Abstract: A multimodal polyethylene copolymer comprising: (III) 35 to 55 wt % of a lower molecular weight ethylene homopolymer component having an MFR2 of 200 to 400 g/10 min; (IV) 45 to 65 wt % of a higher molecular weight ethylene copolymer component of ethylene and at least one C3-12 alpha olefin comonomer; wherein said multimodal polyethylene copolymer has a density of 955 to 962 kg/m3, an MFR2 of 2.0 to 10 g/10 min and an Mw/Mn of more than 9.0.

Abstract: A propylene-based polymer composition is characterized by a melt strength at 190° C. of at least 20 cN, a melt drawability at 190° C. of at least 100 mm/s, and a flexural modulus at room temperature of at least 240,000 psi. The propylene-based polymer composition includes a propylene-based polymer resin having a crystallinity of at least 50% coupled with a poly(sulfonyl azide).

Abstract: The present invention relates to a bimodal polypropylene composition comprising a blend of a HMW polypropylene component and a LMW polypropylene component, where the high molecular weight (HMW) component of the bimodal composition has a z-average molecular weight Mz of more than 400,000 g/mole, and a process to make such composition. The composition is suitable for thermoformed articles and injection molded articles.

Abstract: A molding material mixture contains cellulose nanofibers (CNFs) and at least one base material selected from the group consisting of a resin and fibers. A hydrophobic polymer is chemically bonded to at least some of the —OH groups of the cellulose nanofibers. The base material and the cellulose nanofibers are ground or pelletized.

Abstract: The disclosure concerns polymer compositions comprising: a) from about 55 wt % to about 85 wt % polycarbonate polymer; b) from about 10 wt % to about 30 wt % polypropylene polymer; and c) from about 2 wt % to about 15 wt % of a compatibilizer comprising (i) a polymer having styrene and ethylene/butylene blocks, (ii) a triblock copolymer, (iii) hydrogenated styrene isoprene copolymer, or (iv) mixtures thereof.

Abstract: An ultraviolet crosslinkable composition that can provide a cured product that is easy to mold, can maintain a molded shape even under a high temperature environment, and has excellent physical properties, for example, chemical resistance, scratch resistance and the like. The ultraviolet crosslinkable composition can contain a thermoplastic acrylic resin in which a glass transition temperature is 25° C. or higher and a (meth) acrylic copolymer having an ultraviolet crosslinkable site in which a glass transition temperature is 25° C. or higher.

Abstract: According to a tire comprising a CFRP comprising a matrix resin and a carbon fiber, in which the matrix resin comprises a resin component comprising 20 to 80% by mass of an epoxy resin and 20 to 80% by mass of a functional group-modified acrylonitrile butadiene copolymer, it is possible to provide a tire which is lightened while maintaining the strength of a tire with a steel cord and/or a bead wire.

Abstract: A resin composition comprising a binder resin (A), a compound (B) having an acidic group or latent acidic group, an organic solvent (C), and a compound (D) having one atom selected from a silicon atom, titanium atom, aluminum atom, and zirconium atom and having a hydrocarbyloxy group or hydroxy group bonded with that atom, wherein the compound (B) is at least one type selected from the group consisting of an aliphatic compound, aromatic compound, and heterocyclic compound, and a content of the compound (B) is 0.1 to 2.5 parts by weight and a content of the compound (D) is 2.2 to 7.0 parts by weight with respect to 100 parts by weight of the binder resin (A) is provided.

Abstract: A block copolymer composition comprising: a polymer (a) comprising more than 95% by mass and 100% by mass or less of a vinyl aromatic monomer unit and 0% by mass or more and less than 5% by mass of a conjugated diene monomer unit; and a block copolymer (b) comprising 15% by mass or more and 50% by mass or less of a vinyl aromatic monomer unit and 50% by mass or more and 85% by mass or less of a conjugated diene monomer unit, wherein a mass ratio of the polymer (a) to the block copolymer (b) satisfies: (a)/(b)=70/30 to 30/70.

Abstract: An article is formed from a thermoplastic elastomer compound that includes styrenic block copolymer and high softening point tackifier. The styrenic block copolymer has a Copolymer Tan Delta Peak Temperature and the thermoplastic elastomer compound has a Compound Tan Delta Peak Temperature. The Compound Tan Delta Peak Temperature is greater than the Copolymer Tan Delta Peak Temperature. The article exhibits useful damping properties at or above room temperature while also exhibiting low compression set, which makes the article especially suitable for use as a seal or a gasket.

Abstract: A thermoplastic elastomer compound includes styrenic block copolymer that is high vinyl styrene-(ethylene/butylene)-styrene block copolymer and high softening point tackifier. The high vinyl styrene-(ethylene/butylene)-styrene block copolymer has a Copolymer Tan Delta Peak Temperature and the thermoplastic elastomer compound has a Compound Tan Delta Peak Temperature. The Compound Tan Delta Peak Temperature is greater than the Copolymer Tan Delta Peak Temperature. The thermoplastic elastomer compound exhibits useful damping properties at or above room temperature while also advantageously possessing improved stability for processing and/or applications at high temperatures and upon exposure to weathering.

Abstract: A method for preparing a polymer compound including copolymerizing a monomer (m0-1) and a monomer (m0-2) to obtain a first polymer compound and causing the first polymer compound and an acid component to react with each other to obtain a second polymer compound. In the formulae, R1 and R2 are each a hydrogen atom, an alkyl group having 1 to 5 carbon atoms and a halogenated alkyl group having 1 to 5 carbon atoms, Va01 is a divalent hydrocarbon group which may have an ether bond, na01 is an integer of 0 to 2, Ra10 is a tertiary alkyl ester-type acid dissociable group, Va02 is a divalent linking group containing a heteroatom, or a single bond, Ra07 is a monovalent organic group, na021 is an integer of 0 to 3, Ra20 is an acid dissociable group, and na022 is an integer of 1 to 3.

Abstract: Flame retardant thermoplastic compositions that are capable of being used in a laser direct structuring process. The compositions include a thermoplastic resin, a laser direct structuring additive, and a flame retardant. The compositions offer flame retardant characteristics while also substantially maintaining the mechanical properties of the base thermoplastic resin, such as the impact strength and/or HDT of the composition. The compositions can be used in a variety of applications such as personal computers, notebook and portable computers, cell phone and other such communications equipment.

Abstract: In an embodiment, a process for forming a quenched composition comprises mixing an unquenched melt polycarbonate and a quenched melt polycarbonate to form the quenched composition; wherein the quenched polycarbonate was formed from a first melt polymerization, wherein the first melt polymerization comprises adding a quencher to form the quenched polycarbonate, wherein the unquenched polycarbonate was formed from a second melt polymerization, wherein the unquenched melt polycarbonate comprises an active catalyst used during the second melt polymerization, and wherein the second melt polymerization is free of a quencher addition.

Abstract: The present invention provides a low-dielectric resin composition comprising (A) a urethane resin obtained by reacting a polycarbonate diol and an isocyanate, (B) an epoxy resin, and (C) a filler, wherein the (A) urethane resin has a carboxyl group equivalent weight of 1,100 to 5,700 g/eq; the epoxy equivalent weight of the (B) epoxy resin is 0.3 to 4.5 equivalents per 1.0 equivalent of the carboxyl group of the (A) urethane resin, the (A) urethane resin has a weight-average molecular weight of 5,000 to 80,000; the (A) urethane resin has a polycarbonate content of 35% by mass or lower; the resin composition comprises 50 parts by mass or less of the (C) filler per 100 parts by mass of the (A) urethane resin; and the resin composition comprises substantially no imido group.

Abstract: Provided is a polyamide resin composition including 0.01 to 50 parts by mass of cellulose fiber in relation to 100 parts by mass of a polyamide resin, having a relative viscosity of 2.3 or more, and having an L-value, an a-value and a b-value in an Lab color space of 20 or more, 10 or less and 20 or less, respectively. The aforementioned polyamide resin composition is obtained by subjecting a polyamide resin composition having a relative viscosity of 2.2 or less to a solid phase polymerization.

Abstract: A polymer blend comprising polyamide, polypropylene (PP) and at least one of poly (lactic acid) (PLA) and a multi-phase compatibilizer comprising PA11-co-PP-maleic anhydride (MA). The polymer blend can be reinforced with hybrid fillers including biocarbon, glass fiber, carbon fiber and nano-clay to create composites useful in the creation of products of manufacture such as auto parts.

Abstract: A method for preparing a colorant for use in an ink composition including a substantially non-aqueous carrier composition includes providing a chromophore precursor including one or multiple functional groups which may be subjected to a chemical reaction to form a salt with a preselected counter ion; providing a salt including the preselected counter ion; and providing an organic solvent that is not miscible with water and wherein the reaction product of the chromophore precursor and the salt including the preselected counter ion is soluble; preparing a chromophore precursor solution in water by dissolving a quantity of the chromophore precursor in water adding a quantity of the organic solvent while stirring; adding the salt including the preselected counter ion while stirring to form a resalted chromophore; separating the resalted chromophore from the reaction mixture.

Abstract: A detailing agent for three-dimensional (3D) printing includes a colorant present in an amount ranging from about 1.00 wt % to about 3.00 wt % based on a total weight of the detailing agent. The colorant is a dye having substantially no absorbance in a range of 650 nm to 2500 nm. The detailing agent also includes a co-solvent, a surfactant, and a balance of water.

Abstract: A coated particulate inorganic material includes a particulate inorganic material selected from at least one of titanium dioxide and a doped titanium dioxide, and a coating. The particulate inorganic material has an average crystal size of 0.4-2 ?m. The coating includes a first and second layer. The first layer includes an inorganic oxide and/or an inorganic phosphate. The second layer is alumina. The first layer is from 0.1 to 2.2% w/w based on a total weight of the first layer with respect to a total weight of the particulate inorganic material. The second layer is 0.1 to 3.5% w/w based on a total weight of the second layer with respect to the total weight of the particulate inorganic material. The coating is from 0.2 to 4.5% w/w based on the total weight of the first and second layer with respect to the total weight of the particulate inorganic material.

Abstract: Apparatus and process for the continuous production of carbon black or carbon containing compounds. The process is performed by converting a carbon containing feedstock, including generating a plasma gas with electrical energy, accelerating the plasma gas through a nozzle, whose diameter is narrowing in the direction of the plasma gas, guiding the plasma gas into a reaction area where feedstock is injected under conditions generated by aerodynamic and electromagnetic forces, including intense rapid mixing between the plasma gas and feedstock occurs. There is no significant recirculation of feedstock into the plasma chamber, and the reaction zone does not immediately come into contact with any contact surfaces. The products of reaction are cooled, and the carbon black or carbon containing compounds are separated from the other reaction products.

Abstract: Provided is a method for easily producing an oxidized carbon black aqueous dispersion that can highly remove multivalent metal ions and exhibit excellent dispersion stability. A method for producing an oxidized carbon black aqueous dispersion by successively performing on an aqueous slurry of oxidized carbon black having one or more anionic functional groups on a surface thereof a neutralization step of mixing an alkali metal hydroxide and performing heating/neutralization in the presence of one or more selected from a water-soluble chelating agent and a salt thereof or after mixing an alkali metal hydroxide and performing heating/neutralization, mixing one or more selected from a water-soluble chelating agent and a salt thereof and a separation and removal step of separating and removing a multivalent metal ion chelate complex from a mixed solution obtained at the neutralization step using a separation membrane.

Abstract: An electrical steel sheet has an insulating coating on a steel sheet surface. The insulating coating includes one or more selected from an inorganic salt, an oxide, and an organic resin. The insulating coating includes the inorganic salt and/or the oxide in an amount of 50% or more by mass in total based on the total mass of the insulating coating. The insulating coating has a fluorine concentration ranging from 2 ppm to 130 ppm. The insulating coating is free of a chromium compound. The insulating coating of this electrical steel sheet has excellent coating compatibility.

Abstract: Certain example embodiments relate to coated articles supporting high-entropy nitride and/or oxide thing film inclusive coatings, and/or methods of making the same. The example high-entropy alloys systems described herein are heat stable and may be used in optical coatings. A first material system that may be used in connection with certain example embodiments includes SiAlN with one or more (and preferably two or more) of elements such as Hf, Y, Zr, Ti, Ta, and Nb. A second material system that may be used in connection with certain example embodiments includes TiO, with one or more (and preferably two or more) of elements such as Fe, Co, Ni, Sn, Zn, and N. The material systems may in some cases be high-index materials that can serve as a substitute for titanium oxide in layer stacks, in some example applications.

Abstract: Certain example embodiments relate to coated articles supporting high-entropy nitride and/or oxide thing film inclusive coatings, and/or methods of making the same. The example high-entropy alloys systems described herein are heat stable and may be used in optical coatings. A first material system that may be used in connection with certain example embodiments includes SiAlN with one or more (and preferably two or more) of elements such as Hf, Y, Zr, Ti, Ta, and Nb. A second material system that may be used in connection with certain example embodiments includes TiO, with one or more (and preferably two or more) of elements such as Fe, Co, Ni, Sn, Zn, and N. The material systems may in some cases be high-index materials that can serve as a substitute for titanium oxide in layer stacks, in some example applications.

Abstract: A low-reflection coated glass sheet of the present invention includes a glass sheet and a low-reflection coating. The low-reflection coating is formed on at least a portion of one principal surface of the glass sheet, and contains a binder containing silica as a main component, fine silica particles bound by the binder, and fine titania particles bound by the binder. For the low-reflection coated glass sheet, a transmittance gain is 1.7% or more. The low-reflection coating contains 25 mass % to 43 mass % of the silica which is the main component of the binder, 40 mass % to 64 mass % of the fine silica particles, and 10 mass % to 20 mass % of the fine titania particles, based on the total mass of the low-reflection coating. As such, the low-reflection coated glass sheet of the present invention has high abrasion resistance and is capable of exhibiting photocatalytic properties and hydrophilicity when irradiated with light.

Abstract: A paint system having a base coating composition and a top coating composition, each having a low VOC value preferably below 50 g/l, is disclosed. The base coating composition includes a release material and the top coating composition includes a pigment and a paint emulsion. The base coat formulation is applied to a surface to form a base coating and the top coat layer is applied over the top coating. When dry, the top coating has high cohesion relative to the adhesion of top coating to base coating, thereby permitting the top coating to be manually peeled away from the surface. Related methods are also disclosed.

Abstract: A method for preparing an aqueous based coating system, and coating systems made thereby, for coating onto paper and/or paperboard for providing barrier to liquid, moisture vapor, oil and grease including a pigment and a polymer emulsion system or natural based binding system. One alternative of the method includes surface treating a pigment to form a pigment system and mixing a polymer emulsion system or natural based binding system with the pigment system. Another alternative of the method includes mixing a pigment and polymer emulsion system or natural based binding system and hydrophobizing the polymer emulsion system or natural based binding system by adding silanes, siloxanes, siloxane/silicone resin blends, or their carbon based analogs.

Abstract: A powder coating material includes powder particles and inorganic particles and have a dielectric loss factor of from 40×10?3 to 150×10?3.

Abstract: A fluorine-containing copolymer that is a copolymer of: a polyfluoroalkyl alcohol (meth)acrylate represented by the general formula: CnF2n+1(CH2CF2)a(CF2CF2)b(CH2CH2)cOCOCR?CH2??[I] (R: a hydrogen atom, a methyl group, n: 1 to 6, a: 1 to 4, b: 1 to 3, and c: 1 to 3); benzyl (meth)acrylate or styrene; and a Si group-containing crosslinkable (meth)acrylate represented by the general formula: CH2?CRCOO(CH2)dSi(OR1)eR23-e??[II] (R: a hydrogen atom, a methyl group, R1, R2: an alkyl group having 1 to 10 carbon atoms, d: 1 to 3, e: 1 to 3). The surface-modifying agent comprising this fluorine-containing copolymer as an active ingredient have an excellent dynamic slip angle after washing with hexadecane, and anti-corrosive properties.

Abstract: Coating compositions for coil coating, methods for making such coating compositions and coil coating methods are provided. In an exemplary embodiment, a coating composition includes an organic solvent carrier and a film-forming binder dispersed in the organic solvent carrier. The film-forming binder contains an epoxy-amine adduct and a blocked or unblocked polyisocyanate crosslinking agent. The film-forming binder has associated amine groups until subjected to a temperature of at least about 165.5° C. (330° F.). The coating composition also contains a pigment and a grinding resin. The coating composition has a solids content of at least about 50 wt. % based on a total weight of the coating composition.

Abstract: An alkoxysilane is contacted with water and an inorganic acid to form a first composition. A zirconium alkoxide is contacted with an organic acid to form a second composition. One or more alkoxysilanes and an organic acid are contacted with a mixture of the first and second compositions to form a sol-gel composition, to which a photoinitiator is added. The sol-gel composition has a ratio of a number of moles of silicon to a number of moles of zirconium (nSi/nZr) ranging from about 2 to about 10. The sol-gel composition is applied on a substrate (e.g., an aluminum alloy substrate) multiple times to form multiple sol-gel layers, and at least one of the sol-gel layers is cured by UV radiation. The multiple sol-gel layers are then thermally cured.

Abstract: A Zn—Al layered double hydroxide (LDH) composition is added to a solution including a corrosion inhibitor and stirred, and a precipitate of the solution is collected, washed, and dried to form a corrosion inhibiting material (CIM), in which the LDH composition is intercalated with the corrosion inhibitor. An inorganic CIM and/or an organic CIM may be formed. The organic CIM may be added to a sol-gel composition to form an organic CIM-containing sol-gel composition, and the inorganic CIM may be added to a sol-gel composition to form an inorganic CIM-containing sol-gel composition. Further, the organic CIM-containing sol-gel composition may be applied on a substrate (e.g., an aluminum alloy substrate) to form an organic CIM-containing sol-gel layer and cured by ultraviolet (UV) radiation, the inorganic CIM-containing sol-gel composition may be applied on the substrate to form an inorganic CIM-containing sol-gel layer and cured by UV radiation, and the sol-gel layers may be thermally cured.

Abstract: A corrosion-resistant coating on an aluminum-containing substrate such as an aluminum substrate, an aluminum alloy substrate (e.g., AA 2024, AA 6061, or AA7075), or other aluminum-containing substrate includes a corrosion inhibitor-incorporated Zn—Al layered double hydroxide (LDH) layer and a sol-gel layer. A zinc salt and a corrosion inhibitor (e.g., a salt of an oxyanion of a transition metal such as a vanadate) is dissolved to form a zinc-corrosion inhibitor solution, and the substrate is immersed in or otherwise contacted with the solution to form the corrosion inhibitor-incorporated Zn—Al LDH layer on the substrate. A sol-gel composition is applied on the corrosion inhibitor-incorporated Zn—Al LDH layer of the substrate to form a sol-gel layer, and the sol-gel layer is cured.

Abstract: A method includes coating a substrate to provide a flame resistant substrate. In an embodiment, the method includes preparing an aqueous solution. The aqueous solution comprises a phosphate material, a cationic material, and a water. The method further includes exposing the substrate to the aqueous solution to produce a coating on the substrate. The coating includes the cationic material and the phosphate material. The method also includes exposing the coating on the substrate to a melamine solution.

Abstract: The invention relates to cation borate present in powder form, with a small grain size and low water solubility. The cation borate present in powder form and a suspension produced therefrom are suitable for example for the treatment of coating materials (such as wood preservatives), in particular fungicidal, biocidal and insecticidal treatment.

Abstract: A method of forming a passivated pigment slurry includes combining a resin and a pigment to form a pigment-resin slurry, wherein the pigment includes a plurality of flakes each having a surface. After combining, the method includes firstly reacting an orthosilicate and the pigment in the presence of the resin to form a coated pigment-resin slurry. The coated pigment-resin slurry includes the resin and a coated pigment including the plurality of flakes each encapsulated by a first layer formed from the orthosilicate on the surface. The method further includes, concurrent to or after firstly reacting, secondly reacting the coated pigment-resin slurry and an organosilane compound having a hydrolysable group and an organic group to coat the first layer and form the passivated pigment slurry. The passivated pigment slurry includes the resin and a passivated pigment including the plurality of flakes each coated with a second layer disposed on the first.

Abstract: Disclosed are methods of protecting porous substrates and/or increasing the peel-resistance of coatings and stains for porous substrates. The methods may include providing a stain or coating comprising a microencapsulated self-healing material; and applying the stain or coating to a porous substrate. Damage to the stain or coating may release the self-healing material at a site of damage, such as a crack or scratch in the stain or coating. The self-healing material may be a polymeric precursor, .an unsaturated polyester resin or alkyd, a fatty acid-based natural oil or derivative thereof, or a cross-linkable silane or siloxane monomer or resin.

Abstract: An anti-fogging coating composition comprises a dopamine, a hydrophilic polymer, a plurality of inorganic oxide particles, and a solvent. The dopamine reduces film forming time of an anti-fogging coating. An anti-fogging film using the anti-fogging coating composition, and a transparent article using the anti-fogging film are also provided.

Abstract: The invention relates to the use of phosphoric acid and/or of monoesters and/or diesters of phosphoric acid in aqueous basecoat materials for improving adhesion of these coating materials to overbaked clearcoat materials which comprise boron compounds.

Abstract: Provided are a near infrared absorbing fine particle dispersion liquid having an absorption ability in a near infrared region, a clear contrast, and applicable to offset printing, and a method for producing the same, an anti-counterfeit ink composition using the near infrared absorbing fine particle dispersion liquid and an anti-counterfeit printed matter using near infrared absorbing fine particles. Also provided are a near infrared absorbing fine particle dispersion liquid containing a solvent of one or more kinds selected from vegetable oils or vegetable oil-derived compounds; near infrared absorbing fine particles in an amount of 2 mass % or more and 25 mass % or less, selected from one or more kinds of hexaboride fine particles expressed by a general formula XBa (wherein element X is at least one or more kinds selected from a group consisting of La, Ce, Pr, Nd, Gd, Tb, Dy, Ho, Y, Sm, Eu, Er, Tm, Yb, Lu, Sr, and Ca, satisfying 4.0?a?6.

Abstract: The present invention provides a photocurable ink composition for ink jet recording with excellent curability. The photocurable ink composition for ink jet recording includes polymerizable compounds, a photopolymerization initiator, and a colorant, wherein the polymerizable compounds include a vinyl ether group-containing (meth)acrylate represented by general formula (I): CH2?CR1—COOR2—O—CH?CH—R3??(I) (wherein R1 is a hydrogen atom or a methyl group, R2 is a divalent organic residue having 2 to 20 carbon atoms, and R3 is a hydrogen atom or a monovalent organic residue having 1 to 11 carbon atoms) and phenoxyethyl (meth)acrylate.

Abstract: Novel water-based electron beam (EB) curable inkjet inks along with printed substrates, drying processes, and printing equipment are disclosed. The inks are effectively dried by EB energy alone or in combination with optional thermal drying.

Abstract: A precise, quick mark showing a surgical operation site is allowed to put on a marking target irrespective of the skin or a surgical drape attached onto the skin in surgical operation. An ink for a surgical marker is made of isopropyl alcohol as a solvent, polyvinyl pyrrolidone involved in film formation, and methylrosanilinium chloride as a pigment, and, in particular, the content of the polyvinyl pyrrolidone is set to be greater than or equal to 2% but smaller than or equal to 12%. The composition described above allows the ink to be smoothly discharged and a film containing the pigment to be quickly formed and adhered as the ink dries. A mark can therefore be put in a precise, quick manner irrespective of a marking target, the skin or a surgical drape attached onto the skin.

Abstract: The purpose of the present invention is to provide an active ray-curable inkjet ink capable of further enhancing gloss uniformity, surface curability, and scratch resistance of a formed image. The purpose is achieved by an active ray-curable inkjet ink containing a polymerization initiator, a photopolymerizable compound, and a gelling agent, and that undergoes a reversible sol-gel phase transition by temperature change. The inkjet ink contains a polymerization initiator with a molecular weight of 360 or more, and a polyfunctional photopolymerizable compound. The inkjet ink contains 3.0 mass % or more and less than 8.0 mass % of the polymerization initiator with a molecular weight of 360 or more, 1.0 mass % or more and less than 5.0 mass % of the gelling agent, less than 0.1 mass % of the initiator with a molecular weight of 360 or more, and less than 5.0 mass % of the monofunctional photopolymerizable compound.

Abstract: Optical inks suitable for 3D printing fabrication of gradient refractive index (GRIN) optical components are composed a monomer matrix material doped with ligand-functionalized nanoparticles, wherein the monomer has a viscosity less than 20 cPoise and is UV curable to form a solid polymer. The matrix material doped with the ligand-functionalized nanoparticles has a transmittance of at least 90% in a predetermined optical wavelength range, wherein the ligand functionalized nanoparticles have a size less than 100 nm, are loaded in the monomer matrix material at a volume percent of at least 2%, and alter an index of refraction of the monomer matrix by at least 0.02. The ligand-functionalized nanoparticles have a plurality of ligands attached to a nanoparticle core surface with an anchor functional group and terminated with a buoy functional group that are reactive, non-reactive, or combinations thereof. In some embodiments the ligands have a length less than 1.

Abstract: The present invention provides an electroconductive paste which is excellent in a stability upon storage for a long period and in an anti-migration property, and capable of forming electrodes, wirings and sheets having a low resistance, an extensibility and a repetitive stretchability. An electroconductive silver paste, characterized in that, it contains a silver powder (A) and a rubber (B) containing a nitrile group, that a ratio by weight of (A)/(B) is within a range of from 77/23 to 90/10, that the silver powder (A) is an amorphous aggregated powder and/or a flaky powder, and that a content of an alkali metal in the nitrile group-containing rubber (B) is 4,000 ppm or less.

Abstract: A method of forming transparent electrodes using printable conductive ink containing conductive materials dispersed in a viscous liquid which upon printing and thermal treatment will vaporise fully leaving behind the conductive material only. The viscous liquid acts as a medium by which conductive material dispersions are made processable for use in various printing techniques, allowing conductive patterns to be printed onto substrates (e.g. plastics, glass, metals, ceramics).

Abstract: A representative printable composition comprises a liquid or gel suspension of a plurality of metallic particles; a plurality of semiconductor particles; and a first solvent. The pluralities of particles may also be comprised of an alloy of a metal and a semiconductor. The composition may further comprise a second solvent different from the first solvent. In a representative embodiment, the first solvent comprises a polyol or mixtures thereof, such as glycerin, and the second solvent comprises a carboxylic or dicarboxylic acid or mixtures thereof, such as glutaric acid. In various embodiments, the metallic particles and the semiconductor particles are nanoparticles between about 5 nm to about 1.5 microns in any dimension. A representative metallic and semiconductor particle ink can be printed and annealed to produce a conductor.

Abstract: The present invention is a process for preparing a stable aqueous dispersion of polymer particles comprising structural units of a phosphorus acid monomer or a salt thereof and structural units of a photoinitiator monomer. Gloss retention of paints containing the latex prepared by the process of the present invention are improved over paints that do not have photoinitiator chemically bound to the latex particles.