OPTIMIZED PROCESS FOR THE PREPARATION OF OLEFINS BY DIRECT CONVERSION OF MULTIPLE HYDROCARBONS

Abstract

A process for hydrocarbon conversion to prepare lower olefins such as ethylene, propylene, etc., and light aromatics by bringing hydrocarbons into contact with a solid granular catalyst. In order to optimize the reaction conditions and product structure and save the capital and operating costs, a piston flow reactor is used in this process and multiple groups of feed inlets, which allow hydrocarbons with different properties to enter the device from different feed inlets and proceed pyrolysis under different operation conditions, are set on the reactor. This process is usable for individual pyrolysis or co-feed pyrolysis of hydrocarbons from refinery gases, liquid hydrocarbons, to heavy residues.

Description

FIELD OF THE INVENTION

[0001] The present invention relates to a technological process for the preparation of lower olefins with stress on ethylene by conversion of hydrocarbons.

BACKGROUND ARTS

[0002] Research on the production of ethylene by the pyrolysis of heavy oils has been very active in recent years both in china and abroad, for example, the QC (quick contact) reaction system developed by Stone & Webster Eng Co. of USA (U.S. Pat. No. 4,663,019, ZL88102644.1 and EP 0381870A etc.): this technology uses a downward tubular reactor and a feeding mode of a single feed oil. The steam pyrolysis technology developed by British Petroleum Ltd. (U.S. Pat. No. 4,087,350): this technology uses a tubular fixed bed catalytic reactor. The technology developed by Tokyo Science and Technology Co. of Japan for producing olefins using coke particles as a heat carrier (U.S. Pat. No. 4,259,177): this technology uses a fluidized bed reactor of the reaction-regeneration type. The HCC (Heavy-oil contact cracking) technology developed by SINOPEC Loyang Petro-Chemical Engineering Co. (ZL 92105507.2): this technology uses an up flow or down flow tubular piston flow reactor and a feeding mode of a single feed oil. The above technologies are all able to produce ethylene from heavy oils. But in the flow sheets of the above technologies, only the case of feeding a single fresh feed oil is considered. American patent U.S. Pat. No. 5,348,644 is patent for an invention relating to the improvement of the feeding equipment and technological process of a lift pipe catalytic cracking device. The fluidization state of the catalyst in the lift pipe is optimized by installation of special equipment in the pre-lift section of the lift pipe and thereby the contact state of the catalyst and the feed oil for the catalytic cracking in the lift pipe is improved and more ideal product distribution of the catalytic cracking is obtained. Chinese patent ZL 8910052, U.S. Pat. Nos. 5,264,115 and 5,506,365 provide a fluidized bed process and device for converting hydrocarbons which consists of a steam pyrolysis section for light hydrocarbon fractions at the upstream of a reaction zone and a catalytic cracking section for heavy hydrocarbon fractions at the downstream of said reaction zone in a tubular reaction zone with an upstream or downstream flow in the presence of the catalyst particles in a fluidized phase. The applied catalyst belongs to the type of catalytic cracking. The purpose is to obtain a propylene yield slightly higher than the conventional catalytic cracking while raising the yields of gasoline and diesel oil in the product. The major characteristic is to separate C2 components from the product and then introduce them into an oligomerization reactor to proceed the oligomerization reaction; the remained C2 components and the oligomerization the catalyst is recycled for reuse after regeneration, different feeds are introduced from different positions, hydrocarbons difficult to pyrolyze are first introduced into the reactor and brought into contact with the catalyst of high temperatures and high activities from the regenerator and the pyrolysis takes place, meanwhile, the catalyst cools down and deactivates; then other hydrocarbons easier to pyrolyze are introduced in sequence from the upstream to downstream of the reaction zone, the hydrocarbons introduced later play a role of quenching those introduced earlier, the temperature of the reaction zone and the activity of the catalyst are lowered step by step from the upstream to the downstream; the positions from which various hydrocarbons enter the reactor are determined as such that the residence times of various hydrocarbons in the reactor are gradually decreased in the sequence from difficulty to ease in pyrolysis, the differences in the residence times of every adjacent two hydrocarbon feeds in the reactor are 0.01-3 s.

[0003] Another aspect of the present invention is to provide a process for direct conversion of heavy hydrocarbons to produce lower olefins with stress on ethylene and co-produce light aromatics, which is to bring the hydrocarbon feeds into contact with a solid granular catalyst in a piston flow reactor to proceed catalytic pyrolysis, the feed hydrocarbons are mixed with steam and introduced, the general reaction conditions in the reaction zone are: temperature 600-900° C., pressure 0.13-0.40 MPa (absolute), total steam/hydrocarbon ratio 0.1-1.0, total catalyst/oil ratio 5-100 and the catalyst/oil contact time 0.02-5 s; the oil gas after reaction is separated quickly from the catalyst and quenched, the catalyst is recycled for reuse after regeneration; the oil gas enters a fractionation and separation system to proceed the separation, a product gas mainly containing ethylene, the by-product ethane, and a liquid product rich in aromatics can be obtained, the highly pure by-product ethane from the separation system and/or the gases containing ethane from other sources return to the pyrolysis reactor of the piston flow type from the upstream inlet of the reactor and come into contact with the catalyst of high temperatures and high activities, fast pyrolysis takes place at temperatures higher than 780° C. to produce ethylene and meanwhile, the catalyst cools down and deactivates, steam is introduced at the same time when ethane feed is introduced from the upstream inlet of the reactor; heavy hydrocarbon feeds are introduced at position certain distance from downstream of the inlet for ethane, the hydrocarbons introduced later play a role of quenching those introduced earlier, the reaction temperature at this moment is lowered to 680-800° C.; the feeding positions of the by-product ethane and the heavy hydrocarbons are determined as such that the residence time of ethane, which is difficult to pyrolyze, is long, while that of heavy hydrocarbons, which are easy to pyrolyze, is short, the differences in the residence times of ethane and heavy hydrocarbons in the reactor are 0.01-3 s.

BRIEF DESCRIPTION OF THE DRAWING

[0004] FIG. 1—Schematic diagram of the lift pipe reactor of the present invention as an example

[0005] 1-Lift pipe

[0006] 2-Pre-lift gas

[0007] 3-Subsider

[0008] 4-Regenerated catalyst

[0009] 5-Pipeline for stripping steam

[0010] 6-Outlet of the pyrolyzed gas

[0011] I, II, III, IV are all the feed inlets

DETAILED DESCRIPTION OF THE INVENTION

[0012] Hydrocarbons entering the reactor from different inlets are subjected to different reaction conditions, for light hydrocarbons, which are difficult to pyrolyze, the pyrolysis temperature is higher and the pyrolysis time is longer, while for heavy hydrocarbons, which are difficult to pyrolyze, the reaction temperature is lower and the pyrolysis time is shorter. Hydrocarbons with different properties are fed to the reactor in sequence and the differences in the residence times in the reactor of adjacent hydrocarbons are 0.0-3 s. Hydrocarbons hard to pyrolyze are first fed to the reactor and brought into contact with the catalyst of high temperatures and high activities from the regenerator and the pyrolysis reaction takes place, at the same time, the catalyst cools down and deactivates and then other hydrocarbon feeds easy to pyrolyze are fed in sequence, the hydrocarbons fed later play a role of quenching those fed earlier.

[0013] This method is usable for the technology in which one or multiple hydrocarbon oil(s) are used as the feed(s), said hydrocarbons include ethane, propane, butane, light hydrocarbons and heavy hydrocarbons. Said heavy hydrocarbons are referred to the hydrocarbons with a distillation range higher than 350° C., including straight run heavy hydrocarbons and secondary processing heavy hydrocarbons, i.e., various straight run wax oils, coker wax oils, straight run vacuum gas oils, atmospheric residues, coker gas oils, thermal cracking heavy oils, solvent-deasphalted oils and various solvent extraction residues of heavy hydrocarbons; said light hydrocarbons are referred to hydrocarbons with a distillation range lower than 350° C., such as LPG, refinery petroleum gases, oil field gases, oil field light hydrocarbons, naphtha and light diesel oil.

[0014] Citing a lift pipe reactor as an example, the particular process is described as follows (see FIG. 1): the regenerated catalyst 4 from the regenerator enters the lift pipe 1, and then flows upward under the driving of the pre-lifting steam and pre-lifting dry gas introduced from the bottom of the lift pipe; the pre-lifting dry gas is highly pure ethane from the separation zone of the pyrolyzed gas and/or light hydrocarbon gases of other sources containing ethane, steam is added at the same time; ethane quickly pyrolyzes under the action of the hot catalyst at 780-900° C., ethane may also be sprayed from inlet I. A mixture of propane and/or butane from the separation zone and/or other sources and a certain amount of steam is atomized and sprayed from feed inlet II into the lift pipe, where the mixture comes into contact with the mixed stream of the catalyst and the ethane reactant at about 780-850° C. and the catalytic pyrolysis reaction takes place. A mixture of the light hydrocarbons having a distillation range lower than 350° C. and a certain amount of steam is atomized and sprayed from feed inlet II into the lift pipe, where the mixture comes into contact with the mixture of the catalyst and the upstream reactants at 720-830° C. and the catalytic pyrolysis reaction takes place. A mixture of heavy hydrocarbons having a distillation range higher than 350° C. and a certain amount of steam is atomized and sprayed from feed inlet IV into the lift pipe, where the mixture comes into contact with the mixture of the catalyst and the upstream reaction stream at about 680-800° C. and the catalytic pyrolysis reaction takes place. The distances among the feed inlets for various hydrocarbons are calculated to allow the differences in the residence time of the adjacent hydrocarbons introduced into the reactor in sequence to be 0.0-3 s. Heavier feed oils are sprayed in sequence into the lift pipe at the inlets above the inlets from which the lighter feed oils are sprayed and may play a role of quenching the pyrolyzed stream of lighter feed oils so that the secondary reactions of the pyrolyzed stream of the lighter feed oils are quickly stopped or slowed down. The mixture of the catalyst and the reaction stream of the hydrocarbon feeds in the lift pipe flows upward and enters the subsider 3, wherein fast separation of gas/solid stream is performed. The reaction stream is removed from the outlet 6 at the top of the subsider, while the deactivated catalyst drops down along the subsider and is stripped by the stripping steam sprayed from the pipeline 5. The stripped catalyst to be regenerated goes down and enters the regenerator, wherein the coke-burning regeneration reaction is carried out, the regeneration temperature being 700-950° C. During the coke-burning regeneration, the catalyst absorbs a great amount of heat and its temperature rises to 800-900° C. After steam stripping in the transfer pipeline, the high temperature regenerated catalyst is recycled back to the pre-lift section of the lift pipe along the regeneration inclined pipe for reuse. After quenching, the reaction stream removed from exit 6 enters the fractionation system and separates into pyrolyzed gas and a liquid product rich in aromatics, the pyrolyzed gas is then separated in the separation system into highly pure individual hydrocarbons (CH4, C2H4, C2H6, C3H6, C3H8, C4H8, C4H6, C4H10), wherein the highly pure ethane returns to be bottom of the lift pipe for pyrolysis or is delivered to the ethane pyrolysis heater for pyrolysis.

[0015] The components of the special catalyst (LCM) used for the catalytic pyrolysis can be selected from SiO2, Al2O3 and oxides of alkali metals, alkali earth metals and transition metals or mixtures thereof, aluminum silicate modified with oxides of alkali or alkali earth metals can also be used, and optionally, a part of molecular sieves are added.

[0016] If the feed hydrocarbon to be pyrolyzed are two or more in the scope of ethane, propane, butane, light hydrocarbons having a distillation range lower than 350° C. and heavy hydrocarbons having a distillation range higher than 350° C., different feeds can enter the device from different positions according to the above method to realize the optimization of the pyrolysis conditions.

[0017] The effect of the present invention. Realization of the pyrolysis of the feeds with different properties under different process conditions results in the optimization of the reaction conditions and product structure, e.g., the yield of ethylene attains 23.76 wt % or higher, as well as savings of capital and operating costs.

EXAMPLE 1

[0018] This example is the pyrolysis results using an atmospheric residue and ethane as a co-feed. The pyrolysis test is carried out on a high-low parallel lift pipe pilot-scale device with a total length of the lift pipe being 15.42 m, its internal diameter being 19 mm and a capacity being 0.24 t/d. Ethane, which is difficult to pyrolyze, is first introduced into the lift pipe from the bottom of the lift pipe and brought into contact with the hot and active regenerated catalyst so that reaction takes place, the temperature of the regenerated catalyst at this moment is 820° C., the temperature of the hydrocarbon/catalyst mixture after introducing ethane is 810° C. The inlet of the atmospheric residue is located 4.2 m above the inlet of ethane. The residence time of ethane from the bottom to this point is 0.45 s. The temperature of the mixed stream after introducing the atmospheric residue is 740° C., the temperature at the outlet of the lift pipe is 710° C. The catalyst used in this example is numbered as LCM-A, its properties and composition are shown in Table 1. The process conditions and the material balance in a pilot-scale test of the lift pipe are shown in Table 2. For comparison, the result of the pilot-scale test is also shown when the atmospheric residue and ethane is mixed and fed from the same inlet.

[0019] The results in Table 2 show that, in the technology of ethylene production from atmospheric residues with ethane re-refining, rather optimal pyrolysis conditions for both the atmospheric residue and ethane are realized and the conversions are appropriate when the method of multiple feed at separate point of the present invention are adopted. The yield of ethylene from the individual pyrolysis of the atmospheric residue is 22.36 wt %, while that after the re-refining of 4.56% of ethane attains 25.63 wt %.

[0020] It can also be seen from Table 2 that when the pyrolyzed ethane from the atmospheric residue is not re-refined and additional 6.5 wt % ethane is added, if ethane and the heavy oil are fed from the same feed inlet and the temperature of catalyst/oil mixture is 740° C., the yield of ethylene is only 21.30%; if ethane and the heavy oil are fed into the device from different feed inlets, i.e., the temperature at the inlet for ethane is 810° C. and that for the residue is 740° C., the yield of ethylene is 23.76%. Moreover, the aromatic content in the pyrolyzed gasoline is greater than 86 wt %, that in the pyrolyzed liquid product having a distillation range higher than 200° C. is greater than 89 wt %.

EXAMPLE 2

[0021] This example is the pyrolysis results using an atmospheric residue and a straight run gasoline as a co-feed, the process conditions and the material balance in a pilot-scale test of the lift pipe are shown in Table 3. The straight run gasoline is introduced into the device from the bottom of the lift pipe, the number of the catalyst used is LCM-B, its propertied and composition are seen in Table 1. The temperature of the catalyst/oil mixture is 780° C., the atmospheric residue is sprayed at the position 4.2 m above the inlet of the straight run gasoline, the residence time of the straight run gasoline from the bottom to this point is 0.6 s, and the temperature of the mixed stream after spraying the atmospheric reside is 700° C., the temperature at the outlet of the lift pipe is 660° C.

[0022] The results in Table 3 show that, by using the method of mixed feed of the atmospheric residue and the straight run gasoline, the total pyrolysis extent of the mixed feed is rather low when the optimal conditions for the pyrolysis of the atmospheric residue are ensured, in the total material balance, the yields of ethylene and propylene are 21.84% and Z12.93%, respectively, either of them is lower than that when only the atmospheric reside is pyrolyzed, indicating that the pyrolysis extent of the straight run gasoline is not high; rather high pyrolysis extent of the straight run gasoline is attained while ensuring that the pyrolysis of the atmospheric residue proceeds under the optimal conditions by using the method of the multiple feed at separate point of the present invention: in the total material balance of the mixed feed, the yield of ethylene reaches 24.50%, that of propylene reaches 14.51%, either of them exceeds that when only the atmospheric residue is pyrolyzed.

[0023] Table 1 Properties and composition of the catalyst 1 TABLE 1 Properties and composition of the catalyst Catalyst LCM-A Catalyst LCM-B Item Alkali Transition metal Type of the active component earth metal Oxides oxides Chemical composition Al2O3, wt % 40 42 Na2O, wt % <0.3 <0.3 Fe2O3, wt % 0.8 0.8 Active component, wt % 8.2 6.5 Specific surface, m2/g 58 65 Porosity, ml/g 0.12 0.13 Bulk density, g/ml 0.85 0.85 Sieve composition, wt %  0-20 &mgr; 2.6 3.2 20-40 &mgr; 19.4 20.2 40-60 &mgr; 31.5 32.1 60-80 &mgr; 24.7 23.9 >80 &mgr; 21.8 20.6

[0024] Table 2 Pyrolysis result using ethane and an atmospheric residue 2 TABLE 2 Pyrolysis result using ethane and an atmospheric residue Material balance Material balance for the pyrolysis for the pyrolysis of the atmospheric of the atmospheric Item residue residue and ethane Feeding mode Single Separate* Mixed Separate Whether ethane is refined No Yes No No Ethane content in feed, wt % 0.0 0.0 6.5 6.5 Temp. of regeneration 820 820 820 820 bed, ° C. Temp. of stripping steam for 400 400 400 400 regenerated catalyst, ° C. Stream temp. after spraying / 810 740 810 ethane, ° C. Stream temp. after spraying 740 740 740 740 atmospheric residue, ° C. Temp. at the outlet of lift 710 710 710 710 pipe, ° C. Temp. after quenching, ° C. 600 600 600 600 Catalyst type A A A A Steam/hydrocarbon ratio, 0.23 0.23 0.23 0.23 wt/wt Catalyst/oil ratio, wt/wt 18.0 18.0 18.0 10 Yield of major products, wt % Hydrogen 0.87 1.09 0.84 1.03 Methane 11.44 11.81 10.76 11.13 Ethylene 22.36 25.63 21.30 23.76 Ethane 4.56 / 10.20 6.79 Propylene 12.86 13.25 12.05 12.21 Propane 0.71 0.72 0.67 0.68 Butane 0.22 0.22 0.21 0.21 Butylene 3.04 3.10 2.85 2.90 Butadiene 1.87 1.91 1.75 1.76 Pyrolyzed gasoline (<200° C.) 12.46 12.76 11.68 11.85 Pyrolyzed middle distillate 5.23 5.24 4.94 4.89 Pyrolyzed heavy oil 9.86 9.88 9.30 9.22 (>300° C.) Coke 13.23 13.27 12.40 12.37 Loss 1.29 1.12 1.05 1.21 Where: (1) Aromatic content 88.12 87.75 86.54 87.87 in pyrolyzed gasoline (2) Aromatic content in the 90.13 89.89 90.10 91.39 pyrolyzed product having a distillation range higher than 200° C. *Ethane in the pyrolyzed product from the atmospheric residue is returned back to the lift pipe for re-refining.

[0025] *: Ethane in the pyrolyzed product from the atmospheric residue is returned back to the lift pipe for re-refining.

[0026] Table 3 Pyrolysis result using straight run gasoline and an atmospheric residue 3 TABLE 3 Pyrolysis result using straight run gasoline and an atmospheric residue Material balance Material balance Material balance for for the pyrolysis for pyrolysis of pyrolysis of of atmospheric straight run atmospheric residue and Item residue gasoline straight run gasoline Feeding mode Single Single Mixed Separate Gasoline proportion in feed, wt % 0.0 100 20 20 Temp. of regeneration bed, ° C. 800 / 800 800 Temp. of stripping steam for regenerated 400 / 400 400 catalyst, ° C. Stream temp. after spraying gasoline, ° C. / 780 700 780 Stream temp. after spraying atmospheric residue, ° C. 700 700 700 700 Temp. at the outlet of the lift pipe, ° C. Temp. after quenching, ° C. 660 660 660 660 Catalyst type 600 600 600 600 Steam/hydrocarbon ratio, wt/wt B B B B Catalyst/oil ratio, wt/wt 0.25 / 0.25 0.25 18.6 / 19.2 19.0 Yield of major products, wt % Ethylene 23.05 30.30 21.84 24.50 Propylene 14.01 16.51 12.93 14.51 C4 olefins 6.73 8.48 6.24 7.08 Pyrolyzed gasoline (<200° C.) 13.45 19.20 23.16 14.60 Pyrolyzed middle distillate 6.60 2.00 5.50 5.68 Pyrolyzed heavy oil (>300° C.) 9.31 0.01 7.45 7.45 Coke plus loss 9.00 0.50 7.30 7.30 Where: (1) Aromatic content in pyrolyzed 88.44 92.30 78.52 89.10 gasoline (2) Aromatic content in the pyrolyzed product 92.65 / 92.50 93.76 having a distillation range higher than 200° C.

Claims

1. A process for catalytic pyrolysis of hydrocarbon feeds to produce lower olefins with stress on ethylene and co-produce light aromatics, in which the hydrocarbon feeds are brought into contact with a solid granular catalyst in a piston flow reactor to proceed catalytic pyrolysis, the hydrocarbon feeds including two or more hydrocarbons having different physicochemical properties, the feed hydrocarbons being mixed with steam and introduced, the general reaction conditions in the reaction zone being: temperature 600-900° C., pressure 0.13-0.40 MPa (absolute), total steam/hydrocarbon ratio 0.1-1.0, total catalyst/oil ratio 5-100 and the catalyst/oil contact time 0.02-5 s; the oil gas after reaction is separated quickly from the catalyst and quenched, the catalyst is recycled for reuse after regeneration; different feeds are introduced from different positions, hydrocarbons difficult to pyrolyze are first introduced into the reactor and brought into contact with the catalyst of high temperatures and high activities from the regenerator and the pyrolysis takes place, meanwhile, the catalyst cools down and deactivates; other hydrocarbons easier to pyrolyze are introduced in sequence from the upstream to downstream of the reaction zone, the hydrocarbons introduced later play a role of quenching those introduced earlier, the temperature of the reaction zone and the activity of the catalyst are lowered step by step from the upstream to the downstream; the positions from which various hydrocarbons enter the reactor are determined as such that the residence times of various hydrocarbons in the reactor are gradually decreased in the sequence from difficulty to ease in pyrolysis, the differences in the residence times of every adjacent two hydrocarbon feeds in the reactor are 0.0-3 s.

2. A process according to

claim 1, wherein the hydrocarbon feeds having different physicochemical properties include ethane, propane, butane, light hydrocarbons with a distillation range lower than 350° C., and heavy hydrocarbons with a distillation range higher than 350° C.

3. A process according to

claim 2, wherein the light hydrocarbons with a distillation range lower than 350° C. include LPG, refinery petroleum gases, oil field gases, oil field light hydrocarbons, naphtha and light diesel oil; the heavy hydrocarbons with a distillation range higher than 350° C. include straight run and secondary processing heavy hydrocarbons, i.e., straight run wax oils, coker wax oils, straight run vacuum gas oils, atmospheric residues, coker gas oils, thermal cracking heavy oils, solvent-deasphalted oils and various residues from solvent extraction of heavy hydrocarbons.

4. A process according to

claim 2, wherein the controlled temperature ranges for various hydrocarbons are: ethane, 780-900° C.; propane and/or butane, 750-850° C.; the light hydrocarbons with a distillation range higher lower than 350° C., 720-830° C.; and the heavy hydrocarbons with a distillation range higher than 350° C., 680-800° C.

5. A process according to

claim 3 or

4, wherein the two hydrocarbon feeds are ethane and atmospheric residues respectively.

6. A process according to

claim 1-4, wherein the components of the pyrolysis catalyst used can be selected from SiO2, Al2O3 and oxides of alkali metals, alkali earth metals and transition metals or mixtures thereof, aluminum silicate modified with oxides of alkali or alkali earth metals can also be used, and optionally, a part of molecular sieves are added.

7. A process according to

claim 1, wherein, the deactivated catalyst is delivered to the regenerator for regeneration by burning off the coke after stream stripping; the regeneration temperature is 750-950° C., the high temperature regenerated catalyst is drawn after steam stripping and recycled back to the reactor through the inclined pipe for reuse.

8. A process for direct conversion of heavy hydrocarbon to produce lower olefins with stress on ethylene and co-produce light aromatics, in which the hydrocarbon feed is bought into contact with a solid granular catalyst in a piston flow reactor to proceed catalytic pyrolysis, the feed hydrocarbon is mixed with steam and introduced, the general reaction conditions in the reaction zone are: temperature 660-900° C., pressure 0.13-0.40 MPa (absolute), total steam/hydrocarbon ratio 0.1-1.0, total catalyst/oil ratio 5-100 and the catalyst/oil contact time 0.02-5 s; the oil gas after reaction is separated quickly from the catalyst and quenched, the catalyst is recycled for reuse after regeneration; the oil gas enters a fractionation and separation system to proceed the separation, a product gas mainly containing ethylene, the by-product ethane, and a liquid product rich in aromatics can be obtained; the highly pure by-product ethane from the separation system and/or the gases containing ethane from other sources return to the pyrolysis reactor of the piston flow type from the upstream inlet of the reactor and come into contact with the catalyst of high temperatures and high activities, fast pyrolysis takes place at temperatures higher than 780° C. to produce ethylene and meanwhile, the catalyst cools down and deactivates, steam is introduced at the same time when ethane feed is introduced from the upstream inlet of the reactor; heavy hydrocarbon feed is introduced at position certain distances from downstream of the inlet for ethane, the hydrocarbon introduced later play a role of quenching those introduced earlier, the reaction temperature at this moment is lowered to 680-800° C.; the feeding positions of the by-product ethane and the heavy hydrocarbon are determined as such that the residence time of ethane, which is difficult to pyrolyze, is long, while that of heavy hydrocarbon, which are easy to pyrolyze, is short, the differences in the residence times of ethane and heavy hydrocarbons in the reactor are 0.0-3 s.

9. A process according to

claim 8, wherein the heavy hydrocarbon is the hydrocarbon having a distillation range higher than 350° C., including straight run heavy hydrocarbons and secondary processing heavy hydrocarbons, i.e., straight run wax oils, coker wax oils, straight run vacuum gas oils, atmospheric residues, coker gas oils, thermal cracking heavy oils, solvent-deasphalted oils and various residues from solvent extraction of heavy hydrocarbons.

10. A process according to

claim 8 or

9, wherein the components of the catalyst used for pyrolysis can be selected from SiO2, Al2O3 and oxides of alkali metals, alkali earth metals and transition metals or mixtures thereof, aluminum silicate modified with oxides of alkali or alkali earth metals can also be used, and optionally, a part of molecular sieves are added.

11. A process according to

claim 8 or

9, wherein the deactivated catalyst is delivered to the regenerator for regeneration by burning off the coke after stream stripping, the regeneration temperature is 750-950° C., the high temperature regenerated catalyst is drawn after stripping and recycled back to the reactor through the inclined pipe for reuse.