Abstract: A recording material of Ag1-xSbx (x=10.8˜25.5 at. %) films for WORM optical disk recording media is invented. The thermal analysis shows that the phase change temperature of AgSb film is between 250 and 270?. The optical property analysis shows that all the as deposited films have good optical absorption and high reflectivity. The X-ray Diffraction analysis shows that the as deposited film and the annealed film are kept at ??-AgSb crystalline phase. The TEM analysis shows that the grain size of the Ag80.9Sb19.1 film will grow after annealing. The dynamic test shows that the carrier-to-noise ratio (CNR) of the Ag80.9Sb19.1 optical disc is about 45 dB with ?=657 nm, NA=0.65 and a linear velocity of 3.5 m/s. These Ag1-xSbx films have good optical absorption, high reflectivity and good carrier-to-noise ratio. It can be used as the WORM optical disk recording film.

Abstract: A novel heat assisted magnetic recording (HAMR) medium and the fabrication method therefor are provided. The exchange coupling effect occurring at the interface of FePt/CoTb double layers is adopted, and thus the resulting magnetic flux would be sufficient enough to be detected and readout under the room temperature. The provided HAMR medium exhibits a relatively high saturation magnetization and perpendicular coercivity, and thus possesses a great potential for the ultra-high density recording application.