Abstract: Methods for selectively forming a transition metal dichalcogenide (TMDC) film comprise exposing a substrate comprising a silicon oxide-based surface and a tungsten (W) segment to a sulfur source to selectively form the transition metal dichalcogenide film with the tungsten segment relative to the silicon oxide-based surface. Chemical vapor deposition (CVD) at a temperature in a range of 350° C. to 600° C. is used to form the TMDC film. CVD may be conducted by low pressure CVD (LPCVD) or atmospheric pressure CVD (APCVD). Methods of making devices incorporating the TMDC films are also provided.

Abstract: Processing methods to form self-aligned high aspect ratio features are described. The methods comprise depositing a metal film on a structured substrate, volumetrically expanding the metal film, depositing a second film between the expanded pillars and optionally recessing the pillars and repeating the process to form the high aspect ratio features.

Abstract: Methods of depositing a carbon film are discussed. Some embodiments selectively deposit a carbon film on a metal surface over a dielectric surface. Some embodiments form carbon pillars on metal surfaces selectively over dielectric surfaces. Some embodiments utilize carbon pillars in forming self-aligned vias.

Abstract: Methods of forming semiconductor device with fluorine-incorporated metal nitride films are described. A substrate surface is exposed to a metal fluoride precursor to form a metal-fluorine species on the substrate surface. The substrate surface is exposed to a nitriding agent to react with the metal-fluorine species to form a fluorine-incorporated metal nitride film.

Abstract: Memory devices and methods of manufacturing memory devices are provided. A plasma enhanced chemical vapor deposition (PECVD) method to form a memory cell film stack having more than 50 layers as an alternative for 3D-NAND cells is described. The memory stack comprises alternating layers of a first material layer and a second material layer.

Abstract: Methods and apparatus for forming a plurality of nonvolatile memory cells are provided herein. In some embodiments, the method, for example, includes forming a plurality of nonvolatile memory cells, comprising forming, on a substrate, a stack of alternating layers of metal including a first layer of metal and a second layer of metal different from the first layer of metal; removing the first layer of metal to form spaces between the alternating layers of the second layer of metal; and one of depositing a first layer of material to partially fill the spaces to leave air gaps therein or depositing a second layer of material to fill the spaces.

Abstract: Processing methods comprising selectively orthogonally growing a first material through a mask to provide an expanded first material are described. The mask can be removed leaving the expanded first material extending orthogonally from the surface of the first material. Further processing can create a self-aligned via.

Abstract: Methods and apparatus for forming a plurality of nonvolatile memory cells are provided herein. In some embodiments, the method, for example, includes forming a plurality of nonvolatile memory cells, comprising forming, on a substrate, a stack of alternating layers of metal including a first layer of metal and a second layer of metal different from the first layer of metal; removing the first layer of metal to form spaces between the alternating layers of the second layer of metal; and one of depositing a first layer of material to partially fill the spaces to leave air gaps therein or depositing a second layer of material to fill the spaces.

Abstract: In one embodiment, a method of forming a barrier layer is provided. The method includes positioning a substrate in a processing chamber, forming a barrier layer over the substrate and in contact with the underlayer, and annealing the substrate. The substrate comprises at least one underlayer having cobalt, tungsten, or copper. The barrier layer has a thickness of less than 70 angstroms.

Abstract: Methods and apparatus for forming a plurality of nonvolatile memory cells are provided herein. In some embodiments, the method, for example, includes forming a plurality of nonvolatile memory cells, comprising forming, on a substrate, a stack of alternating layers of metal including a first layer of metal and a second layer of metal different from the first layer of metal; removing the first layer of metal to form spaces between the alternating layers of the second layer of metal; and one of depositing a first layer of material to partially fill the spaces to leave air gaps therein or depositing a second layer of material to fill the spaces.

Abstract: Embodiments described herein relate to methods and materials for fabricating semiconductor device structures. In one example, a metal film stack includes a plurality of metal containing films and a plurality of metal derived films arranged in an alternating manner. In another example, a metal film stack includes a plurality of metal containing films which are modified into metal derived films. In certain embodiments, the metal film stacks are used in oxide/metal/oxide/metal (OMOM) structures for memory devices.

Abstract: Apparatuses and methods to provide a fully self-aligned via are described. A first metallization layer comprises a set of first conductive lines extending along a first direction on a first insulating layer on a substrate, the set of first conductive lines recessed below a top portion of the first insulating layer. A capping layer is on the first insulating layer, and a second insulating layer is on the capping layer. A second metallization layer comprises a set of second conductive lines on the second insulating layer and on a third insulating layer above the first metallization layer. The set of second conductive lines extend along a second direction that crosses the first direction at an angle. At least one via is between the first metallization layer and the second metallization layer. The via is self-aligned along the second direction to one of the first conductive lines. The tapering angle of the via opening may be in a range of from about 60° to about 120°.

Abstract: Methods of dep-etch in semiconductor devices (e.g. V-NAND) are described. A metal layer is deposited in a feature. The metal layer is removed by low temperature atomic layer etching by oxidizing the surface of the metal layer and etching the oxide in a layer-by-layer fashion. After removal of the metal layer, the features are filled with a metal.

Abstract: Embodiments described herein generally relate to methods of depositing thin films and, more particularly, to depositing metal thin films. The methods herein provide a nucleation free conversion (NFC) approach which involves forming an amorphous silicon layer over the dielectric layer, and performing an NFC process which acts to convert the amorphous silicon layer into a thin metal film. In some embodiments, the NFC process is performed multiple times until the resulting thin metal film is continuous. A bulk metal is formed over the thin metal film.

Abstract: Methods of forming memory structures are described. A metal film is deposited in the features of a structured substrate and volumetrically expanded to form pillars. A blanket film is deposited to a height less than the height of the pillars and the blanket film is removed from the top of the pillars. The height of the pillars is reduced so that the top of the pillars are below the surface of the blanket film and the process is optionally repeated to form a structure of predetermined height. The pillars can be removed from the features after formation of the predetermined height structure to form high aspect ratio features.

Abstract: Methods of producing a self-aligned structure are described. The methods comprise forming a metal sub-oxide film in a substrate feature and oxidizing the sub-oxide film to form a self-aligned structure comprising metal oxide. In some embodiments, a metal film is deposited and then treated to form the metal sub-oxide film. In some embodiments, the process of depositing and treating the metal film to form the metal sub-oxide film is repeated until a predetermined depth of metal sub-oxide film is formed within the substrate feature.

Abstract: Methods of forming semiconductor device with fluorine-incorporated metal nitride films are described. A substrate surface is exposed to a metal fluoride precursor to form a metal-fluorine species on the substrate surface. The substrate surface is exposed to a nitriding agent to react with the metal-fluorine species to form a fluorine-incorporated metal nitride film.

Abstract: Methods and apparatus for forming a plurality of nonvolatile memory cells are provided herein. In some embodiments, the method, for example, includes forming a plurality of nonvolatile memory cells, comprising forming, on a substrate, a stack of alternating layers of metal including a first layer of metal and a second layer of metal different from the first layer of metal; removing the first layer of metal to form spaces between the alternating layers of the second layer of metal; and one of depositing a first layer of material to partially fill the spaces to leave air gaps therein or depositing a second layer of material to fill the spaces.

Abstract: A method of forming an electronic device is disclosed. The method comprises forming depositing a metal on a substrate, the metal comprising one or more of copper (Cu), titanium (Ti), or tantalum (Ta). A metal cap is deposited on the metal, the metal cap comprising one or more of molybdenum (Mo), ruthenium (Ru), iridium (Ir), rhodium (Rh), palladium (Pd), silver (Ag), osmium (Os), platinum (Pt), or gold (Au). The substrate is then exposed to a hydrogen high-pressure anneal. The formation of the metal cap on the metal minimizes parasitic adsorption of hydrogen by the underlying metal.

Abstract: A first metallization layer comprises a set of first conductive lines that extend along a first direction on a first dielectric layer on a substrate. Pillars are formed on recessed first dielectric layers and a second dielectric layer covers the pillars. A dual damascene etch provides a contact hole through the second dielectric layer and an etch removes the pillars to form air gaps.