 Ramge et al.
4406683 September 27, 1983 Demarest
4413882 November 8, 1983 Bailey et al.
4422862 December 27, 1983 Wardlaw
4432780 February 21, 1984 Propster et al.
4488537 December 18, 1984 Laurent
4539034 September 3, 1985 Hanneken
4542106 September 17, 1985 Sproull
4545800 October 8, 1985 Won et al.
4626199 December 2, 1986 Bounini
4632687 December 30, 1986 Kunkle et al.
4634461 January 6, 1987 Demarest, Jr. et al.
4657586 April 14, 1987 Masterson et al.
4735642 April 5, 1988 Jensen et al.
4738938 April 19, 1988 Kunkle et al.
4758259 July 19, 1988 Jensen
4798616 January 17, 1989 Knavish et al.
4814387 March 21, 1989 Donat
4816056 March 28, 1989 Tsai et al.
4877436 October 31, 1989 Sheinkop
4877449 October 31, 1989 Khinkis
4878829 November 7, 1989 Anderson
4882736 November 21, 1989 Pieper
4927886 May 22, 1990 Backderf et al.
4953376 September 4, 1990 Merlone
5032230 July 16, 1991 Shepherd
5052874 October 1, 1991 Johanson
5062789 November 5, 1991 Gitman
5097802 March 24, 1992 Clawson
5100453 March 31, 1992 Richards
5168109 December 1, 1992 Backderf et al.
5169424 December 8, 1992 Grinnen et al.
5199866 April 6, 1993 Joshi et al.
5204082 April 20, 1993 Schendel
5299929 April 5, 1994 Yap
5352258 October 4, 1994 DeGreve et al.
5360171 November 1, 1994 Yap
5374595 December 20, 1994 Dumbaugh et al.
5405082 April 11, 1995 Brown et al.
5412882 May 9, 1995 Zippe et al.
5449286 September 12, 1995 Snyder et al.
5483548 January 9, 1996 Coble
5490775 February 13, 1996 Joshi et al.
5522721 June 4, 1996 Drogue et al.
5526580 June 18, 1996 Zippe et al.
5545031 August 13, 1996 Joshi et al.
5575637 November 19, 1996 Slavejkov et al.
5595703 January 21, 1997 Swaelens et al.
5606965 March 4, 1997 Panz et al.
5613994 March 25, 1997 Muniz et al.
5615668 April 1, 1997 Panz et al.
5636623 June 10, 1997 Panz et al.
5672827 September 30, 1997 Jursich
5709728 January 20, 1998 Fleckenstein et al.
5713668 February 3, 1998 Lunghofer et al.
5718741 February 17, 1998 Hull et al.
5736476 April 7, 1998 Warzke et al.
5743723 April 28, 1998 Iatrides et al.
5765964 June 16, 1998 Calcote et al.
5772126 June 30, 1998 Hanvey et al.
5814121 September 29, 1998 Travis
5829962 November 3, 1998 Drasek et al.
5833447 November 10, 1998 Bodelin et al.
5849058 December 15, 1998 Takeshita et al.
5863195 January 26, 1999 Feldermann
5887978 March 30, 1999 Lunghofer et al.
5944507 August 31, 1999 Feldermann
5944864 August 31, 1999 Hull et al.
5954498 September 21, 1999 Joshi et al.
5975886 November 2, 1999 Philippe
5979191 November 9, 1999 Jian
5984667 November 16, 1999 Philippe et al.
5993203 November 30, 1999 Koppang
6029477 February 29, 2000 Hanvey
6029910 February 29, 2000 Joshi et al.
6036480 March 14, 2000 Hughes et al.
6039787 March 21, 2000 Edlinger
6045353 April 4, 2000 VonDrasek et al.
6068468 May 30, 2000 Philippe et al.
6071116 June 6, 2000 Philippe et al.
6074197 June 13, 2000 Philippe
6077072 June 20, 2000 Marin et al.
6085551 July 11, 2000 Pieper et al.
6109062 August 29, 2000 Richards
6113389 September 5, 2000 Joshi et al.
6116896 September 12, 2000 Joshi et al.
6120889 September 19, 2000 Turner et al.
6123542 September 26, 2000 Joshi et al.
6126438 October 3, 2000 Joshi et al.
6154481 November 28, 2000 Sorg et al.
6156285 December 5, 2000 Adams et al.
6171100 January 9, 2001 Joshi et al.
6210151 April 3, 2001 Joshi et al.
6210703 April 3, 2001 Novich
6237369 May 29, 2001 LeBlanc et al.
6241514 June 5, 2001 Joshi et al.
6244197 June 12, 2001 Coble
6244857 June 12, 2001 VonDrasek et al.
6247315 June 19, 2001 Marin et al.
6250136 June 26, 2001 Igreja
6250916 June 26, 2001 Philippe et al.
6274164 August 14, 2001 Novich
6276924 August 21, 2001 Joshi et al.
6276928 August 21, 2001 Joshi et al.
6293277 September 25, 2001 Panz et al.
6314760 November 13, 2001 Chenoweth
6314896 November 13, 2001 Marin et al.
6338337 January 15, 2002 Panz et al.
6344747 February 5, 2002 Lunghofer et al.
6357264 March 19, 2002 Richards
6386271 May 14, 2002 Kawamoto et al.
6418755 July 16, 2002 Chenoweth
6422041 July 23, 2002 Simpson et al.
6454562 September 24, 2002 Joshi et al.
6460376 October 8, 2002 Jeanvoine et al.
6536651 March 25, 2003 Ezumi et al.
6558606 May 6, 2003 Kulkarni et al.
6660106 December 9, 2003 Babel et al.
6694791 February 24, 2004 Johnson et al.
6701617 March 9, 2004 Li et al.
6705118 March 16, 2004 Li et al.
6708527 March 23, 2004 Ibarlucea et al.
6711942 March 30, 2004 Getman et al.
6715319 April 6, 2004 Barrow et al.
6722161 April 20, 2004 LeBlanc
6736129 May 18, 2004 Sjith
6739152 May 25, 2004 Jeanvoine et al.
6796147 September 28, 2004 Borysowicz et al.
6797351 September 28, 2004 Kulkarni et al.
6854290 February 15, 2005 Hayes et al.
6857999 February 22, 2005 Jeanvoine
6883349 April 26, 2005 Jeanvoine
6918256 July 19, 2005 Gutmark et al.
7027467 April 11, 2006 Baev et al.
7116888 October 3, 2006 Aitken et al.
7134300 November 14, 2006 Hayes et al.
7168395 January 30, 2007 Engdahl
7175423 February 13, 2007 Pisano et al.
7231788 June 19, 2007 Karetta et al.
7273583 September 25, 2007 Rue et al.
7383698 June 10, 2008 Ichinose et al.
7392668 July 1, 2008 Adams et al.
7428827 September 30, 2008 Maugendre et al.
7441686 October 28, 2008 Odajima et al.
7448231 November 11, 2008 Jeanvoine et al.
7454925 November 25, 2008 DeAngelis et al.
7509819 March 31, 2009 Baker et al.
7565819 July 28, 2009 Jeanvoine et al.
7578988 August 25, 2009 Jacques et al.
7581948 September 1, 2009 Borders et al.
7622677 November 24, 2009 Barberree et al.
7624595 December 1, 2009 Jeanvoine et al.
7748592 July 6, 2010 Koga et al.
7767606 August 3, 2010 McGinnis et al.
7778290 August 17, 2010 Sacks et al.
7781562 August 24, 2010 Crawford et al.
7802452 September 28, 2010 Borders et al.
7832365 November 16, 2010 Hannum et al.
7845314 December 7, 2010 Smith
7855267 December 21, 2010 Crawford et al.
8033254 October 11, 2011 Hannum et al.
8279899 October 2, 2012 Kitabayashi
8285411 October 9, 2012 Hull et al.
8650914 February 18, 2014 Charbonneau
8707739 April 29, 2014 Huber et al.
8707740 April 29, 2014 Huber et al.
8769992 July 8, 2014 Huber
8875544 November 4, 2014 Charbonneau
8973400 March 10, 2015 Charbonneau et al.
8997525 April 7, 2015 Shock et al.
20020086077 July 4, 2002 Noller et al.
20020134112 September 26, 2002 Barrow et al.
20020152770 October 24, 2002 Becher et al.
20020162358 November 7, 2002 Jeanvoine et al.
20020166343 November 14, 2002 LeBlanc
20030015000 January 23, 2003 Hayes et al.
20030029197 February 13, 2003 Jeanvoine et al.
20030037571 February 27, 2003 Kobayashi et al.
20040131988 July 8, 2004 Baker et al.
20040168474 September 2, 2004 Jeanvoine et al.
20040224833 November 11, 2004 Jeanvoine et al.
20050039491 February 24, 2005 Maugendre et al.
20050103323 May 19, 2005 Engdahl
20050236747 October 27, 2005 Rue et al.
20060000239 January 5, 2006 Jeanvoine et al.
20060174655 August 10, 2006 Kobayashi et al.
20060233512 October 19, 2006 Aitken et al.
20060257097 November 16, 2006 Aitken et al.
20060287482 December 21, 2006 Crawford et al.
20060293494 December 28, 2006 Crawford et al.
20060293495 December 28, 2006 Crawford et al.
20070106054 May 10, 2007 Crawford et al.
20070122332 May 31, 2007 Jacques et al.
20070130994 June 14, 2007 Boratav et al.
20070212546 September 13, 2007 Jeanvoine et al.
20070220922 September 27, 2007 Bauer et al.
20080035078 February 14, 2008 Li
20080227615 September 18, 2008 McGinnis et al.
20080256981 October 23, 2008 Jacques et al.
20080276652 November 13, 2008 Bauer
20080293857 November 27, 2008 Crawford et al.
20080302136 December 11, 2008 Bauer et al.
20090042709 February 12, 2009 Jeanvoine et al.
20090220899 September 3, 2009 Spangelo et al.
20090235695 September 24, 2009 Pierrot
20100064732 March 18, 2010 Jeanvoine et al.
20100087574 April 8, 2010 Crawford et al.
20100089383 April 15, 2010 Cowles
20100120979 May 13, 2010 Crawford et al.
20100143601 June 10, 2010 Hawtof et al.
20100227971 September 9, 2010 Crawford et al.
20100236323 September 23, 2010 D'Angelico et al.
20100300153 December 2, 2010 Zhang et al.
20100304314 December 2, 2010 Rouchy et al.
20100307196 December 9, 2010 Richardson
20100326137 December 30, 2010 Rouchy et al.
20110054091 March 3, 2011 Crawford et al.
20110061642 March 17, 2011 Rouchy et al.
20110088432 April 21, 2011 Purnode et al.
20110107670 May 12, 2011 Galley
20110236846 September 29, 2011 Rue et al.
20110308280 December 22, 2011 Charbonneau
20120077135 March 29, 2012 Charbonneau
20120104306 May 3, 2012 Kamiya et al.
20130086944 April 11, 2013 Shock et al.
20130086951 April 11, 2013 Charbonneau et al.
20130086952 April 11, 2013 Charbonneau et al.
20130283861 October 31, 2013 Mobley et al.
20130327092 December 12, 2013 Charbonneau
Foreign Patent Documents
3217414 July 1983 DE
3716687 November 1988 DE
4000358 September 1990 DE
19619919 August 1997 DE
10029983 September 2003 DE
102005033330 August 2006 DE
0181248 October 1989 EP
1337789 December 2004 EP
1990321 November 2008 EP
2133315 December 2009 EP
2138465 December 2009 EP
1986966 April 2010 EP
1667934 February 2011 EP
2 397 446 December 2011 EP
2404880 January 2012 EP
2578548 April 2013 EP
2740860 September 1997 FR
WO 2007116183 October 2007 FR
191301772 January 1914 GB
191407633 March 1914 GB
164073 May 1921 GB
1 449 439 September 1976 GB
1208172 November 2007 IT
2000351633 December 2000 JP
2002120224 April 2002 JP
465272 December 2004 KR
114827 July 1999 RO
WO 1998055411 December 1998 WO
WO 2008103291 August 2008 WO
WO 2009/091558 July 2009 WO
WO 2009091558 July 2009 WO
WO 2010011701 January 2010 WO
WO 2010045196 April 2010 WO
Other references
  • “Glass Industry of the Future”, United States Department of Energy, report 02-GA50113-03, pp. 1-17, Sep. 30, 2008.
  • “Glass Technologies—The Legacy of a Successful Public-Private Partnership”, 2007, U.S. Department of Energy, pp. 1-32.
  • Furman, BJ, ME 120 Experimental Methods, “Vibration Measurement”, San Jose University Department of Mechanical and Aerospace Engineering, Nov. 22, 2005, 14 pgs.
  • Higley, BA, “Glass Melter System Technologies for Vitrification of High-Sodium Content Low-Level, Radioactive, Liquid Wastes—Phase 1: SBS Demonstration With Simulated Low-Level Waste—Final Test Report”, Westinghouse Hanford Company, Sep. 1, 1995, 296 pgs.
  • Olabin, V.M. et al, “Submerged Combustion Furnace for Glass Melts,” Ceramic Engineering and Science Proceedings, Jan. 1, 1996, pp. 84-92, vol. 17—No. 2, American Ceramic Society Inc. US.
  • Ross, C. Philip et al., “Glass Melting Technology: A Technical and Economic Assessment”, Oct. 2004, U.S. Department of Energy—Industrial Technologies Program, pp. 1-292.
  • Rue, David, “Energy-Efficient Glass Melting—The Next Generation Melter”, Gas Technology Institute, Project No. 20621, Final Report, Mar. 2008, 82 pgs.
  • Thor Treatment Technologies, LLC, “Report for Treating Hanford LAW and WTP SW Simulants: Pilot Plant Mineralizing Flowsheet”, Apr. 2009, Department of Energy Environmental Management Consolidated Business Center, 250 pgs.
Patent History
Patent number: RE46896
Type: Grant
Filed: Jul 28, 2015
Date of Patent: Jun 19, 2018
Assignee: JOHNS MANVILLE (Denver, CO)
Inventor: Johns Manville (Denver, CO)
Primary Examiner: Sean E Vincent
Application Number: 14/811,453
Classifications
Current U.S. Class: Including Work Heating Or Contact With Combustion Products (134/19)
International Classification: C03B 3/00 (20060101); C03C 1/00 (20060101); C03B 5/00 (20060101); C03B 5/235 (20060101);