Abstract: A semiconductor process is disclosed. The semiconductor process includes the steps of: providing a substrate having a specific area defined thereon; and performing an etch process by using an etchant comprising H2O2 to etch the specific area for forming a recess.

Abstract: A process for forming a shallow trench isolation structure is provided. Firstly, a semiconductor substrate is provided. Then, a hard mask is formed over the semiconductor substrate, wherein the hard mask includes a pad oxide layer, a silicon nitride layer and an opening. Then, a trench is formed in the semiconductor substrate according to the opening Then, a pull-back process is performed to treat the silicon nitride layer at a sidewall of the opening, wherein the pull-back process is a wet etching process carried out in a phosphoric acid solution. After the pull-back process is performed, an insulating material is filled in the trench, thereby forming the shallow trench isolation structure.

Abstract: A manufacturing method of a metal gate structure includes providing a substrate having at least a first metal oxide layer formed thereon, and transferring the surface of the first metal oxide layer into a second metal oxide layer. The first metal oxide layer includes a metal oxide (M1Ox) of a first metal (M1) and the second metal oxide layer includes a metal oxide ((M1M2Oy) of the first metal and a second metal (M2).

Abstract: A method of fabricating a semiconductor structure, in which after an etching process is performed to form at least one recess within a semiconductor beside a gate structure, a thermal treatment is performed on the recess in a gas atmosphere including an inert gas before a silicon-containing epitaxial layer is formed in the recess through an epitaxy growth process.

Abstract: A semiconductor process includes the following steps. A substrate is provided, which includes an isolation structure and an oxide layer. The isolation structure divides the substrate into a first region and a second region. The oxide layer is located on the surface of the first region and the second region. A dry cleaning process is performed to remove the oxide layer. A dielectric layer is formed on the first region and the second region. A wet etching process is performed to remove at least one of the dielectric layers located on the first region and the second region. A semiconductor structure is fabricated by the above semiconductor process.

Abstract: A process for manufacturing a stress-providing structure is applied to the fabrication of a semiconductor device. Firstly, a substrate with a channel structure is provided. A silicon nitride layer is formed over the substrate by chemical vapor deposition in a halogen-containing environment. An etching process is performed to partially remove the silicon nitride layer to expose a portion of a surface of the substrate beside the channel structure. The exposed surface of the substrate is etched to form a recess in the substrate. Then, the substrate is thermally treated at a temperature between 750° C. and 820° C. After the substrate is thermally treated, a stress-providing material is filled in the recess to form a stress-providing structure within the recess. The semiconductor device includes a substrate, a recess and a stress-providing structure. The recess has a round inner surface. The stress-providing structure has a round outer surface.

Abstract: A manufacturing method for a semiconductor structure includes providing a substrate having at least a gate structure formed thereon, performing a first wet etching process to etch the substrate at two sides of the gate structure, performing a second wet etching process to etch the substrate to form a recess respectively at two sides of the gate structure, and performing a selective epitaxial growth method to form an epitaxial layer having a diamond shape with a flat bottom respectively in the recess.

Abstract: A method of fabricating a semiconductor structure, in which after an etching process is performed to form at least one recess within a semiconductor beside a gate structure, a thermal treatment is performed on the recess in a gas atmosphere including an inert gas before a silicon-containing epitaxial layer is formed in the recess through an epitaxy growth process.

Abstract: A method of fabricating an epitaxial layer includes providing a substrate. The substrate is etched to form at least a recess within the substrate. A surface treatment is performed on the recess to form a Si—OH containing surface. An in-situ epitaxial process is performed to form an epitaxial layer within the recess, wherein the epitaxial process is performed in a hydrogen-free atmosphere and at a temperature lower than 800° C.

Abstract: A manufacturing method of a metal gate structure includes providing a substrate having at least a first metal oxide layer formed thereon, and transferring the surface of the first metal oxide layer into a second metal oxide layer. The first metal oxide layer includes a metal oxide (M1Ox) of a first metal (M1) and the second metal oxide layer includes a metal oxide ((M1M2Oy) of the first metal and a second metal (M2).

Abstract: A semiconductor structure including a substrate and a gate structure disposed on the substrate is disclosed. The gate structure includes a gate dielectric layer disposed on the substrate, a gate material layer disposed on the gate dielectric layer and an outer spacer with a rectangular cross section. The top surface of the outer spacer is lower than the top surface of the gate material layer.

Abstract: A fin field-effect transistor structure includes a substrate, a fin channel and a high-k metal gate. The high-k metal gate is formed on the substrate and the fin channel. A process of manufacturing the fin field-effect transistor structure includes the following steps. Firstly, a polysilicon pseudo gate structure is formed on the substrate and a surface of the fin channel. By using the polysilicon pseudo gate structure as a mask, a source/drain region is formed in the fin channel. After the polysilicon pseudo gate structure is removed, a high-k dielectric layer and a metal gate layer are successively formed. Afterwards, a planarization process is performed on the substrate having the metal gate layer until the first dielectric layer is exposed, so that a high-k metal gate is produced.

Abstract: A method for forming a metal gate is provided. First, a dummy material is formed to completely cover a substrate. Second, a dopant is selectively implanted into the dummy material. Then, some of the dummy material is removed to expose part of the substrate and to form a dummy gate including a dopant region disposed between a first region and a second region. Later an interlayer dielectric layer is formed to surround the dummy gate. Next, a selective etching step is carried out to remove the first region to form a recess without substantially removing the dopant region. Afterwards, the recess is filled with a material set to form a metal gate.

Abstract: A method of fabricating a MOS device comprises steps as follows: An interfacial layer, a high-k dielectric layer and a cover layer on a substrate are sequentially formed. Then an in-situ wet etching step is performed by sequentially using a first etching solution to etch the cover layer and using a second etching solution to etch the high-k dielectric layer and the interfacial layer until the substrate is exposed, wherein the second etching solution is a mixed etching solution containing the first etching solution.

Abstract: A method for removing a photoresist is disclosed. First, a substrate including a patterned photoresist is provided. Second, an ion implantation is carried out on the substrate. Then, a non-oxidative pre-treatment is carried out on the substrate. The non-oxidative pre-treatment provides hydrogen, a carrier gas and plasma. Later, a photoresist-stripping step is carried out so that the photoresist can be completely removed.

Abstract: A method for fabricating a fin-FET, wherein the method comprises several steps as follows: A substrate is first provided, and a silicon fin is then formed in the substrate. Next a dielectric layer is formed on the silicon fin and the substrate. A poly silicon layer is subsequently formed on the dielectric layer, and the poly silicon layer is then planarized. Subsequently, a poly silicon gate is formed and a portion of the silicon fin is exposed by patterning the planarized poly silicon layer. A source and a drain are separately formed on two opposite sides of the exposed silicon fin adjacent to the poly silicon gate.

Abstract: A method for fabricating a semiconductor device is provided. A high dielectric constant (high-k) layer and a work function metal layer are formed in sequence on a substrate. A hard mask layer is formed on the work function metal layer, where the material of the hard mask layer is lanthanum oxide. The work function metal layer is patterned by using the hard mask layer as a mask. The hard mask layer is then removed. Afterwards, a gate structure is formed on the substrate.

Abstract: A method of fabricating a CMOS device having high-k dielectric layer and metal gate electrode is provided. First, an isolation structure is formed in a substrate to define a first-type and a second-type MOS regions; an interfacial layer and a high-k dielectric layer are sequentially formed over the substrate; a first and a second cover layers are respectively formed over a portion of the high-k dielectric layer at the first-type MOS region and another portion of the high-k dielectric layer at the second-type MOS region; afterwards, an in-situ etching step is performed to sequentially etch the first and second cover layers using a first etching solution and to etch both the high-k dielectric layer and the interfacial layer using a second etching solution until the substrate is exposed. Wherein, the second etching solution is a mixed etching solution containing the first etching solution.

Abstract: A strained silicon substrate structure includes a first transistor and a second transistor disposed on a substrate. The first transistor includes a first gate structure and two first source/drain regions disposed at two sides of the first gate structure. A first source/drain to gate distance is between each first source/drain region and the first gate structure. The second transistor includes a second gate structure and two source/drain doped regions disposed at two side of the second gate structure. A second source/drain to gate distance is between each second source/drain region and the second gate structure. The first source/drain to gate distance is smaller than the second source/drain to gate distance.

Abstract: A method for manufacturing a multi-gate transistor device includes providing a semiconductor substrate having a first patterned semiconductor layer formed thereon, sequentially forming a gate dielectric layer and a gate layer covering a portion of the first patterned semiconductor layer on the semiconductor substrate, removing a portion of the first patterned semiconductor layer to form a second patterned semiconductor layer, and performing a selective epitaxial growth process to form an epitaxial layer on a surface of the second patterned semiconductor layer.