Abstract: To provide a railway wheel which is excellent in corrosion fatigue resistance. The railway wheel according to the present embodiment has a chemical composition consisting of: in mass %, C: 0.65 to 0.80%, Si: 0.10 to 1.0%, Mn: 0.10 to 1.0%, P: not more than 0.030%, S: not more than 0.030%, Cr: 0.05 to 0.20%, Sn: 0.005 to 0.50%, Al: 0.010 to 0.050%, N: 0.0020 to 0.015%, Cu: 0 to 0.20%, Ni: 0 to 0.20%, Mo: 0 to 0.20%, V: 0 to 0.20%, Nb: 0 to 0.030%, and Ti: 0 to 0.030%, with the balance being Fe and impurities. A plate portion has a matrix structure composed of pearlite.

Abstract: The present invention relates to a formed product used in vehicle components and the like, and to a method for manufacturing the same. The present invention provides heat treatable steel, a formed product using the same having ultra-high strength and excellent durability, and a method for manufacturing the same, wherein the heat treatable steel contains, in wt %, C (0.22-0.42%), Si (0.05-0.3%), Mn (1.0-1.5%), Al (0.01-0.1%), P (0.01% or less (including 0), S (0.005% or less), Mo (0.05-0.3%), Ti (0.01-0.1%), Cr (0.05-0.5%), B (0.0005-0.005%), N (0.01% or less), the balance Fe, and other inevitable impurities, Mn and Si satisfying Relationship formula (1), below, Mo/p satisfying Relationship formula (2), below: [Relationship formula 1] Mn/Si?5 [Relationship formula 2] Mo/P?15.

Abstract: A steel sheet for hot pressing use according to the present invention has a specified chemical component composition, wherein some of Ti-containing precipitates contained in the steel sheet, each of which having an equivalent circle diameter of 30 nm or less, have an average equivalent circle diameter of 6 nm or less, the precipitated Ti amount and the total Ti amount in the steel fulfill the relationship represented by formula (1) shown below, and the sum total of the fraction of bainite and the fraction of martensite in the metal microstructure is 80 area % or more. Precipitated Ti amount (mass %)?3.4[N]?0.5×[(total Ti amount (mass %))?3.4[N]]??(1) (In the formula (1), [N] represents the content (mass %) of N in the steel.

Abstract: A hot-rolled austenitic iron/carbon/manganese steel sheet is provided. The strength of which is greater than 900 MPa, the product (strength (in MPa)×elongation at fracture (in %)) of which is greater than 45000 and the chemical composition of which includes, the contents being expressed by weight 0.5%?C?0.7%, 17%?Mn?24%, Si?3%, Al?0.050%, S?0.030%, P?0.080% and N?0.1%. A remainder of the composition includes iron and inevitable impurities resulting from the smelting. A recrystallized fraction of the structure of the steel is greater than 75%, a surface fraction of precipitated carbides of the steel is less than 1.5% and a mean grain size of the steel is less than 18 microns. A reinforcing element is also provided.

Abstract: A cold-rolled austenitic iron/carbon/manganese steel sheet is provided. The strength of which is greater than 950 MPa, the product (strength (in MPa)×elongation at fracture (in %)) of which is greater than 45000 and the chemical composition of which includes, the contents being expressed by weight 0.5%?C?0.7%, 17%?Mn?24%, Si?3%, Al?0.050%, S?0.030%, P?0.080% and N?0.1%. A remainder of the composition includes iron and inevitable impurities resulting from the smelting. A recrystallized fraction of the structure of the steel is greater than 75%, a surface fraction of precipitated carbides of the steel is less than 1.5% and a mean grain size of the steel is less than 6 microns. A reinforcing element is also provided.

Abstract: A steel comprises, by mass percent, C: 0.10 to 0.15%, Si: not less than 0.02% and less than 0.10%, Mn: more than 0.90% and not more than 2.50%, P?0.030%, S?0.050%, Cr: 0.80 to 2.0%, V: 0.05 to 0.50%, Al: 0.01 to 0.07%, N?0.0080%, O?0.0030%, and one or more selected from Mo, Cu, Ni, Ti, Nb, Zr, Pb, Ca, Bi, Te, Se and Sb, the balance being Fe and impurities. The composition satisfies [35?Mn/S?200], [20?(669.3×logeC?1959.6×logeN?6983.3)×(0.067×Mo+0.147×V)?80], [140×Cr+125×Al+235×V?160] and [150?511×C+33×Mn+56×Cu+15×Ni+36×Cr+5×Mo+134×V?200].

Abstract: Alloy steel compositions having improved resistance to hydrogen brittleness and methods of heat treating same are provided. The alloy steel compositions find applications in hydrogen storage containers, piping systems for hydrogen fuel cell vehicles, or reinforced boards for sound absorption/insulation on a multiple layers. The alloy steel compositions include 1.0 to 2.5% by weight of aluminum (Al), based on the total weight of the composition. Improved resistance to hydrogen brittleness is effected by stabilizing an inner part of the composition and forming an Al2O3 layer on a surface of the composition.

Abstract: A steel sheet for hot pressing use according to the present invention has a specified chemical component composition, wherein some of Ti-containing precipitates contained in the steel sheet, each of which having an equivalent circle diameter of 30 nm or less, have an average equivalent circle diameter of 3 nm or more, the precipitated Ti amount and the total Ti amount in the steel fulfill the relationship represented by formula (1) shown below, and the sum total of the fraction of bainite and the fraction of martensite in the metal microstructure is 80 area % or more. Precipitated Ti amount (mass %)?3.4[N]>0.5×[total Ti amount (mass %)?3.4[N]]??(1) (In the formula (1), [N] represents the content (mass %) of N in the steel.

Abstract: The present invention relates a high-strength nonmagnetic stainless steel, containing, by weight percent, 0.01 to 0.06% of C, 0.10 to 0.50% of Si, 20.5 to 24.5% of Mn, 0.040% or less of P, 0.010% or less of S, 3.1 to 6.0% of Ni, 0.10 to 0.80% of Cu, 20.5 to 24.5% of Cr, 0.10 to 1.50% of Mo, 0.0010 to 0.0050% of B, 0.010% or less of O, 0.65 to 0.90% of N, and the remainder being Fe and inevitable impurities; the steel satisfying the following formulae (1) to (4): [Cr]+3.3×[Mo]+16×[N]?30??(1), {Ni}/{Cr}?0.15??(2), 2.0?[Ni]/[Mo]?30.0??(3), and [C]×1000/[Cr]?2.5??(4), wherein [Cr], [Mo], [N], [Ni], [Mo] and [C] represent the content of Cr, the content of Mo, the content of N, the content of Ni, the content of Mo and the content of C in the steel, respectively, and {Ni} represents the sum of [Ni], [Cu] and [N], and {Cr} represents the sum of [Cr] and [Mo]. The present invention further relates to a high-strength nonmagnetic stainless steel part containing the steel and a process for producing the same.

Abstract: A rolled steel bar has a composition consisting, by mass percent, of C: 0.27 to 0.37%, Si: 0.30 to 0.75%, Mn: 1.00 to 1.45%, S: 0.008% or more and less than 0.030%, Cr: 0.05 to 0.30%, Al: 0.005 to 0.050%, V: 0.200 to 0.320%, and N: 0.0080 to 0.0200%, the balance being Fe and impurities. The contents of P, Ti and O in the impurities are, by mass percent, P: 0.030% or less, Ti: 0.0040% or less, and O: 0.0020% or less. Y1 expressed by the formula <1> is 1.05 to 1.18. Y1=C+(1/10)Si+(1/5)Mn+(5/22)Cr+1.65V?(5/7)S ??<1>. C, Si, Mn, Cr, V, and S in the formula represent mass percent of the elements. A hot-forged part having a tensile strength of 900 MPa or higher and a transverse endurance ratio of 0.47 can be obtained by the rolled steel bar.

Abstract: A weld metal according to the present invention has a specific chemical composition, contains carbide particles each having an equivalent circle diameter of greater than 0.5 ?m in a number of 0.25 or less per micrometer of grain boundary length, and has an A-value as specified by Formula (1) of 0.12 or more, Formula (1) expressed as follows: A-value=([V]/51+[Nb]/93)/([Cr]/52+[Mo]/96) ??(1) where [V], [Nb], [Cr], and [Mo] are contents (percent by mass) of V, Nb, Cr, and Mo, respectively, in the weld metal.

Abstract: The present invention provides high strength steel pipe for line pipe superior in low temperature toughness suppressed in drop of toughness of the HAZ and a method of production of the same, more particularly high strength steel plate for line pipe used as a material for high strength steel pipe for line pipe and a method of production of the same, in particular high strength steel pipe for line pipe superior in low temperature toughness characterized in that the chemical compositions of the base metal is, by mass %, C: 0.020 to 0.080%, Si: 0.01 to 0.50%, Mo: 0.01 to 0.15%, Al: 0.0005 to 0.030%, and Nb: 0.0001 to 0.030% contained in a range of C+0.25Si+0.1Mo+Al+Nb: 0.100% or less and the mixture of austenite and martensite present along prior austenite grain boundaries of the reheated part of the heat affected zone has a width of 10 ?m or less and a length of 50 ?m or less.

Abstract: Provided is a low yield ratio, high strength and high toughness steel plate having excellent strain ageing resistance equivalent to API 5L X70 Grade or lower and a method for manufacturing the same. The steel plate has a metallographic microstructure that is a three-phase microstructure including bainite, M-A constituent, and quasi-polygonal ferrite, the area fraction of the bainite being 5% to 70%, the area fraction of the M-A constituent being 3% to 20%, the remainder being the quasi-polygonal ferrite, the equivalent circle diameter of the M-A constituent being 3.0 ?m or less. The steel plate has a yield ratio of 85% or less and a Charpy impact test absorbed energy of 200 J or more at ?30° C. before or after being subjected to strain ageing treatment at a temperature of 250° C. or lower for 30 minutes or less.

Abstract: Disclosed is a steel having high manufacturability and better rolling-contact fatigue properties. The steel contains C of 0.65% to 1.30%, Si of 0.05% to 1.00%, Mn of 0.1% to 2.00%, P of greater than 0% to 0.050%, S of greater than 0% to 0.050%, Cr of 0.15% to 2.00%, Al of 0.010% to 0.100%, N of greater than 0% to 0.025%, Ti of greater than 0% to 0.015%, and O of greater than 0% to 0.0025% and further contains iron and unavoidable impurities. Al-containing nitrogen compound particles dispersed in the steel have an average equivalent circle diameter of 25 to 200 nm, and Al-containing nitrogen compound particles each having an equivalent circle diameter of 25 to 200 nm are present in a number density of 1.1 to 6.0 per square micrometer.

Abstract: There is provided a hot press-formed product, including a thin steel sheet formed by a hot press-forming method, and having a metallic structure that contains martensite at 80% to 97% by area and retained austenite at 3% to 20% by area, the remainder structure of which is at 5% by area or lower, whereby balance between strength and elongation can be controlled in a proper range and high ductility can be achieved.

Abstract: There is provided a hot press-formed product, including a steel sheet formed by a hot press-forming method, and having a metallic structure that contains ferrite at 30% to 80% by area, bainitic ferrite at lower than 30% by area (not including 0% by area), martensite at 30% by area or lower (not including 0% by area), and retained austenite at 3% to 20% by area, whereby balance between strength and elongation can be controlled in a proper range and high ductility can be achieved.

Abstract: There is provided a hot press-formed product, including a thin steel sheet formed by a hot press-forming method, and having a metallic structure that contains bainitic ferrite at 70% to 97% by area, martensite at 27% by area or lower, and retained austenite at 3% to 20% by area, the remainder structure of which is at 5% by area or lower, whereby balance between strength and elongation can be controlled in a proper range and high ductility can be achieved.

Abstract: A high strength galvanized steel sheet has a TS of 590 MPa or more and excellent processability. The component composition contains, by mass %, C: 0.05% to 0.3%, Si: 0.7% to 2.7%, Mn: 0.5% to 2.8%, P: 0.1% or lower, S: 0.01% or lower, Al: 0.1% or lower, and N: 0.008% or lower, and the balance: Fe or inevitable impurities. The microstructure contains, in terms of area ratio, ferrite phases: 30% to 90%, bainite phases: 3% to 30%, and martensite phases: 5% to 40%, in which, among the martensite phases, martensite phases having an aspect ratio of 3 or more are present in a proportion of 30% or more.

Abstract: There is provided a hot press-formed product, including a thin steel sheet formed by a hot press-forming method, and having a metallic structure that contains retained austenite at 3% to 20% by volume, whereby balance between strength and elongation can be controlled in a proper range and high ductility can be achieved.

Abstract: A steel for nitriding having a chemical composition consisting of, by mass percent, C: 0.07-0.14%, Si: 0.10-0.30%, Mn: 0.4-1.0%, S: 0.005-0.030%, Cr: 1.0-1.5%, Mo: ?0.05% (including 0%), Al: 0.010% or more to less than 0.10%, V: 0.10-0.25%, optionally at least one element selected from Cu: ?0.30% and Ni: ?0.25% [0.61Mn+1.11Cr+0.35Mo+0.47?2.30], and the balance of Fe and impurities. P, N, Ti and O among the impurities are P: ?0.030%, N: ?0.008%, Ti: ?0.005%, and O: ?0.0030%. The steel is easily subjected to cutting before nitriding and suitable for use as an automobile ring gear. The nitrided component having a surface hardness of 650-900 HV, core hardness being ?150 HV, and effective case depth of ?0.15 mm has excellent bending fatigue strength and surface fatigue strength although the content of Mo is as low as ?0.05% and has a small amount of expansion caused by nitriding.

Abstract: A high-strength non-oriented electrical steel sheet contains: in mass %, C: 0.010% or less; Si: not less than 2.0% nor more than 4.0%; Mn: not less than 0.05% nor more than 0.50%; Al: not less than 0.2% nor more than 3.0%; N: 0.005% or less; S: not less than 0.005% nor more than 0.030%; and Cu: not less than 0.5% nor more than 3.0%, a balance being composed of Fe and inevitable impurities. An expression (1) is established where a Mn content is represented as [Mn] and a S content is represented as [S], and not less than 1.0×104 pieces nor more than 1.0×106 pieces of sulfide having a circle-equivalent diameter of not less than 0.1 ?m nor more than 1.0 ?m are contained per 1 mm2.

Abstract: This weld metal has a predetermined chemical composition, controls the number of oxides in accordance with size, and has an A value stipulated by the belowmentioned formula of no greater than 5.0. A value=(100×[C]?6×[insol.Cr]?2×[insol.Mo]?24×[insol.V]?13×[insol.Nb])×([Mo]?[insol.Mo]), where [insol.Cr], [insol.Mo], [insol.Nb], and [insol.V] are contents (in mass percent) of Cr, Mo, Nb, and V, respectively, present as a compound after stress-relief heat treatment, and [C] and [Mo] are contents (in mass percent) of C and Mo, respectively, contained in the weld metal.

Abstract: This weld metal has excellent creep characteristics and has a given chemical composition. In the weld metal, the value A defined by equation (1) is 200 or greater, and carbide particles each having an equivalent-circle diameter of 0.40 ?m or more have an average equivalent-circle diameter less than 0.85 ?m. In the segments that connect the centers of three or more carbide particles which are present on a 6-?m straight line and which each has an equivalent-circle diameter of 0.40 ?m or more, the sum of the lengths of the portions where the segments intersect the carbide particles is 25% or more of the overall length of the segments. Value A=([V]/51+[Nb]/93)/{[V]×([Cr]/5+[Mo]/2)}×104??(1) In the equation, [V], [Nb], [Cr], and [Mo] respectively indicate the contents (mass %) of V, Nb, Cr, and Mo in the weld metal.

Abstract: A wire-form spray material, in particular for arc wire spraying, essentially comprising iron. The spray material is formed at least with carbon as a microalloy such that upon solidification of the spray material a fine pearlitic, bainitic, martensitic structure arises in which finely dispersed nitrides are present.

Abstract: This steel wire material contains 0.05%-1.2% C (“%” means “% by mass,” same hereinafter for chemical components.), 0.01%-0.7% Si, 0.1%-1.5% Mn, 0.02% max. P (not including 0%), 0.02% max. S (not including 0%), and 0.005% max. N (not including 0%), with the remainder being iron and unavoidable impurities. The steel wire material has a scale 6.0-20 ?m thick and holes of an equivalent circle diameter of 1 ?m max. in said scale that occupy 10% by area max. Said scale does not detach in the cooling process after hot rolling or during storage or transportation but can readily detach during mechanical descaling.

Abstract: The steel wire material of the present invention contains 0.05 to 1.2% of C (mass %; same for the chemical components hereafter), 0.01 to 0.5% of Si, 0.1 to 1.5% of Mn, 0.02% or less (but not 0%) of P, 0.02% or less (but not 0%) of S, and 0.005% or less (but not 0%) of N, with the balance being iron and inevitable impurities. The wire material has a scale layer that is no thicker than 7.0 ?m or less. The scale layer has an FeO percentage of 30 to 80 vol % and an Fe2SiO4 percentage of less than 0.1 vol %. The scale layer that is formed will not peel when cooled after hot rolling or during storage and transport, but will easily peel during mechanical descaling.

Abstract: A lead free free-cutting steel is described having the following composition in percent by weight: C 0.85-1.2 Si 0.1-0.6 Mn 0.4-1.2 P max 0.05 S 0.04-0.3 Cr max 2 Ni max 1 Mo max 0.5 Cu max 2 Al max 0.1 B max 0.008 Bi+Se+Te max 0.005 Ti+Nb+Zr+V max 0.2 balance Fe and normally occurring impurities. The steel is mainly intended for small/thin dimensions and/or low cutting speeds during manufacture of a product formed of the steel.

Abstract: A rolled steel bar or a wire rod for hot forging capable of coping with both bending/surface fatigue strength of components and machinability at a high level includes: a composition containing, in mass %, C: 0.1 to 0.25%, Si: 0.01 to 0.10%, Mn: 0.4 to 1.0%, S: 0.003 to 0.05%, Cr: 1.60 to 2.00%, Mo: 0.10% or less (including 0%), Al: 0.025 to 0.05%, and N: 0.010 to 0.025%, where a value of fn1 represented in a following formula (1) satisfies 1.82?fn1?2.10: fn1=Cr+2×Mo (1); impurities containing P: 0.025% or less, Ti: 0.003% or less, and O (oxygen): 0.002% or less; and a cross section in which a maximum value/a minimum value of an average ferrite grain diameter is 2.0 or less when measurement by observation is randomly carried out in 15 visual fields with an area per visual field set to be 62500 ?m2.

Abstract: Provided is bearing steel excellent in workability after spheroidizing-annealing and in hydrogen fatigue resistance property after quenching and tempering. The bearing steel has a chemical composition containing, by mass %: 0.85% to 1.10% C; 0.30% to 0.80% Si; 0.90% to 2.00% Mn; 0.025% or less P; 0.02% or less S; 0.05% or less Al; 1.8% to 2.5% Cr; 0.15% to 0.4% Mo; 0.0080% or less N; and 0.0020% or less O, which further contains more than 0.0015% to 0.0050% or less Sb, with the balance being Fe and incidental impurities, to thereby effectively suppress the generation of WEA even in environment where hydrogen penetrates into the steel, so as to improve the roiling contact fatigue life and also the workability such as cuttability and forgeability of the material.

Abstract: A steel for electron-beam welding according to the present invention includes at least C: 0.02% to 0.10%, Si: 0.03% to 0.30%, Mn: 1.5% to 2.5%, Ti: 0.005% to 0.015%, N: 0.0020% to 0.0060%, and O: 0.0010% to 0.0035%, further includes S: limited to 0.010% or less, P: limited to 0.015% or less, and Al: limited to 0.004% or less, with a balance including iron and inevitable impurities. An index value CeEBB obtained by substituting composition of the steel into following Formula 1 falls in the range of 0.42 to 0.65%, the number of oxide having an equivalent circle diameter of 1.0 ?m or more is 20 pieces/mm2 or less at a thickness center portion in cross section along the thickness direction of the steel, and the number of oxide containing Ti of 10% or more and having an equivalent circle diameter of not less than 0.05 ?m or more and less than 0.5 ?m falls in the range of 1×103 to 1×105 pieces/mm2 at the thickness center portion.

Abstract: A steel sheet for enameling for eliminating surface defects such as fish scale defects and having excellent formability, and provides a steel sheet for enamel having no surface defects, including: more than 0 wt % and 0.005 wt % or less of C, 0.1 to 0.5 wt % of Mn, more than 0 wt % and 0.03 wt % or less of Si, 0.05 to 0.3 wt % of Cr, more than 0 wt % and 0.03 wt % or less of Al, 0.03 to 0.1 wt % of O, more than 0 wt % and 0.03 wt % or less of P, more than 0 wt % and 0.02 wt % or less of S, more than 0 wt % and 0.015 wt % or less of Cu, more than 0 wt % and 0.005 wt % or less of N, Fe in a remaining content, and other inevitable impurities.

Abstract: Provided is a bearing steel capable of exhibiting excellent cold workability in cold working that follows spheroidizing annealing and also capable of ensuring excellent abrasion resistance and rolling fatigue characteristics as a bearing member or the like. The bearing steel contains C: 0.9 to 1.10%, Si: 0.05 to 0.49%, Mn: 0.1 to 1.0%, P: not more than 0.05% (excluding 0%), S: not more than 0.05% (excluding 0%), Cr: 0.03 to 0.40%, Al: not more than 0.05% (excluding 0%), N: 0.002 to 0.025%, Ti: not more than 0.0030% (excluding 0%), and 0: not more than 0.0025% (excluding 0%), with the remainder being iron and unavoidable impurities. The average aspect ratio of cementite is not more than 2.00, the average circle-equivalent diameter of cementite is 0.35 to 0.6 ?m, and the number density of cementite having a circle-equivalent diameter of not less than 0.13 ?m is not less than 0.45/?m2.

Abstract: A ferritic stainless steel sheet having excellent corrosion resistance and a method of manufacturing the steel sheet are provided. Specifically, the ferritic stainless steel sheet of the invention contains C of 0.03% or less, Si of 1.0% or less, Mn of 0.5% or less, P of 0.04% or less, S of 0.02% or less, Al of 0.1% or less, Cr of 20.5% to 22.5%, Cu of 0.3% to 0.8%, Ni of 1.0% or less, Ti of 4×(C %+N %) to 0.35%, Nb of less than 0.01%, N of 0.03% or less, and C+N of 0.05% or less, and has the remainder including Fe and inevitable impurities, wherein 240+35×(Cr %?20.5)+280×{Ti %?4×(C %+N %)}?280 is satisfied.

Abstract: A multi-phase steel sheet having microstructure having in combination ferrite, martensite of between 3% and 65% by volume, and at least one microstructure selected from the group consisting of, bainite and retained austenite, and having fine complex precipitates selected from the group of TiC, NbC, TiN, NbN, (Ti.Nb)C, (Ti.Nb)N, and (Ti.Nb)(C.N) particles having at least 50% smaller than 20 nm in size, and physical properties having tensile strength greater than about 780 megapascals and at least one of the properties of elongation greater than about 10%, yield ratio greater than about 70%, and hole expansion ratio greater than about 50%.

Abstract: Disclosed is a high-strength steel plate having a predetermined chemical composition, in which a microstructure of the steel plate at a depth of one-fourth to one half the thickness from a surface has an area fraction of bainite of 90% or more, an average lath width of bainite of 3.5 ?m or less, and a maximum equivalent circle diameter of martensite-austenite constituents in bainite of 3.0 ?m or less. The steel plate exhibits high strengths and good drop weight properties and is useful as structural materials for offshore structure, ships, and bridges, as well as materials for pressure vessels in nuclear power plants.

Abstract: A master alloy used to produce the steel part and a process for producing a sinter hardened steel part from the master alloy are described. The powdered master alloy having a composition of iron, about 1 to less than 5 weight % C, about 3 to less than 15 weight % Mn, and about 3 to less than 15 weight % Cr, wherein the master alloy comprises a microstructure composed of a solid solution of the alloying elements and carbon, the microstructure comprising at least 10 volume % austenite and the remainder as iron compounds. The process comprises: preparing the master alloy, mixing the master alloy with a steel powder to produce a mixture wherein the weight % of the master alloy is from 5 to 35 weight % of the mixture, compacting the mixture into a shape of a part and sintering the mixture to produce the steel part, and controlling the cooling rate after sintering to produce sinter hardening. The master alloy powder can also be used as a sinter hardening enhancer when mixed with low-alloy steel powders.

Abstract: Provided is a high-carbon steel wire which gives steel wires having high strength and has excellent suitability for wiredrawing and which after being wiredrawn, has excellent fatigue properties. The high-carbon steel wire has an adequately regulated chemical composition and has a pearlite structure in an areal proportion of 90% or more. In 2,000 ?m2 of the pearlite structure, the number of BN compound grains having an equivalent-circle diameter of 100 nm or more but less than 1,000 nm is 100 or less (including 0) and the number of BN compound grains having an equivalent-circle diameter of 1,000 nm or more is 10 or less (including 0).

Abstract: A non-oriented electrical steel sheet contains Cr: 0.3 mass % to 5.3 mass %, Si: 1.5 mass % to 4 mass %, Al: 0.4 mass % to 3 mass %, and W: 0.0003 mass % to 0.01 mass %. A C content is 0.006 mass % or less, a Mn content is 1.5 mass % or less, a S content is 0.003 mass % or less, and a N content is 0.003 mass % or less, and the balance is composed of Fe and inevitable impurities.

Abstract: Disclosed is a high-strength electric resistance welded steel pipe which is manufacture from a steel sheet containing, on mass basis, 0.2% to 0.4% C, 0.05% to 0.5% Si, 0.5% to 2.5% Mn, 0.025% or less P, 0.01% or less S, 0.01% to 0.15% or Al, 0.01% to 2% Cu, 0.05% to 2% Cr, 0.005% to 0.2% Ti, and 0.0002% to 0.005% B, with the remainder being iron and inevitable impurities. The steel pipe has a tensile strength of 1750 N/mm2 or more, a 0.1%-proof stress of 1320 N/mm2 or more, and a Charpy impact value at a testing temperature of minus 40° C. of 50 J/cm2 or more.

Abstract: A spring steel contains 0.15-0.40% carbon, 1-3.5% silicon, 0.20-2.0% manganese, 0.05-1.20% chromium, at most 0.030% phosphorus, at most 0.02% sulfur, and at least one of the following: 0.005-0.10% titanium, 0.005-0.05% niobium, and at most 0.25% vanadium. The remainder of said spring steel includes iron and unavoidable impurities. The carbon equivalent (Ceq1) of the provided spring steel, as calculated by formula (1), is at most 0.55. (1) Ceq1=[C]+0.108×[Si]?0.067×[Mn]+0.024×[Cr]?0.05×[Ni]+0.074×[V]. In the formula (1), each symbol in brackets represents the content (mass %) of the corresponding element.

Abstract: Disclosed is steel for a leaf spring with high fatigue strength containing, in mass percentage, C: 0.40 to 0.54%, Si: 0.40 to 0.90%, Mn: 0.40 to 1.20%, Cr: 0.70 to 1.50%, Ti: 0.070 to 0.150%, B: 0.0005 to 0.0050%, N: 0.0100% or less, and a remainder composed of Fe and impurity elements. Also disclosed is a high fatigue-strength leaf spring part obtained by forming the steel. The steel for a leaf spring is prepared to have a Ti content and a N content to satisfy a relation of Ti/N?10. Preferably, the leaf spring part is subjected to a shot peening treatment in a temperature range of the room temperature through 400° C. with a bending stress of 650 to 1900 MPa being applied to it.

Abstract: The present invention provides a wire rod with a composition at least including: C: 0.95-1.30 mass %; Si: 0.1-1.5 mass %; Mn: 0.1-1.0 mass %; Al: 0-0.1 mass %; Ti: 0-0.1 mass %; P: 0-0.02 mass %; S: 0-0.02 mass %; N: 10-50 ppm; O: 10-40 ppm; and a balance including Fe and inevitable impurities, wherein 97% or more of an area in a cross-section perpendicular to the longitudinal direction of the wire rod is occupied by a pearlite, and 0.5% or less of an area in a central area in the cross-section and 0.5% or less of an area in a first surface layer area in the cross-section are occupied by a pro-eutectoid cementite.

Abstract: A high strength steel sheet contains, in percent by mass, 0.03 to 0.2% of C, 0.5 to 2.5% of Si, 1 to 3.0% of Mn, 0.01 to 0.5% of Cr, 0.01 to 0.5% of Mo, 0.02 to 0.15% of Al, 0.15% or less of Ti, 0.15% or less of No, and 0.15% or less of V; wherein the remainder includes Fe and inevitable impurities, and the content of Si satisfies the following formula (1), ?-4.1[Si]?-2.4??(1), provided, ?=6.9×([C]+[Mn]/6+[Cr]/5+[Mo]/4+[Ti]/15+[Nb]/17+[V]/14)1/2 is given, wherein [ ] shows the quantity (mass percent) of each element contained in the steel sheet. The high strength steel sheet is improved in formability (particularly, elongation), and excellent in balance between strength and elongation.

Abstract: A steel material composition, in particular for producing piston rings and cylinder liners, comprises the following elements in the listed quantities, relative to 100% by weight of the steel material: 0.5-1.2% by weight C, 0-3.0% by weight Cr, 72.0-94-5% by weight Fe, 3.0-15.0% by weight Mn and 2.0-10.0% by weight Si. The composition can be produced by producing a melt of the starting materials and casting the melt in a prefabricated mold.

Abstract: A cobalt-free low cost high strength martensitic stainless steel, with concentration of Ni up to 3.0% and Mo up to 1.0% of weight, has HRC of 53, UTS of 297 ksi, YS of 220 ksi, Charpy V-notch impact energy of 17.8 ft-lb, corrosion resistance in salt spray test ASTM 117. The steel was melted in an open induction furnace and vacuum arc remelting (VAR) and/or electroslag remelting (ESR) were not used to refine the steel. Further processing included homogenized annealing, hot rolling, and recrystallization annealing. The steel was heat treated by oil quenching, refrigeration, and low tempering. The steel has a microstructure consisting essentially of small packets of fine martensite laths, retained austenite, and carbides as centers of growth of the martensite laths. The cost and energy in making the steel are substantially reduced.

Abstract: A cold-rolled steel sheet has a chemical composition of C: 0.12% to 0.3%, Si: 0.5% or less, Mn: less than 1.5%, Al: 0.15% or less, N: 0.01% or less, P: 0.02% or less, and S: 0.01% or less, with the remainder including iron and inevitable impurities and has a martensite single-phase structure as its steel microstructure. In a surface region of the steel sheet from the surface to a depth one-tenth the gauge, the number density of n-ary groups of inclusions determined by specific n-th determinations is 120 or less per 100 cm2 of a rolling plane, where the distance in steel sheet rolling direction between outermost surfaces of two outermost particles of the group of inclusions is 100 ?m or more. The steel sheet is a high-strength cold-rolled steel sheet which has a sufficiently minimized rate of bending fracture starting from inclusions and thereby has excellent bending workability.

Abstract: The invention provides a steel material with satisfactory hydrogen embrittlement resistance, and particularly it relates to high-strength steel with satisfactory hydrogen embrittlement resistance and a strength of 1200 MPa or greater, as well as a process for production thereof. At least one simple or compound deposit of oxides, carbides or nitrides as hydrogen trap sites which trap hydrogen with a specific trap energy is added to steel, where the mean sizes, number densities, and length-to-thickness ratios (aspect ratio) are in specific ranges. By applying the specific steel components and production process it is possible to obtain high-strength steel with excellent hydrogen embrittlement resistance.

Abstract: Provided are a steel sheet for an automotive muffler and a method for producing the steel sheet. The steel sheet includes 0.01% by weight or less of C, 0.1 to 0.3% by weight of Si, 0.3 to 0.5% by weight of Mn, 0.015% by weight or less of P, 0.015% or less by weight of S, 0.02 to 0.05% by weight of Al, 0.004% or less of N, 0.2 to 0.6% by weight of Cu, 0.01 to 0.04% by weight of Co, and a remainder of Fe and unavoidable impurities. The method includes 0.01% by weight or less of C, 0.1 to 0.3% by weight of Si, 0.3 to 0.5% by weight of Mn, 0.015% by weight or less of P, 0.015% or less by weight of S, 0.02 to 0.05% by weight of Al, 0.004% or less of N, 0.2 to 0.6% by weight of Cu, 0.01 to 0.

Abstract: The present invention provides high strength thick steel plate superior in crack arrestability high in strength, free of deterioration of HAZ toughness, and free of anisotropy, that steel plate containing, by mass %, C: 0.03 to 0.15%, Si: 0.1 to 0.5%, Mn: 0.5 to 2.0%, P: ?0.02%, S: ?0.01%, Al: 0.001 to 0.1%, Ti: 0.005 to 0.02%, Ni: 0.15 to 2%, and N: 0.001 to 0.008% and having a balance of iron and unavoidable impurities as chemical components, having a microstructure of a ferrite and/or pearlite structure with bainite as a matrix phase, and having an average circle equivalent diameter of crystal grains with a crystal misorientation angle of 15° or more of 15 ?m or less in the regions of 10% of plate thickness from the front and rear surfaces and of 40 ?m or less in the other region including the center part of plate thickness.

Abstract: To provide a production process of an electrode catalyst for fuel cell whose initial voltage is high and whose endurance characteristics, especially, whose voltage drop being caused by high-potential application is less. A production process according to the present invention of an electrode catalyst for fuel cell is characterized in that: it includes: a dispersing step of dispersing a conductive support in a solution; a loading step of dropping a platinum-salt solution, a base-metal-salt solution and an iridium-salt solution to the resulting dispersion liquid, thereby loading respective metallic salts on the conductive support as hydroxides under an alkaline condition; and an alloying step of heating the conductive support with metallic hydroxides loaded in a reducing atmosphere to reduce them, thereby alloying them.