Catalyst ink
A catalyst ink is provided, comprising: 25-95% by weight water; 1-50% by weight of at least one solid catalyst, typically a highly dispersed platinum catalyst; 1-50% by weight of at least one polymer electrolyte in acid (H+) form; and 1-50% by weight of at least one polar aprotic organic solvent. The catalyst ink typically has a viscosity at 1 sec−1 of 10 Pa·sec or less. The catalyst ink typically does not ignite spontaneously when dried to completion in air at a temperature of 80° C. or greater. The catalyst ink may be used in the fabrication of membrane electrode assemblies for use in fuel cells.
Latest 3M Innovative Properties Company Patents:
[0001] This invention relates to a catalyst ink composition, typically for use in the fabrication of membrane electrode assemblies used in fuel cells.
BACKGROUND OF THE INVENTION[0002] European Patent Application EP 0 955 687 A2 discloses a method for preparing a slurry for forming a catalyst layer of a PEM fuel cell electrode. In the disclosed method, MOH is added to a water/alcohol solution of a perfluorosulfonate ionomer (PFSI)(such as Nafion™) to convert the PFSI to M+ form. An organic polar solvent such as dimethyl sulfoxide, N,N-dimethyl formamide or ethylene glycol is added ('687 at para. 24, para. 27, and claim 6). The mixture is then heated to drive off alcohol and catalyst is added to form the slurry. After the slurry has been applied to a backing layer and dried to form a catalyst layer, the catalyst layer is treated with acid to convert the PFSI from M+ form to H+ form. ('687 at para. 44 and claim 5).
[0003] U.S. patent application Publication US2002/0045081 discloses the use of sulfonated PEEK polymers dissolved in N-methyl pyrrolidone (NMP), a polar aprotic solvent ('081 at Example 1).
[0004] U.S. Pat. No. 5,906,716 discloses a metalized cation exchange membrane preferably made with a cation-exchange polymer that is soluble in a polar aprotic solvent (such as NMP) and comprises arylene units in the backbone of the polymer, e.g., sulfonated PEEK polymers ('716 at Example 1).
[0005] U.S. patent application Publication US2002/0019308 discloses a composite catalyst.
[0006] Japanese Unexamined Patent Publication 2000-353528 discloses a porous electrode catalyst layer and a method of making a porous electrode catalyst layer. The Examples appear to disclose the use of a solution of Nafion™ in NMP, obtained by solvent exchange of a stock solution of Nafion™.
[0007] Japanese Unexamined Patent Publication 2001-273907A discloses a porous electrode catalyst layer and a phase separation method of making a porous electrode catalyst layer. The Examples appear to disclose the application of suspension of catalyst in Nafion™ solution followed by drying and then application of a PVdF/NMP solution followed by solvent exchange with water to create a porous layer of PVdF.
[0008] International Patent Application WO 01/71835 A2 discloses a method of manufacturing a membrane/electrode composite.
[0009] UK Patent Application GB 2 316 802 A discloses gas diffusion electrodes based on polyethersulfone carbon blends.
[0010] U.S. Pat. No. 5,716,437 discloses an aqueous ink for use in electrode manufacture.
[0011] WO 99/21239 discloses a method for the production of metal colloid solutions by reducing dissolved catalyst metals in the presence of a cation exchange polymer.
SUMMARY OF THE INVENTION[0012] Briefly, the present invention provides a catalyst ink comprising: 25-95% by weight water; 1-50% by weight of at least one solid catalyst, typically a highly dispersed platinum catalyst; 1-50% by weight of at least one polymer electrolyte in acid (H+) form; and 1-50% by weight of at least one polar aprotic organic solvent. The catalyst ink typically has a viscosity at 1 sec−1 of 10 Pa·sec or less. The catalyst ink typically does not ignite spontaneously when dried to completion in air at a temperature of 80° C. or greater.
[0013] In this application:
[0014] “highly dispersed platinum catalyst” means a platinum-containing catalyst having a specific surface area of greater than 100 m2/g, more typically greater than 500 m2/g, and most typically greater than 900 m2/g, such as a catalyst dispersed on a powdered carbon support;
[0015] “highly fluorinated” means containing fluorine in an amount of 40 wt % or more, typically 50 wt % or more and more typically 60 wt % or more;
[0016] “dried to completion” means dried until water content is essentially in equilibrium with ambient air, or lower; and
[0017] “standard boiling point” means the boiling point reported in standard reference works.
[0018] It is an advantage of the present invention to provide a catalyst ink, in particular a catalyst ink for use in fuel cell fabrication, which exhibits favorable rheology during application and does not spontaneously ignite when dried to completion in air at an elevated temperature.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS[0019] The present invention provides a catalyst ink comprising: 25-95% by weight water; 1-50% by weight of at least one solid catalyst, typically a highly dispersed platinum catalyst; 1-50% by weight of at least one polymer electrolyte in acid (H+) form; and 1-50% by weight of at least one polar aprotic organic solvent. The catalyst ink typically has a viscosity at 1 sec−1 of 10 Pa·sec or less. The catalyst ink typically does not ignite spontaneously when dried to completion in air at a temperature of 80° C. or greater.
[0020] The catalyst ink according to the present invention may be used in the fabrication of membrane electrode assemblies (MEA's) for use in fuel cells. An MEA is the central element of proton exchange membrane fuel cells such as hydrogen fuel cells. Fuel cells are electrochemical cells which produce usable electricity by the catalyzed combination of a fuel such as hydrogen and an oxidant such as oxygen. Typical MEA's comprise a polymer electrolyte membrane (PEM) (also known as an ion conductive membrane (ICM)), which functions as a solid electrolyte. One face of the PEM is in contact with an anode electrode layer and the opposite face is in contact with a cathode electrode layer. Each electrode layer includes electrochemical catalysts, typically including platinum metal. The anode and cathode electrode layers may be applied to the PEM in the form of a catalyst ink to form a catalyst coated membrane (CCM). Fluid transport layers (FTL's) facilitate gas transport to and from the anode and cathode electrode materials and conduct electrical current. In a typical PEM fuel cell, protons are formed at the anode via hydrogen oxidation and transported to the cathode to react with oxygen, allowing electrical current to flow in an external circuit connecting the electrodes. The FTL may also be called a gas diffusion layer (GDL) or a diffuser/current collector (DCC). In an alternate manufacturing method, the anode and cathode electrode layers may be applied to the FTL in the form of a catalyst ink, rather than to the PEM, and the coated FTL's sandwiched with a PEM to form an MEA.
[0021] Any suitable catalyst may be used in the practice of the present invention. The catalyst is typically a highly dispersed platinum catalyst having a specific surface area of greater than 100 m2/g, more typically greater than 500 m2/g, and most typically greater than 900 m2/g. Typically, carbon-supported catalyst particles are used. Typical carbon-supported catalyst particles are 50-90% carbon and 10-50% catalyst metal by weight, the catalyst metal typically comprising Pt for the cathode and Pt and Ru in a weight ratio of 2:1 for the anode.
[0022] Any suitable polymer electrolyte may be used in the practice of the present invention. The polymer electrolyte is typically highly fluorinated or perfluorinated. The polymer electrolyte is typically an acid-functional fluoropolymer, such as Nafion® (DuPont Chemicals, Wilmington Del.) and Flemion™ (Asahi Glass Co. Ltd., Tokyo, Japan). The polymer electrolytes useful in inks for use in the present invention are typically copolymers of tetrafluoroethylene and one or more fluorinated, acid-functional comonomers. Typically the polymer electrolyte bears sulfonate functional groups. Typically the polymer electrolyte contains no arylene units in the polymer backbone. Most typically the polymer electrolyte is Nafion®. The polymer electrolyte typically has an equivalent weight of 1200 or less, more typically 1100 or less, more typically 1050 or less, and most typically about 1000. In the ink according to the present invention, the polymer electrolyte is substantially in protonated form or acid (H+) form, rather than in salt form.
[0023] The polar aprotic organic solvent typically has a standard boiling point of at least 80° C., more typically at least 100° C., more typically at least 160° C., and most typically at least 200° C. The polar aprotic organic solvent is typically selected from the group consisting of: dimethylsulfoxide (DMSO), N,N-dimethyacetamide (DMA), ethylene carbonate, propylene carbonate, dimethylcarbonate, diethylcarbonate, N,N-dimethylformamide (DMF), N-methylpyrrolidinone (NMP), dimethylimidazolidinone, acetonitrile, butyrolactone, hexamethylphosphoric triamide, isobutyl methyl ketone, and sulfolane; and more typically selected from the group consisting of N-methyl pyrrolidinone (NMP), N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsufoxide (DMSO) and acetonitrile. Most typically, the polar aprotic organic solvent is N-methyl pyrrolidinone (NMP).
[0024] The catalyst ink typically contains 25-95% water, more typically 50-80% water, and more typically 60-75% water. The catalyst ink typically contains 1-50% solid catalyst, more typically 5-25% solid catalyst, and more typically 10-20% solid catalyst. The catalyst ink typically contains 1-50% polymer electrolyte, more typically 1-20% polymer electrolyte, more typically 1-10% polymer electrolyte, and more typically 3-8% polymer electrolyte. The catalyst ink typically contains 1-50% of a second solvent, typically a polar aprotic organic solvent, more typically 3-25% polar aprotic organic solvent, more typically 5-15% polar aprotic organic solvent, and more typically 8-14% polar aprotic organic solvent. The catalyst ink typically contains 5-30% solids (i.e. polymer and catalyst).
[0025] The ink may be mixed by any suitable method. The ink is typically made by stirring with heat which may be followed by dilution to a coatable consistency. The ink typically has a viscosity at 1 sec−1 of 10 Pa·sec or less, more typically 6 Pa·sec or less, more typically 2 Pa·sec or less, and most typically 1.0 Pa·sec or less.
[0026] The ink may be used in the manufacture of a CCM or MEA for use in a fuel cell. The ink may be applied to a PEM or FTL by any suitable means, including both hand and machine methods, including hand brushing, notch bar coating, fluid bearing die coating, wire-wound rod coating, fluid bearing coating, slot-fed knife coating, three-roll coating, or decal transfer. In the case of decal transfer, the ink is first applied to a transfer substrate and dried, and thereafter applied as a decal to a PEM. Coating may be achieved in one application or in multiple applications. After coating, the ink may be dried in an oven or the like, in air, at temperatures in excess of 80° C., more typically in excess of 110° C., and more typically in excess of 140° C. The ink according to the present invention preferably will not self-ignite when dried to completion under these conditions. Typically, an ink that will not self-ignite during drying will also be more safe to manufacture, handle and use.
[0027] This invention is useful in the fabrication of membrane electrode assemblies for use in fuel cells.
[0028] Objects and advantages of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention.
EXAMPLES[0029] Unless otherwise noted, all reagents were obtained or are available from Aldrich Chemical Co., Milwaukee, Wis., or may be synthesized by known methods.
[0030] Formulation of Inks
[0031] With reference to Table I, several catalyst inks were made, including comparative catalyst inks and catalyst inks according to the present invention. Anode inks (Examples 1C (comparative), 2C (comparative), and 3-6) and cathode inks (Examples 7C (comparative), 8C (comparative), 9 and 10) were made.
[0032] Anode inks were made as follows: 30 g of catalyst powder (SA27-13RC, 27% Pt & 13% Ru on 60% carbon from N.E. Chemcat Corp., Tokyo, Japan) were weighed into a (16 oz) glass jar (8.9 cm diameter by 8.9 cm height). Then, 112.2 g of a Nafion™ solution (SE-10172, 10% in Water, CAS#31175-20-9, DuPont Fluoroproducts, Wilmington, Del., USA) were gradually added to the catalyst powder in the glass jar while the contents were uniformly dispersed with a spatula to ensure no dry clumps of catalyst powder remained in the mixture. The glass jar was then placed in ice bath, to minimize solvent evaporation, under a rotor-stator high-shear mixer (Ultra-Turrax T25, IKA Works, Wilmington, N.C.) and deagglomerated for 1 minute at 16,000 rpm. Then 20.4 g of the additional solvent indicated in Table I was added and high-shear mixing at 16,000 rpm was continued for an additional 10 min. Additional solvents were selected from: Water (B.P. 100° C.), Ethylene Glycol (B.P. 197° C., CAS#107-21-1), N-methyl pyrrolidinone (NMP)(B.P. 202° C., CAS#872-50-4), N,N-Dimethylformamide (DMF)(B.P. 153° C. CAS#68-12-2), N,N-Dimethylacetamide (DMA)(B.P. 165° C., CAS#127-19-5), and Dimethylsulfoxide (DMSO)(B.P. 189° C., CAS#67-68-5). After high shear deagglomeration, a rubber spatula was used to scrape the catalyst dispersion off the rotor-stator mixing head and off the wall of the glass jar and the jar was tightly sealed to prevent solvent loss from the catalyst dispersion.
[0033] Cathode inks were made as follows: 30 g of catalyst powder (SA50BK, 50% Pt on 50% carbon from N.E. Chemcat Corp., Tokyo, Japan) were weighed into a (16 oz) glass jar (8.9 cm diameter by 8.9 cm height). Then, 84 g of a Nafion™ solution (SE-10172, 10% in Water, CAS#31175-20-9, DuPont Fluoroproducts, Wilmington, Del., USA) were gradually added to the catalyst powder in the glass jar while the contents were uniformly dispersed with a spatula to ensure no dry clumps of catalyst powder remained in the mixture. 80.1 g of additional water were added. The glass jar was then placed in ice bath, to minimize solvent evaporation, under a rotor-stator high-shear mixer (Ultra-Turrax T25, IKA Works, Wilmington, N.C.) and deagglomerated for 1 minute at 16,000 rpm. Then 22.5 g of the additional solvent indicated in Table I was added and high-shear mixing at 16,000 rpm was continued for an additional 10 min. Additional solvents were selected from: Water (B.P. 100° C.), Ethylene Glycol (B.P. 197° C., CAS#107-21-1), N-methyl pyrrolidinone (NMP)(B.P. 202° C., CAS#872-50-4), and Acetonitrile (B.P. 81.6° C., CAS#75-05-8). After high shear deagglomeration, a rubber spatula was used to scrape the catalyst dispersion off the rotor-stator mixing head and off the wall of the glass jar and the jar was tightly sealed to prevent solvent loss from the catalyst dispersion. For Example 10, the weights reported above were cut to one third, i.e., 10 g of anode catalyst powder, 28 g of Nafion™ solution, 26.7 g of additional water and 7.5 g of additional solvent (acetonitrile) were used.
[0034] Properties of Inks
[0035] The ink from each Example was examined for flocculation, measured for viscosity, and tested for incineration under drying conditions.
[0036] The ink from each Example was examined for flocculation by eye and classified as strongly flocculated or weakly flocculated. The results are reported in Table I.
[0037] A Bohlin Constant Stress Rheometer (available from Bohlin Instruments Inc., East Brunswick, N.J.) was used to continuously measure the viscosity of a catalyst dispersion as a function of shear rate. Flow properties under constant stress conditions were measured using a C14 cup-and-bob geometry at shear rates of between 1 and 800 sec−1.
[0038] A plot was made of shear viscosity vs. shear rate. Shear rate (S) and shear viscosity (V) are related by the following equation, known as the “Power Law Fluid” equation:
V=k S(n−1)
[0039] where, “k” is a constant that indicates viscosity at 1 sec−1 and “n” is the Power Law Index (PLI), which indicates of the effect of shear on viscosity. If the shear viscosity of a material is insensitive to shear rate, i.e., the fluid is a Newtonian fluid, the PLI is 1.0. Those dispersions whose viscosity decreases with shear are non-Newtonian and known as thixotropic. The PLI of these thixotropic fluids range from 0 to 1. The principles of the power law index are further described in C. W. Macosko, “Rheology: Principles, Measurements, and Applications”, ISBN #1-56081-579-5, at page 85, incorporated herein by reference.
[0040] Incineration was tested by notch-bar application of a 3″ (7.6 cm) wide by 3-mil (76 micron) thick coating of the catalyst ink on a release liner comprising a 1-mil thick silicone-coated microstructured polypropylene having microfeatures with a depth of about 50 micron. Immediately after coating, the coating along with the liner were placed in aluminum pan and placed in a convective air oven at 140° C. The coating was allowed to dry for 10 min. Later, the coatings were examined for either complete drying or incineration of the catalyst coating. 1 TABLE I Ex. 1C Ex. 2C Ex.3 Ex. 4 Ex. 5 Ex. 6 Ex. 7C Ex. 8C Ex. 9 Ex. 10 Type of Ink Anode Anode Anode Anode Anode Anode Cathode Cathode Cathode Cathode Additional Water Ethyene NMP NMF DMA DMSO Water Ethylene NMP Acetonitrile Solvent Glycol Glycol Type of Solvent Inorganic Protic- Aprotic- Aprotic- Aprotic- Aprotic- Inorganic Protic- Aprotic- Aprotic- Organic Organic Organic Organic Organic Organic Organic Organic Total Solids 25.4% 25.4% 25.4% 25.4% 25.4% 25.4% 17.7% 17.7% 17.7% 17.7% Flocculation strong weak weak weak weak weak strong strong weak weak Viscosity at 1 sec−1 14.5 0.92 0.9 1.67 5.79 1.86 14.6 12.62 0.45 0.95 (Pa · sec) Power Law Index 0.3956 0.6622 0.6604 .06155 0.5016 0.6014 0.2509 0.2414 0.6823 0.6361 Incineration No Yes No No No No No Yes No No
[0041] Various modifications and alterations of this invention will become apparent to those skilled in the art without departing from the scope and principles of this invention, and it should be understood that this invention is not to be unduly limited to the illustrative embodiments set forth hereinabove. All publications and patents are herein incorporated by reference to the same extent as if each individual publication or patent was specifically and individually indicated to be incorporated by reference.
Claims
1. A catalyst ink comprising:
- a) 25-95% by weight water;
- b) 1-50% by weight of at least one solid catalyst;
- c) 1-50% by weight of at least one polymer electrolyte in acid (H+) form; and
- d) 1-50% by weight of at least one polar aprotic organic solvent.
2. The catalyst ink according to claim 1 wherein said solid catalyst is a highly dispersed platinum catalyst.
3. The catalyst ink according to claim 2 wherein said polar aprotic organic solvent has a standard boiling point of at least 80° C.
4. The catalyst ink according to claim 2 wherein said polar aprotic organic solvent is selected from the group consisting of: dimethylsulfoxide (DMSO), N,N-dimethyacetamide (DMA), ethylene carbonate, propylene carbonate, dimethylcarbonate, diethylcarbonate, N,N-dimethylformamide (DMF), N-methylpyrrolidinone (NMP), dimethylimidazolidinone, acetonitrile, butyrolactone, hexamethylphosphoric triamide, isobutyl methyl ketone, and sulfolane.
5. The catalyst ink according to claim 2 wherein said polar aprotic organic solvent is selected from the group consisting of: N-methyl pyrrolidinone (NMP), N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsufoxide (DMSO) and acetonitrile.
6. The catalyst ink according to claim 2 wherein said polar aprotic organic solvent is N-methyl pyrrolidinone (NMP).
7. The catalyst ink according to claim 2 wherein said polymer electrolyte is highly fluorinated.
8. The catalyst ink according to claim 7 wherein said polymer electrolyte contains no arylene units in the polymer backbone.
9. The catalyst ink according to claim 2 comprising 50-80% water.
10. The catalyst ink according to claim 2 comprising 10-20% of said solid catalyst.
11. The catalyst ink according to claim 2 comprising 1-10% of said polymer electrolyte in acid (H+) form.
12. The catalyst ink according to claim 2 comprising 5-15% of said polar aprotic organic solvent.
13. The catalyst ink according to claim 2 having a viscosity at 1 sec−1 of 10 Pa·sec or less.
14. The catalyst ink according to claim 2 having a viscosity at 1 sec−1 of 1.0 Pa·sec or less.
15. The catalyst ink according to claim 2 wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 80° C. or greater.
16. The catalyst ink according to claim 2 wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 110° C. or greater.
17. The catalyst ink according to claim 2 wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 140° C. or greater.
18. A catalyst ink comprising:
- a) 25-95% by weight water;
- b) 1-50% by weight of at least one highly dispersed platinum catalyst;
- c) 1-50% by weight of at least one polymer electrolyte in acid (H+) form; and
- d) 1-50% by weight of at least one second solvent which is not water;
- wherein said catalyst ink has a viscosity at 1 sec−1 of 10 Pa·sec or less, and
- wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 80° C. or greater.
19. The catalyst ink according to claim 18 wherein said second solvent has a standard boiling point of at least 80° C.
20. The catalyst ink according to claim 18 wherein said second solvent is selected from the group consisting of: dimethylsulfoxide (DMSO), N,N-dimethyacetamide (DMA), ethylene carbonate, propylene carbonate, dimethylcarbonate, diethylcarbonate, N,N-dimethylformamide (DMF), N-methylpyrrolidinone (NMP), dimethylimidazolidinone, acetonitrile, butyrolactone, hexamethylphosphoric triamide, isobutyl methyl ketone, and sulfolane.
21. The catalyst ink according to claim 18 wherein said second solvent is selected from the group consisting of: N-methyl pyrrolidinone (NMP), N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsufoxide (DMSO) and acetonitrile.
22. The catalyst ink according to claim 18 wherein said second solvent is N-methyl pyrrolidinone (NMP).
23. The catalyst ink according to claim 18 wherein said polymer electrolyte is highly fluorinated.
24. The catalyst ink according to claim 23 wherein said polymer electrolyte contains no arylene units in the polymer backbone.
25. The catalyst ink according to claim 18 comprising 50-80% water.
26. The catalyst ink according to claim 18 comprising 10-20% of said solid catalyst.
27. The catalyst ink according to claim 18 comprising 1-10% of said polymer electrolyte in acid (H+) form.
28. The catalyst ink according to claim 18 comprising 5-15% of said second solvent.
29. The catalyst ink according to claim 18 having a viscosity at 1 sec−1 of 1.0 Pa·sec or less.
30. The catalyst ink according to claim 18 wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 110° C. or greater.
31. The catalyst ink according to claim 18 wherein said catalyst ink does not ignite spontaneously when dried to completion in air at a temperature of 140° C. or greater.
Type: Application
Filed: Dec 10, 2002
Publication Date: Jun 10, 2004
Applicant: 3M Innovative Properties Company
Inventors: Bhaskar V. Velamakanni (Woodbury, MN), David Robert Mekala (Maplewood, MN), Eric Joseph Hanson (Hudson, WI)
Application Number: 10315589
International Classification: C09D011/00; H01M004/86;