Process for the manufacture of piezoceramic multilayer actuators

For the manufacture of multilayer actuators, the laminate is split into several actuators, which are pyrolized and then sintered. Because lamination in the unsintered body often produces non-homogeneity in the density, and the shrinkage during the firing of the ceramic is not of a constant value, the final geometry of the actuators can only be accurately obtained by the hardening of the sintered actuators. But in this case the internal electrode layers deposited in the actuators are thereby also processed, which can cause electrical flashovers and leakage currents during operation.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description

[0001] The invention concerns a process for the manufacture of piezoceramic multilayer actuators according to the preamble of the first claim.

[0002] A piezoceramic multilayer actuator 1 is shown schematically in FIG. 1. The actuator consists of stacked thin layers 2 of piezoelectrically active material, for example lead zirconate titanate (PZT), with conductive internal electrodes 3, which are led out alternately to the surface of the actuator, disposed between said layers. External electrodes 4, 5 interconnect the internal electrodes 3. As a result, the internal electrodes 3 are electrically connected in parallel and combined into two groups. The two external electrodes 4, 5 are the connecting poles of the actuator 1. They are connected via the connections 6 to a voltage source, not shown here. If an electrical voltage is applied via the connections 6 to the external electrodes 4, 5, this electrical voltage is transmitted in parallel to all internal electrodes 3 and produces an electric field in all layers 2 of the active material, which is consequently mechanically deformed. The sum of all of these mechanical deformations is available at the end faces of the head region 7 and the foot region 8 of the actuator 1 as a useable expansion 9 and/or force.

[0003] Piezoceramic multilayer actuators are fabricated according to the prior art as monoliths, that is to say the active material onto which internal electrodes are deposited by a silk screen process prior to sintering, is disposed as a so-called green film in successive layers as a stack that is compressed into a green body. The compression of the green body is usually carried out by lamination under the action of pressure and temperature in laminating moulds. Depending on the lamination tool used, this process determines to a large extent the external shape of the actuators. The laminate is separated into several actuators, which are pyrolized and then sintered. Since lamination in the unsintered body often produces non-homogeneity in the density, and the shrinkage during the firing of the ceramic is not of a constant value, the final required geometry of the actuators can only be accurately obtained by the hardening of the sintered actuators. However, in this case the internal electrode layers deposited in the actuators are thereby also processed. If the processed surfaces are not subsequently electrically insulated, then when these piezoceramic multilayer actuators are actively operated, there is a risk of an electrical flashover at the actuator surface because the dielectric field strength in air, which amounts to approximately 1000 V/mm, is exceeded by the operating field strengths of over 2000 V/mm. At the same time the smearing of the electrodes caused by the hardening additionally leads to reduced dielectric strength and/or leakage currents.

[0004] The object of the present invention is to present a process that simplifies the manufacture of multilayer actuators and by which the demonstrated disadvantages are avoided.

[0005] This object is achieved by means of the characterising features of the first claim. Advantageous developments of the invention are claimed in the sub-claims.

[0006] By stacking green films made of piezoceramic material, which are printed with the corresponding patterns of the internal electrodes for at least one piezoceramic multilayer actuator and by corresponding lamination under pressure of around 100 bar at a temperature of approximately 120° C., a green body is obtained with high mechanical strength, good adhesion between film layers, good mechanical machinability and homogeneous density. According to the invention, it is therefore possible to easily detach the multilayer actuators from such a green body as a laminate and subsequently by machining to yield their shape, which is usually already the final shape, so that after sintering the actuators require no further finishing. The insulating sinter skin needs only to be removed at the connecting faces where the internal electrodes have to be connected to the respective external electrode, for example by grinding. Due to the high mechanical strength of the laminate blocks, all machining operations, such as turning, milling, sawing, drilling or grinding are possible. In this case the bodies are neither damaged nor deformed. Due to the lower hardness of the material compared to the sintered state, tool wear is considerably reduced, thus making low-cost production possible.

[0007] Due to sintering, a so-called sinter skin forms all over the surface of the piezoceramic multilayer actuator, which sinter skin has such a high electrical insulating capability, even in the region where the internal electrodes emerge at the surface of the actuator, that subsequent insulation of the surfaces of the piezoceramic multilayer actuator can usually be omitted.

[0008] Through suitable choice and/or combination of machining methods, the good machinability of the laminate enables piezoceramic multilayer actuators to be manufactured with different shapes. The cross-sectional areas can be circular, elliptical, square or polygonal. All edges of the green bodies can be broken, chamfered or rounded off prior to sintering. The ease of machining of the ceramic material in the green phase also enables rotationally symmetric mouldings to be produced.

[0009] The laminated block with the at least one multilayer actuator has a high strength and a high dimensional stability. It is thus possible, prior to sintering, to place several boreholes or pocket holes in the block and/or the unsintered piezoceramic multilayer actuator, which can additionally be provided with a thread. Such an arrangement can be advantageous for subsequent applications, such as fixings or connections. Since the layers of the internal electrodes are penetrated by the boreholes or pocket holes as well as by the mahine-cut thread, in this case the sinter skin produced by sintering can also be advantageously used as an insulating layer.

[0010] A further option for shaping the multilayer actuators consists in punching holes of the required size, shape and number in the green films in the same operating cycle, prior to lamination, in which the green films are suitably punched out for the laminating mould. The green films with the printed internal electrodes thereon are then stacked one on top of the other in the required number and arrangement, so that the boreholes or pocket holes are produced in the desired arrangement and depth. Here again, threads can be machine-cut in the holes following lamination.

[0011] To increase stability and to maintain dimensional accuracy, the boreholes, through-holes or pocket holes can be filled prior to lamination with a filler which prevents any plastic deformation of the recesses which otherwise may occur during lamination. This filler is chosen so that under lamination conditions it is not more plastic or cannot be deformed to a greater degree than the piezoceramic material of the green films.

[0012] A filler may consist of a hard, dimensionally stable and, during lamination, thermally stable material, for example metal or ceramic. According to the shaping, pins or threaded pins can be inserted into the boreholes or pocket holes.

[0013] Furthermore, plastic or thermoplastic fillers, in particular a highly-flexible rubber or rubber-like plastic, are suitable. Here too the filler can have the form of a pin or threaded pin.

[0014] Following lamination, the pins or threaded pins are withdrawn or unscrewed from the laminate.

[0015] Fillers which remain dimensionally stable up to the lamination temperature are also suitable. During lamination or sintering these fillers smelt or pyrolize. For example, wax or low-melting-point polymers can be removed from the laminate by heating. A suitable organic material can also be used as a filler, such as is known from the prior art for forming porous ceramics, for example carbon black or a polymer that pyrolizes without residues during lamination or sintering at temperatures up to 700° C.

[0016] The thermal removal may also be achieved by melting out and/or thermal decomposition in a thermal process preceding sintering, for example an appropriate debonding process.

[0017] The invention is explained in further detail with the aid of an exemplifying embodiment in which:

[0018] FIG. 2 shows a green film with several internal electrodes, and

[0019] FIG. 3 shows a multilayer actuator manufactured according to the process according to the invention.

[0020] FIG. 2 shows a green film 10 made of piezoceramic material already punched out for the laminating mould. Six internal electrodes 11 are each placed on this green film, this application usually being achieved by the silk screen process. The assignment of several internal electrodes to one green film allows the efficient manufacture of several multilayer actuators at the same time. On one side of the circular cross-sectional area 12, a circular section is cut out so that the area is limited by a secant 13. A hole 15 is punched out concentrically to the mid-point 14.

[0021] The required numbers of green films are stacked one above the other to form a block, so that the internal electrodes lie one above the other. The number of films depends on the size of the multilayer actuator. In the present exemplifying embodiment, the block has six multilayer actuators. Due to the ease of separation, following lamination, the multilayer actuators, still in the green state, are separated from each other around the internal electrodes. Likewise still in the green state, the final machining of the multilayer actuators can then take place until the specified basic diameter of the multilayer actuator is obtained. Only after this are the multilayer actuators sintered.

[0022] The arrangement of the internal electrodes 11 on the green film 10 always has the same orientation. These are internal electrodes of the same polarity. The internal electrodes of the opposite polarity can be fabricated in the same way. In this case, however, their orientation is opposite to the orientation of the internal electrodes of opposite polarity assigned to them, that is to say rotated by 180 degrees on the subsequent green film. The electrode layers with the opposite polarity therefore alternate. In a block which shows the contour of a multilayer actuator, the holes 15 lying one above the other form a continuous recess.

[0023] A multilayer actuator 16 that has been manufactured according to the process according to the invention is shown in a schematic, much enlarged representation in FIG. 3. It has a circular cross-section 12 and is fully coated by a sinter skin 17. The internal electrodes 11 of the same polarity are fully exposed on the peripheral face, whereas in the case of the internal electrodes of opposite polarity the circumference is broken because of the missing circular section. This design is advantageously utilised to connect the internal electrodes of the same polarity to the respective external electrode 18, at the opposite sides of the multilayer actuator where the internal electrodes of the same polarity can now be seen at the periphery. The sinter skin 17 is removed in this region by grinding, and the internal electrodes 11 are exposed at their peripheral face. A continuous recess 20, formed from the holes 15 lying one above the other in the green films 10, which can be used for fixing purposes, runs concentrically to the axis 19 of the multilayer actuator 16.

Claims

1. Process for the manufacture of piezoelectric multilayer actuators, in which thin layers made from a piezoceramic material, termed green films, onto which at least one internal electrode is placed, are stacked one above the other into a block, so that the internal electrodes are led out alternately at opposing faces of the actuator, where they are interconnected by an external electrode, characterised in that the block is laminated, that at least one actuator is separated from this block, that the actuator obtains its shape by means of a machining operation, that it is then sintered, that the sinter skin produced by the sintering is used as an insulating layer and that the sinter skin is abraded at the points where the internal electrodes are connected to the external electrodes.

2. Process according to claim 1, characterised in that the shaping is achieved by machining.

3. Process according to claim 1 or 2, characterised in that multilayer actuators, which have square, polygonal, circular or elliptical cross-sectional areas, are produced by the shaping.

4. Process according to claim 1 or 2, characterised in that rotationally symmetric multilayer actuators are produced by the shaping.

5. Process according to one of claims 1 to 4, characterised in that one or more through-holes or pocket holes are introduced into the laminated block of at least one multilayer actuator.

6. Process according to one of claims 1 to 4, characterised in that prior to lamination, holes of the required size, shape and number are punched in the green films and the green films provided with the internal electrodes are then stacked one on top of the other in the required number and arrangement, so that the boreholes or pocket holes are produced in the desired arrangement and depth.

7. Process according to one of claims 5 or 6, characterised in that a thread is machine-cut in the boreholes or in the pocket holes, respectively.

8. Process according to one of claims 5 to 7, characterised in that to increase stability and to maintain dimensional accuracy, the borehole or the pocket holes in the multilayer actuators can be filled prior to lamination with a filler.

9. Process according to claim 8, characterised in that a hard, dimensionally stable and, during lamination, thermally stable material, is used as a filler.

10. Process according to claim 8 or 9, characterised in that a filler made from metal or ceramic or another hard, dimensionally stable and, during lamination, thermally stable, material is used.

11. Process according to claim 8, characterised in that a plastic or thermoplastic material is used as a filler.

12. Process according to claim 11, characterised in that a highly-flexible rubber or a rubber-like plastic is used.

13. Process according to one of claims 8 to 12, characterised in that the filler is used in the form of pins or threaded pins.

14. Process according to claim 13, characterised in that following lamination, the pins or threaded pins are withdrawn or unscrewed from the laminate.

15. Process according to claim 8, characterised in that a filler is used that remains dimensionally stable approximately up to the lamination temperature and is thermally removed.

16. Process according to claim 15, characterised in that a wax or a low-melting-point polymer is used as a filler, and that these fillers smelt during lamination or sintering.

17. Process according to claim 15, characterised in that a suitable organic material that pyrolizes without residues during lamination or sintering is used as a filler.

18. Process according to claim 15, characterised in that the thermal removal is achieved by smelting and/or thermal decomposition in a thermal process preceding sintering, for example an appropriate debonding process.

Patent History
Publication number: 20020175591
Type: Application
Filed: Feb 20, 2002
Publication Date: Nov 28, 2002
Inventors: Hans-Jurgen Schreiner (Neunkirchen am Sand-Rollhofen), Reiner Bindig (Binlach), Matthias Simmerl (Henfenfeld), Jurgen Schmidt (Marktredwitz)
Application Number: 10079946
Classifications
Current U.S. Class: Piezoelectric Elements And Devices (310/311); Piezoelectric Device Making (029/25.35); Electrode Arrangement (310/365)
International Classification: H04R017/00; H01L041/04;